FI94438C - Coating in the form of a plate or mat - Google Patents
Coating in the form of a plate or mat Download PDFInfo
- Publication number
- FI94438C FI94438C FI925898A FI925898A FI94438C FI 94438 C FI94438 C FI 94438C FI 925898 A FI925898 A FI 925898A FI 925898 A FI925898 A FI 925898A FI 94438 C FI94438 C FI 94438C
- Authority
- FI
- Finland
- Prior art keywords
- weight
- coating
- binder
- coating according
- eba
- Prior art date
Description
9443894438
Laatan tai maton muodossa oleva päällysteCoating in the form of a tile or mat
Keksintö koskee laatan tai maton muodossa olevaa päällystettä, joka sideaineena sisältää etyleeni-butyylia-• 5 krylaatti-kopolymeeriä (EBA). Keksinnön mukainen päällyste soveltuu erityisesti lattioden ja seinien päällystämiseen.The invention relates to a coating in the form of a tile or mat which contains ethylene-butyl acrylate copolymer (EBA) as a binder. The coating according to the invention is particularly suitable for coating floors and walls.
Lattianpäällysteiden valmistamiseen on yleisesti käytetty sideaineena polyvinyylikloridia (PVC). Tällaisia päällysteitä on kuvattu mm. patenttijulkaisuissa US 10 3761555, EP 106148 ja EP 227029. PVC-pohjaisten päällys teiden on katsottu eroavan esimerkiksi fysikaalisilta ominaisuuksiltaan edukseen aikaisemmin yleisesti käytetyistä halogeeneja sisältämättömistä päällysteistä, kuten kumi-ja linoleumpäällysteistä.Polyvinyl chloride (PVC) has been commonly used as a binder in the manufacture of floor coverings. Such coatings have been described e.g. in U.S. Pat. No. 10,376,1555, EP 106148 and EP 227029. PVC-based coatings have been found to differ, for example, in their physical properties from halogen-free coatings such as rubber and linoleum coatings previously commonly used.
15 Halogeeneja sisältävien materiaalien, kuten PVC:n, käyttö päällysteissä on kuitenkin havaittu haitalliseksi esim. elektronisten laitteistojen yhteydessä, voimalaitosten ohjaamoissa, hienoelektroniikkateollisuudessa ja erityisesti paloriskialttiissa ympäristössä. Myös ympäristön-20 suojelusyistä johtuen pyritään lisääntyvässä määrin käyt tämään eri tarkoituksiin, esim. pakkauksiin, rakentamiseen, jne., halogeeeneja sisältämättömiä materiaaleja. Lattianpäällysteiden osalta voidaan tässä yhteydesssä viitata EP-patenttijulkaisuun 321760, josta on tunnettua 25 käyttää perussideainekomponenttina etyleeni-vinyyliase- taatti-kopolymeeriä (EVA), johon madollisesti on lisätty polypropeenej a.15 However, the use of halogen-containing materials, such as PVC, in coatings has been found to be harmful, for example, in connection with electronic equipment, power plant cabs, the fine electronics industry and, in particular, in flammable environments. Also for reasons of environmental protection, the use of non-halogenated materials for various purposes, e.g. packaging, construction, etc., is increasingly being sought. With regard to floor coverings, reference may be made in this connection to EP 321760, from which it is known to use ethylene-vinyl acetate copolymer (EVA) to which polypropylenes have been added as basic binder component.
