GB2595745A - Active electrode material

Info

Publication number: GB2595745A
Application number: GB2011681.0A
Authority: GB
Inventors: Groombridge Alexander; Zhang Wanwei; Slater Peter; Wu Jianshen
Original assignee: Echion Technologies Ltd
Current assignee: Echion Technologies Ltd
Priority date: 2019-10-18
Filing date: 2020-07-28
Publication date: 2021-12-08
Anticipated expiration: 2040-07-28
Also published as: GB2595745B; GB202011681D0

Abstract

A phosphorus niobium oxide active electrode material has the composition M1aPx-aM2bNb9-bO25-c-dQd, wherein: M1 is selected from Na, K, Mg, Ca, Sr, Y, Ti, Zr, Hf, V, Nb, Ta, Cr, Mo, W, Mn, Fe, Co, Ni, Cu, Zn, B, Al, Ga, Si, Ge, Sn, Bi, Sb, and mixtures thereof; M2 is selected from Na, K, Mg, Ca, Sr, Y, Ti, Zr, Hf, V, Ta, Cr, Mo, W, Mn, Fe, Co, Ni, Cu, Zn, B, Al, Ga, Si, Ge, Sn, Bi, P, Sb, and mixtures thereof; Q is selected from F, Cl, Br, I, N, S, Se, and mixtures thereof; 0 ≤ a ≤ 0.5; 0 ≤ b ≤ 2; -0.5 ≤ c ≤ 1.25; 0 ≤ d ≤ 5; 1 ≤ x ≤ 2; and one or more of a, b, c, and d does not equal 0; with the proviso that if M1 consists of Nb and if M2 consists of P then c is > 0. The electrochemical properties of a PNb9O25-based material are improved by cationic substitution for P and/or Nb, anionic substitution for O, and/or by providing an oxygen deficiency or excess. Such materials are of interest as active electrode materials, especially anode materials, in lithium-ion or sodium-ion batteries, since they have significantly improved capacity retention at high C-rates compared to PNb9O25.

Description

Active electrode material

Field of the Invention

The present invention relates to active electrode materials and to methods for the manufacture of active electrode materials. Such materials are of interest as active electrode materials in lithium-ion or sodium-ion batteries, for example as anode materials for lithium-ion batteries.

Background

Lithium-ion (Li-ion) batteries are a commonly used type of rechargeable battery with a global market predicted to grow to $200bn by 2030. Li-ion batteries are the technology of choice for electric vehicles that have multiple demands across technical performance to environmental impact, providing a viable pathway for a green automotive industry.

A typical lithium-ion battery is composed of multiple cells connected in series or in parallel. Each individual cell is usually composed of an anode (negative polarity electrode) and a cathode (positive polarity electrode), separated by a porous, electrically insulating membrane (called a separator), immersed into a liquid (called an electrolyte) enabling lithium ions transport.

In most systems, the electrodes are composed of an electrochemically active material -meaning that it is able to chemically react with lithium ions to store and release them reversibly in a controlled manner -mixed if necessary with an electrically conductive additive (such as carbon) and a polymeric binder. A slurry of these components is coated as a thin film on a current collector (typically a thin foil of copper or aluminium), thus forming the electrode upon drying.' In the known Li-ion battery technology, the safety limitations of graphite anodes upon battery charging is a serious impediment to its application in high-power electronics, automotive and industry. Among a wide range of potential alternatives proposed recently, lithium titanate (LTO) and mixed niobium oxides are the main contenders to replace graphite as the active material of choice for high power, fast-charge applications.

Batteries relying on a graphitic anode are fundamentally limited in terms of charging rate. Under nominal conditions, lithium ions are inserted into the anode active material upon charging. When charging rate increases, typical graphite voltage profiles are such that there is a high risk that overpotentials lead to the potential of sites on the anode to become < 0 V vs. Li/Li+, which leads to a phenomenon called lithium dendrite electroplating, whereby lithium ions instead deposit at the surface of the graphite electrode as lithium metal. This leads to irreversible loss of active lithium and hence rapid capacity fade of the cell. In some cases, these dendritic deposits can grow to such large sizes that they pierce the battery separator and lead to a short-circuit of the cell. This can trigger a catastrophic failure of the cell leading to a fire or an explosion. Accordingly, the fastest-charging batteries having graphitic anodes are limited to charging rates of 5-7 C, but often much less.

Lithium ntanate (LTO) anodes do not suffer from dendrite electroplating at high charging rate thanks to their high potential (1.6 V vs. Li/Li+), and have excellent cycle life as they do not suffer from significant volume expansion of the active material upon intercalation of Li ions due to their accommodating 3D crystal structure. LTO cells are typically regarded as high safety cells for these two reasons. However, LTO is a relatively poor electronic and ionic conductor, which leads to limited capacity retention at high rate and resultant power performance, unless the material is nanosized to increase specific surface area, and carbon-coated to increase electronic conductivity. This particle-level material engineering increases the porosity and specific surface area of the active material, and results in a significantly lower achievable packing density in an electrode. This is significant because it leads to low density electrodes and a higher fraction of electrochemically inactive material (e.g. binder, carbon additive), resulting in much lower gravimetric and volumetric energy densities.

A key measure of anode performance is the electrode volumetric capacity (mAh/cm3), that is, the amount of electric charges (that is lithium ions) that can be stored per unit volume of the anode. This is an important factor to determine the overall battery energy density on a volumetric basis (Wh/L) when combined with the cathode and appropriate cell design parameters. Electrode volumetric capacity can be approximated as the product of electrode density (g/ce), active material specific capacity (mAh/g), and fraction of active material in the electrode. LTO anodes typically have relatively low specific capacities (c. 165 mAh/g, to be compared with c. 330 mAh/g for graphite) which, combined with their low electrode densities (typically <2.0 g/crns) and low active material fractions (<90%) discussed above, lead to very low volumetric capacities (<300 mAh/cm3) and therefore low battery energy density and high $/kVVh cost in various applications. As a result, LTO batteries/cells are generally limited to specific niche applications, despite their long cycle life, fast-charging capability, and high safety.

Mixed niobium oxide structures based on phosphorus niobium oxides have been of recent interest for use in Li-ion cells. The crystal structure of PNb90" was first reported by Roth et al in 1965,2 consisting of a Wadsley-Roth Re03shear structure with corner shared NbOs octahedra connected into blocks in a 3x3r0 arrangement. The blocks are connected to adjacent blocks by edge sharing and corner-shared PO4 tetrahedra. A similar structure with a slight distortion due to excess P was reported in 1994 by Xu et al (P2,Nb100").3 Electrochemical insertion and use in Li ion cells was first reported by Patoux et al in 2002, and more recently by others in 2020.4" This material has a higher theoretical and practical capacity (>200 mAh/g), low nominal voltage (<1.6 V vs Li/Lr), and 3 orders of magnitude higher Li ion diffusion coefficient (10-9-102 cr02 S-1) than LTO. Due to the much higher Li-ion diffusion coefficients, these materials no longer have to be highly nanostructured and engineered, as is necessary for use of LTO cells at high charge and discharge current. This also means commercial electrodes can be readily manufactured, with low quantities of additives and binders, reaching high electrode densities. This allows for higher volumetric energy densities and reduced $/kVVh cell cost.

However, due to the nature of PNb902., as a composite oxide material, it is not electronically conductive enough to allow for efficient charging and discharging in Li-ion cells for commercial use, resulting in excess impedance. In addition, improvements can still be made in Li ion capacity, cycling efficiency (at cycle life), and in tuning the voltage profile of charge and discharge. Making these improvements as described herein without the need for extensive nanoscale or particle-level engineering, and without coatings, is an important step to low-cost battery materials for mass market uptakes. If these improvements are not addressed, then there is excess electrical resistance in a resultant device and lower energy densities, leading to increased polarisation, reduced power densities, lower energy efficiencies, and increased cost. Accordingly, there remains a need to further improve the properties of PNIV.325 and closely related structures for use in lithium-ion batteries.

Summary of the Invention

In a first aspect, the invention provides a phosphorus niobium oxide active electrode material with the composition MlaPx-.M2bNbs-b025-c-dQd, wherein: M1 is selected from Na, K, Mg, Ca, Sr, Y, Ti, Zr, Hf, V, Nb, Ta, Cr, Mo, W, Mn, Fe, Co, Ni, Cu, Zn, B, Al, Ga, Si, Ge, Sn, Bi, Sb, and mixtures thereof; M2 is selected from Na, K, Mg, Ca, Sr, Y, Ti, Zr, Hf, V, Ta, Cr, Mo, W, Mn, Fe, Co, Ni, Cu, Zn, B, Al, Ga, Si, Ge, Sn, Bi, P, Sb, and mixtures thereof; Q is selected from F, Cl, Br, I, N, S, Se, and mixtures thereof; 0 a 0.5; 0 b 5 2; -0.5 c 5 1.25; 0 d 5; 1 x 5 2; one or more of a, b, c, and d does not equal 0; with the proviso that if M1 consists of Nb and if M2 consists of P then c is > 0.

It will be understood that the composition of the active electrode material does not correspond to stoichiometric PNI39025. The present inventors have found that by modifying materials including PNb9025 by either incorporating further cations (M1 and/or M2) to form mixed cation active electrode materials, and/or by creating an induced oxygen deficiency or excess, and/or by forming mixed anion active electrode materials (comprising 0 and 0) the resulting material has improved electrochemical properties, and in particular improved electrochemical properties when used as an anode material. For instance, the inventors have found that materials according to the invention have a significantly improved capacity retention at high C-rates compared to PNI39025, as shown by the present examples. This is an important result in demonstrating the advantages of the material of the invention for use in batteries designed for fast charge/discharge.

