EP0000107A1 - Metallic or metallised article coated with a polyphenylene oxide film carrying reactive groups, its electrochemical preparation and its use - Google Patents

Metallic or metallised article coated with a polyphenylene oxide film carrying reactive groups, its electrochemical preparation and its use Download PDF

Info

Publication number
EP0000107A1
EP0000107A1 EP78400001A EP78400001A EP0000107A1 EP 0000107 A1 EP0000107 A1 EP 0000107A1 EP 78400001 A EP78400001 A EP 78400001A EP 78400001 A EP78400001 A EP 78400001A EP 0000107 A1 EP0000107 A1 EP 0000107A1
Authority
EP
European Patent Office
Prior art keywords
polymeric films
ortho
para
films obtained
formula
Prior art date
Legal status (The legal status is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the status listed.)
Granted
Application number
EP78400001A
Other languages
German (de)
French (fr)
Other versions
EP0000107B1 (en
Inventor
Jacques Emile Dubois
Minh-Chau Pham
Pierre Camille Lacaze
Current Assignee (The listed assignees may be inaccurate. Google has not performed a legal analysis and makes no representation or warranty as to the accuracy of the list.)
Bpifrance Financement SA
Original Assignee
Agence National de Valorisation de la Recherche ANVAR
Priority date (The priority date is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the date listed.)
Filing date
Publication date
Application filed by Agence National de Valorisation de la Recherche ANVAR filed Critical Agence National de Valorisation de la Recherche ANVAR
Publication of EP0000107A1 publication Critical patent/EP0000107A1/en
Application granted granted Critical
Publication of EP0000107B1 publication Critical patent/EP0000107B1/en
Expired legal-status Critical Current

Abstract

Films d'oxydes de polyphénylène comportant des groupes réactifs et leur préparation par voie électrochimique. Films obtenus à partir de monomères répondant à la formula: <IMAGE> dans laquelle R représente un groupe acyle de 1 à 7 atomes de carbone, un groupe hydroxy, carboxy, alcoxy-carbonyle, amino, alkylamino ou phénylamino, et n est un nombre entier qui peut être nul dans le cas où R est un groupe acyle. Usage pour la fixation par voie chimique d'enzymes, résines, laques ou peintures, notamment sur des surfaces métalliques ou métallisées.Polyphenylene oxide films comprising reactive groups and their preparation by electrochemical means. Films obtained from monomers corresponding to the formula: <IMAGE> in which R represents an acyl group of 1 to 7 carbon atoms, a hydroxy, carboxy, alkoxy-carbonyl, amino, alkylamino or phenylamino group, and n is a number integer which can be zero in the case where R is an acyl group. Use for the chemical fixing of enzymes, resins, lacquers or paints, in particular on metallic or metallized surfaces.

Description

La présente invention a pour objet des films d'oxydes de polyphénylène comportant des groupes réactifs et leur préparation par voie électrochimique.The present invention relates to polyphenylene oxide films comprising reactive groups and their preparation by electrochemical means.

L'invention concerne plus particulièrement de nouveaux polymères comportant des groupes chimiques réactifs et qui sont préparés par voie électrolytique et déposés sous forme de films sur des surfaces métalliques.The invention relates more particularly to new polymers comprising reactive chemical groups and which are prepared electrolytically and deposited in the form of films on metal surfaces.

La polymérisation par oxydation électrolytique du phénol et de certains de ses dérivés ainsi que le dépôt sur des surfaces métalliques des films polymères obtenus sont connus d'après le brevet des Etats-Unis d'Amé- rique N° 2.961.384. Par ailleurs, l'obtention de films polymères à partir de phénols disubstitués en positions 2 et 6 et leur dépôt électrolytique sur des métaux tels que le fer, le cuivre et le nickel sont décrits dans le brevet français N° 74.16158. Ces couches polymères sont très adhérentes, hydrophobes et uniformes et trouvent leur application dans la protection des métaux.The polymerization by electrolytic oxidation of phenol and certain of its derivatives, as well as the deposition on metal surfaces of the polymer films obtained are known from United States Patent No. 2,961,384. Furthermore, the production of polymer films from phenols disubstituted in positions 2 and 6 and their electrolytic deposition on metals such as iron, copper and nickel are described in French patent No. 74.16158. These polymer layers are very adherent, hydrophobic and uniform and find their application in the protection of metals.

