ITTO20010647A1 - USE OF A MULTI-LAYER FILM MATERIAL TO REALIZE ENVELOPES. - Google Patents

USE OF A MULTI-LAYER FILM MATERIAL TO REALIZE ENVELOPES. Download PDF

Info

Publication number
ITTO20010647A1
ITTO20010647A1 IT2001TO000647A ITTO20010647A ITTO20010647A1 IT TO20010647 A1 ITTO20010647 A1 IT TO20010647A1 IT 2001TO000647 A IT2001TO000647 A IT 2001TO000647A IT TO20010647 A ITTO20010647 A IT TO20010647A IT TO20010647 A1 ITTO20010647 A1 IT TO20010647A1
Authority
IT
Italy
Prior art keywords
layers
layer
film material
material according
polyethylene
Prior art date
Application number
IT2001TO000647A
Other languages
Italian (it)
Inventor
Martinetto Lorenzo Pezzetti
Original Assignee
Nova Plast S R L
Priority date (The priority date is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the date listed.)
Filing date
Publication date
Application filed by Nova Plast S R L filed Critical Nova Plast S R L
Priority to IT2001TO000647A priority Critical patent/ITTO20010647A1/en
Priority to PCT/IT2002/000431 priority patent/WO2003004268A1/en
Publication of ITTO20010647A1 publication Critical patent/ITTO20010647A1/en

Description

DESCRIZIONE dell'invenzione industriale dal titolo: "Impiego di un materiale pellicolare multistrato per realizzare involucri" DESCRIPTION of the industrial invention entitled: "Use of a multilayer film material to make casings"

DESCRIZIONE DESCRIPTION

La presente invenzione si riferisce ad un impiego di un materiale pellicolare multistrato per realizzare involucri, in particolare di prodotti alimentari . The present invention relates to the use of a multilayer film material for making wraps, in particular for food products.

Come noto, alcuni prodotti alimentari, quali ad esempio caramelle, vengono confezionati in un involucro costituito da una pellicola di materiale plastico, solitamente trasparente o semitrasparente, che viene chiuso impartendo una torsione a tale pellicola . As is known, some food products, such as sweets, for example, are packaged in a wrapper consisting of a film of plastic material, usually transparent or semi-transparent, which is closed by imparting a twist to said film.

È scopo dell'invenzione realizzare confezioni per prodotti, in particolare prodotti alimentari, mediante l'impiego di un involucro pellicolare in grado di tenere bene la torsione che gli viene impartita per chiudere la confezione. It is an object of the invention to produce packages for products, in particular food products, by means of the use of a film wrapper capable of holding well the twisting imparted to it to close the package.

Un altro scopo dell'invenzione è di realizzare un involucro pellicolare multistrato in grado di essere stampato o metallizzato su almeno una delle sue superfici esterne senza compromettere le caratteristiche meccaniche sopra citate. Another object of the invention is to provide a multilayer film envelope capable of being printed or metallized on at least one of its external surfaces without compromising the mechanical characteristics mentioned above.

Questi scopi sono raggiunti in accordo con la presente invenzione, mediante l'impiego di un materiale pellicolare multistrato come rivendicato nella rivendicazione 1. Caratteristiche preferenziali dell'invenzione sono definite nelle rivendicazioni dipendenti. These objects are achieved in accordance with the present invention, by using a multilayer film material as claimed in claim 1. Preferred characteristics of the invention are defined in the dependent claims.

Le caratteristiche e i vantaggi dell'invenzione risulteranno dalla descrizione dettagliata di alcuni suoi esempi di realizzazione, fatta con riferimento ai disegni allegati, dati a titolo indicativo e non limitativo, che sono viste schematiche in sezione di quattro forme di realizzazione alternative di un materiale pellicolare multistrato secondo l'invenzione destinato ad essere impiegato come involucro per confezionare prodotti di vario genere. The characteristics and advantages of the invention will emerge from the detailed description of some of its embodiment examples, made with reference to the attached drawings, given by way of non-limiting example, which are schematic sectional views of four alternative embodiments of a multilayer film material according to the invention intended to be used as a wrapper for packaging products of various kinds.

Facendo inizialmente riferimento alla figura 1, con il numero 10 è indicato un materiale pellicolare multistrato in cui si distinguono cinque strati: uno strato centrale o di nucleo interno 11, due strati intermedi opposti 12 e 13, e due strati esterni 14, 15. Referring initially to Figure 1, the number 10 indicates a multilayer film material in which five layers are distinguished: a central or inner core layer 11, two opposite intermediate layers 12 and 13, and two outer layers 14, 15.

