IT202100001001A1 - ECO-SUSTAINABLE TANNING METHOD, SUITABLE FOR WASHING, TREATMENT AND PRODUCTION OF WORKABLE LEATHER AND ASSOCIATED DRUM - Google Patents
ECO-SUSTAINABLE TANNING METHOD, SUITABLE FOR WASHING, TREATMENT AND PRODUCTION OF WORKABLE LEATHER AND ASSOCIATED DRUM Download PDFInfo
- Publication number
- IT202100001001A1 IT202100001001A1 IT102021000001001A IT202100001001A IT202100001001A1 IT 202100001001 A1 IT202100001001 A1 IT 202100001001A1 IT 102021000001001 A IT102021000001001 A IT 102021000001001A IT 202100001001 A IT202100001001 A IT 202100001001A IT 202100001001 A1 IT202100001001 A1 IT 202100001001A1
- Authority
- IT
- Italy
- Prior art keywords
- hides
- weight
- treated
- tanning
- phases
- Prior art date
Description
Descrizione dell?invenzione avente per titolo: Description of the invention entitled:
?METODO DI CONCIATURA ECOSOSTENIBILE, ATTO AL LAVAGGIO, AL TRATTAMENTO E ALLA PRODUZIONE DI PELLI LAVORABILI E BOTTALE ASSOCIATO? ?ECO-SUSTAINABLE TANNING METHOD, SUITABLE FOR WASHING, TREATMENT AND PRODUCTION OF WORKABLE LEATHER AND ASSOCIATED DRUM?
Descrizione Description
Campo della tecnica field of technique
L?invenzione si riferisce ad nuovo metodo industriale per la conservazione e il trattamento di pelli. In particolare il metodo di seguito dettagliatamente descritto e rivendicato ha lo scopo di garantire l?ecosostenibilit? e la resistenza nel tempo del prodotto cos? trattato. The invention refers to a new industrial method for preserving and treating hides. In particular, the method described and claimed in detail below has the purpose of guaranteeing eco-sustainability? and the resistance over time of the product cos? treated.
Arte nota Known art
Tradizionalmente, la concia ? il trattamento a cui vengono sottoposte le pelli al fine di essere conservate e lavorate. Traditionally, tanning? the treatment to which the hides are subjected in order to be preserved and processed.
L?industria conciaria ? il settore industriale che produce pelli e cuoio recuperando e valorizzando un sottoprodotto dell?industria alimentare: la pelle animale grezza proveniente dalla macellazione, che altrimenti andrebbe smaltita o peggio ancora seppellita, destabilizzando l?ecosistema del pianeta. The tanning industry? the industrial sector that produces skins and leather by recovering and enhancing a by-product of the food industry: raw animal skin from slaughter, which otherwise would have to be disposed of or worse yet buried, destabilizing the planet?s ecosystem.
La pelle ? un materiale organico proteico e la scoperta della concia alle aldeidi (di cui il fumo di legni freschi ? ricco) e la concia vegetale ai tannini (contenuti nel legno e in tutti i vegetali) risale alla preistoria. Le aldeidi, i tannini e la calce (il calcare delle pietre che per effetto del calore si trasforma in calce viva (CaO) che con acqua forma calce spenta (Ca(OH)2)) sono sostanze che ancora oggi, seppure con metodi diversi, vengono utilizzate nei moderni processi conciari. Dunque l?attivit? conciaria ? antica quanto l?uomo e questo aiuta a capire perch? ancora oggi l?uomo ha con il cuoio e la pelle un rapporto molto intenso. Skin ? an organic protein material and the discovery of aldehyde tanning (of which the smoke of fresh wood is rich) and vegetable tanning with tannins (contained in wood and in all vegetables) dates back to prehistoric times. Aldehydes, tannins and lime (the limestone of the stones which, due to the effect of heat, transforms into quicklime (CaO) which forms slaked lime (Ca(OH)2) with water) are substances which still today, albeit with different methods , are used in modern tanning processes. So the activity? tannery? as old as? man and this helps to understand why? still today man has a very intense relationship with leather and skin.