The active electrode materials of the invention are particularly useful in electrodes, preferably for use in anodes for lithium-ion or sodium-ion batteries. Therefore, a further implementation of the invention is a composition comprising the active electrode material of the first aspect and at least one other component; optionally wherein the at least one other component is selected from a binder, a solvent, a conductive additive, an additional active electrode material, and mixtures thereof Such a composition is useful for fabricating an electrode. A further implementation of the invention is an electrode comprising the active electrode material of the first aspect in electrical contact with a current collector. A further implementation of the invention is an electrochemical device comprising an anode, a cathode, and an electrolyte disposed between the anode and the cathode, wherein the anode comprises an active electrode material according to the first aspect; optionally wherein the electrochemical device is a lithium-ion battery or a sodium-ion battery.

In a second aspect, the invention provides a method of making an active electrode material as defined by the first aspect, the method comprising steps of: providing one or more precursor materials; mixing said precursor materials to form a precursor material mixture; and heat treating the precursor material mixture in a temperature range from 400 °C -1350 °C or 800 -1350 °C, thereby providing the active electrode material. This represents a convenient and efficient method of making the active electrode material of the first aspect.

The invention includes the combination of the aspects and features described herein except where such a combination is clearly impermissible or expressly avoided.

Summary of the Figures

The principles of the invention will now be discussed with reference to the accompanying figures in which: Figure 1: Powder XRD of Sample 1 -9.

Figure 2: TGA of Sample 2.

Figure 3: A visualisation of the reference PNI39025 unit cell Figure 4: Galvanostatic lithiation/delithiation curves for Sample 1 and 7 at a rate of C/10 for their first lithiation and de-lithiation cycles, between 1.0-3.0 V. Figure 5: Galvanostatic delithiation curves for Sample 1 and 7 at a rate of 10C, between 1.0-3.0 V. Lithiation curve shown at C/5.

Figure 6: A plot of the derivative of capacity versus voltage (dQ/dV) for Sample 1 and 7 at a rate of C/10 for their second lithiation and de-lithiation cycles, between 1.0 -3.0 V.

Detailed Description of the Invention

Aspects and embodiments of the present invention will now be discussed with reference to the accompanying figures. Further aspects and embodiments will be apparent to those skilled in the art. All documents mentioned in this text are incorporated herein by reference.

The term "mixed niobium oxide" (MNO) refers to an oxide comprising niobium and at least one other cation. MNO materials have a high redox voltage vs. Lithium >0.8V, enabling safe and long lifetime operation, crucial for fast charging battery cells. Moreover, niobium cations can have two redox reactions per atom, resulting in higher theoretical capacities than, for example, LTO. The material described herein is derived from the base structure of PN139025 (also the isostructural P2 5Nb18050, and other isostructures where PxNbiaOso, and 2 < x < 4),3 which are phosphorus niobium oxide (PNO) materials.

PN139025 may be considered to have a Re03-derived MO3, crystal structure. Preferably, the PNO has a Wadsley-Roth crystal structure or a Phosphate Bronze crystal structure. Wadsley-Roth crystal structures are considered to be a crystallographic off-stoichiometry of the MOs (Re03) crystal structure containing crystallographic shear, with simplified formula of M03. As a result, these structures typically contain [MOs] octahedral subunits in their crystal structure alongside others. The PNO materials with these structures are believed to have advantageous properties for use as active electrode materials, e.g. in lithium-ion batteries.

The open tunnel-like MO3 crystal structure of PNO materials also makes them ideal candidates for having high capacity for Li ion storage and high rate intercalation/de-intercalation. The crystallographic offstoichiometry present in the PNO structure causes the Wadsley-Roth crystallographic superstructure. These superstructures, compounded by other qualities such as the Jahn-Teller effect and enhanced crystallographic disorder by making use of multiple mixed cations, stabilise the crystal and keep the tunnels open and stable during intercalation, enabling extremely high rate performance due to high Li-ion diffusion rates (reported as 10-9-1010 cm251).5 The crystal formulae of PNb9025 can be described as having a 3x3xec. crystallographic block structure, with corner-sharing tetrahedra, as shown in Fig. 3. The crystal formulae of P2Ab18O50 can be described as an isostructural phase to PNI39025 with slight differences in some bond lengths due to additional P (P-O and Nb3-02, Nb2-02 for example). This has previously been reported as a Phosphate Bronze materia1,3 but it and related theorised structures (i.e. P2_4Nbi8050) are considered as a distorted WadsleyRoth crystal structure herein.

The total crystal composition of the materials described herein are preferably charge neutral and thermodynamically favourable to follow the above description. Structures deficient in their oxygen content through introduction of oxygen vacancy defects are preferable when reducing the material's electrical resistance such that MO y becomes Mx0y_.5. Structures that have had cations (Le. P and Nb) or anions (Le. 0) substituted may have been so with matching valency (Le. a 5+ cation for equal proportions of a 4+ and 6+ cation) or with unmatched valency, which can induce oxygen deficiency or excess if substitution takes place at equivalent crystal sites (e.g. Alo osPo 95N bs024 95 for deficiency, or Moo osPo 9sN139025 025 for excess). Substitution may also take place at different crystal sites, such as interstitial sites.

The crystal structure of a material may be determined by analysis of X-ray diffraction (XRD) patterns, as is widely known. For instance, XRD patterns obtained from a given material can be compared to known XRD patterns to confirm the crystal structure, e.g. via public databases such as the ICDD crystallography database. Rietveld analysis can also be used to determine the crystal structure of materials, in particular for the unit cell parameters. Therefore, the active electrode material may have a VVadsley-Roth or Phosphorus Bronze crystal structure, as determined by X-ray diffraction, preferably a Wadsley-Roth crystal structure.

Preferably, the crystal structure of the active electrode material, as determined by X-ray diffraction, corresponds to the crystal structure of one or more of PNID9025, VNI39025, or P2 5N b18050, or one or more of PNb9025 or P25Nbi8050; or most preferably PN139025. The crystal structure of PNb9025 may be found at ICDD crystallography database entry JCPDS 81-1304. The crystal structure of VNb9025 may be found at JCPDS 49-0289. The crystal structure of P2 5Nbi8Oso may be found at ICDD 01-082-0081. The active electrode material may have unit cell parameters a, b, and c wherein a is 15.4-15.8 A preferably 15.5- 15.7 A, b is 15.4-15.8 A preferably 15.5-15.7 A, and c = 3.6-4.0 A preferably 3.7-3.9 A. Most preferably a = b. The active electrode material have unit cell parameters a, p, and y each being about 90°, preferably wherein a = 3 = y = 90°. Unit cell parameters may be determined by X-ray diffraction. The active electrode material may have a crystallite size of 10-100 nm, preferably 30-60 nm, determined according to the Scherrer equation.

Here the term 'corresponds' is intended to reflect that peaks in an X-ray diffraction pattern may be shifted by no more than 0.5 degrees (preferably shifted by no more than 0.25 degrees, more preferably shifted by no more than 0.1 degrees) from corresponding peaks in an X-ray diffraction pattern of the material listed above.

The phosphorus niobium oxide has the composition Ml.P.,M2bNbs-b025,,dQd, wherein: M1 is selected from Na, K, Mg, Ca, Sr, Y, Ti, Zr, Hf, V, Nb, Ta, Cr, Mo, W, Mn, Fe, Co, Ni, Cu, Zn, B, Al, Ga, Si, Ge, Sn, Bi, Sb, and mixtures thereof; M2 is selected from Na, K, Mg, Ca, Sr, Y, Ti, Zr, Hf, V, Ta, Cr, Mo, W, Mn, Fe, Co, Ni, Cu, Zn, B, Al, Ga, Si, Ge, Sn, Bi, P, Sb, and mixtures thereof; Q is selected from F, Cl, Br, I, N, S, Se, and mixtures thereof; 0 5 a 5 0.5; 05 b 5 2; -0.5 5 c 5 1.25; 0 d 5 5; 1 x 5 2; one or more of a, b, c, and d does not equal 0; with the proviso that if M1 consists of Nb and if M2 consists of P then c is > 0.

By 'and mixtures thereof, it is intended that Ml, M2, or Q may each represent two or more elements from their respective lists. An example of such a material is Tioo5M0005P0.90Nb9025. Here, M1 represents TiaMos, (where a' + a" = a), a=0.1, b=0, c=0, and d=0. Another example of such a material is AID osPo osTio 22sMoo.22sNba 55024 95. Here, M1 represents Ala, M2 represents Tib*Mob-(where b' + b" = b), a=0.05, b=0.45, c=0.05, and d=0.

The precise values of a, b, c, d within the ranges defined may be selected to provide a charge balanced, or substantially charge balanced, crystal structure. Additionally or alternatively, the precise values of a, b, C, d within the ranges defined may be selected to provide a thermodynamically stable, or thermodynamically metastable, crystal structure.

When exchange of the cations or anions in the structure (La P, Nb, 0) have taken place without preserving the initial valency, this can give rise to both oxygen deficiency and excess. For example, a material that substitutes P5+ for Mo6+ to some extent will demonstrate minor oxygen excess (i.e. P205 vs Mo03), whereas substitution of P5+ for Al3+ will show a minor oxygen deficiency (i.e. P205 vs A1203).

Oxygen deficiency can also be induced through thermal treatment in inert or reducing conditions, which results in induced oxygen vacancy defects in the structure.