Esillä olevan keksinnön tarkoituksena oli saada aikaan päällyste, joka ensinnäkin on halogeeniton, jolloin 30 se täyttää erikoisalojen vaatimukset ja on ympäristöystävällinen. Päällyste ei saa sisältää normaaleissa käyttö-lämpötiloissa ympäröivään tilaan haihtuvia terveydelle haitallisia aineita, kuten liuottimia, pehmittimiä, jne.. Lisäksi tuotteen tulee olla termoplastinen niin, että tuo-35 te on työstettävissä käyttäen tunnettuja teknologisia me- 2 94438 netelmiä ja sen kierrättäminen on mahdollista. Tuote pitää voida valmistaa joko laattamaisena tai rullattavana mattona ja ulkonäöllisten ominaisuuksien pitäisi olla helposti varioitavissa. Päällysteen asentaminen ja irroittaminen 5 (vrt. ed. kierrätys) tulee myös olla helppoa. Lopuksi päällysteen tulee peruskäyttöominaisuuksiltaan vastata tunnettuja päällystetuotteita. Perusominaisuuksiin luetaan paitsi erilaiset mekaaniset yleisesti tunnetut ominaisuudet, kuten painuman (kuormituksen) kesto, kulutuskestä-10 vyys, mittojen pysyvyys, jne., myös puhtaanapito-ominaisuudet .The object of the present invention was to provide a coating which is, first of all, halogen-free, so that it meets the requirements of special fields and is environmentally friendly. The coating must not contain substances which are harmful to health, such as solvents, plasticizers, etc., which are volatile to the environment at normal operating temperatures. In addition, the product must be thermoplastic so that the product can be processed using known technological methods and recyclable. . The product should be able to be made as either a tiled or rollable mat and the appearance properties should be easily variable. Installing and removing the cover 5 (cf. previous recycling) should also be easy. Finally, the coating must correspond in known basic properties to known coating products. The basic properties include not only the various well-known mechanical properties, such as the duration of deflection (load), wear resistance, dimensional stability, etc., but also the cleaning properties.
Esillä olevan keksinnön mukainen päällyste täyttää edellä esitetyt peruskriteerit. Edellä mainitusta EP-pa-tenttijulkaisusta 321761 tunnetut tuotteet täyttävät eräi-15 den ominaisuuksien, kuten halogeenittomuuden, termoplasti-suuden ja kierrätettävyyden, suhteen osittain edellä asetetut kriteerit. Nyt on kuitenkin havaittu, että esillä olevan keksinnön mukaisella päällysteellä on huomattavia etuja mainittuihin tunnettuihin tuotteisiin nähden.The coating of the present invention meets the basic criteria set forth above. The products known from the above-mentioned EP patent publication 321761 partially meet the criteria set out above with regard to certain properties, such as halogen-free, thermoplasticity and recyclability. However, it has now been found that the coating according to the present invention has considerable advantages over said known products.
20 Esillä oleva keksintö koskee laatan tai maton muo dossa olevaa päällystettä, jonka pinta on kulutuksenkestä-vä ja joka on valmistettu seoksesta, joka sisältää sideainetta, täyteainetta ja mahdollisesti lisäaineita. Päällysteelle on tunnusomaista, että sideaine sisältää etylee- 25 ni-butyyliakrylaatti-kopolymeeriä (EBA).The present invention relates to a coating in the form of a tile or mat, the surface of which is abrasion-resistant and which is made of a mixture containing a binder, a filler and optionally additives. The coating is characterized in that the binder contains ethylene-butyl acrylate copolymer (EBA).
Keksinnön mukainen päällyste on tyypillisesti puolijäykkä laatta tai taipuisa matto ja se voi olla homogeeninen tai kerroksellinen, yksivärinen tai kuvioitu. EBA:n osuus käytettävästä sideaineesta on sopivasti 20 - 80 pai-30 no-%. Sopivia EBA-polymeerejä ovat sellaiset, joiden bu- ·. tyyliakrylaattipitoisuus on 5 - 28 %. Haluttujen lattian päällysteille tyypillisten ominaisuuksien saavuttamiseksi ja parantamiseksi voidaan EBA:n lisäksi muina sideaineina käyttää eimerkiksi erilaisia propeenipolymeerejä ja -kopo-35 lymeerejä, kuten satunnaispolypropeenejä. Sideaineiden ko konaismäärä päällysteessä on sopivasti 20 - 80 paino-%, \ laskettuna päällysteen kokonaispainosta. Päällyste sisäl- 3 94438 tää sideaineen lisäksi sopivia epäorgaanisia tai orgaanisia täyteaineita ja mahdollisesti lisäaineita. Täyteaineina voidaan käyttää esimerkiksi liitua, kaoliinia, kalkki-kivi- tai dolomiittijauhetta, erilaisia silikaattimineraa-5 lijauheita, kvartsijauhetta tai -hiekkaa sekä orgaanisia tai epäorgaanisia kuituja. Tyypillisiä lisäaineita ovat antistaattiset aineet, valostabilisaattorit, antioksidan-tit ja väriaineet. Täyte- ja lisäaineiden määrä on sopivasti 20 - 80 paino-%, josta lisäaineiden osuus on yleensä •10 enintään 5 paino-%, laskettuna päällysteen kokonaispainosta.The coating of the invention is typically a semi-rigid tile or flexible mat and may be homogeneous or layered, monochromatic or textured. The proportion of EBA in the binder used is suitably from 20 to 80% by weight. Suitable EBA polymers are those having a bu-. the style acrylate content is 5 to 28%. In addition to EBA, various propylene polymers and copolymers, such as random polypropylenes, can be used as other binders, in addition to EBA, to achieve and improve the desired properties typical of floor coverings. The total amount of binders in the coating is suitably 20 to 80% by weight, based on the total weight of the coating. The coating contains, in addition to the binder, suitable inorganic or organic fillers and, if appropriate, additives. Examples of fillers that can be used are chalk, kaolin, lime-rock or dolomite powder, various silicate mineral powders, quartz powder or sand, and organic or inorganic fibers. Typical additives include antistatic agents, light stabilizers, antioxidants and colorants. The amount of fillers and additives is suitably from 20 to 80% by weight, of which the additives generally account for up to 5% by weight, based on the total weight of the coating.
