FR2528060A1 - Sealing compsn. comprising hydrophilic polymer and poly:ol - used to seal sliding contact sections in aerosol containers - Google Patents

Sealing compsn. comprising hydrophilic polymer and poly:ol - used to seal sliding contact sections in aerosol containers Download PDF

Info

Publication number
FR2528060A1
FR2528060A1 FR8309240A FR8309240A FR2528060A1 FR 2528060 A1 FR2528060 A1 FR 2528060A1 FR 8309240 A FR8309240 A FR 8309240A FR 8309240 A FR8309240 A FR 8309240A FR 2528060 A1 FR2528060 A1 FR 2528060A1
Authority
FR
France
Prior art keywords
composition according
gum
polymer
sliding contact
polyol
Prior art date
Legal status (The legal status is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the status listed.)
Granted
Application number
FR8309240A
Other languages
French (fr)
Other versions
FR2528060B1 (en
Inventor
Toshio Miyake
Katsumi Hirao
Current Assignee (The listed assignees may be inaccurate. Google has not performed a legal analysis and makes no representation or warranty as to the accuracy of the list.)
Hayashibara Seibutsu Kagaku Kenkyujo KK
Original Assignee
Hayashibara Seibutsu Kagaku Kenkyujo KK
Hayashibara Biochemical Laboratories Co Ltd
Priority date (The priority date is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the date listed.)
Filing date
Publication date
Application filed by Hayashibara Seibutsu Kagaku Kenkyujo KK, Hayashibara Biochemical Laboratories Co Ltd filed Critical Hayashibara Seibutsu Kagaku Kenkyujo KK
Priority to FR8309240A priority Critical patent/FR2528060B1/en
Publication of FR2528060A1 publication Critical patent/FR2528060A1/en
Application granted granted Critical
Publication of FR2528060B1 publication Critical patent/FR2528060B1/en
Expired legal-status Critical Current

Abstract

The compsn. (I) comprises 1 pt.wt. hydrophilic organic polymer (II) and 5-20 pts.wt. polyol (III). Pref. (II) has average mol.wt. 10000-10000000, and is polyethylene oxide, polyvinyl alcohol, polyvinylpyrrolidone, and partic. water-sol. polysaccharide esp. pullulan, elsinan, dextran, laevan, mannan, gum arabic, gum tragacanth, guar gum, xanthan gum, Carraginan, pectin, hydroxyethylstarch, carboxymethylcellulose, hydroxyethyl cellulose, or mixts. thereof. No. of C atoms and OH gps. per mol. in (III) is 2-20; partic. (III) is one or more of ethylene glycol, propylene glycol, glycerol, erythritol, xylitol, sorbitol, mannitol, maltitol, isomaltitol, lactitol, starch, hydrogenated starch, starch sugar, hydrogenated starch sugar, and polyglycerol. (I) also contains water, partic. 0.05-20 pts.wt. per pt. wt. (II), and/or a surfactant partic. nonionic or anionic. Surfactant may be alkali metal salt, sulphosuccinate, sorbitan ester, monoglyceride, or sugar ester of a fatty acid, or mixt. of these. Esp. (I) contains 10-100 pts.wt. (III) per pt.wt. (II). For preventing escape of liqs. or compressed gases through sliding contact sections in aerosol containers described in Japanese utility model patent No. 1474/70, also microcompressors. (I) is stable over prolonged usage, unlike silicone rubbers, has high sealing efficiency, and is nontoxic.

Description

La présente invention concerne une composition pour assurer l'étanchéité dans une zone de contact de glissement, plus particulièrement pour empêcher la fuite d'un gaz liquéfié ou comprimé par une telle zone. The present invention relates to a composition for sealing in a sliding contact zone, more particularly for preventing the leakage of a liquefied or compressed gas from such a zone.

Pour étancher des zones de contact de coulissement, on utilise en général des joints mécaniques et de l'huile. Cependant, il est très difficile de sceller par ces moyens un gaz liquéfié ou comprimé. To seal sliding contact areas, mechanical seals and oil are generally used. However, it is very difficult to seal by this means a liquefied or compressed gas.

