GB1602603A - Coated metalworking tools - Google Patents
Coated metalworking tools Download PDFInfo
- Publication number
- GB1602603A GB1602603A GB22749/77A GB2274977A GB1602603A GB 1602603 A GB1602603 A GB 1602603A GB 22749/77 A GB22749/77 A GB 22749/77A GB 2274977 A GB2274977 A GB 2274977A GB 1602603 A GB1602603 A GB 1602603A
- Authority
- GB
- United Kingdom
- Prior art keywords
- coating
- inch
- tool
- hour
- working
- Prior art date
- Legal status (The legal status is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the status listed.)
- Expired
Description
(54) COATED METAL-WORKING TOOLS
(71) We, ROCOL LIMITED, of Rocol House, Swillington, Leeds, LS26 8BS, a British Company, do hereby declare the invention, for which we pray that a patent may be granted to us, and the method by which it is to be performed, to be particularly described in the following statement:- The invention relates to lubricants for metal-working tools.
Tools used in machining, drawing and general metal forming, cutting and other working operations are customarily lubricated with liquid lubricants in the form of straight oils or emulsions. Tool life however is not always satisfactory and we have sought to improve it.
Our approach is to coat the tool with an adherent, solid lubricant film of the
kind described below that remains on the tool when it is used with conventional
lubricants and gives a protective and wear-reducing effect.
Thus, according to one aspect of the invention, there is provided a composition for coating a metal-working tool, comprising by weight:
a) molybdenum disulphide, graphite or other solid lubricant in an amount of 5 to 60 parts, in an aqueous solution of:
b) an aluminum phosphate binder, in an amount of 1 to 5 parts calculated as aluminum hydroxide, c) ortho-phosphoric acid, in an amount of 3 to 25 parts calculated as the 88 to 93% acid, d) optionally a chromate or dichromate incorporated as such or as chromium trioxide, in an amount of up to 5 parts calculated as chromium trioxide.
Preferably the phosphate is mono-aluminum phosphate Al(H2PO4)3.
The invention also provides a metal working tool, particularly a metallic tool, given an adherent solid lubricant film by application of such a composition.
Preferably the binder is derived from a chromium trioxide (chromic anhydridetcontaining mono-aluminum phosphate, Al(H2PO4)3 solution. The phosphoric acid in the compositions gives a smoother coating and slight etching to help adhesion. The solid lubricant is present in dispersed form, and desirably a surface-active agent is present to aid maintenance of the dispersion.
A suitable proportion of the above monoaluminum phosphate would be for example 100 to 500 g per litre of solution, i.e. 10 to 50% weight by volume.
The composition as used preferably contains 50 to 80 parts of water total but may be sold with or without all or part of the water. A surface active agent, for example "Texafor 85FP" (Trade Mark) is preferably present, for example 0.1 to 2 parts on the same basis.
Alternatives to the chromium trioxide, containing equivalent amounts of chromium as chromium trioxide, are:
Potassium Chromate up to 10 parts
Potassium Dichromate up to 8 parts
Sodium Chromate up to 8 parts
Sodium Dichromate up to 12 parts
The purpose of the chromium content is to inhibit the acid phosphoric binder from undesired chemical action on the tool. The Texafor 85FP is an alkyl phenol condensate surface active agent of HLB value 12.4.
In preparing the tools at least the working edges or faces are coated, together,
in the case of cutting tools, with faces over which swarf will pass. Usually the whole
tool will be coated.
The ease with which swarf passes away from the cutting edge of a cutting tool
is an important benefit of the invention gained by such coating, prolonging the life
of the cutting edge itself. A similar effect is obtained in a punch for example, where
the working parts of the tool effectively include not only the face which punches
out metal from the hole but the sides also, which are in contact with the sides of the
hole as the punch carries out its stroke.
Application may be by spray, dip, brush or other method, the dispersion desirably
being kept thoroughly agitated. Application is followed by heat curing to improve
adhesion, for example an hour or more at 200"C to 2500C or three hours or more at 180"C. A typical final coating thickness is for example 0.0001 or 0.0002 inch, but
thicker coatings for example up to 0.001 inch can be obtained if required by
multiple applications with intermediate drying. Air drying, for example 10 minutes
at 20"C to 250C or 2 to 3 minutes at 600C to 800 C, is suitable. The dispersion itself
is preferably kept at 1 50C to 300C during application and tools to be coated may be
warmed if desired, for example to 600C to 80"C, to speed drying. The final coating
is heat cured as before. Neither drying nor curing temperatures are critical.
