GB2091456A - Controlling aluminium alloy strip production - Google Patents
Controlling aluminium alloy strip production Download PDFInfo
- Publication number
- GB2091456A GB2091456A GB8100156A GB8100156A GB2091456A GB 2091456 A GB2091456 A GB 2091456A GB 8100156 A GB8100156 A GB 8100156A GB 8100156 A GB8100156 A GB 8100156A GB 2091456 A GB2091456 A GB 2091456A
- Authority
- GB
- United Kingdom
- Prior art keywords
- strip
- width
- heating
- conductance
- heat treatment
- Prior art date
- Legal status (The legal status is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the status listed.)
- Granted
Abstract
In the production of aluminium alloy strip, in which hardening of the material is effected by heat treatment to dissolve pre-existing precipitates in the metal matrix followed by quenching and ageing, the electrical conductance of the strip after quenching is measured using a conductivity probe scanned across the width of the strip. Heating is controlled in accordance with the measured conductance so as to obtain uniform electrical conductance across the width of the strip. This measured conductance has a close correlation with the required mechanical properties. The conductance is measured by a transmitter 33 producing an electromagnetic field. The transmitter is movable on a C-shaped frame 35 across the strip. A receiver 36 picks up signals due to the eddy currents in the strip and provides an output processed in a computer system 57 to control the movement of flux modifiers of a transverse flux induction heater so as to control the strip heating. <IMAGE>
Description
SPECIFICATION
Production of aluminium alloy strip
This invention relates to the production of aluminium alloy in strip form.
In a continuous process line for producing an aluminium alloy in strip form, cold rolling is often used to obtain a strip with accurate dimensions and a good surface. Cold rolling leaves the material in a work-hardened state in which it tends to be strong but not very ductile. To restore the ductility, the strip is annealed by maintaining it for a suitable time at a temperature in the range of 2000--4500C. Another method of obtaining high strengths in aluminium alloy strip is precipitation hardening. This precipitation hardening treatment hardens the strip by causing an extremely fine precipitate dispersion to form in the matrix.The heat treatment required to produce this dispersion consists of solution treatment in which any preexisting precipitates are dissolved to give a uniform solid solution, the heat treatment being followed by rapid quenching of the material to room temperature so as to retain the solid solution. The quenching is followed by ageing, which can take place at room temperature and/or temperatures in the range of 100 to 2000C during which the solid solution breaks down to give the fine precipitate dispersion.
On a continuous heat treatment line, there is a possibility of temperature variations across the width of the strip. In some aluminium alloys where the solution treatment is a sensitive function of the solution treatment time and temperature, such temperature variations across the width of the strip can lead to differential solution treatment across the strip width.
It is known to measure the thermal profile across the width of the strip by a scanning system sensitive to the radiation from the strip.
However radiation sensitive scanning systems have been found to be very sensitive to the emissivity of the surface being scanned. With some alloys, which usually are the same alloys as are very sensitive to the solution treatment conditions, the emissivity changes at high temperatures. This change in emissivity masks the true thermal profile of the strip as detected by radiation sensitive scanning systems.
We have found that the electrical conductance of the strip, as quenched, has a close correlation with the final mechanical properties which it is required to achieve.
According to one aspect of the present invention, in the method of producing aluminium alloy strip in which hardening of the material is effected by heat treatment to dissolve pre-existing precipitates in the metal matrix so as to give a uniform solid solution followed by quenching in a quenching bath and subsequent ageing, the electrical conductance of the strip after quenching is measured using a conductivity probe scanned across the width of the strip or an array of probes across the width of the strip and the degree of heating across the width of the strip is controlled in accordance with the measured conductance so as to tend to obtain uniform electrical conductance across the width of the strip.
Preferably the heat treatment is effected using a transverse flux induction heater having adjustable means for controlling the degree of heating across the width of the strip.
The electrical conductance may be measured by means of a non-contacting conductance probe which is repetitively scanned across the strip or an array of probes may be used to determine the conductance profile across the width of the strip.
