Abstract

The invention relates to a fluidic device (1), comprising a housing (2) comprising a channel (3) delimited by walls, of which a first main wall (10), the channel (3) extending between two orifices, said inlet (4A) and outlet (4B), and a porous open-pore medium of a metallic material, said metal foam (30), located in the channel (3) between said inlet ports (4A) and output (4B). The metal foam (30) and said first main wall (10) are made in one piece and in the same material, and the metal foam (30) has a random spatial distribution of the pores.

Description

FLUIDIC DEVICE WITH METALLIC FOAM TECHNICAL FIELD

The field of the invention is that of fluidic devices comprising a channel formed in a housing, in which there is a porous medium with open pores in a metallic material called metal foam. The invention applies for example as a heat exchanger ensuring the heat transfer between a component disposed against a wall of the housing, for example an electronic power component or a component of the automotive or nuclear field, and a circulating heat transfer fluid in the canal and passing through the metal foam. The invention can also be applied to the field of fluid filtration.

STATE OF THE PRIOR ART

Heat exchangers, also known as heat sinks, are known in the form of a fluidic device having a channel, formed in a housing, which extends between inlet and outlet ports. The housing may then comprise a main wall, called the heat exchange wall, whose inner face participates in delimiting the channel and the outer face forms a support for receiving a component to be cooled, for example an electronic component. Finally, it is expected that a heat transfer fluid, liquid or gaseous, flows into the channel to receive and then remove the heat produced by the electronic component.

In order to increase the heat exchange surface with the heat transfer fluid, a porous medium with open pores forming a three-dimensional fluidic network may be arranged in the channel so as to be in contact with the exchange wall.

The document WO2004 / 079792 describes an example of such a fluidic fluid exchange device. A channel is delimited in part by a housing and comprises a porous medium with open pores able to be traversed by a coolant. A main heat exchange wall of the housing has an outer face against which is disposed a component to be cooled, and an inner face in contact with this porous medium. In this example, the porous medium is a regular network of balls assembled to each other, fixed to the internal faces of the channel via a solder material.

However, it would be desirable to have a fluidic device having an improved heat transfer coefficient, this coefficient being relative to the heat transfer between the main heat exchange wall for receiving a component to be cooled and the coolant circulating in the channel . This heat transfer coefficient is also called the global exchange coefficient.

It would also be desirable to have, more generally, a fluidic device having, in operation, an improved mechanical strength, thus preserving the flow properties of the fluid in the channel and, where appropriate, the thermal transfer properties between the main heat exchange wall and the coolant.

There is also a need to have a simplified method for producing a fluidic device having one and / or the other of these improvements.

DISCLOSURE OF THE INVENTION The object of the invention is to remedy at least in part the drawbacks of the prior art, and more particularly to propose a fluidic device comprising a channel in which is located a porous material with open pores, exhibiting improved mechanics and, where appropriate, an improved overall exchange rate.

For this, the object of the invention is a fluidic device, comprising: a housing comprising a channel delimited by walls, of which a first main wall, the channel extending between two orifices, said inlet and outlet ports; ; - A porous medium with open pores of a metal material, said metal foam, located in the channel between said inlet and outlet ports.

According to the invention, the metal foam and said first main wall are made in one piece and in the same material, and the metal foam has a random spatial distribution of the pores.

Some preferred but non-limiting aspects of this fluidic device are the following:

Preferably, the metal foam has a specific surface area of between 200 m 2 / m 3 and 1500 m 2 / m 3, a porosity of between 65% and 85%, and an average pore size of between 2 mm and 8 mm.

The cross section of the inlet and outlet ports may have a smaller area than the cross section of the channel.

The housing may comprise a second main wall opposite the first main wall, partially delimiting the channel, the metal foam and said second main wall being further made in one piece and the same material.

The housing may include a second main wall opposite the first main wall partially defining the channel, said second main wall being an insert wall sealingly attached to a side wall of the housing.

The housing may have a side wall extending between the first main wall and a second main wall opposite the first wall, and delimiting the channel circumferentially, the metal foam and said side wall being further integrally formed. and in the same material.

The inlet and outlet ports may open into hollow chambers of the channel located on either side of the metal foam along a longitudinal axis of the channel.

According to one embodiment, the fluidic device may comprise: a first metal foam made in one piece with said first main wall and in the same material, and a second metal foam made in one piece with a second wall the first and second metal foams being assembled to each other via a fluidic collector comprising at least one collection duct extending between two inlet ends opening at said first and second metal foams and an outlet end opening at the outlet.

The first and second main walls, the first and second metal foams - and the manifold may have a substantially circular profile, the main walls and the manifold being sealingly joined to a circumferential side wall of the housing. The inlet orifice may have a diameter adapted to allow the introduction of a fluid on either side of the manifold so as to be able to flow into the first and second metal foams before reaching the inlet ends collection conduit. The invention also relates to a method for producing a fluidic device according to any one of the preceding characteristics, in which the metal foam and the first main wall are produced by molding, during the same casting step of a metal material in a mold, during which there is an infiltration, by said metallic material, of a porous destructible preform located in a cavity of the mold, said casting step being carried out by the application of a pressing force to the surface of said metal material so as to cause it to rise into the mold and infiltrate into the preform, said preform being made of salt paste or silicone-based.

