GB741995A - Improvements in or relating to plain bearings - Google Patents
Improvements in or relating to plain bearingsInfo
- Publication number
- GB741995A GB741995A GB2140252A GB2140252A GB741995A GB 741995 A GB741995 A GB 741995A GB 2140252 A GB2140252 A GB 2140252A GB 2140252 A GB2140252 A GB 2140252A GB 741995 A GB741995 A GB 741995A
- Authority
- GB
- United Kingdom
- Prior art keywords
- aluminium alloy
- temperature
- per cent
- rolling
- critical temperature
- Prior art date
- Legal status (The legal status is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the status listed.)
- Expired
Abstract
741,995. Making composite bearing material. GLACIER METAL CO., Ltd. July 22, 1953 [Aug. 26, 1952], No. 21402/52. Classes 83 (2) and 83 (4). Jointing by rolling.-A method of producing composite bearing material of the kind comprising a steel backing and a bearing surface layer of aluminium alloy bonded to the backing with or without an interlayer of a metal such as silver, copper, nickel or pure aluminium is characterized in that an aluminium alloy, e.g. containing 5 to 50 per cent of tin and having a relatively low critical temperature, is bonded to a steel backing by applying in a reducing atmosphere the aluminium alloy at a relatively low temperature to the steel or coated steel backing which has been heated sufficiently above the said critical temperature, e.g. to about 520‹ C., to ensure that when the layers are rolled together the temperature at the interface will be sufficiently high to effect the bond. ing, the temperature of at least the major part of the aluminium alloy layer being maintained below the critical temperature thereof, the composite material finally being rolled to effect substantial reduction in the thickness of the aluminium alloy layer, e.g. 30 per cent to 40 per cent. The aluminium alloy layer is cooled during the rolling by using a cooled roller or by sprays of cooling fluid. The material may be further reduced in thickness by cold rolling in one or more steps with intermediate heat treatments to 'improve ductility. Specification 666,087, [Group II], is referred to.
Priority Applications (1)
Application Number | Priority Date | Filing Date | Title |
---|---|---|---|
GB2140252A GB741995A (en) | 1952-08-26 | 1952-08-26 | Improvements in or relating to plain bearings |
Applications Claiming Priority (1)
Application Number | Priority Date | Filing Date | Title |
---|---|---|---|
GB2140252A GB741995A (en) | 1952-08-26 | 1952-08-26 | Improvements in or relating to plain bearings |
Publications (1)
Publication Number | Publication Date |
---|---|
GB741995A true GB741995A (en) | 1955-12-14 |
Family
ID=10162326
Family Applications (1)
Application Number | Title | Priority Date | Filing Date |
---|---|---|---|
GB2140252A Expired GB741995A (en) | 1952-08-26 | 1952-08-26 | Improvements in or relating to plain bearings |
Country Status (1)
Country | Link |
---|---|
GB (1) | GB741995A (en) |
Cited By (2)
Publication number | Priority date | Publication date | Assignee | Title |
---|---|---|---|---|
US2916337A (en) * | 1956-06-18 | 1959-12-08 | Borg Warner | Composite bonded article |
WO2014090764A1 (en) * | 2012-12-13 | 2014-06-19 | Federal-Mogul Wiesbaden Gmbh | Plain bearing composite material |
-
1952
- 1952-08-26 GB GB2140252A patent/GB741995A/en not_active Expired
Cited By (4)
Publication number | Priority date | Publication date | Assignee | Title |
---|---|---|---|---|
US2916337A (en) * | 1956-06-18 | 1959-12-08 | Borg Warner | Composite bonded article |
WO2014090764A1 (en) * | 2012-12-13 | 2014-06-19 | Federal-Mogul Wiesbaden Gmbh | Plain bearing composite material |
CN104837621A (en) * | 2012-12-13 | 2015-08-12 | 联合莫古尔威斯巴登有限公司 | Plain bearing composite material |
US10066670B2 (en) | 2012-12-13 | 2018-09-04 | Federal-Mogul Wiesbaden Gmbh | Plain bearing composite material |
Similar Documents
Publication | Publication Date | Title |
---|---|---|
US2386951A (en) | Method of making bearings | |
US2735170A (en) | Method-of producing a multilayer strep | |
KR850001296A (en) | Aluminum base bearing alloy | |
US2809422A (en) | Method of making a composite article | |
US3386161A (en) | Method of making bearing material | |
US3912152A (en) | Method for cladding a ferrous substrate with non-ferrous metals | |
US3180008A (en) | Method of manufacturing bearings | |
US2325071A (en) | Bearing and like article | |
GB940924A (en) | Improvements in or relating to the production of composite metal strip suitable for the manufacture of bearings | |
US2965963A (en) | Aluminum cladding of steel | |
US1939467A (en) | Method of making bearings | |
GB1463464A (en) | ||
US2693121A (en) | Method of making composite aluminum-lined steel-backed bearing material | |
GB2080336A (en) | Method of producing multi-layer sliding material | |
GB741995A (en) | Improvements in or relating to plain bearings | |
US2433903A (en) | Method of making clad metal bodies | |
JPH0323624B2 (en) | ||
US3832147A (en) | Composite article comprising three dissimilar metals | |
US3325282A (en) | Method of forming a zinc-aluminum coating on a ferrous base | |
JPS5844140B2 (en) | Composite sliding material | |
US2423857A (en) | Method of treating composite metal | |
US3384950A (en) | Method of making bearing material | |
US3406445A (en) | Method for coating steel with white metal | |
US2771409A (en) | Method of making grid bearings | |
GB1275431A (en) | A metal laminate suitable for use in the manufacture of plain bearings |