Per molti secoli la tecnologia conciaria ? rimasta praticamente invariata, con l?uso quasi soltanto di acqua, calce, tannini vegetali e grassi animali (solo piccole quantit? di pelli erano conciate con allume, cio? all?alluminio, ottenendo un cuoio bianco ma non resistente all?acqua) e tanta attivit? manuale. Nella seconda met? dell?Ottocento fu introdotto il bottale, una macchina costituita da un cilindro ruotante intorno al proprio asse. L?acqua, le pelli e i prodotti chimici venivano introdotti nel bottale, che veniva poi fatto girare pi? o meno velocemente. L?azione meccanica di rotazione favorisce in modo notevole la penetrazione dei prodotti all?interno della pelle e quindi il processo conciario, che in precedenza durava molti mesi, ne risult? molto accelerato. L?introduzione del bottale ha rappresentato il primo passo per la trasformazione dell?attivit? conciaria da attivit? prettamente artigianale ad attivit? pi? propriamente industriale. For many centuries the tanning technology ? remained practically unchanged, with the use almost only of water, lime, vegetable tannins and animal fats (only small quantities of hides were tanned with alum, that is with aluminum, obtaining a white leather but not resistant to water) and a lot of activity manual. In the second half? In the 19th century the drum was introduced, a machine consisting of a cylinder rotating around its own axis. The water, the skins and the chemical products were introduced into the drum, which was then turned over and over again. or slower. The mechanical action of rotation considerably favors the penetration of the products inside the leather and therefore the tanning process, which previously lasted many months, resulted very accelerated. Was the introduction of the drum the first step in transforming the business? tanning business purely artisanal activity more properly industrial.
Il passo forse pi? importante verso una radicale trasformazione della produzione conciaria fu tuttavia la scoperta, verso la fine dell?Ottocento-inizi del Novecento, della concia al cromo, cio? della capacit? conciante dei composti del cromo trivalente (Cr+3) che sono in grado di legarsi stabilmente alla pelle rendendola imputrescibile. Questo tipo di concia ? ormai di gran lunga il pi? diffuso (l?85-90% di tutti i cuoi prodotti nel mondo sono conciati al cromo) a causa della sua semplicit?, rapidit? (poche ore invece che giorni), flessibilit? (con la concia al cromo si pu? produrre qualsiasi tipo di cuoio, eccetto il cuoio da suola per scarpe), economicit?. The step perhaps more? However, towards the end of the 19th century and the beginning of the 20th century, the discovery of chrome tanning was important towards a radical transformation of tanning production. of the capacity? tanning agent of trivalent chromium compounds (Cr+3) which are able to bind stably to the leather making it rot-proof. This type of tanning? now by far the most? widespread (85-90% of all leather produced in the world are tanned with chrome) due to its simplicity, rapidity? (a few hours instead of days), flexibility? (with chrome tanning you can produce any type of leather, except shoe sole leather), economy.
Il bottale, la concia al cromo, gli enormi sviluppi della chimica negli ultimi anni, l?introduzione anche nell?industria conciaria di moderne tecnologie (laser, stampa ink-jet, informatica) hanno ormai trasformato l?attivit? conciaria in una vera industria, che ancora oggi, come nella preistoria, trasforma un rifiuto della ben pi? importante industria alimentare in un prodotto utile e durevole, adatto per la produzione di innumerevoli oggetti. The drum, chrome tanning, the enormous developments in chemistry in recent years, the introduction of modern technologies in the tanning industry as well (laser, ink-jet printing, information technology) have by now transformed the business? tanning in a real industry, which still today, as in prehistory, transforms a waste of the much more? important food industry into a useful and durable product, suitable for the production of countless objects.
La problematica centrale, frutto di notevole ricerca ad oggi ? la produzione di articoli a rilascio non intenzionale di sostanze dovuta nella fattispecie proprio alla presenza del cromo all?interno del processo di conciatura, infatti, i composti del Cr(VI), il cromo come si trasforma a seguito della lavorazione, sono noti per la relativa classificazione come cancerogeni. The central issue, the result of considerable research to date? the production of articles with unintentional release of substances due in this case precisely to the presence of chromium within the tanning process, in fact, the compounds of Cr(VI), how chromium is transformed following processing, are known for their its classification as a carcinogen.
Una prima restrizione imposta dal regolamento UE 301/14 riguarda il rischio di sensibilizzazione cutanea indotto dal contatto della cute con articoli in cuoio. La restrizione ? scaturita su proposta della Danimarca che ha presentato, nel 2012, un?indagine in cui si evidenziava che circa il 30% degli articoli in cuoio testati contenevano Cr(VI) in quantit? superiore a 3 ppm. A first restriction imposed by EU regulation 301/14 concerns the risk of skin sensitization induced by skin contact with leather articles. The restriction? originated on a proposal from Denmark which presented, in 2012, a survey which highlighted that approximately 30% of the leather articles tested contained Cr(VI) in quantities greater than 3ppm.