Bien entendu, les divers polymères ainsi obtenus ne comportent pas de groupes réactifs. Certains auteurs ont cependant réussi à introduire des groupes chimiques réactifs dans des films polymères par des méthodes physiques élaborées..Dans un tel cas, des groupes carbonyles ont été introduits sur le surface du polymère (pcly- propyline) par action de l'oxygène après une irradiation de la surface par UV ou électrons (K. KATO, J. of Applied Polymer Science, 19 (1975), p.951-957). On a également pu introduire des groupes NH2 par le procédé de la décharge électrique. (J.R. Hollahan et Coll. J. Appl. Polym. Science, 13, (1969), p.807). Les rares groupes réactifs ainsi introduits dans les films sont distribués au hasard et par ailleurs les films ont tendance à vieillir en raison du grand nombre d'espèces radicalairès piégées (M. MILLARD, Synthe- sis of Organic Polymer Films in Plasmas, Chap. V, p.177, dans technics and Application of Plasma Chemistry. J.H. HOLLAHAN et A.T. BELL, 1974, J. WILEY).Of course, the various polymers thus obtained do not contain reactive groups. Some authors have however succeeded in introducing reactive chemical groups into polymer films by sophisticated physical methods. In such a case, carbonyl groups have been introduced on the surface of the polymer (pcly- propyline) by the action of oxygen after irradiation of the surface by UV or electrons (K. KATO, J. of Applied Polymer Science, 19 (1975), p.951-957). It was also possible to introduce NH 2 groups by the method of electric discharge. (JR Hollahan and Coll. J. Appl. Polym. Science, 13, (1969), p.807). The rare reactive groups thus introduced into the films are distributed at random and, moreover, the films tend to age due to the large number of trapped radical species (M. MILLARD, Synthesis of Organic Polymer Films in Plasmas, Chap. V , p.177, in technics and Application of Plasma Chemistry, JH HOLLAHAN and AT BELL, 1974, J. WILEY).

Le but de la présente invention est de réaliser, par le procédé de polymérisation électrolytique mentionné ci-dessus, la synthèse de polymères réactifs qui se caractérise par la présence, dans chaque maillon de leur chaîne, de groupes fonctionnels capables de réagir selon une réaction chimique spécifique.The object of the present invention is to carry out, by the electrolytic polymerization process mentioned above, the synthesis of reactive polymers which is characterized by the presence, in each link of their chain, of functional groups capable of reacting according to a chemical reaction specific.

Les films polymères de l'invention sont obtenus à partir de phénols répondant à la formule

Figure imgb0001
dans laquelle

  • R représente un groupe acyle de 1 à 7 atomes de carbone, un groupe hydroxy, carboxy, alcoxycarbonyle, amino, alkylamino ou phénylamino, et
  • n est un nombre entier, qui peut être nul dans le cas où R est un groupe acyle.
The polymer films of the invention are obtained from phenols corresponding to the formula
Figure imgb0001
 in which
  • R represents an acyl group of 1 to 7 carbon atoms, a hydroxy, carboxy, alkoxycarbonyl, amino, alkylamino or phenylamino group, and
  • n is an integer, which can be zero in the case where R is an acyl group.

L'invention concerne plus particulièrement les films polymères obtenus à partir de monomères de formule(I) dans laquelle -(CH2)n R représente un groupe formyle, acétyle, propionyle, benzoyle, oxo-3 butyle, hydroxyméthyle, carboxyméthyle aminoéthyle ou anilinométhyle.The invention relates more particularly to the polymer films obtained from monomers of formula (I) in which - (CH2) n R represents a formyl, acetyl, propionyl, benzoyl, 3-oxo-butyl, hydroxymethyl, carboxymethyl aminoethyl or anilinomethyl group.

Les polymères de l'invention comportent donc comme groupe fonctionnel réactif un groupe carbonyle, hydroxy, carboxy ou amino par motif.The polymers of the invention therefore have as reactive functional group a carbonyl, hydroxy, carboxy or amino group per unit.

Selon l'invention les films polymères sont préparés par oxydation anodique des phénols monomères (I) dans un bain électrolytique alcoolique et fortement basique. Les polymères formés se déposent directement sur l'anode, le cas échéant un substrat conducteur - ou rendu conducteur - que l'on désire revêtir d'une mince couche de polymère.According to the invention, the polymer films are prepared by anodic oxidation of the monomeric phenols (I) in an alcoholic and strongly basic electrolytic bath. The polymers formed are deposited directly on the anode, where appropriate a conductive substrate - or made conductive - which it is desired to coat with a thin layer of polymer.