Keksinnön mukainen päällyste voidaan valmistaa sinänsä tunnetulla tavalla käyttämällä vastaavien PVC-poh-jaisten tuotteiden valmistuksesta tunnettuja mentelmiä.The coating according to the invention can be prepared in a manner known per se using methods known for the production of corresponding PVC-based products.
15 Esimerkiksi pääasiallisesti kvartsihiekkaa (raekoko 0,1 -0,8 mm) täyteaineena ja EBArta sekä satunnaispolypropeene-jä sideaineena sisältävän lattialaatan valmistus tapahtuu sekoittamalla täyte- ja sideainekomponentit keskenään kui-vasekoitin-tyyppisellä sekoittimella ja sulattamalla saatu 20 seos suulakepuristimella. Sulanut seos siirretään edelleen kaksitelavalssille, josta se syötetään kalanterille kalan-teroitavaksi halutun paksuiseksi aihiolevyksi. Sulatus voidaan suorittaa myös suoraan kaksitelavalssilla. Lopullisen tiiviin ja sileän pinnan aikaansaamiseksi joko (a) 25 aihiolevy syötetään jatkuvana ratana ns. kaksoisnauhapu-ristimeen ja puristetaan levynauhaksi,josta leikataan halutun kokoiset, esim. 30 x 30 cm tai 50 x 50 cm laatat, tai (b) aihionauha katkotaan sopivan pituisiksi levyiksi, jotka jäähdytetään ja puristetaan eri työvaiheena kerros-30 puristimessa, ja näin saaduista valmiista aihioista leika-; taan halutun kokoiset laatat. Kuviointi saadaan aikaan ku ten PVC-perustaisella tuotteella joko sekoittamalla kaksitelavalssilla samasta tai koostumukseltaan osittain modifioidusta massasta valmistettuja 1 - 15 mm kokoisia eri-35 värisiä rakeita kylmänä kuumaan massaan tai puristammalla 4 94438 nämä kuumaan aihiolevyyn kaksoisnauha- tai kerrospuristi-messa.For example, a floor tile containing mainly quartz sand (grain size 0.1-0.8 mm) as a filler and EBA and random polypropylenes as a binder is prepared by mixing the filler and binder components together with a dry mixer-type mixer and melting the resulting mixture with an extruder. The molten mixture is further transferred to a twin-roll roll, from where it is fed to a calender to a fish plate to be sharpened to the desired thickness. Defrosting can also be performed directly on a twin roll. In order to obtain a final compact and smooth surface, either (a) 25 the blank is fed as a continuous web in the so-called into a double strip press and pressed into a sheet strip from which tiles of the desired size, e.g. 30 x 30 cm or 50 x 50 cm, are cut, or (b) the blank is cut into sheets of suitable length, cooled and pressed in a different step in a layer 30 press, and blanks; tiles of the desired size. The patterning is achieved, for example, with a PVC-based product, either by mixing 1 to 15 mm granules of different colors of the same or partially modified composition in a cold hot mass or by pressing 4,94438 on a hot preform in a double strip or layer press.
