GB2526905A - Sintering Particulate material - Google Patents

Sintering Particulate material Download PDF

Info

Publication number
GB2526905A
GB2526905A GB1504080.1A GB201504080A GB2526905A GB 2526905 A GB2526905 A GB 2526905A GB 201504080 A GB201504080 A GB 201504080A GB 2526905 A GB2526905 A GB 2526905A
Authority
GB
United Kingdom
Prior art keywords
layer
elongate elements
particulate material
radiation
surface portion
Prior art date
Legal status (The legal status is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the status listed.)
Granted
Application number
GB1504080.1A
Other versions
GB2526905B (en
GB201504080D0 (en
Inventor
Mark Alfred Potter
Matthew Nicholas Stevens
Current Assignee (The listed assignees may be inaccurate. Google has not performed a legal analysis and makes no representation or warranty as to the accuracy of the list.)
BAE Systems PLC
Original Assignee
BAE Systems PLC
Priority date (The priority date is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the date listed.)
Filing date
Publication date
Application filed by BAE Systems PLC filed Critical BAE Systems PLC
Publication of GB201504080D0 publication Critical patent/GB201504080D0/en
Publication of GB2526905A publication Critical patent/GB2526905A/en
Application granted granted Critical
Publication of GB2526905B publication Critical patent/GB2526905B/en
Active legal-status Critical Current
Anticipated expiration legal-status Critical

Abstract

A method of selectively sintering particulate material, the method comprising: providing a layer 6 of particulate material; providing an amount of a radiation absorbent material, such as carbon black in powder form, over a selected surface portion of the layer of particulate material; providing an amount of a material that comprises a plurality of elongate elements 16 over at least part of the selected surface portion of the layer of particulate material; and providing radiation 8 across the selected surface portion so as to sinter a portion of the material of the layer including causing the plurality of elongate elements to become embedded in the sintered portion of material. The elongate elements are selected from the group consisting of carbon nanotubes and elongate graphene plates. The radiation absorbent material and elongate elements may be provided together in a compound 14, wherein the compound can be a liquid comprising a solvent. An apparatus for selectively sintering particulate material is also claimed which comprises one or more printing devices 12 and a radiation source 10. A compound for use in a process of selectively sintering particulate material is also claimed.

Description

SINTERING PARTICULATE MATERIAL
FIELD OF THE INVENTION
The present invention relates to the sintering of particulate material.
BACKGROUND
Additive Manufacturing (AM) (also known as Additive Layer Manufacture (ALM), 3D printing, etc.) is a process that may be used to produce functional, complex objects, layer by layer, without moulds or dies. Typically, such processes include providing material (e.g. metal or plastic) in the form of a powder or a wire, and, using a powerful heat source such as a laser beam, electron beam or an electric, or plasma welding arc, melting an amount of that material and depositing the melted material (e.g. on a base plate of a work piece). Subsequent layers are then built up upon each preceding layer.
A number of AM methods are currently available including, but are not limited to, Laser Blown Powder, Laser Powder Bed, and Wire and Arc technologies.
EP 1 648 686 (Loughborough University Enterprises Ltd.) discloses an AM method in which a layer of particulate material is provided, an amount of radiation absorbing material is provided over a selected portion of the provided layer of particulate material, and radiation is provided across the selected portion to sinter the particulate material of the selected portion. This process is then repeated to form a three-dimensional object.
SUMMARY OF THE INVENTION
In a first aspect, the present invention provides a method of selectively sintering particulate material, the method comprising: providing a layer of particulate material; providing an amount of a radiation absorbent material over a selected surface portion of the layer of particulate material; providing an amount of a material that comprises a plurality of elongate elements over at least part of the selected surface portion of the layer of particulate material; and providing radiation across the selected surface portion of the layer of particulate material so as to sinter a portion of the material of the layer including causing the plurality of elongate elements to become embedded in the sintered portion of material. The elongate elements may be selected from the group of elongate elements consisting of carbon nanotubes and elongate graphene plates.
Providing the radiation absorbent material may include depositing or applying the radiation absorbent material (e.g. as a layer of radiation absorbent material) onto the surface of the layer of particulate material.
Providing the material that comprises the elongate elements may include depositing or applying the elongate elements (e.g. as a layer of material) onto the surface of the layer of particulate material.
The elongate elements may be fibres, e.g. nano-fibres having lengths of several lOs of nanometres. The lengths the fibres may be at least ten times larger than the widths or diameters of the fibres.
The elongate elements may include carbon nanotubes, glass fibres, and/or graphene fibres.
Providing the elongate elements over at least part of the selected surface portion of the layer of particulate material may comprise ejecting (e.g. in a carrier fluid), from a printing device, the elongate elements as the printing device moves over the selected surface portion of the layer of particulate material. Thus, the elongate elements tend to be aligned, for example, along a direction of travel of the printing device.
