FR2765514A1 - Hard rubber key pad forming process - Google Patents

Hard rubber key pad forming process Download PDF

Info

Publication number
FR2765514A1
FR2765514A1 FR9708525A FR9708525A FR2765514A1 FR 2765514 A1 FR2765514 A1 FR 2765514A1 FR 9708525 A FR9708525 A FR 9708525A FR 9708525 A FR9708525 A FR 9708525A FR 2765514 A1 FR2765514 A1 FR 2765514A1
Authority
FR
France
Prior art keywords
silicone rubber
keyboard key
printing
hard
forming
Prior art date
Legal status (The legal status is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the status listed.)
Pending
Application number
FR9708525A
Other languages
French (fr)
Inventor
Jason Tsai
Current Assignee (The listed assignees may be inaccurate. Google has not performed a legal analysis and makes no representation or warranty as to the accuracy of the list.)
Silitek Corp
Original Assignee
Silitek Corp
Priority date (The priority date is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the date listed.)
Filing date
Publication date
Priority to SE9702300A priority Critical patent/SE514041C2/en
Priority to GB9712823A priority patent/GB2326370A/en
Priority to DE19726886A priority patent/DE19726886C2/en
Application filed by Silitek Corp filed Critical Silitek Corp
Priority to FR9708525A priority patent/FR2765514A1/en
Publication of FR2765514A1 publication Critical patent/FR2765514A1/en
Pending legal-status Critical Current

Abstract

A monobloc process for forming a hard-rubber keypad comprises filling a mould with either (a) an epoxy resin, (b) a diallyl phthalate/acrylate copolymer or (c) polycaprolactone resin, hot cure hardening and adding silicone resin to the hardened mixture for heated combination at 100 to 180 deg C for 2-15 minutes. The keypad can then be printed by front printing or laser engraved after forming a metal layer of Ti, Cr or Au.

Description

TOUCHE DE CLAVIER DURE FORMEE D'UN SEUL BLOC
Description de l'invention
La présente invention concerne un type de touche de clavier en caoutchouc dur formée d'un seul bloc, qui est applicable à une touche de clavier en caoutchouc silicone, en d'autres termes, à généralement tous les types d'ordinateurs, de postes téléphoniques, de téléphones mobiles, de téléphones PHS, de dictionnaires audio, etc., équipés de touches de clavier en caoutchouc dur. Cette technologie peut être utilisée pour obtenir une touche de clavier dure.HARD KEYBOARD KEY FORMED FROM A SINGLE BLOCK
Description of the invention
The present invention relates to a type of hard rubber keyboard key formed in one piece, which is applicable to a silicone rubber keyboard key, in other words, to generally all types of computers, telephone sets , mobile phones, PHS phones, audio dictionaries, etc., equipped with hard rubber keyboard keys. This technology can be used to get a hard keyboard key.

Dans la technologie classique, une telle touche de clavier dure est obtenue par un procédé de formage, dans lequel le moule extrudera la touche de clavier dure, laquelle touche de clavier est ensuite combinée à un caoutchouc silicone, c'est-à-dire que la touche de clavier en matières plastiques normales peut être en polycarbonate, acrylate, résine ABS, résine AS, etc., ces matières étant extrudées selon la forme de touche de clavier souhaitée, puis après addition d'un caoutchouc, de préférence un caoutchouc silicone, avec une utilisation d'une liaison instantanée de type silane silicone, résine époxy ou acrylique améliorée à titre de couche d'accrochage, elles sont empâtées, et la touche de clavier formée est collée à titre de traitement, à l'aide d'une résine époxy ou autre résine similaire. In conventional technology, such a hard keyboard key is obtained by a forming process, in which the mold will extrude the hard keyboard key, which keyboard key is then combined with a silicone rubber, i.e. the keyboard key in normal plastic materials can be polycarbonate, acrylate, ABS resin, AS resin, etc., these materials being extruded according to the shape of the keyboard key desired, then after addition of a rubber, preferably a silicone rubber , with the use of an instantaneous bond of the silane silicone, epoxy resin or acrylic type improved as a bonding layer, they are pasted, and the keyboard key formed is glued as a treatment, using epoxy or other similar resin.

