GB2100874A

GB2100874A - Photosensitive compositions and their use

Info

Publication number: GB2100874A
Application number: GB08217461A
Authority: GB
Inventors: John D Renwick; John Robert Curtis
Original assignee: Sericol Ltd
Current assignee: Sericol Ltd
Priority date: 1981-06-19
Filing date: 1982-06-16
Publication date: 1983-01-06
Also published as: GB2100874B

Abstract

The invention provides photosensitive compositions useful in the production of screen printing stencils which comprise, in addition to a water-soluble cross-linkable polymer, a diazo salt as photosensitizer and water, also an acid base indicator to show when a layer formed from the said composition has been insolubilised by exposure to actinic light.

Description

SPECIFICATION Photosensitive compositions and their use The present invention relates to compositions useful for the preparation of photosensitive layers for the production of screen printing stencils, and their use.

In screen printing, three methods of making stencils are used. In the first, the so-called "indirect method", a photosensitive composition is coated onto a suitable support, usually of a transparent polymer such as a polyester. The coated support is then irradiated with actinic light through a positive transparency after which, depending upon the type of photopolymerisation system used, the image obtained is either immediately developed with water or activated with a per compound and then developed with water. The wet image on the support is then transferred to the screen mesh by application of gentle even pressure, and, after drying, the support is removed to leave the photopolymerised image on the screen mesh ready for printing.

In the second system, the so-called "direct method", a water-soluble crosslinkable colloid is photosensitised with a suitable crosslinking agent activated by actinic light, for example a dichromate or a polymeric diazo salt, and then coated onto the screen mesh. The sensitised coated layer, after drying, is exposed to actinic light through a positive transparency to produce a latent image which is developed with water. The irradiated areas remain on the screen as they have been insolubilised, while the unirradiated areas, which are still water soluble, are washed away, to leave an image on the screen which, after drying, is ready for printing.

In the third system, the so-called "direct-indirect method", an unsensitised composition is coated onto a suitable support sheet, e.g. of a polyester. The screen mesh, suitably supported, e.g. by stretching on a frame, is placed on top of the unsensitised coating in good contact therewith. A photosensitive composition is then spread over the screen mesh and allowed to dry. This composition may be the same as that in the "direct method". The photosensitiser partially migrates into the unsensitised coating. When the photosensitive composition has completely dried, the support sheet is removed and the resultant assembly exposed to actinic light through a positive transparency. It is then developed with water in the same way as that described for the "direct system" to leave, after drying, an imaged screen ready for printing.

Known methods of producing stencil images by these methods have the disadvantage that, after the exposure to actinic light, it is difficult to see which areas have been exposed to light and which have not. Although many photochemical compositions will, by degradation of sensitizing agent or other component, show a slight colour change on exposure to UV light, the resulting contrast is generally insufficient for any use to be made of it. There is thus no satisfactory way of inspecting the image before it is developed, and it is difficult, where multiple exposures are used, to ensure exact registration between the different images. Thus if the exposure or the positioning of the photosensitive layer is incorrect, the fault cannot be detected until after the stencil image has been developed.It is clearly desirable, therefore, to provide a photosensitive composition for use in the production of screen printing stencils which is such that it is easy to see where areas have been exposed to actinic light, even before the stencil image has been developed.

According to the present invention, an aqueous photosensitive composition useful for making screen printing stencils comprises a water-soluble crosslinkable polymeric colloid, a diazonium salt as photosensitiser, and an acid base indicator, the pH of the composition being such that after a layer thereof has been exposed to light the hue of the indicator shifts from that of the acid or base form into that of the base or acid form respectively. The term "acid base indicator" as used herein means any compound the hue of which is noticeably changed by a change in pH over a narrow range, eg less than 3 units, and and usually less than 2 units. It will be understood that a change in hue involves significant shift in the wavelength of the absorption maximum in the visible spectrum. Such compounds are well known and are widely used in analytical applications.Examples of such indicators suitable for use in the present invention with the pH ranges over which they change hue are: Metanil Yellow (pH 1.2-2.3), Bromophenol Blue (pH 3-4.6), Methyl Red (pH 4.4-6), Bromocresol Green (pH 3.8-5.4), Thymol Blue (pH 1.2-2.8), and Methyl Orange (pH 3.1-4.4).

Normally, the compositions of the present invention are adjusted, e.g. by addition of suitable buffering substances, to have a pH on the high side of and close to the pH range over which the indicator changes hue. Exposure of a dried layer of the composition then causes the hue of the indicator to shift from the base form to the acid form. The resulting change in the hue of the exposed layer is readily visible.

