FR2611587A1 - Decorative coloured composite - Google Patents
Decorative coloured composite Download PDFInfo
- Publication number
- FR2611587A1 FR2611587A1 FR8703507A FR8703507A FR2611587A1 FR 2611587 A1 FR2611587 A1 FR 2611587A1 FR 8703507 A FR8703507 A FR 8703507A FR 8703507 A FR8703507 A FR 8703507A FR 2611587 A1 FR2611587 A1 FR 2611587A1
- Authority
- FR
- France
- Prior art keywords
- complex
- colored
- decorative
- layer
- layers
- Prior art date
- Legal status (The legal status is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the status listed.)
- Withdrawn
Abstract
Description
L invention est relative à un complexe coloré décoratif. The invention relates to a decorative colored complex.
Elle trouvera notamment son application dans le domaine de 1 imprimerie, des papiers peints, du papier d'emballage.It will find its application in particular in the field of 1 printing works, wallpapers, wrapping paper.
Toutefois, l'utilisation du complexe coloré décoratif de la présente invention pourrait être diverse et il pourrait être notamment utilisé dans le domaine de la confection de certains vêtements, de calicots de signalisation, banderoles ou similaires. En effet, les utilisations de substrats colorés sont nombreuses de meme que leurs réalisations. However, the use of the decorative colored complex of the present invention could be diverse and it could be used in particular in the field of making certain garments, signal banners, banners or the like. Indeed, the uses of colored substrates are numerous as are their achievements.
Dans la majorité des cas, pour colorer un substrat ou un support, on a recours aux différentes techniques d'imprimerie notamment dans le cas du papier. on réalise des impressions selon les teintes à obtenir. Toutefois, certaines qualités du support sont requises pour obtenir une bonne qualité du produit fini. In the majority of cases, to color a substrate or a support, recourse is had to various printing techniques, in particular in the case of paper. prints are made according to the colors to be obtained. However, certain qualities of the support are required to obtain good quality of the finished product.
Pour cette raison, les fabricants s'orientent vers une autre technique connue qui consiste à réaliser un complexe formé d'un film plastifié collé sur un support papier traditionnel. Les avantages de cette structure sont multiples en particulier, le complexe est étanche, à l'abri de l'humidité extérieure, résistant et présente une qualité esthetique appréciable. For this reason, manufacturers are turning to another known technique which consists in producing a complex formed from a plasticized film bonded to a traditional paper support. The advantages of this structure are manifold in particular, the complex is waterproof, protected from external humidity, resistant and has appreciable aesthetic quality.
Afin d'obtenir la coloration de tels complexes, il est connu de réaliser la coloration au moment du collage notamment en saupoudrant de pigments colorés 1 enduction de colle ou en mélangeant ces pigments à la colle. In order to obtain the coloring of such complexes, it is known to carry out the coloring at the time of bonding, in particular by sprinkling colored pigments with 1 coating of glue or by mixing these pigments with glue.
Plus récemment, des techniques perfectionnées ont permis d'obtenir une colle plus homogène que celle obtenue par mélange des pigments. More recently, improved techniques have made it possible to obtain a more homogeneous glue than that obtained by mixing pigments.
Plus précisément. on réalise une coloration uniforme de la colle par adjonction d'une encre soluble dans le solvant de la colle. More precisely. uniform coloring of the adhesive is carried out by adding an ink soluble in the adhesive solvent.
Ensuite, cette colle est enduite par exemple sur le film plastifié et la coloration apparait par transparence de ce dernier.Then, this glue is coated for example on the plasticized film and the coloring appears by transparency of the latter.
Dans le domaine des papiers peints, d'autres problémes techniques apparaissent: il s'agit par exemple d'obtenir une gamme de couleurs trés étendues permettant l'harmonisation parfaite des peintures et du papier peint ou encore de ce dernier aux tentures. In the field of wallpapers, other technical problems appear: it is for example a question of obtaining a very wide range of colors allowing the perfect harmonization of paints and wallpaper or even of the latter with hangings.
