JP2000071383A - Salt-injury resistant stainless-clad steel and tank using the same - Google Patents
Salt-injury resistant stainless-clad steel and tank using the sameInfo
- Publication number
- JP2000071383A JP2000071383A JP10246060A JP24606098A JP2000071383A JP 2000071383 A JP2000071383 A JP 2000071383A JP 10246060 A JP10246060 A JP 10246060A JP 24606098 A JP24606098 A JP 24606098A JP 2000071383 A JP2000071383 A JP 2000071383A
- Authority
- JP
- Japan
- Prior art keywords
- salt
- tank
- clad steel
- stainless steel
- stainless
- Prior art date
- Legal status (The legal status is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the status listed.)
- Pending
Abstract
Description
【０００１】[0001]
【発明の属する技術分野】本発明は、耐塩害用ステンレ
スクラッド鋼及びそれを用いたタンクに関するものであ
る。The present invention relates to a stainless steel clad steel for salt damage and a tank using the same.
【０００２】[0002]
【従来の技術】従来、ステンレス製のタンクは、海岸近
くの塩害地域においては、タンクの表面に塩分が付着し
て耐蝕性が落ちるので、タンクの表面にさらにエポキシ
樹脂、ウレタン樹脂又はフッ素樹脂を塗布している。2. Description of the Related Art Conventionally, stainless steel tanks have a tendency to adhere to the surface of the tank in a salt-hazardous area near the coast, thereby reducing the corrosion resistance. Therefore, an epoxy resin, a urethane resin or a fluorine resin is further applied to the tank surface. Coated.
【０００３】[0003]
【発明が解決しようとする課題】ところが、上記従来の
錆防止対策は、エポキシ樹脂やウレタン樹脂塗装の場合
には寿命が５〜６年と短く、フッ素樹脂でも１０年程度
であり、短い周期で保守・管理を行う必要があった。
又、樹脂を塗布するのでタンクの外観を損ねるという問
題もあった。However, the conventional rust prevention measures described above have a short service life of 5 to 6 years in the case of epoxy resin or urethane resin coating and about 10 years in the case of fluorine resin. Maintenance and management had to be performed.
There is also a problem that the appearance of the tank is impaired because the resin is applied.
【０００４】本発明は、上記従来の技術に存在する問題
点に着目してなされたものであって、その目的は、塩分
に対する耐蝕性を向上することができるステンレスクラ
ッド鋼を提供することにある。、又、この発明の別の目
的は、上記目的に加えて、保守・管理を容易に行うこと
ができるタンクを提供することにある。[0004] The present invention has been made in view of the problems existing in the prior art, and an object of the present invention is to provide a stainless steel clad steel capable of improving corrosion resistance to salt. . Another object of the present invention is to provide a tank which can be easily maintained and managed in addition to the above objects.
【０００５】[0005]
【課題を解決するための手段】上記の目的を達成するた
めに、請求項１に記載のステンレスクラッド鋼の発明
は、金属製の母材の表裏両面のうち少なくとも表面側に
耐塩害性ライニング材を接合している。In order to achieve the above object, the invention of the stainless steel clad steel according to the first aspect of the present invention is to provide a salt damage resistant lining material on at least the front side of both front and back surfaces of a metal base material. Are joined.
【０００６】請求項２に記載の発明では、請求項１にお
いて、耐塩害性ライニング材はステンレス鋼のＳＵＳ３
２９Ｊ4Ｌである。前記別の目的を達成するために、請
求項３に記載のタンクの発明は、金属製の母材の表裏両
面のうち少なくとも表面側に耐塩害性ライニング材を接
合した耐塩害用ステンレスクラッド鋼により形成されて
いる。According to a second aspect of the present invention, in the first aspect, the salt damage resistant lining material is stainless steel SUS3.
29J 4 L. In order to achieve the other object, the invention of the tank according to claim 3 is based on a salt-resistant stainless clad steel in which a salt-resistant lining material is bonded to at least the surface side of both front and back surfaces of a metal base material. Is formed.
【０００７】請求項４に記載の発明では、請求項３にお
いて、耐塩害性ライニング材はステンレス鋼のＳＵＳ３
２９Ｊ4Ｌである。請求項５に記載の発明は、請求項４
において、耐塩害性ライニング材は母材の表裏両面に熱
間圧延により接合されている。According to a fourth aspect of the present invention, in the third aspect, the salt damage resistant lining material is stainless steel SUS3.
29J 4 L. The invention according to claim 5 is the invention according to claim 4.
In the above, the salt damage resistant lining material is joined to both front and back surfaces of the base material by hot rolling.
【０００８】[0008]
【発明の実施の形態】以下に、本発明を具体化した一実
施形態を図１〜図３を用いて説明する。図１に示すよう
に、ステンレス鋼よりなる平板状の母材１１の表裏両面
には塩分等の耐蝕性に優れたライニング材よりなる外層
１２と内層１３が接合層１４を介して接合され、図２に
示すような四角板状のステンレスクラッド鋼１５が形成
されている。DETAILED DESCRIPTION OF THE PREFERRED EMBODIMENTS One embodiment of the present invention will be described below with reference to FIGS. As shown in FIG. 1, an outer layer 12 and an inner layer 13 made of a lining material having excellent corrosion resistance such as salt are joined to both sides of a flat base material 11 made of stainless steel via a joining layer 14. A stainless steel clad steel 15 having a square plate shape as shown in FIG.