The preform may be arranged in an impression of a mold and kept at a distance from an inner face of a mold clevis, the space separating said inner face and the preform being intended to form the first main wall.

The preform may be interposed longitudinally between two cores, said cores being intended to form hollow chambers of the channel.

Each core may comprise a second portion intended to form an inlet or outlet orifice, said second portion extending from a first portion intended to form one of said hollow chambers of the channel.

BRIEF DESCRIPTION OF THE DRAWINGS Other aspects, objects, advantages and characteristics of the invention will appear better on reading the following detailed description of preferred embodiments thereof, given by way of non-limiting example, and made in reference to the accompanying drawings, in which: FIG. 1a is a diagrammatic view in longitudinal section and in perspective of a fluidic device according to a first embodiment, in which the metal foam is made in one piece and in a same material with the walls of the housing which transversely delimit the channel; Figure 1b is a schematic bottom view of the fluidic device shown in Figure 1a; and Figure 1 illustrates different surface area values of the metal foam for different porosity and average pore size values; Figures 2a to 2e show steps of a method of producing the fluidic device according to the first embodiment; FIG. 3 is a schematic perspective view of a fluidic device according to a second embodiment, in which one of the main walls delimiting the channel forms an attached cover; FIGS. 4a to 4f represent steps of a method for producing the fluidic device according to the second embodiment; FIG. 5 is a schematic perspective view of a fluidic device according to a third embodiment, in which two metal foams, each made in one piece and in one and the same material with main walls, are assembled together; to the other by a fluidic collector.

DETAILED PRESENTATION OF PARTICULAR EMBODIMENTS

In the figures and in the remainder of the description, the same references represent identical or similar elements. In addition, the various elements are not represented on the scale so as to favor the clarity of the figures.

In the remainder of the description, the terms "substantially", "approximately", "about", "of the order of" are "within 10%". In addition, the terms "between ... and ..." and "from ... to ..." mean that the terminals are included unless otherwise stated. The limits are also "within 10%". The invention relates to a fluidic device comprising a channel in which a fluid is intended to flow, the channel being delimited by the walls of a housing. Inside the channel is a porous medium with open pores able to be traversed by the fluid. The porous medium is subsequently called metallicfoam (metallicfoam). According to the invention, the metal foam and at least a first main wall of the housing partially delimiting the channel are made of the same metallic material and in one piece.

The fluidic device can find various applications, for example in the field of heat exchangers or in that of filtration. In the following description, and purely illustrative, the fluidic device forms a heat exchanger adapted to dissipate the heat produced by a component, for example an electronic power component, the latter being disposed against a wall of the fluidic device . Other types of components can be cooled by such a heat exchanger, for example automotive or nuclear components. The heat transfer fluid intended to flow in the channel 3 of the fluidic device may be liquid or gaseous.

The fluidic device comprises, located inside the channel, a metal foam in the form of a porous solid medium with open pores. This porous medium thus forms a three-dimensional network of interconnected pores. The metal foam is made of a solid metal material such as, for example, aluminum or an aluminum alloy, for example an alloy of the type AISi7MgO, 6, but any other type of molding alloy having good flowability can be used. Other materials can also be used such as, for example, alloys of zinc, copper, cast iron, steel, etc.

According to the invention, the metal foam has a pore network spatially distributed in a random manner. Random spatial distribution means that the mutual arrangement of the pores is substantially aperiodic and has substantially no preferred direction. Such a pore network thus differs from regular networks of beads such as that described in the example of the prior art mentioned above.

In addition, according to the invention, the metal foam and at least a first main wall of the housing defining at least part of the channel are made of the same metallic material and in one piece. By "made in one piece and in the same material" is meant that the metal foam and the first main wall are made monolithically, that is to say in one piece, the mechanical connection being provided by the metallurgical continuity of the metallic material forming these two pieces, cast together in one and the same operation. It is thus understood that, being made in one piece and in the same metallic material, the metal foam is assembled to the first main wall without the presence of an intermediate fixing layer, such as a layer of a material brazing or welding, located at the interface between the metal foam and the first main wall.

The metal foam may have a porosity greater than or equal to 10%, for example between 60% and 90%, and preferably between 65% and 85%. Porosity is understood as the ratio of the cumulative volume of pores to the total volume of the metal foam.

In addition, the pores may have a mean millimeter size. The average size of the pores can be, for example, between 1 mm and 10 mm, or even between 2 mm and 8 mm. The average size is understood as the average, for example arithmetic, of the average maximum dimension and the average minimum pore size. The average maximum dimension is the average of the maximum pore size and the average minimum dimension is the average of the minimum pore size.