Techniquement, la touche de clavier en matière plastique empâté avec un caoutchouc silicone se détachera facilement alors que le coût des moules pour les extrudeuses est très élevé, et que les procédés de production sont très compliqués, de sorte que les coûts de production sont très élevés et que, de plus, la touche de clavier formée, collée par un procédé par points, ne peut être fabriquée que dans un style, et que les produits de touche de clavier obtenus ont une efficacité d'application non satisfaisante, ce qui explique la nécessité d'une amélioration. Le présent inventeur a consacré beaucoup de temps et d'efforts à la recherche et au développement de la présente invention. Technically, the keyboard key made of plastic mashed with silicone rubber will come off easily while the cost of molds for extruders is very high, and the production processes are very complicated, so the production costs are very high and that, in addition, the keyboard key formed, glued by a point process, can only be produced in one style, and that the keyboard key products obtained have an unsatisfactory application efficiency, which explains the need for improvement. The present inventor has devoted a great deal of time and effort to the research and development of the present invention.

L'objectif de la présente invention est de fournir une touche de clavier en caoutchouc dur applicable à une touche de clavier en caoutchouc silicone, en d'autres termes, tous les ordinateurs, postes téléphoniques, téléphones mobiles, téléphones PHS, dictionnaires audio, etc., équipés d'une touche de clavier en matière plastique à tête dure peuvent utiliser la technologie de la présente invention pour obtenir une touche de clavier dure ; ceci constitue une amélioration qui remédiera aux défauts des produits conventionnels et accroîtra l'efficacité du produit. The objective of the present invention is to provide a hard rubber keyboard key applicable to a silicone rubber keyboard key, in other words, all computers, telephone sets, mobile telephones, PHS telephones, audio dictionaries, etc. ., equipped with a hard key plastic keyboard key can use the technology of the present invention to obtain a hard keyboard key; this constitutes an improvement which will remedy the defects of conventional products and will increase the efficiency of the product.

La présente invention concerne une touche de clavier en caoutchouc dur formée d'un seul bloc, comprenant principalement 1. Une résine époxy, c'est-à-dire

Figure img00020001

dans laquelle n = 0 à 5
Figure img00030001
The present invention relates to a hard rubber keyboard key formed in one piece, mainly comprising 1. An epoxy resin, that is to say
Figure img00020001

where n = 0 to 5
Figure img00030001

ou 2. Un diallyle phtalate, c'est-à-dire

Figure img00030002

et un acrylate, c'est-à-dire un copolymère méthacrylate de propényle ou méthacrylate de 2-hydroxyéthyle, ou 3. Une résine polycaprolactone.or 2. A diallyl phthalate, that is to say
Figure img00030002

and an acrylate, ie a propenyl methacrylate or 2-hydroxyethyl methacrylate copolymer, or 3. A polycaprolactone resin.

Charger ladite résine époxy, ou ledit copolymère diallyle phtalate - acrylate, ou une résine polycaprolactone quelconque, respectivement, dans un moule à l'aide d'une machine de remplissage multipoint, à la température de 100 à 1800C pour un durcissement de 2 à 15 minutes, puis ajouter le caoutchouc silicone extrudé liquide ou le caoutchouc silicone solide obtenu au moyen d'une matrice de compression, pour un formage en un seul bloc par compression à chaud.Load said epoxy resin, or said diallyl phthalate - acrylate copolymer, or any polycaprolactone resin, respectively, into a mold using a multipoint filling machine, at the temperature of 100 to 1800C for a hardening of 2 to 15 minutes, then add the liquid extruded silicone rubber or the solid silicone rubber obtained by means of a compression matrix, for forming in a single block by hot compression.

L'adoption de ladite résine époxy, ou dudit copolymère diallyle phtalate - acrylate, ou d'une résine polycaprolactone fournira facilement l'effet de liaison avec le caoutchouc silicone liquide ou le caoutchouc silicone solide, sans qu'il soit nécessaire d'insérer une couche d'accrochage entre les deux. The adoption of said epoxy resin, or of said diallyl phthalate-acrylate copolymer, or of a polycaprolactone resin will readily provide the bonding effect with liquid silicone rubber or solid silicone rubber, without the need to insert a bonding layer between the two.

