HRP20070032T3 - Hardened concrete and fresh concrete for producing hardened concrete and use of a concrete for producing a structural component with a high temperature resistance - Google Patents
Hardened concrete and fresh concrete for producing hardened concrete and use of a concrete for producing a structural component with a high temperature resistanceInfo
- Publication number
- HRP20070032T3 HRP20070032T3 HR20070032T HRP20070032T HRP20070032T3 HR P20070032 T3 HRP20070032 T3 HR P20070032T3 HR 20070032 T HR20070032 T HR 20070032T HR P20070032 T HRP20070032 T HR P20070032T HR P20070032 T3 HRP20070032 T3 HR P20070032T3
- Authority
- HR
- Croatia
- Prior art keywords
- concrete
- producing
- hardened
- reinforcement
- high temperature
- Prior art date
Abstract
Otvrdnuti beton, posebno betonski dogradni element, s mješavinom od 10,0 mas. % do 25,0 mas. % računato bez ojačanja, vezanog hidrauličkog i/ili latentnog hidrauličkog veziva, npr. portland cementa, cementa za visoke peći 75,0 mas. % do 90,0 mas. % računato bez ojačanja, s dodatnim tvarima, vlaknima iz termoplasta, polimera, celuloze, papira, prema potrebi sa sredstvima za ukapljivanje, disperzatima i prema potrebi s ojačanjem, naznačen time, dazbroj dodatnih tvari ima slijedeći kemijski sastav: MgO: 25,0 do 50,0 mas. %, posebno 30,0 do 40,0 mas. %;SiO2: 30,0 do 55,0 mas. %, posebno 40,0 do 45,0 mas. %;Fe2O3: 5,0 do 15,0 mas. %;Cr2O3: najviše 1,0 mas. %;Al2O3: najviše 1,0 mas. %;slobodni SiO2 kao kvarc: najviše 5,0 mas. %, posebno maks. 1,0 mas. %; iprimjese i vlakna: ostatak, od 0,3 mas. o/oo do 3,0 mas. o/oo, posebno 0,4 mas. o/oo do 1,0 mas. o/oo.Patent sadrži još 8 patentnih zahtjeva.Hardened concrete, especially concrete extension element, with a mixture of 10.0 wt. % to 25.0 wt. % calculated without reinforcement, bonded hydraulic and / or latent hydraulic binder, eg portland cement, blast furnace cement 75.0 wt. % to 90.0 wt. % calculated without reinforcement, with additives, fibers of thermoplastics, polymers, cellulose, paper, optionally with liquefying agents, dispersants and optionally with reinforcement, characterized in that the number of additives has the following chemical composition: MgO: 25.0 to 50.0 wt. %, especially 30.0 to 40.0 wt. %; SiO2: 30.0 to 55.0 wt. %, especially 40.0 to 45.0 wt. %; Fe2O3: 5.0 to 15.0 wt. %; Cr2O3: not more than 1.0 wt. % Al2O3: not more than 1.0 wt. free SiO2 as quartz: not more than 5.0 wt. %, especially max. 1.0 wt. %; and impurities and fibers: residue, of 0.3 wt. o / oo up to 3.0 wt. o / oo, especially 0.4 wt. o / oo up to 1.0 wt. o / oo.The patent contains 8 more patent claims.
Applications Claiming Priority (2)
Application Number | Priority Date | Filing Date | Title |
---|---|---|---|
AT0106903A AT413281B (en) | 2003-07-11 | 2003-07-11 | FESTIVAL AND FRESHBETON FOR THE PRODUCTION OF A FESTIVAL |
PCT/AT2004/000245 WO2005005339A1 (en) | 2003-07-11 | 2004-07-09 | Hardened concrete and fresh concrete for producing hardened concrete and use of a concrete for producing a structural component with a high temperature resistance |
Publications (1)
Publication Number | Publication Date |
---|---|
HRP20070032T3 true HRP20070032T3 (en) | 2007-06-30 |
Family
ID=33569169
Family Applications (1)
Application Number | Title | Priority Date | Filing Date |
---|---|---|---|
HR20070032T HRP20070032T3 (en) | 2003-07-11 | 2007-02-02 | Hardened concrete and fresh concrete for producing hardened concrete and use of a concrete for producing a structural component with a high temperature resistance |
Country Status (6)
Country | Link |
---|---|
EP (1) | EP1646593B9 (en) |
AT (1) | AT413281B (en) |
DE (1) | DE502004002200D1 (en) |
HR (1) | HRP20070032T3 (en) |
PL (1) | PL1646593T3 (en) |
WO (1) | WO2005005339A1 (en) |
Families Citing this family (2)
Publication number | Priority date | Publication date | Assignee | Title |
---|---|---|---|---|
KR100921406B1 (en) * | 2009-02-27 | 2009-10-14 | (주)대우건설 | Fire-resistant concrete with high impact property |
US10759697B1 (en) | 2019-06-11 | 2020-09-01 | MSB Global, Inc. | Curable formulations for structural and non-structural applications |
Family Cites Families (7)
