GB2101759A - Reflective data storage medium - Google Patents

Abstract

A reflective data storage medium having electrically conductive metal particles with a size less than .05 microns dispersed in the surface of a low melting temperature dielectric material. In this manner there is produced a reflective electrically non-conducting recording medium.

Description

SPECIFICATION Reflective data storage medium The invention relates to laser recording media, and more particularly to a reflective silver data recording and storage medium useful for reading laser recordings immediately after laser writing.

Previously, many types of optical recording media have been developed for laser writing.

Some of these media require post write processing before they can be read, and some can be read immediately after laser writing. The media of interest herein are for "direct read after write" capability, commonly known as "DRAW" media. Presently known laser DRAW media are thin metal films in which holes may be melted, composite shiny films whose reflectivity at a spot may be reduced by evaporation, thin films of dyes or other coatings which can be ablated at.a spot, and dielectric materials whose refractive-index may be changed at a point, causing a scattering of light when scanned with a read laser.

The most common DRAW media are thin metal films, usually on a glass substrate. Thin metal films have several advantages. First, they can be produced easily in small quantities with commercially available sputtering equipment. Second, they can be read either by reflection or by transmission. Third, films of tellurium and bismuth have relatively high recording sensitivies.

Fortunately, for all of these reasons, metal films have enabled a large amount of research to be conducted and progress to be made in the design of optical data storage systems. To date, tellurium has evolved as the most widely used of the metal films. However, tellurium must be manufactured by an expensive, batch-type, vacuum sputtering technique; it does not form a tenacious coating; and it introduces manufacturing and environmental complications because of its toxicity and since it rapidly oxidizes in air it must be encapsulated in an airtight system in order for it to achieve an acceptable archival life.

What is particularly desirable about tellurium is that it has a low melting temperature for a metal, 450"C, and also a very low thermal conductivity of 2.4 watts per meter per degree Kelvin at 573"K. In comparison, silver metal has a melting temperature of 960"C and a thermal conductivity of 407 watts per meter per degree Kelvin at the same elevated temperature. When these two metals are considered for laser recording with short pulses of laser power, the tellurium is far superior from a recording sensitivity standpoint since the low thermal conductivity keeps the heat generated by the laser beam confined to a small area and the lower melting temperature facilitiates the melting of the hole. Conversely, silver metal, because of its high thermal conductivity, about 1 70 times that of tellurium, would not normally be considered suitable for laser recording.

Although it is possible to produce reflective metallic coatings of many types on substrates by vacuum sputtering or evaporation, silver is relatively unique in that it can also be created by photographic techniques and, in particular, by silver diffusion transfer. In U.S. patent 3,464,822 Blake discloses a silver diffusion transfer reversal process for creating electrically conducting silver images for the fabrication of printed circuit boards. That invention, in turn, is based upon silver diffusion transfer process inventions of the reversal type, leading to black nonreflective and non-conductive images, one example being U.S. patent 2,500,421 by Dr. E. H.

Land. The silver diffusion transfer reversal process forms the basis of direct positives by the Polaroid Land process of Polaroid Corporation and the Gevacopy and Copyrapid processes of Agfa-Gevaert. These reversal processes should be distinguished from the silver diffusion negative process. One such process leading to black non-reflecting and non-conducting images, is described in U.S. patent 3,179,517 by Tregillus. A silver diffusion transfer negative process is used in the present invention.

It is well known that if very small, high electrical conductivity metal spheres or spherical particles are distributed through a dielectric medium, the effective dielectric constant or refractive index will rise owing to the added induced dipoles of the metal particles.

Previously, a reflective silver laser recording medium was the subject of a prior invention wherein a processed black silver emulsion was converted to a reflective recording medium by heating at least to 250"C until a shiney reflective appearance is achieved.

The present invention provides a reflective data storage medium comprising electrically conductive metal particles having a size primarily less than .05 microns dispersed in a surface of low melting temperature dielectric material so as to produce a reflective electrically nonconductive recording medium.

According to a feature of this invention there is provided a method of making the reflective laser recording media of the invention comprising dispersing electrically conductive metal particles having a size primarily less than .05 microns in a surface layer of low melting temperature dielectric material so as to produce a reflective electrically non-conductive recording medium.

Among the advantages of the preferred embodimants of the invention are the fact that it may be manufactured without the use of a vacuum system and on a continuous basis and which may be used to record low-reflective spots in a reflective field with relatively low energy laser pulses.

Control indicia and certain data base data may be pre-recorded by photographic means to faciiitate the use of discs or plates in both the recording apparatus and the playback apparatus.

Replication of optically recording media is permitted by photographic contact printing on a rigid or flexible substrate that can be read in reflection or transmission. The laser recording and data storage medium disclosed herein can be fabricated from commercially available photoplates and films or minor modifications thereto, to achieve low cost. A high temperature processing step is not required and therefore the use of ordinary, low-cost photographic plastic film bases or other available plastics as substrate materials is permitted thus allowing fabrication of recording discs with center holes by a low-cost stamping operation. Also disclosed herein is a single-step silver diffusion transfer photographic process which could produce a highly reflective electrically nonconductive surface layer having a thickness of 1 micron or less contained almost entirely within the gelatin or colloidal carrier.

It has been discovered that the silver in a photosensitive, silver-halide emulsion of a photoplate or film can be brought to a surface of the emulsion in a pre-exposed pattern to form a reflective laser recording and storage medium by a novel single step silver diffusion transfer negative photographic process. First a volume concentration gradient of silver precipitating nuclei is created at one surface of the emulsion by actinic radiation or other methods, with the gradient of decreasing concentration in the depthwise direction, and this is followed by a single step monobath silver diffusion transfer development process that is primarily a solution physical development process which is used to build up the volume concentration of silver at the surface containing the precipitating nuclei until the surface becomes reflective.

This reflective surface layer is typically less than 1 micron thick; has a reflectivity of 15% to 50%; is electrically a non-conductor and thermally a poor conductor since the matrix is typically gelatin, which holds the high concentration of tiny particles and agglomerates of silver particles which are separated and isolated from each other by the gelatin matrix. Thus, although the layer reflects light like a metal, it melts easily like a plastic, with the result that its recording sensitivity is in the class of bismith and tellurium and at least an order of magnitude more sensitive than that of a thin, continuous silver metal layer.

A principal step in the process is an exposure or surface activation of the area to be used for data recording or alternatively non-data recording, which affects mainly the silver-halide grains close to one of the surfaces of the emulsion. Such an exposure or activation creates a surface latent image having a depthwise exposure gradient, with a concentration of exposed silver-halide which is greatest at the one surface and least in the interior of the emulsion. The surface of greatest concentration may be either the surface distal to the substrate or proximate thereto, depending on where laser writing will initially impinge on the medium.

For example, if laser writing is on the upper surface, the emulsion surface distal to the substrate has the greatest concentration of exposed silver-halide.