It is course necessary to choose the indicator so that, having regard to the other components present in the composition, the change in hue which takes place is immediately visible. In particular, it is necessary to take into account the colour of the diazo salts used as photosensitiser. The presence of additional colouring substances in the composition may render the change in hue of the indicator itself either more or less conspicuous, and it is within the scope of the invention to include in the compositions one or more further coloured materials which are not indicators in order to improve the visibility of the change in hue of the indicator itself. For example, a red colouring matter may be used to improve the appearance of the change in hue shown by Bromophenol Blue, or a blue colouring matter may be used to improve the visibility of the change in hue shown by Methyl Red.

It is generally convenient to use an indicator which changes hue within the pH range of 2 to 5, as the selection of the other ingredients of the new composition then presents no problem. The pH of the composition prior to coating may then be in the range 5 to 7.

The photosensitiser used in the compositions of the present invention may be any of the diazo photosensitisers which have heretofore been used in photosensitive compositions for making screen stencils. Condensation products of formaldehyde with a p-diazo diphenylamine salt are preferred. It is usual to supply such a photosensitiser separately from the remainder of the composition and to add it to the composition immediately before coating of the support sheet or stencil screen. The proportion used is normally 0.2 to 2.5% by weight of the composition, and preferably 0.4 to 1.2% by weight. The acidity of the diazo sensitizer must be taken into account in formulating the composition ready for coating.

Apart from the acid-base indicator, the remaining ingredients of the novel compositions are similar to those heretofore used in photosensitive compositions for making screen stencils. The preferred water-soluble crosslinkable polymer is polyvinyl alcohol which may be included in the composition in a proportion of 4 to 20%, and preferably 5 to 13% by weight. To improve the durability of the stencil obtained, it is usual to include a second polymeric material which is not necessarily water-soluble or crosslinkable and which may be dissolved or dispersed, for example polyvinyl acetate in a proportion of O to 60% by weight of the composition and preferably 20 to 40% by weight.

The compositions of the present invention contain water as the essential solvent in a proportion which is usually between 30 and 80% by weight and preferably 45 to 60% by weight. In order partly to improve the compatibility of the various ingredients of the composition and also to promote the flowout of the compositions over the various types of mesh on which they may be used, one or more additional solvents may be included in minor proportion, e.g. up to 5% by weight. Examples of such additional solvents are 2-ethoxyethanol and other water miscible aliphatic solvents. When such additional solvents are used, a proportion of 0.1 to 2.5% by weight is normally all that is required.

In order further to improve the properties of the crosslinked polymer, and in particular its durability and/or flexibility in use, the compositions of the invention may contain one or more fillers such as starch in a proportion up to 20% by weight and preferably not more than 12% by weight and/or a plasticiser such as dibutyl phthalate in a proportion normally from 0.5 to 8% by weight and preferably 2 to 5% by weight based on the composition.

The indicator itself is only required in sufficient proportion to give a clearly detectable change in hue when exposure has taken place. A suitable proportion is normally from 0.03 to 0.3% and preferably 0.06 to 0. 15% by weight based on the composition. When additional colouring matters are present, the proportion may be up to 0.2% by weight, but is normally 0.02 to 0. 12% when the addition of such a further colouring matter is considered desirable.

As already indicated, one or more buffering compounds may be included in the compositions to stabilise the pH to a value at which the dried layer is most sensitive to exposure by light. This does not normally require incorporation in the compositions of more than 4% by weight of suitable buffering compounds, and in most cases only 1 to 2% by weight of the buffering compounds is required. The normal kinds of buffers may be used, for example potassium sodium tartrate, trisodium or tripotassium citrate by itself or with a small amount of acetic acid, a combination of sodium acetate and acetic acid, or a combination of a sodium or potassium dihydrogen phosphate and a disodium or dipotassium hydrogen phosphate.In every case, of course, the exact nature of the buffering compounds and their amounts is chosen to provide a pH higher than but adjacent to the pH range over which the indicator changes hue.

The aforesaid novel compositions may be used in the indirect, direct and direct-indirect methods for producing screen printing stencils in place of previously known photosensitive compositions and in the same way, but with the important advantage that a dried layer of the new compositions shows clearly whether it has been exposed to actinic light, whether intentionally or by mistake, or not.

So far as we are aware, this desirable result has never previously been achieved, although Specification No. 1041463 discloses light sensitive sheets, primarily for the preparation of lithographic plates, comprising a base sheet coated with a light sensitive layer comprising a diazo compound and an acid base indicator. These sheets are said to change colour upon exposure to light, but it is to be noted that the compositions described in this prior specification are based primarily on organic solvents and contain quite a different type of polymeric material.