In addition, the metal foam may have a specific surface area of between 200 m 2 / m 3 and 1500 m 2 / m 3. Specific surface area means the actual surface area of the pore area, that is, the developed area of the foam, over the total volume of the metal foam. It can be estimated conventionally by X-ray tomography.

As described below, the metal foam may be made of aluminum, by a molding process comprising a casting step during which an infiltration of a destructible preform takes place. This preform can be made of a material based on salt dough, as described for example in EP2118328, or even a silicone-based material as described for example in FR2992660.

In this heat exchanger application, the first main wall 10 is preferably a heat exchange wall whose outer face has a surface adapted to receive a component to be cooled. By external face, we mean a face of the wall opposite to the inner face facing the channel 3.

Figure la is a schematic longitudinal sectional view and perspective of a fluidic device 1 according to a first embodiment and Figure lb is a schematic bottom view in longitudinal section of the fluidic device 1 shown in Figure la.

In this example, as it is explained later, the fluidic device 1 comprises a channel 3 which extends along a substantially rectilinear longitudinal axis. Furthermore, the metal foam 30 is made in one piece and in the same material with the main walls 10, 20 delimiting transversely the channel 3.

Here we define a three-dimensional orthonormal coordinate system (Χ, Υ, Ζ), where the plane (X, Y) is substantially parallel to the plane of the main walls 10, 20 of the fluidic device 1, the Z axis being oriented in a substantially orthogonal direction on the plane (X, Y). Thus, the terms "vertical" and "vertically" extend as being relative to an orientation along the Z axis, and the terms "lower" and "higher" extend as being relative to Z-axis positioning. .

The length of the channel 3 is defined as the distance, here along the X axis, between two inlet ports 4A and 4B outlet; the width of the channel 3 as the distance, along the Y axis, between two internal faces opposite to each other of a side wall 40 of the channel 3; and the height of the channel 3 as the distance, along the Z axis, between the two inner faces 11, 21 of the main walls 10, 20.

The fluidic device 1 comprises a housing 2 formed of walls whose internal faces delimit a channel 3. The housing 2 is here formed of two main walls 10, 20 opposite one another along the axis Z, and of a side wall 40 circumferentially connecting the main walls 10, 20 to one another, that is to say along the perimeter of the channel 3. The internal faces of the different walls, that is to say the faces facing the channel 3, together define the channel 3.

In this example, the first and second main walls 10, 20 are substantially parallel and parallel to each other. They each have an inner face 11, 21 and an outer face 12, 22, opposite to one another, substantially flat. They are connected to each other in a sealed manner by the side wall 40. In this example, the first main wall 10 forms a heat exchange wall with a component to be cooled, and has a surface of its outer face. 12 substantially flat in order to receive the component to be cooled.

The housing 2 here has a profile in the plane (X, Y) of rectangular shape, but other shapes are possible, for example circular or oval, or square or polygonal. The channel 3 here has a general shape of flattened parallelepiped. In other words, the channel has a height less than its width and its length, thus making it possible to optimize the exchange surface between the coolant and the first main heat exchange wall.

The housing 2 has through holes which open into the channel 3, and form inlet ports 4A and 4B outlet. They are arranged along the longitudinal axis of the channel 3 so as to allow the introduction and evacuation of the coolant in the channel 3. In this example, the inlet ports 4A and 4B exit are formed through the same second main wall 20, and are intended to receive fluidic conduit ends (not shown) for supply and discharge of the coolant. Alternatively, the orifices 4A, 4B may be disposed at the level of the first main wall 10, or even at the side wall 40. Moreover, the cross section of the orifices 4A, 4B has a surface area smaller than that of a section right of the channel 3. By cross section, means a section along a plane orthogonal to the longitudinal axis of the element.

The fluidic device 1 further comprises a metal foam 30, located in the channel 3 between the inlet ports 4A and 4B outlet. It is in the form of a porous block with open pores spatially distributed in a random manner, which here fills a part of the channel 3. More precisely, the metal foam 30 fills the surface of a cross section of the channel 3, in the plane (Y, Z), and extends longitudinally along the axis X on a portion of the channel 3. Thus, it is in contact with a portion of the internal faces of the main walls 10, 20 and lateral 40, so that the heat transfer fluid, flowing in the channel 3 between the inlet 4A and outlet 4B ports, necessarily passes through the metal foam 30.

The metal foam 30 is made of the same material and in one piece with the first main wall 10, and, in this example, with the second main wall 20 and the side wall 40. Thus, the metal foam 30 and the walls main 10, 20 and lateral 40 of the housing 2 form a single piece, monolithic, made of the same material. It is therefore understood that the metal foam 30 is not fixed to said walls by an intermediate fixing layer such as a layer of a solder or solder material but that the mechanical connection is provided by a metallurgical continuity formed by the material metal foam and said walls, cast together in one and the same operation.