Lo strato interno 11 è essenzialmente a base di polietilene o polipropilene, mentre i due strati intermedi 12, 13 sono essenzialmente a base di polistirene e gli strati di rivestimento esterni 14, 15 sono essenzialmente a base di polietilene. The internal layer 11 is essentially based on polyethylene or polypropylene, while the two intermediate layers 12, 13 are essentially based on polystyrene and the external covering layers 14, 15 are essentially based on polyethylene.

Lo strato interno 11 e gli strati esterni 14, 15 a base di polietilene, possono essere realizzati come una composizione comprendente polietilene a bassa densità con polietilene ad alta densità, e preferibilmente comprendono polietilene metallocene, ad esempio il polietilene metallocene disponibile con i nomi commerciali Exxon ML 1018 o 18Pfax Basel. Per quanto riguarda lo strato interno 11, il polietilene metallocene è presente ad una concentrazione di circa il 90% in peso rispetto al peso complessivo dello strato interno. Negli strati esterni 14, 15, il polietilene metallocene è presente ad una concentrazione di circa il 90% in peso. The inner layer 11 and the outer layers 14, 15 based on polyethylene, can be made as a composition comprising low density polyethylene with high density polyethylene, and preferably comprise metallocene polyethylene, for example the metallocene polyethylene available under the trade names Exxon ML 1018 or 18Pfax Basel. As regards the inner layer 11, the metallocene polyethylene is present at a concentration of about 90% by weight with respect to the total weight of the inner layer. In the outer layers 14, 15, the metallocene polyethylene is present at a concentration of about 90% by weight.

Gli strati intermedi 12, 13 sono invece di preferenza realizzati come una composizione comprendente polistirene base miscelato con polistirene modificato quale ad esempio il copolimero di stirene-butadiene commercializzato dalla Phillips Chemical Company con il nome commerciale K-Resin®. The intermediate layers 12, 13 are instead preferably made as a composition comprising basic polystyrene mixed with modified polystyrene such as the styrene-butadiene copolymer marketed by Phillips Chemical Company under the trade name K-Resin®.

Nella forma di realizzazione alternativa rappresentata schematicamente nella figura 2, ciascuno strato intermedio comprende a sua volta due strati: In the alternative embodiment schematically represented in Figure 2, each intermediate layer in turn comprises two layers:

uno strato più interno 12a, 13a a base di polistirene, a contatto con lo strato centrale 11, e uno strato più esterno 12b, 13b a base di polistirene modificato quale ad esempio il copolimero di stirene-butadiene disponibile in commercio sotto il nome commerciale K-Resin®. an innermost layer 12a, 13a based on polystyrene, in contact with the central layer 11, and an outermost layer 12b, 13b based on modified polystyrene such as for example the styrene-butadiene copolymer commercially available under the trade name K -Resin®.

Le funzioni svolte dai vari strati sono le seguenti. The functions performed by the various layers are as follows.

Lo strato di nucleo centrale 11, oltre a svolgere una funzione di legante per i due strati intermedi 12, 13, sfrutta le proprietà elastiche del polietilene o del polipropilene per conferire alla pellicola multistrato nel suo insieme buone proprietà di flessibilità nonché di resistenza alle deformazioni locali, in particolare quelle prodotte per torsione, senza permettere la formazione di fessure o discontinuità che potrebbero consentire l'ingresso, all'interno di una confezione, di agenti contaminanti esterni quali acqua, polvere, sporcizia, ecc. The central core layer 11, in addition to performing a binder function for the two intermediate layers 12, 13, exploits the elastic properties of polyethylene or polypropylene to give the multilayer film as a whole good properties of flexibility as well as resistance to local deformations , in particular those produced by twisting, without allowing the formation of cracks or discontinuities that could allow the entry, inside a package, of external contaminants such as water, dust, dirt, etc.

Gli strati intermedi 12, 13, intimamente legati tramite lo strato centrale 11, sono invece più inclini, rispetto a questo, di subire deformazioni plastiche permanenti, in particolare quando al materiale multistrato viene impartita una torsione. The intermediate layers 12, 13, intimately bonded by means of the central layer 11, are instead more prone, with respect to the latter, to undergo permanent plastic deformations, in particular when a torsion is imparted to the multilayer material.