The material that comprises the plurality of elongate elements may further comprise further elongate elements selected from a group of further elongate elements consisting of carbon fibres, glass fibres, silicon carbide fibres and graphene fibres.
The radiation absorbent material and the plurality of elongate elements may be provided together in a compound that comprises both the radiation absorbent material and the plurality of elongate elements.
The compound may be a liquid that may be "jetted" onto the surface of the particulate material. The compound may comprise a solvent. The radiation absorbent material and the plurality of elongate elements may be dispersed throughout the solvent.
The method may further comprise performing the following steps (i) to (iv) one or more times so as to form a three dimensional object. Step (i) may include providing a further layer of particulate material overlying the prior layer of particulate material including the previously sintered portion of material. Step (ii) may include providing an amount of the radiation absorbent material over a selected surface portion of the further layer of particulate material. Step (iii) may include providing an amount of the material that comprises a plurality of elongate elements over at least part of the selected surface portion of the further layer of particulate material. Step (iv) may include providing radiation across the selected surface portion of the further layer of particulate material so as to sinter a further portion of the material including causing the plurality of elongate elements to become embedded in the sintered further portion and to sinter the further portion with the previously sintered portion of the material in the prior layer.
The elongate elements in a first layer may be aligned in a different direction to the elongate elements in a second layer, the first layer being different to the second layer.
The step of providing an amount of a material that comprises a plurality of elongate elements may comprise providing a first level of the material that comprises a plurality of elongate elements on a first area of the selected surface portion of the layer of particulate material, and providing a second level of the material that comprises a plurality of elongate elements on a second area of the selected surface portion of the layer of particulate material, the second level being different to the first level.
The radiation absorbent material and the elongate elements may be the same material.
The method may further comprise, prior to providing radiation across the selected surface portion of the layer of particulate material, providing an amount of a material that comprises a plurality of electrically conductive elements over at least part of the selected surface portion of the layer of particulate material, and sintering the portion of the material of the layer causes the plurality of electrically conductive elements to become embedded in the sintered portion of material.
The radiation absorbent material, the plurality of elongate elements, and the plurality electrically conductive elements may be provided together in a compound that comprises the radiation absorbent material, the plurality of elongate elements, and the plurality electrically conductive elements.
The method may further comprise apply a force or a field to the deposited elongate elements so as to improve alignment of the elongate elements. The application of the force of field may include generating an electric field or a magnetic field, and exposing the deposited carbon nanotubes or graphene plates to the generated electric or magnetic field. This tends to improve alignment of the elongate elements.
In a further aspect, the present invention provides a three dimensional object formed using a method according to the preceding aspect.
In a further aspect, the present invention provides apparatus for selectively sintering particulate material, the apparatus comprising: one or more printing devices configured to provide an amount of a radiation absorbent material over a selected surface portion of a provided layer of particulate material, and provide an amount of a material that comprises a plurality of elongate elements over at least part of the selected surface portion of the layer of particulate material. The apparatus further comprises a radiation source operable to provide radiation across the selected surface portion of the layer of particulate material so as to sinter a portion of the material of the layer including causing the plurality of elongate elements to become embedded in the sintered portion of material. The elongate elements may be selected from the group of elongate elements consisting of carbon nanotubes and elongate graphene plates.
A single printing device may be operable to provide both the radiation absorbent material and the plurality of elongate elements together in a compound that comprises both the radiation absorbent material and the plurality of elongate elements.
In a further aspect, the present invention provides a compound for use in a process of selectively sintering particulate material, the compound comprising a radiation absorbent material and a plurality of elongate elements. The elongate elements may be selected from the group of elongate elements consisting of carbon nanotubes and elongate graphene plates.
The compound may be a liquid. The compound may further comprise a solvent. The radiation absorbent material and the plurality of elongate elements may be dispersed throughout the solvent.
BRIEF DESCRIPTION OF THE DRAWINGS
Figure 1 is a schematic illustration (not to scale) of an apparatus for combining particulate material according to an embodiment; Figure 2 is a schematic illustration (not to scale) of an apparatus for combining particulate material according to a further embodiment; and Figure 3 is a schematic illustration (not to scale) of an apparatus for combining particulate material being used to form a three dimensional object.
DETAILED DESCRIPTION
The terminology "Additive Manufacturing' is used herein to refer to all additive processes that may be used to produce functional, complex objects, layer by layer, without moulds or dies e.g. by providing material (e.g. metal or plastic) typically in the form of a powder or a wire, and, using a powerful heat source such as a laser beam, electron beam or an electric, or plasma welding arc, melting an amount of that material and depositing the melted material (e.g. on a base plate/work piece), and subsequently building layers of material upon each preceding layer.
