ITTV20090223A1 - PROCEDURE FOR OBTAINING A HEATING FABRIC. - Google Patents
PROCEDURE FOR OBTAINING A HEATING FABRIC. Download PDFInfo
- Publication number
- ITTV20090223A1 ITTV20090223A1 IT000223A ITTV20090223A ITTV20090223A1 IT TV20090223 A1 ITTV20090223 A1 IT TV20090223A1 IT 000223 A IT000223 A IT 000223A IT TV20090223 A ITTV20090223 A IT TV20090223A IT TV20090223 A1 ITTV20090223 A1 IT TV20090223A1
- Authority
- IT
- Italy
- Prior art keywords
- fabric
- layer
- slots
- carbon fiber
- wires
- Prior art date
Description
TITOLO: PROCEDIMENTO PER L'OTTENIMENTO DI UN TESSUTO RISCALDANTE TITLE: PROCEDURE FOR OBTAINING A HEATING FABRIC
DESCRIZIONE DESCRIPTION
La presente domanda ha per oggetto un procedimento per l'ottenimento di un tessuto riscaldante, particolarmente utilizzabile nel settore domestico, farmaceutico e ospedaliero, sotto forma di applicazioni quali scaldini da letto o da tavolo operatorio, scalda sedute e divani, tendaggi scaldanti da arredo, termocoperte . The present application relates to a process for obtaining a heating fabric, particularly usable in the domestic, pharmaceutical and hospital sectors, in the form of applications such as bed or operating table warmers, seat and sofa warmers, warming curtains for furniture, electric blankets.
Oggigiorno sono note termocoperte dotate di resistori interni che, per effetto joule, si riscaldano al passaggio di una corrente elettrica e raggiungono la temperatura impostata dall 'utente . Electric blankets are currently known which are equipped with internal resistors which, due to the joule effect, heat up when an electric current passes and reach the temperature set by the user.
Le tensioni usate per il funzionamento di questi resistor!, per motivi di sicurezza, sono basse, generalmente di 24 Volt. The voltages used for the operation of these resistors, for safety reasons, are low, generally 24 Volts.
La maggioranza di queste note termocoperte comprende resistor!metallici disposti all'interno del tessuto che male si prestano ad essere lavati e stirati. The majority of these known electric blankets comprise metal resistors disposed within the fabric which do not lend themselves to being washed and ironed.
Inoltre tali resistori metallici, presentano una limitata elasticità e risultano quindi particolarmente sensibili agli urti alle flessioni agli stessi imposti presentano problemi di usura Furthermore, these metal resistors have a limited elasticity and are therefore particularly sensitive to shocks and bending imposed on them, they present wear problems.
Il possibile malfunzionamento questi conduttori metallici può generare surriscaldamenti della termocoperta che possono provocare combustioni che talvolta possono degenerare in incendi, essendo il tessuto costituente la termocoperta in materiale infiammabile. The possible malfunction of these metal conductors can generate overheating of the electric blanket which can cause combustion which can sometimes degenerate into fires, since the fabric constituting the electric blanket is made of flammable material.
Un ulteriore inconveniente ascrivile alle soluzioni di tipo noto appena sopra descritte consiste nella ossidabilità dei metalli, specialmente in presenza di umidità , che à ̈ causa di malfunzionamento dei resistori. A further drawback ascribable to the solutions of the known type just described above consists in the oxidability of the metals, especially in the presence of humidity, which causes malfunctioning of the resistors.
Un ulteriore svantaggio delle soluzioni di tipo noto consiste anche nel complesso lavoro necessario per applicare i resistor! e le varie connessioni elettriche all'interno del tessuto costituente la termocoperta stessa. A further disadvantage of known solutions also consists in the complex work required to apply the resistors! and the various electrical connections inside the fabric constituting the electric blanket itself.
Compito principale di quanto forma oggetto del presente trovato à ̈ quindi quello di risolvere i problemi tecnici evidenziati, eliminando gli inconvenienti di cui alla tecnica nota citata e quindi escogitando un procedimento che permetta di ottenere un tessuto riscaldante che presenti ottimali caratteristiche di conducibilità elettrica ed elevate condizioni di sicurezza nel suo impiego. The main task of the subject matter of the present invention is therefore to solve the technical problems highlighted, eliminating the drawbacks of the aforementioned known art and therefore devising a procedure that allows to obtain a heating fabric which has excellent characteristics of electrical conductivity and high safety conditions in its use.
