ES378679A1 - A procedure to manufacture an artificial magnetic rock, very hard, resistant to wear, to the thermal variations, to the acids and to the bases. (Machine-translation by Google Translate, not legally binding) - Google Patents

A procedure to manufacture an artificial magnetic rock, very hard, resistant to wear, to the thermal variations, to the acids and to the bases. (Machine-translation by Google Translate, not legally binding)

Info

Publication number
ES378679A1
ES378679A1 ES378679A ES378679A ES378679A1 ES 378679 A1 ES378679 A1 ES 378679A1 ES 378679 A ES378679 A ES 378679A ES 378679 A ES378679 A ES 378679A ES 378679 A1 ES378679 A1 ES 378679A1
Authority
ES
Spain
Prior art keywords
weight
oxides
crystalline
translation
bases
Prior art date
Legal status (The legal status is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the status listed.)
Expired
Application number
ES378679A
Other languages
Spanish (es)
Current Assignee (The listed assignees may be inaccurate. Google has not performed a legal analysis and makes no representation or warranty as to the accuracy of the list.)
Individual
Original Assignee
Individual
Priority date (The priority date is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the date listed.)
Filing date
Publication date
Application filed by Individual filed Critical Individual
Publication of ES378679A1 publication Critical patent/ES378679A1/en
Expired legal-status Critical Current

Abstract

A method of manufacturing an artificial magmatic rock, very hard, resistant to wear, thermal variations, acids and bases, comprising, starting from a raw material that has a melting point of below 1500ºC, which is It originates from the combustion of stone coal and (or fly ash and/or the material from coal mine waste material piles, melting the raw material and adjusting the composition thereof by mixing additives, in such a way that obtain a composition consisting essentially of 45-60% by weight of SiO2, 15-40% by weight of trivalent metal oxides (Al, Fe3 +), with at least 40% by weight of said Fe2O3 oxides, 10-20% by weight of divalent oxides and 1-5% by weight of alkali oxides, maintaining the molten mixture at a temperature in the range of 1500ºC to 1350ºC, after the removal of the inherent gases, strain the melt in a temperature range of approximately one 350ºC to 1200ºC, crystallize it in a temperature range of around 1200ºC to 900ºC, during 0.5-4 hours, so that crystalline associations are formed, said crystalline associations consisting, said crystalline associations consisting essentially of 55 to 75% by weight of labradorite-feldspar composed of albite 30-40- anortite 60-70, 5-15% by weight of manoclinic pyroxene, 1-10% by weight of rhombic pyroxene (hypersthene) containing magnesium, 2-25%, by weight of oxides, having predominantly spinel structure and Fe2O3 modifications, and carrying out the crystallization heat treatment with a constant or gradually decreasing temperature gradient, thereafter cooling the crystallized melt at a rate of 80-20ºC/h, resulting in an artificial rock that has substantially a crystalline texture, the grain size of the crystals being around 2 to 20 μm. (Machine-translation by Google Translate, not legally binding)
ES378679A 1969-04-17 1970-04-16 A procedure to manufacture an artificial magnetic rock, very hard, resistant to wear, to the thermal variations, to the acids and to the bases. (Machine-translation by Google Translate, not legally binding) Expired ES378679A1 (en)

Applications Claiming Priority (1)

Application Number Priority Date Filing Date Title
HUTA001016 HU162340B (en) 1969-04-17 1969-04-17

Publications (1)

Publication Number Publication Date
ES378679A1 true ES378679A1 (en) 1973-02-01

Family

ID=11001738

Family Applications (1)

Application Number Title Priority Date Filing Date
ES378679A Expired ES378679A1 (en) 1969-04-17 1970-04-16 A procedure to manufacture an artificial magnetic rock, very hard, resistant to wear, to the thermal variations, to the acids and to the bases. (Machine-translation by Google Translate, not legally binding)

Country Status (14)

Country Link
JP (1) JPS5144131B1 (en)
AT (2) AT302152B (en)
BE (2) BE749139A (en)
CA (2) CA945570A (en)
CH (2) CH564494A5 (en)
CS (2) CS153075B2 (en)
ES (1) ES378679A1 (en)
FR (2) FR2045438A5 (en)
GB (2) GB1305641A (en)
HU (1) HU162340B (en)
NO (2) NO127003B (en)
RO (2) RO57531A (en)
SE (2) SE350957B (en)
SU (2) SU390711A3 (en)