Keksinnön mukaisen päällysteen ominaisuudet eroavat edukseen vastaavan PVC-pohjäisen tuotteen vastaavista mer-5 kittävästi ja yllättävän monelta osin perusvaatimukseksi asetetun halogeenittomuuden lisäksi: - Samaa täyteainekoostumusta ja sideaine/täyteaine-suhdetta käyttäen on havaittu keksinnön mukaisen päällysteen olevan muiden tasavertaisten ominaisuuksien ohella selväs- 10 ti jäykemmän, millä seikalla on suuri merkitys käyännössä asennustyössä sekä myös aluslattialle asetettavien vaatimusten osalta.The properties of the coating according to the invention differ significantly from those of the corresponding PVC-based product significantly and surprisingly in many respects in addition to the basic halogen-free requirement: Using the same filler composition and binder / filler ratio, the coating according to the invention has a clearer , which is of great importance in practice during the installation work, as well as with regard to the requirements for the subfloor.
- Painumankestävyys, joka on lattianpäällysteen tärkeimpiä ominaisuuksia, on keksinnön mukaisella päällysteellä sel- 15 västi parempi.- The compressive strength, which is one of the most important properties of the floor covering, is clearly better with the coating according to the invention.
- Keksinnön mukaisen päällysteen käyttölämpötila-alue on laajempi, ts. ominaisuudet eivät muutu oleellisesti lämpötilan funktiona lämpötila-alueella 0-50 °C.- The operating temperature range of the coating according to the invention is wider, i.e. the properties do not change substantially as a function of temperature in the temperature range 0-50 ° C.
- Keksinnön mukaisen päällysteen sisältämällä sideaineella 20 saadaan paremmat ns. kylmävirumisominaisuudet, ts. parempi pitkäaikaisen kuormituksen kestävyys.- The binder 20 contained in the coating according to the invention gives better so-called cold creep properties, i.e., better long-term load resistance.
- Keksinnön mukaisen päällysteen kulutuksenkestävyys on selvästi parempi samaa täyteaine/sideaine-tilavuussuhdetta käyttäen.- The abrasion resistance of the coating according to the invention is clearly better using the same filler / binder volume ratio.
2*5 - Keksinnön mukainen päällyste on noin 20 % PVC-pohjäistä tuotetta keveämpi, millä seikalla on merkitystä käsittelyn, kuljetuskustannusten sekä askeläänenvaimennusominai-suuksien kannalta.2 * 5 - The coating according to the invention is about 20% lighter than a PVC-based product, which is important in terms of handling, transport costs and step sound attenuation properties.
- Keksinnön mukaisen päällysteen lianhylkivyys ja yleensä 30 puhtaanapito-ominaisuudet ovat paremmat kuin PVC-pohjais- ·. ten tuotteiden.- The dirt repellency and generally the cleaning properties of the coating according to the invention are better than those of PVC-based. products.
- Koska keksinnön mukainen päällyste ei sisällä erillisiä nestemäisiä pehmittimiä, ei myöskään tapahdu näiden mig-rautumista päällysteen pinnalle, eikä vastaavasti ulkopuo- 35 listen esim. öljyliukoisten värillisten tai värittömien • * 5 94438 ainesten imeytymistä päällysteen pintaa syvemmälle kuten on PVC-pohjaisilla tuotteilla asianlaita.- Since the coating according to the invention does not contain separate liquid plasticizers, there is also no migration of these to the surface of the coating, and no absorption of external e.g. oil-soluble colored or colorless substances deeper than the surface of the coating, as is the case with PVC-based products.
- Keksinnön mukainen päällyste poikkeaa edukseen kitkaomi-naisuuksien suhteen verrattuna vastaavaan PVC-pohjäiseen ’ 5 tuotteeseen.- The coating according to the invention differs in advantage in terms of friction properties compared to the corresponding PVC-based '5 product.