In this example, the metal foam 30 is located between two hollow chambers, called inlet 5A and outlet 5B, and therefore does not extend over the entire length of the channel 3. The inlet chamber 5A, in which opens the inlet orifice 4A is delimited by the walls of the housing 2 and an upstream free face 31A of the metal foam 30. The outlet chamber 5B, into which the outlet orifice 4B opens, is delimited by the walls of the housing 2 and a so-called free face 31B of the metal foam 30.

Thus, in that the first main wall 10 and the metal foam 30 are made in one piece and in the same material on the one hand, and the metal foam 30 forms a network of open pores spatially distributed randomly on the other hand, the thermal transfer properties of the fluidic device 1 are improved, and in particular the overall exchange coefficient. In addition, the mechanical strength of the fluidic device 1 is also improved, which makes it possible to preserve the fluidic and thermal properties of the device 1 during operation.

Indeed, the fixing of the metal foam 30 to the first main wall 10 is ensured by the metallurgical continuity between these two parts and is therefore not performed by means of a spacer layer of a solder or solder material, such a material being capable of having a thermal conductivity lower than that of the metallic material of the first main wall 10 and of the metal foam 30. The thermal transfer properties of the fluidic device 1, and in particular the overall exchange coefficient, are thus improved. hg of the device. By global exchange coefficient hg, or overall heat transfer coefficient, is meant the coefficient quantifying the flow of energy through the first main wall 10 and the metal foam 30, from the component to be cooled to the heat transfer fluid. This coefficient depends in particular on the exchange coefficient hp of the first main wall 10 and the hm coefficient of the metal foam 30, and in general on any possible intermediate layer located between the first main wall 10 and the metal foam 30. The exchange coefficient is conventionally defined as the ratio AQ / S.AT where AQ is the transferred thermal energy, S the exchange surface, and ΔΤ the temperature difference on either side of the surface of exchange. The absence here of such an intermediate layer of solder or solder therefore makes it possible not to degrade the value of the overall exchange coefficient of the fluidic device 1, which results in an optimization of the thermal transfer properties of the fluidic device. 1.

The thermal transfer properties of the fluidic device 1 are further improved by the fact that the open pores of the metal foam are spatially distributed randomly. The heat transfer fluid then flows into the metal foam 30 without having a preferred flow direction, which tends to improve the heat transfer between the fluidic device 1 and the heat transfer fluid.

Furthermore, the mechanical strength of the fluidic device 1 is improved insofar as the absence of an intermediate layer of solder or solder between the metal foam 30 and the first main wall 10, and here between the foam and the other walls of the housing , leads to a better mechanical strength vis-à-vis a possible concentration of mechanical stresses at the interface between the metal foam 30 and the walls of the housing. Indeed, the operating conditions of the fluidic device 1 in operation, in particular in pressure and / or temperature, can generate mechanical stresses coming to focus at the interface between the metal foam 30 and the wall or walls in contact therewith. When an intermediate layer of solder or solder is present, the concentration of the stresses can cause a detachment of the wall from the metal foam 30. This detachment can then cause a degradation of the fluid flow properties in the metal foam 30, and, where appropriate, a degradation of the thermal transfer properties.

In addition, such a fluidic device 1, whose first main wall 10 and the metal foam 30 are made in one piece and in the same material, can be obtained by a simplified embodiment, an example of which is described now.

Furthermore, the metal foam 30 advantageously has a porosity ranging from about 65% to 85% and an average pore size of between about 2mm and 8mm. The inventors have indeed found that such a metal foam 30 with open pores and spatially distributed randomly then has a particularly important specific surface area, ranging from 200 m 2 / m 3 to 1500 m 2 / m 3, which greatly increases the heat transfer properties. of the fluidic device 1.

FIG. 1a illustrates the specific surface area values of the metal foam as a function of porosity and average pore size, these specific surface area values being obtained from X-ray tomography measurements. porosity ε between about 65% and 85%, the specific surface area Sp increases sharply, ranging from about 200 m 2 / m 3 for an average pore size of about 8 mm to about 1500 m 2 / m 3 for an average pore size of about 2 mm. As an illustration, the specific surface area of the metal foam 30 is of the order of 630 m 2 / m 3 for a porosity of about 73.9% and an average pore size of about 5 mm. The specific surface area can increase to 1490 m2 / m3 for a porosity of about 72.4% and an average pore size of about 2 mm. The presence in the channel 3 of a metal foam 30 having these high specific surface area values makes it possible to substantially increase the heat transfer properties of the fluidic device 1.

FIGS. 2a to 2e illustrate various steps of an exemplary method of producing the fluidic device 1 according to the first embodiment as illustrated in FIG. The fluidic device is here produced by a "low pressure" type molding technique comprising a step of infiltrating a preform simultaneously with the casting of the liquid metal.

"Low pressure" type molding is a technique in which a pressure force, here an overpressure, is applied to the surface of a liquid metal located in an oven feeding the mold, so as to cause the rise of the liquid metal in the mold and its infiltration into the preform. Alternatively, a vacuum can be applied in the mold so that the liquid metal undergoes a so-called suction vacuum force causing the filling of the mold and its infiltration into the preform. The pressure values used are adapted so that the liquid metal infiltrates the interstices of the preform so as ultimately to obtain the desired metal foam.

