FR2576013A1 - Composition for the production of coatings - Google Patents

Composition for the production of coatings Download PDF

Info

Publication number
FR2576013A1
FR2576013A1 FR8500521A FR8500521A FR2576013A1 FR 2576013 A1 FR2576013 A1 FR 2576013A1 FR 8500521 A FR8500521 A FR 8500521A FR 8500521 A FR8500521 A FR 8500521A FR 2576013 A1 FR2576013 A1 FR 2576013A1
Authority
FR
France
Prior art keywords
liquid
composition according
potassium
weight
sodium
Prior art date
Legal status (The legal status is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the status listed.)
Granted
Application number
FR8500521A
Other languages
French (fr)
Other versions
FR2576013B1 (en
Inventor
Jean Rivoallon
Current Assignee (The listed assignees may be inaccurate. Google has not performed a legal analysis and makes no representation or warranty as to the accuracy of the list.)
Sanofi Aventis France
Original Assignee
Francaise Hoechst Ste
Priority date (The priority date is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the date listed.)
Filing date
Publication date
Application filed by Francaise Hoechst Ste filed Critical Francaise Hoechst Ste
Priority to FR8500521A priority Critical patent/FR2576013B1/en
Priority to AT85400156T priority patent/ATE31293T1/en
Priority to EP19850400156 priority patent/EP0158541B1/en
Priority to DE8585400156T priority patent/DE3561148D1/en
Priority to US06/698,537 priority patent/US4586959A/en
Priority to DK51085A priority patent/DK159877C/en
Priority to ES540140A priority patent/ES8606221A1/en
Publication of FR2576013A1 publication Critical patent/FR2576013A1/en
Application granted granted Critical
Publication of FR2576013B1 publication Critical patent/FR2576013B1/en
Anticipated expiration legal-status Critical
Expired - Lifetime legal-status Critical Current

Abstract

Composition for the production of a coating based on rock wool A, characterised in that it comprises: 1 - at least one powdered product B containing at least 30 % by weight of potassium bicarbonate, the remainder comprising sulphamic acid and optionally sodium bicarbonate; and 2 - at least one aqueous solution C of sodium or potassium silicate.

Description

La présente invention concerne une composition destinée à la confection de revêtements. The present invention relates to a composition for making coatings.

Actuellement on connait des -revetements isolants, insonores et ignifuges. réalisés par projection, au moyen d'une lance adéquate, d'un mélange aqueux de laine de roche avec, soit du ciment, soit du silicate de sodium ou de potassium, du bicarbonate de sodium ou de potassium et du chlorure de calcium (demande de brevet français N' 84.01764). Currently we know of insulating, soundproof and flame retardant coatings. made by spraying, using a suitable lance, an aqueous mixture of rock wool with either cement or sodium or potassium silicate, sodium or potassium bicarbonate and calcium chloride (request French Patent No. 84.01764).

Toutefois, de tels revêtements, notamment les revêtements contenant du chlorure de calcium ne peuvent que difficilement être appliqués sur des supports contenant du fer. Ouant aux revêtements liés avec du ciment, ils présentent un temps de prise de quelques heures ; de ce fait, ils nécessitent, très souvent, surtout pour des épaisseurs importantes, la présence de treillis métalliques de soutien. However, such coatings, in particular coatings containing calcium chloride, can only be applied with difficulty to supports containing iron. Like coatings bonded with cement, they have a setting time of a few hours; therefore, they very often require, especially for large thicknesses, the presence of supporting metal mesh.

Or, la Demanderesse a découvert de façon tout à fait inattendue, une composition à base de laine de roche et de silicates d'au moins un métal alcalin, susceptible de remédier à ces inconvénients. However, the Applicant has discovered, quite unexpectedly, a composition based on rock wool and silicates of at least one alkali metal, capable of remedying these drawbacks.

Elle permet la confection aisée de revêtements isolants, insonores et ignifuges présentant, en outre, des caractéristiques physiques améliorées, leur conférant notamment une vitesse de prise rapide, et une faible densité.It allows the easy manufacture of insulating, soundproof and flame retardant coatings having, in addition, improved physical characteristics, giving them in particular a rapid setting speed, and a low density.