Keksinnön mukainen päällyste erottuu selvästi ja yllättäen edukseen myös EVA-pohjäisistä päällysteistä (ks.The coating according to the invention also clearly and surprisingly differs from EVA-based coatings (see
EP 321761) siten, että keksinnön mukaisen päällysteen käyttölämpötila-alue on laajempi, ts. lämpötilan muutoksen 10 vaikutus päällysteen mekaanisiin ominaisuuksiin on vähäisempi kuin EVA-pohjäisillä tuotteilla. EBA-perustaisten lattianpäällysteiden lianhylkimis- ja puhtaanapito-ominaisuudet ovat oleellisesti paremmat kuin vastaavilla EVA-poh jäisillä päällysteillä, joiden pinta on käytetystä si-15 deainekoostumuksesta johtuen tahmeahko. Keksinnön mukaisen päällysteen painumankesto- ja virumisominaisuudet ovat samoin paremmat kuin vastaavilla EVA-pohjäisillä tuotteilla. Todettakoon vielä, että EVA-pohjäisten tuotteiden sisältämä vinyyliasetaatti on luokiteltu syöpääaiheuttaviksi epä-20 iltyihin aineisiin.EP 321761) so that the operating temperature range of the coating according to the invention is wider, i.e. the effect of the temperature change 10 on the mechanical properties of the coating is less than with EVA-based products. The dirt-repellent and sanitizing properties of EBA-based floor coverings are substantially better than those of the corresponding EVA-based floor coverings, which have a tacky surface due to the si-15 adhesive composition used. The coating resistance and creep properties of the coating according to the invention are also better than those of the corresponding EVA-based products. It should also be noted that the vinyl acetate contained in EVA-based products is classified as a non-carcinogenic substance.
Seuraavat esimerkit valaisevat keksintöä.The following examples illustrate the invention.
Esimerkki 1Example 1
Valmistettiin päällyste käyttäen seuraavia aineosia 25 ja määriä:A coating was prepared using the following ingredients 25 and amounts:
Etyleeni-butyyliakrylaatti- kopolymeeriä 1) 100,0 kg 25,8 paino-%Ethylene-butyl acrylate copolymer 1) 100.0 kg 25.8% by weight
Polypropeeniä 2) 25,0 kg 6,5 paino-%Polypropylene 2) 25.0 kg 6.5% by weight
Kalsiumkarbonattia 3) 60,0 kg 15,5 paino-% 30 Hiekkaa 4) 190,0 kg 49,0 paino-% . : Stabilisaattoria 5) 0,01 kgCalcium carbonate 3) 60.0 kg 15.5% by weight 30 Sand 4) 190.0 kg 49.0% by weight. : Stabilizer 5) 0.01 kg
Pigmenttiä 6) 12,5 kg 3,2 paino-% 1) NCPE 8019, valmistaja Neste Oy, akrylaattipitoisuus 17 35 %, sulaindeksi 1,5 g/10 min 6 94438 2) Satunnaiskopolymeeri, valmistaja Neste Oy, sulaindeksi 1,8 g/10 min 3) Jauhettu kalkkikivi, raekoko 10 - 200 μιη 4) Luonnonhiekka, raekoko 0 - 800 μπι 5 5) CHIMASSORB 944 LD, valmistaja Ciba-GeigyPigment 6) 12.5 kg 3.2% by weight 1) NCPE 8019, manufacturer Neste Oy, acrylate content 17 35%, melt index 1.5 g / 10 min 6 94438 2) Random copolymer, manufacturer Neste Oy, melt index 1.8 g / 10 min 3) Ground limestone, grain size 10 - 200 μιη 4) Natural sand, grain size 0 - 800 μπι 5 5) CHIMASSORB 944 LD, manufactured by Ciba-Geigy
6) Ti02, valmistaja Kemira Oy, RF2S6) TiO2, manufactured by Kemira Oy, RF2S
Aineosat sekoitettiin huoneenlämpötilassa homogeeniseksi seokseksi. Tätä seosta syötettiin kaksitelavals-sille, jonka telojen lämpötila oli +210 °C. Muokkauksen 10 aikana massan lämpötila nousi +195 °C:een. Valssilta kuuma massa siirrettiin jatkuvana nauhana kaksitelakalanteriin, jonka telojen lämpötila oli +140 °C. Telojen välinen etäisyys säädettiin sellaiseksi, että kalanterista saatava 70 cm leveä nauha oli 2,15 mm paksua. Nauhan päälle ripotel-15 tiin samasta massasta etukäteen valmistettua, halutun väristä, rouhetta kuvioinnin aikaansaamiseksi. Rouhe puristettiin nauhaan kiinni teräsvalssiparilla. Tämän jälkeen nauha katkottiin 100 cm pitkiksi aihioiksi, jotka jäähdytettiin huoneenlämpötilaan.The ingredients were mixed at room temperature to a homogeneous mixture. This mixture was fed to a twin roll roll with a roll temperature of +210 ° C. During the work-up 10, the temperature of the pulp rose to +195 ° C. From the roll, the hot pulp was transferred as a continuous strip to a twin-roll calender with a roll temperature of +140 ° C. The distance between the rollers was adjusted so that the 70 cm wide strip obtained from the calender was 2.15 mm thick. A pre-made crumb of the same color, of the desired color, was sprinkled on top of the strip to provide a pattern. The crumb was pressed onto the strip with a pair of steel rollers. The tape was then cut into 100 cm long blanks which were cooled to room temperature.
