FR1465689A - Cold bituminous mortar without cracking based on cationic bitumen emulsion, cement and aggregates, intended for paving or improving roads, sidewalks, industrial floors - Google Patents

Cold bituminous mortar without cracking based on cationic bitumen emulsion, cement and aggregates, intended for paving or improving roads, sidewalks, industrial floors Download PDF

Info

Publication number
FR1465689A
FR1465689A FR40776A FR40776A FR1465689A FR 1465689 A FR1465689 A FR 1465689A FR 40776 A FR40776 A FR 40776A FR 40776 A FR40776 A FR 40776A FR 1465689 A FR1465689 A FR 1465689A
Authority
FR
France
Prior art keywords
mortar
cement
emulsion
parts
bituminous
Prior art date
Legal status (The legal status is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the status listed.)
Expired
Application number
FR40776A
Other languages
French (fr)
Inventor
Sauveur Ingrassia
Jean Orsini
Priority date (The priority date is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the date listed.)
Filing date
Publication date
Application filed filed Critical
Priority to FR40776A priority Critical patent/FR1465689A/en
Application granted granted Critical
Publication of FR1465689A publication Critical patent/FR1465689A/en
Expired legal-status Critical Current

Description

Mortier bitumineux à froid sans fissuration à base d'émulsion de bitume cationique,
de ciment et d'agrégats, destinés aux revêtements ou aménagements de routes,
trottoirs, sols industriels.Cold bituminous mortar without cracking based on cationic bitumen emulsion,
cement and aggregates, intended for road surfaces or improvements,
sidewalks, industrial floors.

La présente invention concerne un mortier bitu
mineux sans fissurations et un proeédé éliminant le
phénomène d'adsorption entre les composants de
ce mortier pendant sa préparation et son utilisation.The present invention relates to a bitu mortar
miners without cracking and a process that eliminates
adsorption phenomenon between the components of
this mortar during its preparation and use.

La réalisation de revêtements de sols à partir
d'émuision de bitume à froid se heurte à de grandes
difficultés dès lors que lesdits revêtements doivent
présenter après séchage une aptitude au vieillisse
ment qu'il est très difficile de prétendre et d'obte
nir d'après lles procédés actuels. Par certains pro
cédés déjà existants on se trouve à bref délai devant
des phénomènes de fissuration et d'effritement. Par
d'autres, plus courants, on se limite à effectuer un
répandage au sol sur un agrégat sec ou mouillé sur
lequel on répand un autre agrégat qui vient se
fixer plus ou moins bien sur l'émulsion précédem
ment répandue. Par ailleurs l'utilisation de ces
émulsions de bitume pour réaliser des mortiers à
base de ciment et d'agrégats poussiéreux, s'est trou
vée handicapée par les Iphénomènes d'adsorption
ou de rupture d'émulsion se présentant lors
des mélanges émulsion bitumineuse- ciment- agrégats. The realization of floor coverings from
cold bitumen emulsion is fraught with large
difficulties since said coatings must
show an ability to age after drying
ment that it is very difficult to claim and obtain
nir according to current methods. By some pro
ceded already existing we find ourselves shortly before
phenomena of cracking and crumbling. By
others, more common, we limit ourselves to carrying out a
spreading on the ground on a dry or wet aggregate on
which we spread another aggregate that comes
fix more or less well on the previous emulsion
widespread. Moreover, the use of these
bitumen emulsions to make mortars with
cement base and dusty aggregates, has
vee handicapped by adsorption phenomena
or emulsion breakage occurring during
bituminous emulsion-cement-aggregate mixtures.

L'invention a notamment pour but de remédier aux
inconvénients des procédés connus.The object of the invention is in particular to remedy the
disadvantages of known methods.

Elle a pour objet : Un mortier bitumineux à
froid sans fissuration et ne présentant pas de rup
ture d'émulsion pendant sa préparation et son uti
lisation, constitué au moins en partie par du ciment
Portland, des agrégats, une émulsion de bitume
cationique et un détergent.Its purpose is: A bituminous mortar with
cold without cracking and showing no rup
emulsion ture during preparation and use
lization, formed at least in part by cement
Portland, aggregates, bitumen emulsion
cationic and detergent.

