IN2014MN01793A - - Google Patents

Download PDF

Info

Publication number
IN2014MN01793A
IN2014MN01793A IN1793MUN2014A IN2014MN01793A IN 2014MN01793 A IN2014MN01793 A IN 2014MN01793A IN 1793MUN2014 A IN1793MUN2014 A IN 1793MUN2014A IN 2014MN01793 A IN2014MN01793 A IN 2014MN01793A
Authority
IN
India
Prior art keywords
heating
silicon steel
stage
slab
hot rolled
Prior art date
Application number
Inventor
Huawei Zhang
Yaping Wu
Yu Gong
Yezhong Sun
Hongxu Hei
Original Assignee
Baoshan Iron & Steel
Priority date (The priority date is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the date listed.)
Filing date
Publication date
Application filed by Baoshan Iron & Steel filed Critical Baoshan Iron & Steel
Publication of IN2014MN01793A publication Critical patent/IN2014MN01793A/en

Abstract

A hot rolled silicon steel producing method comprises: silicon steel slab heating process rough rolling process and finish rolling process. The heating process comprises a pre heating stage a heating stage and a soaking stage. The pre heating stage satisfies the following formula (1). In the formula VTp is a temperature rise rate in the pre heating stage whose unit is °C/min; t is a total heating time of the slab in the heating furnace and t=180 240min; and Tc is an initial temperature when the slab is put into the furnace whose unit is °C. By using the foregoing formula the heating process and the rough rolling process are changed an occurrence rate of edge defects during the production of the hot rolled silicon steel can be reduced and the hot rolled silicon steel with good surface quality can be produced.
IN1793MUN2014 2012-03-13 2012-03-29 IN2014MN01793A (en)

Applications Claiming Priority (2)

Application Number Priority Date Filing Date Title
CN201210065610.0A CN103302104B (en) 2012-03-13 2012-03-13 Method for manufacturing hot rolled silicon steel
PCT/CN2012/000401 WO2013134897A1 (en) 2012-03-13 2012-03-29 Hot rolled silicon steel producing method

Publications (1)

Publication Number Publication Date
IN2014MN01793A true IN2014MN01793A (en) 2015-07-03

Family

ID=49128073

Family Applications (1)

Application Number Title Priority Date Filing Date
IN1793MUN2014 IN2014MN01793A (en) 2012-03-13 2012-03-29

Country Status (9)

Country Link
US (1) US9496078B2 (en)
EP (1) EP2826871B1 (en)
JP (1) JP6283617B2 (en)
KR (1) KR101609174B1 (en)
CN (1) CN103302104B (en)
IN (1) IN2014MN01793A (en)
MX (1) MX357221B (en)
RU (1) RU2591788C2 (en)
WO (1) WO2013134897A1 (en)

Families Citing this family (23)