The new compositions may be used in the same way as known photosensitive compositions useful for making screen printing stencils. The invention therefore includes within its scope: 1. A process for preparing a screen stencil by the indirect method which comprises coating a photosensitive composition of the invention onto a transparent, normally polymeric support, drying the coating, exposing the coating to actinic light via a positive transparency, developing the exposed coating, causing the developed coating to adhere to the screen mesh by pressure, drying the coating, and removing the support to produce a screen stencil.

2. A method for preparing a screen stencil by the direct method which comprises coating a photosensitive composition of the invention onto a screen mesh, drying the coating, exposing the dried coating to actinic light via a positive transparency, and developing and drying the exposed layer to produce a screen stencil.

3. A method for preparing a screen stencil by the direct-indirect method which comprises coating a photosensitive composition of the invention onto a screen mesh which is in direct contact with an unsensitised film in a support, drying the coating and removing the support, exposing the dried coating to actinic light via a positive transparency, and developing the exposed coating to produce a screen stencil.

The following are Examples of photosensitive compositions in accordance with the present invention. Parts are parts by weight.

Example 1 Parts Gohsenol GH20 (a polyvinyl alcohol of high molecular weight, containing 12% residual acetate groups from Nippon Gohsei 7.7 Vinamul 8440 (polyvinyl acetate emulsion having 521 56% solids content of Vinyl Products Limited) 27 Potassium Sodium tartrate 2.25 Bromophenol Blue Indicator 0.04 Dibutyl phthalate 2.25 2-Ethoxyethanol 1.5 Water to 100 The change in hue is from green (unexposed) to pale brown (exposed) Example 2 Parts Gohsenol GH20 5 Emultex 328 (polyvinyl acetate emulsion of 56% solids content of Harco Limited) 53 Tripotassium Citrate monohydrate 3 Acetic Acid 0.4 Bromophenol Blue Indicator 0.1 Methylated Spirit 1 Dibutyl phthalate 3.4 Imperon Red KB Paste (Hoechst) 0.1 Water to 100 The change in hue is from green/black (unexposed) to dull pink (exposed).

Example 3 Parts Gohsenol GH 17 (a medium/high molecular weight polyvinyl alcohol containing approximately 12% residual acetate groups) 15 Rice Starch 3.1 Tripotassium citrate monohydrate 1.6 Bromocresol Green Indicator 0.3 2-Ethoxyethanol 2.6 Dibutyl phthalate 5.2 Water to 100 The change in hue is from bright green (unexposed) to buff (exposed) Example 4 Parts Gohsenol KH 1 7 (a medium/high molecular weight polyvinyl alcohol containing approximately 20% residual acetate groups) 9.3 Vinamul 8440 23 Sodium Acetate 1.2 Thymol Blue Indicator 0.3 Dibutyl phthalate 1.7 Acetic Acid 0.01 Water to 100 The change in hue is from yellow (unexposed) to red (exposed) Example 5 Parts Gohsenol GH20 8.5 Vinamul 8440 33 Potassium dihydrogen phosphate 0.3 Disodium hydrogen phosphate hydrate 0.7 Methyl Orange Indicator 0.05 Dibutyl phthalate 2.2 Water to 100 The change in hue is from orange (unexposed) to red (exposed) Example 6 Parts Ertivinol 23/88 (a Polvvinvl alcohol of medium/hiah molecular weight containing 12% of residual acetate groups, from Union Explosives Rio Tinto S.A.) 15 National 1 25-1033 (a polyvinyl acetate emulsion of 55% solids from National Adhesives and Resins Ltd.) 8.5 Tripotassium citrate monohydrate 1.1 Methyl Red 0.1 Dibutyl phthalate 2 Water to 100 The change in hue of the sensitised layer of the composition is from orange (unexposed) to red (exposed).

Example 7 Parts Ertivinol 23/88 15 Metanil Yellow 0.2 Methylated spirit 2 2-Ethoxyethanol 2.5 Dibutyl phthalate 5 Bevaloid 691 M (a defoamerfrom Bevaloid Ltd.) 0.1 Water to 100 The change in hue on exposure is from deep yellow (unexposed) to red-brown (exposed) Example 8 Parts Ertivinol 23/88 4.3 Vinamul 8440 60 Potassium sodium tartrate 1.9 Bromophenol Blue 0.1 Dibutyl phthalate 2.6 2-Ethoxyethanol 1.3 Bevaloid 691 M 0.1 Water to 100 The change in hue is from dark green (unexposed) to buff (exposed) Example 9 Parts Gohsenol GH 20 8.2 National 225-1025 (a polyvinyl acetate emulsion of 55% solids content from National Adhesives and Resins Ltd.) 30 Tripotassium citrate monohydrate 1.9 Methyl Red 0.4 Dibutyl phthalate 2.2 2-Ethoxyethanol 1 Unisperse Blue GE paste (a pigment paste from Ciba-Geigy) 0.02 Water to 100 The change in hue is from yellow-brown (unexposed) to purple-pink (exposed).