Un autre problème spécifique du papier peint réside dans sa faculté d'absorption de l'humidité et dans la qualité de son adhérence sur le support à recouvrir. Another specific problem with wallpaper is its ability to absorb moisture and the quality of its adhesion to the support to be covered.
Un des buts de la présente invention est de proposer un complexe coloré décoratif qui trouvera notamment son application dans le domaine du papier peint et qui permettra de répondre aux différents critères spécifiques précités. One of the aims of the present invention is to propose a decorative colored complex which will find its application in particular in the field of wallpaper and which will make it possible to meet the various specific criteria mentioned above.
Un but de la présente invention est de proposer un complexe coloré décoratif qui constituera un papier peint coloré avec une palette de couleurs infinies autorisant son adaptation à tout type de décoration. De plus, le papier peint ainsi constitué sera lavable, indéchirable et d'aspect esthétique trés agréable. An object of the present invention is to provide a decorative colored complex which will constitute a colored wallpaper with an infinite palette of colors allowing its adaptation to any type of decoration. In addition, the wallpaper thus created will be washable, tear-proof and very aesthetically pleasing.
En outre, le papier peint ainsi constitué aura un pouvoir d'absorption de l'humidité important et son accrochage sur le support sera renforcé de par la structure du complexe utilise. In addition, the wallpaper thus formed will have a significant moisture absorption power and its attachment to the support will be reinforced by the structure of the complex used.
Un autre but de la présente invention est de proposer un complexe coloré décoratif qui, grâce aux avantages conférés par sa structure spécifique, permettra son utilisation pour l'emballage, la protection de produits, et également pour la réalisation de certains vetements ou de banderoles ou calicots de signalisation. Another object of the present invention is to propose a decorative colored complex which, thanks to the advantages conferred by its specific structure, will allow its use for packaging, protection of products, and also for the production of certain clothing or banners or signaling banners.
D'autres buts et avantages de la présente invention apparaitront au cours de la description qui va suivre qui n'est cependant donnée qu'à titre indicatif et qui n'a pas pour but de la limiter. Other objects and advantages of the present invention will appear during the description which follows which is however given only for information and which is not intended to limit it.
Selon l'invention, le complexe coloré décoratif, qui trouvera notamment son application dans le domaine des papiers peints, ou du papier d'emballage, constitué au moins de deux couches, la première couche, formant le verso du complexe, étant constituée d'une feuille support, la deuxième couche, formant le recto du complexe, étant constituée par un film plastifié transparent imperméable, l'une des deux couches étant encollée par une enduction de colle colorée, est caractérisé par le fait qu'il comporte une troisième couche intermédiaire perméable, disposée entre le recto et le verso du dit complexe, après la dite enduction de colle colorée, cette dernière assurant l'adhésion des trois couches. According to the invention, the decorative colored complex, which will find its application in particular in the field of wallpapers, or wrapping paper, consisting of at least two layers, the first layer, forming the back of the complex, consisting of a support sheet, the second layer, forming the front side of the complex, being constituted by a transparent transparent plastic film, one of the two layers being glued with a coating of colored glue, is characterized in that it comprises a third layer permeable intermediate, disposed between the front and back of said complex, after said coating of colored glue, the latter ensuring the adhesion of the three layers.
L'invention sera mieux comprise à la lecture de la description suivante accompagnée des dessins en annexe qui en font partie intégrante. The invention will be better understood on reading the following description accompanied by the accompanying drawings which form an integral part thereof.
La figure 1 schématise une vue en coupe des différents constituants du complexe coloré décoratif de la présente invention. Figure 1 shows schematically a sectional view of the various constituents of the decorative colored complex of the present invention.
La figure 2 illustre schématiquement un type d'installation qui permette la fabrication du complexe selon la présente invention. FIG. 2 schematically illustrates a type of installation which allows the manufacture of the complex according to the present invention.
