GB2139259A

GB2139259A - Method of preparing fabric softening compositions

Info

Publication number: GB2139259A
Application number: GB08409037A
Authority: GB
Inventors: Robert Michael Butterworth; Martin Alan Wells
Original assignee: Unilever PLC
Current assignee: Unilever PLC
Priority date: 1983-04-08
Filing date: 1984-04-06
Publication date: 1984-11-07
Also published as: GB2139259B; AU2648584A; EP0122140A3; JPS59199865A; GR81778B; PT78379A; AU550895B2; IN159970B; EP0122140A2; ZA842586B; NZ207721A; GB8409037D0; ES531386A0; ES8602106A1; MY8700539A; NO841373L; CA1204562A; BR8401627A

Abstract

A process for preparing an aqueous liquid fabric softening composition comprises making a hot molten mixture of a cationic fabric softener and a nonionic material with a HLB of not more than 10, such as a fatty acid, fatty ester, fatty alcohol or lanolin, adding the molten mixture to water while still hot, mixing to form a dispersion of droplets in the water and thereafter adding an electrolyte such as a salt of lithium, sodium, potassium, calcium, magnesium or aluminium. By forming the dispersion before adding the electrolyte, the viscosity of the end product is reduced and long term stability is improved.

Description

1 GB 2 139 259A 1

SPECIFICATION

Method for preparing fabric softening compositions The present invention relates to a method of preparing fabric softening compositions, in particular for preparing concentrated aqueous liquid fabric softening compositions containing water-insoluble cationic fabric softening agents and fatty acids or other nonionic materials with a low H LB.

It is known from GB 2 039 556 (UNILEVER-Case C.567) to form aqueous liquid fabric softening compositions containing up to 20% of a mixture of a water- insoluble cationic material 10 and fatty acid, the fatty acid acting to improve the efficiency of softening, thereby enabling the level of the cationic material to be reduced without loss of performance. It is also known from EP 13780-A (PROCTER & GAMBLE) to form concentrated aqueous liquid fabric softening compositions from a mixture of a water-insoluble cationic material and a nonionic material selected from hydrocarbons, fatty acids, fatty esters and fatty alcohols, the nonionic material 15 acting to improve the viscosity characteristics of the product when the level of cationic material is above 8%. It is also known from GB 2 039 556 and EP 13780 that preferred compositions can also include low levels of electrolyte such as respectively sodium chloride or calcium chloride, to further control product viscosity.

It is found that when such a composition is prepared by dispersing a premix of the cationic 20 and nonionic materials in water to which the electrolyte has already been added, followed by thorough mixing, the viscosity of the end product is often still higher than desired, particularly when the total active level exceeds about 8%.

It has been proposed in EP 52517 (PROCTER & GAMBLE) that where the composition is based on a mixture of cationic materials, some electrolyte is added, together with a premix of the cationic materials, to water-with vigorous agitation and thereafter a remaining portion of the electrolyte is added. Also in US 3 681 241 (RUDY) it is proposed that compositions based on a mixture of cationic materials are preferably formed in such a manner as to be substantially free of electrolytes, electrolytes being optionally added to the resulting product to regulate the viscosity thereof. Further, GB 1 104 441 (UNILEVER) discloses that products based on a 30 cationic softener and a fatty acid ethanolamide may be made by adding water to a premix of the cationic and nonionic and then, after cooling, adding an electrolyte such as sodium carbonate to thin the product.

We have surprisingly found that, where the composition is based on a mixture of a cationic fabric softener and a nonionic material of low HLB, and is formed by adding a premix of the cationic and the nonionic to water, if the electrolyte is added only after the mixing stage but not before, the end product viscosity is lower. This enables the level of electrolyte used to be reduced without detriment to the properties of the product. It has also surprisingly been found that this post-addition of electrolyte can improve the long term stability of the product.