The surface latent image may include images in the photographic recording sense or may cover the entire surface, but is always located primarily at a surface of a photographic emulsion, which also contains some unexposed silver halide, in the interior of the emulsion. Such a surface latent image may be made by light itself, i.e., by intentionally exposing one surface or the other of the photosensitive emulsion to light where data recording will occur, the remaining area being masked. Alternatively the surface treatment may be made by a surface activating chemical, namely a fogging agent, such as hydrazine or a borohydride salt such as potassium borohydride, which performs a surface latent image activation on silver-halide emulsions similar to a light exposure. Alternatively during the original manufacture of the silver-halide photographic plate or film a very thin gelatin layer containing silver-precipitating nuclei would be included at the surface distal to or the surface proximate to the substrate, which would be the basis for creating a reflective surface at either of these two surfaces.

The second principal step of the process involves contacting the exposed or activated and unexposed silver-halide with a monobath containing a silver-halide developing agent for developing the surface latent image created in the exposure or activation step. Simultaneously a silver-halide solvent in the monobath, preferably a soluble thiocyanate or ammonium hydroxide, reacts rapidly with unexposed and undeveloped silver-halide to form soluble complexed silver ions which are transported by diffusion transfer to nuclei of the developing latent image or in the alternative case to the layer containing nuclei, where the silver in the complexed silver ions is precipitated in the presence of the silver halide developing agent. This process forms a reflective silver image which is a negative of the light exposed or surface activated latent image.

Recording is accomplished by puncturing through the reflective component with a laser beam so as to create a hole in the reflective component which may later be detected by a variety of means such as reduced reflection of the hole; scattering of light from the hole; increased light transmission through the hole; and, if the recording is done on the surface distal to the substrate, detection may be accomplished by means of mechanically probing the surface relief image of the hole.

An advantage of the above method for making a reflective recording medium is that it allows a low-cost manufacturing process to create a precise very thin patterned reflective silver layer on the medium which could be used for laser recording without resorting to high-temperature processes which could limit the selection of substrate materials. Several embodiments of the present method may be carried out by continuous manufacturing operations, as opposed to batch operations, but batch procedures may also be used. in the drawings: Figure 1 is a top plan view of the recording medium of the present invention; Figure 2 is a side sectional view of the recording medium of Fig. 1, taken along lines 2-2; Figures 3-8 are detail views of the recording medium of Fig. 1 showing the results of different combinations of photographic processing steps for making the finished recording medium; Figures 9-11 are side sectional views of three versions of the recording medium of Fig. 1 showing methods of laser reading or writing; Figure 12 is a plot of relative contrast ratio versus laser power for two materials; and Figure 13 is a plot of percent reflectivity versus exposure for two materials.

The reflective laser recording medium of the present invention is made in two principal steps: one step involving formation of a surface latent image, the other step involving silver diffusion transfer.

I. Surface Latent Image Formation Surface latent image formation for a laser recording medium is achieved by exposing a region of unexposed photographic emulsion to light or to a fogging agent over the area where laser writing is to be done. Alternatively during the original manufacture of the silver-halide photographic plate or film a very thin gelatin layer containing silver-precipitaing nuclei would be included at the surface distal to or the surface proximate to the substrate, which would be the basis for creating a reflective surface at either of these two surfaces. To record control indicia on the medium, part of the emulsion may be masked or alternatively may have been exposed and chemically developed prior to this surface latent image formation step. Typically such a medium is a disc, as illustrated in Fig. 1; however it could be a plate or film strip.

Fig. 1 shows a disc 11 having an inner periphery 1 3 and an outer periphery 1 5. The interior of the inner periphery 1 3 is void so that a centering collar may be used to hold disc 11 on a spindle for high speed rotation. While the recording medium of the present invention is described as a disc, a disc configuration is not essential for operating of the recording medium, For example, the recording medium may be a flat sheet-like material which could be square and with a central hub rather than a hole. It could also be a non-rotating rectangular plate. However, rotating discs are preferred for fast random access to medium amounts of data and non-rotating rectangular plates in stacks are preferred to provide intermediate speed random access to large amounts of data by mechanically selecting a plate and scanning it by mechanical and electrooptical means. The disc of Fig. 1 is photographically partitioned into recording and nonrecording areas. For example, a first annular recording zone 1 7 could be spaced from a second annular recording zone 1 9 by an annular guard zone 21. The function of the guard zone may be to separate different recording fields, to carry control information, such as timing signals and to provide space for data read-write transducers to reside when not over recording areas. While such guard bands are preferable, they are not essential to the operation of the present invention.

It should be noted that the recording fields are for data and control signal recording, while the guard band is not for data recording, but may have control signal recording thereon. The recording field 1 9 is shown to have a plurality of concentric, circumferentially-spaced servo guides 23 thereon. Such servo guides are thin lines which define the spaces between circular paths wherein data are written. The pattern for such lines is applied photographically as explained below with reference to Figs. 3-8.

Fig. 2 shows a side sectional view of the recording medium of Fig. 1. The medium consists of a substrate 27 which is a sheet-like layer which may be transparent or translucent, preferably a dimensionally stable material, like glass or plastics used for photographic film bases. Opaque, light-absorptive materials will work in those applications of the present invention where light transmission through the substrate is not desired, Transparency or absorptivity of the substrate is desired so that when the light beam of the reflective playback apparatus impinges upon a recorded spot, it either passes through the substrate or is absorbed by it with minimum reflection. If the substrate is absorptive, it may be absortive at the wavelengths of the recording beam or the reading beam, or preferably both. The most common photographic film bases are polyester polyterephthalate, polycarbonate, or cellulose triacetate.

For the case where the substrate is transparent, recording and reflective reading of the data can be done through the substrate as shown in Figs. 10 and 11, or from the side distal to the substrate as shown in Fig. 9. For transmissive read, the configurations of Figs. 10 and 11 may be used. If the substrate is absorptive then reflective read is the only possibility and the configuration of Fig. 9 would be used.

The thickness of the substrate is not critical when the laser beam is directed onto the surface as shown in Fig. 9, but it should have sufficient thickness to provide strength for resistance against breakage. If the laser beam is directed through a transparent substrate, as in Figs. 10 and 11, then in order to maintain focus of the beam the thickness of the transparent substrate would have to be very uniform (for example, as obtainable from float glass or selected high quality drawn glass). Also, the thickness of the substrate may depend on the overall size of the recording medium being used. For a 1 2-inch disc, a thickness of 1/8 inch may be suitable.

The purpose of substrate 27 is to support a silver-halide emulsion coating 29, which is uniformly applied to the substrate in a conventional manner and which is converted by surface latent image formation and silver diffusion transfer into components 32 and 33 in Figs. 9, 10 and 11. This process for creating the reflective layer 32 does not require any chemical constituent within the emulsion other than a conventional silver-halide held in a suitable colloid carrier, preferably gelatin. They may also contain optical and chemical sensitizers, anti-fogging agents, stabilizing compounds, emulsion hardeners and wetting agents. However, when commerical photoplates or films are used. they may contain certain physical characteristics or added chemical ingredients which could lead to favorable or unfavorable results.