Additive Manufacture (AM) may also be known inter a/ia as 3D printing, Direct Digital Manufacturing (DDM), Digital Manufacturing (DM), Additive Layer Manufacturing (ALM), Rapid Manufacturing (RM), Laser Engineering Net Shaping (LENS), Direct Metal Deposition, Direct Manufacturing, Electron Beam Melting, Laser Melting, Freeform Fabrication, Laser Cladding, Direct Metal Laser Sintering, Selective Laser Melting, Fused Deposition Modelling, and High Speed Sintering.
Figure 1 is a schematic illustration (not to scale) showing example Additive Manufacturing apparatus 2 that is used in an embodiment of a process of producing an object. The apparatus 2 comprises a controller 4 for enabling the exposure of a surface portion of a layer 6 of particulate material to radiation 8 provided by a radiation source 10.
In this embodiment, the particulate material is a plastic in powder form.
However, in other embodiments, the particulate material may be a different material such as a metal or ceramic. In this embodiment, the radiation 8 is infrared radiation. However, in other embodiments, radiation other than infrared radiation may be used. The radiation source 10 may be any appropriate source such as halogen lighting or a scanning laser.
In this embodiment, the controller 4 is configured to control the variation of radiation absorption across the surface portion of the layer 6 of particulate material. In particular, the controller controls a printing head 12 to deposit desired amounts of a first compound 14 onto the surface portion of the layer 6.
The movement of the printing head 12 and the amount of first compound 14 deposited by the printing head 12 is controlled by the controller 4.
In some embodiments, a temperature sensor or an infrared camera, or the like may be used to determine the surface temperature of the layer 6. The amount of the first compound 14 that is to be deposited onto the surface portion of the layer 6 may be determined by the controller 4 depending on the determined temperature.
In this embodiment, the first compound 14 is in liquid form and is jetted onto the surface of the layer 6 by the printing head 12.
Advantageously, the jetting or ejection of the first compound onto the layer 6 as the printing head moves across the surface of the layer 6 advantageously tends to cause the carbon nanotubes 16 to align.
In this embodiment, the first compound 14 comprises a solvent in which is dispersed a radiation absorbent material and a plurality of carbon nanotubes 16. The solvent may be any appropriate solvent for example an aqueous medium that evaporates when exposed to the radiation 8 emitted from the radiation source 10.
The radiation absorbent material is for absorbing infrared radiation 8 emitted by the radiation source 10 and may be, for example, a material such as carbon black in powder form. In some embodiments, the radiation absorbent material is carbon black nano-particles, for example having a primary particle size of lSnm or less and finely dispersed throughout the solvent.
The carbon nanotubes 16 are elongate particles, i.e. elongate elements.
The carbon nanotubes 16 may have lengths that are at least ten times larger than the widths or diameters of the carbon nanotubes 16. The carbon nanotubes 16 typically have length-to-diameter ratio of up to 132,000,000:1.
The carbon nanotubes 16 have substantially cylindrical nanostructure. The carbon nanotubes 16 may have, for example, a diameter of <1 nm up to 50 nm.
The carbon nanotubes 16 may have lengths of several microns or longer, e.g. at least 10pm. The carbon nanotubes may have diameters in the range 1-5Onm, and lengths in the range 10 to 500nm. In some embodiments, one or more different types of elongate element is used instead of or in addition to the carbon nanotubes 16. Examples of appropriate other elongate elements include, but are not limited to, glass fibres, silicon carbide whiskers, and graphene fibres, graphene flakes, and graphene platelets.
In use, radiation 8 provided by the radiation source 10 is absorbed by the radiation absorbent material within the first compound 14 where it is present on the surface of the layer 6. This causes the radiation absorbent material to heat up. Heat from the radiation absorbent material is transferred (i.e. radiated) to the underlying particulate material raising the temperature of individual particles of the layer 6 of particulate material. The particles of the layer 6 are heated to at least their melting temperature and the particles coalesce. Thus, the particulate material onto which the first compound 14 is deposited is fully melted.
Also, in this embodiment, the heating up of the radiation absorbent material causes the solvent of the first compound 14 to evaporate, thereby leaving the radiation absorbent material and the carbon nanotubes 16 deposited on the layer 6. As the particulate material onto which the first compound 14 is deposited is fully melted, the radiation absorbent material and the carbon nanotubes 16 tend to diffuse into, and become embedded within, the melted particulate material.
The fully melted material is subsequently allowed to cool so as to form a layer of solid material with the radiation absorbent material and the carbon nanotubes 16 embedded therein. Thus, a coherent mass of combined particulate material, radiation absorbent material and the carbon nanotubes 16 is formed.