Ce procédé peut être suivi, si nécessaire par un procédé d'impression qui peut être par exemple un procédé d'impression par apport de matière ou un procédé d'impression par gravure en creux. This process can be followed, if necessary by a printing process which can be for example a printing process by adding material or a printing process by intaglio printing.

Pour démontrer les aspects techniques et les caractéristiques de la présente invention, des exemples de modes de réalisation sont décrits ci-après, mais ils ne devront pas être utilisés pour limiter la portée des revendications de la présente invention. To demonstrate the technical aspects and features of the present invention, exemplary embodiments are described below, but they should not be used to limit the scope of the claims of the present invention.

Brève description des dessins
La Fig. 1 est la vue d'une touche de clavier en caoutchouc dur de la présente invention.Brief description of the drawings
Fig. 1 is the view of a hard rubber keyboard key of the present invention.

La Fig. 2 est la vue d'une touche de clavier en caoutchouc dur de la présente invention avec impression frontale. Fig. 2 is the view of a hard rubber keyboard key of the present invention with front printing.

La Fig. 3 est la vue d'une touche de clavier en caoutchouc dur de la présente invention avec gravure au laser. Fig. 3 is the view of a hard rubber keyboard key of the present invention with laser engraving.

Description des chiffres de référence 1 caoutchouc silicone 2 tête dure 3 impression couleur 4 couche métallique 5 gravure de caractères ou de symboles < Exemple d'un mode de réalisation 1 >
D'abord, prendre une quantité appropriée de la résine époxy ci-dessus, suivant la hauteur du produit, ajuster la viscosité à 450 + 50 centipoises, charger une quantité spécifiée dans un moule, à 100 à 1500C, pour un formage par durcissement à chaud de 2 à 10 minutes.Description of reference numbers 1 silicone rubber 2 hard head 3 color printing 4 metallic layer 5 engraving of characters or symbols <Example of an embodiment 1>
First, take an appropriate amount of the above epoxy resin, depending on the height of the product, adjust the viscosity to 450 + 50 centipoise, load a specified amount into a mold, at 100 to 1500C, for hardening forming at hot for 2 to 10 minutes.

Puis, ajouter le caoutchouc silicone liquide ou le caoutchouc silicone solide à la résine durcie ci-dessus pour le formage par matrice de compression, à 100 à 1500C, pour un traitement de 2 à 10 minutes (voir
Fig. 1). Then add liquid silicone rubber or solid silicone rubber to the hardened resin above for compression matrix forming, at 100 to 1500C, for a treatment of 2 to 10 minutes (see
Fig. 1).

La touche de clavier dure obtenue par le procédé ci-dessus peut être traitée par un procédé d'impression couleur par sérigraphie, ou la touche de clavier dure peut être recouverte d'une couche de Ti, Cr, Au, etc., par vaporisation sous vide (métallisation sous vide), avant gravure au laser de caractères appropriés, tels que des lettres ou des symboles, etc. (voir Fig. 2 et 3). The hard keyboard key obtained by the above method can be treated by a color printing process by screen printing, or the hard keyboard key can be covered with a layer of Ti, Cr, Au, etc., by vaporization under vacuum (vacuum metallization), before laser engraving of suitable characters, such as letters or symbols, etc. (see Fig. 2 and 3).

< Exemple d'un mode de réalisation 2 >
De la même façon que dans l'exemple 1, utiliser le copolymère diallyle phtalate-acrylate ci-dessus, suivant la hauteur du produit, ajuster la viscosité à 450 t 50 centipoises, charger une quantité spécifiée dans un moule, à 120 à 1500C, pour un formage par durcissement à chaud de 2 à 10 minutes.<Example of an embodiment 2>
In the same way as in Example 1, use the diallyl phthalate-acrylate copolymer above, depending on the height of the product, adjust the viscosity to 450 t 50 centipoise, load a specified quantity into a mold, at 120 to 1500C, for hot curing 2 to 10 minutes.