Par exemple, dans le cas d'un réservoir à aérosol tel que décrit dans la publication d'utilité japonaise ne1474/70, un piston mobile est placé à l'intérieur pour séparer la zone du gaz liquéfié de celle du produit. Lorsque le piston va et vient dans le réservoir, le gaz de propulsion liquéfié s'écoule dans la zone du produit au travers de la zone de contact de glissement, c'est-d-dire par une ouverture étroite entre le piston et la paroi interne du réservoir. Afin d'arr8ter cette fuite, on a proposé d'utiliser, comme agent d'obturation, de la gomme de silicone. Cependant, l'utilisation de la gomme de silicone procure une tanchéité insuffisante et présente un inconvénient supplémentaire du fait que cette gomme ne tolère pas une utilisation de longue durée car elle s'abîme rapidement.Comme aucune autre composition d'étanchement,qui puisse remplacer la gomme de silicone, n'a été trouvée à ce jour, le réservoir à aérosol est toujours réalisé comme susindiqué.For example, in the case of an aerosol tank as described in the Japanese utility publication ne1474 / 70, a movable piston is placed inside to separate the zone of the liquefied gas from that of the product. When the piston comes and goes in the tank, the liquefied propellant gas flows into the product area through the sliding contact area, i.e. through a narrow opening between the piston and the wall internal tank. In order to stop this leak, it has been proposed to use, as a sealing agent, silicone gum. However, the use of silicone gum provides insufficient sealing and has an additional disadvantage that this gum does not tolerate long-term use because it deteriorates quickly. Like no other sealing composition which can replace silicone gum, has not been found to date, the aerosol container is still made as indicated above.

Il existe donc un besoin impérieux d'avoir une composition d'obturation beaucoup plus efficace, pour empêcher de telles fuites. There is therefore an urgent need to have a much more effective sealing composition, to prevent such leaks.

La présente invention permet d'éviter ces inconvénients de l'art antérieur et d'obtenir une composition d'étanchement d'une zone de contact de glissement, qui empêche la fuite d'un gaz de propulsion liquéfié ou comprimé, est utilisable dans un réservoir à aérosol, à température relativement basse, et fonctionne pendant une longue durée, tout en étant non toxique et sans danger pour l'utilisation à usages domestiques.  The present invention makes it possible to avoid these drawbacks of the prior art and to obtain a composition for sealing a sliding contact zone, which prevents the leakage of a liquefied or compressed propellant gas, can be used in a aerosol container, relatively low temperature, and works for a long time, while being non-toxic and safe for use for domestic purposes.

La nouvelle composition selon l'invention est caractérisée en ce qu'elle comprend 1 partie en poids d' un polymère organique hydrophile et 5 à 200 parties en poids d'un polyol. Par la suite, chaque fois qu'il est question de "partie", il s'agit de partie en poids. The new composition according to the invention is characterized in that it comprises 1 part by weight of a hydrophilic organic polymer and 5 to 200 parts by weight of a polyol. Thereafter, each time it is a question of "part", it is a part by weight.

Pour aboutir à ce résultat, les demanderesses ont étudié et expérimenté un certain nombre de compositions susceptibles d'empêcher la fuite du gaz liquéfié, ou comprimé, par la zone de contact de glissement ; ces compositions satisfont aux exigences suivantes. To achieve this result, the applicants have studied and tested a certain number of compositions capable of preventing the leakage of the liquefied or compressed gas through the sliding contact zone; these compositions meet the following requirements.

(1) Posséder une élasticité et une viscosité appro
priées.(1) Possess elasticity and viscosity appr
prayed.

(2) Adhérer uniformément à la totalité de la zone de
contact de glissement, de manière à assurer une
obturation parfaite.(2) Adhere evenly to the entire area of
sliding contact, so as to ensure
perfect shutter.