Gli strati esterni di rivestimento 14, 15 sono quelli che ricevono gli inchiostri di stampaggio, che vengono applicati sul materiale pellicolare multistrato per riportare immagini e/o scritte in funzione della sua destinazione finale. The external coating layers 14, 15 are those that receive the printing inks, which are applied on the multilayer film material to carry images and / or writings according to its final destination.

Le esperienze condotte dal Richiedente dimostrano che per effetto delle diverse caratteristiche elastiche e plastiche dei vari strati, la tendenza dello strato interno (più elastico) di riprendere la sua forma originale in contrasto alla torsione che viene impartita alla pellicola multistrato, è contrastata efficacemente dagli strati intermedi 12 e 13, i quali reagiscono al movimento di ritorno elastico dello strato centrale agendo con un braccio di coppia resistente "b" elevato e approssimativamente individuabile come la distanza che unisce i baricentri G12 e G13 dei due strati intermedi, misurata in direzione perpendicolare al piano di sviluppo della pellicola. The experiments carried out by the Applicant show that due to the different elastic and plastic characteristics of the various layers, the tendency of the inner (more elastic) layer to resume its original shape in contrast to the torsion that is imparted to the multilayer film, is effectively counteracted by the layers. intermediate layers 12 and 13, which react to the elastic return movement of the central layer by acting with a high resistant torque arm "b" and approximately identifiable as the distance that joins the centers of gravity G12 and G13 of the two intermediate layers, measured perpendicular to the film development plan.

Le esperienze condotte dal Richiedente hanno dimostrato che un materiale multistrato di questo tipo permette di conseguire risultati eccellenti per il confezionamento di prodotti alimentari, quali ad esempio prodotti dolciari, dove l'involucro viene avvolto attorno al prodotto, ad esempio una caramella, e quindi chiuso impartendo all'involucro una torsione. The experiences carried out by the Applicant have shown that a multilayer material of this type allows excellent results to be achieved for the packaging of food products, such as confectionery products, where the wrapping is wrapped around the product, for example a candy, and then closed. giving the casing a twist.

In assenza degli strati esterni 14, 15, se lo stampaggio fosse effettuato direttamente sugli strati 12, 13 a base di polistirene, questi ultimi verrebbero intaccati dalle sostanze con proprietà solventi (alcool, acetati) presenti nella maggior parte degli inchiostri, e pertanto il materiale pellicolare tenderebbe ad attorcigliarsi o accartocciarsi (subendo il fenomeno noto con il termine anglosassone "curling"), con conseguente perdita di caratteristiche tecniche ed estetiche del prodotto. In the absence of the external layers 14, 15, if the molding were carried out directly on the polystyrene-based layers 12, 13, the latter would be affected by the substances with solvent properties (alcohol, acetates) present in most of the inks, and therefore the material film would tend to twist or crumple (undergoing the phenomenon known with the Anglo-Saxon term "curling"), with consequent loss of technical and aesthetic characteristics of the product.

Il materiale pellicolare multistrato della presente invenzione può quindi essere stampato vantaggiosamente anche con qualsiasi inchiostro normalmente utilizzato per lo stampaggio su polipropilene, e non richiede necessariamente l'utilizzazione di inchiostri all'acqua (che non intaccano il polistirene) . The multilayer film material of the present invention can therefore be advantageously printed also with any ink normally used for printing on polypropylene, and does not necessarily require the use of water-based inks (which do not damage the polystyrene).

Secondo una ulteriore forma di attuazione della presente invenzione, come illustrato schematicamente nella figura 3, è previsto un solo strato di rivestimento esterno 14 atto ad essere stampato ed avente le caratteristiche sopra citate con riferimento agli esempi di realizzazione già descritti. According to a further embodiment of the present invention, as schematically illustrated in Figure 3, a single outer coating layer 14 is provided which is suitable for being molded and having the characteristics mentioned above with reference to the embodiments already described.

Secondo un'altra forma di attuazione della presente invenzione, come illustrato in figura 4, il singolo strato 14 o i due strati 14, 15 di rivestimento esterno/i possono essere realizzati in PET (tereftalato di polietilene) o PETG (poliestere amorfo di acido tereftalico), unito/i allo strato intermedio 12, 13 mediante un adesivo 16. According to another embodiment of the present invention, as illustrated in Figure 4, the single layer 14 or the two layers 14, 15 of the outer coating (s) can be made of PET (polyethylene terephthalate) or PETG (amorphous polyester of terephthalic acid). ), joined to the intermediate layer 12, 13 by means of an adhesive 16.