Nell'ambito del compito sopra esposto un altro scopo del trovato à ̈ quello di ottenere un tessuto riscaldante che non risenta di malfunzionamenti dovuti alla sua manipolazione da parte degli operatori . Within the scope of the above aim, another object of the invention is to obtain a heating fabric which is not affected by malfunctions due to its manipulation by the operators.
Ancora uno scopo à ̈ quello di realizzare un procedimento che permetta di accrescere la sicurezza in tema di emissione elettromagnetiche del relativo prodotto. Another object is to provide a process which allows to increase the safety in terms of electromagnetic emissions of the relative product.
Un ulteriore scopo del trovato à ̈ realizzare un procedimento che permetta di ottenere un prodotto che assicuri un riscaldamento uniforme ed abbia una lunga durata di funzionamento, potendosi inoltre sanitizzare. A further object of the invention is to provide a process which allows to obtain a product which ensures uniform heating and has a long operating life, and can also be sanitized.
Non ultimo scopo à ̈ quello di realizzare un procedimento che consenta di ottenere un trovato che sia strutturalmente semplice e che sia realizzabile con macchinari e impianti di tipo noti . Not least object is to provide a method which allows to obtain an invention which is structurally simple and which can be produced with known machines and plants.
Il compito e gli scopi accennati, nonché altri che più chiaramente appariranno in seguito, vengono raggiunti da un procedimento per l'ottenimento di un tessuto riscaldante che si caratterizza per il fatto di comprendere le seguenti fasi: The aforementioned task and purposes, as well as others that will appear more clearly later, are achieved by a process for obtaining a heating fabric which is characterized by the fact that it comprises the following phases:
a)apposizione secondo un'asse trasversale ed in fase di tessitura di detto tessuto, di più distinti filamenti o fili o resistori in fibra di carbonio presentanti, in prossimità delle loro estremità terminali, almeno due asole sporgenti; a) affixing according to a transverse axis and during the weaving phase of said fabric, of several distinct filaments or threads or carbon fiber resistors having, near their terminal ends, at least two protruding slots;
b)apposizione su detto tessuto, in corrispondenza di dette almeno due asole, di almeno uno strato di colla del tipo riattivante ad una temperatura prefissata; b) affixing on said fabric, in correspondence of said at least two slots, of at least one layer of glue of the reactivating type at a predetermined temperature;
c)piegatura su detto tessuto, secondo la medesima direzione, di dette almeno due asole di ciascuno di detti più distinti fili così da disporle in sequenza; c) folding on said fabric, in the same direction, of said at least two slots of each of said more distinct threads so as to arrange them in sequence;
d)apposizione di un primo strato di fili di carbonio nichelato su dette almeno due asole piegate; d) affixing a first layer of nickel-plated carbon wires on said at least two folded slots;
e)apposizione, su detto primo strato, di un secondo strato di fili in rame stagnato alle estremità connesso a predisposti conduttori applicati ad una presa di alimentazione; e) affixing, on said first layer, a second layer of tinned copper wires at the ends connected to predisposed conductors applied to a power socket;
f)piegatura dei bordi longitudinali di detto tessuto per una profondità circa pari alla larghezza di detti primo e secondo strato; f) folding of the longitudinal edges of said fabric for a depth approximately equal to the width of said first and second layer;
g)pressatura a caldo di detti bordi longitudinali piegati; g) hot pressing of said folded longitudinal edges;
h)cucitura di detto bordo piegato per il bloccaggio meccanico in pressione di detti primo e secondo strato a dette almeno due asole; h) sewing of said folded edge for mechanical locking under pressure of said first and second layer to said at least two slots;
ripiegatura e cucitura del bordo trasversale di detto tessuto. folding and sewing of the transversal edge of said fabric.