(3) Posséder une fluidité suffisante pour satisfaire
à l'exigence (2), même lorsque la zone de contact
de glissement en soi se déplace, comme c'est le
cas lorsque le piston est en mouvement de va-et
vient.(3) Have sufficient fluidity to satisfy
to requirement (2), even when the contact area
of slip in itself moves, as is the
case when the piston is back and forth
come.

(4) Etre insoluble dans le gaz de propulsion liquéfié,
utilisé.(4) Be insoluble in liquefied propellant gas,
used.

(5) Ne pas modifier ou altérer le produit, lorsqu'el
les viennent en contact avec le produit et/ou le
gaz liquéfié, comme c'est le cas dans un réservoir
à aérosol.(5) Do not modify or alter the product, when it
come in contact with the product and / or the
liquefied gas, as is the case in a tank
aerosol.

(6) Satisfaire à toutes les exigences de (1) à (5) aux
températures ambiantes, ctest-à-dire entre environ
0 et 450C, et conserver longtemps ces propriétés,
notamment jusqu'à 6 mois, et de préférence au
delà de 2 ans.(6) Meet all the requirements of (1) to (5)
ambient temperatures, i.e. between approximately
0 and 450C, and keep these properties for a long time,
especially up to 6 months, and preferably at
beyond 2 years.

(7) Etre, si possible, non toxique et sans danger du
fait de la possibilité d'une mise en contact avec
le corps humain ou d'une pénétration à l'intérieur
de celui-ci. (7) Be, if possible, non-toxic and harmless from
made the possibility of putting in contact with
the human body or a penetration inside
of it.

Ainsi qu'il a été dit plus haut, ces efforts ont abouti à la con-statation qu'une composition renfermant 1 partie de polymère organique hydrophile et 5 à 200 parties d'un polyol, satisfait à ces exigences. As mentioned above, these efforts have led to the conclusion that a composition containing 1 part of hydrophilic organic polymer and 5 to 200 parts of a polyol, satisfies these requirements.

Conviennent comme polymères organiques hydrophiles, conformément à l'invention, outre des polymères synthétiques, tels qu'oxyde de polyéthylène, alcool polyvinylique et polyvinyl pyrrolidone, et de préférence, des po polymères naturels et leurs dérivés, y compris des polysaccharides hydrosolubles,notamment pullulane, elsinane, dextrane, lévane, mannane, gomme arabique, gomme adragante, gomme guar, gomme xanthane, carrageenane, substance pectique, hydroxyéthyl amidon, carboxyméthyl cellulose et hydro xyéthyl cellulose. Est plus particulièrement recommandée l'utilisation de pullulane et d'elsinane, composés principalement d'unités répétées de maltotriose, parce qu'ils répondent beaucoup mieux aux exigences (1) à (7) ci-dessus. Suitable as hydrophilic organic polymers, in accordance with the invention, in addition to synthetic polymers, such as polyethylene oxide, polyvinyl alcohol and polyvinyl pyrrolidone, and preferably, natural po polymers and their derivatives, including water-soluble polysaccharides, in particular pullulan , elsinane, dextran, levane, mannan, gum arabic, tragacanth, guar gum, xanthan gum, carrageenan, pectic substance, hydroxyethyl starch, carboxymethyl cellulose and hydro xyethyl cellulose. More particularly recommended is the use of pullulan and elsinane, mainly composed of repeating units of maltotriose, because they respond much better to requirements (1) to (7) above.

La masse moléculaire moyenne de ces polymères est comprise dans l'intervalle de 10 000 à 10 000 000, de préférence de 20 000 à 2 000 000.The average molecular weight of these polymers is in the range of 10,000 to 10,000,000, preferably 20,000 to 2,000,000.