20 Valmistetut aihiot ladottiin puristamista varten tähän tarkoitukseen valmistettujen teräslevyjen väliin, yksi aihio teräslevyparia kohti. Puristaminen suoritettiin kaksivaiheisessa kerrospuristimessa, jossa ensimmäisessä vaiheessa lämpötila oli +155 °C, paine 4 MPa ja puristus-25 aika 15 min. Toisessa vaiheessa paine oli 8 MPa, puristus-aika 12 min ja levyjä jäähdytettiin siten, että loppuläm-pötila oli +30 °C. Puristamisen aikana aihiot tulivat 2,0 mm paksuiksi. Aihioista stanssattiin joko 30 cm x 30 cm tai 50 cm x 50 cm suuruisia laattoja.20 The prepared blanks were stacked for pressing between steel plates prepared for this purpose, one blank per pair of steel plates. Compression was performed in a two-stage bed press with a temperature of +155 ° C, a pressure of 4 MPa and a compression time of 15 min in the first stage. In the second stage, the pressure was 8 MPa, the pressing time 12 min and the plates were cooled so that the final temperature was +30 ° C. During pressing, the blanks became 2.0 mm thick. Tiles measuring either 30 cm x 30 cm or 50 cm x 50 cm were punched from the blanks.
9 • · 7 944389 • · 7 94438
Esimerkki 2Example 2
Esimerkissä 1 kuvatulla tavalla valmistettiin päällyste käyttäen seuraavia aineosia ja määriä: Etyleeni-butyyliakrylaatti- 5 kopolymeeriä 100,0 kg 15,7 paino-%As described in Example 1, a coating was prepared using the following ingredients and amounts: Ethylene-butyl acrylate copolymer 100.0 kg 15.7% by weight
Polypropeeniä 167,0 kg 26,2 paino-%Polypropylene 167.0 kg 26.2% by weight
Kalsiumkarbonaattia 80,0 kg 12,6 paino-%Calcium carbonate 80.0 kg 12.6% by weight
Hiekkaa 250,0 kg 39,2 paino-%Sand 250.0 kg 39.2% by weight
Selluloosakuitua 1) 25,0 kg 3,9 paino-% 10 Stabilisaattoria 0,07 kg 0,01 paino-%Cellulose fiber 1) 25.0 kg 3.9% by weight 10 Stabilizer 0.07 kg 0.01% by weight
Kalsiumstearaattia 0,20 kg 0,03 paino-%Calcium stearate 0.20 kg 0.03% by weight
Pigmenttiä 15,0 kg 2,36 paino-% 1) Arbocel PWC 500, J. Rettenmeier & Sohn 15 Kuidun keskimääräinen pituus 700 μιη Kuidun keskimääräinen paksuus 3 5 μιηPigment 15.0 kg 2.36% by weight 1) Arbocel PWC 500, J. Rettenmeier & Sohn 15 Average fiber length 700 μιη Average fiber thickness 3 5 μιη
Valmistetun päällysteen mitatut käyttöominaisuudet: m2 - paino DIN 53 352 2698 g/m2 20 Painuma DIN 51 955 0,07 mm Jäännöspäinuma DIN 51 955 0,03 mmMeasured performance of the manufactured coating: m2 - weight DIN 53 352 2698 g / m2 20 Depression DIN 51 955 0.07 mm Residual deflection DIN 51 955 0.03 mm
Kulutus, (20 sykliä) DIN 51 963 0,09 mmConsumption, (20 cycles) DIN 51 963 0.09 mm
Valonkesto DIN 53 387 7Light fastness DIN 53 387 7
Paloluokitus DIN 4 102 B1 •.Fire classification DIN 4 102 B1 •.