Si consegue un tessuto riscaldante che si caratterizza per il fatto di comprendere al suo interno una pluralità di distinti fili in carbonio disposti trasversalmente a detto tessuto e parallelamente tra loro e presentanti, in prossimità delle estremità , delle asole per la interconnessione elettrica ad un primo strato di fili di carbonio nichelato e ad un secondo strato di fili in rame stagnato raggruppati alle estremità a conduttori applicati ad una spina Ulteriori caratteristiche e vantaggi del trovato risulteranno maggiormente dalla descrizione dettagliata di una particolare forma di realizzazione, illustrata a titolo indicativo e non limitativo nelle tavole di disegni allegate, in cui: The result is a heating fabric which is characterized by the fact that it comprises a plurality of distinct carbon wires arranged transversely to said fabric and parallel to each other and having, near the ends, slots for electrical interconnection to a first layer of nickel-plated carbon wires and a second layer of tinned copper wires grouped at the ends with conductors applied to a plug Further characteristics and advantages of the invention will become clearer from the detailed description of a particular embodiment, illustrated by way of non-limiting tables of drawings attached, in which:
la fig. 1 illustra, in una vista di tre quarti laterale, un prodotto ottenibile con il procedimento; fig. 1 illustrates, in a three-quarter side view, a product obtainable with the process;
la fig. 2 illustra, in una vista schematica di tre quarti laterale e parzialmente sezionata, il tessuto in una fase in cui vi sono asole in fibra di carbonio che sporgono verticalmente vicino ad un bordo del tessuto; fig. 2 illustrates, in a schematic three-quarter lateral and partially sectioned view, the fabric in a step in which there are carbon fiber slots which project vertically close to an edge of the fabric;
la fig. 3 illustra, in una vista di tre quarti laterale, una ulteriore fase in cui à ̈ apposto del collante in prossimità del bordo del tessuto senza interessare le asole; fig. 3 shows, in a lateral three-quarter view, a further phase in which the glue is applied in proximity to the edge of the fabric without affecting the buttonholes;
la fig. 4 illustra, in una vista di tre quarti laterale, la fase di piegatura delle asole in fibra di carbonio; fig. 4 shows, in a three-quarter side view, the step of folding the carbon fiber slots;
la fig.5 illustra, in una vista di tre quarti laterale, la fase in cui si ha la posa di fibre di carbonio nichelato al di sopra delle asole in fibra di carbonio; Fig. 5 illustrates, in a three-quarter side view, the phase in which the nickel-plated carbon fibers are laid over the carbon fiber slots;
la fig. 6 illustra, in una vista di tre quarti laterale schematica, la fase in cui si ha la posa di fili di rame stagnato al di sopra delle fibre di carbonio nichelato; fig. 6 illustrates, in a schematic side three-quarter view, the phase in which the tinned copper wires are laid over the nickel-plated carbon fibers;
la fig. 7 illustra, in una vista di tre quarti laterale, la fase in cui si ha la unione delle estremità dei fili di rame stagnato e la loro giunzione a dei conduttori; fig. 7 illustrates, in a three-quarter side view, the phase in which the ends of the tinned copper wires are joined and their junction to conductors;
la fig. 8 illustra, in una vista, la fase in cui si ha la piegatura dei bordi del tessuto e la connessione dei conduttori ad una spina. fig. 8 illustrates, in a view, the phase in which the edges of the fabric are folded and the conductors connected to a plug.
Con riferimento alle citate figure si à ̈ indicato con il numero (1) un prodotto finito costituito da un tessuto riscaldante, particolarmente utilizzabile nel settore domestico, farmaceutico e ospedaliero, sotto forma di applicazioni quali scaldini da letto o da tavolo operatorio, scalda sedute e divani, tendaggi scaldanti da arredo, termocoperte. With reference to the aforementioned figures, the number (1) indicates a finished product consisting of a heating fabric, particularly usable in the domestic, pharmaceutical and hospital sectors, in the form of applications such as bed or operating table warmers, seat warmers and sofas, heating curtains for furniture, electric blankets.
Tale tessuto riscaldante (1) Ã ̈ ottenuto mediante un procedimento che prevede, durante la fase di tessitura di un generico tessuto (2), l'inserimento nella trama, secondo un asse trasversale al tessuto (2), dei filamenti o fili o resistor! in fibra di carbonio (3). This heating fabric (1) is obtained by means of a procedure which foresees, during the weaving phase of a generic fabric (2), the insertion in the weft, according to an axis transversal to the fabric (2), of filaments or threads or resistor ! carbon fiber (3).
Tale fibra di carbonio, avvolta originariamente in bobine per il normale uso in tessitura, viene inserita, in fase di tessitura, in posizione di trama o di ordito a distanze sia regolari che irregolari, predefinite in funzione del tipo di riscaldatore che si intende ottenere. This carbon fiber, originally wound in reels for normal use in weaving, is inserted, during the weaving phase, in the weft or warp position at both regular and irregular distances, predefined according to the type of heater to be obtained.