L'invention vise un complexe coloré décoratif dont les applications sont multiples dans le domaine des papiers peints ou du papier d'emballage ou encore prévu pour la réalisation de vêtements, calicots ou banderoles de signalisation. The invention relates to a decorative colored complex whose applications are manifold in the field of wallpapers or wrapping paper or else provided for the production of clothing, banners or signaling banners.
Plus spécialement, dans le domaine des papiers peints, l'invention permet d'obtenir un complexe coloré décoratif délivré en continu avec une seule étape principale de fabrication. More specifically, in the field of wallpapers, the invention makes it possible to obtain a decorative colored complex delivered continuously with a single main manufacturing step.
En effet, grâce à la mise en oeuvre de laprésente invention, on formera le complexe en tant que tel et, en même temps, on obtiendra sa coloration, ce sans aucune limitation.de nuances et de coloris. In fact, thanks to the implementation of the present invention, the complex will be formed as such and, at the same time, its color will be obtained, without any limitation of shades and colors.
Ceci va à l'encontre des procédés traditionnels de fabrication qui genéralement nécessitaient, après la formation du papier peint support, une reprise en imprimerie pour colorer et décorer ce dernier. This goes against traditional manufacturing processes which generally required, after the formation of the support wallpaper, a return to printing to color and decorate the latter.
Ainsi, la solution sera plus économique tout en obtenant des résultats, sur le plan esthétique et résistance, égaux et même supérieurs au papier obtenu par la technique traditionnelle. Thus, the solution will be more economical while obtaining results, on the aesthetic level and resistance, equal and even superior to the paper obtained by the traditional technique.
La figure 1 montre schématiquement une vue en coupe du complexe coloré décoratif 1 de la présente invention. Figure 1 schematically shows a sectional view of the decorative colored complex 1 of the present invention.
La base de composition du complexe 1 s'inspire des techniques connues généralement dénommées par techniques de pelliculage. The composition base of complex 1 is inspired by known techniques generally known as film-coating techniques.
Ainsi, le complexe 1 est constitué au moins de deux couches 2 et 3, la première couche 3, formant le verso du complexe 1, étant constituée d'une feuille support et, la deuxième couche 2, formant le recto du complexe, étant constituée par un film plastifié transparent imperméable. Thus, the complex 1 is made up of at least two layers 2 and 3, the first layer 3, forming the back side of the complex 1, being made up of a support sheet and, the second layer 2, forming the front side of the complex, being made up by a transparent waterproof plastic film.
En outre, selon la présente invention, le complexe comporte une troisième couche intermédiaire 5, perméable, disposée entre la couche recto 2 et la couche 'verso 3. In addition, according to the present invention, the complex comprises a third intermediate layer 5, permeable, disposed between the front layer 2 and the back layer 3.
Pour constituer l'assemblage du complexe 1, l'une des deux couches 2 ou 3 est encollée par une enduction 4 de colle colorée, cette dernière assurant l'adhésion des trois couches 2, 3, 5. To constitute the assembly of the complex 1, one of the two layers 2 or 3 is glued by a coating 4 of colored glue, the latter ensuring the adhesion of the three layers 2, 3, 5.
Les différentes phases de la fabrication seront expliquées ultérieurement en regard de la figure 2. The different phases of manufacturing will be explained later with reference to Figure 2.
Selon l'invention, la troisième couche intermédiaire 5 se présente sous la forme d une armature synthétique tramée. De plus, on choisira celle-ci de manière à ce qu'elle présente de bonnes qualités de résistance mécanique, d'absorption de liquide, et de perméabilité à l'eau. According to the invention, the third intermediate layer 5 is in the form of a woven synthetic reinforcement. In addition, it will be chosen so that it has good qualities of mechanical resistance, absorption of liquid, and permeability to water.