【０００９】この実施形態では、母材１１の材質として
ステンレス鋼ＳＵＳ３０４を用いている。外層１２及び
内層１３の材質として、同じく耐塩害性に優れたステン
レス鋼である二相合金系のＪＩＳ規格でＳＵＳ３２９Ｊ
4Ｌを使用している。In this embodiment, stainless steel SUS304 is used as the material of the base material 11. The material of the outer layer 12 and the inner layer 13 is SUS329J according to JIS standard of a two-phase alloy system which is also a stainless steel excellent in salt damage resistance.
4 L is used.
【００１０】母材１１に対する両層１２，１３の接合は
両面熱間圧延により行われる。なお、図２ではクラッド
鋼は肉厚寸法を四辺の長さ寸法に対して大きく描いてい
るが、母材１１の厚さを例えば２〜５ｍｍとすると、外
層１２と内層１３の厚さは０．１〜０．４ｍｍ程度、一
辺の長さは０．５〜８ｍである。The joining of the layers 12 and 13 to the base material 11 is performed by hot rolling on both sides. In FIG. 2, the thickness of the clad steel is drawn larger than the length of the four sides. However, when the thickness of the base material 11 is, for example, 2 to 5 mm, the thickness of the outer layer 12 and the inner layer 13 becomes 0. 0.1 to 0.4 mm, and the length of one side is 0.5 to 8 m.
【００１１】前述したステンレスクラッド鋼１５を用い
て例えば図３に示す四角箱状の貯水タンク１６が構成さ
れる。以上のように構成された貯水タンク１６の作用、
効果を構成とともに列記する。The above-described stainless steel clad steel 15 is used to form, for example, a rectangular box-shaped water storage tank 16 shown in FIG. The operation of the water storage tank 16 configured as described above,
The effects are listed together with the configuration.
【００１２】（１）母材１１の外表面がＳＵＳ３２９Ｊ
4Ｌよりなる外層１２で覆われているので、海水の塩分
による害が及ぶ塩害地域での耐蝕性が高く、貯水タンク
１６の寿命を長くすることができる。このため、樹脂の
塗装、及びその塗り替え等の保守・管理が不要でコスト
の低減を図ることができる。(1) The outer surface of the base material 11 is SUS329J
Since it is covered with the outer layer 12 made of 4 L, it has high corrosion resistance in a salt-damaged area where salt water damages, and the life of the water storage tank 16 can be extended. For this reason, maintenance and management, such as painting and repainting of the resin, are unnecessary, and the cost can be reduced.
【００１３】（２）貯水タンク１６の内表面もＳＵＳ３
２９Ｊ4Ｌよりなる内層１３で覆われているので、水道
水に含まれている塩素ガスに対する耐蝕性を向上するこ
とができ、タンクの耐久性を向上することができる。(2) The inner surface of the water storage tank 16 is also SUS3
Since it is covered with the inner layer 13 made of 29J 4 L, the corrosion resistance to chlorine gas contained in tap water can be improved, and the durability of the tank can be improved.
【００１４】（３）平板状をなす母材１１の表裏両面に
外層１２及び内層１３を熱間圧延により接合してステン
レスクラッド鋼１５が形成されているので、工場でクラ
ッド鋼１５を製造し、これを施工現場において互いに溶
接し貯水タンク１６を構築することができる。このた
め、現場でのライニング層の形成を不要にして貯水タン
ク１６の製造を容易に行うことができる。(3) The stainless steel clad steel 15 is formed by joining the outer layer 12 and the inner layer 13 by hot rolling to both the front and back surfaces of the base material 11 having a flat plate shape. These can be welded to each other at the construction site to construct the water storage tank 16. Therefore, it is not necessary to form a lining layer on site, and the water storage tank 16 can be easily manufactured.
【００１５】なお、前記実施形態は以下のように変更し
て具体化することができる。 ・図４及び図５に示す実施形態では、円筒状の貯水タン
ク２１に具体化している。この貯水タンク２１は前記ス
テンレスクラッド鋼１５を円筒状に湾曲し、その対向端
面を接触して溶接により連結している。The above embodiment can be modified and embodied as follows. -In the embodiment shown in Drawing 4 and Drawing 5, it is embodied in cylindrical water storage tank 21. The water storage tank 21 is formed by bending the stainless clad steel 15 into a cylindrical shape, and connecting the opposite end surfaces thereof by welding.
【００１６】この実施形態のタンク２１も前述した実施
形態のタンク１６と同様の作用・効果を奏する。 ・図６に示す実施形態では、長楕円筒状をなす大型の貯
水タンク３１に具体化している。The tank 21 of this embodiment has the same operation and effect as the tank 16 of the above-described embodiment. In the embodiment shown in FIG. 6, the present invention is embodied in a large water storage tank 31 having a long elliptical cylindrical shape.
