GB1084417A - The soldering together of ceramic and sheet metal members - Google Patents
The soldering together of ceramic and sheet metal membersInfo
- Publication number
- GB1084417A GB1084417A GB3269/65A GB326965A GB1084417A GB 1084417 A GB1084417 A GB 1084417A GB 3269/65 A GB3269/65 A GB 3269/65A GB 326965 A GB326965 A GB 326965A GB 1084417 A GB1084417 A GB 1084417A
- Authority
- GB
- United Kingdom
- Prior art keywords
- rings
- ceramic
- soldering
- soldered
- silver
- Prior art date
- Legal status (The legal status is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the status listed.)
- Expired
Abstract
1,084,417. Soldering. SIEMENS-SCHUCKERTWERKE A.G. Jan. 25, 1965 [Jan. 24, 1964; March 13, 1964], No. 3269/65. Heading B3R. [Also in Division H1] A sheet metal member of thickness not greater than 0À5 mm. and of silver, copper or gold is joined to a metallized ceramic member having a thickness at least 10 times that of the metal member using hard solder. In encapsulating a semi-conductor element 2 having two molybdenum electrodes 3, 4 in a housing comprising two sintered aluminium oxide ceramic rings 5, 6, two metal rings 9, 10 secured to the ceramic rings, and two metal foils 7, 8 soldered to the ceramic rings, the rings 9, 10 of iron-nickel-cobalt alloy are hard soldered to the ceramic rings and the foils 7, 8 of silver, copper or gold are soldered to the ceramic rings before, after or simultaneously with the soldering of the rings 9, 10. In soldering the foils, 200 Á thick to the metallized ceramic rings, at least 2 mm. thick, a silver-copper eutectic solder in powder, ring-shaped foil or wire is employed, heating being effected in a hydrogen or forming gas (nitrogen/hydrogen) electric furnace. After melting the solder air may be blown for cooling purposes and cold protective gas may be passed over the joint. After the soldering is complete the rings 9, 10 are welded, soldered or flanged preferably in nitrogen.
Applications Claiming Priority (2)
Application Number | Priority Date | Filing Date | Title |
---|---|---|---|
DE1964S0089205 DE1251629C2 (en) | 1964-01-24 | 1964-01-24 | HARD SOLDER CONNECTION BETWEEN A PLATE MADE OF A METAL OF THE FIRST SUB-GROUP OF THE PERIOD SYSTEM OF ELEMENTS AND A CERAMIC PART |
DES0089997 | 1964-03-13 |
Publications (1)
Publication Number | Publication Date |
---|---|
GB1084417A true GB1084417A (en) | 1967-09-20 |
Family
ID=25997549
Family Applications (1)
Application Number | Title | Priority Date | Filing Date |
---|---|---|---|
GB3269/65A Expired GB1084417A (en) | 1964-01-24 | 1965-01-25 | The soldering together of ceramic and sheet metal members |
Country Status (4)
Country | Link |
---|---|
CH (1) | CH445266A (en) |
GB (1) | GB1084417A (en) |
NL (1) | NL6500770A (en) |
SE (1) | SE307273B (en) |
Cited By (1)
Publication number | Priority date | Publication date | Assignee | Title |
---|---|---|---|---|
EP0085914A2 (en) * | 1982-02-06 | 1983-08-17 | BROWN, BOVERI & CIE Aktiengesellschaft | Method for the direct bonding of copper articles to oxide-ceramic substrates |
-
1964
- 1964-12-09 CH CH1587164A patent/CH445266A/en unknown
-
1965
- 1965-01-19 SE SE678/65A patent/SE307273B/xx unknown
- 1965-01-21 NL NL6500770A patent/NL6500770A/xx unknown
- 1965-01-25 GB GB3269/65A patent/GB1084417A/en not_active Expired
Cited By (2)
Publication number | Priority date | Publication date | Assignee | Title |
---|---|---|---|---|
EP0085914A2 (en) * | 1982-02-06 | 1983-08-17 | BROWN, BOVERI & CIE Aktiengesellschaft | Method for the direct bonding of copper articles to oxide-ceramic substrates |
EP0085914A3 (en) * | 1982-02-06 | 1985-10-02 | Brown, Boveri & Cie Aktiengesellschaft | Method for the direct bonding of metal pieces to oxide-ceramic substrates |
Also Published As
Publication number | Publication date |
---|---|
CH445266A (en) | 1967-10-15 |
SE307273B (en) | 1968-12-23 |
NL6500770A (en) | 1965-07-26 |
Similar Documents
Publication | Publication Date | Title |
---|---|---|
GB939871A (en) | Method of bonding aluminum members | |
GB1477521A (en) | Vacuum-tight soldered joint between a metal connection member and an apertured ceramic body | |
US3119052A (en) | Enclosures for semi-conductor electronic elements | |
GB1022432A (en) | Improvements in or relating to the bonding of a ceramic to a metal | |
US3988825A (en) | Method of hermetically sealing an electrical component in a metallic housing | |
GB1078779A (en) | Semiconductor devices | |
FR2321193B1 (en) | ||
JPS594008A (en) | Ceramic condenser filled in sealed glass capsule | |
GB1084417A (en) | The soldering together of ceramic and sheet metal members | |
GB1339166A (en) | Capacitors | |
GB1257148A (en) | ||
JPS5464049A (en) | Bonding of metals or alloys | |
US3414964A (en) | Method for the production of a soldered joint | |
GB975827A (en) | A semi-conductor arrangement | |
GB1062006A (en) | Semiconductor device with flexible lead | |
GB1215535A (en) | Improvements in and relating to headers for the envelope of a semiconductor device | |
GB1175122A (en) | Improvements in and relating to Semiconductor Devices | |
US3897624A (en) | Method for bonding ceramics with metal | |
GB917416A (en) | Improvements in and relating to methods of securing together parts of ceramic material | |
GB1081908A (en) | Improvements in or relating to contact connections for wire-shaped heating elements | |
JP2868851B2 (en) | Gas sealed arrester | |
US3402276A (en) | Hermetically sealed switches | |
US3147361A (en) | Vacuum tight joint and method of making such joint | |
US3202490A (en) | Sealing structure | |
GB1026054A (en) | Improvements relating to vacuum electric devices |