Thus, according to the invention there is provided a process for preparing a concentrated aqueous liquid fabric softening composition containing at least 8% by weight water-insoluble cationic fabric softener, said process comprising the steps of:

(i) forming a molten mixture containing the water-insoluble cationic fabric softener and a nonionic material having an H LB of not more than 10; (ii) adding the molten mixture to water at an elevated temperature; (iii) mixing the molten mixture and the water together to form a dispersion of the molten mixture in droplet form in the water; and (iv) adding electrolyte in the form of a source of lithium, sodium, potassium, calcium, magnesium or aluminium ions thereto, characterised in that the electrolyte is added after, but not before, the formation of said dispersion.

The water-insoluble cationic fabric softener can be any fabricsubstantive cationic compound that has a solubility in water at pH 2.5 and 20C of less than 10 g/1, Highly preferred materials are quaternary ammonium salts having two C12-C2, alkyl or alkenyl chains, optionally substituted or interrupted by functional groups such as -OH, -0-, -CONH, COO-, etc.

Well known species of substantially water-insoluble quaternary ammonium compounds have 55 the formula R1 R3 + 11.1 N X 1-1 R2 R4 wherein R, and R2 represent hydrocarbyl groups of from about 12 to about 24 carbon atoms; R3 and R4 represent hydrocarbyl groups containing from 1 to about 4 carbon atoms; and X is an 65 2 GB 2 139 259A 2 anion, preferably selected from halide, methyl sulfate and ethyl sulfate radicals. Representative examples of these quaternary softeners include ditallow dimethyl ammonium chloride; ditallow dimethyl ammonium methyl sulfate; dihexadecyl dimethyl ammonium chloride; di(hydrogenated tallow alkyl) dimethyl ammonium chloride; dioctadecyl dimethyl ammonium chloride; dieicosyl dimethyl ammonium chloride; didocosyl dimethyl ammonium chloride; di (hydrogenated tallow) 5 dimethyl ammonium methyl sulfate; dihexadecyl diethyl ammonium chloride; di(coconut alkyl) dimethyl ammonium chloride. Ditallow dimethyl ammonium chloride, di(hydrogenated tallow alkyl) dimethyl ammonium chloride, di(coconut alkyl) dimethyl ammonium chloride and di(coco nut alkyl) dimethyl ammonium methosulfate are preferred.

Another class of preferred water-insoluble cationic materials are the alkylimidazolinium salts 10 believed to have the formula:

CH2-CH2 0 1 11 15 N -2H4-N-C-R7 4_ ,\\ c / 1 1 R6 R9 R8 wherein R,, is an alkyl or hydroxyalkyl group containing from 1 to 4, preferably 1 or 2 carbon atoms, R7 is an alkyl or alkenyl group containing from 8 to 25 carbon atoms, R, is an alkyl or alkenyl group containing from 8 to 25 carbon atoms, and R. is hydrogen or an alkyl group containing from 1 to 4 carbon atoms and A- is an anion, preferably a halide, methosulfate or 25 ethosulfate. Preferred imidazolinium salts include 1 -methyl- 1 (tallowylamido-) ethyl -2-tallowy] 4,5-dihydro-imidazolinium methosulfate and 1 -methyl- 1 -(palmitoylamido) ethyl -2-octadecyi-4,5 dihydro-imidazolinium chloride. Other useful imidazolinium materials are 2-heptadecy]-1 -methyl 1- (2-stearylamido)-ethyl-imidazolinium chloride and 2-lauryl-l - hydroxyethylA -oleyi-imidazoli nium chloride. Also suitable herein are the imidazolinium fabric softening components of US Patent No 4 127 489, incorporated herein by reference.

In the present invention, the water-insoluble cationic softener is present at a total level of at least 8%. The maximum level of cationic softener is determined by practical considerations; even with the nonionic materials to control viscosity it is not generally possible to prepare stable-, pourable emulsions containing more than 26% of cationic softener. When particularly high concentrations are desired, it is preferred to use an imidazolinium softener and preferred compositions contain from 12% to 26% of imidazolinium softener. When a di- long chain non cyclic mono-quaternary softener is employed, it is preferred not to exceed a level of 22%, and a preferred range is 10% to 18%.