La composition selon l'invention est essentiellement caractérisée par le fait qu'elle comprend, en combinaison avec ladite laine de roche, désignée ci-après A, les composés suivants : (1) au moins un produit en poudre, désigné ci-après B et renfermant au moins 30 X en poids de bicarbonate de potassium, le reste comprenant de l'acide sulfamique et, éventuellement, du bicarbonate de sodium et (2) au moins une solution aqueuse, désignée ci-après C, de silicate de sodium ou de potassium.  The composition according to the invention is essentially characterized in that it comprises, in combination with said rock wool, hereinafter designated A, the following compounds: (1) at least one powdered product, hereinafter designated B and containing at least 30% by weight of potassium bicarbonate, the remainder comprising sulfamic acid and, optionally, sodium bicarbonate and (2) at least one aqueous solution, hereinafter designated C, of sodium silicate or potassium.

La composition selon l'invention est préparée juste avant l'emploi, par mélange intime des trois produits A, 8 et C. Le produit A est de la laine de roche à fibres longues couramment commercialisée pour cette application ; habituellement, les fibres ont un diamètre de 4 à 6 micromètres et une longueur de 1 à 2 centimètres. The composition according to the invention is prepared just before use, by intimate mixing of the three products A, 8 and C. Product A is rock wool with long fibers commonly sold for this application; usually the fibers have a diameter of 4 to 6 micrometers and a length of 1 to 2 centimeters.

Le produit B est une poudre, contenant pondéralement :
- de 30 à 98 Z de bicarbonate de potassium.Product B is a powder, containing by weight:
- from 30 to 98% of potassium bicarbonate.

- de 2 à 10 Z d'acide sulfamique,
- et, si nécessaire, le complément à 100 Z de bicarbonate de sodium.- from 2 to 10% of sulfamic acid,
- and, if necessary, the supplement to 100 Z of sodium bicarbonate.

Le produit C est un liquide contenant
- de 0 à 40 Z- d'eau,
- de 100 à 60 Z d'un mélange de 0 à 100 Z, avantageusement de 60 à 80 Z de silicate de sodium liquide commercial, de rapport pondéral SiO2/Na20 compris entre 1,60 et 3,35, de rapport moléculaire compris entre 1,65 et 3,*5 et contenant 60 + 10 Z en poids d'eau, et de 100 à 0 Z, avantageusement de 40 à 20Z de silicate de potassium liquide commercial, de rapport pondéral SiO2/K20 compris entre 1,8 et 2,6 et de rapport moléculaire compris entre 2,85 et 4.1 et contenant 70 + 10 Z en poids d'eau.Product C is a liquid containing
- from 0 to 40 Z- of water,
- from 100 to 60 Z of a mixture of 0 to 100 Z, advantageously from 60 to 80 Z of commercial liquid sodium silicate, of SiO2 / Na20 weight ratio between 1.60 and 3.35, of molecular ratio between 1.65 and 3, * 5 and containing 60 + 10 Z by weight of water, and from 100 to 0 Z, advantageously from 40 to 20Z of commercial liquid potassium silicate, of SiO2 / K20 weight ratio of between 1.8 and 2.6 and of molecular ratio between 2.85 and 4.1 and containing 70 + 10 Z by weight of water.

Dans un mode de réalisation préféré de l'invention, le produit B renferme pondéralement de 35 à 60 Z de bicarbonate de potassium, de 60 à 35 Z de bicarbonate de sodium et de 5 à 7 Z d'acide sulfamique et le produit C renferme pondéralement de 0 à 40 Z d'eau et de 100 à 60 Z d'un mélange
- de 60 à 80 Z de silicate de sodium liquide commercial, de rapport pondéral SiO2/Na20 3,35, de rapport moléculaire 3,45 et contenant 65 + 4 Z d'eau, désigné ci-après "silicate de sodium liquide NA et de 40 à 20 Z de silicate de potassium liquide, de rapport pondéral SiO2/K2O 2,6 de rapport moléculaire d'environ 4 et contenant 75 t 4 Z d'eau, désigné ci-après "silicate-de potassium liquide KA/O". In a preferred embodiment of the invention, the product B contains by weight from 35 to 60 Z of potassium bicarbonate, from 60 to 35 Z of sodium bicarbonate and from 5 to 7 Z of sulfamic acid and the product C contains by weight from 0 to 40 Z of water and from 100 to 60 Z of a mixture
- from 60 to 80% of commercial liquid sodium silicate, of SiO2 / Na20 weight ratio 3.35, of molecular ratio 3.45 and containing 65 + 4% of water, hereinafter referred to as "liquid sodium silicate NA and from 40 to 20 Z of liquid potassium silicate, of SiO2 / K2O weight ratio 2.6 of molecular ratio of about 4 and containing 75 t 4 Z of water, hereinafter referred to as "potassium potassium silicate KA / O ".

