GB1446026A - Composite particles - Google Patents

Composite particles

Info

Publication number
GB1446026A
GB1446026A GB3761073A GB3761073A GB1446026A GB 1446026 A GB1446026 A GB 1446026A GB 3761073 A GB3761073 A GB 3761073A GB 3761073 A GB3761073 A GB 3761073A GB 1446026 A GB1446026 A GB 1446026A
Authority
GB
United Kingdom
Prior art keywords
sheath
core
powder
coating
particles
Prior art date
Legal status (The legal status is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the status listed.)
Expired
Application number
GB3761073A
Current Assignee (The listed assignees may be inaccurate. Google has not performed a legal analysis and makes no representation or warranty as to the accuracy of the list.)
Fujimi Kenmazai Kogyo Co Ltd
Fujimi Inc
Mitsubishi Petrochemical Co Ltd
Original Assignee
Fujimi Abrasives Co Ltd
Fujimi Kenmazai Kogyo Co Ltd
Mitsubishi Petrochemical Co Ltd
Priority date (The priority date is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the date listed.)
Filing date
Publication date
Application filed by Fujimi Abrasives Co Ltd, Fujimi Kenmazai Kogyo Co Ltd, Mitsubishi Petrochemical Co Ltd filed Critical Fujimi Abrasives Co Ltd
Publication of GB1446026A publication Critical patent/GB1446026A/en
Expired legal-status Critical Current

Abstract

1446026 Porous-coated particles MITSUBISHI PETROCHEMICAL CO Ltd and FUJIMI KENMAZAI KOGYO KK 8 Aug 1973 [10 Aug 1972] 37610/73 Headings B1E and B2E [Also in Division C1] A particle comprises a core of metal or metal oxide catalyst having a coating or a sheath which is formed with pores to allow the passage of fluid through the coating or sheath, the coating or sheath having greater crush strength and abrasion resistance than the core. A space may be formed between the sheath and core. In a preferred method, catalyst core material is mixed with water to form a paste which is granulated. The granules are then coated with a paste of sheath material and the particles are then dried and sintered. Sintering is omitted when coatings of powdered organic particles are used. The sheath material may be particulate or be formed of particles and a fusable binder. The material of the sheath may include or comprise the same material as the core. The core material may be an oxidation catalyst such as MnO 2 or catalysts such as Pt or Pd supported on an inert carrier. The space between the sheath and core may be formed by providing an intermediate coating of a material which is combustible during sintering, such materials being e.g. walnut husk powder or fibres, sawdust cellulose, polyolefins, polystyrene, wheat flour, microcrystalline cellulose, cornstarch, saccharide or polyvinyl alcohol. It is also possible to use materials which are soluble in water, acid or alkali, or a sublimatable material (e.g. camphor) to make the space. The space forming material can be used in forming the pores in the sheath or in the core. The sheath material may. be ceramic powder (e.g. fused Al 2 O 3 , SiC, Al 2 O 3 , SiO 2 , or zircon), glass powder (e.g. sodium, lead or borosilicate glass), metal powder (e.g. Fe, Al, Cu, Sn, Pb or Zn), alloy powder (e.g. gun metal, stainless steel), MgO, cements (e.g. Portland or alumina cement), or organic polymers. When the sheath material is difficult to bond by sintering a binder such as clay, kaolin, feldspar or glass powder is used. An MnO 2 / Fe 2 O 3 core with a glass/alumina powder sheath is stated to catalyse oxidation CO and Hydrocarbons in exhaust gases. Examples of MnO 3 with various sheaths are given wherein phenol is converted to 2, 6 xylenol and o-cresol.
GB3761073A 1972-08-10 1973-08-08 Composite particles Expired GB1446026A (en)

Applications Claiming Priority (1)

Application Number Priority Date Filing Date Title
JP47080252A JPS5831978B2 (en) 1972-08-10 1972-08-10 Kinobutsutsushihogokouzotai

Publications (1)

Publication Number Publication Date
GB1446026A true GB1446026A (en) 1976-08-11

Family

ID=13713109

Family Applications (1)

Application Number Title Priority Date Filing Date
GB3761073A Expired GB1446026A (en) 1972-08-10 1973-08-08 Composite particles

Country Status (4)

Country Link
JP (1) JPS5831978B2 (en)
DE (2) DE2340604A1 (en)
FR (1) FR2195478B1 (en)
GB (1) GB1446026A (en)

Cited By (2)

* Cited by examiner, † Cited by third party
Publication number Priority date Publication date Assignee Title
CN106220011A (en) * 2016-06-17 2016-12-14 李高明 A kind of preparation method of the hollow baking-free ceramicite of gardening
CN110038564A (en) * 2019-03-25 2019-07-23 宁波大学 A kind of catalyst with core-casing structure and preparation method thereof of high-efficient purification burning waste gas

Families Citing this family (10)