M1 is a cation which substitutes for P in the crystal structure. M1 may be selected from Ti, Zr, Hf, V, Nb, Ta, Cr, Mo, W, Mn, Fe, Co, Ni, Cu, Zn, B, Al, Ga, Si, Ge, Sn, Bi, Sb, and mixtures thereof; or Ti, Zr, Hf, Cr, Mo, W, B, Al, Ga, Bi, Sb, and mixtures thereof; or Ti, Mo, Al, B, and mixtures thereof Preferably M1 is not Nb. Preferably, M1 is not Na. M1 may have a different valency than P. This gives rise to oxygen deficiency or excess. Preferably, M1 has a lower valency than P5+. This gives rise to oxygen deficiency, i.e. the presence of oxygen vacancies providing the advantages discussed herein. M1 preferably has a different ionic radius than P5', most preferably a larger ionic radius. This gives rise to changing unit cell size and local distortions in crystal structure, providing the advantages discussed herein.

Ionic radii referred to herein are the Shannon ionic radii (available at reference 7) at the coordination and valency that the ion would be expected to adopt in the crystal structure of the active electrode material. For example, the crystal structure of PNb9025 includes Nb5+0, octahedra and P504 tetrahedra.

The amount of M1 is defined by a, meeting the criterion 0 5 a 5 0.5. a may be 0 5 a 5 0.3, preferably 0 5 a 5 0.2. In each of these cases a may be > 0.

M2 is a cation which substitutes for Nb in the crystal structure. M2 may be selected from Ti, Zr, Hf, V, Ta, Cr, Mo, W, Mn, Fe, Co, Ni, Cu, Zn, B, Al, Ga, Si, Ge, Sn, Bi, P, Sb, and mixtures thereof; or Ti, Zr, Hf, Cr, Mo, W, V, Ta, and mixtures thereof; or Ti, Mo, and mixtures thereof. Preferably, M2 is not P. Preferably, M2 is not Na. M2 may have a different valency than Nb5+. This gives rise to oxygen deficiency or excess. Preferably, M2 has a lower valency than Nb51-. This gives rise to oxygen deficiency, i.e. the presence of oxygen vacancies providing the advantages discussed herein. M2 preferably has a different ionic radius than Nb54, most preferably a larger ionic radius. This gives rise to changing unit cell size and local distortions in crystal structure, providing the advantages discussed herein.

The amount of M2 is defined by b, meeting the criterion 0 b 5 2. b may be 0 b 5 1.5, preferably 0 b 1. In each of these cases b may be > O. Preferably, at least one of a and b is > 0. Both of a and b can be > 0.

c reflects the oxygen content of the active electrode material. When c is greater than 0, it forms an oxygen-deficient material, i.e. the material has oxygen vacancies. Such a material would not have precise charge balance without changes to cation oxygen state, but is considered to be "substantially charge balanced" as indicated above. Alternatively, c may equal 0, in which it is not an oxygen-deficient material. c may be below 0, which is a material with oxygen-excess. c may be -0.25 5 c 5 1.25. Preferably c is 0 c 5 1.25. Optionally, if a = b = 0 then c 0; preferably if a = b = 0 then c > 0.

When c is 1.25, the number of oxygen vacancies is equivalent to 5% of the total oxygen in the crystal structure. c may be greater than 0.0125 (0.05% oxygen vacancies), greater than 0.025(0.1% oxygen vacancies), greater than 0.05 (0.2% oxygen vacancies), or greater than 0.125 (0.5% oxygen vacancies). c may be between 0 and 1 (4% oxygen vacancies), between 0 and 0.75 (3% oxygen vacancies), between 0 and 0.5 (2% oxygen vacancies), or between 0 and 0.25(1% oxygen vacancies). For example, c may satisfy 0.01 5 c 1.25. When the material is oxygen-deficient, the electrochemical properties of the material may be improved, for example, resistance measurements may show improved conductivity in comparison to equivalent non-oxygen-deficient materials. As will be understood, the percentage values expressed herein are in atomic percent.

The invention relates to phosphorus niobium oxides comprising oxygen vacancies (oxygen-deficient phosphorus niobium oxides), or having oxygen excess. Oxygen vacancies may be formed in a phosphorus niobium oxide by the sub-valent substitution of a base material as described above, and oxygen excess may be formed in a phosphorus niobium oxide by substitution for increased valency. Oxygen vacancies may also be formed by heating a phosphorus niobium oxide under reducing conditions, optionally without cation substitution. Therefore, the phosphorus niobium oxide active electrode material may have the composition P.Nbp.025.c.dQd where x, c, d, and Q are as defined herein.

The amount of oxygen vacancies and excess may be expressed relative to the total amount of oxygen in the base material, i.e. the amount of oxygen in the un-substituted material (e.g. PNI39025) or the material before heating under reducing conditions.

A number of methods exist for determining whether oxygen vacancies are present in a material. For example, Thermogravimetric Analysis (TGA) may be performed to measure the mass change of a material when heated in air atmosphere. A material comprising oxygen vacancies can increase in mass when heated in air due to the material "re-oxidising" and the oxygen vacancies being filled by oxide anions. The magnitude of the mass increase may be used to quantify the concentration of oxygen vacancies in the material, on the assumption that the mass increase occurs entirely due to the oxygen vacancies being filled. It should be noted that a material comprising oxygen vacancies may show an initial mass increase as the oxygen vacancies are filled, followed by a mass decrease at higher temperatures if the material undergoes thermal decomposition. Moreover, there may be overlapping mass loss and mass gain processes, meaning that some materials comprising oxygen vacancies may not show a mass gain (and sometimes not a mass loss or gain) during TGA analysis.

Other methods of determining whether oxygen vacancies are present include electron paramagnetic resonance (EPR), X-ray photoelectron spectroscopy (XPS, e.g. of oxygen is and/or and of cations in a mixed oxide), X-ray absorption near-edge structure (XANES, e.g. of cations in a mixed metal oxide), and TEM (e.g. scanning TEM (STEM) equipped with high-angle annular darkfield (HAADF) and annular bright-field (ABF) detectors). The presence of oxygen vacancies can be qualitatively determined by assessing the colour of a material relative to a non-oxygen-deficient sample of the same material, indicative of changes to its electronic band structure through interaction with light. For example, stoichiometric PNI39025 has a white or off-white colour whereas oxygen-deficient PN139024 990 has a light blue colour. The presence of vacancies can also be inferred from the properties, e.g. electrical conductivity, of a stoichiometric material compared to those of an oxygen-deficient material.

When d >0, additional anions Q are introduced into the phosphorus niobium oxide. Due to their differing electronic structure (i.e. F-vs 02-), and differing ionic radii (6-coordinate 02-= 1.40 A, 6-coordinate F- 1.33 A) they may improve electrochemical performance in the active material! This is due to altering unit cell characteristics with differing ionic radii allowing for improved Li ion capacity, or improved Coulombic efficiencies by improving reversibility. They may additionally improve electrical conductivity as for oxygen vacancy defects, or sub-valent cation substitutions, by altering the electronic structure of the crystal (i.e. doping effects). d may be 0 d 2.5, or 0 d 1. In each of these cases d may be > 0. Q may be selected from F, Cl, N, S, and mixtures thereof; or F, N, and mixtures thereof; or Q is N. Optionally d = 0, in which case the material has the composition MlaPx_aM2bNlas-1,025 c where Ml, M2, a, b, c, and x are as defined herein. Advantageously, materials where d = 0 are free from anion Q and may be easier to synthesise.

x reflects the amount of phosphorus in the material, meeting the criterion 1 x 5 2. x may be 1 x 1.25.

Preferably, x = 1. When x = 1 the composition is based on the crystal structure of PNID9025.

It will be understood that the discussion of the variables of the composition (M1, M2, Q, a, b, c, d, and x) is intended to be read in combination. For example, preferably M1 is selected from Ti, Zr, Hf, V, Nb, Ta, Cr, Mo, W, Mn, Fe, Co, Ni, Cu, Zn, B, Al, Ga, Si, Ge, Sn, Bi, Sb, and mixtures thereof and M2 is selected from Ti, Zr, Hf, V, Ta, Cr, Mo, W, Mn, Fe, Co, Ni, Cu, Zn, B, Al, Ga, Si, Ge, Sn, Bi, P, Sb, and mixtures thereof. M1 may be selected from Ti, Zr, Hf, Cr, Mo, W, B, Al, Ga, Bi, Sb, and mixtures thereof and M2 may be selected from Ti, Zr, Hf, Cr, Mo, W, V, Ta, and mixtures thereof. M1 may be selected from Ti, Mo, Al, B, and mixtures thereof and M2 may be selected from Ti, Mo, and mixtures thereof. M1 is preferably not Nb and M2 is preferably not P. M1 and M2 are preferably not Na. M1 and M2 may be different. a may be 0 5 a 5 0.3 and b may be 0 b 5 1.5. Preferably 0 5 a 5 0.2 and 0 b 1. In each of these cases a and/or b may be > 0.

For example, the phosphorus niobium oxide active electrode material may have the composition M1aPx_aM2bNbs-b025,_dQd, wherein: M1 is selected from Ti, Zr, Hf, V, Ta, Cr, Mo, W, Mn, Fe, Co, Ni, Cu, Zn, B, Al, Ga, Si, Ge, Sn, Bi, Sb, and mixtures thereof; M2 is selected from Ti, Zr, Hf, V, Ta, Cr, Mo, W, Mn, Fe, Co, Ni, Cu, Zn, B, Al, Ga, Si, Ge, Sn, Bi, Sb, and mixtures thereof; Q is selected from F, Cl, N, 5, and mixtures thereof; 0 5 a 5 0.3; 0 b 1.5; -0.25 5 c5 1.25; 0 5 d 5 2.5; 1 5 x 5 1.25; one or more of a, b, c, and d does not equal 0.