The compositions further contain nonionic materials having an HLB of not more than 10, 40 preferably not more than 8. The HLB scale is a known measure of the hydrophilic-lipophilic balance in any compound and can be determined from trade literature. Nonionic materials having lower HLB values are less hydrophilic than those having higher HLB values.

Preferred nonionic materials are selected from:

(i) Ce-C,, fatty acids; (ii) esters Of C,_C24 fatty acids with monohydric alcohols containing from 1 -3 carbon atoms; (iii) C10-C,8 fatty alcohols; (iv) lanolin and derivatives thereof; and (v) fatty acid esters of C,-C, polyhydric alcohols.

Particularly preferred examples of such nonionic materials include lauric acid, myristic acid, 50 palmitic acid, iso-stearic acid, stearic acid, oleic acid, linoleic acid, undecanoic acid, methyl laurate, ethyl myristate, ethyl stearate, methyl palmitate, dodecanol, tetradecanol, hexadecanol, octadecanol, lanolin, lanolin alcohols, hydrogenated lanolin, ethylene glycol monostearate, glycerol monostearate and mono-iso-stearate, sorbitan monostearate and mono-iso-stea rate.

The nonionic material may be present at a level of about 1.0% to about 6. 0%, preferably 55 between about 1.6% and about 4.0%.

The electrolyte is selected from the salts of lithium, sodium, potassium, calcium, magnesium, aluminium and mixtures thereof. Aluminium salts are most preferred. Sodium and potassium salts are least preferred. Preferably the salts contain monovalent anions. Preferred examples include aluminium chloride, aluminium chlorhydrate, calcium chloride, calcium bromide, calcium 60 nitrate and magnesium chloride. The preferred level of highly ionic electrolyte in the final product is at least 10 ppm and less than 3,000 ppm, most preferably 50 ppm to 2,000 ppm. In the case of electrolytes with a more covalent character such as aluminium chlorhydrate, the preferred level is at least 50 ppm and less than 12,000 ppm, most preferably from 120 to 6,000 ppm.

1 1.

3 GB 2 139 259A 3 The first step in the process of the invention is the formation of a molten mixture of cationic and nonionic components. The temperature of this mixture is suitably less than 1 OWC. When this molten mixture is added to water at an elevated temperature, such as above 4WC, preferably above 60C, and thoroughly mixed, a dispersion of the active materials in droplet form is created. The water preferably contains substantially no electrolyte at this stage. Some electrolyte may be tolerated however provided that the weight ratio of electrolyte in the final product to that initially present is at least 3:1 and provided that the water initially contains no more than 300 ppm electrolyte. It is preferred that the level of cationic material in this dispersion is from 8% to 40% by weight, and the level of the nonionic material is preferably 1 % to 9% by weight. While this dispersion may be cooled to ambient temperature at this stage, 10 it is preferred not to cool the dispersion until after the addition of the electrolyte. The electrolyte must be added after the dispersion of the active material in droplet form has been created. At this stage, provided that at least 8% cationic fabric softener has been added, fuFther amounts of the molten mixture may be added. The electrolyte is preferably added in the form of a concentrated solution, such as about 1 - 10% by weight.

Thus in a preferred embodiment of the invention the electrolyte is added in the form of a concentrated solution, after the formation of the dispersion but before the dispersion is cooled below 4WC. This is of particular benefit if the cationic softener contains hardened (ie mainly saturated) alkyl groups.

Where the cationic raw material used for making the product already contains electrolyte, we 20 have found it to be of advantage if at least a portion of the added electrolyte contains the same cation. Thus, where for example the cationic raw material contains sodium ions, the added electrolyte preferably also contains some sodium ions, advantageously together with an electrolyte containing more highly charged ions, such as calcium ions.

