FR2681858A1

FR2681858A1 - Improvements made to combustion inhibitors, especially for solid rocket fuels

Info

Publication number: FR2681858A1
Application number: FR7416181A
Authority: FR
Inventors: Societe Dite Imperi Industries; Kynoch Limited
Original assignee: Imperial Metal Industries Kynoch Ltd
Current assignee: Imperial Metal Industries Kynoch Ltd
Priority date: 1973-05-11
Filing date: 1974-05-10
Publication date: 1993-04-02
Also published as: NO741642L; IT1235558B; DE2422601C1; SE468767B; NO113607C; AU632274B2; GB1605362A; CA1326597C; SE7406216L

Abstract

The composition according to the invention is characterised in that it contains a copolymer of a hydrocarbon substance forming a carbon-carbon chain, with at least one constituent chosen from the group including methyl methacrylate, methacrylic acid, acrylic acid, methyl acrylate and ethyl hydroxymethacrylate. Application to solid rocket fuels.

Description

La présente invention concerne des inhibiteurs pour propergols solides etThe present invention relates to inhibitors for solid propellants and

en particulier, mais de façon non ex- clusive, l'invention concerne des inhibiteurs engendrant peu de fumée L'invention concerne aussi une composition qui, tout en étant susceptible d'être utilisée comme inhibiteur de com- bustion, trouve aussi d'autres applications dans une chambre de combustion d'un moteur-fusée. Les moteurs-fusées à propergols solides comportent une charge de propergol, un inhibiteur sur certaines parties de la charge pour contrôler la surface de la zone de combustion et une enveloppe extérieure L'inhibiteur est utilisé pour contrô- ler localement la surface de combustion du propergol de manière que la charge brûâle d'une façon géométrique désirée L'inhibiteur doit être chimiquement et physiquement compatible avec la char- ge L'inhibiteur peut être totalement ou partiellement consumé au cours de la mise à feu du moteur-fusée. in particular, but not exclusively, the invention relates to low smoke inhibitors The invention also relates to a composition which, while being capable of being used as a combustion inhibitor, also finds other applications in a combustion chamber of a rocket engine. Solid rocket engines have a propellant charge, an inhibitor on certain parts of the charge to control the surface of the combustion zone and an outer jacket The inhibitor is used to locally control the combustion surface of the propellant so that the charge burns in a desired geometric manner The inhibitor must be chemically and physically compatible with the charge The inhibitor may be totally or partially consumed during the firing of the rocket engine.

Si un moteur-fusée émet de la fumée, la traînée peut déceler la rampe de lancement du missile et sa trajectoire Le dégagement de fumée obscurcit la cible et camoufle le missile à la personne chargée de son lancement, ce qui est particulièrement défavorable si le missile doit être guidé visuellement le long de sa ligne de tir vers sa cible Ainsi, fréquemment, une des principales conditions pour moteurs-fusées est que l'émission de fumée au cours de la combustion soit aussi faible que pos- sible Cette condition est réalisée par l'utilisation d'un pro- pergol à double base, mais les parties inertes, principalement l'inhibiteur de la charge, évitent l'obtention d'un dégagement sans fumée. De plus, les charges de propergol sont largement utili- sées comme générateurs de gaz ou de puissance pour les car- touches en vue d'opérations mécaniques et, dans ces cas, la fumée se condense et constitue une nuisance en raison du fait qu'elle peut polluer l'aire dans laquelle elle est déchargée et provoque des interférences avec les mécanismes de soupapes et les sur- faces en mou emant. If a rocket engine emits smoke, the drag can detect the launching pad of the missile and its trajectory The release of smoke obscures the target and camouflages the missile to the person in charge of its launching, which is particularly unfavorable if the missile must be guided visually along its line of fire towards its target Thus, frequently, one of the main conditions for rocket engines is that the emission of smoke during combustion is as low as possible This condition is achieved by the use of a double base propergol, but the inert parts, mainly the charge inhibitor, avoid obtaining smoke-free release. In addition, propellant charges are widely used as gas or power generators for cartridges for mechanical operations and, in these cases, the smoke condenses and is a nuisance due to the fact that it can pollute the area in which it is unloaded and cause interference with valve mechanisms and surfaces when wetting.