For example, the phosphorus niobium oxide active electrode material may have the composition MlaPi_aM2bN139-b025-e-dQd, wherein: M1 is selected from Ti, Zr, Hf, V, Ta, Cr, Mo, W, Mn, Fe, Co, Ni, Cu, Zn, B, Al, Ga, Si. Ge, Sn, Bi, Sb, and mixtures thereof; M2 is selected from Ti, Zr, Hf, V, Ta, Cr, Mo, W, Mn, Fe, Co, Ni, Cu, Zn, B, Al, Ga, Si, Ge, Sn, Bi, Sb, and mixtures thereof; Q is selected from F, N, and mixtures thereof; 0 5 a 5 0.3; 0 b 5 1.5; 0 c 5 1.25; 0 d 5 2.5; one or more of a, b, c, and d does not equal 0.

The active electrode material may further comprise Li and/or Na. For example, Li and/or Na may enter the crystal structure when the active electrode material is used in a metal-ion battery electrode.

The active electrode material is preferably in particulate form. The material may have a D50 particle diameter in the range of 0.1-100 pm, or 0.5-50 pm, or 1-20 pm. These particle sizes are advantageous because they are easy to process and fabricate into electrodes. Moreover, these particle sizes avoid the need to use complex and/or expensive methods for providing nanosized particles. Nanosized particles (e.g. particles having a D50 particle diameter of 100 nm or less) are typically more complex to synthesise and require additional safety considerations.

The active electrode material may have a D10 particle diameter of at least 0.05 pm, or at least 0.1 pm, or at least 0.5 pm, or at least 1 pm. By maintaining a Dio particle diameter within these ranges, the potential for parasitic reactions in a Li ion cell is reduced from having reduced surface area, and it is easier to process with less binder in the electrode slurry.

The active electrode material may have a D90 particle diameter of no more than 200 pm, no more than 100 pm, no more than 50 pm, or no more than 20 pm. By maintaining a D90 particle diameter within these ranges, the proportion of the particle size distribution with large particle sizes is minimised, making the material easier to manufacture into a homogenous electrode.

The term "particle diameter?' refers to the equivalent spherical diameter (esd), i.e. the diameter of a sphere having the same volume as a given particle, where the particle volume is understood to include the volume of any intra-particle pores. The terms "Do" and "Dn particle diameter" refer to the diameter below which n% by volume of the particle population is found, i.e. the terms "D50" and "Dso particle diameter" refer to the volume-based median particle diameter below which 50% by volume of the particle population is found. Where a material comprises primary crystallites agglomerated into secondary particles, it will be understood that the particle diameter refers to the diameter of the secondary particles.

Particle diameters can be determined by laser diffraction. For example, particle diameters can be determined in accordance with ISO 13320:2009.

The active electrode material may have a BET surface area in the range of 0.1-100 m2/g, or 0.5-50 m2/g, or 1-20 m2/g. In general, a low BET surface area is preferred in order to minimise the reaction of the active electrode material with the electrolyte, e.g. minimising the formation of solid electrolyte interphase (SEI) layers during the first charge-discharge cycle of an electrode comprising the material. However, a BET surface area which is too low results in unacceptably low charging rate and capacity due to the inaccessibility of the bulk of the active electrode material to metal ions in the surrounding electrolyte.

The term "BET surface area" refers to the surface area per unit mass calculated from a measurement of the physical adsorption of gas molecules on a solid surface, using the Brunauer-Emmett-Teller theory. For example, BET surface areas can be determined in accordance with ISO 9277:2010.

The specific capacity/reversible delithiation capacity of the active electrode materials may be 180 mAh/g or more, 190 mAh/g or more, up to about 200 mAh/g or more. Here, specific capacity is defined as that measured in the 2nd cycle of a half cell galvanostatic cycling test at a rate of 0.1C with a voltage window of 1.0-3.0V vs Li/Lie in a half cell. It may be advantageous to provide materials having a high specific capacity, as this can provide improved performance in an electrochemical device comprising the active electrode material.

When formulated or coated as an electrode according to the below description (optionally with conductive carbon additive and binder materials), the sheet resistance of the active electrode materials may be 750 0 per square or less, more preferably 675 0 per square or less. Sheet resistance can be a useful proxy measurement of the electronic conductivity of such materials. It may be advantageous to provide materials having a suitably low sheet resistance, as this can provide improved performance in an electrochemical device comprising the active electrode material.

The active electrode material may have a lithium diffusion rate greater than 10-14 cm2 5-1, or more preferably greater than 10-12 cm2 -1.

It may be advantageous to provide materials having a suitably high lithium diffusion rate, as this can provide improved performance in an electrochemical device comprising the active electrode material.

The active electrode material may be able to form composite electrodes with a suitable binder and conductive additive according to the below description to provide an electrode density of 2.5 g/cm3 or more after calendaring. This enables a composite electrode with an electrode porosity (calculated by the measured electrode density / average of the true density of each component) in the range of 30-40%, in-line with industrial requirements for high energy and high power cells. For example, electrode densities of up to 3.2 g/cm3 have been achieved. It may be advantageous to provide materials having such an electrode density, as this can provide improved performance in an electrochemical device comprising the active electrode material. Specifically, when the electrode density is high, high volumetric capacities can be achieved, as gravimetric capacity X electrode density X active electrode material fraction = volumetric capacity.

Initial coulombic efficiency has been measured as the difference in the lithiation and de-lithiafion capacity on the 1s' charge/discharge cycle at C/10 in a half-cell. The initial coulombic efficiency of the active electrode material may be greater than 90%, or greater than 92.5%, or greater than 95%. It may be advantageous to provide materials having a suitably high initial coulombic efficiency, as this can provide improved performance in an electrochemical device comprising the active electrode material.

The invention also provides a composition comprising the active electrode material of the first aspect of the invention and at least one other component, optionally wherein the at least one other component is selected from a binder, a solvent, a conductive additive, an additional active electrode material, and mixtures thereof. Such a composition is useful for preparing an electrode, e.g. an anode for a lithium-ion battery.

The invention also provides an electrode comprising the active electrode material of the first aspect of the invention in electrical contact with a current collector. The electrode may form part of a cell. The electrode may form an anode as part of a lithium-ion battery.

The invention also provides the use of the active electrode material of the first aspect of the invention in an anode for a metal-ion battery, optionally wherein the metal-ion battery is a lithium-ion battery.

A further implementation of the invention is an electrochemical device comprising an anode, a cathode, and an electrolyte disposed between the anode and the cathode, wherein the anode comprises an active electrode material according to the first aspect of the invention; optionally wherein the electrochemical device is a lithium-ion battery or a sodium-ion battery. Preferably, the electrochemical device is a lithium-ion battery having a reversible anode active material specific capacity of greater than 200 mAh/g at 20 mA/g, wherein the battery can be charged and discharged at current densities relative to the anode active material of 200 mA/g or more, or 1000 mA/g or more, or 2000 mA/g or more, or 4000 mA/g or more whilst retaining greater than 70% of the initial cell capacity at 20 mA/g. It has been found that use of the active electrode materials of the first aspect of the invention can enable the production of a lithium-ion battery with this combination of properties, representing a lithium-ion battery that is particularly suitable for use in applications where high charge and discharge current densities are desired. Notably, the examples have shown that active electrode materials according to the first aspect of the invention have excellent capacity retention at high C-rates.

The phosphorus niobium oxide active electrode material may be synthesised by conventional ceramic techniques. For example, the material be made by one or more of solid-state synthesis or sol-gel synthesis. The material may additionally be synthesised by one or more of alternative techniques commonly used, such as hydrothermal or microwave hydrothermal synthesis, solvothermal or microwave solvothermal synthesis, coprecipitafion synthesis, spark or microwave plasma synthesis, combustion synthesis, electrospinning, and mechanical alloying.

The second aspect of the invention provides a method of making an active electrode material as defined by the first aspect, the method comprising steps of: providing one or more precursor materials; mixing said precursor materials to form a precursor material mixture; and heat treating the precursor material mixture in a temperature range from 400 °C -1350 °C or 800 -1350 °C, thereby providing the active electrode material.

To provide an active electrode material comprising element Q the method may further comprise the steps of: mixing the active electrode material with a precursor comprising element Q to provide a further precursor material mixture; and heat treating the further precursor material mixture in a temperature range from 400-1200 °C or 800 -120 °C under reducing conditions, thereby providing the active electrode material comprising element Q. The method may comprise the further step of heat treating the active electrode material or the active electrode material comprising element Q in a temperature range from 400-1350 °C or 800-1350 °C under reducing conditions, thereby introducing oxygen vacancies into the active electrode material. The oxygen vacancies may be in addition to oxygen vacancies already present in the active electrode material, e.g. already present due to sub-valent substitution of P and/or Nb with M1 and/or M2. Alternatively, the oxygen vacancies may be new oxygen vacancies, e.g. if M1 and M2 have the same valency as P and Nb or if M1 and M2 are not present. The presence of oxygen vacancies provides the advantages discussed herein.