Les polyols, utilisables conformément à l'invention, sont ceux qui présentent par molécule respectivement 2 à 20 atomes de carbone et de groupements hydroxyle,par exemple, éthylène glycol, propylène glycol, glycérine, érythritol, xylitol, sorbitol, mannitol, maltitol, isomaltitol, lactitol, sirop de mais, sirop de mais hydrogéné et poly-glycérine. The polyols which can be used in accordance with the invention are those which have 2 to 20 carbon atoms and hydroxyl groups per molecule, for example, ethylene glycol, propylene glycol, glycerin, erythritol, xylitol, sorbitol, mannitol, maltitol, isomaltitol. , lactitol, corn syrup, hydrogenated corn syrup and poly-glycerin.

En ce qui concerne le mode de préparation de la composition selon l'invention, on peut utiliser tout procédé dans lequel les proportions de 1 partie de polymère organique hydrophile pour 5 à 200, et de préférence 10 à 100, parties de polyol, sont respectées. En particulier, lorsque le polyol est un liquide non cristallin, par exemple éthylène glycol, propylène glycol ou glycérine, il peut être ajouté d'abord au polymère, puis le tout est homogénéisé par agitation et chauffage à une température généralement de l'ordre de 300 à 1600C. Lorsque le polyol est une poudre cristalline, par exemple xylitol, sorbitol ou maltitol, il peut être fondu par chauffage à une température supérieure à son point de fusion, ou dissous dans un polyol liquide mentionné plus haut.Autre possibilité, la poudre de polyol peut être d'abord dissoute dans de l'eau, et la solution résultante est ensuite homogénéisée avec le polymère organique hydrophile, comme dans le cas du polyol liquide ci-dessus. As regards the method of preparation of the composition according to the invention, any process can be used in which the proportions of 1 part of hydrophilic organic polymer for 5 to 200, and preferably 10 to 100, parts of polyol, are respected . In particular, when the polyol is a non-crystalline liquid, for example ethylene glycol, propylene glycol or glycerin, it can be added first to the polymer, then the whole is homogenized by stirring and heating to a temperature generally of the order of 300 to 1600C. When the polyol is a crystalline powder, for example xylitol, sorbitol or maltitol, it can be melted by heating to a temperature above its melting point, or dissolved in a liquid polyol mentioned above. Alternatively, the polyol powder can first be dissolved in water, and the resulting solution is then homogenized with the hydrophilic organic polymer, as in the case of the liquid polyol above.

L'utilisation de quantités appropriées d'eau et/ou d'agent tensio-actif, peut favoriser l'obtention d' une compositon d'étanchement ayant une homogénéité et une stabilité supérieures. En général, l'eau peut être utilisée pour accélérer la dissolution du polymère, régler la viscosité de la composition et dissoudre la poudre de polyol cristallin. La quantité préférée d'eau pour 1 partie de polymère se situe dans l'intervalle de 0,05 à 20 parties. The use of appropriate amounts of water and / or surfactant can promote the production of a sealant composition having superior homogeneity and stability. In general, water can be used to accelerate the dissolution of the polymer, adjust the viscosity of the composition and dissolve the crystalline polyol powder. The preferred amount of water per 1 part of polymer is in the range of 0.05 to 20 parts.

Conviennent comme agents tensio-actifs ceux qui dissolvent facilement à la fois le polymère et le polyol, et, de préférence, ceux qui sont non toxiques et sans danger. Les préférés sont les agents tensio-actifs non ioniques ou anioniques, par exemple les sels de métaux alcalins et sulfosuccinates d'acides gras supérieurs, ainsi que les esters de sorbitane, les monoglycérides et des esters de sucre d'acides gras. Suitable as surfactants are those which readily dissolve both the polymer and the polyol, and preferably those which are non-toxic and harmless. The preferred are nonionic or anionic surfactants, for example alkali metal salts and sulfosuccinates of higher fatty acids, as well as sorbitan esters, monoglycerides and sugar esters of fatty acids.

La composition ainsi obtenue satisfait aux exigences (1) à (7) , aussi peut-elle être favorablement utilisée comme agent d'obturation pour empêcher la fuite d'un gaz liquéfié ou comprimé,par la zone de contact de glissement, par exemple dans un réservoir à aérosol dans lequel est utilisé un gaz de propulsion liquéfié, un micro compresseur, une micro pompe ou un appareillage micro oléo hydraulique.  The composition thus obtained meets the requirements (1) to (7), so it can be favorably used as a sealant to prevent the escape of a liquefied or compressed gas, through the sliding contact zone, for example in an aerosol tank in which a liquefied propellant gas is used, a micro compressor, a micro pump or micro oleo hydraulic equipment.