L'expression "propergol à double base" utilisée ici couvre la nitrocellulose associée à la nitroglycérine et autre ester nitrique liquide avec ou sans autres additifs, stabili- sants chimiques, plastifiants, agents de modification de la balistique, combustibles comme la poudre d'aluminium et oxy- dants comme le perchlorate d'ammonium. La présente invention fournit une composition convenant pour être utilisée en association avec une charge de propergol solide, cette composition renfermant un copolymère d'une substan- ce hydrocarbonée formant une chaîne carbone-carbone avec au moins un constituant choisi dans le groupe comprenant le mé- thacrylate de méthyle, l'acide méthacrylique, l'acide acry- liquei l'acrylate de méthyle et l'hydroxyméthacrylate d'éthyle. De préférence, la composition renferme un copolymère de la substance hydrocarbonée formant une chaîne carbone-carbone avec au moins deux constituants choisis dans le groupe indiqué ci-dessus. Lia présente invention couvre aussi l'utilisation de la composition dont il-est question ci-dessus comme inhibiteur The term "dual base propellant" used here covers nitrocellulose associated with nitroglycerin and other liquid nitric ester with or without other additives, chemical stabilizers, plasticizers, ballistic modifiers, fuels such as aluminum powder and oxidants such as ammonium perchlorate. The present invention provides a composition suitable for use in association with a solid propellant filler, this composition comprising a copolymer of a hydrocarbon substance forming a carbon-carbon chain with at least one constituent chosen from the group comprising methyl thacrylate, methacrylic acid, acrylic acid, methyl acrylate and ethyl hydroxymethacrylate. Preferably, the composition contains a copolymer of the hydrocarbon substance forming a carbon-carbon chain with at least two constituents chosen from the group indicated above. The present invention also covers the use of the composition referred to above as an inhibitor.

de combustion lorsqu'elle est associée à une charge de pro- pergol solide La présente invention fournit aussi une charge de propergol solide renfermant un inhibiteur de combustion combiné à au moins une partie de sa surface, l'inhibiteur de combustion renfermant un copolymère d'une substance hydrocar- bonée formant une chaîne carbone-carbone avec au moins un constituant choisi dans le groupe comprenant le méthacrylate de méthyle, l'acide méthacrylique, l'acide acrylique, l'acry- late de méthyle et l'hydroxyméthacrylate d'éthyle. Par l'expression "substance hydrocarbonée formant une chaune carbone-carbone", on entend une substance hydrocarbonée .susceptible de polymérisation pour former une substance polymé- risée dont le squelette principal est une longue chaîne carbone-carbone. La substance hydrocarbonée est de préférence l'éthylène et elle peut être présente à raison d'au moins 75 % de la matrice copolymère. The present invention also provides a solid propellant charge containing a combustion inhibitor combined with at least part of its surface, the combustion inhibitor containing a copolymer of a hydrocarbon substance forming a carbon-carbon chain with at least one constituent chosen from the group comprising methyl methacrylate, methacrylic acid, acrylic acid, methyl acrylate and ethyl hydroxymethacrylate . The expression "hydrocarbon substance forming a carbon-carbon chaune" means a hydrocarbon substance capable of polymerization to form a polymerized substance whose main skeleton is a long carbon-carbon chain. The hydrocarbon substance is preferably ethylene and it can be present in an amount of at least 75% of the copolymer matrix.