The precursor materials may include one or more metal oxides, metal hydroxides, metal salts or ammonium salts. For example, the precursor materials may include one or more metal oxides or metal salts of different oxidation states and/or of different crystal structure. Examples of suitable precursor materials include but are not limited to: Nb205, Nb(OH)5, Niobic Acid, NbO, Ammonium Niobate Oxalate, NH4H2PO4, (NH4)2PO4, (NH4)3PO4, P205, H3P03, Ta205, W03, Zr02, Ti02, Mo03, V205, Zr02, CuO, ZnO, A1203, K20, KOH, CaO, Ge02, Ga203, Sn02, Co°, Co203, Fe203, Fe304, MnO, Mn02, NiO, Ni203, H31303, ZnO, and MgO. The precursor materials may not comprise a metal oxide, or may comprise ion sources other than oxides. For example, the precursor materials may comprise metal salts (e.g. NO3-, SO3-) or other compounds (e.g. oxalates). For the substitution of the oxygen anion with other electronegative anions Q, the precursors comprising element Q may include one or more organic compounds, polymers, inorganic salts, organic salts, gases, or ammonium salts. Examples of suitable precursor materials comprising element 0 include but are not limited to: melamine, NH4HCO3, NH3, NH4F,PVDF, PTFE, NH4C1, NH413r, NH41, Br2, C12,12, ammonium oxychloride amide, and hexamethylenetetramine.

Some or all of the precursor materials may be particulate materials. Where they are particulate materials, preferably they have a D50 particle diameter of less than 20 pm in diameter, for example from 10 nm to 20 pm. Providing particulate materials with such a particle diameter can help to promote more intimate mixing of precursor materials, thereby resulting in more efficient solid-state reaction during the heat treatment step. However, it is not essential that the precursor materials have an initial particle size of <20 pm in diameter, as the particle size of the one or more precursor materials may be mechanically reduced during the step of mixing said precursor materials to form a precursor material mixture.

The step of mixing the precursor materials to form a precursor material mixture and/or further precursor material mixture may be performed by a process selected from (but not limited to): dry or wet planetary ball milling, rolling ball milling, high energy ball milling, high shear milling, air jet milling, steam jet milling, and/or impact milling. The force used for mixing/milling may depend on the morphology of the precursor materials. For example, where some or all of the precursor materials have larger particle sizes (e.g. a D50 particle diameter of greater than 20 pm), the milling force may be selected to reduce the particle diameter of the precursor materials such that the such that the particle diameter of the precursor material mixture is reduced to 20 pm in diameter or lower. When the particle diameter of particles in the precursor material mixture is 20 pm or less, this can promote a more efficient solid-state reaction of the precursor materials in the precursor material mixture during the heat treatment step.

The step of heat treating the precursor material mixture and/or the further precursor material mixture may be performed for a time of from 1 hour to 24 hours, more preferably from 3 hours to 18 hours. For example, the heat treatment step may be performed for 1 hour or more, 2 hours or more, 3 hours or more, 6 hours or more, or 12 hours or more. The heat treatment step may be performed for 24 hours or less, 18 hours or less, 16 hours or less, or 12 hours or less.

The step of heat treating the precursor material mixture may be performed in a gaseous atmosphere, preferably air. Suitable gaseous atmospheres include: air, N2, Ar, He, 002, CO, 02, H2, NH3 and mixtures thereof. The gaseous atmosphere may be a reducing atmosphere. Where it is desired to make an oxygen-deficient material, preferably the step of heat treating the precursor material mixture is performed in an inert or reducing atmosphere.

The step of heat treating the further precursor material mixture is performed under reducing conditions. Reducing conditions include under an inert gas such as nitrogen, helium, argon; or under a mixture of an inert gas and hydrogen; or under vacuum. Preferably, the step of heat treating the further precursor material mixture comprises heating under inert gas.

The further step of heat treating the active electrode material and/or the active electrode material comprising element Q under reducing conditions may be performed for a time of from 1 hour to 24 hours, more preferably from 3 hours to 18 hours. For example, the heat treatment step may be performed for 1 hour or more, 2 hours or more, 3 hours or more, 6 hours or more, or 12 hours or more. The further step heat treating may be performed for 24 hours or less, 18 hours or less, 16 hours or less, or 12 hours or less. Reducing conditions include under an inert gas such as nitrogen, helium, argon; or under a mixture of an inert gas and hydrogen; or under vacuum. Preferably heating under reducing conditions comprises heating under inert gas.

In some methods it may be beneficial to perform a two-step heat treatment. For example, the precursor material mixture and/or the further precursor material mixture may be heated at a first temperature for a first length of time, follow by heating at a second temperature for a second length of time. Preferably the second temperature is higher than the first temperature. Performing such a two-step heat treatment may assist the solid-state reaction to form the desired crystal structure.

The method may include one or more post-processing steps after formation of the phosphorus niobium oxide active electrode material. In some cases, the method may include a post-processing step of heat treating the phosphorus niobium oxide, sometimes referred to as 'annealing'. This post-processing heat treatment step may be performed in a different gaseous atmosphere to the step of heat treating the precursor material mixture to form the phosphorus niobium oxide. The post-processing heat treatment step may be performed in an inert or reducing gaseous atmosphere. Such a post-processing heat treatment step may be performed at temperatures of above 500 °C, for example at about 900 °C. Inclusion of a post-processing heat treatment step may be beneficial to e.g. form deficiencies or defects in the phosphorus niobium oxide, for example to form oxygen deficiencies; or to carry out anion exchange on the formed phosphorus niobium oxide e.g. N exchange for the 0 anion.

The method may include a step of milling and/or classifying the phosphorus niobium oxide active electrode material (e.g. impact milling, jet milling, steam jet milling, high energy milling, high shear milling) to provide a material with any of the particle size parameters given above.

There may be a step of carbon coating the phosphorus niobium oxide active electrode material to improve its surface electrical conductivity, or to prevent reactions with electrolyte. This is typically comprised of combining the phosphorus niobium oxide with a carbon precursor to form an intermediate material that may comprise milling, preferably high energy milling. Alternatively or in addition, the step may comprise mixing the phosphorus niobium oxide with the carbon precursor in a solvent, such as water, ethanol or THF. These represent efficient methods of ensuring uniform mixing of the phosphorus niobium oxide with the carbon precursor.

It has been found that a carbon precursor comprising polyaromatic sp2 carbon provides a particularly beneficial carbon coating on active electrode materials of the first aspect of the invention. Therefore, the method of making an active electrode material may further comprise the steps of: combining the active electrode material or the active electrode material comprising element Q with a carbon precursor comprising polyaromatic sp2 carbon to form an intermediate material; and heating the intermediate material under reducing conditions to pyrolyse the carbon precursor forming a carbon coating on the active electrode material and introducing oxygen vacancies into the active electrode material.

The intermediate material may comprise the carbon precursor in an amount of up to 25 wt%, or 0.1-15 wt%, or 0.2-8 wt%, based on the total weight of the active electrode material and the carbon precursor. The carbon coating on the active electrode material may be present in an amount of up to 10 wt %, or 0.05-5 wt%, or 0.1-3 wt%, based on the total weight of the active electrode material. These amounts of the carbon precursor and/or carbon coating provide a good balance between improving the electronic conductivity by the carbon coating without overly reducing the capacity of the active electrode material by overly reducing the proportion of the phosphorus niobium oxide. The mass of carbon precursor lost during pyrolysis may be in the range of 30-70 wt%.

The step of heating the intermediate material under reducing conditions may be performed at a temperature in the range of 400-1,200 °C, or 500-1100 °C, or 600-900 °C. The step of heating the intermediate material under reducing conditions may be performed for a duration within the range of 30 minutes to 12 hours, 1-9 hours, or 2-6 hours.

The step of heating the intermediate material under reducing conditions may be performed under an inert gas such as nitrogen, helium, argon; or may be performed under a mixture of an inert gas and hydrogen; or may be performed under vacuum.

The carbon precursor comprising polyaromatic sp2 carbon may be selected from pitch carbons, graphene oxide, graphene, and mixtures thereof. Preferably, the carbon precursor comprising polyaromatic sp2 carbon is selected from pitch carbons, graphene oxide, and mixtures thereof. Most preferably, the carbon precursor comprising polyaromatic sp2 carbon is selected from pitch carbons. The pitch carbons may be selected from coal tar pitch, petroleum pitch, mesophase pitch, wood tar pitch, isotropic pitch, bitumen, and mixtures thereof Pitch carbon is a mixture of aromatic hydrocarbons of different molecular weights. Pitch carbon is a low cost by-product from petroleum refineries and is widely available. The use of pitch carbon is advantageous because pitch has a low content of oxygen. Therefore, in combination with heating the intermediate material under reducing conditions, the use of pitch favours the formation of oxygen vacancies in the phosphorus niobium oxide.

Other carbon precursors typically contain substantial amounts of oxygen. For example, carbohydrates such as glucose and sucrose are often used as carbon precursors. These have the empirical formula Cm(H20)n and thus contain a significant amount of covalently-bonded oxygen (e.g. sucrose has the formula C12H22011 and is about 42 wt% oxygen). The pyrolysis of carbon precursors which contain substantial amounts of oxygen is believed to prevent or inhibit reduction of a phosphorus niobium oxide, or even lead to oxidation, meaning that oxygen vacancies may not be introduced into the phosphorus niobium oxide. Accordingly, the carbon precursor may have an oxygen content of less than 10 wt%, preferably less than 5 wt%.

The carbon precursor may be substantially free of sp3 carbon. For example, the carbon precursor may comprise less than 10wt% sources of sp3 carbon, preferably less than 5 wt% sources of sp3 carbon. Carbohydrates are sources of sp3 carbon. The carbon precursor may be free of carbohydrates. It will be understood that some carbon precursors used in the invention may contain impurities of sips carbon, for

example up to 3 wt%.