L?aumento dei casi di allergia pu? derivare dal contatto della cute con gli articoli in cuoio e in pelle, allergia da contatto da cromo: terza allergia da metallo dopo l?allergia da nichel e cobalto. The increase in cases of allergy can derive from skin contact with leather and leather articles, chromium contact allergy: third metal allergy after nickel and cobalt allergy.
Dagli inizi degli anni ?90 gli articoli in cuoio hanno suscitato attenzione come causa di allergia e dermatiti da cromo, infatti, numerosi articoli in cuoio analizzati evidenziavano la presenza di Cr(VI) al di sopra di 3 ppm e circa l?1-3% della popolazione adulta in Europa ? allergica al cromo. Since the early 1990s, leather articles have attracted attention as a cause of chromium allergy and dermatitis, in fact, numerous leather articles analyzed showed the presence of Cr(VI) above 3 ppm and about 1-3 % of the adult population in Europe ? allergic to chromium.
Alcune privative industriali gi? allora affrontarono questa problematica. Un esempio ne ? il brevetto, ITPI920017(A1), pubblicato nel ?94 che tratta di un sistema di concia ecologica che abbatte il cromo e le acque di scarico delle concerie evitando i costi, di smaltimento come prevedevano i regolamenti. L?S. C. E. /92E ? un composto di prodotti di facile reperibilit? sul mercato, che utilizzati nelle giuste proporzioni e quantit?, uniti al cromo, risparmia l?uso di quest?ultimo in misura di circa 55-56% mantenendo e non alterando le caratteristiche della conciatura delle pelli. Tale sistema all?epoca consentiva alle imprese di non modificare le consuete fasi di lavorazione, ottenendo cos? un risparmio economico consistente ed un vantaggio per l?ambiente riducendo l?utilizzazione del cromo rispetto ai parametri di scarico e rendendo possibile lo smaltimento direttamente al deposito. Some industrial rights already? then they faced this problem. An example of it? the patent, ITPI920017(A1), published in ?94 which deals with an ecological tanning system that breaks down the chromium and the waste water from the tanneries avoiding disposal costs, as required by the regulations. L?S. C.E. /92E ? a compound of easily available products? on the market, which used in the right proportions and quantities, combined with chromium, saves the use of the latter by about 55-56% while maintaining and not altering the characteristics of the tanning of the hides. At the time, this system allowed companies not to modify the usual processing phases, thus obtaining a substantial economic saving and an advantage for the environment by reducing the use of chromium with respect to the discharge parameters and making it possible to dispose of it directly at the deposit.
Un altro esempio ? il brevetto WO00790011 (A1), il quale riguarda una miscela di THP e un moderatore utilizzati per conciare la pelle. Il moderatore ? selezionato tra metafosfati e composti poliidrossilici o polipirolidilici come glicerolo, carbossidrati PVA o PVP. Another example ? patent WO00790011 (A1), which relates to a mixture of THP and a moderator used to tan leather. The moderator ? selected from metaphosphates and polyhydroxy or polypyrodyl compounds such as glycerol, PVA or PVP carboxylates.
In sintesi, il delicato problema dell?impatto ambientale del processo di conciatura ? stato, nel tempo, oggetto di sviluppi e migliorie per massimizzare la produzione e al tempo stesso ridurre l?inquinamento. In summary, the delicate problem of the environmental impact of the tanning process? Over time, it has been the object of developments and improvements to maximize production and at the same time reduce pollution.
Tuttavia, nessuna soluzione sembra essere stata rivendicata, in questo ambito, che sia completamente esente dall?aggiunta di cromo. However, no solution seems to have been claimed in this area which is completely free from the addition of chromium.
Scopo del presente brevetto ? quindi quello di definire un metodo di conciatura per il trattamento e la produzione di pelli (privo di cromo) ecologico. Purpose of this patent? therefore that of defining an ecological tanning method for the treatment and production of (chrome-free) leather.
Descrizione dell?invenzione Description of the invention
Secondo la presente invenzione viene descritto un metodo per la conciatura di pelli ecosostenibile. Per la realizzazione di tale metodo ? necessario l?utilizzo di un macchinario bottale appositamente configurato e incluso nella presente invenzione. According to the present invention a method for the tanning of eco-sustainable hides is described. For the implementation of this method ? it is necessary to use a specially configured drum machine included in the present invention.