The conductance profile is determined after quenching and preferably automatic control means are provided for controlling the heater to give the required heating power distribution across the width of the strip.
A transverse flux induction heater for the above-described process may comprise a plurality of windings and cores distributed across the width and along the length of the strip. Control of the heating power distribution may be effected by altering the power to individual windings, e.g. by adjusting the air gap, through which the strip passes, or by moving portions of the magnetic cores relative to the windings.
According to another aspect of the invention, heat treatment means for use in a strip mill for producing aluminium alloy strip comprise heating means for heating the strip to a temperature to effect solution treatment in which pre-existing precipitates are dissolved in the metal matrix to give a uniform solid solution, means for quenching the strip after heating so as to retain the solid solution, electrical conductance measuring means arranged to measure the electrical conductance of the strip after quenching either by scanning across the width of the strip or by utilising an array of probes to determine conductance profile and means for differentially adjusting the heating effect across the width of the strip in accordance with the measured conductance profile so as to tend to maintain a uniform conductance across the width of the strip.
The heating means are conveniently transverse flux induction heating means comprising a plurality of windings and corns. The means for differentially adjusting the heating effect conveniently comprises means for altering the air gaps through which the strip passes, between cores on opposite sides of the strip thereby differentially to change the flux distribution across the width of the strip arising from current through windings on the cores. Alternatively the electrical power supplied to said coils may be differentially adjusted to effect the required heating distribution.
The invention furthermore includes within its scope a strip mill incorporating heat treatment means as described above.
The following is a description of one embodiment of the invention, reference being made to the accompanying drawings in which: Figure 1 is a diagrammatic side elevation of part of an apparatus for processing aluminium
alloy strip;
Figure 2 is a diagrammatic transverse section
through the strip and induction heater for
explaining the form of heating control employed in
the apparatus of Figure 1;
Figure 3 is a diagram illustrating a conductivity
sensing assembly used in the apparatus of Figure 1;and Figure 4 shows diagramatically the apparatus
processing the output of the conductivity sensor of
Figure 3.
Referring to Figure 1 an aluminium alloy strip
10, which is to be heat treated in a continuous
process plant, passes over a roller 11 and thence
vertically downwards through a transverse flux
induction heater 12 to a quenching bath 13 in
which it passes around a roller 14 to leave the
bath upwardly at 1 6. Here the electrical
conductance of the strip is measured by a
scanning probe 1 7. The strip then passes over a roller 18 and is fed out at 1 9 for ageing at room
temperature, inspection and winding into a roil for
subsequent transport and use.
The present invention is concerned more
particularly with the control of the heating by the transverse flux induction heater 12. In a continuous heat treatment line using a transverse flux inductor, unless the heating is controlled, there is a possibility of temperature variations across the width of the strip. In some aluminium alloys, where the degree of solution treatment is sensitive to the solution treatment time and temperature, such temperature variations across the width can lead to differential solution treatment across the width.In the apparatus of the present invention, the electrical conductance of the strip is measured across the width of the strip after the quenching operation by a scanning probe 1 7. This is a non-contacting electrical conductivity measuring device which is mechanically repetitively scanned across the width of the strip by scanning means 20 to provide output information to a data processor storage device 21 which stores information representative of the conductance or conductance variations across the width of the strip. The conductivity measurement will be described later in further detail with reference to Figures 3 and 4.
The data processor 21 provides output control signals for actuator means 22 which adjusts the heating across the width of the strip by the transverse flux induction heater 12. As shown diagrammatically in Figure 2, the control means 22 may comprise a plurality of actuators 23 which act respectively on individual core and coil units 24 of the transverse induction heater 12. This induction heater comprises core and coil assemblies 24 adjacent one face of the strip and co-operating cores 25 on the opposite face. By moving the assemblies 24 towards and away from their respective co-operating cores 25, the air gap between the cores in each pair may be altered differentially and hence the heating effect may be adjusted differentially across the width of the strip 10.The actuators 23 are controlled by the data processor 21 in such a manner as to tend to
maintain a uniform conductance across the width of the strip.