In this embodiment, no first compound 14 (and therefore no radiation absorbent material) is provided on the regions of surface portion of the layer 6 of the particulate material that are not to be consolidated. Where no radiation absorbent material is applied to the layer 6, the heating of the particulate material in those regions by the incident radiation 8 is not sufficient to cause melting of the particulate material. Thus, there is no combination of the particulate material in the regions to which no radiation absorbing material is applied when the layer 6 is exposed to the radiation 8.
After the material has been allowed to cool and solidify, a further layer of particulate material may be applied across the top surface of the layer 6. The above described process may then be repeated, i.e. a further layer of first compound 14 may be applied to the further layer of particulate material and radiation may be applied thereafter. In this way, many layers of material are laid on top of one another (in accordance with a digital design model for the object being produced which may be accessible by the controller 4) to produce the object. Further information about apparatus that may be used to perform this process is described in more detail later below with reference to Figure 3.
The carbon nanotubes 16 embedded within the produced object tend to provide that the object has improved structural stiffness, for example, compared to objects produced without the carbon nanotubes 16. Also, the carbon nanotubes 16 embedded within the produced object tend to provide that the object has improved mechanical strength, for example, compared to objects produced using conventional processes. Also, the carbon nanotubes 16 embedded within the produced object tend to provide that the object has improved stability, for example, compared to objects produced using conventional processes.
The deposition of the first compound 14 directly onto the surface portion of the layer 6 advantageously enables the radiation absorptive properties of the particulate material to be varied and carefully controlled, as desired.
Also, the deposition of the first compound 14 directly onto the surface portion of the layer 6 advantageously enables the strengthening or stiffening properties of the carbon nanotubes 16 to be varied and carefully controlled, as desired. For example, in areas where a greater amount of first compound 14 applied, a greater amount of the carbon nanotubes 16 will tend to become embedded in the consolidated material. Thus, the resulting solidified layer will tend to have increased strength and/or stiffness properties in region where a greater amount of the first compound 14 was applied compared to regions where a lesser amount of the first compound 14 was applied.
In conventional processes, when the particulate material is combined by sintering at a slow rate (e.g. lower temperate), the produced object tends to have good material properties (e.g. relatively high strength) but relatively poor definition at the object edges. Also, in conventional processes, when the particulate material is combined by sintering at a rapid rate (e.g. higher temperate), the produced object tends to have inferior material properties (e.g. lower strength) but good edge definition. Use of the carbon nanotubes 16 within the first compound 14 advantageously tends to provide a solution to this problem encountered in conventional processes by providing increased strength, i.e. improved structural properties, even when rapid sintering is used.
Thus, particulate material is combined by sintering at a rapid rate (e.g. higher temperate), thereby achieving good edge definition, whilst the carbon nanotubes 16 tend to provide the produced object with material properties that tend to be at least as good as those achieved if sintering at a slow rate (e.g. lower temperate) was performed.
Advantageously, when the first compound 14 is jetted onto to the surface of the layer, the carbon nanotubes 16 within the further compound tend to align.
For example, carbon nanotubes within the first compound 14 tend to line up with one another when deposited onto the layer 6. This advantageously tends to further increase the mechanical strength of the produced object at least in the direction along which the carbon nanotubes are aligned.
In some embodiments, alignment of carbon nanotubes in a layer is improved, effected, or facilitated by exposing the deposited nanotubes to a force or field prior to the solidification of that layer. In some embodiments, the force or field is applied prior to the application of the radiation to the object (i.e. before melting of the particulate material). In some embodiments, the force or field is applied during the application of the radiation to the object (i.e. during melting of the particulate material). In some embodiments, the force or field is applied after the application of the radiation to the object (i.e. after melting of the particulate material, and before its solidification).
One example of a field that may be used to improve alignment of deposited carbon nanotubes is a magnetic field. A magnetic field may, for example, be applied across deposited carbon nanotubes prior to those nanotubes being embedded in a solid layer of the object being formed. A magnetic field may be applied by any appropriate device or system.
Advantageously, a magnetic field may be applied to a deposited layer of carbon nanotubes remotely, for example there may be a significant distance between any part of an aligning magnet and the deposited carbon nanotubes.
A further example of a field that may be used to improve alignment of deposited carbon nanotubes is an electric field. Preferably, an AC electric field is used. Nevertheless, a DC electric field may be used, however carbon nanotubes may accumulate near an electrode applying the DC field. An electric field may be applied across deposited carbon nanotubes prior to those nanotubes being embedded in a solid layer of the object being formed. An electric field may be applied by any appropriate device or system.
In some embodiments, a different carbon nanotube alignment process may be performed instead of or in addition to the application of magnetic and/or electric field. For example, in some embodiments, acoustic waves may be applied through the deposited carbon nanotubes to improve alignment. In some embodiments, a standing or stationary wave is applied to improve alignment.
