IT1146738B - PROCEDURE FOR THE PREPARATION OF AN ALDEHYDIDE PHENOL RESIN AND RESIN COMPOSITION FOR THE TREATMENT OF GLASS FIBERS USED FOR TIRES REINFORCEMENT - Google Patents
PROCEDURE FOR THE PREPARATION OF AN ALDEHYDIDE PHENOL RESIN AND RESIN COMPOSITION FOR THE TREATMENT OF GLASS FIBERS USED FOR TIRES REINFORCEMENTInfo
- Publication number
- IT1146738B IT1146738B IT67145/81A IT6714581A IT1146738B IT 1146738 B IT1146738 B IT 1146738B IT 67145/81 A IT67145/81 A IT 67145/81A IT 6714581 A IT6714581 A IT 6714581A IT 1146738 B IT1146738 B IT 1146738B
- Authority
- IT
- Italy
- Prior art keywords
- aldehyde
- phenolic compound
- adhesive
- mixture
- resin
- Prior art date
Abstract
A method of preparing a thermoplastic, water-soluble, phenolic aldehyde resin involves two steps. Firstly, the phenolic compound and aldehyde are reacted to less than 100 percent completion at an aldehyde to phenolic compound mole ratio of 0.6 to 1.5 and at a pH of 3.5 to 5.5 for 3 to 10 hours at a temperature of 13 to 32 DEG C. Secondly the pH of the reaction is adjusted to above 7.0 to 7.5 and the reaction is continued between the unreacted phenolic compound and aldehyde and resinous mixture to produce a resinous mixture that has a predominant amount of trimer polymer with slight cross-linking and a minor amount of dimer and higher oligomers. The phenolic compound is preferably resorcinol or a mixture of resorcinol and phenol. The resin mixture is processed into an adhesive by combining it with one or more elastomeric latex and various latex additives. The adhesive is aged and has added to it an amine or ammonia to tie up any unreacted aldehyde. Also additional phenolic compound may be added. The adhesive is used to coat filamentary materials in particular glass fibres and the coated filamentary materials are dried to produce reinforcement material for rubber. Uses:- Tyre cords adhesives
Applications Claiming Priority (1)
| Application Number | Priority Date | Filing Date | Title |
|---|---|---|---|
| US16335580A | 1980-06-26 | 1980-06-26 |
Publications (2)
| Publication Number | Publication Date |
|---|---|
| IT8167145A0 IT8167145A0 (en) | 1981-02-03 |
| IT1146738B true IT1146738B (en) | 1986-11-19 |
Family
ID=22589667
Family Applications (1)
| Application Number | Title | Priority Date | Filing Date |
|---|---|---|---|
| IT67145/81A IT1146738B (en) | 1980-06-26 | 1981-02-03 | PROCEDURE FOR THE PREPARATION OF AN ALDEHYDIDE PHENOL RESIN AND RESIN COMPOSITION FOR THE TREATMENT OF GLASS FIBERS USED FOR TIRES REINFORCEMENT |
Country Status (8)
| Country | Link |
|---|---|
| JP (1) | JPS5714614A (en) |
| BE (1) | BE887384A (en) |
| CA (1) | CA1173580A (en) |
| DE (1) | DE3121382A1 (en) |
| FR (1) | FR2485435A1 (en) |
| GB (1) | GB2082607A (en) |
| IT (1) | IT1146738B (en) |
| NL (1) | NL8100369A (en) |
Families Citing this family (14)
| Publication number | Priority date | Publication date | Assignee | Title |
|---|---|---|---|---|
| GB2125451B (en) * | 1982-08-13 | 1986-01-02 | Borg Warner | Extrusion coated continuous tape |
| EP1762654B1 (en) * | 2004-06-28 | 2014-04-23 | Nippon Sheet Glass Company, Limited | Cord for reinforcing rubber, method of manufacturing the cord, and rubber product using the cord |
| FR2978771B1 (en) | 2011-08-04 | 2013-09-27 | Michelin Soc Tech | AQUEOUS ADHESIVE COMPOSITION BASED ON POLYALDEHYDE AND 2,2 ', 4,4'-TETRAHYDROXYDIPHENYL SULFIDE |
| FR2978770B1 (en) | 2011-08-04 | 2013-09-27 | Michelin Soc Tech | AQUEOUS ADHESIVE COMPOSITION BASED ON POLYALDEHYDE AND PHLOROGLUCINOL |
| FR2978769B1 (en) | 2011-08-04 | 2013-09-27 | Michelin Soc Tech | AQUEOUS ADHESIVE COMPOSITION BASED ON POLYALDEHYDE AND POLYPHENOL |
| FR3008707B1 (en) * | 2013-07-16 | 2017-11-10 | Michelin & Cie | AQUEOUS ADHESIVE COMPOSITION BASED ON BIOSOURCE ALDEHYDE AND POLYPHENOL |
| FR3017070B1 (en) * | 2014-02-06 | 2017-08-25 | Michelin & Cie | STEEL REINFORCING ELEMENT COATED BY AN ADHESIVE COMPOSITION BASED ON AROMATIC ALDEHYDE AND POLYPHENOL |
| FR3031746A1 (en) | 2015-01-21 | 2016-07-22 | Michelin & Cie | HIGH RIGIDITY RUBBER COMPOSITION |
| FR3031745A1 (en) | 2015-01-21 | 2016-07-22 | Michelin & Cie | HIGH RIGIDITY RUBBER COMPOSITION |
| WO2016116468A1 (en) | 2015-01-21 | 2016-07-28 | Compagnie Generale Des Etablissements Michelin | High-rigidity rubber composition |
| CN109266283A (en) * | 2018-08-06 | 2019-01-25 | 岳西县明杰电子有限公司 | A kind of ageing-resistant insulation adhesive of transformer |