Families Citing this family (7)

* Cited by examiner, † Cited by third party
Publication number Priority date Publication date Assignee Title
AU542869B2 (en) * 1980-12-29 1985-03-21 Nippon Kokan Kabushiki Kaisha Blue silicon based artificial stone
FR2697451B1 (en) * 1992-11-04 1995-01-13 Mediterranee Construction Indl Vitrification process for solid residues from incineration of household and / or industrial waste, and product from this process.
US6311522B1 (en) * 1999-07-13 2001-11-06 Slaytech Inc. Process for casting and forming slag products
CN102249567B (en) * 2010-09-27 2013-12-04 山东焦化集团有限公司 Method for producing reduced stone raw material utilizing melting slag
CN103224328B (en) * 2013-05-16 2016-04-27 承德华富玻璃技术工程有限公司 A kind of devitrified glass and preparation method thereof
CN114685049B (en) * 2020-12-30 2024-04-26 北京科立科盈科技有限公司 Method for preparing microcrystalline cast stone by using gas slag
CN113415999B (en) * 2021-05-25 2022-11-18 赵凤宇 Micro glass metal 3D printing micro powder for liquid printer

Also Published As

Publication number Publication date
CA950929A (en) 1974-07-09
DE2016752A1 (en) 1970-11-05
CS152354B2 (en) 1973-12-19
HU162340B (en) 1973-01-29
AT302151B (en) 1972-10-10
BE749138A (en) 1970-10-01
DE2016766A1 (en) 1970-11-05
NO127003B (en) 1973-04-24
BE749139A (en) 1970-10-01
GB1305642A (en) 1973-02-07
FR2045437A5 (en) 1971-02-26
NO127002B (en) 1973-04-24
GB1305641A (en) 1973-02-07
AT302152B (en) 1972-10-10
RO57531A (en) 1975-02-15
SE350957B (en) 1972-11-13
SU364158A3 (en) 1972-12-25
SE350958B (en) 1972-11-13
JPS5144131B1 (en) 1976-11-26
RO59495A (en) 1976-03-15
CS153075B2 (en) 1974-02-22
CH564494A5 (en) 1975-07-31
FR2045438A5 (en) 1971-02-26
CA945570A (en) 1974-04-16
DE2016766B2 (en) 1977-02-17
CH545257A (en) 1973-12-15
SU390711A3 (en) 1973-07-11
DE2016752B2 (en) 1976-01-22

Similar Documents

Publication Publication Date Title
ES403104A1 (en) Method for making glass ceramic materials
ES378679A1 (en) A procedure to manufacture an artificial magnetic rock, very hard, resistant to wear, to the thermal variations, to the acids and to the bases. (Machine-translation by Google Translate, not legally binding)
US3620781A (en) Partially stabilized zirconia refractory
US3928047A (en) Artificial stone and method for making the stone from a coal byproduct
ES378678A1 (en) A process of manufacturing artificial holocrystalline magnetic rocks. (Machine-translation by Google Translate, not legally binding)
JPS6228118B2 (en)
US2990289A (en) Method of making siliceous refractories
US2801183A (en) Refractories and methods of making them
US1897183A (en) Method of and material employed in the manufacture of refractory
US3677781A (en) Method of making cement clinkers
SU435048A1 (en) CERAMIC MASS FOR THE MAKING OF RODS
US3652306A (en) High density refractory shapes and method for production of same
US2231024A (en) Calcium oxide-chromium oxide refractory
US2106598A (en) Ceramic compositions and methods of making the same
GB962732A (en) Improvements in or relating to the growth of single crystals of corundum and gallium oxide
JP3852790B2 (en) Method for producing oxide ceramics
SU553226A1 (en) Ceramic mass for building products
DE2016766C3 (en) Artificial stone and method of making the same
US2617736A (en) Process for production of refractory siliceous material and products thereof or therewith obtained
JPS5933547B2 (en) Manufacturing method of crystallized aggregate
ES393962A1 (en) Producing refractory material
US3499777A (en) Process for producing substantially pure dead burned magnesia with high density and low porosity having decreased effective crystal surfaces for refractory or ceramic purposes
JPS63117985A (en) Production of single crystal of oxide
SU487861A1 (en) A method of making claydite
SU390711A1 (en) METHOD OF MANUFACTURING STONE CASTING