GB201320481D0 - Tungsten carbide composite material comprising aluminium oxide particles and silicon nitridewhiskers and preparation process thereof - Google Patents

Tungsten carbide composite material comprising aluminium oxide particles and silicon nitridewhiskers and preparation process thereof

Info

Publication number
GB201320481D0
GB201320481D0 GBGB1320481.3A GB201320481A GB201320481D0 GB 201320481 D0 GB201320481 D0 GB 201320481D0 GB 201320481 A GB201320481 A GB 201320481A GB 201320481 D0 GB201320481 D0 GB 201320481D0
Authority
GB
United Kingdom
Prior art keywords
composite material
tungsten carbide
oxide particles
aluminium oxide
preparation process
Prior art date
Legal status (The legal status is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the status listed.)
Granted
Application number
GBGB1320481.3A
Other versions
GB2506287B (en
GB2506287A (en
Current Assignee (The listed assignees may be inaccurate. Google has not performed a legal analysis and makes no representation or warranty as to the accuracy of the list.)
South China University of Technology SCUT
Original Assignee
South China University of Technology SCUT
Priority date (The priority date is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the date listed.)
Filing date
Publication date
Application filed by South China University of Technology SCUT filed Critical South China University of Technology SCUT
Publication of GB201320481D0 publication Critical patent/GB201320481D0/en
Publication of GB2506287A publication Critical patent/GB2506287A/en
Application granted granted Critical
Publication of GB2506287B publication Critical patent/GB2506287B/en
Expired - Fee Related legal-status Critical Current
Anticipated expiration legal-status Critical

Abstract

Disclosed in the present invention are a tungsten carbide composite material comprising aluminium oxide particles and silicon nitride whiskers and a preparation process thereof. The tungsten carbide composite material comprises 0.5-3% aluminium oxide particles by mass percent, and 0.4-10% silicon nitride whiskers by mass percent, and the balance is tungsten carbide and an inevitable impurity phase; the silicon nitride whiskers are authigenic ß-Si3N4 whiskers. The WC composite material prepared in the present invention does not contain any metal bonding phase, has good hardness, abrasion resistance and mechanical performance at high temperatures, and medium toughness; the present invention can not only reduce the costs of preparing the WC composite material, but also effectively expand the scope of application thereof; and the material is suitable as a cutter such as a indexable blade, etc., a plastic machining tool such as a wire-drawing die, etc., and is also suitable as a shearing tool, such as a punching and shearing die, etc.
GB1320481.3A 2011-08-05 2011-09-08 Tungsten Carbide Composite Containing Alumina Grains and Silicon Nitride Whiskers and the Preparation Method Thereof Expired - Fee Related GB2506287B (en)

Applications Claiming Priority (2)

Application Number Priority Date Filing Date Title
CN2011102234058A CN102390998B (en) 2011-08-05 2011-08-05 Tungsten carbide composite material containing aluminum oxide particles and silicon nitride whiskers, and preparation method thereof
PCT/CN2011/079485 WO2013020317A1 (en) 2011-08-05 2011-09-08 Tungsten carbide composite material comprising aluminium oxide particles and silicon nitride whiskers and preparation process thereof

Publications (3)

Publication Number Publication Date
GB201320481D0 true GB201320481D0 (en) 2014-01-01
GB2506287A GB2506287A (en) 2014-03-26
GB2506287B GB2506287B (en) 2019-07-31

Family

ID=45858406

Family Applications (1)

Application Number Title Priority Date Filing Date
GB1320481.3A Expired - Fee Related GB2506287B (en) 2011-08-05 2011-09-08 Tungsten Carbide Composite Containing Alumina Grains and Silicon Nitride Whiskers and the Preparation Method Thereof

Country Status (3)

Country Link
CN (1) CN102390998B (en)
GB (1) GB2506287B (en)
WO (1) WO2013020317A1 (en)

Families Citing this family (13)

* Cited by examiner, † Cited by third party
Publication number Priority date Publication date Assignee Title
CN102581271A (en) * 2012-03-30 2012-07-18 吉林大学 Powder metallurgy material mixing method
CN102863218B (en) * 2012-09-27 2014-06-11 华南理工大学 Tungsten carbide composite material containing zirconium oxide particles and silicon nitride whiskers and preparation method thereof
CN103360074A (en) * 2013-07-11 2013-10-23 东华大学 Preparation method for WC-Al2O3 nanometer composite material
CN104388724B (en) * 2014-11-24 2016-08-24 中南大学 A kind of process for dispersing of ultrafine WC powder
CN106542838B (en) * 2016-10-28 2019-10-18 华南理工大学 A kind of cubic network toughening WC composite material and preparation method
CN106513670B (en) * 2016-11-10 2018-12-18 株洲硬质合金集团有限公司 A kind of sintering method of ultra-fine cemented carbide
CN106591747B (en) * 2016-12-14 2018-07-20 华南理工大学 A kind of β-Si3N4Whisker and Ni3The WC composite material and preparation methods of Al Binder Phase coordination plasticizings
CN110845249B (en) * 2019-11-01 2022-04-22 华南理工大学 Silicon nitride composite material with improved elastic modulus and preparation method thereof
CN112622115A (en) * 2020-11-06 2021-04-09 浙江海洋大学 Screw rod rubber lining die of screw pump and using method of screw rod rubber lining die
CN113845743B (en) * 2021-10-12 2023-10-31 深圳妙将来新科技有限公司 Preparation method of polyethylene containing nano material
CN113732332A (en) * 2021-10-18 2021-12-03 南京理工大学 Temperature-sensing intelligent cutting tool and manufacturing method thereof
CN114956846B (en) * 2022-06-21 2023-10-27 郑州大学 Preparation method of SiC whisker toughened alumina ceramic cutter material
CN116969763B (en) * 2023-09-25 2023-12-12 成都先进金属材料产业技术研究院股份有限公司 Graphene-toughened non-bonding-phase WC-based hard alloy and preparation method thereof