On peut avoir une ou des charges dans l'inhibiteur pou- vant être choisies parmi les composés ayant un faible rapport carbone:oxygène de 1:1 ou moins, comme la cellulose, les hy- drates de carbone, l'oxamide, le polyoxyméthylène, l'urée- formaldéhyde, l'oxalate d'urée et l'acide tartrique D'autres charges appropriées sont sous forme particulaire et sont du carbone élémentaire et des oxydes, hydroxydes, carbonates et nitrates d'au moins un des éléments choisis parmi les suivants (a) magnésium, calcium, zinc, strontium, cadmium et baryum ; (b) bore et aluminium ; (c) silicium et titane ; (d) arsenic, antimoine et bismuth ; et (e) fer, cobalt et nickel. Si on désire obtenir une charge sans fumée ou sensible- ment sans fumée, la matière de charge à utiliser dans l'inhibiteur et la granulométrie desparticules sont telles que l'ex- position de l'inhibiteur comportant sa charge à la combustion de la charge de propergol dans la chambre du moteur-fusée ou There may be one or more charges in the inhibitor which can be chosen from compounds having a low carbon: oxygen ratio of 1: 1 or less, such as cellulose, carbohydrates, oxamide, polyoxymethylene , urea formaldehyde, urea oxalate and tartaric acid Other suitable fillers are in particulate form and are elemental carbon and oxides, hydroxides, carbonates and nitrates of at least one of the elements chosen from the following (a) magnesium, calcium, zinc, strontium, cadmium and barium; (b) boron and aluminum; (c) silicon and titanium; (d) arsenic, antimony and bismuth; and (e) iron, cobalt and nickel. If it is desired to obtain a smoke-free or substantially smoke-free charge, the charge material to be used in the inhibitor and the particle size distribution are such that the exposure of the inhibitor comprising its charge to the combustion of the charge propellant in the rocket engine chamber or

autre chambre de combustion conduit à un produit entièrement ga- zeux ou contenant des particules de dimension inférieure à 1 micron ou supérieure à 15 microns. De ce qui précède, il ressort que pour une substance de charge choisie il suffit d'un essai simple pour décider si les dimensions des particules de la matière de charge dans l'inhibiteur de combustion sont importantes et si ces dimen- sions conviennent. Lorsqu'on désire obtenir un inhibiteur sans fumée la présence de charge peut réduire le rapport carbone:oxygène pour l'inhibiteur comportant sa charge jusqu'au-dessous de 2:1, .de préférence au-dessous de 1,5:1. Les exemples suivants sont donnés à titre illustratif et nullement limitatif de l'invention. Exemule 1 On copolymérise de l'éthylène, de l'acide méthacrylique et du méthacrylate de méthyle. another combustion chamber leads to a product which is entirely gaseous or contains particles of size less than 1 micron or greater than 15 microns. From the foregoing, it appears that for a selected filler, a simple test suffices to decide whether the particle sizes of the filler in the combustion inhibitor are large and whether these dimensions are suitable. When it is desired to obtain a smoke-free inhibitor, the presence of a charge can reduce the carbon: oxygen ratio for the inhibitor comprising its charge to below 2: 1, preferably below 1.5: 1. The following examples are given by way of illustration and in no way limit the invention. Example 1 Ethylene, methacrylic acid and methyl methacrylate are copolymerized.

Les proportions sont de 15 % pour l'acide méthacrylique, CH 3-CH=C-H + 15 % de méthacrylate de méthyle CH 3-CH=C-H 3 3 COOH 3 OCH 3 + 70 % d'éthylène CH 2 =CH 2. Suivant une variante, le copolymère ci-dessus peut ëtre modifié par copolymérisation avec un additif à base d'hydroxyméthacrylate d'éthyle CH 2 = C CH 20 H. COOC 2 H 5 Les copolymères ci-dessus en utilisant des charges du type précédemment décrit peuvent être chargés jusqu'à un degré de 3:1 en poids de charge par rapport à la matrice ou plus. La charge et le copolymère peuvent 8 tre broyés pour former une galette de mélange intime Le mélange sous forme de galette de charge et de polymère est essentiellement formé par fusion du mélange copolymère et malaxage avec la charge qui est enrobée par le mélange copolymère fondu On forme ainsi des plaques du mélange de copolymère fondu et de charge que l'on peut utiliser pour l'obtention de feuilles par moulage ou par pressage Le produit obtenu par le procédé de mélange décrit ci-dessus peut The proportions are 15% for methacrylic acid, CH 3-CH = CH + 15% methyl methacrylate CH 3-CH = CH 3 3 COOH 3 OCH 3 + 70% ethylene CH 2 = CH 2. Next a variant, the above copolymer can be modified by copolymerization with an additive based on ethyl hydroxymethacrylate CH 2 = C CH 20 H. COOC 2 H 5 The above copolymers using fillers of the type described above can be loaded to a degree of 3: 1 by weight of load relative to the matrix or more. The filler and the copolymer can be ground to form a wafer for intimate mixing. The mixture in the form of filler wafer and of polymer is essentially formed by melting the copolymer mixture and kneading with the filler which is coated with the molten copolymer mixture. thus plates of the blend of molten copolymer and filler which can be used for obtaining sheets by molding or pressing. The product obtained by the mixing process described above can