Figures 3 and 4 illustrate further details of the conductivity measuring apparatus. In Figure 3, there is shown a roller 30 over which the strip 31 passes, together with a conductivity measurement device 32 situated close to the roller. This device comprises a transmitter 33 with a transmitting
head 34 producing an electromagnetic field at a frequency of about 5 kHz, the head being mounted on a C-shaped frame 35 so as to be about 25 mm above the upper surface of the strip 31. Typically the transmitter has a ferrite core driven from a medium power square wave oscillator running at the required frequency, e.g. 5 kHz. The transmitter has a high Q tuned circuit so that the output has a substantially sinusoidal waveform. This fieid from the transmitter induces eddy currents in the strip 31.A receiver 36 has a receiving head 37 mounted on the frame 35 below the strip, typically about 25 mm away from the strip surface. The receiver has a ferrite head which picks up the signals from the strip and amplifies them.
Changes in the amplitude of the output of the receiver will be due either to gauge variation in the strip or due to conductivity changes. The gauge
can be measured automatically, a gauge signal employed in processing the information from the receiver if this should be necessary.
The C-shaped frame 35 is mounted on rollers 40 running on rails 41 for movement to and fro across the width of the strip 31, the frame being driven by a servo drive motor 42 through a pinion 43 and rack 44. A signal representative of the transverse position of the transmitter/receiver is obtained from an electrically linear potentiometer 45 which mechanically is constructed as a helical potentiometer drive by a steel wire 46 attached to the frame 35 and tensioned by a counterweight 47.
The transmitter 33 is connected to its head 34 by a flexible cable 47. The receiver 36 is connected to the receiver head 37 by a second flexible cable 48. Output information from the receiver is produced at terminals 50 and output positional information from the potentiometer 45 at terminals 51. The input drive signals for the servo motor are applied at terminals 52.
Referring to Figure 4, the positional signals and receiver output signals are applied to a digital storage oscilloscope 55 to give a conductivity profile across the width of the strip. The information is in digital form and consists of 512 bytes of information representing the extent of the x-axis (that is the transverse position) and the amplitude for each of these 512 segments is digitised information representative of the appropriate one of 256 conductivity levels.
If the frame 35 is scanned beyond the edges of the strip 31, the resultant large changes in the receiver output gives indications enabling the actual width of the strip to be determined. When the strip line is running normally, cracks, flaws, etc. can be detected on the oscilloscope and
appropriate action taken.
The digital output from the oscilloscope 55 is
clocked, via an 8-bit data bus 56, into a
minicomputer 57. The minicomputer processes
the digital information and, via a bus 58 feeds
control signals to terminals 52 of the motor 42.
The minicomputer also provides digital inputs to
first and second digital-to-analogue converters 59,
60. The first digital-to-analogue converter 59
provides instructions, via flux modifier servo
amplifiers 61, to a servo motor system 62 for
effecting the necessary movements required by
the flux modifiers of the transverse flux induction
heater. These movements are determined from
the conductivity profile by periodic examination of
that profile. The second digital-to-analogue
converter 60 feeds signals to a strip width slitter
servo amplifier 63 controlling a servo motor 64.
Instead of mechanically scanning the
conductance probe as described above, it would
alternatively be possible to use a plurality of
probes spaced apart across the width of the strip
to provide, in the data processor, the required
information representing the conductance profile
(or variations in the conductance) across the strip.
