GB962061A - Improvements in or relating to organosilicon compositions - Google Patents

Improvements in or relating to organosilicon compositions

Info

Publication number
GB962061A
GB962061A GB38769/62A GB3876962A GB962061A GB 962061 A GB962061 A GB 962061A GB 38769/62 A GB38769/62 A GB 38769/62A GB 3876962 A GB3876962 A GB 3876962A GB 962061 A GB962061 A GB 962061A
Authority
GB
United Kingdom
Prior art keywords
moisture
radical
exposure
atoms
absence
Prior art date
Legal status (The legal status is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the status listed.)
Expired
Application number
GB38769/62A
Current Assignee (The listed assignees may be inaccurate. Google has not performed a legal analysis and makes no representation or warranty as to the accuracy of the list.)
Dow Silicones Corp
Original Assignee
Dow Corning Corp
Priority date (The priority date is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the date listed.)
Filing date
Publication date
Application filed by Dow Corning Corp filed Critical Dow Corning Corp
Publication of GB962061A publication Critical patent/GB962061A/en
Expired legal-status Critical Current

Abstract

A siloxane rubber stock is made by mixing in the absence of moisture (1) a siloxane having a viscosity of at least 25 cs. at 25 DEG C. and having the average formula: <FORM:0962061/C3/1> in which z has an average value from 1 to 1.10, y has an average value from 1.90 to 2.0 and the sum z+y is 3, R is a monovalent radical of 1 to 18 C atoms and is a hydrocarbon (saturated or unsaturated) halohydrocarbon or cyanoalkyl radical, and n is an integer, (2) a silane of the formula RxSi(OR1)4-x, wherein R1 is a monovalent-aliphatic or haloaliphatic hydrocarbon radical (having no halogen alpha to the oxygen) containing less than 5 C atoms and x is 0 or 1, in an amount of at least 0.5 mol per mol of Si-bonded hydroxyl in (1), and (3) at least 0.1% (by wt. of (1)) of an organic titanate. The titanate (3) can be monomeric, polymeric or a chelated material, numerous examples of which are given. Fillers with or without organosilyl surface modifications, e.g. oxides of Al, Ti, Zn, Mg and Zn, aluminium silicate, mica, glass, diatomaceous earth, sand, crushed quartz, silica (fume, xerogel and precipitated), C black, graphite, phthalocyanine and copper phthalocyanine, plasticizers, e.g. end-blocked dimethylpolysiloxane liquids, compression set additives, oxidation inhibitors and ultra-violet absorbers, may also be added. The compositions cure spontaneously upon exposure to moisture. In a typical example (2) a hydroxy-terminated dimethylpolysiloxane liquid was mixed with methyltrimethoxysilane and tetrapropyltitanate to yield a liquid which was stable in the absence of moisture, but gelled to a rubber in 4 or 5 hours on exposure to air. Uses: in caulking, coating and insulating applications. Specification 762,819 is referred to.
GB38769/62A 1961-10-16 1962-10-12 Improvements in or relating to organosilicon compositions Expired GB962061A (en)

Applications Claiming Priority (1)

Application Number Priority Date Filing Date Title
US14544361A 1961-10-16 1961-10-16

Publications (1)

Publication Number Publication Date
GB962061A true GB962061A (en) 1964-06-24

Family

ID=22513139

Family Applications (1)

Application Number Title Priority Date Filing Date
GB38769/62A Expired GB962061A (en) 1961-10-16 1962-10-12 Improvements in or relating to organosilicon compositions

Country Status (2)

Country Link
CH (1) CH453711A (en)
GB (1) GB962061A (en)

Cited By (10)

* Cited by examiner, † Cited by third party
Publication number Priority date Publication date Assignee Title
US3294739A (en) * 1964-11-19 1966-12-27 Dow Corning Method of making one component room temperature curing siloxane rubbers
US3334067A (en) * 1966-04-08 1967-08-01 Dow Corning Method of making one component room temperature curing siloxane rubbers
EP0028137A1 (en) * 1979-10-25 1981-05-06 Toray Industries, Inc. Dry planographic printing plate
US4546017A (en) * 1984-01-14 1985-10-08 Dow Corning Limted Organopolysiloxane composition curable to an elastomer and use thereof
US4585821A (en) * 1984-05-30 1986-04-29 Dow Corning Ltd. Elastomer forming compositions
EP0718371A1 (en) 1994-12-23 1996-06-26 DOW CORNING GmbH Silicone elastomer-forming composition
EP0916801A2 (en) 1997-11-15 1999-05-19 Dow Corning S.A. Insulating glass units
US5958317A (en) * 1996-08-14 1999-09-28 Dow Corning France S.A. Method for manufacturing a controlled-release device
US7022800B2 (en) 2000-01-06 2006-04-04 Dow Corning S.A. Organosiloxane compositions
EP3527771A1 (en) 2014-07-28 2019-08-21 Dow Silicones Corporation Panelized shadow box