* Cited by examiner, † Cited by third party
Publication number Priority date Publication date Assignee Title
CN103551398B (en) * 2013-11-06 2015-09-30 北京首钢股份有限公司 A kind of non-orientation silicon steel hot rolled coil Wedge Control
CN105200441A (en) * 2014-05-30 2015-12-30 宝山钢铁股份有限公司 Hot-dip coated product with oxide layer and its manufacturing method and use
JP6748375B2 (en) 2016-10-19 2020-09-02 Ｊｆｅスチール株式会社 Descaling method for Si-containing hot rolled steel sheet
CN108237148B (en) * 2017-10-16 2019-10-08 首钢集团有限公司 A method for eliminating defects of target steel burr chain
CN108246812B (en) * 2017-12-22 2019-06-04 包头钢铁（集团）有限责任公司 A kind of hot rolled steel plate edge sticks up the control method of skin
CN109513753B (en) * 2018-10-10 2020-12-11 北京首钢股份有限公司 Method for testing metal fluidity of corner of plate blank
KR20210153033A (en) 2019-04-20 2021-12-16 타타 스틸 이즈무이덴 베.뷔. Method for manufacturing steel strip and steel strip produced thereby
CN110055391A (en) * 2019-04-24 2019-07-26 首钢集团有限公司 A method of eliminating fine steel hot rolling edge crack defect
CN110180895B (en) * 2019-05-28 2021-05-14 北京首钢股份有限公司 Method for solving edge linear defect of hot-rolled high-carbon alloy steel
CN111349778B (en) * 2020-03-20 2021-12-21 首钢京唐钢铁联合有限责任公司 Method and device for controlling charging distance of plate blank
CN111443666B (en) * 2020-03-25 2022-08-09 唐山钢铁集团有限责任公司 Intelligent tracking method for steel coil quality judgment parameters based on database model
CN112296102B (en) * 2020-09-30 2022-08-19 首钢集团有限公司 Control method and control device for low-temperature heating of non-oriented silicon steel plate blank
CN112575156A (en) * 2020-11-06 2021-03-30 邢台钢铁有限责任公司 Cogging method for improving segregation of medium carbon alloy steel casting blank
CN112605122B (en) * 2020-12-15 2023-01-10 首钢智新迁安电磁材料有限公司 A Processing Method for Improving Edge Quality of Hot Rolled Silicon Steel Sheet
CN113198866B (en) * 2021-05-07 2023-03-17 新余钢铁股份有限公司 Thin-gauge middle-high-grade non-oriented silicon steel acid rolling production process
CN113393753B (en) * 2021-05-24 2022-08-16 攀钢集团攀枝花钢钒有限公司 Semi-universal rolling metal flow plane demonstration control method for steel rail
CN113539653B (en) * 2021-09-16 2021-12-10 西安钢研功能材料股份有限公司 Preparation method of soft magnetic alloy bar
CN114378114B (en) * 2021-12-10 2024-06-28 天津市新天钢钢铁集团有限公司 Method for producing medium plate with excellent quality by using defective continuous casting blank
CN114472518B (en) * 2021-12-24 2023-12-29 安阳钢铁股份有限公司 Method for improving thickness precision of hot continuous rolling non-oriented silicon steel
CN114535315B (en) * 2022-02-08 2023-10-20 山西太钢不锈钢股份有限公司 A process for preventing edge cracks in hot rolling of high magnetic induction oriented silicon steel
CN114632818B (en) * 2022-03-14 2023-12-05 安阳钢铁股份有限公司 Technological method for reducing hot rolling edge cracking of oriented silicon steel
CN116851457B (en) * 2023-07-13 2026-03-27 广西钢铁集团有限公司 A production method for controlling black lines on the edges of cold-rolled galvanized steel sheets
CN121103862A (en) * 2025-11-14 2025-12-12 鞍钢股份有限公司 A method for improving the black line defect on the edge of hot-rolled non-oriented silicon steel

Family Cites Families (14)

* Cited by examiner, † Cited by third party
Publication number Priority date Publication date Assignee Title
US4204891A (en) * 1978-11-27 1980-05-27 Nippon Steel Corporation Method for preventing the edge crack in a grain oriented silicon steel sheet produced from a continuously cast steel slab
JPS61243118A (en) 1985-04-18 1986-10-29 Sumitomo Metal Ind Ltd Production of hot-rolled two-phase stainless steel
US5572892A (en) 1992-12-28 1996-11-12 Kawasaki Steel Corporation Method of producing silicon steel hot rolled sheets having excellent surface properties
KR100273094B1 (en) * 1996-06-17 2000-12-01 이구택 Method for heating a slab of a directional electric steel sheet reducing edge cracking of a hot-rolled sheet
JPH11123404A (en) * 1997-10-23 1999-05-11 Nippon Steel Corp Method for heating rectangular bloom for manufacturing shape and method for rough rolling shape
RU2133283C1 (en) * 1998-07-06 1999-07-20 Открытое акционерное общество Верхнесалдинское металлургическое производственное объединение Ingot heating method
KR100419641B1 (en) * 1999-04-15 2004-02-25 주식회사 포스코 Method for preventing cracks in edge part of grain oriented electrical hot rolled steel sheet
CN1258608C (en) * 2003-10-27 2006-06-07 宝山钢铁股份有限公司 Method for manufacturing cold-rolled orientation-free electrical sheet
JP2005152953A (en) * 2003-11-26 2005-06-16 Jfe Steel Kk Method for suppressing tip warpage of high silicon steel
CN100467625C (en) * 2005-10-31 2009-03-11 宝山钢铁股份有限公司 A method for producing grain-oriented silicon steel
CN100535168C (en) * 2007-02-16 2009-09-02 宝山钢铁股份有限公司 Method for producing hot-rolled ferritic stainless steel strip steel
CN101607266A (en) * 2009-07-20 2009-12-23 山东泰山钢铁集团有限公司 A kind of steekle mill that is applicable to is produced the method for ferritic stainless steel hot-rolling steel band
RU2403293C1 (en) * 2009-08-03 2010-11-10 Открытое акционерное общество "Новолипецкий металлургический комбинат" Manufacturing method of anisotropic electrotechnical steel
CN101947549A (en) * 2010-09-10 2011-01-19 山东泰山钢铁集团有限公司 Production technology for inhibiting nickel-saving austenitic stainless steel hot-rolled plate edge crack