Ajouter le caoutchouc silicone liquide ou le caoutchouc silicone solide à la résine durcie ci-dessus pour le formage par matrice de compression, à 100 à 1500C, pour un traitement de 2 à 10 minutes (voir
Fig. 1). Add liquid silicone rubber or solid silicone rubber to the hardened resin above for compression matrix forming, at 100 to 1500C, for a treatment of 2 to 10 minutes (see
Fig. 1).

La touche de clavier dure ainsi obtenue peut être soumise à un traitement d'impression selon l'exemple 1 (voir Fig. 2 et 3).  The hard keyboard key thus obtained can be subjected to a printing treatment according to Example 1 (see Fig. 2 and 3).

< Exemple d'un mode de réalisation 3 >
De la même façon que dans l'exemple 1, utiliser le polycaprolactone ci-dessus, suivant la hauteur du produit, ajuster la viscosité à 450 t 50 centipoises, charger une quantité spécifiée dans un moule, à 120 à 1500C, pour un formage par durcissement à chaud de 2 à 10 minutes.<Example of an embodiment 3>
In the same way as in Example 1, use the polycaprolactone above, depending on the height of the product, adjust the viscosity to 450 t 50 centipoise, load a specified quantity into a mold, at 120 to 1500C, for forming by hot curing 2 to 10 minutes.

Ajouter le caoutchouc silicone liquide ou le caoutchouc silicone solide à la résine durcie ci-dessus pour le formage par matrice de compression, à 100 à 1700C, pour un traitement de 2 à 10 minutes (voir
Fig. 1). Add liquid silicone rubber or solid silicone rubber to the hardened resin above for compression matrix forming, at 100 to 1700C, for a treatment of 2 to 10 minutes (see
Fig. 1).

La touche de clavier dure ainsi obtenue peut être soumise à un traitement d'impression selon l'exemple 1 (voir Fig. 2 et 3).  The hard keyboard key thus obtained can be subjected to a printing treatment according to Example 1 (see Fig. 2 and 3).

Claims (5)

REVENDICATIONS 1. Type de procédé de formage d'un seul bloc pour touche de clavier en caoutchouc dur, comprenant les étapes suivantes 1. Type of self-contained forming process for a hard rubber keyboard key, comprising the following steps (1) Charger une résine époxy, un (1) Load an epoxy resin, a copolymère de diallyle phtalate-acrylate ou diallyl phthalate-acrylate copolymer or une résine polycaprolactone choisi dans un a polycaprolactone resin selected from a moule pour un formage par durcissement à mold for forming by hardening at chaud hot (2) Ajouter du caoutchouc silicone liquide (2) Add liquid silicone rubber ou du caoutchouc silicone solide au moule de or solid silicone rubber to the mold résine durcie ci-dessus pour une combinaison à cured resin above for combination with chaud. hot. 2. Procédé selon la revendication 1, dans lequel la combinaison dans l'étape (2) peut être soit un caoutchouc silicone extrudé liquide, soit un caoutchouc silicone solide obtenu à l'aide d'une matrice de compression, à une température de traitement de 100 à 180 0C, pendant une durée de 2 à 15 minutes. 2. The method of claim 1, wherein the combination in step (2) can be either a liquid extruded silicone rubber or a solid silicone rubber obtained using a compression matrix, at a processing temperature from 100 to 180 0C, for a period of 2 to 15 minutes. 3. Procédé selon la revendication 1, dans lequel l'étape (2) peut être suivie, si nécessaire, par un procédé d'impression. 3. The method of claim 1, wherein step (2) can be followed, if necessary, by a printing process. 4. Procédé selon la revendication 3, dans lequel l'impression peut être soit un procédé par apport de matière, soit un procédé d'impression par gravure en creux.  4. The method of claim 3, wherein the printing can be either a process by adding material, or a printing process by intaglio. 5. Procédé selon la revendication 3, dans lequel le procédé d'impression peut comprendre au choix Ti, Cr, 5. Method according to claim 3, in which the printing method can optionally comprise Ti, Cr, Au ou autre métal comparable, qui est déposé par métallisation avant une gravure au laser de caractères ou de symboles. Au or other comparable metal, which is deposited by metallization before a laser engraving of characters or symbols.
FR9708525A 1997-06-17 1997-07-04 Hard rubber key pad forming process Pending FR2765514A1 (en)