FR2476067A1 - Hardened moulded porous clay block mfr. - by expanding in mould a clay paste contg. two reacting blowing agents, then hardening away from air

Info

Publication number: FR2476067A1
Application number: FR8003380A
Authority: FR
Inventors: Raymond Bois; Frederic Wagner; Guy Jallon
Original assignee: Individual
Current assignee: Individual
Priority date: 1980-02-15
Filing date: 1980-02-15
Publication date: 1981-08-21

Abstract

Method for fabricating a moulded block of cellular clay hardened without firing, comprises expanding in a mould an aq. clay paste by reacting in the paste at least two blowing agents which effect the blowing by reacting together, and hardening the expanded paste by means of a hardening agent dispersal in the paste. Specifically, particles of density below 1, of particle size 0.5-5 mm at least 50 % of which are 1-2 mm., and previously control with one of the blowing agents, are dispersed in the paste. The expansion can be maintained after the initial reaction without loss of expanded volume during hardening.

Description

L'invention concerne la fabrication d'un bloc moulé en argile cellulaire durcie sans cuisson. The invention relates to the manufacture of a molded block of hardened cellular clay without firing.

On connais différents procédés pour fabriquer des blocs d'argile durcis sans cuisson, le durcissement étant obtenu en incorporant à la pâte un agent approprié. Various processes are known for making blocks of hardened clay without baking, the hardening being obtained by incorporating into the paste an appropriate agent.

La présente invention vise également à la fabrication d'un bloc en argile durcie sans cuisson, mais elle concerne plus particulierement l'obtention d'un bldc en argile cellulaire. The present invention also relates to the manufacture of a block of hardened clay without firing, but it relates more particularly to the production of a bldc of cellular clay.

L'expansion d'une pâte d'argile, par réaction dans la pâte de deux agents de gonflement aptes à réagir l'un sur l'autre pour assurer le gonflement, est très rapide (par exemple, de l'ordre d'une minute) alors que le durcissement de cette pâte sous l'action d'un agent incorporé à la pâte demande plusieurs heures pendant lesquelles il faut maintenir la pâte à l'état gonflé, bien que la pâte a tendance à "retomber". The expansion of a clay paste, by reaction in the paste of two blowing agents capable of reacting one on the other to ensure swelling, is very rapid (for example, of the order of one minute) while the hardening of this dough under the action of an agent incorporated in the dough requires several hours during which it is necessary to keep the dough in the swollen state, although the dough tends to "drop".

La fabrication sans cuisson d'un bloc d'argile cellulaire présente donc une difficulté fondamentale qui est de maintenir la masse d'argile à l'état cellulaire pendant son durcissement. The production without cooking of a block of cellular clay therefore presents a fundamental difficulty which is to maintain the mass of clay in the cellular state during its hardening.

On a maintenant découvert que ceci peut être obtenu en utilisant des particules solides de densité inférieure à 1, en quantité appropriée, pour véhiculer dans la pâte l'un des réactifs de gonflement. It has now been discovered that this can be achieved by using solid particles of density less than 1, in an appropriate amount, to convey one of the swelling reagents into the dough.

Un procédé de fabrication typique, selon l'invention, est un procédé dans lequel on fait gonfler dans un moule une pâte aqueuse d'argile en faisant réagir dans la pâte au moins deux agents de gonflement qui assurent le gonflement en réagissant l'un sur l'autre et dans lequel on fait durcir la pâte gonflée au moyen d'un agent de durcissement dispersé dans la pâte, caractérisé par le fait que l'on disperse dans la pâte des particules de densité inférieure à 1 et ayant une grosseur de 0,5 à 5 mm, 50 % au moins de ces particules ayant une grosseur de l a 2 mm, ces particules ayant été préalablement enrobées avec l'un des dits agents de gonflement. A typical manufacturing process according to the invention is a process in which an aqueous clay paste is swollen in a mold by reacting in the paste at least two swelling agents which ensure swelling by reacting one on the other and in which the swollen dough is hardened by means of a hardening agent dispersed in the dough, characterized in that particles of density less than 1 and having a size of 0 are dispersed in the dough , 5 to 5 mm, at least 50% of these particles having a thickness of 2 mm, these particles having been previously coated with one of said swelling agents.