Vantaggiosamente tali fili in fibra di carbonio (3) vengono disposti parallelamente tra loro. Advantageously, these carbon fiber threads (3) are arranged parallel to each other.
L'inserimento della fibra carbonio nel tessuto à ̈ consentito ad esempio da un tunnel (4), creato in dimensioni idonee alla sezione della fibra, con una intensità di filo tessile tale da permettere una totale protezione alla fibra stessa in esso contenuta ottenendo un completo isolamento ed una elevata protezione agli eventi meccanici. The insertion of the carbon fiber into the fabric is allowed for example by a tunnel (4), created in dimensions suitable for the section of the fiber, with an intensity of the textile thread that allows total protection to the fiber itself, thus obtaining a complete insulation and high protection against mechanical events.
Per alimentare i resistori in fibra carbonio (3) inseriti in detto tessuto (2) à ̈ necessario creare, in prossimità di ciascuna delle loro estremità terminali (5) attigue il bordo longitudinale (6) del tessuto (2), almeno una asola (7) conformata a ponte o ad arco e che si sviluppa al disopra della superficie superiore (8) del tessuto (2). To power the carbon fiber resistors (3) inserted in said fabric (2), it is necessary to create at least one slot ( 7) shaped like a bridge or arch and which develops above the upper surface (8) of the fabric (2).
E' preferibile avere a disposizione, per ogni asola (7), una lunghezza utile H di almeno 3 cm di fibra ad interessare uno spazio Li di tessuto (2) piano sottostante di almeno 2 cm. It is preferable to have available, for each slot (7), a useful length H of at least 3 cm of fiber to involve a space Li of fabric (2) underneath of at least 2 cm.
Le asole (7) sono tutte posizionate nello stesso senso della direzione del resistore in fibra di carbonio (3). The slots (7) are all positioned in the same direction as the direction of the carbon fiber resistor (3).
Si ottiene così un corridoio di larghezza pari circa a Li e quindi a 2 era e di lunghezza illimitata che viene utilizzato, come in seguito descritto, per la connessione dei resistori in fibra di carbonio (3) stessi. In this way a corridor is obtained having a width of approximately Li and therefore 2 era and of unlimited length which is used, as described below, for the connection of the carbon fiber resistors (3) themselves.
Tra ogni bordo (6) del tessuto (2)ed il corridoio definito dalla asole (7) à ̈ presente una porzione L2 di tessuto (2) che può presentare ancora una struttura a definire detto tunnel (4) ed una larghezza di circa 3 cm compresa la cimossa . Between each edge (6) of the fabric (2) and the corridor defined by the slots (7) there is a portion L2 of fabric (2) which can still have a structure defining said tunnel (4) and a width of about 3 cm including the selvedge.
Con la determinazione della lunghezza di tessuto (2) necessario per costruire una determinata superficie in tessuto riscaldante (1) , si procede alla connessione dei resistori in fibra di carbonio (3) applicando sulla porzione di detto tessuto (2) sottostante dette asole (7) e per una voluta zona ad esse attigua, uno strato di colla o collante (9) liquido che si impregna nella porzione di tessuto (2) senza andare a contatto delle asole (7) in fibra di carbonio. With the determination of the length of fabric (2) necessary to construct a certain surface in heating fabric (1), the carbon fiber resistors (3) are connected by applying said slots (7) to the underlying portion of said fabric (2). ) and for a desired area adjacent to them, a layer of liquid glue or glue (9) which soaks into the fabric portion (2) without coming into contact with the carbon fiber slots (7).
Detto collante (9) liquido à ̈ di tipo riattivante a temperatura prefissata, preferibilmente di 80°C. Said liquid glue (9) is of the reactivating type at a predetermined temperature, preferably of 80 ° C.
Completata la distribuzione di detto collante (9), il procedimento prevede la piegatura, preferibilmente orientate nella medesima direzione, di tutte dette asole (7) che vengono così appoggiate in corrispondenza del corridoio di larghezza pari a LI. Once the distribution of said glue (9) has been completed, the process provides for the folding, preferably oriented in the same direction, of all said slots (7) which are thus placed in correspondence with the corridor having a width equal to L1.