Il metodo si compone cos?: The method is composed as follows:
? una fase A di sgrassamento; ? a degreasing phase A;
? una fase B di aggiunta di neutralizzante; ? a neutralizer addition step B;
? una fase C di macerazione; ? a phase C of maceration;
? una fase D di aggiunta di sale e bicarbonato di sodio; ? a step D of adding salt and sodium bicarbonate;
? una fase E di aggiunta di additivo sbiancante; ? a step E of adding a whitening additive;
? una fase F di aggiunta di sale; ? a step F of adding salt;
? una fase G di aggiunta di acido formico; ? a step G of adding formic acid;
? una fase H di aggiunta di tannini liquidi; ? a phase H of addition of liquid tannins;
? una fase I di aggiunta di ingrassi speciali. ? a phase I of addition of special fatliquors.
Durante la fase A s?impiega uno sgrassante etassilato, in una quantit? al 2-6% in rapporto al peso e lo sbagnante a base di esteri naturali allo 0,5-1,5% sempre in rapporto al peso, ad una temperatura dell?acqua compresa tra 20?C e 30?C per una durata di 2 ore a 10 giri di bottale al minuto. Il neutralizzante aggiunto nella suddetta fase B ? a base di sale bicarbonato all?1-3% in peso, in detto macchinario bottale dove rimane per un intervallo di tempo di circa 1 ora-1 ora e mezzo a seconda delle dimensioni delle pelli trattate. La suddetta fase di macerazione avviene per mezzo dell?aggiunta di macerante enzimatico in polvere, ad 800-1000 unit?, allo 0,8-2% in peso, per una durata di 1 ora. A seguire il metodo prosegue con l?aggiunta di sale per un 10% in peso, proseguendo la lavorazione per un intervallo di tempo di 15-30 minuti e a seguire con l?aggiunta di bicarbonato di sodio e lavorazione per ulteriori 30-36 minuti sempre in base alle pelli trattate. L?aggiunta di additivo sbiancante (in una percentuale di 1-2% in peso) ? mirata a modificare la lunghezza d?onda dei raggi UV rendendo le pelli trattate bianche. ? attraverso dosatori automatizzati che avviene il rilascio di sale, di 7 be, in una quantit? calcolata in base al peso della pelle trattata che viene rilevato in tempo reale al momento del rilascio. Anche l?acido formico viene aggiunto in rapporto al peso in una percentuale di 1-1,5% per un intervallo di tempo di 3 ore. Nelle fasi finali i tannini liquidi a basso contenuto di fenoli, si aggiungono per un 20-30% in rapporto al peso e mantenuti per un intervallo di tempo di 12 ore mentre gli ingrassi speciali, del tipo per rifinizione, vengono utilizzati in una quantit? di 8-12% in rapporto al peso prima dell?aggiunta finale di acido. During phase A an ethoxylated degreaser is used, in a quantity at 2-6% in relation to the weight and the natural ester-based wetting agent at 0.5-1.5% again in relation to the weight, at a water temperature between 20?C and 30?C for a duration 2 hours at 10 drum revolutions per minute. The neutralizer added in the aforementioned phase B ? based on bicarbonate salt at 1-3% by weight, in said drum machine where it remains for a time interval of about 1-1 hour and a half depending on the size of the treated hides. The aforementioned maceration phase takes place by means of the addition of enzymatic macerating powder, at 800-1000 units, at 0.8-2% by weight, for a duration of 1 hour. Then the method continues with the addition of salt for 10% by weight, continuing the processing for a time interval of 15-30 minutes and following with the addition of sodium bicarbonate and processing for a further 30-36 minutes always based on the treated leathers. The addition of whitening additive (in a percentage of 1-2% by weight) is aimed at modifying the wavelength of UV rays, making the treated skins white. ? through automated dispensers that is the release of salt, of 7 be, in a quantity? calculated on the basis of the weight of the treated leather which is detected in real time at the time of release. Formic acid is also added in a ratio of weight in a percentage of 1-1.5% for a time interval of 3 hours. In the final phases, the liquid tannins with a low phenol content are added for 20-30% in relation to the weight and kept for a time interval of 12 hours while the special fatliquors, of the type for finishing, are used in a quantity of 8-12% by weight before final acid addition.
In qualunque caso di mancata conservazione delle condizioni termoigrometriche prestabilite, il metodo dovr? essere interrotto e ripreso dalla fase precedente. Vantaggiosamente, la rigorosa adesione al metodo fin qui descritto garantisce la conservazione delle pelli cos? prodotte a lungo termine. In any case of non-preservation of the pre-established thermo-hygrometric conditions, the method will have to be interrupted and resumed from the previous phase. Advantageously, the rigorous adherence to the method described up to now guarantees the preservation of the hides as produced in the long term.