Les alcools utilisables pour le bain sont des alcools inférieurs, tels que le méthanol, éthanol, propanol ou isopropanol, ou un mélange d'alcool inférieur et de polyol tel que le glycol ou le glycérol.The alcohols usable for the bath are lower alcohols, such as methanol, ethanol, propanol or isopropanol, or a mixture of lower alcohol and polyol such as glycol or glycerol.

Les bases fortes peuvent être par exemple l'hydroxyde de sodium ou de potassium, ou bien l'amidure de sodium. Leur concentration peut être de 0,05 à 1 M, de préférence 0,1 à 0,3 M pour assurer le bon déroulement de l'électrolyse.The strong bases can be, for example, sodium or potassium hydroxide, or else sodium amide. Their concentration can be from 0.05 to 1 M, preferably 0.1 to 0.3 M to ensure the smooth running of the electrolysis.

Le phénol monomère est utilisé à des concentrations d'au moins 6 g/1 d'électrolyte, de préférence de 12 à 25 g/1.The monomeric phenol is used at concentrations of at least 6 g / l of electrolyte, preferably from 12 to 25 g / l.

Par ailleurs il est recommandé de prévoir environ 3 g de monomère par dm2 de substrat à revêtir.Furthermore, it is recommended to provide approximately 3 g of monomer per dm 2 of substrate to be coated.

L'anode ou le substrat conducteur devant être re- couvert par le polymère de l'invention peut être constitué par la plupart des métaux courants tels que le fer, l'argent, le nickel, le chrome, le cuivre, l'or, le platine, etc., ou leurs alliages.The anode or the conductive substrate to be coated with the polymer of the invention can consist of most common metals such as iron, silver, nickel, chromium, copper, gold, platinum, etc., or their alloys.

L'électrolyse est effectuée dans une cuve (par exemple en acier) de manière habituelle à température ambiante avec une tension de sortie initiale du générateur dé l'ordre de 10 Volt et ne densité de courant initiale de O,1 à 1 A/dm2. Le film polymère se forme rapidement sur la surface de l'anode (ou du substrat) et un recouvrement total, obtenu en général entre 5 à 30 minutes, peut être décelé lorsque le courant devient très faible.The electrolysis is carried out in a tank (for example made of steel) in the usual way at room temperature with an initial output voltage of the generator of the order of 10 Volt and an initial current density of 0.1 to 1 A / dm 2 . The polymer film forms quickly on the surface of the anode (or of the substrate) and a total covering, generally obtained between 5 to 30 minutes, can be detected when the current becomes very weak.

Après l'électrolyse, le substrat revêtu du film polymère est lavé à l'eau puis à l'alcool afin d'éliminer les traces résiduelles de base, de phénol monomère et des produits secondaires éventuels.After the electrolysis, the substrate coated with the polymer film is washed with water and then with alcohol in order to remove the residual traces of base, of phenol monomer and of any secondary products.

Les films polymères obtenus selon l'invention sont homogènes, continus, uniformes, de faible épaisseur (300 0 à 3500 A selon le polymère) insolubles dans l'eau et les alcools, très adhérents et hydrophiles selon le groupe réactif qu'ils comportent.The polymer films obtained according to the invention are homogeneous, continuous, uniform, thin (300 0 to 3500 A depending on the polymer) insoluble in water and alcohols, very adherent and hydrophilic depending on the reactive group they contain.

Les exemples suivants illustrent l'invention.The following examples illustrate the invention.

Exemple 1 :Example 1: Polymère de l'alcool métahydroxybenzylique ou poly(oxyde de hydroxyméthyl-2 phénylène-1,4).Polymer of metahydroxybenzyl alcohol or poly (2-hydroxymethyl-1,4-phenylene oxide).

On effectue l'électrolyse d'une solution de 0,62 g (O,1 M) d'alcool métahydroxybenzylique et 0,6 g d'hydroxyde de sodium (0,3 M) dans 50 cm3 d'alcool méthylique en utilisant comme anode du cuivre massif ayant une surface de 12 cm2. On applique une différence de potentiel ΔV = 0,94 volt par rapport à une électrode de calomel saturé (ECS). La densité de courant est initialement ii = 2 mA/cm2 et tombe à if = 0,5 mA/cm2 au bout de t = 40 minutes.Electrolysis of a solution of 0.62 g (0.1 M) of metahydroxybenzyl alcohol and 0.6 g of sodium hydroxide (0.3 M) in 50 cm 3 of methyl alcohol is carried out using as solid copper anode with a surface of 12 cm 2 . A potential difference ΔV = 0.94 volts is applied relative to a saturated calomel electrode (DHW). The current density is initially i i = 2 m A / cm 2 and drops to i f = 0.5 mA / cm 2 after t = 40 minutes.