L'agent de gonflement véhiculé par les particules est, de préférence, un agent à réaction acide, notamment un acide liquide ou cristallisé, par exemple de l'acide sulfurique, phosphorique ou oxalique, destiné à réagir avec un autre agent de gonflement, par exemple un carbonate, comme le plâtre ou la craie, qui a été dispersé par ailleurs dans la pâte, par exemple dispersé dans la pâte elle-même ou dans lleau de constitution de la pâte ou dans un autre composant de la pâte. The blowing agent conveyed by the particles is preferably an acid reaction agent, in particular a liquid or crystallized acid, for example sulfuric, phosphoric or oxalic acid, intended to react with another blowing agent, by for example a carbonate, such as plaster or chalk, which has been dispersed elsewhere in the dough, for example dispersed in the dough itself or in the water of constitution of the dough or in another component of the dough.

Dans une réalisation typique, on enrobe les particules avec un agent hydrofuge, puis on les mouille avec l'agent de gonflement avant de les disperser dans la pâte. In a typical embodiment, the particles are coated with a water-repellent agent, then they are wetted with the swelling agent before dispersing them in the paste.

L'agent hydrofuge éventuel est, de préférence, une huile, notamment une huile végétale, en particulier de huile de palme. The optional water-repellent agent is preferably an oil, in particular a vegetable oil, in particular palm oil.

Comme agent de durcissement, on utilise, de préférence, une colle hydrosoluble naturelle ou synthétique, en particulier une colle d'origine animale. Dans une réalisation typique, on dissout cette colle dans l'eau qui servira & préparer la pâte d'argile. As curing agent, use is preferably made of a natural or synthetic water-soluble adhesive, in particular an adhesive of animal origin. In a typical realization, we dissolve this glue in the water which will serve & prepare the clay paste.

Il est également préconisé d'incorporer à la pâte ou à l'veau de constitution de cette pâte ou aux particules une résine auto-émulsionnable qui renforcera les qualités mécaniques du mélange, par exemple on utilise une émulsion vinylique. It is also recommended to incorporate into the paste or to the calf of which this paste is made or to the particles a self-emulsifying resin which will reinforce the mechanical qualities of the mixture, for example a vinyl emulsion is used.

On connaît de tres nombreuses particules solides de densité inférieure a celle de liteau convenant aux fins de la présente invention et l'on citera, par exemple les particules d'origine végétale, minérale ou synthétique, en particulier les particules de broyage de végétaux, les particules obtenues lors de la préparation des déchets de mousse synthétique rigide, les laitiers de hauts fourneaux, la vermiculite, la perlite, les particules de bois. Numerous solid particles of lower density than that of a batten suitable for the purposes of the present invention are known and mention will be made, for example, of particles of vegetable, mineral or synthetic origin, in particular particles of grinding plants, particles obtained during the preparation of rigid synthetic foam waste, blast furnace slag, vermiculite, perlite, wood particles.

Les proportions des différents constituants de la pâte sont choisies sans difficulté par l'homme de métier en fonction des caractéristiques particulières qu'il désire conférer au bloc selon l'usage prévu. The proportions of the various constituents of the dough are chosen without difficulty by those skilled in the art according to the particular characteristics which it wishes to impart to the block according to the intended use.

La pâte peut être préparée directement dans le moule ou préparée en dehors du moule et versée dans le moule. Les différentes opérations du procédé peuvent comprendre des phases distinctes ou des phases simultanées. The dough can be prepared directly in the mold or prepared outside the mold and poured into the mold. The different operations of the process can include distinct phases or simultaneous phases.