également être mis sous forme de granulés et traité à nouveau comme lot de charge pour l'extrusion de tubes ou de feuilles. Suivant une variante de formation du mélange, le copo- lymère et les charges sont séparément broyés pour obtenir une poudre fine et le mélange de poudre est ensuite mis sous forme de feuille ou de plaque sous l'action de la pression et de la chaleur, la température de la poudre au cours de l'opération de pressage étant maintenue en particulier entre 110 et 150 C sous une pression de 100 kg/cm 2 ou plus Les feuilles et les plaques peuvent alors être moulées pour avoir la forme désirée pour obtenir les inhibiteurs. Exem-le 2 Dans un second exemple de l'invention, on copolymérise 20 parties d'acide acrylique CH = C-H , 15 parties d'acrylate COOH de méthyle CH = C-H et 65 parties d'éthylène CH 2 CH 2 2 OCF 2 C 000 CH 3 also be granulated and re-treated as a batch of filler for the extrusion of tubes or sheets. According to a variant formation of the mixture, the copolymer and the fillers are separately ground to obtain a fine powder and the powder mixture is then put into sheet or plate form under the action of pressure and heat, the temperature of the powder during the pressing operation being maintained in particular between 110 and 150 C under a pressure of 100 kg / cm 2 or more The sheets and the plates can then be molded to have the desired shape to obtain the inhibitors. Example 2 In a second example of the invention, 20 parts of acrylic acid CH = CH, 15 parts of methyl COOH acrylate CH = CH and 65 parts of ethylene CH 2 CH 2 2 OCF 2 C are copolymerized. 000 CH 3

100 parties du mélange copolymère on ajoute 50 parties de polyoxyméthylène (CH 20)n On mélange ensemble les constituants et on comprime le mélange à 1300 C pour avoir des feuilles ou des plaques Sui- vant une variante, on peut aussi utiliser l'une des méthodes décrites ci-dessus. le degré de copolymérisation peut être ajusté pour mo- difier les propriétés physiques de l'inhibiteur solide et il peut contrôler le degré d'état caoutchouteux de l'inhibiteur. Si l'on ne désire pas une composition sans fumée, on peut utiliser tout caoutchouc ou tous additifs plastiques nor- maux De même, l'inhibiteur peut être utilisé pour des pro- pergols solides autres que les propergols à double base, c'est-à-dire les propergols composites. Cependant,l'un des avantages des inhibiteurs de l'in- vention lorsqu'on les utilise avec des propergols à double base sous la forme particulaire décrite ci-dessus,réside dans le fait que non seulement ils constituent le système virtuelle- ment sans fumée au cours de la combustion à des pressions éle- 100 parts of the copolymer mixture 50 parts of polyoxymethylene (CH 20) are added n The components are mixed together and the mixture is compressed at 1300 ° C. to have sheets or plates Depending on a variant, one of the following can also be used methods described above. the degree of copolymerization can be adjusted to modify the physical properties of the solid inhibitor and it can control the degree of rubbery state of the inhibitor. If a smoke-free composition is not desired, any normal rubber or plastic additives can be used. Similarly, the inhibitor can be used for solid propergols other than double base propellants, that is ie composite propellants. However, one of the advantages of the inhibitors of the invention when used with dual base propellants in the particulate form described above is that not only do they constitute the system virtually without smoke during combustion at high pressures