【００１７】この実施形態のタンク３１も前述した実施
形態のタンク１６と同様の作用・効果を奏する。 ・前記実施形態において、内層１３を省略してもよい。
この場合には、一般の貯水タンクとして使用することが
できる。The tank 31 of this embodiment has the same operation and effect as the tank 16 of the above-described embodiment. In the above embodiment, the inner layer 13 may be omitted.
In this case, it can be used as a general water storage tank.
【００１８】・前記母材としてＳＳ４００，ＳＵＳ３１
６等の鉄あるいはステンレス鋼を用いてもよい。 ・前記二相合金系のＪＩＳ規格のＳＵＳ３２９Ｊ4Ｌに
代えて、耐塩害性ライニング材としてチタンクラッド鋼
を使用してもよい。· SS400, SUS31 as the base material
For example, iron such as No. 6 or stainless steel may be used. - the place of the SUS329J 4 L of a two-phase alloy system of JIS standards may be used titanium clad steel as salt damage resistance lining material.
【００１９】・前記実施形態では貯水タンクとして具体
化したが、これを各種の化学薬品を収容するタンクに具
体化してもよい。In the above embodiment, the present invention is embodied as a water storage tank, but this may be embodied as a tank containing various chemicals.
【００２０】[0020]
【発明の効果】本発明は、以上のように構成されている
ため、次のような効果を奏する。請求項１又は２に記載
のステンレスクラッド鋼の発明は、塩分に対する耐蝕性
を向上することができる。、請求項３〜５のいずれかに
記載のタンクの発明は、塩分に対する耐蝕性を向上する
ことができるとともに、保守・管理を容易に行うことが
できる。Since the present invention is configured as described above, it has the following effects. The invention of the stainless steel clad steel according to claim 1 or 2 can improve corrosion resistance to salt. The invention of the tank according to any one of claims 3 to 5 can improve corrosion resistance against salt and can easily perform maintenance and management.
【図１】 ステンレスクラッド鋼を示す部分断面図。FIG. 1 is a partial cross-sectional view showing a stainless clad steel.
【図２】 ステンレスクラッド鋼の斜視図。FIG. 2 is a perspective view of a stainless clad steel.
【図３】 貯水タンクの斜視図。FIG. 3 is a perspective view of a water storage tank.
【図４】 この発明の別の実施形態の貯水タンクの横断
面図。FIG. 4 is a cross-sectional view of a water storage tank according to another embodiment of the present invention.
【図５】 貯水タンクの斜視図。FIG. 5 is a perspective view of a water storage tank.
【図６】 この発明の別の実施形態の貯水タンクの正面
図。FIG. 6 is a front view of a water storage tank according to another embodiment of the present invention.
１１…母材、１２…耐塩害性ライニング材としての外
層、１３…耐塩害性ライニング材としての内層、１４…
接合層、１５…ステンレスクラッド鋼、１６，２１，３
１…貯水タンク。11: Base material, 12: Outer layer as salt-resistant lining material, 13: Inner layer as salt-resistant lining material, 14 ...
Bonding layer, 15 ... stainless clad steel, 16, 21, 3
1 ... water storage tank.
───────────────────────────────────────────────────── フロントページの続き Ｆターム(参考） 4E067 AA03 AB02 AD13 BD01 4F100 AB01A AB04B AB04C AR00B AR00C BA02 BA03 BA06 BA10B BA10C EJ372 EJ422 GB16 JB02B JB02C ────────────────────────────────────────────────── ─── Continued on the front page F term (reference) 4E067 AA03 AB02 AD13 BD01 4F100 AB01A AB04B AB04C AR00B AR00C BA02 BA03 BA06 BA10B BA10C EJ372 EJ422 GB16 JB02B JB02C
Claims (5)
も表面側に耐塩害性ライニング材を接合した耐塩害用ス
テンレスクラッド鋼。1. A stainless steel clad steel for salt damage, wherein a salt damage-resistant lining material is joined to at least the surface of both front and back surfaces of a metal base material.
材はステンレス鋼のＳＵＳ３２９Ｊ4Ｌである耐塩害用
ステンレスクラッド鋼。2. The stainless steel clad steel for salt damage resistance according to claim 1, wherein the salt damage resistant lining material is SUS329J 4 L of stainless steel.
も表面側に耐塩害性ライニング材を接合した耐塩害用ス
テンレスクラッド鋼により形成されたタンク。3. A tank made of a stainless steel clad steel for salt damage, wherein a salt damage-resistant lining material is joined to at least the front surface of both front and back surfaces of a metal base material.
材はステンレス鋼のＳＵＳ３２９Ｊ4Ｌであるタンク。4. The tank according to claim 3, wherein the salt-resistant lining material is stainless steel SUS329J 4 L.
材は母材の表裏両面に熱間圧延により接合されているタ
ンク。5. The tank according to claim 4, wherein the salt damage resistant lining material is joined to the front and back surfaces of the base material by hot rolling.