Le moule est un moule fermé sur tous ses côtés ou un moule ouvert ou un moule à couvercle flottant. The mold is a mold closed on all sides or an open mold or a mold with a floating lid.

A titre d'exemple, on prépare une pâte en mélangeant dans un moule de l'argile et de l'eau en quantité suffisante pour obtenir une pâte fluide après avoir ajouté dans l'eau 30 grammes de colle d'origine animale pour 1 litre d'eau. On disperse dans la pâte 3 à 4 % en poids de plâtre. By way of example, a paste is prepared by mixing in a mold clay and water in sufficient quantity to obtain a fluid paste after having added 30 grams of glue of animal origin to 1 liter in the water. of water. Dispersed in the paste 3 to 4% by weight of plaster.

Par ailleurs, on enrobe avec de l'huile de palme puis avec de l'acide oxalique cristallisé, des granulés de vermiculite et on disperse ces granulés dans la pâte d'argile à raison de 5 % de granulés en poids par rapport au poids de la pâte. La masse gonfle et durcit dans le moule. Furthermore, vermiculite granules are coated with palm oil and then with crystallized oxalic acid, and these granules are dispersed in the clay paste at a rate of 5% of granules by weight relative to the weight of dough. The mass swells and hardens in the mold.

L'invention permet d'obtenir des blocs de toutes formes, notamment pour des constructions, en particulier des blocs de mur, de plancher ou de plafond. The invention makes it possible to obtain blocks of all shapes, in particular for constructions, in particular wall, floor or ceiling blocks.

La quantité de particules à incorporer dans la pâte pour véhiculer l'un des agents de gonflement est choisie suffisante pour maintenir le gonflement désiré pendant le durcissement. Cette quantité est déterminée par des essais selon le degré de gonflement désiré. The quantity of particles to be incorporated into the paste to convey one of the swelling agents is chosen to be sufficient to maintain the desired swelling during hardening. This amount is determined by tests according to the degree of swelling desired.

Claims

1 - Process for manufacturing a molded block of hardened cellular clay without firing, in which an aqueous clay paste is made to swell in a mold by reacting in the paste at least two swelling agents -which ensure swelling by reacting the one on the other and in which the swollen dough is made to harden by means of a hardening agent dispersed in the dough, characterized in that particles of density less than 1 and having a size are dispersed in the dough from 0.5 to 5 mm, at least 50% of these particles having a thickness of 1 to 2 mm, these particles having been previously coated with one of said swelling agents.

2 - Process according to claim 1, characterized in that the said particles are coated with a swelling agent reacting like an acid.

3 - A method according to claim 2, characterized in that one chooses a liquid or crystallized acid as swelling agent, in particular an acid from the group consisting of sulfuric, phosphoric, oxalic acids.

4 - Method according to one of claims l to 3, characterized in that the said particles are coated with a water-repellent agent before coating them with the swelling agent.

5 - Process according to claim 4, characterized in that an oil is used as a water-repellent agent, in particular a vegetable oil, in particular palm oil.

6 - Method according to one of claims l to 5, characterized in that the other swelling agent is dispersed either directly in the dough, or in one of the elements which will be used to prepare the dough.

7 - Method according to one of claims l to 6, characterized in that one uses a natural or synthetic water-soluble adhesive as curing agent, in particular an adhesive of animal origin.

8 - Process according to claim 7, characterized in that the glue is dissolved in the water which will be used to prepare the dough.

9 - Method according to one of claims l to 7, characterized in that one incorporates into the clay paste, the water of constitution of this paste or said particles a self-emulsifiable resin.

10 - Process according to claim 9, characterized in that a vinyl emulsion is used as a self-emulsifying resin.

it - Method according to one of the preceding claims, characterized in that one chooses particles of plant, mineral or synthetic origin, in particular particles from the grinding of plants, rigid synthetic foam waste, blast furnace slag, vermiculite, perlite, wood particles.

12 - The cellular clay blocks obtained by a process according to one of claims 1 to li and characterized in particular by the presence of said particles.