On obtient un film ayant une épaisseur de 2500 A mesuré avec un appareil interférentiel Tolansky monté sur un microscope métalloplan Leitz.A film having a thickness of 2500 A is obtained, measured with a Tolansky interference device mounted on a Leitz metalloplan microscope.

Exemple 2 :Example 2: Polymère de l'acide o-hydroxyphénylacétique ou poly(oxyde de carboxyméthyl-2 phénylène-1,4).Polymer of o-hydroxyphenylacetic acid or poly (2-carboxymethyl-1,4-phenylene oxide).

De la même manière que dans l'exemple 1, on effectue l'électrolyse d'une solution de 0,76 g (O,1 M) d'acide salicylique et 0,6 g de NaOH dans 50 cm3 d'alcool méthylique, en utilisant comme anode un miroir de fer (fer évaporé sur une plaque de verre) et en appliquant une tension de Δ V = 0,85 V/ECS

Figure imgb0002
On obtient un film polymère ayant 1200 A d'épaisseur.In the same way as in Example 1, electrolysis is carried out of a solution of 0.76 g (0.1 M) of salicylic acid and 0.6 g of NaOH in 50 cm 3 of methyl alcohol, using an iron mirror as anode (iron evaporated on a glass plate) and applying a voltage of Δ V = 0.85 V / DHW
Figure imgb0002
 A polymer film having 1200 A thickness is obtained.

Exemple 3 :Example 3: Polymère de la p-hydroxyphényl-2 éthylamine ou poly(oxyde d'aminoéthyl-4 phénylène-1,2).Polymer of p-hydroxyphenyl-2 ethylamine or poly (4-aminoethyl-1,2-phenylene oxide).

  • a) De la même manière que dans l'exemple 1, on effectue l'électrolyse d'une solution méthanolique (50 cm3) de 0,68 g de parahydroxyphényl-2 éthylamine (Tyramine) et de 0,6 g de NaOH en utilisant une anode en cuivre massif de 18 cm2. Δ V = 0,5 V/ECS.
    Figure imgb0003
    Le film obtenu a 2 500 A d'épaisseur.    a) In the same way as in Example 1, electrolysis of a methanolic solution ( 50 cm 3 ) of 0.68 g of 2-parahydroxyphenyl ethylamine (Tyramine) and 0.6 g of NaOH using an 18 cm 2 solid copper anode. Δ V = 0.5 V / DHW.
    Figure imgb0003
     The film obtained is 2,500 A thick.
  • b) On a répété l'expérience ci-dessus en remplaçant l'anode cuivre par un miroir de fer de 8,8 cm2. ΔV = 0,9 V/ECS.
    Figure imgb0004
         b) The above experiment was repeated, replacing the copper anode with an 8.8 cm 2 iron mirror. ΔV = 0.9 V / DHW.
    Figure imgb0004
Exemple 4 :Example 4: Polymère de N-o-hydroxybenzyl-aniline ou poly (oxyde d'anilino-méthyl-2 phénylène-1,4).Polymer of N-o-hydroxybenzyl-aniline or poly (anilino-methyl-2-phenylene-1,4-oxide).

  • a) On a effectué l'électrolyse de la même manière que dans les exemples précédents mais en faisant varier la différence de potentiel ΔV de O à 1,3 V/ECS et en utilisant un miroir de fer de 9 cm2.
    Figure imgb0005
     Epaisseur du film : 3000 A    a) The electrolysis was carried out in the same manner as in the previous examples but by varying the potential difference ΔV from O to 1.3 V / ECS and using an iron mirror of 9 cm 2 .
    Figure imgb0005
     E p has isseur film: 30 00 A
  • b) On a répété l'expérience avec du fer massif (7 cm2) et tension constante.
    Figure imgb0006
         b) The experiment was repeated with solid iron (7 cm 2 ) and constant tension.
    Figure imgb0006
Exemple 5 :Example 5: Polymère de p-hydroxyphényl-4 butanone-2.Polymer of p-hydroxyphenyl-4 butanone-2.