Naturalmente, il riferimento all'utilizzazione del materiale multistrato per il confezionamento di prodotti dolciari non deve essere in alcun modo interpretato come limitativo della portata del brevetto. L'invenzione potrà, in particolare, essere utilizzata per il confezionamento di prodotti alimentari in generale e/o di prodotti di altro genere che si desidera confezionare mediante un involucro pellicolare che si chiude per mantenimento della torsione che viene ad esso impartita. Naturally, the reference to the use of multilayer material for the packaging of confectionery products must in no way be interpreted as limiting the scope of the patent. The invention can, in particular, be used for the packaging of food products in general and / or of other kinds of products that it is desired to pack by means of a film wrapper which closes by maintaining the torsion imparted to it.

Ovviamente la caratteristica meccanica della pellicola multistrato è funzione del suo spessore; tuttavia, anche utilizzando pellicole aventi uno spessore complessivo di circa 20 micron si sono ottenute caratteristiche di tenacia eccellenti. Obviously the mechanical characteristic of the multilayer film is a function of its thickness; however, even using films having an overall thickness of about 20 microns excellent tenacity characteristics were obtained.

Idealmente, per gli scopi e le applicazioni sopra menzionate, lo spessore complessivo della pellicola dovrebbe essere generalmente compreso tra circa 20 e circa 50 micron. In una forma di attuazione particolarmente preferita, le percentuali di spessore dei vari strati costituenti la pellicola sono ripartite uniformemente. Tuttavia, al fine di ottenere un prodotto che complessivamente non sia troppo fragile né troppo elastico, è preferibile che gli strati intermedi, essenzialmente a base di polistirene, abbiano ciascuno uno spessore compreso tra circa il 20% e circa il 40% dello spessore totale della pellicola, mentre lo strato centrale, a base di polietilene, dovrebbe avere uno spessore compreso tra il 20% ed il 60% dello spessore totale. Ideally, for the purposes and applications mentioned above, the overall film thickness should generally be between about 20 and about 50 microns. In a particularly preferred embodiment, the percentages of thickness of the various layers constituting the film are uniformly distributed. However, in order to obtain a product that overall is neither too fragile nor too elastic, it is preferable that the intermediate layers, essentially based on polystyrene, each have a thickness between about 20% and about 40% of the total thickness of the film, while the central layer, based on polyethylene, should have a thickness between 20% and 60% of the total thickness.

Claims (11)