Plusieurs formes de réalisation de l'invention non limitatives sont décrites ci-dessous. Several non-limiting embodiments of the invention are described below.

EXEMPLE 1
Un mélange de 6 parties de pullulane, de poids moléculaire re moyen de 200 000, 93,5 parties de glycérine et 0,5 partie d'ester de sucre, est homogénéisé par agitation et chauffage à 1100C. La viscosité relative de la composition résultante est de 84 à 102 poises à 400C, et de 920 à 1 140 poises à 120C.EXAMPLE 1
A mixture of 6 parts of pullulan, with an average molecular weight of 200,000, 93.5 parts of glycerin and 0.5 part of sugar ester, is homogenized by stirring and heating at 1100C. The relative viscosity of the resulting composition is from 84 to 102 poises at 400C, and from 920 to 1140 poises at 120C.

Cette composition peut être utilisée de façon avantageuse pour obturer la zone de contact de glissement d'un réservoir d'aérosol, dans lequel est utilisé un gaz de propulsion liquéfié.This composition can be advantageously used for sealing the sliding contact zone of an aerosol tank, in which a liquefied propellant gas is used.

Le maintien au repos cependant 6 mois de cette composition, à 450C, n'amène ni altération ni modification.Maintaining at rest, however, 6 months of this composition, at 450C, does not lead to any alteration or modification.

Cet exemple illustre une composition qui n'entraîne ni to xicité ni dommage pour l'homme ou les animaux ; aussi, la composition est-elle utilisable pour différents produits ménagers, dans lesquels un gaz liquéfié ou comprimé vient en contact avec la zone de glissement.This example illustrates a composition which does not cause toxicity or damage to humans or animals; also, the composition can be used for various household products, in which a liquefied or compressed gas comes into contact with the sliding zone.

EXEMPLE 2
On homogénéise par agitation et chauffage à 1200C, un mélange de 10 parties de pullulane, de poids moléculaire moyen = 100 000, et90 parties d'éthylène glycol.EXAMPLE 2
Homogenized by stirring and heating to 1200C, a mixture of 10 parts of pullulan, of average molecular weight = 100,000, and 90 parts of ethylene glycol.

Cette composition est également intéressante pour obturer la zone de contact de glissement, comme il est décrit dans l'exemple 1.This composition is also advantageous for sealing the sliding contact zone, as described in example 1.

EXEMPLE 3
Un mélange de 3 parties d'elsinane, de poids moléculaire moyen = 200 000, 54 parties de glycérine, 42,5 parties de poudre de sorbitol et 0,5 partie de sel de métal alcalin d'acide gras supérieur, est homogénéisé par agitation et chauffage à 1200C.EXAMPLE 3
A mixture of 3 parts of elsinane, of average molecular weight = 200,000, 54 parts of glycerin, 42.5 parts of sorbitol powder and 0.5 part of alkali metal salt of higher fatty acid, is homogenized by stirring and heating to 1200C.

Cette composition est aussi intéressante pour étancher la zone de contact de glissement, comme décrit dans l'exemple 1. This composition is also advantageous for sealing the sliding contact zone, as described in example 1.

EXEMPLE 4
On homogénéise par agitation et chauffage à 800C, un mélange de 5 parties d'elsinane, ayant un poids moléculaire moyen = 300 000, 3 parties d'eau, 52 parties d'éthylène glycol, 39,7 parties de poudre de maltitol, et 0,3 partie de monoglycéride d'acide gras.EXAMPLE 4
Homogenized by stirring and heating at 800C, a mixture of 5 parts of elsinane, having an average molecular weight = 300,000, 3 parts of water, 52 parts of ethylene glycol, 39.7 parts of maltitol powder, and 0.3 parts of fatty acid monoglyceride.