The active electrode material of the first aspect of the invention may comprise a carbon coating. Preferably the carbon coating comprises polyaromatic sp2 carbon. Such a coating is formed by pyrolysing a carbon precursor comprising polyaromatic sp2 carbon since the sp2 hybridisation is largely retained during pyrolysis. Typically, pyrolysis of a polyaromatic sp2 carbon precursor under reducing conditions results in the domains of sp2 aromatic carbon increasing in size. Accordingly, the presence of a carbon coating comprising polyaromatic sp2 may be established via knowledge of the precursor used to make the coating. The carbon coating may be defined as a carbon coating formed from pyrolysis of a carbon precursor comprising polyaromatic sp2 carbon. Preferably, the carbon coating is derived from pitch carbons.

The presence of a carbon coating comprising polyaromatic sp2 carbon may also be established by routine spectroscopic techniques. For instance, Raman spectroscopy provides characteristic peaks (most observed in the region 1,000-3,500 cm-1) which can be used to identify the presence of different forms of carbon. A highly crystalline sample of sp3 carbon (e.g. diamond) provides a narrow characteristic peak at -1332 cm-1. Polyaromatic sp2 carbon typically provides characteristic D, G, and 2D peaks. The relative intensity of D and G peaks (ID/IG) can provide information on the relative proportion of sp2 to sp3 carbon. The active electrode material may have an lo/IG ratio as observed by Raman spectroscopy within the range of 0.85-1.15, or 0.90-1.10, or 0.95-1.05.

X-ray diffraction may also be used to provide information on the type of carbon coating. For example, an XRD pattern of a phosphorus niobium oxide with a carbon coating may be compared to an XRD pattern of the uncoated phosphorus niobium oxide and/or to an XRD pattern of a pyrolysed sample of the carbon precursor used to make the carbon coating.

The carbon coating may be semi-crystalline. For example, the carbon coating may provide a peak in an XRD pattern of the active electrode material centred at 20 of about 26° with a width (full width at half maximum) of at least 0.20°, or at least 0.25°, or at least 0.30°.

Examples

The base phosphorus niobium oxide material was synthesised by a solid-state route. In a first step precursor materials (Nb205, NH41-12PO4, h02, Mo03, H3B03, A1203) were mixed in stoichiometric proportions (3509 total) and ball-milled at 550 rpm with a ball to powder ratio of 10:1 for 3 h. The resulting powders were heat treated in an alumina crucible in a muffle furnace in air at Tia = 250 -600 °C for 1 -12 h followed by T1 b = 800 -1350 °C for 4-16 h, providing the desired Wadsley-Roth phase. An additional heat treatment step was also applied in some cases under a N2 atmosphere at 12 = 800-1350 °C for 1 -12 h to result in induced oxygen deficiencies (oxygen vacancies) in the base crystal structure.

For inclusion of anions, there was an additional milling/mixing step with the precursor (NH141-1CO3) prior to heat treatment in a N2 atmosphere at T2 = 400-1200 °C for 1 -12 h. A final de-agglomeration step was utilised by impact milling or jet milling to adjust to the desired particle size distribution where necessary. Specifically, the material was de-agglomerated by impact milling at 20,000 RPM for 10 seconds.

Sample Material Ma Ti b T2 D10 D50 D90 (°C; h) (°C; h) (°C; h) (pm) (01) (pm) 1" PN138025 380; 6 1200; 12 2.7 5.7 11.0 2 PN139024.990" 380; 6 1200; 24 1200; 5 4.0 6.9 11.5 3 Tio osMoo osPosoN109025 380; 6 1200; 12 2.6 5.4 10.0 4 PTio 4sMoo 45Ni:13.i002s 380; 6 1200; 12 3.9 6.8 12.1 PTio 225M00.225N bEI 45025 380; 6 1200; 16 3.7 6.6 11.7 6 Alo osPo osTio 225M00 225N bs 55024 95** 380; 6 1200; 16 4.5 7.9 13.5 7 Ala asPo 95Tio 225M00 225N b8.55024.937** 380; 6 1200; 12 1200; 5 4.2 7.0 11.7 8 PTio 225M00.225N b8 55025-dNd 380; 6 1200; 16 900; 1 5.0 9.0 17.6 9 Bo 05Po asN b9024 95** 380; 6 1200; 12 2.8 6.0 11.3 *Comparative sample -unmodified **Induced oxygen deficiency calculated from TGA mass loss, and inherent oxygen deficiency or excess calculated from cation or anion exchange assuming a charge-balanced structure and site-specific substitution.

Table 1: A summary of the materials synthesised. Particle size distribution has been evaluated by thy powder laser diffraction.

Materials Characterisation The phase purity of samples was analysed using a Rigaku Miniflex powder X-ray diffractometer in 2e range (20-70°) at 1°/min scan rate.

Figure 1 shows the measured XRD diffraction patterns for Samples 1 -9. Diffraction patterns have peaks at the same locations (with some shift due to doping, up to around 0.2°), and match ICDD crystallography database entry JCPDS 81-1304, which corresponds to PNID9025. There is no amorphous background noise and the peaks are sharp and intense. This means that all samples are phase-pure and crystalline, with crystallite size 30-60 nm according to the Scherrer equation and crystal structure matching PN139025. This confirms the presence of a Wadsley-Roth crystal structure.

Sample a = b c [A] a=13 Crystallite [A] size [nrn] References 15.639 3.831 90 90 1* 15.6237 3.8377 90 90 7.4 48 ± 5 2 15.6272 3.8373 90 90 4.0 51 ± 7 3 15.6312 3.8347 90 90 2.6 47 ± 9 4 15.6410 3.8312 90 90 4.2 47 ± 8 15.6319 3.8346 90 90 7.9 51 ± 8 6 15.6279 3.8328 90 90 3.5 35 ± 4 7 15.6225 3.8328 90 90 8.3 40 ± 6 8 15.6032 3.8355 90 90 2.4 49 ± 9 9 15.6292 3.8362 90 90 6.9 48 ± 8 Table 2 A summary table of unit cell parameters for each sample calculated by Rietveld refinement of their powder XRD spectra with software GSASII, and average crystallite size calculated by the Scherrer equation across the spectra. **2 represents the goodness of fit and is a representation of how accurate the Rietveld refinement is, a value <10 supports the accuracy of the data.

Thermogravimetric Analysis (TGA) was performed on some samples using a Perkin Elmer Pyris 1 system in an air atmosphere. Samples were heated from 30°C to 900°C at 5°C/min and held at 900°C for 30 mins, with an air flow of 20 mL/min. TGA was performed on samples 2, and 7 to quantify mass changes on oxidation. The mass gain measured was assumed to correspond to the degree of induced oxygen deficiency present.

Sample Mass gain by TGA analysis [w/w°/.] 2 0.041 7 0.054 Table 3: A summary of TGA analysis carried out on some samples in air Particle Size Distributions were obtained with a Horiba laser diffraction particle analyser for dry powder. Air pressure was kept at 0.3 MPa. The results are set out in Table 1.

Electrochemical Characterisation Li-ion cell charge rate is usually expressed as a "C-rate". A 1C charge rate means a charge current such that the cell is fully charged in 1 h, 10C charge means that the battery is fully charged in 1/10th of an hour (6 minutes). C-rate hereon is defined from the reversible capacity of the anode within the voltage limits applied, i.e. for an anode that exhibits 1.0 mAh cm-2 capacity within the voltage limits of 1.0-3.0 V, a 1C rate corresponds to a current density applied of 1.0 mA cm-2.

Electrochemical tests were carried out in half-coin cells (CR2032 size) for analysis. In half-coin tests, the active material is tested in an electrode versus a Li metal electrode to assess its fundamental performance. In the below examples, the active material composition to be tested was combined with N-Methyl Pyrrolidone (NMP), carbon black acting as a conductive additive, and poly(vinyldifluoride) (PVDF) binder and mixed to form a slurry using a lab-scale centrifugal planetary mixer. The non-NMP composition of the slurries was 90 wt% active material, 6 wt% conductive additive, 4 wt% binder. The slurry was coated on an Al foil current collector to the desired loading of 70 g m-2 by doctor blade coating and dried. The electrodes were then calendared to a density of 2.6 -3.2 g cm-sat 80°C to achieve targeted porosities of 35-40%. Electrodes were punched out at the desired size and combined with a separator (Celgard porous PP/PE), Li metal, and electrolyte (1.3 M LiPF6 in EC/DEC) inside a steel coin cell casing and sealed under pressure. Cycling was then carried out at 23°C at low current rates (C/10) for 2 full cycles of lithiafion and de-lithiation between 1.0 -3.0 V. Afterwards, the cells were tested for their performance at increasing current densities. During rate tests, the cells were cycled asymmetric at 23°C, with a slow charge (C/5) followed by increasing discharge rates (e.g. 1C, then 2C, then 5C, then 10C) for dis-chargeability tests (e.g. measuring capacity retention).

The electrical resistivity of the electrode coating was assessed by a 4-point-probe method with an Ossila instrument. An electrode coating was prepared to a mass loading of 70 g cm-2 and calendared to a porosity of 35-40% on a sheet of insulating mylar for all samples. The sheet resistance was then measured on a 15 mm diameter disc in units oil/ per square at constant temperature of 23°C.

Homogeneous, smooth coatings on both Cu and Al current collector foils, the coatings being free of visible defects or aggregates were also prepared as above for selected samples with a centrifugal planetary mixer to a composition of up to 94 wt% active material, 4 wt% conductive additive, 2 wt% binder. These have been prepared with both PVDF and CMC:SBR-based binder systems. The coatings were calendared at 80°C for PVDF and 50°C for CMC:SBR to porosities of 35-40% at loadings from 1.0 to 3.5 mAh cm-2. This is an important demonstration of these materials being viable in a commercially focussed electrodes for both high energy and high-power applications.