Also Published As

Publication number Publication date
KR20140131952A (en) 2014-11-14
RU2014132737A (en) 2016-05-10
CN103302104A (en) 2013-09-18
JP6283617B2 (en) 2018-02-21
US9496078B2 (en) 2016-11-15
US20150243418A1 (en) 2015-08-27
MX2014010516A (en) 2014-10-14
MX357221B (en) 2018-06-29
WO2013134897A1 (en) 2013-09-19
EP2826871A4 (en) 2015-11-18
RU2591788C2 (en) 2016-07-20
CN103302104B (en) 2015-07-22
EP2826871B1 (en) 2018-10-17
EP2826871A1 (en) 2015-01-21
KR101609174B1 (en) 2016-04-05
JP2015511533A (en) 2015-04-20

Similar Documents

Publication Publication Date Title
MX357221B (en) Hot rolled silicon steel producing method.
IN2015DN00612A (en)
IN2014KN01251A (en)
IN2015DN00610A (en)
MY196820A (en) Ferritic stainless steel sheet and method for producing the same
MX2014002935A (en) Method for producing a non-grain-oriented higher-strength electrical strip and use thereof.
SG195248A1 (en) Thermo-mechanical processing of nickel-base alloys
ZA201104514B (en) A method and apparatus for achieving higher cooling rates of a gas during bypass cooling in a batch annealing furnace of cold rolling mills
NZ598496A (en) Processes for reducing flatness deviations in alloy articles
WO2011095417A3 (en) Metal strip having a constant thickness and varying mechanical properties
IN2015DN00425A (en)
MY186189A (en) Method for manufacturing glass blank for magnetic disk, method for manufacturing glass substrate for magnetic disk, glass blank for magnetic disk, glass substrate for magnetic disk and magnetic disk
MX380408B (en) METHOD OF PRODUCTION OF GALVANO-ANNELED STEEL SHEET.
IN2014CN02983A (en)
WO2008120535A1 (en) Process for producing flat glass, apparatus for forming buffer layer of flat glass, and flat glass producing equipment
MY172529A (en) Method and apparatus for cooling in liquefaction process
MY156573A (en) Method for producing carbonaceous film, method for producing graphite film, roll of polymer film, and roll of carbonaceous film
IN2015KN00599A (en)
MX2015011184A (en) Method for manufacturing hot dip galvanized steel sheet and continuous hot dip galvanization device.
IN2014DN08376A (en)
CN102145349B (en) Method for stably controlling finish rolling temperature of oriented silicon steel
CN104190711A (en) Production technology for pure copper plate
UA118966C2 (en) METHOD OF MANUFACTURING Seamless Hot Rolled Pipes from Improved Steel
CN103131837A (en) Sheet milling cutter air cooling micro-distortion quenching process
UA92301C2 (en) method of pressing profiles from metal alloys