Cette composition s'avère également intéressante pour obturer la zonede contact de glissement, comme décrit dans l'exemple 1.This composition also proves to be advantageous for sealing the sliding contact area, as described in Example 1.

EXEMPLE 5
Une composition est préparée comme dans l'exemple 2, à ceci près que le pullulane est remplacé par de l'hydroxyéthyl amidon, de poids moléculaire moyen 100 000.EXAMPLE 5
A composition is prepared as in Example 2, except that the pullulan is replaced by hydroxyethyl starch, of average molecular weight 100,000.

Le pouvoir adhésif de cette composition est relativement inférieur à celui de la composition qui est décrite dans l'exemple 2, mais il est suffisant en vue de l'utilisation pratique comme composition d'obturation de la zone de contact de glissement.The adhesive power of this composition is relatively lower than that of the composition which is described in Example 2, but it is sufficient for practical use as a sealing composition for the sliding contact area.

EXEMPLE 6
On prépare une composition similaire à celle de l'exemple 4, mais en utilisant, au lieu dlelsinane, une gomme arabique ayant un poids moléculaire moyen de 300 000.EXAMPLE 6
A composition similar to that of Example 4 is prepared, but using, instead of elsinane, an arabic gum having an average molecular weight of 300,000.

Le pouvoir adhésif de cette composition est relativement inférieur à celui de la composition de l'exemple 4, mais il est suffisant en pratique pour l'étanchement de la zone de contact de glissement.The adhesive power of this composition is relatively lower than that of the composition of Example 4, but it is sufficient in practice for sealing the sliding contact zone.

EXEMPLE 7
Un mélange de 10 parties d'alcool polyvinylique, de masse moléculaire moyenne de 100 000, 60 parties de glycérine, 29,5 parties d'eau et 0,5 partie d'ester de sucre, est homogénéisé par agitation et chauffage à 300C.EXAMPLE 7
A mixture of 10 parts of polyvinyl alcohol, with an average molecular weight of 100,000, 60 parts of glycerin, 29.5 parts of water and 0.5 part of sugar ester, is homogenized by stirring and heating to 300C.

La stabilité à l'entreposage de cette composition est relativement faible, mais elle est en pratique suffisante pour son utilisation en vue de l'obturation de la zone de contact de glissement. The storage stability of this composition is relatively low, but it is in practice sufficient for its use with a view to sealing the sliding contact zone.

Il ressort de ce qui précède que la présente invention fournit une composition d'obturation pratique, pour arrêter la fuite d'un gaz liquéfié, ou comprimé, à travers la zone de contact de glissement d'un appareil dans lequel on utilise un tel gaz. It appears from the above that the present invention provides a practical sealing composition for stopping the leakage of a liquefied or compressed gas through the sliding contact area of an apparatus in which such a gas is used. .

Il est bien entendu que la description détaillée et les exemples particuliers, indiquant des formes de réalisation préférées de l'invention, ne sont donnés qu'à titre d'illustration ; différents changements et modifications possibles apparaitront à l'homme de l'art en partant de cette description détaillée, sans sortir du cadre de l'invention.  It is understood that the detailed description and the specific examples, indicating preferred embodiments of the invention, are given only by way of illustration; various changes and possible modifications will appear to those skilled in the art from this detailed description, without departing from the scope of the invention.

Claims (10)