Suivant un mode réalisation de l'invention, le
mortier bitumineux renferme 150 parties de déter
gent, 850 parties d'émulsion bitumineuse cationique à à 65 So, 1000 parties de ciment et 5 000 parties
d'agrégats silico calcaires.According to one embodiment of the invention, the
bituminous mortar contains 150 parts of
gent, 850 parts of cationic bituminous emulsion at 65 So, 1000 parts of cement and 5000 parts
silico-limestone aggregates.

Selon l'invention on mélange d'abord, sans
moyen spécial et à froid, d'émulsion de bitume ca-
tionique et le détergent, soit au moment de son utilisation, soit au préalable, ce mélange pouvant être stocké sans crainte de détérioration de l'émulsion. On ajoute au moment de la mise en oeuvre, le mélange ciment-agrégats. According to the invention, the mixture is first mixed, without
special, cold medium, bitumen emulsion ca-
tionic and detergent, either at the time of its use, or beforehand, this mixture being able to be stored without fear of deterioration of the emulsion. At the time of implementation, the cement-aggregate mixture is added.

Le mortier bitumineux ainsi obtenu présente, dans les différentes phases de sa préparation, un mélange homogène de consistance comprise entre celle d'une huile épaisse et celle d'un miel épais, donnant 'l'impression d'une tendance naturelle à l'étalement pendant la mise en oeuvre. The bituminous mortar thus obtained presents, in the different phases of its preparation, a homogeneous mixture of consistency between that of a thick oil and that of a thick honey, giving the impression of a natural tendency to spread. during implementation.

Selon un mode de mise en oeuvre du procédé on verse ledit mortier sur le sol ou sur le matériau qui doit le recevoir et on l'étale soit à la règle soit à la truelle ou Ipar tout autre moyen approprié, sans besoin particulier de le tasser comme on le fait traditionnellement. According to one embodiment of the method, said mortar is poured onto the ground or onto the material which is to receive it and it is spread either with a rule or with a trowel or by any other suitable means, without any particular need to compact it. as is traditionally done.

Suivant une caractéristique de l'invention l'eau n'est, pas utilisée pour la réalisation de ce mortier bitumineux. According to one characteristic of the invention, water is not used for the production of this bituminous mortar.

;Le durcissement dudit mortier bitumineux s'dh- tien t par évaporation naturelle de l'eau contenue dans les matériaux ou dans les produits utilisés. The hardening of said bituminous mortar takes place by natural evaporation of the water contained in the materials or products used.

D'après le procédé on peut indiquer que par temps sec, pour une chape de 1 cm d'épaisseur, le séchage se produit en un temps maximum d'environ 4 heures. From the process it can be indicated that in dry weather, for a screed 1 cm thick, the drying takes place in a maximum time of about 4 hours.

Suivant un mode d'utilisation du mortier suivant l'invention, l'on tpeut citer parmi les émulsions cationiques connues et servant à la réalisation du procédé, celles préparées par la Société Esso S.A.F. en France, commue émulsion bitumineuse acide de répandage 65 So. According to one mode of use of the mortar according to the invention, mention may be made, among the known cationic emulsions used for carrying out the process, of those prepared by the company Esso S.A.F. in France, an acidic bituminous emulsion for spreading 65 So.

Suivant un autre mode de réalisation du mortier bitumineux, le détergent est du type Gardinol tel ceux connus sous la dénomination eommereiale de
Teepol d X d 217, Teepol D X D 222, Lensex LE 40, Pactol.According to another embodiment of the bituminous mortar, the detergent is of the Gardinol type such as those known under the trade name of
Teepol d X d 217, Teepol DXD 222, Lensex LE 40, Pactol.