Sample Sheet resistance [K2 per square] 1* 763 ± 53 2 454 ± 25 3 745 ± 26 4 576 ± 27 668 ± 18 6 517 ± 15 7 559 ± 8 8 751 ±31 9 644 ± 39 " Comparative sample Table 4: A summary of electrical resistance measurements carried out as described. Resistivity was measured by 4-point-probe techniques, on equivalent coatings on mylar.

Sample Delithiation specific capacity Coulombic efficiency 1st Nominal de-lithiation 2nd 0 cycle [mAh/g] cycle / 2nd cycle at C/10 [%] voltage at Sc vs LL/Li * [V] 1" 212 97.41 / 98.40 1.76 2 234 98.13 / 98.82 3 224 96.75 / 98.93 1.72 4 206 91.06 / 97.82 1.75 228 95.58 / 98.88 6 217 93.84 / 98.92 1.77 7 221 95.97 / 99.09 1.72 9 227 97.77 / 99.21 1.75 * Comparative sample Table 5: A summary of electrochemical testing results from Li-ion half coin cells. In general (although not exclusively) it is beneficial to have a higher capacity, a higher ICE, and a lower nominal voltage.

1C/0.5C 2C/0.5C 5C/0.5C 10C/0.5C delithiation delithiation delithiation delithiation Sample capacity retention capacity retention capacity retention capacity retention IN Fol IN ryd 1" 94.7 89.3 82.9 68.4 3 98.1 96.1 94.2 89.8 4 98.4 97.4 94.8 89.6

- -

6 95.2 82.4 7 96.2 89.6 9 98.6 96.7 94.3 83.9 *Comparative sample Table 6: A summary of electrochemical testing results from Li-ion half coin cells. It is beneficial to have a higher capacity retention.

Example A -Samples 1" and 3 Comparative Sample 1" has been modified through cation substitution with the P54-cation, maintaining overall valency as in Sample 3 (i.e. isovalent M1 substitution where a > 0). As valency is maintained, the effects on the PNb9025 active material will be due to changing unit cell size and local distortions in crystal structure as a result of the different ionic radii of the cations used. For example, the ionic radius of the 4-coordinate Ps* cation is 0.17 A vs the ionic radius of 4-coordinate Ti41-cation of 0.42 A. This can give rise to improved electrochemical performance through altering the Li ion site availability by varying cavity size (in this case likely the Type VI cavity in particular),4 and resultant electrochemical properties such as improved specific capacity, or improved Coulombic efficiency through reduction of energy barriers to reversible lithiation. This can also result in improved electrical conductivity through variations in crystal properties, and reduced impedance/polarisation electrochemically by improving Li-ion diffusion.

The exchange of the P51-cations for alternative electrochemically active cations such as TN* or Me* can also aid in the tuning of the redox properties of the material, such as by lowering the nominal voltage vs Li/Lit to increase full cell energy density, or by improving capacity and Coulombic efficiency through more efficient and reversible redox processes.

Table 2 demonstrates the change that has taken place in unit cell parameters between Sample 1" and 3. In particular there has been a change in the a and b parameters increasing by 0.0075 A and the c parameter showing a slight reduction of 0.0030 A. This demonstrates that isovalent substitution with materials of larger ionic radii can cause an expansion in the lattice in the a and b directions. This is carried across to minor improvements in electrical resistance shown in Table 4, reducing from Sample 1" to Sample 3 by 18 Cl per square. Electrochemical performance shows great improvements in Table 5 and Table 6, with improved specific capacity, improved 2nd cycle Coloumbic efficiency, and reduction in polarisation at high voltage (represented by the nominal voltage at 5C). Additionally, there are improvements in the specific capacity retention at increasing rates to 10C, and likely beyond this to rates of 20C or more, or 50C or more, or 100C or more.

It is expected that similar benefits will be observed with the described M1 dopants for use in Li-ion cells. Example B -Samples 1", 4, and 5 Comparative Sample 1" has been modified through cation substitution with the Nb5* cation, maintaining overall valency as in Samples 4 and 5 (i.e. isovalent M2 substitution where b > 0). Similar advantages can be observed as in Example A, as a result of altered unit cell size, electrical, and electrochemical properties. Specifically, Samples 4 and 5 show improved electrical resistance in Table 4 versus Sample 1", and improvements in the specific capacity retention at increasing rates to 10C in Table 6, and likely beyond this to rates of 20C or more, or 50C or more, or 100C or more.

It is expected that similar benefits will be observed with the described M2 dopants for use in Li-ion cells. Example C -Samples 1", 6, and 9 Comparative Sample 1' has been modified through cation substitution without maintaining overall valency in Samples 6 and 9. In both these cases a cation of lower valency has been utilised, with others in the case of Sample 9. The advantages from altering ionic radii by substitution as described in Examples A and B are maintained. For Samples 6 and 9, the lower valency results in crystal structure changes, and electronic structure changes. If the substitution takes place in the same cation site, e.g. P5+ directly substitutes for A134, then the 0-content of the material will be decreased proportionally to maintain a charge-balanced structure (Le. oxygen deficient vs the base PNID9025 structure). This creates defects and additional charge carriers in the structure (i.e. electron holes), improving electrical conductivity. This can also induce crystal distortions due to altered coordination with 0 anions and surrounding P/Nb cations, further improving electrical and electrochemical performance in a similar fashion to altering ionic radii as described.

This is observed in Table 2, where the unit cell parameters demonstrate a decrease in a and b parameters, and a decrease in the c parameter as well, overall demonstrating a minor crystal structure contraction. Electrical resistance measurements show improvements in Table 4, with large reductions in the observed sheet resistance vs Sample 1. Electrochemical measurements additionally show advantages for both Samples 6 and 9 in specific capacity, 2nd cycle Coulombic efficiency, polarisation, and capacity retention at high rates in Table 5 and Table 6.

It is expected that similar benefits will be observed with cation or anion exchange of lower or increased valency vs P5* or Nb54-for use in Li-ion cells.

Example D -Samples 1", 2, 6, and 7 Comparative Sample 1* and Sample 6 have been modified through the introduction of induced oxygen vacancy defects (ci oxygen deficiency) by a heat treatment in an inert or reducing atmosphere to provide Samples 2 and 7. By treating these materials at high temperature in an inert or reducing atmosphere, they may be partially reduced and maintain this upon return to room temperature and exposure to air atmosphere. This is accompanied with an obvious colour change, for example Sample 2 is light blue in colour vs white for Sample 1". This colour change demonstrates a significant change in the electronic structure of the material, allowing it to interact with different energies (Le. wavelength) of visible light due to reduced band gap.

The induced oxygen vacancy is specifically a defect in the crystal structure where an oxygen anion has been removed. This provides excess electrons improving material electrical conductivity significantly, and alters the band gap energy as demonstrated by colour changes. If induced oxygen vacancies are present beyond 5 at% (Le. c> 1.25), then the crystal structure collapses due to a loss in stability. These induced oxygen vacancies can be present in addition to oxygen deficiency caused by the use of subvalent cation exchange, as shown in Sample 7. Evidence of oxygen deficiency is provided here by TGA analysis in air, showing a mass increase upon increasing temperature; this has been assumed to correspond to the degree of oxygen deficiency present as it becomes oxidised to provide once more analogous structures to Sample 1* and 6. A host of other techniques can also be employed as described above to quantify oxygen deficiency.

Table 2 demonstrates the change in unit cell parameters that take place upon inducing oxygen vacancies in Samples 2 and 7. Electrical resistance measurements show improvements in Table 4 for Sample 2 over Sample 1". A similar sheet resistance was observed between Sample 6 and 7, due to Sample 6 already being oxygen deficient due to its subvalent substitution of PS* with A13*. Electrochemical measurements additionally show significant advantages for Sample 7 vs 6 in specific capacity, 1m and 2nd cycle Coulombic efficiencies, polarisation, and capacity retention at high rates in Table 5 and Table 6.

It is expected that similar benefits will be observed with any of the described PNO structures having induced oxygen deficiency for use in Li-ion cells.

Example E -Samples 5 and 8 Sample 5 has been modified through the introduction of N3-anions (cf. nitridation) to provide Sample 8.

This was carried out by a solid-state synthesis route but could equally be carried out with a gaseous route utilising NH3 gas at high temperature, or through use of a dissolved N-containing material in a solvent that is subsequently evaporated followed by high temperature heat treatment. Sample 8 is brown compared to Sample 5, which is off-white/light yellow, demonstrating changes to the active material electronic structure in a similar fashion to Example D. In a similar fashion to Examples A-C, this exchange may take place in an 02-anion site, in which case the increased valency may increase the electronic conductivity of the material. It may also take place in an interstitial site within the crystal structure. In both cases, this may also give rise to different unit cell size and associated crystallographic distortions due to the differing ionic radii and valency of the anions, providing similar potential benefits to Examples A-D.

Table 2 demonstrates the change in unit cell parameters that take place upon introduction of N3-anions for Sample 8 over Sample 5, with large reductions in the a and b parameters, and a small increase in the C parameter, providing evidence for N3-incorporation within the crystal structure.

It is expected that similar benefits will be observed through the use of anions of different electronegativity and valency with any of the described PNO structures for use in Li ion cells.

Discussion Comparative Sample 1" may also be modified with more than one type of cation/anion substitution, or induced oxygen deficiency (i.e. a >0 and b > 0; or a >0, d >0; or a >0, b >0, c >0, and so on). Sample 6 demonstrates the effect of having a > 0 and b> 0; Sample 7 demonstrates the effect of having a > 0, b > 0 and c> 0. A material with additionally d > 0 is expected to provide additional benefits in performance to the active material. Improvements as described for Examples A-E are expected for these materials that demonstrate multiple types of modifications.