vées normales rencontrées dans les moteurs-fusées, mais égale- ment dans le fait -qu'ils sont sans fumée ou presque après mise à feu du moteur, état qui correspond à un abaisse- ment progressif de la pression dans la chambre de combustion. Ceci, bien entendu, constitue un avantage certain. Si on désire une résistance élevée à l'érosion ou une propriété mécanique telle qu'un module élevé d'élasticité ou une résistance élevée, on peut alors utiliser des proportions supérieures de charge pouvant aller jusqu'à 300 parties en poids ou au-delà, comparativement aux 100 parties en poids des composés organiques. D'autres substances formant une chaîne principale car- bone-carbone peuvent être utilisées autres que l'éthylène, bien que ce dernier soit préférable si la nécessité d'avoir une composition sans fumée est recherchée et importante. Suivant un autre procédé de fabrication du produit, les poudres du copolymère et des substances de charge peuvent être normal ves encountered in rocket engines, but also in the fact that they are smoke-free or almost after ignition of the engine, a state which corresponds to a gradual reduction in the pressure in the combustion chamber. This, of course, is a definite advantage. If a high resistance to erosion or a mechanical property such as a high modulus of elasticity or a high resistance is desired, then higher proportions of load can be used which can go up to 300 parts by weight or more , compared to 100 parts by weight of organic compounds. Other substances forming a main carbon-carbon chain can be used other than ethylene, although the latter is preferable if the need for a smoke-free composition is sought and important. According to another process for manufacturing the product, the powders of the copolymer and of the filler substances can be

préalablement mélangées puis admises dans un extrudeur du type à vis pour matières plastiques ou dans une presse d'extrusion. A partir de cet appareil, on extrude la composition copolymère soit sous Mforme physique désirée, par exemple tube ou feuille, soit sous la forme par exemple d'une feuille qui sera ultérieu- rement comprimée pour avoir la forme désirée. Les compositions de la présente invention trouvent leur application dans la chambre de combustion d'un moteur-fusée, dans d'autres buts que l'inhibition de la combustion Ainsi des substances de charges différentes mais appropriées peuvent être utilisées de manière à être compatibles avec la composi- tion en vue de la destination recherchée Une matière de charge particulière consiste en fibre de verre ou autre matériau de renforcement fibreux de manière à améliorer la résistance méca- nique et/ou la rigidité de la composition D'autres matériaux de renforcement filamenteux sont constitués par de l'amiante en copeaux ou des fibres de carbone Suivant la réceptivité de la composition vis-à-vis de la matière de charge en cause, le rapport entre la matière de charge et le polymère peut aller premixed and then admitted to a screw type extruder for plastics or to an extrusion press. From this apparatus, the copolymer composition is extruded either in the desired physical form, for example tube or sheet, or in the form for example of a sheet which will be subsequently compressed to have the desired shape. The compositions of the present invention find their application in the combustion chamber of a rocket engine, for purposes other than inhibiting combustion. Thus substances of different but appropriate charges can be used so as to be compatible with the composition for the intended purpose A particular filler material consists of glass fiber or other fibrous reinforcing material so as to improve the mechanical strength and / or the rigidity of the composition Other filamentary reinforcing materials consist of asbestos in shavings or carbon fibers Depending on the receptivity of the composition vis-à-vis the filler in question, the ratio between the filler and the polymer can range

jusqu'à 3:1 ou plus. Les propriétés que l'on peut obtenir sont illustrées par les compositions ayant les teneurs en charge et les pro- priétés physiques indiquées au tableau ci-après,toutes ces pro- priétés étant basées sur un polymère à 70 % en poids d'éthylène, 15 % en poids d'acide méthacrylique et 15 % en poids de méthacry- late de méthyle. up to 3: 1 or more. The properties which can be obtained are illustrated by the compositions having the filler contents and the physical properties indicated in the table below, all of these properties being based on a polymer containing 70% by weight of ethylene, 15% by weight of methacrylic acid and 15% by weight of methyl methacrylate.

TABLEAU Teneur de Résistance à la Allongement la charge traction en 2 % méganewtons/m O 38 490 Polyoxyméthylène 75 4,4 2,2 Oxamide 40 17,5 417 Oxamide 75 9,3 8 Fibres de verre 75 20 3 Fibres de verre 30 15 380 TABLE Content of Resistance to Elongation the tensile load in 2% meganewtons / m O 38 490 Polyoxymethylene 75 4.4 2.2 Oxamide 40 17.5 417 Oxamide 75 9.3 8 Glass fibers 75 20 3 Glass fibers 30 15 380