La composition selon l'invention contient en proportions pondérales
- de 30 à 65 X de produit A.The composition according to the invention contains in weight proportions
- from 30 to 65 X of product A.

- de 3 à 10 Z deproduit 8 et,
- de 25 à 60 Z de produit C.- from 3 to 10 Z of product 8 and,
- from 25 to 60 Z of product C.

La composition préférée selon l'invention contient en proportions pondérales de 40 à 65 Z de produit A, de 4 à 6 Z de produit B et de 30 à 55 X de produit- C.The preferred composition according to the invention contains in weight proportions from 40 to 65% of product A, from 4 to 6% of product B and from 30 to 55% of product- C.

C'est ainsi qu'une composition tout particulièrement préférée peut être l'une des deux compositions données ci-après à titre d'exemple et désignées première et deuxième composition. Thus, a very particularly preferred composition can be one of the two compositions given below by way of example and designated first and second composition.

La composition selon l'invention présente un temps de prise quasi instantané. De ce fait, elle est préparée extemporanément par mélange des produits A, 9 et C dans le cône d'éjection d'une lance à projection couramment utilisée par l'homme de métier pour réaliser des revêtements à base de laine de roche et de ciment. The composition according to the invention has an almost instant setting time. Therefore, it is prepared extemporaneously by mixing products A, 9 and C in the ejection cone of a spray lance commonly used by those skilled in the art to produce coatings based on rock wool and cement. .

Cette lance est alimentée en produits A, B et
C par des mayens connus. Ainsi, les produits A et B, solides, seuls ou en mélange, sont mis en suspension puis propulsés Vers la buse centrale de la lance par de l'air comprimé. Quant au produit C, liquide, il est acheminé vers la lance, sous pression, gråce à une pompe puis il est éjecté par des buses latérales réparties à la périphérie de la buse centrale. La composition selon l'invention est ainsi obtenue au cours de sa projection sur les parois à enduire.Grâce à son temps de prise très rapide, la composition se fixe sur la paroi quelle que soit sa pente, aussi bieh sur des parois verticales que sur des plafonds, sans produire des coulures et/ou des décrochements et ceci, jusqu'à des épaisseurs de dépôts de 100 millimètres, tout en laissant la possibilité à l'homme de métier expérimenté de la travailler pendant quelques minutes à la truelle ou à la taloche de maniere à ameliorer la présentation du revêtement ainsi obtenu.This lance is supplied with products A, B and
C by known mayens. Thus, the products A and B, solid, alone or in mixture, are suspended and then propelled towards the central nozzle of the lance by compressed air. As for product C, liquid, it is conveyed to the lance, under pressure, thanks to a pump then it is ejected by lateral nozzles distributed around the periphery of the central nozzle. The composition according to the invention is thus obtained during its projection on the walls to be coated. Thanks to its very fast setting time, the composition is fixed on the wall whatever its slope, as bieh on vertical walls as on ceilings, without producing drips and / or indentations and this, up to thicknesses of deposits of 100 millimeters, while leaving the possibility for the skilled tradesman to work it for a few minutes with a trowel or float so as to improve the presentation of the coating thus obtained.

En outre, le temps de prise quasi instantané de la composition selon 1 invention ne permet pas à l'air occlus dans le revêtement de s'échapper. En effet, lorsque la composition selon l'invention est projetée sur la paroi pour former un revêtement, un certain volume d'air est piégé. De ce fait, on obtient un revêtement très poreux de faible densité, de l'ordre de 130 # 15 kg au m nettement inférieure à la densité de
3 250 + 25 kg au m des revêtements connus à base de laine de roche et de ciment.In addition, the almost instantaneous setting time of the composition according to the invention does not allow the air occluded in the coating to escape. When the composition according to the invention is sprayed onto the wall to form a coating, a certain volume of air is trapped. As a result, a very porous coating of low density is obtained, of the order of 130 # 15 kg per m much lower than the density of
3,250 + 25 kg per m of known coatings based on rock wool and cement.