Il corretto espletamento della procedura ? monitorato da apposite attrezzature incluse nel macchinario bottale che sono atte a verificare, oltre i parametri termoigrometrici e la durata di ciascuna fase, anche il colore e l?odore delle pelli trattate. Uno dei vantaggi principali della presente invenzione, oltre al metodo consiste nei sistemi di monitoraggio installati all?interno del suddetto macchinario. The correct completion of the procedure? monitored by special equipment included in the drum machinery which is able to verify, in addition to the thermo-hygrometric parameters and the duration of each phase, also the color and smell of the treated hides. Apart from the method, one of the main advantages of the present invention consists in the monitoring systems installed inside the aforementioned machinery.
Infatti, almeno un controllore logico programmabile (PLC) e sistemi di autoregolazione termoigrometrica sono associati a sistemi temporizzatori che svolgono autonomamente ciascuna delle fasi del metodo mentre un sistema antistratificatore dell?aria, interno, fa circolare costantemente l?aria interna al suddetto macchinario rendendo la temperatura e l?umidit? omogenee in tutto il volume dello stesso. In fact, at least one programmable logic controller (PLC) and thermo-hygrometric self-regulation systems are associated with timer systems which independently carry out each of the phases of the method while an internal anti-stratifier system makes the air inside the aforementioned machinery circulate constantly, making the temperature and? humidity? homogeneous throughout the volume of the same.
Un sistema di analisi dell?immagine, inquadra le pelli in ciascuna delle fasi e ne rileva il colore e le dimensioni per l?impostazione automatica della durata temporale delle fasi di sgrassamento e macerazione. An image analysis system frames the hides in each of the phases and detects their color and dimensions for the automatic setting of the time duration of the degreasing and maceration phases.
Un sistema di analisi degli odori interni, rilevando gli odori emanati dalle pelli in lavorazione, segnala eventuali difformit? che sono sintomo di un cattivo svolgimento del metodo ed un sistema automatico di rilevazione del peso delle pelli durante la lavorazione rileva in tempo reale il peso in ciascuna delle fasi del metodo in oggetto, regolando automaticamente la durata temporale di ciascuna delle fasi A, B, D, ed il dosaggio di ciascuno degli elementi additivi in ogni fase del suddetto metodo. Eventualmente e vantaggiosamente, vengono installati un sistema contalitri, integrato in detto sistema automatico di rilevazione del peso, il quale rilascia acqua misurata in funzione del peso rilevato, ed uno stabilizzatore del PH delle pelli che rileva lo stato delle stesse durante tutte le fasi del metodo sopra descritto. An internal odor analysis system, by detecting the odors emanating from the leathers being processed, signals any discrepancies? which are a symptom of a bad performance of the method and an automatic system for detecting the weight of the hides during processing detects the weight in each of the phases of the method in question in real time, automatically adjusting the time duration of each of the phases A, B, D, and the dosage of each of the additive elements in each step of the above method. Possibly and advantageously, a litre-counter system is installed, integrated in said automatic weight detection system, which releases water measured according to the weight detected, and a PH stabilizer of the hides which detects the state of the same during all phases of the method described above.
Vantaggiosamente, tutti i dati rilevati dai sistemi contenuti nel macchinario bottale sono inviati a un PLC, in esso integrato e dotato di mezzi di segnalazione di eventuali parametri eccedenti soglie prestabilite tramite comuni dispositivi di segnalazione acustica e/o luminosa. Advantageously, all the data detected by the systems contained in the drum machine are sent to a PLC, integrated therein and equipped with means for signaling any parameters exceeding pre-established thresholds by means of common acoustic and/or light signaling devices.
I vantaggi offerti dalla presente invenzione sono evidenti alla luce della descrizione fin qui esposta e saranno ancora pi? chiari grazie alle figure annesse e alla relativa descrizione dettagliata. The advantages offered by the present invention are evident in the light of the description set forth up to now and will be even more clear thanks to the annexed figures and the relative detailed description.
Descrizione delle figure Description of the figures
L?invenzione verr? qui di seguito descritta in una forma di realizzazione preferita a titolo esplicativo e non limitativo con l?ausilio delle figure annesse, nelle quali: - FIGURA 1 mostra le fasi del metodo in oggetto dalla A alla I. The invention will come described hereinafter in a preferred embodiment by way of explanation and without limitation with the aid of the annexed figures, in which: - FIGURE 1 shows the phases of the method in question from A to I.