Table 2 demonstrates changes in unit cell parameters for Sample 6 and 7 reflecting the alterations to the materials that have taken place. Samples 6 and 7 both show large improvements in the electrical resistance vs Sample 1* as shown in Table 4. Electrochemical measurements additionally show significant advantages for both Samples 6 and 7 vs 1" in specific capacity, 2nd cycle Coulombic efficiencies, polarisation (for Sample 7), and capacity retention at high rates in Table 5 and Table 6.

By introducing increased degrees of disorder in the crystal structure (cf entropy) this can aid in reversible lithiafion processes by providing less significant energy barriers to reversible lithiafion, and to prevent Li ion ordering within a partially lithiated crystal. This can also be defined as creating a spread in the energetic states for Li ion intercalation, which prevents unfavourable lithium ordering and entropic energy barriers. This can be inferred from examining the dQ/dV plot shown in Fig. 6, with less significant peaks present for Sample 1* vs Sample 7.

It is expected that similar benefits will be observed in any of the described PNO structures utilising any combination of Ml, M2, Q, a, b, c, and d within the described limits for use in Li ion cells.

While the invention has been described in conjunction with the exemplary embodiments described above, many equivalent modifications and variations will be apparent to those skilled in the art when given this disclosure. Accordingly, the exemplary embodiments of the invention set forth above are considered to be illustrative and not limiting. Various changes to the described embodiments may be made without departing from the spirit and scope of the invention. For the avoidance of any doubt, any theoretical explanations provided herein are provided for the purposes of improving the understanding of a reader.

The inventors do not wish to be bound by any of these theoretical explanations.

Any section headings used herein are for organizational purposes only and are not to be construed as limiting the subject matter described.

References A number of publications are cited above in order to more fully describe and disclose the invention and the state of the art to which the invention pertains. Full citations for these references are provided below. The entirety of each of these references is incorporated herein.

1. J.B. Goodenough et.al., J. Am. Chem. Soc., 135, (2013), 1167-1176.

2. R. S. Roth et al, Acta Cryst., 18, 1965, 643-647.

3. J. Xu et al, lnorg. Chem., 33, 1994, 267-270.

4. S. Patoux et al, J. Electrochem. Soc., 149, 2002, A391-A400.

5. H. Yu et al, Mater Chem. Front, 4, 2020, 631-637.

6. M. B. Preefer et al, Chem. Mater, 32, 2020, 4553-4563.

7. R. D. Shannon, Acta Cryst., A32, 1976, 751-767.

8. A. Benabbas, Acta Cryst. Cryst Struct. Comm., 47, 1991, 849-850.

Claims

Claims: 1. 2. 3. 4. 5. 6. 7. 8. 9.A phosphorus niobium oxide active electrode material with the composition M1 aPx-aM2bNb9-b025-c-c1(11, wherein: M1 is selected from Na, K, Mg, Ca, Sr, Y, Ti, Zr, Hf, V, Nb, Ta, Cr, Mo, W, Mn, Fe, Co, Ni, Cu, Zn, B, Al, Ga, Si, Ge, Sn, Bi, Sb, and mixtures thereof; M2 is selected from Na, K, Mg, Ca, Sr, Y, Ti, Zr, Hf, V, Ta, Cr, Mo, W, Mn, Fe, Co, Ni, Cu, Zn, B, Al, Ga, Si, Ge, Sn, Bi, P, Sb, and mixtures thereof; Q is selected from F, Cl, Br, I, N, S, Se, and mixtures thereof; 0 0.5;0 c1.25;0 5;1.)2; one or more of a, b, c, and d does not equal 0; with the proviso that if M1 consists of Nb and if M2 consists of P then c is > 0.
The active electrode material of claim 1, wherein (i) a> 0; and/or (ii) 0 a 0.3; and/or (iii) 0 a 5 0.2.
The active electrode material of any preceding claim, wherein (i) b> 0; and/or (ii) 0 b 1.5; and/or (iii)0 b 1.
The active electrode material of any preceding claim, wherein (i) c # 0; or (ii) 0 c 1.25; or (iii) 0 < c 1.25.
The active electrode material of any preceding claim, wherein d > 0; and/or (ii) 0 d 2.5; and/or (iii) 0 d 1; or (iv) d = 0.
The active electrode material of any preceding claim, wherein (i) 1 x 1.25; or (ii) x = 1.
The active electrode material of any preceding claim, wherein at least one of a and b is >0, or when both a and b are > 0.
The active electrode material of any preceding claim, wherein M1 is selected from (i) Ti, Zr, Hf, V, Nb, Ta, Cr, Mo, W, Mn, Fe, Co, Ni, Cu, Zn, B, Al, Ga, Si, Ge, Sn, Bi, Sb, and mixtures thereof; or (ii) Ti, Zr, Hf, Cr, Mo, W, B, Al, Ga, Bi, Sb, and mixtures thereof; or (iii) Ti, Mo, Al, B, and mixtures thereof.
The active electrode material of any preceding claim, wherein M2 is selected from (i) Ti, Zr, Hf, V, Ta, Cr, Mo, W, Mn, Fe, Co, Ni, Cu, Zn, B, Al, Ga, Si, Ge, Sn, Bi, P, Sb, and mixtures thereof; or (ii) Ti, Zr, Hf, Cr, Mo, W, V, Ta, and mixtures thereof; or (iii) Ti, Mo, and mixtures thereof.
10. The active electrode material of any preceding claim, wherein (i) M1 has ionic radius 0.1 < r < 1.0 A; and/or (ii) M1 has a different ionic radius than P5+, optionally a larger ionic radius than P5+.
11. The active electrode material of any preceding claim, wherein (I) M2 has ionic radius 0.1 <r < 1.0 A; and/or (ii) M2 has a different ionic radius than NID5*, optionally a larger ionic radius than Nb54-.
12. The active electrode material of any preceding claim, wherein M1 does not comprise Nb and wherein M2 does not comprise P.
13. The active electrode material of any preceding claim, wherein (i) 0 is selected from F, Cl, N, S, and mixtures thereof; or (ii) 0 is selected from F, N, and mixtures thereof; or (iii) wherein Q is N.
14. The active electrode material according to any preceding claim, wherein the active electrode material is oxygen deficient.
15. The active electrode material according to any preceding claim, wherein the active electrode material is coated with carbon.
16. The active electrode material according to claim 14, wherein the carbon coating comprises polyaromatic sp2 carbon, optionally wherein the carbon coating is derived from pitch carbons.
17. The active electrode material according to any preceding claim, wherein the active electrode material is in particulate form, optionally wherein the active electrode material has a D50 particle diameter in the range of 0.1-100 pm, or 0.5-50 pm, or 1-20 pm.
18. The active electrode material according to any preceding claim, wherein the active electrode material has a BET surface area in the range of 0.1-100 m2/g, or 0.5-50 m2/g, or 1-20 m2/g.
19. The active electrode material according to any preceding claim, further comprising Li and/or Na.
20. The active electrode material according to any preceding claim, wherein the crystal structure of the active electrode material as determined by X-ray diffraction corresponds to the crystal structure of one or more of PNb9025, VNI39025, or P25Nbi8050; or corresponds to the crystal structure of one or more of PNI39025 or P2.5Nbi8050; or corresponds to the crystal structure of PNb9025.
21. A composition comprising the active electrode material of any preceding claims and at least one other component; optionally wherein the at least one other component is selected from a binder, a solvent, a conductive additive, an additional active electrode material, and mixtures thereof
22. An electrode comprising the active electrode material of any of claims 1-20 in electrical contact with a current collector.
23. An electrochemical device comprising an anode, a cathode, and an electrolyte disposed between the anode and the cathode, wherein the anode comprises an active electrode material according 24. 25. 26. 27. 28.to any of claims 1-20; optionally wherein the electrochemical device is a lithium-ion battery or a sodium-ion battery.An electrochemical device according to claim 23, wherein the electrochemical device is a lithium-ion battery having a reversible anode active material specific capacity of greater than 200 mAh/g at 20 mA/g, wherein the battery can be charged and discharged at current densities relative to the anode active material of 200 mA/g or more, or 1000 mA/g or more, or 2000 mA/g or more, or 4000 mA/g or more whilst retaining greater than 70% of the initial cell capacity at 20 mA/g. A method of making an active electrode material as defined by any of claims 1-20, the method comprising steps of: providing one or more precursor materials; mixing said precursor materials to form a precursor material mixture; and heat treating the precursor material mixture in a temperature range from 400 °C -1350 °C or 800 °C -1350 °C, thereby providing the active electrode material.The method of claim 25, further comprising the steps of: mixing the active electrode material with a precursor comprising element Q to provide a further precursor material mixture; and heat treating the further precursor material mixture in a temperature range from 400 -1200 °C or 800-1200 °C under reducing conditions, thereby providing the active electrode material comprising element Q. The method of claim 25 or 26, comprising the further step of heat treating the active electrode material or the active electrode material comprising element Q in a temperature range from 400 -1350 °C or 800 -1350 °C under reducing conditions, thereby introducing oxygen vacancies into the active electrode material.The method of any of claims 25-27, further comprising the steps of: combining the active electrode material or the active electrode material comprising element Q with a carbon precursor comprising polyaromafic sp2 carbon to form an intermediate material; and heating the intermediate material under reducing conditions to pyrolyse the carbon precursor forming a carbon coating on the active electrode material and introducing oxygen vacancies into the active electrode material.