In some embodiments, a series of many layers of material are laid on top of one another to produce the object. In such embodiments, the carbon nanotubes in a layer of material may be oriented or aligned in a direction to the carbon nanotubes in one or more previous and/or subsequent layers of material. This may be performed as follows. Firstly, a first layer of material is formed including depositing carbon nanotubes, aligning those carbon nanotubes in a first direction (e.g. by applying a magnetic field along the first direction), and melting and subsequently solidifying the first layer of material.
Secondly, a second, subsequent layer of material is formed on the first layer including depositing carbon nanotubes, aligning those carbon nanotubes in a second direction different to the first (e.g. by applying a magnetic field along the second direction), and melting and subsequently solidifying the second layer of material.
By orienting in different directions the carbon nanotubes in different layers, multi-directional improved material properties can be realised.
Alternatively, improved material properties (e.g. tensile strength) in only a single direction can be realised.
As described in more detail later below with reference to Figure 2, electrically conductive tracks or paths may be formed in the object. By orienting differently the carbon nanotubes in different layers as described in more detail above, the carbon nanotubes may be steered" or directed along such paths or tracks. Thus, advantageously the carbon nanotubes may be aligned along meandering paths through the formed object, thereby providing improved electrical conductivity along such paths.
Figure 2 is a schematic illustration (not to scale) showing a further example Additive Manufacturing apparatus according to a further embodiment in which corresponding elements have been given corresponding reference numerals.
In this further embodiment, the controller 4 controls the printing head 12 to deposit desired amounts of a second compound 18 onto the surface portion of the layer 6. The movement of the printing head 12 and the amount of the second compound 18 deposited by the printing head 12 is controlled by the controller 4.
In some embodiments, a temperature sensor or an infrared camera, or the like may be used to determine the surface temperature of the layer 6. The amount of the second compound 18 that is to be deposited onto the surface portion of the layer 6 may be determined by the controller 4 depending on the determined temperature.
In this embodiment, the second compound 18 is in liquid form and is jetted onto the surface of the layer 6 by the printing head 12.
In this embodiment, the second compound 18 comprises a solvent in which is dispersed a radiation absorbent material and a plurality of electrically conductive elements 20.
The solvent may be any appropriate solvent for example an aqueous medium that evaporates when exposed to the radiation 8 emitted from the radiation source 10.
The radiation absorbent material is for absorbing infrared radiation 8 emitted by the radiation source 10 and may be, for example, a material such as carbon black in powder form. In some embodiments, the radiation absorbent material is carbon black nano-particles, for example having a primary particle size of l5nm or less and finely dispersed throughout the solvent.
The electrically conductive elements 20 are provided by electrically conductive particulate material that is distributed throughout the solvent. The electrically conductive elements 20 may be nano-particles and may, for example, have sizes within the range <1 nm up to 150 nm. The electrically conductive elements 20 may be metal, such as copper, or any other electrically conductive material. Preferably, the electrically conductive elements 20 are carbon nanotubes. However, in some embodiments, the electrically conductive elements 20 are not carbon nanotubes. Carbon nanotubes may have, for example, a diameter of <1 nm up to 50 nm. Carbon nanotubes may have is lengths are several microns or longer, e.g. at least 10pm. Carbon nanotubes may have diameters in the range 1-SOnm, and lengths in the range 10 to SOOnm. Advantageously, carbon nanotubes tend to have good electrical conductivity and tend to align and connect together when deposited and/or when sintering occurs so as to form an electrically conductive path.
In this embodiment, the electrically conductive elements are also thermally conductive elements.
Similarly to as described above, in use, radiation 8 provided by the radiation source 10 is absorbed by the radiation absorbent material within the second compound 18 where it is present on the surface of the layer 6. This causes the radiation absorbent material to heat up. Heat from the radiation absorbent material is transferred (i.e. radiated) to the underlying particulate material raising the temperature of individual particles of the layer 6 of particulate material. The particles of the layer 6 are heated to at least their melting temperature and the particles coalesce. Thus, the particulate material onto which the second compound 18 is deposited is fully melted.
Also, in this embodiment, the heating up of the radiation absorbent material causes the solvent of the second compound 18 to evaporate, thereby leaving the radiation absorbent material and the electrically conductive elements 20 deposited on the layer 6. As the particulate material onto which the second compound 18 is deposited is fully melted, the radiation absorbent material and the electrically conductive elements 20 tend to diffuse into, and become embedded within, the melted particulate material.
The fully melted material is subsequently allowed to cool so as to form a layer of solid material with the radiation absorbent material and the electrically conductive elements 20 embedded therein. Thus, a coherent mass of combined particulate material, radiation absorbent material and the electrically conductive elements 20 is formed.