These molding techniques, applied to a preform in salt paste or a silicone-based material, are suitable for producing open-space spatially distributed metal foam in a random manner and capable of reaching high specific surface area values. The inventors have found that other molding techniques, for example gravity molding, do not make it possible to produce metal foams having these characteristics.

During a first step (FIG. 2a), a part 50 formed of a preform 51 is assembled with two cores 53A, 53B disposed on either side of the preform 51. The two cores 53A, 53B are in contact with each other. two transverse faces 52A, 52B opposite to each other of the preform 51, called upstream and downstream faces.

Each core 53A, 53B here comprises a first portion 54A, 54B intended to form the inlet chamber 5A or 5B outlet, which extends along the longitudinal axis of the preform 51. It has here a thickness along the axis Z substantially equal to that of the preform 51, and a profile in the plane (X, Y) substantially triangular rounded apex. Each core 53A, 53B further includes a second portion 55A, 55B, for forming the inlet 4A or outlet 4B, which extends from the first portion 54A, 54B substantially orthogonal to the main plane (X, Y) of the preform 51. Finally, each core 53A, 53B has a third portion 56A, 56B, intended to maintain the piece 50 in a so-called suspended position vis-à-vis the internal faces of a mold 60, which extends in the extension of the second portion 55A, 55B. The cores 53A, 53B are destructible and can be made of sand typically agglomerated with resin.

The preform 51 is intended to form the metal foam 30. It may be made from salt dough according to the process described in EP2118328 or from a silicone-based material according to the method described in the document FR2992660. As an illustration, the preform 51 is made of silicone elastomer according to the process described in the document FR2992660. First of all, separate elements of silicone elastomer of millimeter size are produced, for example by extrusion and then cutting. These elements are then agglomerated using a binder and the resulting assembly is polymerized in a core box whose imprint defines the desired final dimensions of the preform 51. After removal and then removal of any solvents, we obtain a Porous preform 51 with interconnected interstices made of silicone elastomer.

In a second step (FIG. 2b), the piece 50 is placed in a mold 60, for example a sand mold, and more precisely in the cavity 65 of the mold, the dimensions of which define the desired dimensions of the casing 2. The mold 60 is formed of two parts 61, 63, called screeds, which, when in contact, together delineate the cavity 65, namely the inner cavity of the mold 60 in which is placed the part 50. The mold 60 further comprises a supply duct 66 for the introduction of the liquid metal into the cavity 65.

In this example, the upper yoke 63 has an inner face 64 which partially surrounds the part 50 without contacting it. The space separating the upper clevis 63 from the part 50 is intended to form the first main wall 10 and a part of the side wall 40. Furthermore, the lower clevis 61 has an inner face 62 which partially surrounds the piece 50, the space separating the yoke 61 from the part 50 is intended to form the second main wall 20 and a part of the side wall 40. This space is traversed by the second parts 55A, 55B of the cores intended to form the orifices 4A input and 4B output.

Moreover, the part 50, and more particularly the preform 51 and the first parts 54A, 54B of the cores, are kept at a distance from the internal faces of the mold 60 by the engagement of the third parts 56A, 56B of the cores in housings provided in the inner face 62 of the lower yoke 61.

Preferably, prior to its insertion into the cavity 65, the part 50 is preheated to a temperature which may be of the order of 80 ° C. to 250 ° C., for example approximately 150 ° C.

In a third step, the liquid metal is cast in the cavity 65 of the mold 60 according to the so-called "low pressure" process. The most commonly used alloy is of the type AISi7Mg0.6, but any other type of casting alloy having good flowability can be used. The temperature may be of the order of 800 ° C to 820 ° C. The liquid metal thus fills the supply duct 66 and fills the cavity 65 of the mold 60 placed under an overpressure, typically from 700 mbar to 1.5 bar. The metal also infiltrates the interstices of the preform 51 of silicone elastomer, and also surrounds the preform 51 and the cores 53A, 53B.

In a fourth step (FIGS. 2c and 2d), after solidification and cooling, the mold 60 is unhooked and the molded part 57 is removed. After deburring and machining of the molded part 57, and removal of the remaining powder of silica, the fluidic device I shown in FIG. 2e is obtained. For purely illustrative purposes, the metal foam 30 has a length of 105 mm, a width of 50 mm for a thickness of 10 mm to 35 mm. It has a porosity of the order of 70% to 75% open pores and spatially distributed randomly. The first main wall 10 has a thickness of about 2 mm and the second main wall 20 a thickness of about 5 mm. The inlet ports 4A and 4B exit may have a diameter of about 5 to 15mm. The specific surface of the metal foam can be adjusted according to the average pore size and the porosity, these parameters being adapted during the manufacture of the preform, in particular via the dimensions of the agglomerated elements of silicone elastomer.