RIVENDICAZIONI 1. Impiego di un materiale pellicolare multistrato per realizzare involucri, in particolare di prodotti alimentari, atti ad essere chiusi impartendo al materiale pellicolare una torsione, in cui il materiale multistrato ha: uno strato centrale (11) di un primo materiale plastico a base di polietilene o polipropilene; due strati opposti (12, 13) di un secondo materiale plastico a base di polistirene, disposti su lati opposti dello strato centrale (11); almeno uno strato di rivestimento esterno (14, 15) atto a rivestire almeno uno dei due strati opposti (12, 13) e a ricevere un inchiostro di stampaggio, dove detto strato di rivestimento esterno è realizzato in un materiale plastico scelto dal gruppo consistente di: polietilene, polipropilene, PET, PETG. CLAIMS 1. Use of a multilayer film material to make wraps, in particular for food products, suitable to be closed by imparting a twist to the film material, in which the multilayer material has: a central layer (11) of a first plastic material based on polyethylene or polypropylene; two opposite layers (12, 13) of a second polystyrene-based plastic material, arranged on opposite sides of the central layer (11); at least one outer coating layer (14, 15) adapted to coat at least one of the two opposite layers (12, 13) and to receive a molding ink, where said outer coating layer is made of a plastic material chosen from the group consisting of: polyethylene, polypropylene, PET, PETG. 2 . Impiego di un materiale pellicolare secondo la rivendicazione 1, in cui il materiale comprende: uno strato centrale (11) di un primo materiale plastico a base di polietilene o polipropilene; due strati intermedi (12, 13) di un secondo materiale plastico a base di polistirene, disposti su lati opposti dello strato centrale (11); due strati di rivestimento esterni (14, 15) atto a rivestire ciascuno uno dei due strati intermedi (12, 13) e a ricevere un inchiostro di stampaggio, dove detti strati di rivestimenti esterni sono realizzato in materiali plastici scelti dal gruppo consistente di: polietilene, polipropilene, PET, PETG. 2 . Use of a film material according to claim 1, wherein the material comprises: a central layer (11) of a first plastic material based on polyethylene or polypropylene; two intermediate layers (12, 13) of a second polystyrene-based plastic material, arranged on opposite sides of the central layer (11); two outer coating layers (14, 15) adapted to each coat one of the two intermediate layers (12, 13) and to receive a molding ink, where said outer coating layers are made of plastic materials selected from the group consisting of: polyethylene, polypropylene, PET, PETG. 3. Impiego di un materiale pellicolare secondo la rivendicazione 1 o 2, in cui lo strato centrale (11) e lo strato esterno o gli strati esterni (14, 15) sono composizioni comprendenti da circa 20% a circa 90% in peso di polietilene metallocene rispetto al peso complessivo dei rispettivi strati. The use of a film material according to claim 1 or 2, wherein the middle layer (11) and the outer layer or layers (14, 15) are compositions comprising from about 20% to about 90% by weight of polyethylene metallocene with respect to the total weight of the respective layers. 4. Impiego di un materiale pellicolare secondo la rivendicazione 1 o 2, in cui lo strato centrale (11) e lo strato esterno o gli strati esterni (14, 15) sono composizioni comprendenti polietilene a bassa densità. The use of a film material according to claim 1 or 2, wherein the core layer (11) and the outer layer or layers (14, 15) are compositions comprising low density polyethylene. 5. Impiego di un materiale pellicolare secondo la rivendicazione 1 o 2, in cui lo strato centrale (11) e lo strato esterno o gli strati esterni (14, 15) sono composizioni comprendenti polietilene ad alta densità. The use of a film material according to claim 1 or 2, wherein the central layer (11) and the outer layer or the outer layers (14, 15) are compositions comprising high density polyethylene. 6 . Impiego di un materiale pellicolare secondo una qualunque delle rivendicazioni precedenti, in cui gli strati opposti o intermedi (12, 13) comprendono mescole a base di polistirene base e di copolimeri di stirene-butadiene. 6. Use of a film material according to any one of the preceding claims, wherein the opposite or intermediate layers (12, 13) comprise mixtures based on polystyrene base and styrene-butadiene copolymers. 7. Impiego di un materiale pellicolare secondo la rivendicazione 6, in cui gli strati opposti o intermedi (12, 13) comprendono il 20-90% in peso di copolimeri di stirene-butadiene. The use of a film material according to claim 6, wherein the opposite or intermediate layers (12, 13) comprise 20-90% by weight of styrene-butadiene copolymers. 8. Impiego di un materiale pellicolare secondo la rivendicazione 1 o 2, in cui il singolo esterno o i due strati esterni di rivestimento (14, 15) sono realizzati in PET o PETG ed unito/i al rispettivo strato intermedio (12, 13) mediante un adesivo (16). 8. Use of a film material according to claim 1 or 2, wherein the single outer or the two outer coating layers (14, 15) are made of PET or PETG and bonded to the respective intermediate layer (12, 13) by means of a sticker (16). 9. Impiego di un materiale pellicolare secondo una qualunque delle rivendicazioni precedenti, in cui ciascuno strato opposto o intermedio (12, 13) comprende a sua volta due strati: uno strato più interno (12a, 13a) a base di polistirene, a contatto con lo strato centrale (11), e uno strato più esterno (12b, 13b) a base di po-listirene modificato. Use of a film material according to any one of the preceding claims, wherein each opposite or intermediate layer (12, 13) in turn comprises two layers: an innermost layer (12a, 13a) based on polystyrene, in contact with the central layer (11), and an outermost layer (12b, 13b) based on modified polystyrene. 10. Materiale pellicolare multistrato secondo una qualunque delle precedenti rivendicazioni. 10. Multilayer film material according to any one of the preceding claims. 11. Involucro atto ad essere chiuso su un prodotto mediante torsione, realizzato in un materiale pel-licolare multistrato secondo una qualunque delle precedenti rivendicazioni. 11. Casing suitable for being closed on a product by twisting, made of a multilayer film material according to any one of the preceding claims.
IT2001TO000647A 2001-07-04 2001-07-04 USE OF A MULTI-LAYER FILM MATERIAL TO REALIZE ENVELOPES. ITTO20010647A1 (en)