- FIGURA 2 mostra schematicamente un macchinario bottale 100 per la conciatura di pelli da trattare secondo il metodo in oggetto. Sono visibili tutti gli strumenti di controllo e verifica della correttezza del metodo che fanno convergere i dati rilevati al PLC 3 che monitora il tutto e, se al caso, emette segnalazioni di allarme. FIGURE 2 schematically shows a drum machine 100 for tanning hides to be treated according to the method in question. All the control and verification tools of the correctness of the method are visible, which converge the detected data to the PLC 3 which monitors everything and, if necessary, issues alarm signals.
Descrizione dettagliata dell?invenzione Detailed description of the invention
La presente invenzione verr? ora illustrata a titolo puramente esemplificativo ma non limitativo o vincolante, ricorrendo alle figure le quali illustrano alcune realizzazioni relativamente al presente concetto inventivo. This invention will come now illustrated purely by way of example but not in a limiting or binding way, making use of the figures which illustrate some embodiments with respect to the present inventive concept.
Con riferimento alla FIG. 1 ? mostrato il metodo di conciatura, in oggetto, in tutte le sue fasi, finalizzate al lavaggio, trattamento e alla produzione di pelli morbide, resistenti alla luce senza l?aggiunta di cromo. Ciascuna delle pelli trattate viene classificata in base alla razza, l?et?, la provenienza e il regime di vita del bestiame. Il metodo in oggetto avviene interamente all?interno dello stesso macchinario bottale 100 come mostrato in Fig. 2. Le percentuali dei prodotti impiegati in ciascuna fase vengono calcolate sui pesi minimi delle pelli conciate e trattate rilevati in tempo reale tramite detti sistemi di analisi compresi nel macchinario bottale 100. Referring to FIG. 1 ? shown the tanning method, in question, in all its phases, aimed at washing, treating and producing soft, light-resistant leathers without the addition of chromium. Each of the skins treated is classified on the basis of the breed, age, origin and lifestyle of the cattle. The method in question occurs entirely within the same drum machine 100 as shown in Fig. 2. The percentages of the products used in each phase are calculated on the minimum weights of the tanned and treated hides detected in real time by means of said analysis systems included in the drum machine 100.
Il metodo si compone delle seguenti fasi: The method consists of the following stages:
A. Una prima fase di sgrassamento delle pelli attraverso l?impiego di sgrassante etassilato (al 2-6% in rapporto al peso) e di sbagnante a base di esteri naturali allo 0,5-1,5% in rapporto al peso, ad una temperatura dell?acqua compresa tra 20? C e 30?C, il tutto per una durata di 2 ore ad un regime di 10 giri al minuto. A. A first phase of degreasing the hides through the use of an ethoxylated degreaser (at 2-6% by weight) and a wetting agent based on natural esters at 0.5-1.5% by weight, for a water temperature between 20? C and 30?C, all for a duration of 2 hours at a rate of 10 revolutions per minute.
B. Una seconda fase durante la quale viene aggiunto un neutralizzante a base di sale bicarbonato (all?1-3% in rapporto al peso), nel suddetto macchinario bottale 100 dove rimane per un intervallo di tempo compreso 1 ora-1 ora e mezzo a seconda delle dimensioni e del peso, rilevato, delle pelli trattate. C. Una fase di macerazione, che avviene per mezzo dell?aggiunta di macerante enzimatico in polvere (ad 800-1000 unit?, allo 0,8-2% in rapporto al peso) per una durata di 1 ora. B. A second phase during which a bicarbonate salt-based neutralizer (at 1-3% by weight) is added to the aforementioned drum machine 100 where it remains for a time interval of between 1 hour and 1 hour and a half according to the size and weight, detected, of the treated hides. C. A phase of maceration, which takes place by means of the addition of enzymatic macerating powder (at 800-1000 units, at 0.8-2% by weight) for a duration of 1 hour.
D. Successivamente viene aggiunto sale per un 10% in rapporto al peso, proseguendo la lavorazione per un intervallo di tempo di 15-30 minuti a seguito dei quali viene aggiunto bicarbonato di sodio proseguendo il lavaggio per ulteriori 30-36 minuti, a seconda delle pelli trattate. D. Subsequently salt is added for a 10% in relation to the weight, continuing the processing for a time interval of 15-30 minutes following which sodium bicarbonate is added continuing the washing for a further 30-36 minutes, depending on the treated skins.