Il procedimento prevede quindi che sopra alle asole (7) piegate, ed eventualmente anche per parte di una zona attigua alle stesse, venga steso, in uno o più passaggi, un primo strato di fili di carbonio nichelato (10) avendo cura di allargarlo almeno fino alla completa copertura delle porzioni di tessuto (2) su cui sono appoggiate le asole (7). The procedure therefore provides that over the bent slots (7), and possibly also for part of an area adjacent to them, a first layer of nickel-plated carbon wires (10) is spread in one or more passages, taking care to widen it at least until the fabric portions (2) on which the buttonholes (7) rest are completely covered.
Sopra a detto primo strato di fili di carbonio nichelato (10) à ̈ steso, in uno o più passaggi, un secondo strato di fili in rame stagnato (11) di sezione preferibilmente di 0,20 cm in quantità determinata dalla potenza stabilita per il tessuto riscaldante (1). On top of said first layer of nickel-plated carbon wires (10) a second layer of tinned copper wires (11) preferably with a section of 0.20 cm in a quantity determined by the power established for the heating fabric (1).
La tipologia e la metodologia di distribuzione del secondo strato di fili in rame stagnato (11) sopra il primo strato di fili di carbonio nichelato (10) potranno essere le più opportune in funzione di specifiche esigenze. The type and method of distribution of the second layer of tinned copper wires (11) over the first layer of nickel-plated carbon wires (10) may be the most appropriate according to specific needs.
Si ottiene così una stratificazione data dalla somma dei resistori in fibra di carbonio (3) conformati ad asola (7), dal primo strato di fili di carbonio nichelato (10) e dal secondo strato di fili in rame stagnato (11) che vengono così a formare una connessione che in questo stadio à ̈ ancora allo stato libero e quindi non ancora in grado di garantire il passaggio delle cariche elettriche . A stratification is thus obtained given by the sum of the carbon fiber resistors (3) shaped like a slot (7), by the first layer of nickel-plated carbon wires (10) and by the second layer of tinned copper wires (11) which are thus to form a connection which in this stage is still in the free state and therefore not yet able to guarantee the passage of electrical charges.
Il primo strato di fili di carbonio nichelato (10) ed il secondo strato di fili in rame stagnato (11) vengono alle estremità connessi a predisposti conduttori o cavi (12) a loro volta terminanti in una predisposta presa (13) di alimentazione. The first layer of nickel-plated carbon wires (10) and the second layer of tinned copper wires (11) are connected at the ends to suitable conductors or cables (12) which in turn terminate in a suitable power supply socket (13).
Per dare a detta connessione la conducibilità necessaria delle cariche elettriche e la resistenza meccanica indispensabile per la durata nel tempo, si procede quindi alla piegatura dei bordi longitudinali (6) del tessuto (2) per una voluta profondità o larghezza, ad esempio pari alla larghezza di detti primo e secondo strato o solo pari a 3 cm. To give said connection the necessary conductivity of the electrical charges and the mechanical resistance essential for durability, the longitudinal edges (6) of the fabric (2) are then folded for a desired depth or width, for example equal to the width of said first and second layer or only equal to 3 cm.
Si potrà quindi effettuare una ulteriore analoga piegatura piegando il tessuto (2) già piegato ancora all'interno per una porzione ad esempio di 0,5 cm. It is therefore possible to carry out a further similar folding by folding the fabric (2) already folded still inside for a portion of, for example, 0.5 cm.
La parte di tessuto (2) risvoltato, che à ̈ impregnato di detto collante (9) liquido, viene quindi pressato con apposita pressa alla temperatura di reazione del collante (9) stesso, ad esempio di 80°C per riattivare i componenti per dare così una consistenza alla connessione. The part of fabric (2) turned up, which is impregnated with said liquid glue (9), is then pressed with a special press at the reaction temperature of the glue (9) itself, for example 80 ° C to reactivate the components to give thus a consistency to the connection.
Completata l'operazione di pressatura della connessione si eseguono nella lunghezza di detta connessione una serie di prime cuciture (14) a distanza tra loro ed in quantità variabile in funzione della potenza elettrica in gioco; dette prime cuciture (14) sono ad esempio eseguite con cucirino ad alta tenuta, e consentono di bloccare la pressione meccanica ottenuta con il passaggio a caldo sulla connessione in modo da garantire nel tempo la tenuta meccanica ed il passaggio delle cariche elettriche. Once the connection pressing operation has been completed, a series of first seams (14) are carried out along the length of said connection at a distance from each other and in a variable quantity according to the electrical power involved; said first seams (14) are for example carried out with a high-strength sewing thread, and allow to block the mechanical pressure obtained with the hot passage on the connection so as to guarantee the mechanical seal and the passage of electrical charges over time.