Il est également possible de choisir une matière de charge thermoplastique, par exemple en polyoxyméthylène, puis d'extruder ou de mouler à une température appropriée Si la température est supérieure au point de fusion de la matière de charge, on obtient alors un comoulage qui présente largement les propriétés physiques du matériau de charge en association avec certaines propriétés caoutchouteuses provenant du copolymère Si la température est au-dessous du point de fu- sion, on obtient largement les propriétés caoutchouteuses du copolymère Ceci s'applique à l'utilisation de tout matériau thermoplastique de charge Comme exemple, on prépare le copoly- mère à 70 % en poids d'éthylène, 15 % en poids d'acide métha- crylique et 15 % en poids de méthacrylate de méthyle et on le charge au moyen de 75 %, c'est-à-dire 75 parties pour 100 parties de copolymère,de polyoxyméthylène par mélange des deux sous forme pulvérulente Lorsqu'on extrude le mélange à 150 `C, on obtient un caoutchouc thermoplastique chargé présentant lar- gement les propriétés du copolymère Par ailleurs, lorsqu'on extrude le mélange à 1700 C, on obtient un co-moulage dans lequel la résistance à la traction est doublée. Les inhibiteurs de combustion décrits aux exemples 1 et 2 ci-dessus sont essayés quant à la production de fumée en les uti- lisant dans des-charges coulées de propergol à double base solide de 150 mm de diamètre et en mettant à feu avec une durée de combustion de 26 secondes On mesure le degré d'obscurcissement de la lumière polarisée au cours du dégagement des fumées, ce qui est réalisé au moyen d'un photomètre Les résultats obtenus montrent un degré d'obscurcissement de O à 5 % pour diffé- rents échantillons Ceci peut être comparé aux mêmes essais effectués dans les mêmes conditions à l'exception du fait que l'on utilise un inhibiteur du type cellulosique classique sur une charge coulée de propergol solide à double base de 150 mm de dia- mètre Dans ce cas, le degré d'obscurcissement est d'environ 80 %. Les copolymères de l'invention trouvent une application particulière comme substances inhibitrices de combustion en raison de la faible absorption de nitroglycérine provenant. It is also possible to choose a thermoplastic filler material, for example polyoxymethylene, then to extrude or mold at an appropriate temperature. If the temperature is higher than the melting point of the filler material, a co-molding is obtained which has largely the physical properties of the filler material in combination with certain rubber properties from the copolymer If the temperature is below the melting point, the rubber properties of the copolymer are largely obtained This applies to the use of any material thermoplastic filler As an example, the copolymer is prepared at 70% by weight of ethylene, 15% by weight of methacrylic acid and 15% by weight of methyl methacrylate and is charged with 75%, that is to say 75 parts per 100 parts of copolymer, of polyoxymethylene by mixing the two in powder form When the mixture is extruded to 150 `C, a charged thermoplastic rubber is obtained having broadly the properties of the copolymer. Furthermore, when the mixture is extruded at 1700 C, a co-molding is obtained in which the tensile strength is doubled. The combustion inhibitors described in Examples 1 and 2 above are tested for the production of smoke by using them in poured charges of propellant with double solid base 150 mm in diameter and igniting with a duration combustion time of 26 seconds The degree of darkening of the polarized light is measured during the generation of smoke, which is carried out by means of a photometer. The results obtained show a degree of darkening of 0 to 5% for different rents samples This can be compared to the same tests carried out under the same conditions with the exception of the use of an inhibitor of the conventional cellulosic type on a poured charge of solid propellant with double base of 150 mm in diameter. case, the degree of darkening is about 80%. The copolymers of the invention find particular application as combustion inhibiting substances due to the low absorption of nitroglycerin obtained.