One of the advantages of gelatin is that it has a relatively low melting temperature, less than 400on, which aids laser recording. Such low melting temperature carriers are preferred in the present invention.

If a screening dye is used within the emulsion to create an exposure gradient in conjunction with actinic radiation exposure, the dye should be selected so that it is not trapped within layer 32 so as to cause a streaked surface of non-uniform reflectivity.

Emulsion thickness of 3 to 6 microns are adequate to contain sufficient silver-halide emulsion to build up the reflective layer by the complexing and diffusion transfer steps. If thicker commercial emulsions are used along with long processing times, the reflective layer may become too thick or too thermally conducting to permit recording with low-power iasers. The thicker coating requires a higher laser beam power to penetrate it and a higher thermal conductivity leads to faster heat flow away from the spot being recorded, also leading to higher recording powers.

If a hardened emulsion is desired it may be preferable to harden or cross link the gelatin after forming reflective layer 32. If the emulsion is hardened initially, then it will swell to a reduced extend during mono-bath processing thereby reducing the rate at which the silver-halide is dissolved and complexed, thus extending the process time.

Small silver-halide grains typically found in commercially available high resolution or high definition photoplates used in photomask making, holography and high-resolution recording are excellent for producing reflective laser-recording materials. These emulsions typically have mean grain sizes of .05 micron and a spread of about .007 micron. One type, the Agfa-Gevaert Millimask HD photoplate, has a mean grain size of .035 micron and a spread of .0063 micron.

The finer grains result in minimizing the micro variations or granularity in reflectivity and thickness of the reflective component and thereby permit recording and reading of smaller holes than for coarse grain emulsions. The finer grain emulsions also dissolve faster owing to their greater surface-to-volume ratio which leads to a shorter process time.

High resolution emulsion coated glass plates having these characteristics are commercially available and are known as photoplates which are used to make photo-masks for the manufacture of semiconductor integrated circuits. For example, emulsion coated photoplates suitable for use herein are manufactured by Agfa-Gevaert of Belgium, Konishiroku Photo Industries Co., Ltd. Of Japan and the Eastman Kodak Company.

The shiny reflective component 32 in Figs. 9, 10 and 11 result from the photographic monobath processing described herein but the silver is present initially as silver-halide and reflectivity does not initially exist in the emulsion. Thus at the inception the silver of reflective component 32 is found in the photographic emulsion 29, which is uniform in its composition.

An inert snubbing layer, not shown, is usually used to attach the substrate 27 to the emulsion 29. Following the photographic conversion of the present invention the emulsion 29 of Fig. 2 produces a reflective component 32 at the emulsion surface shown in Fig. 9, with a lowreflective underlayer 33 beneath it. The reflective layer 32 is more sharply defined in thickness when nuclei are included during manufacturing or when a fogging agent is used for surface activation. Thus, although Figs. 9, 10 and 11 depict a sharp boundary for reflective component 32, if light exposure is used such is not the case but actually the concentration falls off and continues into underlayer 33.

Thus when light exposure is used underlayer 33, while not completely depleted of silver, contains much less silver than reflective component 32. Optically, underlayer 33 is either clear or reddish in color which is transmissive to red light having wavelengths of 630 nanometers and longer. Underlayer 33 tends to be clear or slightly yellow if the silver-halide therein is not subject to latent image formation. Underlayer 33 tends to be amber or red if latent image formation occurs in the underlayer. As described hereinafter, better definition of the reflective component occurs where a fogging agent is used for surface latent image formation. Since the depth of penetration of the fogging agent can be controlled, for example by the length of time of emulsion dipping into the fogging agent, the unfogged silver-halide below this penetration depth forms underlayer 33. Since the silver in the unfogged silver-halide region subsequently goes into solution as a silver complex, some of which is deposited on silver nuclei in reflective component 32, the underlayer 33 becomes substantially clear and is essentially gelatin.

On the other hand, if surface latent image treatment is achieved by means of exposure to light, the depth of treatment is more difficult to control, but is made easier with screening dyes.

The purpose of the screening dye is to attenuate actinic radiation through the depth of the emulsion so that there is surface latent image formation through only a fraction of the depth of the emulsion. Screening dyes are usually of narrow bandwidth to absorb either blue or green light, but not both. Thus if this type of dye is used the actinic radiation must also be narrow band or filtered accordingly, otherwise unwanted actinic radiation will penetrate the emulsion.

Thus, in general, actinic raidation exposure does not leave a clear boundary between regions of surface latent image formation and regions of no surface latent image formation. Rather, there is a gradient with good surface latent image formation closest to the light source where there is strongest exposure and weak latent image formation further away where there is weakest exposure. In this case the monobath develops the weak latent image in the underlayer 33 which thereby forms a nuclei base for further silver deposits from the silver complex with the result that the underlayer has a red or amber color.

Either method of surface latent image treatment creates an exposure gradient with a greater concentration of exposed silver-halide near the surface of the emulsion where the exposure is greatest. Portions of the exposed and partially developed silver-halide grains become silver nuclei where silver will be reduced from silver ion complexes during diffusion transfer. When the densest concentration of exposed silver-halide grains is desired at the emulsion surface distal to the substrate, either method of surface latent image treatment may be used. However, when the surface having the highest exposed silver-halide concentration is desired proximate to the substrate, then either nuclei are included in manufacturing or actinic radiation exposure through the transparent substrate is necessary to create the surface latent image. An emulsion heavily dyed with a screening dye is necessary in this case to create a surface latent image concentration proximate to the substrate. A short photographic development cycle before monobath development may be used to help create the required silver precipitating nuclei prior to the creation of the silver complex and thus enhance diffusion transfer and reflectivity proximate to the substrate. Owing to the dielectric constant of the glass a much higher volume concentration of silver is necessary to give the same reflectivity as compared to an emulsion side reflective layer. The required layer of high concentration silver precipitating nuclei at the substrate or distal to the substrate can also be incorporated during the film or photoplate manufacturing process.

Once craters are created penetrating reflective component 32, the data contained in the crates may be read by changes in reflectivity of the shiny reflective component throughout the visible spectrum and into the near infrared where it is ultimately limited in its usability as reflective component 32 becomes more and more transparent and therefore less reflective. The craters also may be detected by transmission of red light, provided that the opacity of the reflective layer is sufficiently great at the selected wavelength to permit detection of the craters through differences in light transmission.