Il bordo trasversale (15) del tessuto (2) viene quindi a sua volta risvoltato e sullo stesso si eseguono una serie di seconde cuciture (16) a distanza tra loro ed in quantità variabile in funzione della potenza elettrica in gioco L'alimentazione del tessuto riscaldante (1) così ottenuto avviene collegando i due poli della fonte di energia ai conduttori (12) o alle prese (13) . The transverse edge (15) of the fabric (2) is then turned upside down and a series of second seams (16) are made on it at a distance from each other and in a variable quantity according to the electrical power involved. heating (1) obtained in this way takes place by connecting the two poles of the energy source to the conductors (12) or to the sockets (13).
Detto tessuto riscaldante (1) può essere alimentato con intensità variabili dai 3 Volts ai 55 Volts, con possibilità di usare varie tipologie di strumentazioni per la gestione delle temperature . Said heating fabric (1) can be fed with intensities ranging from 3 Volts to 55 Volts, with the possibility of using various types of instruments for managing temperatures.
Si à ̈ così constatato come il trovato abbia raggiunto il compito e gli scopi prefissati essendosi escogitato un procedimento che permette di ottenere un tessuto riscaldante che presenta ottimali caratteristiche di conducibilità elettrica ed elevate condizioni di sicurezza nel suo impiego, tale tessuto non risentendo di malfunzionamenti dovuti alla sua manipolazione da parte degli operatori e presentando una assenza di emissione elettromagnetiche. It was thus found that the invention has achieved the intended aim and objects, having devised a method which allows to obtain a heating fabric which has excellent electrical conductivity characteristics and high safety conditions in its use, this fabric is not affected by malfunctions. due to its manipulation by operators and presenting an absence of electromagnetic emissions.
Il procedimento permette inoltre di ottenere un prodotto che assicura un riscaldamento uniforme ed una lunga durata di funzionamento, potendosi inoltre lavare mantenendo integre le sue caratteristiche di conducibilità elettrica. The process also makes it possible to obtain a product that ensures uniform heating and a long operating life, as it can also be washed while maintaining its electrical conductivity characteristics intact.
La tecnologia applicata nella costruzione di detto tessuto riscaldante (1) e la tipologia di tessuto (2) che lo compone, consentono di poter lavare lo stesso anche in lavatrice applicando le dovute precauzioni per i conduttori o cavi (12) esterni di alimentazione. The technology applied in the construction of said heating fabric (1) and the type of fabric (2) that composes it, allow it to be washed even in the washing machine by applying the necessary precautions for the external power supply conductors or cables (12).
Il tessuto riscaldante (1) così ottenuto inoltre molto più sicuro nel funzionamento e molto più semplice nelle applicazioni rispetto alle soluzioni note e, data la particolare composizione dei filamenti o fili o resistori in fibra di carbonio (3) applicato nella tessitura, si ottiene un tessuto riscaldante (1) antibatterico e antifiamma che à ̈ supportato anche dall'assenza di emissione elettromagnetiche. The heating fabric (1) thus obtained is also much safer in operation and much simpler in applications than known solutions and, given the particular composition of the filaments or threads or carbon fiber resistors (3) applied in the weaving, it is obtained an antibacterial and flame-retardant heating fabric (1) which is also supported by the absence of electromagnetic emissions.
Naturalmente i materiali impiegati nonché le dimensioni costituenti i singoli componenti del trovato potranno essere più pertinenti a seconda delle specifiche esigenze. The materials used as well as the dimensions that constitute the individual components of the invention may of course be more pertinent according to specific requirements.
I diversi mezzi per effettuare certe differenti funzioni non dovranno certamente coesistere solo nella forma di realizzazione illustrata ma potranno essere di per se presenti in molte forme di realizzazione, anche se non illustrate. The different means for carrying out certain different functions will certainly not have to coexist only in the illustrated embodiment but may be present per se in many embodiments, even if not illustrated.
Le caratteristiche indicate come vantaggiose, opportune o simili possono anche mancare o essere sostituite da equivalenti. The characteristics indicated as advantageous, suitable or similar may also be missing or be replaced by equivalents.
Claims (15)