The compositions may also contain one or rnore optional ingredients selected from non- 25 aqueous solvents such as Cl-C4 alkanols and polyhydric alcohols, pH buffering agents such as weak acids eg phosphoric, benzoic or citric acids (the pH of the compositions are preferably less than 6.0), antigelling agents, perfumes, perfume carriers, fluorescers, colourants, hydrotropes, antifoaming agents, anti rede position agents, enzymes, optical brightening agents, opacifiers, stabilisers such as guar gum and polyethylene glycol, anti-shrinking agents, anti-wrinkle agents, 30 fabric crisping agents, spotting agents, soil-release agents, germicides, fungicides, anti-oxidants, anti-corrosion agents, preservatives, dyes, bleaches and bleach precursors, drape imparting agents and antistatic agents.

These optional ingredients may be added to the active melt, to the water before forming the dispersion or after adding the electrolyte as appropriate.

It is particularly advantageous if the water to which the molten cationic/ nonionic mixture is added already contains a dispersing aid. This dispersing aid should be a water non-anionic surfactant having an H LB of greater than 10, ideally greater than 12. In this context, the term watersoluble- means having a solubility of more than 1.09/1 in water at pH 2.5 and at 2WC.

Preferred examples include water-soluble quaternary ammonium salts (such as Arquad 16, 40 Arquad 2Q, ethoxylated quaternary ammonium salts (such as Ethoquad 0. 12), quaternary diamine and ethoxylated diamine salts (such as Duoquad T), ethoxylated amines and diamines (such as Ethoduomeen T/25, Ethomeen T/ 15) and their acid salts, ethoxylated fatty esters of polyhydric alcohols (such as sorbitan monolaurate 20 EO), ethoxylated fatty alcohols (such as Brij 58-cetyl alcohol 20 EO) and ethoxylated fatty acids (such as Myrj 49- stearic acid 20 EO). 45 A useful test for whether a particular material will be a suitable dispersing aid is one which results in a lower product viscosity after the addition of the electrolyte.

The dispersing aid may be present at a level of at least 0. 1 %, preferably at least 0. 2% by weight based on the final product. Usually, it will not be necessary to use more than 2.5%, preferably not more than 1.0% dispersing aid.

It is preferred that the weight ratio of the cationic fabric softener material to the low H113 nonionic material is in excess of about 2.0A, such as in excess of about 3.0A, most preferably within the range of 5:1 to 20A. A preferred composition contains about 8% to about 22% of the cationic material, about 1.0% to about 6% of the nonionic material and from about 0.01 % to about 0.2% of the electrolyte.

The invention will now be illustrated by the following non-limiting examples, in which parts and percentages are by weight, based on the weight of the end product. Where materials are referred to by their commercial names, the percentages quoted are percentages of the active materials.

EXAMPLE 1

A homogenous molten premix was prepared containing 10.9% di(soft tallow) dimethyl ammonium chloride (Arquad 2T) and 2.6% hardened tallow fatty acid (Pristerene 4916). This premix was added at a temperature of 60'C to demineralised water at the same temperature.

After thorough mixing with a high speed constant torque stirrer the dispersion formed was 65 4 GB 2 139 259A 4 allowed to cool to 25'C and thereafter 0. 1 % calcium chloride (in the form of a 10% solution) and 1 % perfume were added.

The viscosity of the product measured 110 sec - 1 was 30cP.

The experiment was repeated with the only difference that the calcium chloride was predissolved in the water. In this case the product viscosity was 438 cP.

This example demonstrates the benefit of post-addition of the electrolyte.

EXAMPLE 2 Example 1 was repeated using a molten pre-mix of 17% di(soft tallow) imidazolinium methosulphate (Varisoft 47 5) and 3% Pristerene 4916. In this example, various levels of 10 various electrolytes were added. The viscosity of the product was measured immediately after preparation and then again after 12 weeks storage at room temperature. The results are set out in the following Table.