| CN109456516B (en) * | 2018-11-19 | 2021-03-05 | 北京彤程创展科技有限公司 | Bisphenol compound modified resorcinol resin, rubber composition and preparation method thereof |
| CN111088700A (en) * | 2019-12-03 | 2020-05-01 | 浙江尤夫科技工业有限公司 | Rubber canvas gum dipping formula, preparation method thereof and preparation method of rubber canvas |
| CN115353710A (en) * | 2022-08-19 | 2022-11-18 | 山东北方现代化学工业有限公司 | Nylon-reinforced high-strength glass fiber phenolic composite material and preparation method thereof |
Family Cites Families (3)
| Publication number | Priority date | Publication date | Assignee | Title |
|---|---|---|---|---|
| DE365286C (en) * | 1920-06-17 | 1922-12-14 | Hoechst Ag | Process for the preparation of resinous condensation products from phenols and acetaldehyde |
| US2494537A (en) * | 1946-07-26 | 1950-01-17 | Glen E Babcock | Cold-setting resorcinol glue composition and process of preparation |
| GB1034950A (en) * | 1963-11-15 | 1966-07-06 | Pirelli | Improvements in or relating to the preparation of liquid adhesive compositions for the treatment of textile materials and to the treatment of textile materials with suchcompositions |
-
1981
- 1981-01-12 CA CA000368266A patent/CA1173580A/en not_active Expired
- 1981-01-27 NL NL8100369A patent/NL8100369A/en not_active Application Discontinuation
- 1981-02-03 IT IT67145/81A patent/IT1146738B/en active
- 1981-02-04 BE BE0/203697A patent/BE887384A/en not_active IP Right Cessation
- 1981-02-17 FR FR8103100A patent/FR2485435A1/en not_active Withdrawn
- 1981-03-24 JP JP4384881A patent/JPS5714614A/en active Pending
- 1981-05-29 DE DE19813121382 patent/DE3121382A1/en not_active Withdrawn
- 1981-06-04 GB GB8117118A patent/GB2082607A/en not_active Withdrawn
Also Published As
| Publication number | Publication date |
|---|---|
| DE3121382A1 (en) | 1982-02-25 |
| BE887384A (en) | 1981-08-04 |
| GB2082607A (en) | 1982-03-10 |
| FR2485435A1 (en) | 1981-12-31 |
| CA1173580A (en) | 1984-08-28 |
| JPS5714614A (en) | 1982-01-25 |
| IT8167145A0 (en) | 1981-02-03 |
| NL8100369A (en) | 1982-01-18 |
Similar Documents
| Publication | Publication Date | Title |
|---|---|---|
| IT1146738B (en) | PROCEDURE FOR THE PREPARATION OF AN ALDEHYDIDE PHENOL RESIN AND RESIN COMPOSITION FOR THE TREATMENT OF GLASS FIBERS USED FOR TIRES REINFORCEMENT | |
| FI60221B (en) | COMPOSITION FOR IMPREGNERING OF GLASFIBER MATERIAL | |
| US4061620A (en) | Phenol-formaldehyde-resorcinol resins and adhesives | |
| US5032431A (en) | Glass fiber insulation binder | |
| US2563289A (en) | Coated glass fibers and method for producing same | |
| US3437122A (en) | Cord dip of improved stability | |
| US3726752A (en) | Adhesive polyamide laminate with a coating comprising resorcinol,phenol and triisocyanate | |
| ES2058193T3 (en) | METHOD FOR OBTAINING A CHEMICAL UNION BETWEEN POLYPHENYLENE-BASED MOLDING COMPOUNDS; ON THE ONE PART AND EP (D) M RUBBER, VULCANIZED WITH PEROXIDE, ON THE OTHER PART. | |
| US3793130A (en) | Fiber reinforced elastomers | |
| US4476191A (en) | Resorcinol-aldehyde resin composition for an adhesive system to be applied to glass fibers | |
| DE68929346T2 (en) | Process for gluing aromatic polyamide fiber to rubber compounds | |
| US4461859A (en) | Method of preparing a phenolic aldehyde resin and resin composition for an adhesive system to be applied to glass fibers | |
| GB1396184A (en) | Adhesive composition for bonding polyester fibre to rubber | |
| US3706619A (en) | Method of bonding wood and other materials with rapid-curing adhesives using a primer composition | |
| NO864318D0 (en) | THERMOSTABLE RESIN PREPARATION REINFORCED WITH FIBER WITH DIFFERENT LENGTH. | |
| Pizzi et al. | Lignocellulosic substrates influence on TTT and CHT curing diagrams of polycondensation resins | |
| US2489145A (en) | Synthetic resin compositions employing curing catalysts | |
| US4424238A (en) | Adhesive for bonding polyester fibrous material to rubber compositions | |
| US3537932A (en) | Process for adhering rubber layer to polyester textile article | |
| US3817775A (en) | Glass fiber reinforced elastomers | |
| EP0027538A2 (en) | Adhesion of textile cords to rubber by dip coating using an N-methylol group containing polymer | |
| US3749591A (en) | Method for forming a polysiloxane impregnated porous sheet and article thereof | |
| GB1389267A (en) | Method for treating glass fibres | |
| EP0135282A1 (en) | Aramid fiber coated with sulfonyl azide | |
| US3802953A (en) | Glass fibers treated with alkaline compatible chromic complexes and reinforced elastomers produced therefrom |