RevendicationsClaims 1. Composition pour l'étanchement d'une zone de contact de glissement, caractérisée en ce qu'elle comprend 1 partie en poids d'un polymère organique hydrophile et 5 à 200 parties en poids d'un polyol. 1. Composition for sealing a sliding contact zone, characterized in that it comprises 1 part by weight of a hydrophilic organic polymer and 5 to 200 parts by weight of a polyol. 2. Composition selon la revendication 1, caractérisée en ce que la masse moléculaire moyenne du polymère est comprise entre 10 000 et 10 000 000, de préférence entre 20 000 et 2 000 000. 2. Composition according to claim 1, characterized in that the average molecular weight of the polymer is between 10,000 and 10,000,000, preferably between 20,000 and 2,000,000. 3. Composition selon la revendication 1 ou 2, caractérisée en ce que le polymère est un polysaccharide hydrosoluble. 3. Composition according to claim 1 or 2, characterized in that the polymer is a water-soluble polysaccharide. 4. Composition selon une des revendications 1 à 3, caractérisée en ce que le polymère est un oxyde de polyéthylène, alcool polyvinylique, polyvinyl pyrrolidone, pullulane, elsinane, dextrane, lévane, mannane, gomme arabique, gomme adragante, gomme guar, gomme xanthane, carrageenane, substance pectique, hydroxyéthyl amidon, carboxyméthyl cellulose, hydroxyéthyl cellulose, ou leurs mélanges. 4. Composition according to one of claims 1 to 3, characterized in that the polymer is a polyethylene oxide, polyvinyl alcohol, polyvinyl pyrrolidone, pullulan, elsinane, dextran, levane, mannan, gum arabic, gum tragacanth, gum guar, gum xanthan , carrageenan, pectic substance, hydroxyethyl starch, carboxymethyl cellulose, hydroxyethyl cellulose, or mixtures thereof. 5.Composition selon une des revendications 1 à 4, caractérisée en ce que dans le polyol, le nombre d'atomes de carbone et le nombre de groupements hydroxyle sont compris dans l'intervalle de 2 à 20. 5. Composition according to one of claims 1 to 4, characterized in that in the polyol, the number of carbon atoms and the number of hydroxyl groups are in the range from 2 to 20. 6. Composition selon une des revendications 1 à 5, caractérisée en ce que le polyol est éthylène glycol, propylène glycol, glycérine, erythritol, xylitol, sorbitol, mannitol, maltitol, isomaltitol, lactitol, sucre d'amidon, sucre d'amidon hydrogéné, poly-glycérine, ou leurs mélanges. 6. Composition according to one of claims 1 to 5, characterized in that the polyol is ethylene glycol, propylene glycol, glycerin, erythritol, xylitol, sorbitol, mannitol, maltitol, isomaltitol, lactitol, starch sugar, hydrogenated starch sugar , poly-glycerin, or mixtures thereof. 7. Composition selon une des revendications 1 à 6, caractérisée en ce qu'elle renferme en outre de 0,05 à 20 parties en poids d'eau pour 1 partie en poids de polymère. 7. Composition according to one of claims 1 to 6, characterized in that it additionally contains from 0.05 to 20 parts by weight of water per 1 part by weight of polymer. 8. Composition selon une des revendications 1 à 7, caractérisée en ce qu'elle renferme un agent tensio-actif, de préférence non ionique ou anionique, le mieux un sel de métal alcalin, un sulfosuccinate, un ester de sorbitane, un mono-glycéride ou un ester de sucre, d'acides gras, ainsi que leurs mélanges. 8. Composition according to one of claims 1 to 7, characterized in that it contains a surfactant, preferably nonionic or anionic, most preferably an alkali metal salt, a sulfosuccinate, a sorbitan ester, a mono- glyceride or an ester of sugar, fatty acids, as well as their mixtures. 9. Composition selon une des revendications 1 à 8, destinée à un réservoir à aérosol, en particulier un réservoir contenant un gaz de propulsion liquéfié ou comprimé. 9. Composition according to one of claims 1 to 8, intended for an aerosol tank, in particular a tank containing a liquefied or compressed propellant gas. 10. Procédé pour la préparation d'une composition selon une des revendications 1 à 9, qui consiste à homogénéiser le mélange de ses composantes par agitation et chauffage.  10. Process for the preparation of a composition according to one of claims 1 to 9, which consists in homogenizing the mixture of its components by stirring and heating.
FR8309240A 1983-06-03 1983-06-03 COMPOSITION FOR SEALING A SLIDING CONTACT AREA Expired FR2528060B1 (en)