Example 10 Parts Ertivinol 23/88 9 Vinamul 8440 36 Sodium acetate 0.8 Acetic acid 0.05 Methyl Orange 0.24 Dibutyl phthalate 4.8 Methylated spirit 2.4 Water to 100 The change in hue is from orange (unexposed) to brownish red (exposed) Example 11 Parts Ertivinol 23/88 10 Harco 586 (a polyvinyl acetate emulsion of 60% solids from Harco Ltd.) 33 Bromocresol Green 0.1 Dibutyl phthalate 4 2-Ethoxyethanol 2 Sodium acetate 1 Acetic acid 0.05 Water to 100 The change in hue is from green (unexposed) to brown (exposed) Example 12 Parts Ertivinol 23/88 4.0 Vinamul 8440 57 Bromophenol Blue 0.1 Dibutyl phthalate 2.5 2-Ethoxyethanol 1.2 Potassium sodium tartrate 1.6 Tapioca starch 6 Neopralac Golden Yellow (a pigment paste from PCUK) 0.2 Water to 100 The change in hue is from green (unexposed) to yellow (exposed).

Each of the aforesaid compositions may be mixed, immediately before use, with a photosensitizer of known kind, e.g. 0.4 to 1.2% by weight of a condensation product of formaldehyde with a paradiazodiphenylamine salt, usually added in the form of a concentrated aqueous solution containing about 50% by weight of the said condensation product.

Claims

1. A photosensitive composition useful for making screen printing stencils comprising a watersoluble crosslinkable polymer, a diazo salt as photosensitiser, water, and an indicator as hereinbefore defined, the pH of the composition being such that after a layer thereof has been exposed to light the hue of the indicator shifts from that in the acid or base form into that of the base or acid form respectively.

2. A composition according to claim 1, having a pH on the high side of the pH range over which the indicator changes hue and such that in a light sensitive layer formed from the said composition, the indicator has the hue characteristic of its base form.

3. A composition according to claim 2, which also comprises a buffer to maintain the said pH.

4. A composition according to any of claims 1 to 3 in which the indicator is one which changes hue at a pH within the range of 2 to 5.

5. A composition according to any of claims 1 to 4, which also comprises a further colouring substance to provide additional contrast to the change in hue which takes place upon exposure to light.

6. A composition according to any of claims 1 to 5, in which the crosslinkable polymer is polyvinyl alcohol.

7. A composition according to claim 6, which also contains polyvinyl acetate dispersed therein.

8. A composition according to any of claims 1 to 7, in which the indicator is Metanil Yellow, Bromophenol Blue, Methyl Red, Bromocresol Green, Thymol Blue, or Methyl Orange.

9. A composition according to any of claims 1 to 8 comprising 5 to 13% of polyvinyl alcohol or other water-soluble cross-linkabie polymer, 20 to 40% of polyvinyl acetate, 0.4 to 1.2% of the diazo photosensitizer, 45 to 60% of water, 0.06 to 0.1 5% of the indicator, and optionally small amounts of an additional solvent, an additional colouring substance, a filler, and/or a plasticizer, the said percentages being by weight based on the total weight of the composition.

10. A composition according to claim 1, substantially as described in any one of the foregoing Examples.

11. A process for preparing a screen stencil by the indirect method which comprises coating a photosensitive composition as claimed in any of claims 1 to 10 onto a transparent support, drying the coating, exposing the coating to actinic light via a positive transparency, developing the exposed coating, causing the developed coating to adhere to the screen mesh by pressure, drying the coating, and removing the support to produce a screen stencil.

12. A method of preparing a screen stencil by the direct method which comprises coating a composition as claimed in any of claims 1 to 10 onto the screen mesh, drying the coating, exposing the dried coating to actinic light via a positive transparency, and developing and drying the exposed layer to produce a screen stencil.

13. A method of preparing a screen stencil by the direct-indirect method which comprises coating a composition as claimed in any of claims 1 to 10, onto a screen mesh in direct contact with an unsensiiised film on a support, drying the coating, removing the support, exposing the dried coating to actinic light via a positive transparency, and developing the exposed coating to produce a screen stencil.

14. A two-component pack in which one component comprises a diazo photosensitizer and the other component comprises a water-soluble cross-linkable polymer, the ingredients of the two components being such that on mixing a photosensitive composition as claimed in any of claims 1 to 10 is formed.