In this embodiment, no second compound 18 (and therefore no radiation absorbent material) is provided on the regions of surface portion of the layer 6 of the particulate material that are not to be consolidated. Where no radiation absorbent material is applied to the layer 6, the heating of the particulate material in those regions by the incident radiation 8 is not sufficient to cause melting of the particulate material. Thus, there is no combination of the particulate material in the regions to which no radiation absorbing material is applied when the layer 6 is exposed to the radiation 8.
After the material has been allowed to cool and solidify, a further layer of particulate material may be applied across the top surface of the layer 6. The above described process may then be repeated, i.e. a further layer of second compound 18 may be applied to the further layer of particulate material and radiation may be applied thereafter. In this way, many layers of material are laid on top of one another (in accordance with a digital design model for the object being produced which may be accessible by the controller 4) to produce the object. Further information about apparatus that may be used to perform this process is described in more detail later below with reference to Figure 3.
The electrically conductive elements 20 embedded within the produced object advantageously tend to provide that at least a portion of the object is electrically conductive. For example, a sufficient amount of the further compound 18 may be applied to the surface of the layer 6 such that, when sintered and solidified, there is a sufficient amount of electrically conductive elements 20 embedded in the solidified material to provide that that material is electrically conductive. Also for example, the proportion of the further compound 18 that is made up of the electrically conductive elements 20 is sufficient to provide that, when sintered and solidified, there is a sufficient amount of electrically conductive elements 20 embedded in the solidified material to provide that that material is electrically conductive. Preferably, the electrically conductive elements are embedded with the consolidated material such that they are in contact with one another, i.e. such that they are electrically connected. This may be facilitated by using a sufficient amount of the further compound 18 and/or having a sufficient proportion of the further compound 18 be the electrically conductive elements 20. Also, this may be facilitated by having the electrically conductive elements 20 be carbon nanotubes that tend to link together so as to be electrically connected together when deposited or during sintering.
The deposition of the second compound 18 directly onto the surface portion of the layer 6 advantageously enables the electrically conductive properties of the electrically conductive elements 20 to be varied and carefully controlled across the surface portion of the layer 6, as desired. In some embodiments, the second compound 18 is applied to the surface of the layer 6 so as to define one or more electrically conductive paths or tracks across the surface.
For example, one or more electrically conductive tracks that connect together two different points on the surface of the layer 6 may be defined.
In some embodiments, one or more devices may be attached to or embedded in the object at a point along an electrically conductive track formed in the object. For example, in some embodiments, an input port or connector is embedded into the object at one end of an electrically conductive track. In some embodiments, an output port or connector may be embedded into the object at one end of an electrically conductive track, e.g. an opposite end to the end at which the input port is located. In some embodiments, an electrical component (for example a resistor, a capacitor, a diode, a switch, etc.) may be embedded in the object along an electrically conductive track formed therein.
In embodiments in which the electrically conductive elements are elongate, e.g. carbon nanotubes or elongate graphene platelets, the elements may be aligned along the electrically conductive tracks, for example, by movement of the printing head, and/or by using magnetic or electric fields as described in more detail above.
In some regions of the surface (e.g. in regions other than the defined electrically conductive tracks) a compound that does not contain the electrically conductive elements 20, for example a compound that contains only the radiation absorbent material and the solvent, or a compound that contains electrically insulating material, the radiation absorbent material and the solvent, may be applied. Thus, when radiation is applied to the surface and the particulate material is sintered, one or more electrically conductive tracks or paths are formed, which may be surrounded (at least to some extent) with non-electrically conductive material or electrically insulating material. In this way, electrically insulating jackets" may be formed in the object around an electrically conductive track.
In some embodiments, by applying compounds with different concentrations (i.e. loading levels) of the electrically conductive elements 20, the electrical properties across the thickness or surface layer of the deposition layer may be changed to create a functionally graded material. Thus, an object having different electrical (and/or material) properties at different positions of the material may be formed. Using such a technique, the electromagnetic absorption characteristics of the formed object may be optimised with respect to one or more predetermined criteria.
In some embodiments, the second compound 18 is applied to the surface of the layer 6 so that it overlaps at least to some extent with an electrically conductive path formed in the prior sintered layer. The layer 6 may be subsequently sintered thereby forming an electrically conductive track between the current layer and the prior layer. In this way, an electrically conductive track that extends through multiple layers of the produced object may be formed.
Using the above described process, a three dimensional object having one or more three dimensional electrically conductive tracks, or three dimensional network of electrically conductive tracks, embedded therein may be formed.
Figure 3 is a schematic illustration (not to scale) showing example apparatus that may be used to form a three dimensional object 21 using the processes described above with reference to Figures 1 and 2. Elements of the apparatus which have been referred to above have been given corresponding reference numerals. Although a piston-based AM apparatus is implemented here, it will be appreciated by the skilled person that a different AM apparatus, for example a conveyor based AM apparatus, may be used.