Electrolyte Level Viscosity Initial After storage NaCI 0.2% 72 400 CaCI, 0.2% 62 120 20 M9C12 0.17% 48 91 AIC13 0.15% 60 67 This example illustrates the benefit of using calcium, magnesium or aluminium salt as the 25 electrolyte, rather than sodium salts.

EXAMPLE 3

Similarly beneficial results can be obtained by processing in the same manner compositions with the following formulations: 30 A. Arquad 2HT 12.0% Pristerene 4916 1.5% CaC12 (added at 130C) 0.03% Water balance 35 Similar results are obtained when the calcium chloride is replaced by the same level of aluminium chloride or sodium chloride, added at 60C and/or when the levels of Arquad 2HT and Pristerene 4916 are changed to 10.9% and 2.6% respectively. A lower initial viscosity is achieved with these products than if identical formulations are prepared by adding the electrolyte after cooling.

1 B. Varisoft 475 14.5% Hardened rape seed fatty acid 3.5% CaC12 or M9C12 0.2% 45 Water balance C. Arquad 2T 17.0% Pristerene 4916 1.0% Aluminium chlorhydrate 1.0% 50 Water balance D. Arquad 2T.10.9% Pristerene 4916 2.6% Perfume 1.0% 55 CaCI, (added at 60'C) 0.025% Water balance E. Di(hardened tallow) imidazolinium methosulphate (Varisoft 445) 11.0% 60 Commercial iso-stearic acid (ex Emery) 2.5% NaC] 0.15% Water balance This composition is particularly beneficial if the sodium chloride is added at 60'C, and still 65 GB 2 139 259A 5 more beneficial if the sodium chloride is replaced by calcium chloride, magnesium chloride or aluminium chloride..

F Varisoft 445 12.2% Prifac 7962 (unhardened soyabean 5 fatty acid containing 54% linoleic acid and 30% oleic acid) 2.8% Calcium chloride 0.2% Water balance 10 EXAMPLE 4

Similarly beneficial results can be obtained by processing in the same manner compositions with the following formulations:

15 EXAMPLE NO 4A 413 4C 41) 4E 4F 4G Ingredients % Arquad 2HT 22 12 12 8 18 12 8 Lanolin 4 2 6 4 - - - 20 Lanolin alcohol (Hartolan) Calcium chloride Perfume Water 0.1 0.07 1 1 6 1 2 0.05 0.03 0.1 0.1 0.1 1 1 1 1 1 -------------------- balance -------------------- 25 Added to the dispersion after cooling. The calcium chloride may be replaced by a similar level of aluminium chloride. Beneficial results may be obtained by adding the calcium chloride or other electrolyte before cooling the dispersion.

In this Example the Arquad 2HT may be replaced by Varisoft 445.

EXAMPLE 5

EXAMPLE NO 5A 513 5C 5D 5E Ingredients (%) Arquad 2HT 12 8 9 15 12 40 Octadecanol 1 1 3 5 6 Calcium chloride 0.1 0.1 0.06 0.1 0.05 Perfume 0.6 - 1.0 0.8 Water' -------------- balance -------------- In this Example the calcium chloride may be added after or (more preferably) before cooling the dispersion. Calcium chloride may be replaced by magnesium or aluminium chloride. Arquad 2HT may be replaced by Varisoft 445. The octadecanol may be replaced by glycerol monostearate, glycerol mono-iso-stea rate, sorbitan monostearate or sorbitan mono-iso-stea rate. 50 Any two or more of these modifications may be combined.

EXAMPLE 6

The following formulation was prepared by the method set out below.

55 Arquad 2HT 12.0% Lanolin 4.0% Phosphoric acid 0.03% Perfume 0.75% Calcium chloride 0.05% 60 Dye 0.0075% Water balance The molten mix of the Arquad 2HT and the lanolin was formed at 6WC. This molten mix was 65 added to demineralised water at 60Q which already contained the phosphoric acid (added as a 65 6 GB 2 139 259A 6 pH buffer). After thorough mixing to form a dispersion of the active materials in droplet form, the calcium chloride was added in the form of a 10% solution. Thereafter the mixture was cooled to ambient temperature and the perfume and dye added.