Alternatively, as previously mentioned, the embodiment of the fluidic device 1 can be carried out by a "low pressure" type molding technique comprising the infiltration of a preform based on salt dough previously obtained according to the process described in document EP2118328.

The method comprises steps that are identical or similar to those described with reference to FIGS. 2a to 2e. It differs in that, in a first step, the preform 51 is made by mixing ground salt particles, a thermo-degradable organic binder, and a wetting agent. A preform 51 made of porous salt paste with interconnected interstices is thus obtained. A step of removing the wetting agent, decomposing the binder and curing the preform 51 can be carried out, in particular by a step of baking the preform 51 at a temperature of the order of 100 ° C, followed by a pyrolysis step at a temperature of the order of 500 ° C.

In a second step, the part 50 formed of the preform 51 and the cores 53A, 53B are placed in the cavity 65 of the mold 60, this part 50 preferably being preheated to a temperature of, for example, 600.degree. ° C.

In a third step, the liquid metal is cast at a temperature of the order of 750 ° C. with an overpressure typically of 700 mbar at 1.5 bar. The most commonly used alloy is AlSi7Mg0.6, but any other type of casting alloy with good flowability can be used.

During this pouring step, concomitantly with the formation of the walls 10, 20, 40 of the housing, the liquid metal infiltrates the interconnected interstices of the preform 51 so as to form the metal foam 30.

In a fourth step, after solidification and cooling, the molded part 57 is removed from the mold cavity 60 and the salt of the preform 51 is removed by a solvent. After deburring and machining of the molded part, the fluidic device 1 illustrated in FIG. 2e is obtained. The metal foam forms a network of open pores spatially distributed in a random manner. As mentioned above, the specific surface area of the metal foam can be adjusted according to the average pore size and the porosity, these parameters being adapted during the manufacture of the preform, in particular via the dimensions of the agglomerated particles of salt dough.

Thus, the method of producing the fluidic device 1 is simplified insofar as the realization of the metal foam 30 and the first main wall 10 in one piece and in the same material is performed in a single step of casting of the liquid metal, this step allowing the molding of the housing 2 and the infiltration of the preform 51. This avoids any machining step of the housing to form the channel 3, as well as any step of fixing the metal foam 30 to the first main wall 10 via a fixing layer, for example a solder layer.

This example of a method is particularly advantageous here in that the metal foam 30 is also made in one piece and in the same material with the second main wall 20 and with the side wall 40, and that the metal foam obtained forms a network of open pores with random spatial distribution. The mechanical strength of the fluidic device 1 and the overall exchange coefficient are improved.

Figure 3 is a schematic perspective view of a fluidic device 1 to metal foam 30 according to a second embodiment.

The fluidic device 1 differs from the fluidic device 1 described above with reference to FIGS. 1a and 1b in that the metal foam 30 is made in one piece and in one and the same material with the first main wall 10 and the side wall 40, the second main wall 20 being an attached wall forming a cover for the channel 3.

Thus, the housing 2 comprises a channel 3 delimited transversely by the first main wall 10 and the side wall 40. The walls are here made in one piece and in the same material. The metal foam 30 is located in the channel 3 between the two inlet chambers 5A and 5B outlet.

The housing 2 comprises a second main wall 20 which is in the form of an added wall whose attachment to the side wall 40 of the housing 2 allows the channel 3 to be closed in a sealed manner. It has two through-holes, called inlet 4A and outlet 4B, which open respectively into the inlet chamber 5A and the outlet chamber 5B. Alternatively, the inlet and outlet openings 4A and 4B can be made, not at the level of the attached cover, but at the level of the side wall 40 or even at the level of the first main wall 10.

The attached cover 20 can be fixed to the side wall 40 of the housing 2 at its upper contact face 43, and preferably to the metal foam 30. The attachment can be made sealingly by an intermediate layer of a solder material (not shown). Thus, the fixing and sealing is obtained between the attached cover 20 on the one hand, and the side wall 40 of the housing 2 and, where appropriate, the metal foam 30 on the other hand.

The channel 3 and the metal foam 30 here have a general shape and dimensions identical or similar to those described above with reference to Figures 1a and 1b, and are not described again here.

FIGS. 4a to 4f illustrate steps of an exemplary method for producing the fluidic device 1 according to the second embodiment.

In a first step, a porous preform 51 having interconnected interstices made of a salt-paste or silicone-elastomer material is produced, in the same or a similar manner to the processes described above. Moreover, it is not intended here to assemble cores to the preform 51 as in the part 50 described with reference to Figure 2a.

In a second step, as shown in Figure 4a, is prepared a mold 60 with two yokes 61, 63 whose lower yoke 61 is similar or identical to the lower yoke of Figures 2b and 2c. Furthermore, the upper yoke 63 comprises cores 53A, 53B in the form of protruding portions vis-à-vis an inner face 64, these cores being intended to form the inlet chambers 5A and 5B output. These cores are mounted movable in translation vis-à-vis the upper yoke 63 so as to form jaws of a vise to maintain the preform 51 in a so-called suspended position during molding.