Le ciment du mortier suivant un mode de l'in The cement of the mortar following a mode of the in

Claims (14)

vention est constitué par un ciment ordinaire arti ficiel du type Portland. Le mortier suivant l'invention est constitué au moins en partie par des agrégats du groupe com prenant les sables, gravillons ou déchets siliceux, silico-calcaires, terres de carrières, déchets ou concassés de marbre ou de granit, ou tout autre agrégat ne provoquant pas le Iphénomène 'd'adsorption ou rupture d'émulsion, d'après le procédé. Parmi les nombreux modes de mise en #uvre accessibles à l'homme de l'art, l'exemple di-après donne un aperçu sur une possibilité de mise en pratique Exemple. - On ajoute à 850 parties d'émulsion bitumineuse cationique à 65 %, 150 parties de Pactol pour obtenir 1000 parties d'un mélange liquide. On prépare à sec un mortier composé devention consists of an ordinary artificial cement of the Portland type. The mortar according to the invention consists at least in part of aggregates from the group comprising sands, gravel or siliceous, silico-limestone, quarry soil, waste or crushed marble or granite, or any other aggregate not causing not the phenomenon of adsorption or emulsion breakage, depending on the process. Among the many modes of implementation accessible to those skilled in the art, the following example gives an overview of a possibility of putting this into practice. - 150 parts of Pactol are added to 850 parts of 65% cationic bituminous emulsion to obtain 1000 parts of a liquid mixture. A dry mortar composed of 1 000 parties de ciment ordinaire et 5 000 parties 1000 parts of ordinary cement and 5000 parts d'agrégats silico calcaires. silico-limestone aggregates. On place dans un Técipient approprié ou dans un malaxeur, l'émulsion de bitume- cntionique.Pac The bitumen-ionic emulsion is placed in a suitable container or in a mixer. tol et on ajoute au fur eut à mesure ou en une seule fois le mélange ciment-agrégat. On obtient tol and the cement-aggregate mixture is added gradually or all at once. We obtain ainsi un mortier bitumineux pouvant être mis en thus a bituminous mortar that can be used oeuvre immédiatement. works immediately. Les conditions idéales, suivant l'invention, sont atteintes lorsque les mélanges agrégats-ciment, mé- langés à l'émulsion bitumineuse-Pactol, présentent un mortier homogène dont la consistance donne l'impression -d'un miel épais ne s'effritant pas pen The ideal conditions, according to the invention, are reached when the aggregate-cement mixtures, mixed with the bituminous emulsion-Pactol, present a homogeneous mortar, the consistency of which gives the impression of thick honey not crumbling. not pen dant le malaxage ni pendant l'application. Pour neither before mixing nor during application. For cela il suffit d'augmenter ou de diminuer la quan tite de détergent dans l'émulsion de bitume catio- nique, en tenant compte de la qualité de l'agrégat utilisé ou de la quantité de ciment. it suffices to increase or decrease the quantity of detergent in the cationic bitumen emulsion, taking into account the quality of the aggregate used or the quantity of cement. Il est lien entendu que l'invention n'est. pas limitée à l'exemple décrit; eRle est susceptible de nombreuses variantes, accessibles à l'homme de l'art, suivant les applications envisagées et sans s'écarter pour cela du cadre de l'invention. It is understood that the invention is not. not limited to the example described; eRle is capable of numerous variants, accessible to those skilled in the art, depending on the applications envisaged and without thereby departing from the scope of the invention. RESUME ABSTRACT 1 Un mortier bitumineux à froid, sans fissuration et constituté au moins en partie par du ciment du type Portland, un détergent, une émulsion de bitume cationique et des agrégats. 1 A cold bituminous mortar, without cracking and constituted at least in part by Portland type cement, a detergent, a cationic bitumen emulsion and aggregates. 2 Un nouveau mortier qui renferme selon 1 pondéralement 150 parties de détergent, 850 parties d'émulsion bitumineuse cationique à 65 %, 1000 parties de ciment et 5 000 parties d'agrégats. 2 A new mortar which contains 1 by weight of 150 parts of detergent, 850 parts of 65% cationic bituminous emulsion, 1000 parts of cement and 5000 parts of aggregates. 30 Encore un nouveau mortier suivant 10 et 20 dans lequel le ciment est constitué au moins en partie par un ciment Portland. Yet another new mortar according to 10 and 20 in which the cement consists at least in part of Portland cement. 