The tool should be clean before coating but simple solvent washing or vapour
degreasing, for example in 'Genklene' (Trade Mark) (1,1,I-trichlorethane), is
sufficient. Carbon steel and high speed steel tools, including chromium plated
tools, have for example been successfully coated. So also have ceramic tools, for
example sintered aluminium oxide.
Specific examples of final compositions showing various sources of chromate
(parts by weight) are:
A B C D E
Mono-Aluminium Phosphate 25.0 25.0 25.0 25.0 25.0
Solution (below)
Wetting Agent ('Texafor' 0.4 0.4 0.4 0.4 0.4
85FP)
Molybdenum Disulphide 20.0 20.0 20.0 20.0 20.0
Chromium Trioxide 1.3 - - - - Potassium Chromate - 2.6 - -
Sodium Dichromate - - 1.9 -
Potassium Dichromate - - - 1.9
Sodium Chromate - - - - 4.5
Water 53.3 52.0 52.7 52.7 50.1
Specific examples of final compositions showing variation in the solid
lubricants are (parts by weight):
F G H
Mono Aluminium Phosphate 12.5 25.0 12.5
Solution (below)
Wetting Agent ('Texafor' 0.4 1.0 1.0
85FP)
Graphite - 9.5 9.5
Molybdenum Disulphide 20.0 -
Chromium Trioxide 0.65 1.3 0.65
Water 66.45 63.2 76.35
The mono aluminium phosphate solution used was:
Distilled Water 41.9
Orthophosphoric Acid (88 to 93%) 41.9
Aluminium Hydroxide 16.2
Of the coatings, showing variation in the solid lubricant, and referring to A
also, coatings A and F are preferred at normal temperatures and coatings G and H
at high temperatures, for fluid lubricated and non fluid-lubricated applications
respectively in each case.
All the above compositions gave satisfactory results. Tests were further done in a rig loading specimens together under heavy stress and turning, using various amounts of molybdenum disulphide (the composition otherwise being that given at
A above).
The results are given below:
Twist Compression Tests
% MoS2 Revs. to failure u prior to failure 0 (Comparison) 3 0.2
10 50 0.12
20 550 0.05
60 900 0.05
Contact Stress 20 tsi (3 K bar)
Rotational Speed 26 rpm (4ft/min sliding)
Substrate AISI D3 (60 R: 1 ins CLA)
Specimen EN3A (mild steel)
Area of Contact 1.3 sq. ins.
Other tests were done by the 'Falex' method using various amounts of chromate (as CrO3) the rest of the composition being that given at A above, giving results that showed the chromium content, added as noted herein to avoid any difficulty with action of the acid on tool metal, did not prevent the required load wear resistance from being shown.
The following examples of user tests illustrate the invention further. To carry them out the following aluminium phosphate solution (parts by weight) was made up:
Ortho Phosphoric Acid (88 to 93%) 55.80
Aluminium Hydroxide 12.31
Distilled Water 31.89
100.00 and the solution was used to make up the following specific compositions, (composition I) against expressed in parts by weight.
Mono Aluminium Phosphate solution 24.7
Chromium Trioxide 1.3
Molybdenum Disulphide powder 20.0
'Texafor' (Trade Mark) 85FP dispersing agent 0.4
Distilled Water 53.6
100.0
The composition was then used as follows:
Example 1
Aluminium L93 and L94 forgings are milled with a double-flute router or slotter 2 inches diameter and 3 inches long made of high speed steel, at a cutting speed of 1800 ft/min (3500 r.p.m.) taking a cut 2 inches wide and 2 inch deep. The forgings require approximately 24 hours machining time on an N.C. milling machine such as a Marwin Maximill (Trade Mark) Vertical 2 Spindle Head. With flood lubrication using a mineral oil emulsion such as Castrol Almasol A (Trade
Mark) at 20:1 dilution, four components are normally milled before regrinding of the tool.
After coating the tool with the specific composition given earlier and with one spray coat dried one hour each at room temperature, 80"C and 250"C, 15 or 16 such components can regularly be milled before regrinding is required.