More specifically, the jaws are spaced from one another by a distance substantially equal to the length of the preform 51, and are disposed on either side of a surface 64c of the inner face 64 of the yoke upper 63, the latter being intended to be in contact with the preform 51.

As shown in FIG. 4b, the preform 51 is placed in contact with the contact surface 64c, so that the upstream and downstream faces of the preform 51 are in respective contact with the jaws. These exert a holding force on the preform 51 to maintain it in position, without causing compression of the preform 51 may change its porosity.

In a third step (FIG. 4c), the mold 60 is closed by bringing the upper and lower tops 61 into contact with one another. The preform 51 is held in a suspended position with respect to the inner face 62 of the lower clevis 61, this space being intended to form in particular the first main wall 10. A lateral space between the jaws and the inner face 62 of the lower clevis 61 is intended for the formation of the side wall 40 of the housing 2.

The liquid metal is then poured through the supply duct 66, so that the metal fills the mold cavity 60 and therefore the space separating the internal face 62 of the preform 51 from the one hand , and bits on the other hand. At the same time, the metal infiltrates the interstices of the preform 51. This step is similar or identical to that described above with reference to FIG. 2b.

Insofar as the preform 51 is in contact with the contact surface 64c of the upper yoke 63, the second main wall 20 of the housing 2 is not made during this step.

In a fourth step (FIGS. 4d and 4e), after solidification and cooling, the mold 60 is unhooked and the molded part 57 is removed. The housing 2 thus comprises the metal foam 30 made in one piece and in the same material with the first main wall 10 and with the side wall 40 defining the channel 3.

The remaining silica or salt paste is then removed. This step is simplified insofar as the channel 3 does not have a closed cross section and delimited by the different walls of the housing 2. It has indeed access to the channel 3 and the metal foam 30 by an opening formed by the absence of the second main wall 20.

In a last step (FIG. 4f), after deburring and machining of the molded part 57, a layer of a solder material is deposited in the area of contact between the attached cover 20 and the side wall 40, as well as in the zone of contact between the attached cover 20 and the free face of the metal foam 30. The channel 3 is closed with the aid of the attached cover and the fluidic device 1 thus obtained is placed in a brazing furnace.

Figure 5 is an exploded perspective view of a fluidic device 1 according to the third embodiment. In this example, the fluidic device 1 is formed of a housing 2 of substantially circular transverse profile. It comprises a side wall 40 defining the channel 3 in the plane (X, Y) and two opposite main walls 10,20 delimiting the channel 3 along the Z axis.

In this example, the two main walls 10, 20 are attached to the side wall 40 in a sealed manner by a solder layer (not shown). Alternatively, at least one of the main walls 10, 20 may be made in one piece and in one and the same material with the side wall 40.

Each main wall 10, 20 is made in one piece and in the same material with a metal foam 30-1, 30-2. The metal foams 30-1, 30-2 may have a diameter equal to or smaller than that of the main walls 10, 20.

The two main walls 10, 20 provided with the respective metal foams 30-1, 30-2 are assembled to one another along the Z axis via a fluidic collector 6 interposed between the two metal foams 30 -1, 30-2. The collector 6 has a solid volume of cylindrical shape, of a diameter substantially equal to that of the main walls 10, 20, and is sealingly assembled to the side wall 40. The collector 6 comprises a collection duct which extends between two input ends 7A and an output end 7B. The inlet ends 7A open out one and the other on the opposite upper and lower faces of the collector 6, and therefore face the metal foams 30-1,30-2, and are preferably positioned at the center of the collector 6. The outlet end 7B opens on the circumferential face of the collector 6.

Thus, the channel 3 is formed of a lower portion delimited between the first main wall 10 and the lower face of the collector 6 and containing the metal foam 30-1, and an upper portion delimited between the second main wall 20 and the upper face. of the collector 6 and containing the metal foam 30-2. The channel 3 continues with the collection duct which connects the two parts of the channel 3 to the outlet end 7B.

The housing 2 further comprises an inlet port 4A and an outlet port 4B of the channel 3 positioned at the side wall 40 of the housing 2, intended to allow the supply of fluid in the two lower and upper parts of the channel 3, and the evacuation of the fluid from the outlet end 7B of the collection duct. The inlet orifice 4A has a transverse dimension adapted to allow the introduction of the fluid into both parts of the channel 3, so that the fluid flows through the two metal foams 30-1, 30 -2 and receives the heat from one or the other, or both main walls 10, 20. The fluid then flows into the collection duct from the inlet ends 7A to the end output 7B. The outlet orifice 4B is positioned facing the outlet end 7B of the collection duct, so that the fluid can be directly evacuated without circulating again in the lower and upper portions of the channel 3.

