GB1130801A - Production of fiber-reinforced synthetic resins - Google Patents
Production of fiber-reinforced synthetic resinsInfo
- Publication number
- GB1130801A GB1130801A GB55710/66A GB5571066A GB1130801A GB 1130801 A GB1130801 A GB 1130801A GB 55710/66 A GB55710/66 A GB 55710/66A GB 5571066 A GB5571066 A GB 5571066A GB 1130801 A GB1130801 A GB 1130801A
- Authority
- GB
- United Kingdom
- Prior art keywords
- mix
- resin
- working
- reinforced synthetic
- temperature
- Prior art date
- Legal status (The legal status is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the status listed.)
- Expired
Abstract
1,130,801. Fibre-reinforced synthetic resins. FIBERFIL Inc. 13 Dec., 1966 [15 Dec., 1965], No. 55710/66. Heading C3P. A fibre-reinforced synthetic thermoplastic resin is produced by working together into a mix the reinforcing fibres and a liquid comprising a liquid precursor of the resin which is the monomer in the unpolymerized and/or partially polymerized state and has a viscosity of not more than 200,000 cp. at the temperature at which working is commenced, forcing the mix to flow under pressure along a predetermined flow path while continuing its working at least until the fibres have become uniformly dispersed throughout the mix, controlling the temperature of the mix along the flow path to effect polymerization of the liquid resin precursor and extruding the mix through a restricted opening with the resin polymerized to such an extent that the extrudate is solid at the temperature prevailing outside the extruder. In an example a mixture of polystyrene and glass fibres together with a mixture of styrene monomer and polymer, tert. butyl peracetate and ditert. butyl peroxide were treated as above in an extruding apparatus which is illustrated by 4 Figs. (not shown).
Applications Claiming Priority (1)
Application Number | Priority Date | Filing Date | Title |
---|---|---|---|
US51399965A | 1965-12-15 | 1965-12-15 |
Publications (1)
Publication Number | Publication Date |
---|---|
GB1130801A true GB1130801A (en) | 1968-10-16 |
Family
ID=24045401
Family Applications (1)
Application Number | Title | Priority Date | Filing Date |
---|---|---|---|
GB55710/66A Expired GB1130801A (en) | 1965-12-15 | 1966-12-13 | Production of fiber-reinforced synthetic resins |
Country Status (6)
Country | Link |
---|---|
BE (1) | BE691109A (en) |
CH (1) | CH482772A (en) |
DE (1) | DE1753621A1 (en) |
FR (1) | FR1504989A (en) |
GB (1) | GB1130801A (en) |
NL (1) | NL6617363A (en) |
Families Citing this family (2)
Publication number | Priority date | Publication date | Assignee | Title |
---|---|---|---|---|
DE2706755C2 (en) * | 1977-02-17 | 1983-12-22 | Dynamit Nobel Ag, 5210 Troisdorf | Method and device for incorporating glass fibers into thermoplastics |
EP0512730B1 (en) * | 1991-05-06 | 1996-02-21 | Dow Corning S.A. | Manufacture of moisture curable organosiloxane compositions |
-
1966
- 1966-12-09 NL NL6617363A patent/NL6617363A/xx unknown
- 1966-12-12 FR FR87119A patent/FR1504989A/en not_active Expired
- 1966-12-13 GB GB55710/66A patent/GB1130801A/en not_active Expired
- 1966-12-13 BE BE691109D patent/BE691109A/xx unknown
- 1966-12-14 DE DE19661753621 patent/DE1753621A1/en active Pending
- 1966-12-15 CH CH1795166A patent/CH482772A/en not_active IP Right Cessation
Also Published As
Publication number | Publication date |
---|---|
NL6617363A (en) | 1967-06-16 |
BE691109A (en) | 1967-05-16 |
CH482772A (en) | 1969-12-15 |
FR1504989A (en) | 1967-12-08 |
DE1753621A1 (en) | 1972-04-20 |
Similar Documents
Publication | Publication Date | Title |
---|---|---|
US3591674A (en) | Process for the preparation of polymeric materials | |
GB1526398A (en) | Manufacture of extruded products | |
GB1021623A (en) | A process for manufacturing films of expanded polystyrene | |
US3664795A (en) | Screw extruders with dual section ejection zone | |
ES445205A1 (en) | Material and apparatus for extruding a crosslinked polyolefin product | |
GB1131127A (en) | Method and apparatus for forming a composite sheet of thermoplastic resinous material | |
ES405948A1 (en) | Method for the preparation of plastic foam | |
GB1300092A (en) | Improvements in and relating to plants for the production of casting resins | |
GB1521624A (en) | Extruder for the degassing and modification of synthetic resins | |
ES359896A1 (en) | Continuous process for making expandable thermoplastic resin compositions | |
ES483946A1 (en) | A process for extruding ethylene polymers. | |
US3745200A (en) | Extrusion method | |
US3658973A (en) | Method for extruding a foamed thermoplastic polymer | |
GB1130801A (en) | Production of fiber-reinforced synthetic resins | |
GB1346346A (en) | Apparatus and method for the extrusion moulding of foamable synthetic plastics material | |
US3470584A (en) | Extruder for shaping powdery thermoplastic resins | |
US2952041A (en) | Process for intermittent flow of plastic material | |
US3536787A (en) | Process for devolatilizing polymers | |
GB927501A (en) | Extrusion apparatus and processes | |
ES432338A1 (en) | Process for the polymerization of alpha olefins | |
GB1291997A (en) | Method and apparatus for extrusion of synthetic resinous materials | |
GB1048999A (en) | Thermoplastic resin foams | |
FR2218183A1 (en) | Extrusion system for crosslinkable polymers - where the shear work input can be varied independently of the polymer throughput | |
GB1389922A (en) | Process control | |
GB1104926A (en) | Production of foamable resins |