Example 2
Using the same coating composition similar results to Example I have been obtained:
a) With a 6 inchx0.3165 inch side and face milling cutter machining EN 110 steel with soluble oil lubricant. An improvement of two to three times in tool life is given after two brush applications of the coating dried for 10 minutes at room temperature then 1 hour at 2500 C.
b) With end milling cutters machining titanium fan blades in a gang miller with oil emulsion lubrication, showing an improvement in tool life from average 20 to average 38 components after two dip applications of the coating dried 16 hours at room temperature and 1 hour at 2500 C.
c) With a 4 inchx5 inch hob, machining tractor timing gears in 670T steel at 110 r.p.m. and 0.080 inch/rev. feed under soluble oil lubrication. Tool life was iinproved from an average 9 regrinds to an average 12 regrinds using two brushed applications of the coating with drying 16 hours at room temperature and 1 hour at 2500C.
d) With a 28 mm high speed steel drill working at 220 r.p.m. and 0.006 inch/rev.
feed, soluble oil lubrication, on forge steel 605/M 36T components. Coating as in c) raised average drill life from 1600 to 3200 components.
e) With a 3/8 inch UNF tap working in 86/20 colourised hard steel 180/230 Brinell-35/40 ton with Stewarts AP cutting fluid, and also with a Goliath U.K.
KZS M20x 1.573 tap working in cast iron with paraffin lubrication. Increases in tool life of 300% were gained, in the first case using a single dip coat, touched up by brush and dried 16 hours at room temperature and 1 hour at 2500 C, and in the second case using three dip coats with nylon brush burnishing between coats.
Example 3
Panteg 430 (Trade Mark) stainless iron gas burner plates 6.4x10-3 inch thick (16 swg) are punched with 72 holes 17.1 mm diameter, drawn by the punching to 6.3 mm deep. High speed steel punches are used, made by grinding 0.001 inch undersize in diameter, hard chromium plating to 0.002 inch oversize and finishgrinding and polishing to size. Deep drawing lubricant diluted with engine oil is the lubricant.
The internal surfaces of the punched holes must for satisfactory performance be highly polished, without scratches or imperfections, and to achieve this finish, repolishing of the punch after every 4 to 6 holes has been necessary. The punch has generally finished approximately 0.001 inch undersize after making a plate and has been thrown away.
After coating according to the invention with one dipped coat, dried one hour at room temperature and 1 hour at 2500 C, the punches produce a plate without repolishing and without measurable wear, and can continue to be used. A tool life of over twenty complete plates has been achieved.
Similar results were obtained with an 0.109 inch diameter high speed steel piercing punch for fully annealed bright mild steel jewellery components. The uncoated punches on test had an average life of 1500 holes and the coated ones 133000 holes, without use of lubricant.
Example 4
The coating composition used in the above examples was modified by use of flake graphite weight for weight, instead of disulphide, and three dip coatings, each dried 10 minutes at 600C and 1 hour at 2500C and burnished with paper cloth between coats, were applied to a Wickman Wimet (Trade Mark) carbide tipped end milling cutter. Used to machine contact breaker parts of Ferrosil 170 (Trade
Mark) soft iron in fully annealed blue oxide finish, with an unlubricated cut of 0.005 to 0.007 inch at 1125 r.p.m., the cutters showed an increase in average life from 1,750 to 8,500 components.
WHAT WE CLAIM IS:
1. A composition for coating a metal-working tool, comprising by weight:
a) molybdenum disulphide, graphite or other solid lubricant in an amount of 5 to 60 parts, in an aqueous solution of:
b) an aluminum phosphate binder, in an amount of 1 to 5 parts calculated as aluminum hydroxide,
c) ortho-phosphoric acid, in an amount of 3 to 25 parts calculated as the 88 to 93% acid,
d) optionally a chromate or dichromate incorporated as such or as chromium trioxide, in an amount of up to 5 parts calculated as chromium trioxide.