It should be noted that both the recording areas 17, 19 and the non-recording guard band 21 of Fig. 1 initially have silver-halide emulsion covering a substrate. Thus, the designation of recording and non-recording areas is arbitrary and the entire surface could be used for recording if desired. However, as a matter of convenience, it is preferable to designate areas as nonrecording areas. The boundaries between recording and non-recording areas may be defined by concentric lines, just as the servo guides 23 of Fig. 1, which have been greatly enlarged in the Fig, may be defined by lines. Typically, servo guides are closely spaced concentric circles or adjacent lines of a spiral, with data being written on or between the lines, Such servo guide lines, as well as line boundaries for non-recording areas, may be photographically recorded on the recording medium prior to any data recording. Moreover, other alphanumeric information or data base information which is to be a permanent part of the recording medium also may be applied to the recording medium photographically at an early time in the processing cycle since it becomes a permanent part of the recording medium.

One of the advantages of the present invention is that the permanent information to be prerecorded on the recording medium of the present invention may be applied by photographic techniques since the starting material for the recording medium is an unexposed commercially available photoplate used in the manufacture of semiconductor integrated circuits or film-based materials of similar quality. A principal characteristic of silver-halide emulsion photosensitive materials for use in the present invention is fine grain size so that the reflectivity granularity is minimized and very small holes can exhibit measurable changes in reflectivity. Large grain sizes would lead to greater granularity which would tend to mask changes in reflection created by small holes. Pre-recording of information may be achieved by masking off areas as described herein. After photographic processing, this pre-recorded information may be read in reflection since the pre-recording areas will consist of either highly reflective white silver areas or low reflective black silver areas or low reflectivity clear gelatin areas The photographic techniques which may be used to pre-record data base and control information are closely related to the fabrication of emulsion photomasks in the semiconductor industry. Lines having a thickness of one micron may be made using these photomask manufacturing techniques. Some procedures for creating a pre-recorded line pattern are illustrated in Figs. 3-8.

Wi potassium borohydride in aqueous solution, or thirdly, by including a silver-precipitation nuclei layer near the emulsion surface where the surface latent image is desired. Surface latent image formation would be followed by processing as described below.

When the surface latent images are created by a fogging agent, it is of no consequence that the screening dye may have been washed out in the earlier development process. The surface activation of the emulsion could take place either by a few-second dip in a fogging agent, such as an aqueous carrier containing hydrazine or by exposure to hydrazine gas for a period of minutes. Penetration of the fogging agent to the interior of the emulsion can be minimized by starting with a dry emulsion. Afer monobath development, the finished laser recording medium would have the appearance shown in Figs. 5-8. Note that the pre-recorded black control indicia 43 of Fig. 8 would be low reflective black compared to the shiny silver recording areas of 41.

Use of a fogging agent creates nuclei where silver in silver ion complexes may be reduced and absorbed. As an alternative to use of a fogging agent, preformed silver-precipitating nuclei may be. disposed in the unexposed silver-halide emulsion, for example in the manufacturing process.

The commerically available instant photographic films of the Polaroid-Land photographic system have such nuclei layers in contact with the silver-halide emulsion. Note that the use of silverprecipitating nuclei layers incorporated in the emulsion does not preclude the possibility of prerecorded control indicia. The non-data recording areas may be exposed first and chemically developed to low reflectivity black silver and not fixed. The entire plate is then given a monobath development to create reflective data recording areas.

An alternate method of surface latent image formation is by means of actinic radiation exposure of the data recording area. It is desirable for the medium to contain a screening dye to limit the exposure primarily to the surface, but this dye may be washed out if the medium was previously processed as for example in producing black silver control indicia. This problem can be overcome by a dyeing process after the chemical development process is completed or by utilization of a permanent, non-soluble screening dye in the initial manufacture of the emulsion, which does not cause non-uniform reflectivity. The monobath processing may be carried out in the same manner as was described in the case of the fogging agent activation. Also, if desired, the black silver areas created by the initial exposure and development could be bleached out before monobath processing.

The surface latent image formation methods create a depthwise exposure gradient, with a concentration of exposed silver-halide which is greatest at one emulsion surface where exposure was greatest. That concentration falls off in the depthwise direction, rather abruptly in the case of fogging agents, such that the concentration of exposed silver-halide is low throughout the body of the emulsion. In the case of actinic radiation exposure the volume concentration of latent image formation falls continually from the exposed surface and is lowest at or near the opposite emulsion surface. The unexposed silver-halide exists in concentrations inversely related to the exposure concentration. After monobath processing, the volume concentration of reflective silver particles at the reflective surface distal to the substrate will exceed the lowest concentration in the body of the emulsion by a ratio typically exceeding 5:1.

The reflective component 32 of Figs. 9-11 is thus derived from the silver in the silver-halide emulsion. While this reflective silver component may appear at either of the two emulsion surfaces and is concentrated there, the thickness of the reflective component is not well defined when created by actinic radiation exposure because some radiation penetrates below the surface of the emulsion and a silver latent image is created. An advantage of using a fogging agent for surface latent image formation as compared to actinic radiation exposure is that it creates a better defined reflective layer and a lower silver concentration within the body of the emulsion.

With both of these processes, silver-halide in a commercially available photographic emulsion is the starting material for creating the laser-recording medium in the present invention, and the finished product may be considered to be silver particles in a gelatin dielectric matrix, the halide being removed in the monobath processing.

To use the laser recording medium of the present invention, laser light is focused on a spot on the reflective component either from the side distal to the substrate or through a transparent substrate. For laser recording as opposed to data storage applications the reflectivity of the reflective layer preferably ranges between 15% and 50%; thus, the remaining percentage of incident radiation of 85% to 50% is either absorbed by the reflective component or partly passes through it. The absorbed power distorts or melts the gelatin supporting the reflective component so as to reduce the reflectivity at the spot and create an adequate contrast in reflective reading of the recorded data. For data storage applications, i.e., laser reading but not recording the reflectivity may be as high as possible and the thickness of the reflective layer is not critical. The reflective component 32 is located on the underlayer as shown in Fig. 9 and Fig. 11 and adjacent to the substrate as shown in Fig. 1 0. In all three cases a reflective read procedure can be used-for example, as described in U.S. Patent 3,657,707. In the cases shown, the recording laser beam need only affect the reflective component, and further penetration into component 33 is not needed.

In Fig. 9, the substrate could be either transmissive or opaque if reflective read is used, but must be transmissive to the read laser beam if transmissive read is used. The component 33 would consist of a red or amber silver gelatin complex if a soluble screening dye and actinic exposure were used to create component 32. but would be essentially clear gelatin if fogging agent surface activation were used or if the emulsion had been manufactured with a silver precipitating nuclei layer included. The color of component 33 would have little effect on reflective read methods but would affect transmissive read methods. If component 33 is red in color, transmissive reading can be accomplished to a limited extent by use of a red or near infrared laser beam provided that the opacity of the undisturbed reflective coating blocks about 90% of the light and the recorded craters permit transmission of at least about 50% of the light. If component 33 is essentially clear gelatin it would permit transmissive reading with a green or blue laser as well; and since the reflective component is more opaque at these wavelengths, a higher contrast would be achieved than in the case of a red or infrared laser being used for transmissive read.