EXAMPLE 7

The following formulations demonstrate the range of active levels that are possible within the scope of this invention. In each case the active materials were premixed at 60Q added to water at the same temperature and shear mixed to form a dispersion in droplet form. Then the calcium chloride was added in the form of a 10% solution. After further mixing the perfume and dye were added and thereafter the mixture was cooled to ambient temperature.

EXAMPLE NO 7A 713 7C 7D Ingredients % Arquad 2HT (hard) 12.5 Pristerene 4916 1.7 Ca02 0.05 Perfume 0.55 Dye 0.0075 Water 14.7 2.0 0.06 0.75 0.0075 ------------- balance ------------- Total active level 14.2 16.7 20.0 18.0 17.6 2.4 0.07 0.75 14.5 3.5 0.05 1.0 EXAMPLE NO 7E 7F 7G 7H 71 Ingredients (%) Arquad 2T (soft) Pristerene 4916 CaC12 Perfume Dye Water 12.0 14.0 16.53 11.5 11.5 1.5 2.0 2.07 2.0 2.3 30 0.04 0.06 0.07 0.03 0.03 0.55 0.75 0.75 0.55 0.55 0.0075 0.0075 0.0075 0.0075 0.0075 a, 1 EXAMPLE 8

The benefit of including a dispersing aid in the water to which the active premix is added is illustrated as follows. An active premix was prepared by mixing 10.5 parts of Arquad 2HT with 2.5 parts Pristerene 4916 and heating to 70'C. This premix was then added to distilled water at 40 70C containing the dispersing aid. After stirring to form a dispersion in droplet form, calcium chloride was added to the hot mixture using a 10% solution. The end product composition was:

Arquad 2HT 10.5% Pristerene 4916 2.5% 45 CaC12 0.03% Dispersing aid 0.5% After cooling to room temperature the viscosity of each product was measured 'at 110 sec - 1 at 25C. Various materials were used as dispersing aids. The results were as follows:

EXAMPLE NO DISPERSING AID (H LB) VISCOSITY (cP) 8A Ethoduorneen T/25 (18.5) 40 55 8B Myrj 49 (15.0) 30 8C Brij 76 (12.4) 24 8D None (Control) 204-240 BE Span 20 8.6) 351 60 In a further set of experiments using an apparatus of slightly different dimensions but otherwise using a similar technique, the results were:

7 GB 2 139 259A 7 EXAMPLE NO DISPERSING AID (HLB) VISCOSITY (cP) 8F Arquad 16 (15.8) 39 5 8G Ethoquad 0/ 12 (about 15) 27 8H Duornac T (10.7) 219 81 None (control) 300 10 These results demonstrate that the product viscosity is lowered when the dispersing aid has an HLB of more than 10 (Example 8H for instance) but not when the dispersing aid is less than 10 (Example 8 E). Also it is apparent that the benefit is most noticeable where the dispersing aid has an HLB above 12.0 (Examples 8A to 8C, 8F and 8% The dispersing aids used in this Example are commercial materials which are approximately as 15 follows:

Ethoduorneen T/25: Ethoxylated N-tallowyl 1,3 propane diamine with 15 ethoxylene oxide groups per molecule Myrj 49: Ethoxylated stearic acid with 20 ethylene oxide groups per molecule.

Brij 76: Ethoxylated steary] alcohol with 10 ethylene oxide groups per molecule.

Span 20: Sorbitan monolaurate.

Arquad 16: Cetyl trimethyl ammonium chloride.

Ethoquad 0/ 12: Oleyl, methyl bis (2 hydroxyethyl) ammonium chloride.

Duornac T: N-tallowyl 1,3 propane diamine diacetate.