40 Un nouveau mode de réalisation de mortier 40 A new embodiment of mortar suivant 1 , 2 et 3 , dans lequel l'émulsion de according to 1, 2 and 3, in which the emulsion of bitume est constituée au moins en partie par une bitumen is formed at least in part by a émulsion cationique à 65 %. 65% cationic emulsion. 5 Un autre mode de réalisation du mortier sui 5 Another embodiment of the mortar sui vant l'un quelconque des paragraphes de lo à 4 before any of the paragraphs lo to 4 dans lequel le détergent est du type gardinol. in which the detergent is of the gardinol type. 6 Encore un mode de réalisation du mortier 6 Another embodiment of the mortar suivant l'un quelconque des paragraphes de 1 à 5 according to any one of paragraphs 1 to 5 dans lequel l'agrégat est constitué au moins en par in which the aggregate is formed at least by tie par une substance du groupe comprenant les tied by a substance of the group comprising sables, gravillons, déchets siliceux ou silico-calcaires, sands, gravel, siliceous or silico-limestone waste, terres de carrières, déchets ou concassés de marbre quarry land, waste or crushed marble ou de granit, ou tout autre agrégat ne provoquant or granite, or any other aggregate not causing pas le phénomène d'adsorption. not the phenomenon of adsorption. 70 Un procédé de préparation d'un mortier tel 70 A process for preparing a mortar such que décrit de 1 à 6 réalisé à froid et qui consiste as described from 1 to 6 produced cold and which consists à préparer une solution d'émulsion bitumineuse ca to prepare a bituminous emulsion solution ca tionique et de détergent, à malaxer ou à mélanger tionic and detergent, to mix or mix ladite solution avec du ciment et des agrégats pour said solution with cement and aggregates for former un mélange homogène de consistance com form a homogeneous mixture of consistency com prise entre celle d'une huile fluide et celle d'un caught between that of a fluid oil and that of a miel épais, destiné à la réalisation de revêtements thick honey, intended for the realization of coatings ou aménagement de routes, trottoirs, sols indus or development of roads, sidewalks, industrial soils triels, chapes. triels, screeds. 8 Un mode de réalisation suivant 7 par lequel 8 A following embodiment 7 whereby on étale simplement ledit mortier à la règle ou one simply spreads said mortar with the rule or à la truelle ou par tout autre moyen approprié, with a trowel or by any other suitable means, sans besoin particulier de le tasser comme on le without any particular need to pack it as it is fait traditionellement. traditionally done. 9 Un nouveau mode de réalisation du procédé 9 A new embodiment of the method suivant l'un quelconque des paragraphes de 10 à 80 according to any one of paragraphs 10 to 80 permettant d'éviter par ce mortier les fissurations making it possible to avoid cracks by this mortar traditionnelles. traditional. 100 Un nouveau mortier à base d'émulsion de 100 A new mortar based on emulsion of bitumes cationiques ne présentant pas les phéno cationic bitumens not exhibiting pheno mènes d'adsorption ou rupture d'émulsion lors du adsorption or rupture of emulsion during mélange de ses composants suivant les paragraphes mixture of its components according to paragraphs de 1 à 9 , from 1 to 9, 110 Encore un mode de réalisation dudit mortier 110 Another embodiment of said mortar selon les paragraphes de 10 à 100 et dans lequel according to paragraphs 10 to 100 and in which l'eau de gâchage n'est pas utilisée pour la prépa mixing water is not used for the preparation ration de ce mortier bitumineux. ration of this bituminous mortar. 12 Un nouveau mortier suivant les paragraphes 12 A new mortar according to the paragraphs de 1 à 11 d'après lequel on peut indiquer que from 1 to 11 according to which we can indicate that par temps sec et pour une chape d'une épaisseur in dry weather and for a thick screed de 1 cm le séchage et le commencement du dur of 1 cm drying and the beginning of the hard cissement s'effectuent en un temps maximum de 3 curing are carried out in a maximum time of 3 à 5 heures environ. at about 5 o'clock. 13 A titre de produit nouveau industriel, la 13 As a new industrial product, the réalisation de tout revêtement de sol en mortier realization of any mortar flooring bitumineux présentant au moins une 'des caractéris- bituminous material exhibiting at least one of the characteristics tiques décrites dans les paragraphes 10 à 12D du ticks described in paragraphs 10 to 12D of présent résumé this summary
FR40776A 1965-12-03 1965-12-03 Cold bituminous mortar without cracking based on cationic bitumen emulsion, cement and aggregates, intended for paving or improving roads, sidewalks, industrial floors Expired FR1465689A (en)