Fig. 10 illustrates a configuration which could have been produced by photographic exposure using narrow band blue or green actinic radiation through a transparent substrate 27 onto an emulsion heavily dyed to attenuate the selected narrow band actinic radiation. Commercially available soluble screening dyes with adequate absorption properties can accomplish the task.

Dyes contained in commercial photoplates are not adequate to achieve the desired reflectivity.

After final processing the component 33 would be red or amber in color. Recording and reflective reading would be achieved through the substrate. Transmissive read could be accomplished to a limited extent by use of a red or near infrared laser beam such that the opacity of the reflective coating blocks 90% of the read-beam radiation and the recorded craters permit transmission of at least 50% of the light. If this configuration were produced by use of an emulsion which had been manufactured with a silver precipitating nuclei layer included, component 33 would be essentially clear gelatin and transmissive read also could be accomplished in blue and green as describe in the previous paragraph.

Fig. 11 illustrates a configuration where both the substrate and the underlayer are transmissive to visible and near infrared radiation. It has the advantage that layer 32 can be coated with a non-optical flat protective layer which would serve to encapsulate layer 32. This type of protective layer could not be used in the configuration of Fig. 9 because it would be in the optical path. The configuration of Fig. 11 also offers an advantage over the configuration of Fig.

10 in that higher reflectivities are more easily attainable by use of the herein described process.

The essentially clear gelatin component 33 would be created by fogging agent surface activation or actinic radiation exposure distal to the substrate of an emulsion heavily dyed with a screening dye so that almost no silver latent images in the body of the emulsion are reduced during monobath development. This configuration can also be produced by use of an emulsion which had been manufactured with a silver precipitating nuclei layer included at the location of layer 32. In this case in addition to reflective read at visible wave-length and near infrared, the component 33 also permits transmissive read at these wave-lengths by laser light transversing substrate 27 for transmission through the essentially clear gelatin component 33 and through crater 30 in component 32.

Figs. 9, 10 and 11 show emulsion coating 29 on substrate 27 covered by shiny component 32 having a crater 30 damaging the shiny component created by means of laser light indicated by the rays 31. The size of the craters is kept at a minimum, preferably about one micron in diameter but no larger than a few microns in diameter to achieve high data densities. Data written by means of laser light are recorded in the recording areas 17, 1 9 shown in Fig. 1, designated by the letter R. As mentioned previously, these recording areas may also contain prerecorded data base data and control indicia which may be disposed over essentially the entire area of the medium. No data is recorded in the guard band 21, designated by the letter G, although this region may have control indicia written therein. Control indicia in either of the areas may be written by means of photographic techniques or by pyrographic methods such as laser writing.

Thus, the recording medium of the present invention may contain a mix of pre-recorded data and control indicia which has been applied to the recording medium by photographic techniques, as well as subsequently written data applied to the recording medium by laser pyrographic writing. There need be no data storage distinction between the photographically pre-recorded non-reflective spots and non-reflective spots made by laser writing. In the recording mode the pre-recorded control information is used to determine the location of the data craters being recorded.

II. Silver Diffusion Transfer We have found that a very thin, highly reflective, silver surface may be formed by the diffusion transfer of appropriate complexed silver ions to a layer of silver precipitating nuclei.

This reflective layer is electrically non-conducting anc as low thermal conductivity and may be patterned photographically, these latter two properties being highly desirable for laser recording media. The complexed silver ions are created by reaction of an appropriate chemical and the silver-halide used in conventional silver-halide emulsions. A developing or reducing agent must be included in this solution to permit the complexed silver ions to be precipitated on the nuclei layer. This combination of developing agent and silver complexing solvent in one solution is called a monobath solution. Preferred monobath formulations for highly reflective surfaces include a developing agent which may be characterized as having low activity. The specific type of developing agent selected appears to be less critical than the activity level as determined by developer concentration and pH.

The developing agent should have a redox potential sufficient for causing silver ion reduction and absorption or agglomeration on silver nuclei. The concentration of the developing agent and the pH of the monobath should not cause filamentary silver growth which gives a black low reflectivity appearance The developed silver particles should have a geometric shape, such as a spherical or hexagonal shape which when concentrated form a good reflectivity surface.

Developing agents having the preferred characteristics are well known in the art and almost any photographic developing agent can be made to work by selection of concentration, pH and silver complexing agent, such that there is no chemical reaction between the developing agent and complexing agent. It is well known that photographic developing agents require an antioxidant to preserve them. The following developing agent/antioxidant combinations produced the typical indicated reflectivities for exposed and monobath developed Agfa-Gevaert Millimask HD photoplates.

For Monobaths Using Na(SCN) As a Solvent And Silver Complexing Agent Approximate Developing Agent Antioxidant Maximum Reflectivity p-methylaminophenol Ascorbic Acid 46% p-methylaminophenyl Sulfite 37% Ascorbic Acid 10% p-Phenylenediamine Ascorbic Acid 24% Hydroquinone Sulfite 10% Catechol Sulfite 60% For Monobaths Using NH4 OH As a Solvent And Silver Complexing Agent Developing Agent Antioxidant Typical Reflectivity Hydroquinone Sulfite 25% Catechol Sulfite 30% The preferred solvents/silver complexing agents, which must be compatible with the developing agent, are mixed therewith, in proportions promoting the complete diffusion transfer process within reasonably short times, such as a few minutes. Such silver complexing agents in practical volume concentrations should be able to dissolve essentially all of the silver-halide of a fine grain emulsion in just a few minutes.The solvent should not react with the developing silver grains to dissolve them or to form silver sulfide since this tends to create non-reflective silver. The solvent should be such that the specific rate of reduction of its silver complex at the silver nuclei layer is adequately fast even in the presence of developers of low activity, which are preferred to avoid the creation of low-reflectivity black filamentary silver in the initial development of the surface latent image.

The following chemicals act as silver-halide solvents and silver complexing agents in solution physical development. They are grouped approximately according to their rate of solution physical development; that is, the amount of silver deposited per unit on, precipitating nuclei, when used with a p-methylaminophenol-ascorbic acid developing agent.