Il est à noter que l'on a obtenu de bons résultats en utilisant une armature 5 à base de polypropyléne et de polyamide commercialiasée par exemple sous la marque Scrinyl". It should be noted that good results have been obtained using a frame 5 based on polypropylene and polyamide marketed for example under the brand Scrinyl ".
Plus précisément, cette armature est constituée par un réseau de mailles rectangulaires à base de 95 Z de polypropyléne et de 5 Z de polyamide dont l'épaisseur est sensiblement de 0,1 mm et le poids de 8 gain . Toutefois, d'autres qualités d'armatures pourraient être utilisées sans sortir du cadre de la présente invention. More precisely, this reinforcement is constituted by a network of rectangular meshes based on 95% of polypropylene and 5% of polyamide, the thickness of which is substantially 0.1 mm and the weight of 8 gain. However, other qualities of reinforcement could be used without departing from the scope of the present invention.
En ce qui concerne les deux autres couches 2 et 3 utilisées en combinaison avec l'armature 5 propyléne, de bons résultats sont obtenus en utilisant un support papier pour le verso du complexe et un film transparent de polyéthyléne, polypropyléne, polyester, acétate de cellulose, ou PVC pour la couche recto. With regard to the other two layers 2 and 3 used in combination with the propylene reinforcement 5, good results are obtained by using a paper support for the back of the complex and a transparent film of polyethylene, polypropylene, polyester, cellulose acetate. , or PVC for the front layer.
En ce qui concerne la colle colorée, on utilisera une colle de type traditionnel à deux composants à base de résine époxy contenant un solvant. Regarding the colored glue, a traditional type two-component glue based on an epoxy resin containing a solvent will be used.
Pour teinter la colle, on ajoutera de l'encre soluble dans le solvant de la colle. A cet égard, on utilisera des encres compatibles avec la colle et les matériaux formant les couches pour qu'il n'y ait pas de détérioration de l'un d'eux ou de modification de l'adhérence de la colle ou altération des couleurs. To tint the glue, add solvent-soluble ink to the glue. In this regard, we will use inks compatible with the glue and the materials forming the layers so that there is no deterioration of one of them or modification of the adhesion of the glue or alteration of the colors. .
De telles colorations de colle sont connues en soi et l'Homme de l'Art pourra utiliser par exemple de colle à base de résine époxy et d'un durcisseur du type poly-isocyanate dans un rapport 10 à 1. A titre de solvant, ce type de colle utilise l'acétate d'isopropyle ou le méthyl éthylcétone. Such glue stains are known per se and those skilled in the art may use, for example, glue based on epoxy resin and a hardener of the polyisocyanate type in a ratio of 10 to 1. As solvent, this type of glue uses isopropyl acetate or methyl ethyl ketone.
Toutefois, il est à noter que l'utilisation d'acétate d'isopropyle est recommandée pour des films de polyéthvléne, polypropylène, polyester, acétate de cellulose et PVC. Par contre, le méthyl éthylcétone ne convient pas pour l'acétate de cellulose ou certains polyesters insuffisamment polymérisés. However, it should be noted that the use of isopropyl acetate is recommended for polyethylene, polypropylene, polyester, cellulose acetate and PVC films. On the other hand, methyl ethyl ketone is not suitable for cellulose acetate or certain insufficiently polymerized polyesters.
En ce qui concerne le choix de l'encre, il devra être établi non seulement en fonction du type de solvant utilisé mais également en fonction de la viscosité de la colle. A cet égard, il est intéressant pour atteindre un équilibre et une grande régularité dans l'application du mélange d'avoir des viscosités voisines. Regarding the choice of ink, it should be established not only according to the type of solvent used but also according to the viscosity of the adhesive. In this regard, it is advantageous to achieve a balance and a great regularity in the application of the mixture to have similar viscosities.