2. A composition according to claim 1, in which the phosphate is mono aluminum phosphate, AI(H2PO4)3.
3. A metallic or other metal working tool wherein to increase the working life
**WARNING** end of DESC field may overlap start of CLMS **.
Claims (7)
- **WARNING** start of CLMS field may overlap end of DESC **.given after two brush applications of the coating dried for 10 minutes at room temperature then 1 hour at 2500 C.b) With end milling cutters machining titanium fan blades in a gang miller with oil emulsion lubrication, showing an improvement in tool life from average 20 to average 38 components after two dip applications of the coating dried 16 hours at room temperature and 1 hour at 2500 C.c) With a 4 inchx5 inch hob, machining tractor timing gears in 670T steel at 110 r.p.m. and 0.080 inch/rev. feed under soluble oil lubrication. Tool life was iinproved from an average 9 regrinds to an average 12 regrinds using two brushed applications of the coating with drying 16 hours at room temperature and 1 hour at 2500C.d) With a 28 mm high speed steel drill working at 220 r.p.m. and 0.006 inch/rev.feed, soluble oil lubrication, on forge steel 605/M 36T components. Coating as in c) raised average drill life from 1600 to 3200 components.e) With a 3/8 inch UNF tap working in 86/20 colourised hard steel 180/230 Brinell-35/40 ton with Stewarts AP cutting fluid, and also with a Goliath U.K.KZS M20x 1.573 tap working in cast iron with paraffin lubrication. Increases in tool life of 300% were gained, in the first case using a single dip coat, touched up by brush and dried 16 hours at room temperature and 1 hour at 2500 C, and in the second case using three dip coats with nylon brush burnishing between coats.Example 3 Panteg 430 (Trade Mark) stainless iron gas burner plates 6.4x10-3 inch thick (16 swg) are punched with 72 holes 17.1 mm diameter, drawn by the punching to 6.3 mm deep. High speed steel punches are used, made by grinding 0.001 inch undersize in diameter, hard chromium plating to 0.002 inch oversize and finishgrinding and polishing to size. Deep drawing lubricant diluted with engine oil is the lubricant.The internal surfaces of the punched holes must for satisfactory performance be highly polished, without scratches or imperfections, and to achieve this finish, repolishing of the punch after every 4 to 6 holes has been necessary. The punch has generally finished approximately 0.001 inch undersize after making a plate and has been thrown away.After coating according to the invention with one dipped coat, dried one hour at room temperature and 1 hour at 2500 C, the punches produce a plate without repolishing and without measurable wear, and can continue to be used. A tool life of over twenty complete plates has been achieved.Similar results were obtained with an 0.109 inch diameter high speed steel piercing punch for fully annealed bright mild steel jewellery components. The uncoated punches on test had an average life of 1500 holes and the coated ones 133000 holes, without use of lubricant.Example 4 The coating composition used in the above examples was modified by use of flake graphite weight for weight, instead of disulphide, and three dip coatings, each dried 10 minutes at 600C and 1 hour at 2500C and burnished with paper cloth between coats, were applied to a Wickman Wimet (Trade Mark) carbide tipped end milling cutter. Used to machine contact breaker parts of Ferrosil 170 (Trade Mark) soft iron in fully annealed blue oxide finish, with an unlubricated cut of 0.005 to 0.007 inch at 1125 r.p.m., the cutters showed an increase in average life from 1,750 to 8,500 components.WHAT WE CLAIM IS: 1. A composition for coating a metal-working tool, comprising by weight: a) molybdenum disulphide, graphite or other solid lubricant in an amount of 5 to 60 parts, in an aqueous solution of: b) an aluminum phosphate binder, in an amount of 1 to 5 parts calculated as aluminum hydroxide,c) ortho-phosphoric acid, in an amount of 3 to 25 parts calculated as the 88 to 93% acid, d) optionally a chromate or dichromate incorporated as such or as chromium trioxide, in an amount of up to 5 parts calculated as chromium trioxide.
- 2. A composition according to claim 1, in which the phosphate is mono aluminum phosphate, AI(H2PO4)3.
- 3. A metallic or other metal working tool wherein to increase the working lifeof the tool there is provided, on at least the surfaces of the tool to contact the work or material cut from it, an adherent solid film of graphite, molybdenum disulphide or other solid lubricant in a binder comprising a phosphate of aluminum and optionally a chromate or dichromate, derived from a composition according to claim 1 or claim 2.
- 4. A composition for coating a metal-working tool, substantially as the specific composition I disclosed herein.
- 5. A composition for coating a metal-working tool, substantially as any one of the specific compositions A to H disclosed herein,
- 6. A metal-working tool given a lubricant film by coating with a composition according to claim 4.
- 7. A metal-working tool given a lubricant film by coating with a composition according to claim 5.