With the above-described form of apparatus,
the aluminium strip passes through the transverse
flux induction heater 12 (Fig. 1) down into the
quenching bath 1 3. The conductance ,measurement across the width of the strip as the
strip comes out of the quenching bath gives
indications which are representative of any
unevenness of heating across the width of the
strip such as would give non-uniform solution
treatment. The control of the heating therefore
serves to maintain a more uniform treatment. The
measurement of the electrical conductance avoids
the problems which occur in attempting more
directly to measure the thermal profile across the
strip as it leaves the induction heater in that non
contacting temperature sensors are dependent on
the emissivity of the surface of the strip and it is
known that emissivity of some aluminium alloys
changes at high temperatures.
Although one form of heating control has been
described in which coil and core assemblies are
moved, other forms of control of the heating may
be employed, for example by electrical control of
the power to the various coils of the inductor.
A further advantage of the above-described
device is that it also operates to maintain more
uniform heat treatment along the length of the strip.
Claims (16)
1. A method of producing aluminium alloy strip
in which hardening of the material is effected by
heat treatment to dissolve pre-existing precipitates in the metal matrix so as to give a uniform solid solution followed by quenching in a quenching bath and subsequent ageing, wherein the electrical conductance of the strip after quenching is measured using a conductivity probe scanned across the width of the strip or an array of probes across the width of the strip and wherein the degree of heating across the width of the strip is controlled in accordance with the measured conductance so as to tend to obtain uniform electrical conductance across the width of the strip.
2. A method as claimed in claim 1 wherein the heat treatment is effected using induction heating.
3. A method as claimed in claim 2 wherein the heat treatment is effected using a transverse flux induction heater having adjustable means for controlling the degree of heating across the width of the strip.
4. A method as claimed in any of claims 1 to 3 wherein the electrical conductance is measured by means of a non-contacting conductance probe which is repetitively scanned across the strip.
5. A method as claimed in any of claims 1 to 3 wherein an array of probes are used to determine the conductance profile across the width of the strip.
6. A method as claimed in any of the preceding claims wherein automatic control means are provided for controlling the heating means to give the required heating power distribution across the width of the strip.
7. A method as claimed in claim 6 as appendant to either claim 2 or claim 3 wherein the heating power distribution is controlled by altering the power to individual windings of an induction heater having a plurality of windings.
8. A method as claimed in claim 6 as appendant to either claim 2 or claim 3 wherein the heating power distribution is controlled by adjusting the air gap, through which the strip passes, in the induction heater between individual core elements carrying windings on one face of the strip and co-operating core elements on the other face of the strip.
9. Heat treatment means for use in a strip mill for producing aluminium alloy strip wherein there are provided heating means for heating the strip to a temperature to effect solution treatment in which pre-existing precipitates are dissolved in the metal matrix to give a uniform solid solution means for quenching the strip after heating so as to retain the solid solution, electrical conductance measuring means arranged to measure the electrical conductance of the strip after quenching either by scanning across the width of the strip or by utilising an array of probes to determine conductance profile and means for differentially adjusting the heating effect across the width of the strip in accordance with the measured conductance profile so as to tend to maintain a uniform conductance across the width of the strip.
10. Heat treatment means as claimed in claim 9 wherein the heating means comprise an induction heater.
11. Heat treatment means as claimed in claim 9 wherein the heating means comprise transverse flux induction heating means having a plurality of windings and cores.
12. Heat treatment means as claimed in claim 11 wherein the means for adjusting the heating effect comprises means for differentially altering
the air gaps, through which the strip passes,
between cores on opposite sides of the strip of a transverse flux induction heater having a plurality of ferromagnetic cores spaced across the width of the strip on each face thereof thereby to change the flux distribution across the width of the strip arising from current through windings on the cores.
13. Heat treatment means as claimed in claim 11 wherein the means for adjusting the heating effect comprises means for differentially adjusting
the electrical power supplied to said coils.
14. A strip mill incorporating heat treatment
means as claimed in any of claims 9 to 13.
15. A method of producing aluminium alloy strip substantially as hereinbefore described with reference to the accompanying drawings.
16. Apparatus for the heat treatment of aluminium alloy strip substantially as hereinbefore described with reference to the accompanying drawings.