E. In una fase successiva viene aggiunto un additivo sbiancante (in una percentuale dell?1-2% in rapporto al peso) che modifica la lunghezza d?onda dei raggi UV rendendo le pelli trattate bianche e, a seguire, prosecuzione del lavaggio con acqua a 30?C. In questa fase, viene impiegato il percarbonato di sodio, additivo di tipo ecologico, atto ad attivarsi tramite sostanze naturali ad una temperatura di 30?C ed atto a liberare ossigeno attivo ad una temperatura di 50?C agendo come igienizzante, sbiancante, antibatterica, disinfettante, rivitalizzante sulle pelli trattate. E. In a subsequent phase, a whitening additive is added (in a percentage of 1-2% in relation to the weight) which modifies the wavelength of the UV rays, making the treated leathers white and, subsequently, continuation of the washing with water at 30?C. In this phase, sodium percarbonate is used, an ecological type additive, capable of being activated by natural substances at a temperature of 30?C and capable of releasing active oxygen at a temperature of 50?C, acting as a sanitizer, whitener, antibacterial, disinfectant, revitalizing on treated skins.
F. Una fase di aggiunta di sale (di 7 be) attraverso dosatori automatizzati, installati nel suddetto macchinario 100, e progettati per rilasciare una quantit? di sale in base al peso della pelle trattata rilevato in tempo reale al momento del rilascio. F. A phase of adding salt (of 7 be) through automated dispensers, installed in the aforementioned machine 100, and designed to release a quantity of salt based on the weight of the treated skin detected in real time at the time of release.
G. In una fase ulteriore viene aggiunto dell?acido formico (1-1,5% in rapporto al peso) per un intervallo di tempo di 3 ore. G. In a further phase, formic acid is added (1-1.5% by weight) for a time interval of 3 hours.
H. Successivamente si aggiungono tannini liquidi (per un 20-30% in rapporto al peso) a basso contenuto di fenoli per un intervallo di tempo di 12 ore. H. Subsequently, liquid tannins (20-30% in relation to weight) with a low phenol content are added for a time interval of 12 hours.
I. Una fase finale di aggiunta di ingrassi speciali per rifinizione (in una quantit? di 8-12% in rapporto al peso) e di aggiunta finale di acido. I. A final stage of addition of special finishing fats (in an amount of 8-12% by weight) and final addition of acid.
Il suddetto metodo, in qualunque caso di mancata conservazione delle condizioni prestabilite delle pelli trattate, ? programmato per riprendere dalla fase precedente, garantendo la conservazione delle pelli conciate, rendendole, inoltre, resistenti, elastiche, impermeabili e morbide nel tempo. The aforementioned method, in any case of failure to preserve the pre-established conditions of the treated hides, ? programmed to resume from the previous phase, guaranteeing the conservation of the tanned hides, also making them resistant, elastic, waterproof and soft over time.
Ulteriormente ? prevista una fase C.1 di lavaggio con acqua a 30?C, a seguito della fase di macerazione C, la quale avviene tramite un sistema di immissione di nebulizzazione installato nel suddetto macchinario bottale 100. Further ? a washing phase C.1 with water at 30°C is envisaged, following the maceration phase C, which takes place via a nebulization inlet system installed in the aforementioned drum machine 100.
Il metodo di conciatura, in oggetto, comprende il controllo costante, tramite sistemi di analisi dell?immagine e del peso compresi nel macchinario bottale 100, seguendo parametri relativi al colore delle pelli trattate, odore delle pelli trattate, superficie evaporativa delle pelli trattate. In caso di eccedenza dei parametri soglia prestabiliti avviene la segnalazione tramite comuni dispositivi di segnalazione acustica e/o luminosa. The tanning method in question comprises constant control, by means of image and weight analysis systems included in the drum machine 100, following parameters relating to the color of the treated hides, the smell of the treated hides, the evaporative surface of the treated hides. In the event that the pre-established threshold parameters are exceeded, signaling takes place via common acoustic and/or light signaling devices.
Con riferimento alla FIG. 2 ? mostrato il macchinario bottale 100, all?interno del quale avvengono tutte le fasi del metodo in oggetto, progettato per la conciatura di pelli bovine, caprine, ovine, equine e di qualsiasi altro animale differenziato e classificato per razza, et?, provenienza e regime di vita del bestiame monitorando costantemente le condizioni termoigrometriche interne di tutte le fasi di lavaggio, asciugatura e trattamento delle pelli. Referring to FIG. 2 ? shown the drum machine 100, inside which all the phases of the method in question take place, designed for the tanning of bovine, goat, sheep, horse and any other animal skins differentiated and classified by breed, age, origin and regimen life of the livestock by constantly monitoring the internal thermo-hygrometric conditions of all the washing, drying and treatment phases of the hides.