En raison de leur faible densité et de leur structure poreuse, les revêtements obtenus avec la composition selon l'invention présentent d'excellentes propriétés isolantes et ignifuges et ils peuvent être appliqués aisément, en une seule panse, jusqu'à des épaisseurs de 10 cm sur des parois de pente très diverses, aussi bien verticales que horizontales du type plafond. Due to their low density and their porous structure, the coatings obtained with the composition according to the invention have excellent insulating and flame retardant properties and they can be applied easily, in a single layer, up to thicknesses of 10 cm. on walls of very different slopes, both vertical and horizontal of the ceiling type.

A titre indicatif, on donnera ci-apres deux compositions selon l'invention permettant d'obtenir 1 m environ d'un revêtement de 10 cm d'épaisseur, soit 0,10m3.  As an indication, two compositions according to the invention will be given below, making it possible to obtain approximately 1 m of a coating 10 cm thick, or 0.10 m 3.

Première comoosition
- 10 kg {55,5 Z) de laine de roche à fibres longues. de diamètre de 4 à 6 micromêtres et de 5 à 6 cm de longueur,
- 0,6 kg (3,33 Z) de bicarbonate de potassium.First combination
- 10 kg (55.5 Z) of rock wool with long fibers. 4 to 6 micrometers in diameter and 5 to 6 cm in length,
- 0.6 kg (3.33 Z) of potassium bicarbonate.

- 0,35 kg (1,95 Zl de bicarbonate de sodium,
- 0,05 kg (0,27 Z) d'acide sulfamique,
- 4,75 kg (26,4 Z) de silicate de sodium liquide Na 4/1,
- 2,25 kg (12,5 Z) de silicate de potassium liquide KAPO. - 0.35 kg (1.95 Zl of sodium bicarbonate,
- 0.05 kg (0.27 Z) of sulfamic acid,
- 4.75 kg (26.4 Z) of liquid sodium silicate Na 4/1,
- 2.25 kg (12.5 Z) of KAPO liquid potassium silicate.

Seconde composition
- 10 kg (47,62 %) de laine de roche à fibres longues de diamètre de 4 à 6 micromètres et de 5 à 6 cm de longueur,
- 0,6 kg t2,86 Z) de bicarbonate de potassium.Second composition
- 10 kg (47.62%) of long fiber rock wool with a diameter of 4 to 6 micrometers and a length of 5 to 6 cm,
- 0.6 kg t2.86 Z) of potassium bicarbonate.

- 0,35 kg (1,66 X) de bicarbonate de sodium,
- 0,05 kg (0,24 Z) d'acide sulfamique,
- 3 kg (14,28 %) d'eau,
- 4,75 kg (22,62 X) de silicate de sodium liquide Na 4/1,
- 2,25 kg (10,71 X) de silicate de potassium liquide KA/O.- 0.35 kg (1.66 X) of sodium bicarbonate,
- 0.05 kg (0.24 Z) of sulfamic acid,
- 3 kg (14.28%) of water,
- 4.75 kg (22.62 X) of liquid sodium silicate Na 4/1,
- 2.25 kg (10.71 X) of KA / O liquid potassium silicate.

il va de soi que la présente invention n'a été décrite qu'à titre purement explicatif et nullement limitatif et que toute modification pourra y être apportée sans sortir de son cadre.  It goes without saying that the present invention has been described for purely explanatory and in no way limitative and that any modification may be made without departing from its scope.