Most Active Thiocyanates (ammonium, potassium, sodium, etc.) Thiosulphates (ammonium, potassium, sodium, etc.) Ammonium hydroxide Moderately Active a picolinium - P phenylethyl bromide Ethylenediamine 2-Aminophenol Furane n-Butylamine 2-Aminophenol thiophene Isopropylamine Much Less Active Hydroxylamine sulfate Potassium chloride Potassium bromide Triethylamine Sodium sulfite From the above it can be seen that the thiocyanates and ammonium hydroxide are amongst the most active solvents/complexing agents. While almost all developers suitable for solution physical development can be made to work in the silver diffusion transfer process of the present invention with the proper concentration and pH, not all solvents/complexing agents will work within the desired short development time or in the proper manner. For example, the thiosulfate salts, the most common silver-halide solvent used in photography and in Polaroid-Land black and white instant photography's diffusion transfer process, does not work in this process for two reasons. Its complexed silver ions are so stable that it requires a strong reducing agent to precipitate the silver on the nuclei, and this strong reducing or developing agent would have the undesirable effect of developing low reflective black filamentary silver. It has another undesirable effect, also exhibited by the solvent thiourea; namely, it forms black, low reflecting silver sulfide with the developing silver grains. On the other hand in the black and white Polaroid-Land process black silver is a desirable result. Sodium cyanide is not recommended, even though it is an excellent silver-halide solvent, because it is also an excellent solvent of metallic silver and would thus etch away the forming image. It is also about 50 times as toxic as sodium thiocyanate, which is a common photographic reagent.

The process chemicals can be applied by a variety of methods, such as by immersion, doctor blades, capillary applicators, spin-spray processors and the like. The amount of processing chemicals and temperature thereof should be controlled to control reflectivity. Preferably, the molar weight of the developing agent is less than 7% of the rnolar weight of the solvent since higher concentrations of developing agent can lead to low reflective filamentary silver growth, exceptions to this ratio being found among p-phenylenediamine and its N,N-dialkyl derivatives having a half-wave potential between 1 70 mv and 240 mv at a pH of 11.0, which have lower development rates and require higher concentrations, i.e., up to 1 5 grams per liter and minimum of about 2 grams per liter. These derivatives and their half-wave potentials are listed in Table 1 3.4 of the book entitled The Theory of the Photographic Process, 3rd ed., Macmillan Company (1966). The concentation of the solvent in the form of a soluble thiocyanate or ammonium hydroxide should be more than 10 grams per liter but less than 45 grams per liter.

If the concentration is too low the solvent would not be able to convert the halide to a silver complex within a short process time and if the solvent concentration is too great the latent image will not be adequately developed into the necessary silver precipitating nuclei causing much of the silver complex to stay in solution rather than be precipitated. The process by which the silver complex is reduced at the silver precipitating nuclei and builds up the size of the nuclei is called solution physical development.

It is important to note that in solution physical development, as used herein, the silver particles do not grow as filamentary silver as in direct or chemical development, but instead grow roughly equally in all directions, resulting in a developed image composed of compact, rounded particles. As the particles grow, a transition to a hexagonal form is often observed. If the emulsion being developed has an extremely high density of silver nuclei to build upon and there is sufficient silver-halide material to be dissolved, then eventually the spheres will grow until some contact other spheres forming aggregates of several spheres or hexagons. As this process takes place the light transmitted through this medium initially takes on a yellowish appearance when the grains are very small. This changes to a red appearance as the particles build up in size and eventually will take on a metallic-like reflectivity as the aggregates form.

In summary, it was discovered that if silver precipitating nuclei are formed on one of the surfaces of a silver-halide emulsion either in the emulsion manufacturing process, by actinic radiation, or by a fogging agent; and if this emulsion is then developed in a monobath solution containing a weak developer and a very fast solvent which forms complexed silver ions which are readily precipitated by catalytic action of silver nuclei; and if the solvent does not form silver sulfide; then a reflective coating is developed on one of the emulsion surfaces thereby creating a medium for data storage and laser recording. It was also discovered that any of the common developing agents will work whereas only a small number of solvents/complexing agents have all of the desired properties, the most successful of these being the soluble thiocyanates and ammonium hydroxide.

In a common version of the black and white silver diffusion transfer process the silver in the unused silver-halide in the negative image will diffus o a second separatable layer containing precipitating nuclei for reducing the silver and thereby creating a positive image. In the diffusion transfer process of this invention, a volume concentration of silver precipitating nuclei may be created on an emulsion surface without use of a separate layer containing nuclei. When actinic radiation or fogging chemicals are used to create these nuclei in the data recording areas, the desired reflective layer appears where the emulsion surface was exposed or activated so this process may be considered a negative-type process as compared to the positive-type process of the conventional silver diffusion transfer. After the concentrating gradient of silver nuclei is created, a monobath processing step follows. The developing agent-solvent monobath performs several functions; it develops and thus enlarges the silver nuclei of the latent images, dissolves the silver-halide within the body, creates complexed silver ions and provides the reducing agent necessary for the solution physical development process, that is, the reduction and precipitation of the complexed silver ions on the silver precipitating nuclei of the developing latent image.

Thus, the key steps in the present invention involve creating a surface latent image or concentration gradient of silver-precipitating nuclei in the data recording area near a surface of the emulsion and then using a special monobath containing a developing agent and complexing agent to build up the silver grains until they begin to aggregate into groups thereby increasing the volume concentration of the silver in the surface latent image area until it becomes adequately reflective. An alternative procedure is to use a silver-halide emulsion which is coated on one side by, or otherwise incorporates a layer of, silver precipitating nuclei which is then exposed to light in the non-data-recording areas assigned to control indicia. This is then followed by a chemical development to produce black control indicia or other pre-recordings and finally a monobath development of the special type previously described is used to build up the silver grains in the data recording area until it becomes adequately reflective. The resulting reflective laser-recording and data storage medium consists of concentrated reflective silver grains near a surface of an essentially clear gelatin matrix.

Some of the key processing steps of the present invention may be achieved by physical phenomenon, chemical treatments or manufacturing techniques but when these steps are linked together in the proper processing sequence, the result is a reflective laser-recording medium.

Table I presents 1 4 experimental examples to illustrate some of the variations of the individual steps that may be used and to present an overview of two principal steps necessary to create a laser recording media of adequate reflectivity.

See Table I which follows.

TABLE 1

Solvent/ Surface Photographic Typical Example Developing Agent Complexing Activation Material Reflectivity Agent Sodium Agfa HD Photoplate;* Example 1 Light P-Phenylendiamine 20% - 24% Thiocyanate 4-1/2 Micron Emulsion P-Methylaminophenol Sodium Agfa HD Photoplate; Example 2 Light 20% - 35% and Ascorbic Acid Thiocyanate 4-1/2 Micron Emulsion P-Methylaminophenol Sodium Konishiroku ST Photo Example 3 Light 15% - 27% and Ascorbic Acid Thiocyanate plate; 3 Micron Emulsion P-Methylaminophenol Sodium Agfa-Gevaert Type 10R75 Example 4 Light 40% - 43% and Ascorbic Acid Thiocyanate Film; 5 Micron Emulsion Aqueous Hydrazine; P-Methylaminophenol Sodium Kodak S0173 Film; Example 5 32% Surface Fogging and Ascorbic Acid Thiocyanate 6 Micron Emulsion Aqueous Hydrazine; P-Methylaminophenol Sodium Agfa HD photoplate; Example 6 39% - 41% Surface Fogging and Ascorbic Acid Thiocyanate 4-1/2 Micron Emulsion Aqueous Hydrazine; P-Methylaminophenol Sodium Konishiroku SN Photo Example 7 23% Surface Fogging and Ascorbic Acid Thiocyanate plate; 6 Micron Emulsion *Agfa HD is an abbreviation for Agfa-Gevaert Millimask HD Photoplate.