EXAMPLE 9

Using the process described in Example 1, a product was formed containing 10.9% Arquad 2T, 2.6% Pristerene 4916, 0.05% calcium chloride and 0.75% post-dosed perfume. The calcium chloride was added either before addition of the molten active to the water (pre-dosed), after formation of the dispersion (post-dosed) or part pre-dosed and part post-dosed. In each case the viscosity of the product was measured. The results were:

Pre-dosed CaC12(%) Post-dosed Ca02(%) viscosity (CP) 0 0.02 0.05 0.05 0.03 0 38 322 948 These results demonstrate the particular benefit of adding all the electrolyte after the formation of the dispersion.

In all the above Examples, the initial level of electrolyte in the process water was less than 10 ppm.

EXAMPLE 10

82.5 parts of water containing 50 PPM Ca/MgC03 water hardness and small amounts of dye were heated to 66C in a vessel containing 3 inclined paddles of 0.88 X vessel diameter. 17.5 parts of a premix of Arquad 2HT (75% active) and Pristerene 4916 at 65C was added to the stirred hot water over a period of 10 minutes via a jet manifold between the top two agitators. 50 This mixture was stirred for 20 minutes at which point 0.25 parts of a 10% CaCl2 solution was added. After stirring for a further 10 minutes the mixture was cooled to 35C. 0.72 parts of perfume were added and stirring continued for a further 5 minutes. The product was finally cooled to 30C and stored.

The final product had the following composition:

Arquad 2HT 12.0 Pristerene 4916 1.5 Perfume 0.72 Added CaC12 0.025 Water and minor ingredients to 100

Claims

1 - A process for preparing a concentrated aqueous liquid fabric softening composition 65 8 GB 2 139 259A 8 containing at least 8% by weight water-insoluble cationic fabric softener, said process comprising the steps of: (i) forming a molten mixture containing the water-insoluble cationic fabric softener and a nonionic material having an H LB of not more than 10; 5 (ii) adding the molten mixture to water at an elevated temperature; (iii) mixing the molten mixture and the water together to form a dispersion of the molten mixture in droplet form in the water; and (iv) adding electrolyte in the form of a source of lithium, sodium, potassium, calcium, magnesium or aluminium ions thereto, characterised in that the electrolyte is added after, but not before, the formation of said dispersion.

2. A process according to Claim 1, characterised in that the composition is cooled to ambient temperature after the addition of the electrolyte.

3. A process according to Claim 1, characterised in that the electrolyte is selected from a source of calcium, magnesium or aluminium ions.

4. A process according to Claim 1, characterised in that the waterinsoluble cationic fabric 15 softener is selected from water-insoluble quaternary ammonium salts and imidazolinium salts.

5. A process according to Claim 1, characterised in that the nonionic material is selected from (i) C8-C24 fatty acids; (ii) esters Of C,_C24 fatty acids with monohydric alcohols containing from 1 -3 carbon atoms; 20 (iii) C10-C18 fatty alcohols; (iv) lanolin and derivatives thereof; and (v) fatty acid esters Of C2-C, polyhydric alcohols.

6. A process according to Claim 1, characterised in that the weight ratio of the cationic fabric softening agent to the nonionic material in the composition is from 5:1 to 20A.

7. A process according to Claim 1, characterised in that the water to which the molten mixture is added in step (ii), already contains a dispersing aid.

8. A process according to Claim 7, characterised in that the dispersing aid is selected from water-soluble cationic and water-soluble nonionic surfactants having an HI-B of more than 10.

9. A process according to Claim 1, characterised in that after the addition of the electrolyte, 30 the composition contains from 8% to 22% of the water-insoluble cationic fabric softening material, from 0.5% to 4% of the nonionic material, and from 0.01% to 0.2% of the electrolyte.

Printed in the United Kingdom for Her Majesty's Stationery Office, Dd 8818935, 1984, 4235. Published at The Patent Office, 25 Southampton Buildings, London, WC2A l AY, from which copies may be obtained.