The process for producing this fluidic device 1 can be carried out in a manner similar to the production methods described above. Thus, each main wall 10, 20 can be made in one piece and in a same material with the corresponding metal foam 30-1, 30-2, by a low-pressure molding process with an infiltration step of a preform 51 in salt paste or silicone-based, this infiltration step being concomitant with the casting casting. The walls 10, 20, 40 and the collector 6 can be assembled by soldering.

Specific embodiments have just been described. Various variations and modifications will occur to those skilled in the art.

Thus, the fluidic device may not include inlet chambers located on either side of the metal foam. The inlet and outlet ports pass through a wall of the housing and then open directly at the level of the metal foam.

The fluidic device may comprise structures located at the outer faces of the housing walls, these structures may improve the heat dissipation emitted by the component to be cooled. These structures may, for illustrative purposes, be in the form of cooling fins.

Claims (14)

1. fluidic device (1), comprising: - a housing (2) comprising a channel (3) delimited by walls, including a first main wall (10), the channel (3) extending between two orifices, said d input (4A) and output (4B); - A porous medium with open pores of a metal material, said metal foam (30), located in the channel (3) between said inlet (4A) and outlet (4B); characterized in that the metal foam (30) and said first main wall (10) are made in one piece and in the same material, and in that the metal foam (30) has a random spatial distribution of the pores. 2. Fluidic device (1) according to claim 1, wherein the metal foam (30) has a specific surface area of between 200 m 2 / m 3 and 1500 m 2 / m 3, a porosity of between 65% and 85%, and an average pore size. between 2mm and 8mm. 3. fluidic device (1) according to claim 1 or 2, wherein the cross section of the inlet ports (4A) and outlet (4B) has a lower surface than the cross section of the channel (3). 4. Fluidic device (1) according to any one of claims 1 to 3, wherein the housing (2) comprises a second main wall (20) opposite the first main wall (10), partially delimiting the channel (3). ), the metal foam (30) and said second main wall (20) being further made in one piece and in the same material. 5. Fluidic device (1) according to any one of claims 1 to 3, wherein the housing (2) comprises a second main wall (20) opposite the first main wall (10) partially delimiting the channel (3). said second main wall (20) being an insert wall sealingly attached to a side wall (40) of the housing (2). The fluidic device (1) according to any one of claims 1 to 5, wherein the housing (2) has a side wall (40) extending between the first main wall (10) and a second main wall (20). ) opposite to the first wall (10), and delimiting the channel (3) circumferentially, the metal foam (30) and said side wall (40) being further made in one piece and the same material. 7. fluidic device (1) according to any one of claims 1 to 6, wherein the inlet ports (4A) and outlet (4B) open into hollow chambers (5A, 5B) of the channel (3) located on both sides of the metal foam (30) along a longitudinal axis of the channel (3). 8. fluidic device (1) according to any one of claims 1 to 3, comprising: - a first metal foam (30-1) made in one piece with said first main wall (10) and a same material, and - a second metal foam (30-2) made in one piece with a second main wall (20) opposite the first wall (10), and in the same material, - said first and second metal foams (30- 1, 30-2) being assembled to one another via a fluidic collector (6) having at least one collection duct extending between two inlet ends (7A) opening at the level of said first and second metal foams (30-1,30-2) and an outlet end (7B) opening at the outlet (4B). 9. fluidic device (1) according to claim 8, wherein the first and second main walls (10, 20), the first and second metal foams (30-1, 30-2) and the collector have a substantially circular profile, the main walls (10, 20) and the collector being sealingly joined to a circumferential sidewall (40) of the housing (2). 10. fluidic device (1) according to claim 8 or 9, wherein the inlet port (4A) has a diameter adapted to allow the introduction of a fluid on either side of the collector (6). so as to be able to flow into the first and second metal foams (30-1, 30-2) before joining the inlet ends (7A) of the collection duct. 11. A method of producing a fluidic device (1) according to any one of claims 1 to 10, wherein the metal foam (30) and the first main wall (10) are produced by molding, at the same time. casting step of a metallic material in a mold (60), during which an infiltration by said metal material of a porous (51) destructible preform located in a cavity (65) of the mold, said step pouring being effected by applying a pressing force to the surface of said metallic material so as to cause it to rise into the mold (60) and infiltrate into the preform (51), said preform (51) being made into salt dough or silicone based dough. 12. The method of claim 11, wherein the preform (51) is disposed in a cavity (65) of a mold (60) and kept at a distance from an inner face (62, 64) of a mold clevis. (60), the space separating said inner face (62, 64) and the preform (51) being intended to form the first main wall (10). 13. The method of claim 11 or 12, wherein the preform (51) is interposed longitudinally between two cores (53A, 53B), said cores (53A, 53B) being intended to form hollow chambers (5A, 5B) of the channel. (3). The method of claim 13, wherein each core (53A, 53B) has a second portion (55A, 55B) for forming an inlet (4A) or outlet (4B) port, said second portion (55A, 55B) extending from a first portion (54A, 54B) for forming one of said hollow chambers (5A, 5B) of the channel (3).