D'une façon générale; les propriétés physiques de l'encre et de la colle doivent etre identiques pour que toutes modifications des conditions extérieures aient la meme influence sur le mélange qui ainsi conserve son homogénéité en toutes circonstances. Generally speaking; the physical properties of the ink and the adhesive must be identical so that any modification of the external conditions have the same influence on the mixture which thus preserves its homogeneity in all circumstances.
La figure 2 illustre schématiquement une installation de fabrication du complexe coloré décoratif selon la présente invention. FIG. 2 schematically illustrates an installation for manufacturing the decorative colored complex according to the present invention.
Cette installation est alimentée en quatre matières de base constituantes du complexe à savoir le film plastifié 2, la feuille support 3, la colle colorée i, et l'armature intermédiaire perméable 5. This installation is supplied with four basic materials constituting the complex, namely the plasticized film 2, the support sheet 3, the colored glue i, and the permeable intermediate frame 5.
De plus, l'installation comporte une machine du type machine à pelliculerZ 6 réalisée selon des techniques connues de l'Homme de l Art. In addition, the installation comprises a machine of the Z 6 film-coating machine type produced according to techniques known to those skilled in the art.
En particulier, le film plastifié 2 est dispose en forme de rouleaux 7, puis passe dans un poste d encollage 8 du type encolleur par barbotage", lequel permet de déposer un film de colle colorée s régulier sur la surface du film 2. In particular, the plasticized film 2 is arranged in the form of rollers 7, then passes through a gluing station 8 of the sizing type by bubbling ", which makes it possible to deposit a film of regular colored glue on the surface of the film 2.
A la sortie du poste d'encollage 8, le film plastifié encollé et teinté 9 passe dans un tunnel de séchage 10 ou le solvant s'évapore. De plus, le séchage peut être accéléré à l'aide de résistances chauffantes 11 et les vapeurs de solvant sont aspirées par des dispositifs- traditionnels. At the exit from the gluing station 8, the plasticized glued and tinted film 9 passes through a drying tunnel 10 or the solvent evaporates. In addition, the drying can be accelerated using heating resistors 11 and the solvent vapors are sucked by traditional devices.
A la sortie du poste d'encollage 10 est disposé un poste de calandrage 12 qui va autoriser la formation du complexe 1 de la présente invention. At the exit from the gluing station 10, a calendering station 12 is arranged which will allow the formation of the complex 1 of the present invention.
A l'entrée de ce poste de calandrage 12 sont introduites les différentes couches constituantes du complexe 1 respectivement superposées les unes par rapport aux autres à savoir la première couche feuille support 3, la couche intermédiaire armature 5, puis la couche formée par le film plastifié encollé et teinté 9. At the entrance to this calendering station 12 are introduced the various constituent layers of the complex 1 respectively superimposed relative to each other, namely the first support sheet layer 3, the intermediate reinforcing layer 5, then the layer formed by the plasticized film glued and tinted 9.
Ce sandwich est ensuite introduit entre les cylindres de la calandre 12 qui permettront de les appliquer avec une certaine pression sous une température prédéterminée pour réaliser l'adhésion des trois couches formant le complexe 1. This sandwich is then introduced between the cylinders of the calender 12 which will make it possible to apply them with a certain pressure under a predetermined temperature to achieve the adhesion of the three layers forming the complex 1.
A ce sujet, la pellicule de colle 4 qui a été déposée sur le film plastifié 2, du fait de la perméabilité de l'armature intermédiaire 5, permet l'accrochage efficace des trois composants. In this regard, the adhesive film 4 which has been deposited on the plastic film 2, due to the permeability of the intermediate frame 5, allows the effective attachment of the three components.
De plus, la colle étant colorée et le film plastifié transparent, on obtient une coloration du complexe 1 vu du recto du complexe.In addition, the glue being colored and the plastic film transparent, a coloration of the complex 1 is obtained seen from the front of the complex.