TABLE I (Cont'd)

Solvent/ Surface Photografic Typical Example Developing Agent Complexing Activation Material Reflectivity Agent Gaseous Hydrazine; P-Methylaminophenol Sodium Agfa HD Photoplate; Example 8 22% Surface Fogging and Ascorbic Acid Thiocyanate 4-1/2 Micron Emulsion Aqueous Potassium P-Methylaminophenol Sodium Agfa HD Photoplate; Example 9 Borohydride; 75% and Ascorbic Acid Thiocyanate 4-1/2 Micron Emulsion Surface Fogging P-Methylaminophenol Hydroxylamine Agfa HD Photoplate; Example 10 Light 18% and Ascorbic Acid Hydrochloride 4-1/2 Micron Emulsion Catechol Sodium Agfa HD Photoplate; 56% Example 11 Light 1 gms./liter Thiocyanate 4-1/2 Micron Emulsion Catechol Sodium Agfa HD Photoplate; Example 12 Light-Micron Image 35% 1/2 gm./liter Thiocyanate 4-1/2 Micron Emulsion Catechol Ammonium Agfa HD Photoplate; Example 13 Light 30% 1/2 gm./liter Hydroxide 4-1/2 Micron Emulsion Hydroquinone Ammonium Agfa HD Photoplate; Example 14 Light 25% 1/2 gm./liter Hydroxide 4-1/2 Micron Emulsion *Agfa HD is an abbreviation for Agfa-Gevaert Millimask HD Photoplate.

Note that the fourteen examples include creation of surface latent images by actinic radiation, aqueous and gaseous fogging by hydrazine and aqueous fogging by potassium borohydride. A key step is creation of surface latent images in the data recording area if a nuclei layer has not been added in the manufacture of the emulsion; or, as previously mentioned, if a nuclei layer is already present and pre-recordings are desired, then surface latent images must be created in the non-data recording areas. It appears that any silver-halide emulsion may be used to create a reflective silver surface. This invention is not limited to the use of gelatin-based emulsions. Other film-forming colloids may be used as carriers. A variety of commercially available high-resolution films and plates manufactured by three different companies were used to illustrate the general nature of the process. It is also shown that the monobath developing-agent complexing agent can be formulated by use of a variety of developing agents and solvents/silver complexing agents. Table I lists four different developing agents, three different solvents/complexing agents, five different emulsions and four different surface activation procedures. The reflectivities achieved range between 15% and 75%.

Example 1 A photoplate coated with a commercial Agfa-Gevaert HD emulsion 4.5 microns thick and containing a screening dye was exposed to sunlight for several minutes and t

Example 5 A commercially available Eastman Kodak SO 173 film was etched with a Protease WT 0.5% solution for 5 minutes at 35 C in a darkroom to remove the gelatin overcoat. The film was then immersed in a hydrazine 68% aqueous solution for 2 seconds to create the developable surface latent image. It was then developed in a monobath as described in Example 2, for 5 minutes.

After drying it exhibited a reflectivity of 32% and a red density of 1.9 to 2.0.

Example 6 An unexposed commercially available Agfa-Gevaert Millimask HD photoplate was dipped into a 68% aqueous solution of hydrazine for several seconds to create a developable surface latent image. It was then developed in monobath as described in Example 2 for 5 minutes at 23"C and then dried. Samples exhibited reflectivities ranging between 39% and 41 % at the emulsion surface and reflectivities of 17% to 18% when measured through the glass substrate. The gelatin under the reflective silver coating was so clear that the silver coating was visually reflective through the glass substrate. Optical densities in the red ranged between O.8 and 1.0.

Example 7 A commercially available photoplate manufactured by Konishiroku Photo Industries, of Japan, called a KR SN photoplate, has a 6-micron-thick emulsion which does not contain a screening dye but does contain an antihalation backing coated on the back of the glass substrate. This photoplate was dipped into 68% aqueous solution of hydrazine for a few seconds and then developed for 5 minutes at 23"C in monobath as described in Example 2 and then dried. It exhibited a reflectivity from the emulsion side of 23% and an optical density in the red of 1.5.

Example 8 A commercially available Agfa-Gevaert Millimask HD photoplate had latent images created on its surface by means of gaseous hydrazine. The photoplate was placed in a chamber which is exhausted of air down to 13mm of mercury, after which hydrazine is evaporated into the chamber. The photoplate is exposed to this gas for 10 minutes in darkness and then developed in monobath, as described in Example 2, for 5 minutes at 23"C. After drying, the plate exhibited a reflectivity of 22% and an optical density in the red of 2.0.

Example 9 A commericially available Agfa-Gevaert Millimask HD photoplate having a 4.5 micron thick emulsion and containing a screening dye was immersed in a water solution consisting of 5 grams/liter of potassium borohydride (KBH4) for 2 seconds to fog the surface and create silver nuclei for silver diffusion transfer. After it was washed well, the photoplate was developed in the monobath described in Example 2 for five minutes at 23"C. When washed and dried, the plate exhibited a reflectivity of 75%.

Example 10 A commercially available Agfa-Gevaert Millimask HD photoplate having a 4.5 micron thick emulsion and containing a screening dye was exposed to room light for several minutes and then developed for 2 hours in a monobath developer having the following constituents: p methylaminophenol sulfate, 0.25 grams; ascorbic acid, 2.5 grams; sodium hydroxide, 2.0 grams; hydroxylamine hydrochloride (HO-NH2-HCL), 5 grams; in a volume of one liter after adding water. After the photoplate was washed and dried, its reflectivity was measured at 18.5%.

Example 11 A commercially available Agfa-Gevaert Millimask HD photoplate having a 4.5 micron thick emulsion and containing a screening dye was exposed to room light for several minutes and then immersed for five minutes at 23"C in a monobath developer having the following constituents: catechol, 1 gram; sodium sulfite, 10 grams; sodium hydroxide, 2 grams; sodium thiocyanate, 25 grams; in a volume of one liter after adding water. After the photoplate was washed and dried, it exhibited a reflectivity of 56%.

Example 12 A commercially available Agfa-Gevaert Millimask HD photoplate having a 4.5 micron thick emulsion and containing a screening dye was exposed through a photomask containing one micron serpentine lines for 8 seconds using an Ultratech contact printer and them immersed for five minutes at 23"C in a monobath developer having the following constituents: catechol, 1/2 gram; sodium sulfite, 10 grams; sodium hydroxide, 2 grams; sodium thiocyanate, 25 grams; in a volume of one liter after adding water. After the photoplate was washed and dried, its reflectivity was approximately 35%. This reflective serpentine pattern of one micron lines and one micron spaces was of excellent image quality and demonstrated the ability of this process of pre-record data and control indicia having image sizes of one micron.