* Cited by examiner, † Cited by third party
Publication number Priority date Publication date Assignee Title
JPS6025171B2 (en) * 1976-02-18 1985-06-17 積水化成品工業株式会社 Manufacturing method of filter media
LU76412A1 (en) * 1976-12-17 1977-06-10
JPS56100161A (en) * 1980-01-10 1981-08-11 Shiga Prefecture Manufacture of ceramics with hole
DK144996C (en) * 1980-05-19 1982-12-20 Haldor Topsoe As PROCEDURE FOR CARRYING OUT THE CATALYTIC EXOTHERMY GAS PHASE PROCESS AND PROCEDURE FOR THE PREPARATION OF A CATALYST
DE3221306C2 (en) * 1982-06-05 1986-01-09 Kernforschungsanlage Jülich GmbH, 5170 Jülich Process for the reduction or oxidation of reducible or oxidizable substances in aqueous solution
DE3221315C2 (en) * 1982-06-05 1986-04-17 Kernforschungsanlage Jülich GmbH, 5170 Jülich Device for the reduction or oxidation of substances in aqueous solution
US4477492A (en) * 1983-04-22 1984-10-16 E. I. Du Pont De Nemours And Company Process for preparing superficially porous supports for chromatography and catalysts
JPH0798707B2 (en) * 1986-05-31 1995-10-25 イビデン株式会社 Porous refractory molding for firing functional parts
CN101157015B (en) * 2002-06-12 2011-11-02 创普太克公司 Encapsulated active particles and methods for making and using the same
KR101780185B1 (en) * 2010-12-10 2017-09-21 삼성전자주식회사 Absorbent shell and manufacturing method thereof

Family Cites Families (6)

* Cited by examiner, † Cited by third party
Publication number Priority date Publication date Assignee Title
US1874743A (en) * 1928-08-21 1932-08-30 Gyro Process Co Method of producing catalytic cores
US3030300A (en) * 1957-12-11 1962-04-17 California Research Corp Catalytic cracking with an attrition resistant catalyst
US3145183A (en) * 1958-12-16 1964-08-18 Norton Co Catalyst carrying balls
US3399513A (en) * 1964-12-24 1968-09-03 Exxon Research Engineering Co Coated cuprous halide sorbents and a method for sorbing ligands
US3505785A (en) * 1967-06-20 1970-04-14 Du Pont Superficially porous supports for chromatography
CA907292A (en) * 1970-01-28 1972-08-15 H. Stevens William Process and catalyst for enriching a fluid with hydrogen isotopes

Cited By (2)

* Cited by examiner, † Cited by third party
Publication number Priority date Publication date Assignee Title
CN106220011A (en) * 2016-06-17 2016-12-14 李高明 A kind of preparation method of the hollow baking-free ceramicite of gardening
CN110038564A (en) * 2019-03-25 2019-07-23 宁波大学 A kind of catalyst with core-casing structure and preparation method thereof of high-efficient purification burning waste gas

Also Published As

Publication number Publication date
FR2195478B1 (en) 1978-08-11
DE2340604C2 (en) 1990-09-13
DE2340604A1 (en) 1974-02-28
JPS4936705A (en) 1974-04-05
FR2195478A1 (en) 1974-03-08
JPS5831978B2 (en) 1983-07-09

Similar Documents

Publication Publication Date Title
GB1446026A (en) Composite particles
KR940000869B1 (en) Preparation of monolithic catalyst supports having an integrated high surface area phase
US4888317A (en) Catalyst-agglomerate bodies encapsulated in a structure and method for their production
US3145183A (en) Catalyst carrying balls
GB1068186A (en) Improved supported catalysts
US3798176A (en) Method for manufacturing a catalyst and its carrier having a vacant center or a dense center
GB1374273A (en) Catalysis
GB1578833A (en) Articles having self-cleaning coatings
GB1362948A (en) Protective coatings
KR920014521A (en) Catalyst carrier
JP2002527334A5 (en)
US4059544A (en) Active material compositions with porous protective sheath and method for preparing
GB1383477A (en) Process for manufacturing granular foamed products of silica
KR930017618A (en) Silver catalyst for the production of ethylene oxide and its preparation method
US6933255B2 (en) Beta-spodumene ceramics for high temperature applications
JP2006521996A (en) Low thermal expansion calcium aluminate molded product
JP2651170B2 (en) Ceramics porous body
GB2115307A (en) Supported catalysts for purification of waste gas and process for preparing the same
CN102531647A (en) Electroceramic high-temperature-resistant adhesion-isolating special material
CN113061016A (en) Preparation method of integral metal stair ceramic tile with original groove
US2985547A (en) Method for preparing coated bodies
JP2001213665A (en) Ceramics, catalyst carrier, their manufacturing method, catalyst for manufacturing ethylene oxide using carrier, its manufacturing method and manufacturing method of ethylene oxide
GB1357072A (en) Reduction of the surface resistances of ceramic bodies
GB1389007A (en) Catalytic coating
CN116262668B (en) Preparation process of antibacterial high-strength ceramic

Legal Events

Date Code Title Description
PS Patent sealed [section 19, patents act 1949]
PCNP Patent ceased through non-payment of renewal fee