Family Cites Families (7)

* Cited by examiner, † Cited by third party
Publication number Priority date Publication date Assignee Title
CN1453239A (en) * 2003-05-29 2003-11-05 上海交通大学 Large grain spherical sub-micron/nano composite fiber-ceramic powder
CN1271008C (en) * 2004-07-19 2006-08-23 西北工业大学 Preparation method of whisker and pacticle toughening ceramic base composite
CN1793042A (en) * 2006-01-06 2006-06-28 清华大学 In-situ flexible silicon nitride base ceramic and super-speed sintering process
CN101164996B (en) * 2006-10-16 2010-09-01 宁波大学 Silicon carbide ceramic containing silicon carbide whisker and rod-like aluminum oxide embedded particles
CN101008064A (en) * 2007-01-17 2007-08-01 江西省科学院应用物理研究所 Whisker plasticizing tungsten carbide-cobalt base hard alloy material and its preparation process
CN100569699C (en) * 2007-09-28 2009-12-16 清华大学 A kind of wiring board or circuit card special ceramic cutter material and preparation method thereof
BR112012010907A2 (en) * 2009-11-23 2019-09-24 Applied Nanostructured Sols "Ceramic composite materials containing carbon nanotube infused fiber materials and methods for their production"

Also Published As

Publication number Publication date
CN102390998B (en) 2013-07-24
GB2506287B (en) 2019-07-31
WO2013020317A1 (en) 2013-02-14
GB2506287A (en) 2014-03-26
CN102390998A (en) 2012-03-28

Similar Documents

Publication Publication Date Title
GB201320481D0 (en) Tungsten carbide composite material comprising aluminium oxide particles and silicon nitridewhiskers and preparation process thereof
CN104293291B (en) A kind of superhard abrasive compound and preparation method thereof
JP5678955B2 (en) Complex
JP6330387B2 (en) Sintered body and manufacturing method thereof
KR20130040769A (en) Sintered cubic boron nitride tool
JP5909607B1 (en) Cubic boron nitride sintered body and cutting tool
WO2009082180A3 (en) Solid-solution carbide/carbonitride powder and method for preparing thereof
WO2011108959A3 (en) Copper based binder for the fabrication of diamond tools
UA95912C2 (en) Composite rotating tool, method for forming and method for producing rotating tool
RU2011150215A (en) COMPOSITE ROTATING CUTTING TOOLS FROM CEMENT CARBIDE AND PREPARATIONS FOR ROTATING CUTTING TOOLS
CN102505090A (en) Preparation method of high-toughness polycrystalline cubic boron nitride compound sheets
CN101168229A (en) Method for manufacturing ultra-hard composite blade
CN102190497B (en) High-toughness crystalline cubic boron nitride-based ultrahigh pressure sintering material and cutting tool
WO2009082178A3 (en) Solid-solution carbide/carbonitride powder and method for preparing thereof under high temperature
CN102310235B (en) Diamond saw bit used for cutting alloy steel and preparation process thereof
WO2008040885A3 (en) Prealloyed metal powder, process for obtaining it, and cutting tools produced with it
CN106699190B (en) A method of the primary material of cubic boron nitride monocrystal, which is used, as initial feed prepares plycrystalline diamond sintered body
Cedergren et al. The effects of grain size and feed rate on notch wear and burr formation in wrought Alloy 718
CN104831144A (en) Composite hard alloy material and preparing method thereof
CN110512131A (en) Integral metal ceramic alloy bar and preparation method and application thereof
WO2013093847A2 (en) A method for sintering metal-matrix composite materials
CH704682B1 (en) Precision tool and process to achieve it.
CN208879828U (en) It is exclusively used in the saw blade of cutting steel
CN105861960B (en) A kind of TiAl base large amorphous alloys and preparation method thereof
CN105196016A (en) Manufacturing process for diamond tool bit

Legal Events

Date Code Title Description
PCNP Patent ceased through non-payment of renewal fee

Effective date: 20210908