A titre d'exemple non limitatif, de bons résultats ont été obtenus par la mise en oeuvre suivante
Complexe papier peint coloré orange - 34,3 kg de colle composée de : 20 kg de colle époxy
2 kg de poly-isocyanate
10 kg de diluant
1,65 kg encre fluide jaune HA37653
0,450kg jaune HA35125
0,200kg rouge HA35126 34,300ka - Papier couché brillant 1 face 90 g - Armature polypropyléne-polyamide à maille rectangulaire épaisseur
0,1 mm, poids 8 gain2 - 2.0 g de colle par m de papier - Film polypropylène épaisseur : 12 p - Pression calandre : 1,5 t - Température calandre : 45 'C
Naturellement, d'autres mises en oeuvre de la présente invention en particulier des produits de substitution connus de l Homme de l'Art pourraient etre utilisées sans pour autant sortir du cadre de la présente invention.By way of nonlimiting example, good results have been obtained by the following implementation
Complex orange colored wallpaper - 34.3 kg of glue composed of: 20 kg of epoxy glue
2 kg of poly-isocyanate
10 kg of thinner
1.65 kg HA37653 yellow fluid ink
0.450kg yellow HA35125
0,200kg red HA35126 34,300ka - Glossy coated paper 1 side 90 g - Polypropylene-polyamide frame with rectangular mesh thickness
0.1 mm, weight 8 gain2 - 2.0 g of glue per m of paper - Polypropylene film thickness: 12 p - Calender pressure: 1.5 t - Calender temperature: 45 'C
Naturally, other implementations of the present invention, in particular substitution products known to those skilled in the art, could be used without departing from the scope of the present invention.
Les caractéristiques de la présente invention qui viennent d'être décrites permettent d'obtenir un complexe coloré décoratif très intéressant pour une utilisation papier peint. The characteristics of the present invention which have just been described make it possible to obtain a very attractive decorative color complex for use as wallpaper.
En effet, on obtient un complexe de résistance mécanique élevée, indéchirable, lavable, teint à volonté. De plus, l'armature tramée provoque des reflets de moirage. Indeed, we obtain a complex of high mechanical resistance, tear-resistant, washable, dyed at will. In addition, the screened frame causes moire reflections.
En outre, la structure du complexe "sandwich" : feuille papier support - armature tramée polypropyléne - film plastifié, procure d'autres avantages intéressants dans le cas du papier peint. In addition, the structure of the "sandwich" complex: support paper sheet - screened polypropylene frame - plasticized film, provides other advantageous advantages in the case of wallpaper.
En effet, le complexe présente un pouvoir d'absorption de l'humidité grâce à la feuille support papier et à l'armature polypropyléne. De plus, au moment de la pose du papier peint sur la paroi à recouvrir, la colle enduite sur le verso du papier peint profite de la structure de l'armature intermédiaire pour autoriser un meilleur accrochage du papier peint sur la paroi.Indeed, the complex has a power to absorb moisture thanks to the paper backing sheet and the polypropylene frame. In addition, when laying the wallpaper on the wall to be covered, the glue coated on the back of the wallpaper takes advantage of the structure of the intermediate frame to allow better hanging of the wallpaper on the wall.
Enfin, pour obtenir des effets décoratifs supplémentaires, il pourrait être envisagé que la face externe du film plastifié 2 soit préalablement imprimée. Finally, to obtain additional decorative effects, it could be envisaged that the external face of the plasticized film 2 is previously printed.
Toutefois, l'application du complexe de la présente invention, bien qu'avantageuse dans le domaine du papier peint, n'est nullement limitée à celui-ci et on pourra également se servir du complexe coloré de la présente invention comme papier d'emballage, ou pour confectionner certains vêtements, banderoles ou calicots de signalisation. However, the application of the complex of the present invention, although advantageous in the field of wallpaper, is by no means limited thereto and the colored complex of the present invention can also be used as wrapping paper , or to make certain garments, banners or signal banners.
Claims (7)