Claims (6)

REVENDICATIONS 1. Composition destinée à la confection de revêtement base de laine de roche (A), caractérisée en ce qu'elle comprend (1) au moins un produit (B) en poudre renfermant, au moins, 30 Z en poids de bicarbonate de potassium, le reste comprenant. de l'acide sulfamique et, éventuellement, du bicarbonate de sodium et (2) au moins une solution aqueuse (C) de silicate de sodium ou de potassium. 1. Composition intended for making a coating of rock wool base (A), characterized in that it comprises (1) at least one product (B) in powder containing, at least, 30 Z by weight of potassium bicarbonate , the rest including. sulfamic acid and, optionally, sodium bicarbonate and (2) at least one aqueous solution (C) of sodium or potassium silicate. 2. Composition selon la revendication 1, caractérisée en ce qu'elle comprend, environ, en poids 2. Composition according to claim 1, characterized in that it comprises, approximately, by weight - de 30 à 65 Z de laine de roche A. - from 30 to 65 Z of rock wool A. de 100 à 60 Z d'un mélange de 0 à 100 X de silicate de sodium liquide commercial et de 100 à 0 Z de silicate de- potassium liquide commercial. from 100 to 60% of a mixture of 0 to 100% of commercial liquid sodium silicate and from 100 to 0% of commercial liquid potassium silicate. de 0 à 40 Z d'eau, from 0 to 40 Z of water, - de 25 à 60 Z d'un liquide aqueux, C, constitué - from 25 to 60% of an aqueous liquid, C, consisting et, si nécessaire, le complément à 100 X de bicarbonate de sodium and, if necessary, the supplement to 100 X of sodium bicarbonate de 2 à 10 Z d'acide sulfamique, from 2 to 10% of sulfamic acid, de 30 à 98 Z de bicarbonate de potassium, from 30 to 98% of potassium bicarbonate, - de 3 à 10 Z d'un produit B, en poudre, constitué - from 3 to 10 Z of product B, powder, consisting SiO2 /NaO de 3,35 un rapport moléculaire de 3,45 et un taux d'eau de 65 + 4 Z.SiO2 / NaO of 3.35 a molecular ratio of 3.45 and a water level of 65 + 4 Z. 3. Composition selon la revendication 2, caractérisée par le fait que le silicate de sodium liquide utilisé présente un rapport pondéral de 3. Composition according to claim 2, characterized in that the liquid sodium silicate used has a weight ratio of 4 Composition selon la revendication 2, caractérisée par le fait que le silicate de potassium liquide utilisé présente un rapport pondéral SiO2/K20 de 2,6, un rapport moléculaire d'environ 4 et un taux d'eau de 75 f 4 Z.  4 Composition according to Claim 2, characterized in that the liquid potassium silicate used has a SiO2 / K20 weight ratio of 2.6, a molecular ratio of approximately 4 and a water content of 75 f 4 Z. 5. Composition selon la revendication 1, caractérisée par le fait qu'elle renferme pondéralement: 5. Composition according to claim 1, characterized in that it contains by weight: - de 35 à 60 Z de laine de roche A - from 35 to 60 Z of rock wool A - de 3,5 à 6 Z de produit en poudre 6 constitué - from 3.5 to 6% of powdered product 6 made up de 60 à 35 X de bicarbonate de potassium, from 60 to 35 X of potassium bicarbonate, u de 35 à 64 Z de bicarbonate de sodium, u from 35 to 64 Z of sodium bicarbonate, de 5 à 7 Z d'acide sulfamique 5 to 7% sulfamic acid - de 35 à 60 Z d'un liquide aqueux, C, constitué - from 35 to 60% of an aqueous liquid, C, consisting de 0 à 40 Z d'eau, from 0 to 40 Z of water, de 100 à 60 % d'un mélange constitué de from 100 to 60% of a mixture consisting of de 60 à 80 Z de silicate de sodium liquide tel que défini à la revendication 3, from 60 to 80% of liquid sodium silicate as defined in claim 3, de 40 à 20 Z de silicate de potassium liquide tel que défini à la revendication 4. from 40 to 20% of liquid potassium silicate as defined in claim 4. 6. Application de la composition selon l'une quelconque des revendications 1 à 5, à la confection de revêtements isolants, insonores et ignifuges.  6. Application of the composition according to any one of claims 1 to 5, in the manufacture of insulating, soundproof and flame retardant coatings.
FR8500521A 1984-02-06 1985-01-15 COMPOSITION FOR THE MANUFACTURE OF COATINGS Expired - Lifetime FR2576013B1 (en)