The apparatus 2 comprises a first powder repository 22 (or powder bed) containing an amount of the particulate material 23.
In operation, a first piston 24 (that is located at the bottom of the first repository 22) is raised (in the direction indicated by an arrow in Figure 3 and the reference numeral 26) so as to raise an amount of the particulate material 23 above a top level of the first repository 22. A roller 28 is then rolled (in the direction indicated by an arrow in Figure 3 and the reference numeral 30) over the upper surface of the first repository 22 and across an upper surface of a second repository 32. This is performed so that the particulate material 23 that was raised above the level of the first repository 22 by the raising of the first piston 24 is spread over an upper surface of the second repository 32. Thus, a top surface of the contents of the second repository 32 is covered by a layer 6 of the particulate material 23. In other embodiments, a different means of spreading the particulate material 23 across a top surface of the contents of the second repository 32, such as a wiper, may be used instead of or in addition to the roller 28.
After a layer 6 of the particulate material 23 has been spread across a top surface of the contents of the second repository 32, the printing head 12 is controlled by the controller 4 to deposit a layer of a compound containing a radiation absorbing material (e.g. a layer of the first compound 14 and/or a layer of the second compound 15) on the top surface of the layer 6.
After deposition of the compound 14, 18, the controller 4 controls the radiation source 10 to emit radiation 8 onto the top surface of the contents of the second repository 32, thereby sintering a portion of the layer 6 of the particulate material 23 as described in more detail earlier above.
In this embodiment, the particulate material 23 over which the compound has been applied is fully melted by the radiation and subsequently allowed to cool so as to form a layer of solid material. A second piston 34, located at the bottom of the second repository 22 is then lowered (i.e. moved in a direction indicated in Figure 3 by a solid arrow and the reference numeral 36) to allow for a further layer of the particulate material 23 to be spread by the roller 18 across the top surface of the contents of the second repository 22 (and subsequently melted and allowed to solidify).
Many layers of material are laid on top of one another and sintered together, in accordance with a digital design model 38 for the object 21, to produce the object 21.
In the above embodiments, a compound is in liquid form and is jetted onto the surface of the layer of particulate material by the printing head.
However, in other embodiments, a compound is in a different form, for example, solid (e.g. in powder form) or gas. Also, in other embodiments, a compound may be deposited in a different appropriate way.
In the above embodiments, a compound deposited on the surface of the layer of particulate material contains a radiation absorbent material and either carbon nanotubes or a different electrically (and/or thermally) conductive material or elements. In other embodiments, the compound deposited may include both the carbon nanotubes and the different electrically conductive elements or material. In some embodiments, the different electrically conductive elements or material are not used.
In some embodiments, elongate graphene plates or platelets (or elongate graphene flakes) are used instead of or in addition to carbon nanotubes. The jetting or ejection of the elongate graphene platelets as the printing head moves across the surface of the parts being formed tends to align cause the elongate graphene plates. Advantageously, elongate graphene plates tends to provide the same or similar advantages as carbon nanotubes.
In the above embodiments, a compound deposited on the surface of the layer of particulate material contains a radiation absorbent material and one or more separate, different additional materials (such as the carbon nanotubes and/or the different electrically conductive elements). However, in other embodiments, the carbon nanotubes provide both the above described radiation absorbing property and the above described strengthening property. Also, in other embodiments, the different electrically conductive elements may be made of a radiation absorbent material such that the electrically conductive elements provide both the above described radiation absorbing property and the above described electrically and/or thermally conductive property.
In the above embodiments, the radiation absorbent material and the additional material(s), i.e. the carbon nanotubes and/or the different electrically conductive elements, are deposited together as a compound material. In particular, the radiation absorbent material and the additional material(s) are dispersed throughout a common solvent. However, in other embodiments, the radiation absorbent material and one or more of the additional material may be deposited on the surface of the layer of particulate material separately, e.g. by different printing heads or by a common printing head.
In the above embodiments, the carbon nanotubes and/or the different electrically conductive elements are only applied to the portion of the surface of the layer of particulate material that is to be sintered to form the object. This advantageously tends to avoid wastage of carbon nanotubes and/or the different electrically conductive elements, i.e. the carbon nanotubes and/or the -20 -different electrically conductive elements are only deposited where desired. This is in contrast to, for example, providing carbon nanotubes and/or the different electrically/thermally conductive elements in the particulate material itself. -21 -

Claims (15)

  1. CLAIM S1. A method of selectively sintering particulate material, the method comprising: providing a layer (6) of particulate material; S providing an amount of a radiation absorbent material over a selected surface portion of the layer (6) of particulate material; providing an amount of a material that comprises a plurality of elongate elements (16) over at least part of the selected surface portion of the layer (6) of particulate material; and providing radiation (8) across the selected surface portion of the layer (6) of particulate material so as to sinter a portion of the material of the layer (6) including causing the plurality of elongate elements (16) to become embedded in the sintered portion of material; wherein the elongate elements are selected from the group of elongate elements consisting of carbon nanotubes and elongate graphene plates.