Publication number | Priority date | Publication date | Assignee | Title |
---|---|---|---|---|
US2315198A (en) * | 1939-12-21 | 1943-03-30 | Goldschmidt Victor Moritz | Heat resistive material, especially building material, and method of making same |
GB1002368A (en) * | 1962-12-18 | 1965-08-25 | Aluminum Co Of America | Improvements relating to calcium aluminate cements |
CA1239656A (en) * | 1984-08-07 | 1988-07-26 | Lennart Ivarsson | Refractory material and its use |
AT385027B (en) * | 1985-09-27 | 1988-02-10 | Porr Allg Bauges | SOLIDS FOR SPRAY CONCRETE |
IT1274617B (en) * | 1994-08-12 | 1997-07-18 | Roberto Guzzetti | CONCRETE SLAB FOR BILLIARD TOP |
DE19750746A1 (en) * | 1997-11-11 | 1999-05-20 | Arman Emami | Building material, especially concrete or mortar, contains magnetically or electrically aligned parallel fibers |
DE19861060A1 (en) * | 1998-07-24 | 2000-02-03 | Kalksandstein Werk Wemding Gmb | Use of olivine in a hydrothermally produced article comprising silicon dioxide and calcium oxide binder components, especially a lime sandstone block, to improve refractoriness and heat storage properties |
-
2003
- 2003-07-11 AT AT0106903A patent/AT413281B/en not_active IP Right Cessation
-
2004
- 2004-07-09 WO PCT/AT2004/000245 patent/WO2005005339A1/en active IP Right Grant
- 2004-07-09 EP EP04737375A patent/EP1646593B9/en not_active Expired - Lifetime
- 2004-07-09 DE DE200450002200 patent/DE502004002200D1/en not_active Expired - Lifetime
- 2004-07-09 PL PL04737375T patent/PL1646593T3/en unknown
-
2007
- 2007-02-02 HR HR20070032T patent/HRP20070032T3/en unknown
Also Published As
Publication number | Publication date |
---|---|
AT413281B (en) | 2006-01-15 |
WO2005005339A8 (en) | 2005-04-07 |
WO2005005339A1 (en) | 2005-01-20 |
DE502004002200D1 (en) | 2007-01-11 |
ATA10692003A (en) | 2005-06-15 |
EP1646593B1 (en) | 2006-11-29 |
PL1646593T3 (en) | 2007-04-30 |
EP1646593B9 (en) | 2007-05-09 |
EP1646593A1 (en) | 2006-04-19 |
Similar Documents
Publication | Publication Date | Title |
---|---|---|
Awoyera et al. | Role of recycling fine materials as filler for improving performance of concrete-a review | |
KR100717090B1 (en) | Cement composition | |
ATE314331T1 (en) | CONCRETE COMPOSITION AND METHOD FOR PRODUCING THE SAME | |
DK1392616T3 (en) | Plate on the basis of a cement binder | |
JP2016529200A (en) | Calcium sulfoaluminate composite binder | |
DE102010027325A1 (en) | New building material mixtures | |
DE3437680C2 (en) | Binder for restoration mortar and its use | |
MX2008015417A (en) | Cement-based fire door core. | |
CY1116114T1 (en) | HYDRAULIC CONNECTOR BETWEEN INCLUDING A GREAT BREAD SLOT | |
Saikhede et al. | An Experimental Investigation of Partial Replacement of Cement by Various Percentage of Phosphogypsum and Flyash in Cement Concrete | |
DE202010010080U1 (en) | New building material mixtures | |
MXPA05009906A (en) | Fire door core. | |
RU2007142826A (en) | KNITTING COMPOSITION AND CONCRETE FROM THIS COMPOSITION | |
Zainal Abidin et al. | The strength behavior of self-compacting concrete incorporating bottom ash as partial replacement to fine aggregate | |
HRP20070032T3 (en) | Hardened concrete and fresh concrete for producing hardened concrete and use of a concrete for producing a structural component with a high temperature resistance | |
JP2020083660A (en) | Cement admixture, expansion material, and cement composition | |
KR101733053B1 (en) | Binder of concrete by steam curing | |
Tennis et al. | Portland cement characteristics-2004 | |
Abraham et al. | A study on the influence of mineral admixtures in cementitious system containing chemical admixtures | |
Barua et al. | Effectiveness of rice husk ash (RHA) as a partial replacement of cement in concrete | |
CY1107977T1 (en) | HIGH RESISTANCE GUARANTEED CABLES WITH HIGH FLUIDITY | |
PL435080A1 (en) | Normally setting hydraulic binder, especially used in mineral-cement mixtures with MCE asphalt emulsion | |
Bawab et al. | Sustainable concrete containing supplementary cementitious materials | |
CN112661469A (en) | Novel high-ductility refractory concrete | |
Lee et al. | Contribution of Reinforcing Fiber Types on the Mechanical Properties of High Performance Concrete Subjected to High Temperature |