Families Citing this family (1)

* Cited by examiner, † Cited by third party
Publication number Priority date Publication date Assignee Title
US4221693A (en) * 1979-03-02 1980-09-09 Getson John C Composition free of surface cure inhibition and method for preparing the same

Cited By (11)

* Cited by examiner, † Cited by third party
Publication number Priority date Publication date Assignee Title
US3294739A (en) * 1964-11-19 1966-12-27 Dow Corning Method of making one component room temperature curing siloxane rubbers
US3334067A (en) * 1966-04-08 1967-08-01 Dow Corning Method of making one component room temperature curing siloxane rubbers
EP0028137A1 (en) * 1979-10-25 1981-05-06 Toray Industries, Inc. Dry planographic printing plate
US4546017A (en) * 1984-01-14 1985-10-08 Dow Corning Limted Organopolysiloxane composition curable to an elastomer and use thereof
US4585821A (en) * 1984-05-30 1986-04-29 Dow Corning Ltd. Elastomer forming compositions
EP0718371A1 (en) 1994-12-23 1996-06-26 DOW CORNING GmbH Silicone elastomer-forming composition
US5958317A (en) * 1996-08-14 1999-09-28 Dow Corning France S.A. Method for manufacturing a controlled-release device
EP0916801A2 (en) 1997-11-15 1999-05-19 Dow Corning S.A. Insulating glass units
US6238755B1 (en) 1997-11-15 2001-05-29 Dow Corning Corporation Insulating glass units
US7022800B2 (en) 2000-01-06 2006-04-04 Dow Corning S.A. Organosiloxane compositions
EP3527771A1 (en) 2014-07-28 2019-08-21 Dow Silicones Corporation Panelized shadow box

Also Published As

Publication number Publication date
CH453711A (en) 1968-03-31

Similar Documents

Publication Publication Date Title
US3294739A (en) Method of making one component room temperature curing siloxane rubbers
US3035016A (en) Acyloxy siloxanes and a method of using the
CA2123578C (en) Compositions containing tin compounds for use as one of the components of two-component systems which cross-link at room temperature to form organopolysiloxane elastomers
US3383355A (en) Method for preparing organosiloxane polymers
US4221693A (en) Composition free of surface cure inhibition and method for preparing the same
GB1080785A (en) Improvements in &#34;organopolysiloxane compositions&#34;
GB1098899A (en) Organopolysiloxane compositions convertible into elastomers
CA1163393A (en) Room temperature vulcanizable silicone rubber compositions and process of making
GB962061A (en) Improvements in or relating to organosilicon compositions
US3109826A (en) Room temperature curable organo-
US3109013A (en) Acyloxysilcarbosiloxanes and their uses
KR930006362B1 (en) Silicone rubber composition
GB1306680A (en) Organopolysiloxane compositions
JPH02284984A (en) Neutral hardened silicone sealant
GB1338537A (en) Organosiloxane composition
US3922246A (en) Organopolysiloxane compositions which cure at ambient temperature
JPS62252456A (en) Room temperature-curable organopolysiloxane composition
JPS6143660A (en) Room temperature curing organosiloxane composition
US3375223A (en) Method for polymerizing organopolysiloxanes
US3110689A (en) Organosiloxane compositions curable to elastomers at room temperature
US3624022A (en) Room temperature curing organopolysiloxanes
GB1035492A (en) Organopolysiloxane elastomers
US3261801A (en) Reversion resistant organopolysiloxane containing barium oxide or barium peroxide
US3965280A (en) Use of organopolysiloxane compositions which cure at ambient temperature in coating electrical and electronic devices
KR840007019A (en) Process for preparing alkoxy-terminated polysiloxane