GB2114153A - Aluminium silicon alloy - Google Patents
Aluminium silicon alloy Download PDFInfo
- Publication number
- GB2114153A GB2114153A GB08139191A GB8139191A GB2114153A GB 2114153 A GB2114153 A GB 2114153A GB 08139191 A GB08139191 A GB 08139191A GB 8139191 A GB8139191 A GB 8139191A GB 2114153 A GB2114153 A GB 2114153A
- Authority
- GB
- United Kingdom
- Prior art keywords
- alloy
- weight
- silicon
- zinc
- aluminium
- Prior art date
- Legal status (The legal status is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the status listed.)
- Withdrawn
Abstract
An aluminium silicon alloy including zinc, for use as a bearing lining on a steel backing, has a composition of, by weight, @% Si 1-4 Zn 8-12 Cu 0-0.5 Pb 0-3.0 Al balance a
Description
SPECIFICATION
Aluminium silicon alloy
The present invention relates to aluminium alloys for use as a bearing material, for example for use in internal combustion engines.
British Patent No. 1,593,006 discloses analuminium/silicon/zinc alloy comprising 2 to 8% by weight of silicon and 2 to 8% zinc with minor additions of lead and copper, the balance being aluminium. It is believed that this alloy may have been developed from an alloy comprising 1.5% by weight silicon and 5% by weight zinc, which is used in the manufacture of crankshaft bearings in
Germany.
Bearing alloys of the aluminium silicon zinc type are generally continuously cast, rolled, and roll bonded to steel, to produce a bimetal strip from which the crankshaft bearings are formed.
The rolling operation is preferably carried out cold, since cold rolling is a quicker and less costly operation than hot rolling. However, cold rolling of the alloys described in British Patent No.
1 593006 is difficult in that extensive edge cracking is found to occur when the silicon content is towards the top end of the range.
Furthermore, alloys with a silicon content towards the bottom end of the range are less satisfactory in their bearing properties when the zinc content is limited to a maximum of 8%.
It is an object of the present invention to provide an aluminium/silicon/zinc alloy having satisfactory bearing characteristics but having improved processing characteristics.
According to the invention there is provided an alloy comprising from 1 to 4% silicon by weight and from 8 to 12% zinc by weight, the balance being aluminium.
It has been found that by limiting the silicon content to maximum of 4% and increasing the zinc content to 8-12%, there is no loss of bearing properties, but a considerable advantage is gained in processing characteristics.
In fact, it has been found that the alloys described in the present application may be cold rolled to a much greater extent than those described in the prior art without significant edge cracking. Material utilisation and process economics may thereby be improved
Preferably, the silicon content is from 13%, for example about 3% by weight, preferably, the zinc content is from 9 to 1 1% for example about 10% by weight.
Minor additions of up to 3% lead and up to 0.5% copper have proved to be beneficial in certain instances and these may optionally be included in the alloy.
Such an alloy may be used as a bearing lining on a backing, for example a backing of steel, aluminium or aluminium alloy. The bearing may be formed directly or first formed as a blank and subsequently formed into the desired shape.
The invention may be carried into practice in various ways and one embodiment will be described by way of illustration in the following example.
Example I
In this example, an alloy in accordance with the invention is formed as the lining on a steel backed crankshaft bearing.
An alloy having a composition comprising 3% by weight silicon and 10% by weight zinc, the balance being aluminium was established in a melting furnace. The melt was transferred to a continuous casing machine and cast into a billet 200 mm x 25 mm and cut into lengths. The cast surface was removed to a depth of 1 mm by machining. The machined billet was then cold rolled to 1.5 mm thickness in a succession of passes, and coiled.
One surface of the coiled alloy was brushed and roll bonded to the prepared surface of a coil of steel. The bi-metal strip was annealed at 31 0 C to consolidate the bond, and crankshaft bearings were subsequently formed from the annealed bimetal by conventional techniques.
1. An alloy comprising from 1 to 4% silicon by weight and from 8 to 1 2% zinc by weight, the balance being aluminium.
2. An alloy as claimed in Claim 1 in which the silicon content is about 3% by weight.
3. An alloy as claimed in Claim 1 or Claim 2 in which the zinc content is about 10% by weight.
4. An alloy as claimed in any preceding claim further including up to 3% by weight of lead.
5. An alloy as claimed in any preceding claim further including up to 0.5% by weight of copper.
6. A bearing comprising a metal backing having a bearing layer comprising an alloy as claimed in any preceding claim.
7. A bearing constructed and arranged substantially as herein specifically described in
Example I.
**WARNING** end of DESC field may overlap start of CLMS **.
Claims (7)
1. An alloy comprising from 1 to 4% silicon by weight and from 8 to 1 2% zinc by weight, the balance being aluminium.
2. An alloy as claimed in Claim 1 in which the silicon content is about 3% by weight.
3. An alloy as claimed in Claim 1 or Claim 2 in which the zinc content is about 10% by weight.
4. An alloy as claimed in any preceding claim further including up to 3% by weight of lead.
5. An alloy as claimed in any preceding claim further including up to 0.5% by weight of copper.
6. A bearing comprising a metal backing having a bearing layer comprising an alloy as claimed in any preceding claim.
7. A bearing constructed and arranged substantially as herein specifically described in
Example I.