Example 13 A commercially available Agfa-Gevaert Millimask HD photoplate having a 4.5 micron thick emulsion and containing a screening dye was exposed to room light for several minutes and then immersed for five minutes at 23"C in a monobath developer having the following constituents: catechol, 1/2 gram; sodium sulfite, 10 grams; sodium hydroxide, 2 grams; 58% solution of ammonium hydroxide, 50 milliliters; in a volume of one liter after adding water. After the photoplate was washed and dried, its reflectivity was approximately 30%.

Example 14 A commercially available Agfa-Gevaert Millimask HD photoplate having a 4.5 micron thick emulsion and containing a screening dye was exposed to room light for several minutes and then immersed for five minutes at 23"C in a monobath developer having the following constituents: hydroquinone, 1/2 gram; sodium sulfite, 10 grams; sodium hydroxide, 2 grams; 58% solution of ammonium hydroxide, 50 milliliters; in a volume of one liter after adding water. After the photoplate was washed and dried, its reflectivity was approximately 25%.

The appearance of the surface of the finished recording medium varies with the degree of reflectivity. At reflectivities of 50% or more it has a silver-like appearance. In the 35% to 45% range its color is like white gold, and in the 17% to 30% range it looks like yellow gold. Below about 12% reflectivity is has a reflective black appearance similar to black patent leather.

One of the principal differences between the single step diffusion transfer process of the present invention and the prior art is that in the present invention the unexposed and undeveloped silver halide is put into solution quickly so that that silver ion complex forming reaction takes place at a more rapid rate than the chemical development of photographically exposed silver halide. In the prior art the development of the negative black image must be essentially completed before the remaining silver-halide is complexed and transferred; otherwise, the positive image would in essence be fogged. Thus, in the prior art a very high concentration of developing agent is used to rapidly complete the chemical development process. The initial chemical development process of the present invention only slightly develops the latent image before the complex forming reaction takes place since the principal objective is the physical development of the latent image to produce a reflective image of it, not the chemical development of the latent image to permit the remaining silver-halide to produce a reversal image as in the prior art.

Nothing limits the silver diffusion transfer process of the present invention to use as a data storage medium. The process may be used to make other articles where high reflectivity is needed in conjunction with various types of information imaging.

In the broadest sense, the invention comprises dispersing high electrical conductivity tiny metal spheres or spherical particles in a dielectric medium of low thermal conductivity and low melting temperature to form a laser recording medium. If these small particles are of very high volume concentration, e.g. between 20% to 70% of the volume of the reflective surface layer, the medium can exhibit very high reflectives in the visible spectrum even through the reflective surface would have no measurable electrical conductivity. Such a dielectrically based electrically non-conducting reflective medium is desirable for laser recording.

Attention is directed toward our co-pending application number 8020832 which discloses a process for making a reflective electrically non-conducting data storage medium.

CLAIMS 1. A reflective data storage medium comprising electrically conductive metal particles having a size primarily less than .05 microns dispersed in a surface of low melting temperature dielectric material so as to produce a reflective electrically non-conductive recording medium.

Claims (1)

1. 2. The reflective data storage medium of claim 1 wherein said dielectric material is gelatin, the volume concentration of metal particles being between 20% and 70% and the surface layer reflectivity being between 20% and 50% with a minimum optical density of 0.8 as measured in the red by a photographic densitometer so as to produce a reflective electrically non-conductive recording medium.

   3. The data storage medium of claim 1 wherein said metal particles are silver and some of said silver particles are aggregated with similar particles, and having a volume concentration of silver particles greater at said surface than in the interior of said matrix, said surface having an areawise substantially uniform reflectivity to visible light, said uniform reflectivity being between 35% and 75%.

   4. The data storage medium of claim 3 wherein the volume concentration at said reflective surface layer exceeds the lowest silver volume concentration within the interior of said colloid matrix layer by a ratio of at least 5:1.

   5. The data storage medium of claim 3 or 4 wherein said reflective surface layer is less than one micron thick.

   6. The data storage medium of claim 3, 4 or 5, wherein said volume concentration of silver particles in said reflective layer is a minimum of 20% and a maximum of 70%.

   7. The data storage medium of any one of claims 3-6, wherein said colloid matrix layer is photographic gelatin used in the manufacture of silver-halide emulsions.

   8. The data storage medium of any one of claims 3-7, wherein said reflective surface layer is derived from a photographic emulsion.

   9. The data storage medium of any of claims 3-8, wherein said reflective surface layer contains prerecorded information indicia therein.

   10. The data storage medium of claim 9 wherein said prerecorded information indicia comprises a photographic image.

   11. The data storage medium of claim 9 wherein said prerecorded information indicia comprises a pattern of laser writing.

   1 2. The data storage medium of claim 9 wherein said prerecorded information indicia comprises a photographic image and a pattern of laser writing.

   1 3. The data storage medium of any one of claims 3-9, wherein the colloid matrix forms an underlayer component beneath said reflective layer which is transmissive of visible light.

   14. The data storage medium of any one of claims 3-9, wherein the colloid matrix forms an underlayer component beneath said reflective layer which is absorptive of green and blue light.

   15. The data storage medium of any of claims 3-14, wherein said reflective layer of said matrix layer is distal to said substrate.

   16. The data storage medium of any one of claims 3-14, wherein said reflective surface layer of said matrix layer is proximate to said substrate.

   1 7. The data storage medium of any one of claims 3-16, wherein said reflective surface layer includes interspersed regions of essentially clear colloid matrix materal.

   18. The data storage medium of any one of claims 3-17, wherein said reflective surface layer includes interspersed black regions consisting of black filamentary silver particles.

   19. The data storage medium of any one of claims 3-18, wherein the thickness of the colloid matrix layer is less than 1 5 microns.

   20. The data storage medium of claims 3-19 wherein said reflective surface layer has a white gold color.

   21. The data storage medium of claims 3-1 9 wherein said reflective surface layer has a silver-like appearance.

   22. The data storage medium of claims 3-19 wherein said substrate is polyester, polyterephthalate, polycarbonate, or cellulose triacetate.

   23. A reflective data storage medium according to claim 1 constructed and adapted to operate substantially as herein described.

   24. A method of making the reflective laser recording medium of claim 1 comprising, dispersing electrically conductive metal particles having a size primarily less than .05 microns in a surface layer of low melting temperature dielectric material so as to produce a reflective electrically non-conductive recording medium.

   25. The method of claim 24, wherein said low melting temperature dielectric comprises a gelatin.

   26. The method of claim 24 or 25, wherein said electrically conductive metal particles are silver.