  2. 2. A method according to claim 1, wherein providing the elongate elements (16) over at least part of the selected surface portion of the layer (6) of particulate material comprises ejecting, from a printing device (12), the elongate elements (16) as the printing device moves over the selected surface portion of the layer (6) of particulate material, thereby aligning the elongate elements (16) in a direction of travel of the printing device (12).
  3. 3. A method according to claim 1 or 2, wherein the material that comprises the plurality of elongate elements (16) further comprises further elongate elements selected from a group of further elongate elements consisting of carbon fibres, glass fibres, silicon carbide fibres and graphene fibres. -22 -
  4. 4. A method according to any of claims 1 to 3, wherein the radiation absorbent material and the plurality of elongate elements (16) are provided together in a compound (14) that comprises both the radiation absorbent material and the plurality of elongate elements (16).
  5. 5. A method according to claim 4, wherein: the compound (14) is a liquid comprising a solvent; and the radiation absorbent material and the plurality of elongate elements (16) are dispersed throughout the solvent.
  6. 6. A method according to any of claims 1 to 5, the method further comprising performing steps (i) to (iv) one or more times so as to form a three dimensional object (21), wherein: step (i) includes providing a further layer of particulate material overlying the prior layer of particulate material including the previously sintered portion of material; step (ii) includes providing an amount of the radiation absorbent material over a selected surface portion of the further layer of particulate material; step (iD) includes providing an amount of the material that comprises a plurality of elongate elements (16) over at least part of the selected surface portion of the further layer of particulate material; and step (iv) includes providing radiation (8) across the selected surface portion of the further layer of particulate material so as to sinter a further portion of the material including causing the plurality of elongate elements (16) to become embedded in the sintered further portion and to sinter the further portion with the previously sintered portion of the material in the prior layer. -23 -
  7. 7. A method according to claim 6, wherein the elongate elements (16) in a first layer are aligned in a different direction to the elongate elements (16) in a second layer, the first layer being different to the second layer.
  8. 8. A method according to any of claims 1 to 7, wherein the step of providing an amount of a material that comprises a plurality of elongate elements (16) comprises: providing a first amount of the material that comprises a plurality of elongate elements (16) on a first area of the selected surface portion of the layer of particulate material; and providing a second amount of the material that comprises a plurality of elongate elements (16) on a second area of the selected surface portion of the layer of particulate material, the second amount being different to the first amount.
  9. 9. A method according to any of claims 1 to 8, wherein the radiation absorbent material and the elongate elements (16) are the same material.
  10. 10. A method according to any of claims 1 to 9, wherein the method further comprises, after the step of providing the amount of a material that comprises the plurality of elongate elements (16) over at least part of the selected surface portion of the layer (6) of particulate material: generating an electric field or a magnetic field; and exposing the deposited elongate elements (16) to the generated electric or magnetic field, thereby causing the deposited elongate elements (16) to substantially align.
  11. 11. A three dimensional object (21) formed using a method according to any ofclaimsl to 10. -24 -
  12. 12. Apparatus for selectively sintering particulate material, the apparatus comprising: one or more printing devices (12) configured to: provide an amount of a radiation absorbent material over a selected surface portion of a provided layer (6) of particulate material; and provide an amount of a material that comprises a plurality of elongate elements (16) over at least part of the selected surface portion of the layer (6) of particulate material; and a radiation source (10) operable to provide radiation (8) across the selected surface portion of the layer (6) of particulate material so as to sinter a portion of the material of the layer (6) including causing the plurality of elongate elements (16) to become embedded in the sintered portion of material; wherein the elongate elements are selected from the group of elongate elements consisting of carbon nanotubes and elongate graphene plates.
  13. 13. Apparatus according to claim 12, wherein a single printing device (12) is operable to provide both the radiation absorbent material and the plurality of elongate elements (16) together in a compound (14) that comprises both the radiation absorbent material and the plurality of elongate elements (16).
  14. 14. A compound (14) for use in a process of selectively sintering particulate material, the compound (14) comprising: a radiation absorbent material; and a plurality of elongate elements (16), the elongate elements being selected from the group of elongate elements consisting of carbon nanotubes and elongate graphene plates.
  15. 15. A compound (14) according to claim 14, wherein: -25 -the compound (14) is a liquid further comprising a solvent; and the radiation absorbent material and the plurality of elongate elements (16) are dispersed throughout the solvent.
GB1504080.1A 2014-03-11 2015-03-11 Sintering particulate material Active GB2526905B (en)