des charges à double base,de la faible densité ordinaireile:ïi comprise entre 1,1 et 1,2 suivant les matériaux de charge choisis, de la bonne perméabilité aux gaz et de leursbonnes propriétés adhésives On peut également facilement leur donner une forme Cependant, leurqpropriétés mécaniques sont aisément ajustées en choisissant le copolymbre lui-même et les matériaux d.e charge et autres additifs à utiliser de telle sorte queles propriétés mécaniques peuvent être ajustées à celles d'un substrat comme la charge de propergol solide ainsi qu'aux propriétés mécaniques des autres substrats tels que d'autres polymères ou un métal Les copolymères ont par conséquent d'autres applications dans les conditions onéreuses régnant dans la chambre de combustion d'un moteur-fusée et, par exemple, ils peuvent être utilisés comme constituants de haute résistance d'homogénéité d'un bloc de propergol. Il va de soi que la présente invention n'a été décrite qu'à titre purement explicatif et nullement limitatif et que toute modification utile pourra y être apportée sans sortir de son cadre tel que défini par les revendications ci-après. fillers with double base, of low ordinary density: between 1.1 and 1.2 depending on the filler materials chosen, good gas permeability and their good adhesive properties It can also easily be given a form However, their mechanical properties are easily adjusted by choosing the copolymer itself and the filler materials and other additives to be used so that the mechanical properties can be adjusted to those of a substrate such as the solid propellant filler as well as to the mechanical properties of the other substrates such as other polymers or a metal Copolymers therefore have other applications under the expensive conditions prevailing in the combustion chamber of a rocket engine and, for example, they can be used as high strength constituents homogeneity of a propellant block. It goes without saying that the present invention has been described for purely explanatory and in no way limitative and that any useful modification may be made without departing from its scope as defined by the claims below.

Claims

CLAIMS 1 Composition for application in association with

a solid propellant charge, a composition characterized in that it contains a copolymer of a hydrocarbon substance forming a carbon-carbon chain with at least one constituent chosen from the group comprising methyl methacrylate, methacrylic acid, acrylic acid, methyl acrylate and ethyl hydroxymethacrylate.

2 Composition according to Claim 1 :, characterized in that it contains a copolymer of the hydrocarbon substance forming a carbon-carbon chain with at least two constituents chosen from the group indicated in this sub-claim.

3 Composition according to claim 1 or claim 2, characterized in that the hydrocarbon substance forming a carbon-carbon chain is ethylene.

4 Composition according to Claim 3, characterized in that the ethylene is present in an amount of at least 75% of the copolymer matrix.

5 Composition according to any one of claims 1 to 4, characterized in that it contains at least one filler.

6 Composition according to claim 5, characterized in that the filler has a low carbon: oxygen ratio of 1: 1 or less and that it is chosen from the group comprising cellulose, carbohydrates, oxamide , poly-oxymethylene, urea-formaldehyde, urea oxalate and tartaric acid.

7 Composition according to Claim 5, characterized in that the filler is in a particulate form and that it is chosen from the group comprising elementary carbon and oxides, hydroxides, carbonates and nitrates of at least one of the elements chosen from the following: (a) magnesium, calcium, zinc, strontium, cadmium and barium; (b) boron and aluminum; (c) silica and titanium; (d) arsenic, antimony and bismuth; and (e) iron, cobalt and nickel; and that the filler material and the particle size are such that the exposure of the inhibitor comprising its charge to the combustion of the propellant charge in the chamber of a rocket engine results in a product which is entirely gaseous or containing particles smaller than 1 micron or larger than 15 microns.

8 Composition according to claim 5, characterized in that the filler is a filamentary reinforcing material.

9 Composition according to claim 5, characterized in that the filler is a thermoplastic material.

10 Inhibitory composition suitable for its application in combination with a surface of a charge of solid propergol, characterized in that it comprises a composition containing a copolymer of a hydro-carbonaceous substance forming a carbon-carbon chain with at least one constituent chosen from the group comprising methyl methacrylate, methacrylic acid, acrylic acid, methyl acrylate and ethyl hydroxymethacrylate.

11 Inhibitory composition characterized in that it contains a composition according to any one of claims 2 to 9.

12 Solid propellant charge, characterized in that it contains a combined combustion inhibitor on at least part of its surface, this combustion inhibitor containing a copolymer of a hydrocarbon substance forming a carbon-carbon chain with at at least one constituent chosen from the group comprising methyl methacrylate, methacrylic acid, acrylic acid, methyl acrylate and ethyl hydroxymethacrylate.

14 solid propellant charge according to claim 15, characterized in that the propellant is a double base propellant.

13 Solid propellant charge, characterized in that it contains a combined combustion inhibitor on at least part of its surface, this combustion inhibitor being of a composition according to any one of claims 1 to 9.