Il suddetto macchinario comprende: This machinery includes:
- almeno un controllore logico programmabile 3 e sistemi di autoregolazione termoigrometrica 1 associati a sistemi temporizzatori 2 che svolgono autonomamente ciascuna delle fasi del metodo; - at least one programmable logic controller 3 and thermo-hygrometric self-regulation systems 1 associated with timer systems 2 which autonomously carry out each of the phases of the method;
- un sistema antistratificatore 10 dell?aria, interno, che fa circolare l?aria interna al suddetto macchinario 100 rendendo la temperatura e l?umidit? omogenee in tutto il volume dello stesso; - an internal air anti-stratifier system 10, which circulates the air inside the aforementioned machine 100 making the temperature and humidity homogeneous throughout the volume of the same;
- un sistema di analisi dell?immagine 20, che inquadrando le pelli in ciascuna delle fasi, ne rileva il colore e le dimensioni per l?impostazione automatica della durata temporale delle fasi di sgrassamento e macerazione in funzione delle dimensioni delle pelli; - an image analysis system 20 which, by framing the hides in each of the phases, detects their color and dimensions for automatic setting of the time duration of the degreasing and maceration phases according to the dimensions of the hides;
- un sistema di analisi degli odori 30 interni pensato per rilevare gli odori emanati dalle pelli in lavorazione, segnalando eventuali difformit? che sono sintomo di un cattivo svolgimento del metodo; - an internal odor analysis system 30 designed to detect the odors emanating from the leathers being processed, signaling any discrepancies? which are a symptom of a bad performance of the method;
- un sistema automatico di rilevazione del peso 40 delle pelli durante la lavorazione che rilevando in tempo reale il peso in ciascuna delle fasi del metodo in oggetto regola automaticamente la durata temporale di ciascuna delle fasi A, B, D, ed il dosaggio di ciascuno degli elementi additivi in ogni fase del suddetto metodo; - an automatic system 40 for detecting the weight of the hides during processing which, by detecting the weight in real time in each of the phases of the method in question, automatically regulates the time duration of each of the phases A, B, D, and the dosage of each of the additive elements in each step of the above method;
- un sistema contalitri, integrato in detto sistema automatico di rilevazione del peso 40, atto al rilascio di acqua, misurato, ed uno stabilizzatore PH atto a rilevare lo stato delle pelli trattate durante tutte le fasi del metodo sopra descritto. - a litre-counter system, integrated in said automatic weight detection system 40, suitable for releasing measured water, and a PH stabilizer suitable for detecting the state of the treated hides during all the phases of the method described above.
Inoltre, il suddetto PLC 3 ? dotato di un database atto a immagazzinare i dati di ogni ciclo di conciatura eseguito, salvandone i dati rilevati, la tipologia di pelli trattate, la data e la durata di ogni fase. Furthermore, the aforementioned PLC 3 ? equipped with a database suitable for storing the data of each tanning cycle performed, saving the data collected, the type of leather treated, the date and duration of each phase.
I suddetti sistema di autoregolazione termoigrometrica 1, sistema temporizzatore 2, sistema antistratificatore 10, sistema di analisi dell?immagine 20, sistema di analisi degli odori 30 e sistema automatico di rilevazione del peso 40 inviano i dati rilevati al suddetto PLC 3 il quale li analizza in funzione della tipologia di pelli trattate, in caso di superamento di soglie preimpostate o di rilevamento di dati anomali, invia segnalazioni di allarme. The aforementioned thermo-hygrometric self-regulation system 1, timer system 2, anti-stratifier system 10, image analysis system 20, odor analysis system 30 and automatic weight detection system 40 send the data detected to the aforementioned PLC 3 which analyzes them depending on the type of leather treated, in the event of exceeding pre-set thresholds or detecting anomalous data, it sends alarm signals.
? infine chiaro che all?invenzione fin qui descritta possono essere apportate modifiche, aggiunte o varianti ovvie per un tecnico del ramo, senza per questo fuoriuscire dall?ambito di tutela che ? fornito dalle rivendicazioni annesse. ? finally, it is clear that modifications, additions or variations that are obvious to a person skilled in the art can be made to the invention described up to now, without thereby departing from the scope of protection which ? provided by the appended claims.
Claims (8)