8 944388 94438
Esimerkki 3Example 3
Esimerkissä 1 kuvatulla tavalla valmistettiin päällyste käyttäen seuraavia aineosia ja määriä: Etyleeni-butyyliakrylaatti- 5 kopolymeeriä 100,0 kg 8,4 paino-%As described in Example 1, a coating was prepared using the following ingredients and amounts: Ethylene-butyl acrylate copolymer 100.0 kg 8.4% by weight
Polypropeenia 400,0 kg 33,4 paino-%Polypropylene 400.0 kg 33.4% by weight
Kalsiumkarbonaattia 150,0 kg 12,5 paino-%Calcium carbonate 150.0 kg 12.5% by weight
Hiekkaa 500,0 kg 41,8 paino-%Sand 500.0 kg 41.8% by weight
Selluloosakuitua 25,0 kg 2,1 paino-% 10 Stabilisaattoria 0,20 kg 0,02 paino-%Cellulose fiber 25.0 kg 2.1% by weight 10 Stabilizer 0.20 kg 0.02% by weight
Kalsiumstearaattia 0,30 kg 0,03 paino-%Calcium stearate 0.30 kg 0.03% by weight
Antistatista ainetta 1) 1,0 kg 0,1 paino-%Antistatic agent 1) 1.0 kg 0.1% by weight
Pigmenttiä 20,0 kg 1,65 paino-% 15 1) Lankrostat 104, Harcros Chemical GroupPigment 20.0 kg 1.65 wt% 15) Lankrostat 104, Harcros Chemical Group
Esimerkki 4Example 4
Esimerkissä 1 kuvatulla tavalla valmistettiin päällyste käyttäen seuraavia aineosia ja määriä: 20 Etyleeni-butyyliakrylaatti- kopolymeeriä 1) 100,0 kg 18,4 paino-%As described in Example 1, a coating was prepared using the following ingredients and amounts: Ethylene-butyl acrylate copolymer 1) 100.0 kg 18.4% by weight
Polypropeeniä 25,0 kg 4,6 paino-%Polypropylene 25.0 kg 4.6% by weight
Kalsiumkarbonaattia 125,0 kg 23,0 paino-%Calcium carbonate 125.0 kg 23.0% by weight
Hiekkaa 250,0 kg 46,0 paino-% 2b Selluloosakuitua 30,0 kg 5,5 paino-%Sand 250.0 kg 46.0% by weight 2b Cellulose fiber 30.0 kg 5.5% by weight
Kalsiumstearaattia 0,05 kgCalcium stearate 0.05 kg
Stabilisaattoria 0,01 kgStabilizer 0.01 kg
Antistattista ainetta 1,0 kg 0,2 paino-%Antistatic agent 1.0 kg 0.2% by weight
Pigmenttiä 12,5 kg 2,3 paino-% 30 .· 1) NCPE 6427 Neste Oy, akrylaattipitoisuus 27 %, sulain- deksi 4 g/10 min 9 94438Pigment 12.5 kg 2.3% by weight 30. · 1) NCPE 6427 Neste Oy, acrylate content 27%, melting point 4 g / 10 min 9 94438
Esimerkki 5Example 5
Esimerkissä 1 kuvatulla tavalla valmistettiin päällyste käyttäen seuraavia aineosia ja määriä: Etyleeni-butyyliakrylaatti- 5 kopolymeeriä 1) 100,0 kg 20,4 paino-%As described in Example 1, a coating was prepared using the following ingredients and amounts: Ethylene-butyl acrylate copolymer 1) 100.0 kg 20.4% by weight
Polypropeeniä 2) 100,0 kg 20,4 paino-%Polypropylene 2) 100.0 kg 20.4% by weight
Kalsiumkarbonaattia 100,0 kg 20,4 paino-%Calcium carbonate 100.0 kg 20.4% by weight
Hiekkaa 150,0 kg 30,6 paino-%Sand 150.0 kg 30.6% by weight
Selluloosakuitua 30,0 kg 6,2 paino-% 10 Stabilisaattoria 0,05 kgCellulose fiber 30.0 kg 6.2% by weight Stabilizer 0.05 kg
Kalsiumstearaattia 0,05 kgCalcium stearate 0.05 kg
Pigmentti 10,0 kg 2,0 paino-% 1) NCPE 6427 15 2) XB 60 50H, satunnaiskopolymeeri, sulaindeksi 6,0 g/10 min « »Pigment 10.0 kg 2.0% by weight 1) NCPE 6427 15 2) XB 60 50H, random copolymer, melt index 6.0 g / 10 min «»
Claims (10)