  • a) De la même manière que dans les exemples 1 à 3, on effectue l'électrolyse de 0,82 g (O,1M) de p-hydroxyphényl1-4 butanone-2 en utilisant une anode de fer massif de 5 cm2.
    Figure imgb0007
    épaisseur du film : 3 500 A.    a) In the same manner as in Examples 1 to 3, the electrolysis of 0.82 g (0.1 M) of p-hydroxyphenyl 1-4 butanone-2 is carried out using a 5 cm 2 solid iron anode.
    Figure imgb0007
     film thickness: 3,500 A.
  • b) on utilise une anode d'acier de 10 cm2.
    Figure imgb0008
         b) a 10 cm 2 steel anode is used.
    Figure imgb0008
  • c) On utilise une anode en titane massif de 16 cm2.
    Figure imgb0009
         c) A solid titanium anode of 16 cm 2 is used .
    Figure imgb0009

Dans is tableau I

Figure imgb0010
sont rassemblés, en plus des exemples précédents, divers phénols substitués qui ont été polymérisés selon l'invention. Toutes les polymérisations ont été suivies in situ par polaromicrotri- bométrie (PMT) qui permet de détecter les modifications physicochimiques sur la surface métallique (voir par exemple J.E. DUBOIS, P.C. LACAZE, R. COURTEL, C.C. HERM IN, D. MAUGIS, J. of Electrochem. Soc., 122, (1975) p 154).
Figure imgb0011
Figure imgb0012
Figure imgb0013
Figure imgb0014
 In table I
Figure imgb0010
are combined, in addition to the preceding examples, various substituted phenols which have been polymerized according to the invention. All the polymerizations were followed in situ by polaromicrotribometry (PMT) which makes it possible to detect the physicochemical modifications on the metal surface (see for example JE DUBOIS, PC LACAZE, R. COURTEL, CC HERM IN, D. MAUGIS, J. of Electrochem. Soc., 122, (1975) p 154).
Figure imgb0011
Figure imgb0012
Figure imgb0013
Figure imgb0014

Les films polymères ont été traités par des agents chimiques caractéristiques pour la vérification de la présence et de la réactivité des groupes chimiques fonctionnels. Les polymères comportant le groupe carbonyle ont été traités par une solution éthanolique de 1 % de dini- tro-2,4 phényl-hydrazine (2,4 DNPH) et de 2 % HCl.concentré ; les électrodes étaient trempées pendant 5 minutes dans cette solution à l'ébullition puis lavées dans de l'éthanol par agitation ultrasonique. Les polymères comportant le groupe hydroxy ou amino ont été traités par du chlorure d'acétyle.The polymer films were treated with characteristic chemical agents to verify the presence and reactivity of the functional chemical groups. The polymers comprising the carbonyl group were treated with an ethanolic solution of 1% 2,4-dinitro-phenyl-hydrazine (2,4 DNPH) and 2% concentrated HCl; the electrodes were soaked for 5 minutes in this boiling solution and then washed in ethanol by ultrasonic stirring. The polymers comprising the hydroxy or amino group have been treated with acetyl chloride.

Les films polymères de l'invention ainsi que les films traités par les agents chimiques ont été identifiés par spectroscopie IR à réflexions multiples et/ou par ESCA (Electron Spectroscopy for Chemical Analysis).The polymeric films of the invention as well as the films treated with chemical agents were identified by multiple-reflection IR spectroscopy and / or by ESCA (Electron Spectroscopy for Chemical Analysis).

Dans le tableau II suivant sont indiqués les pics caractéristiques des groupes chimiques pour des polymères dont les spectres IR sont bien résolus, tandis que des résultats obtenus en ESCA seront donnés dans le tableaullI pour les autres.In Table II below are indicated the characteristic peaks of the chemical groups for polymers whose IR spectra are well resolved, while results obtained in ESCA will be given in Table 1 for the others.

Dans tous les spectres IR obtenus, la bande correspondant au groupe OH phénolique est complètement absente ; par contre le pic caractérisant le groupe polyoxyde apparaît aux environs de 1200 cm 1. La présence de très intenses bandes d'absorption C=O, correspondant soit à la fonction aldéhyde (1700 cm-1) soit cétone (1680 cm-1) prouve que ces groupes restent inattaqués durant l'électrolyse.

Figure imgb0015
Figure imgb0016
 In all the IR spectra obtained, the band corresponding to the phenolic OH group is completely absent; on the other hand, the peak characterizing the polyoxide group appears around 1200 cm 1 . The presence of very intense absorption bands C = O, corresponding either to the aldehyde function (1700 cm -1 ) or ketone (1680 cm -1 ) proves that these groups remain unaffected during electrolysis.
Figure imgb0015
Figure imgb0016

L'analyse ESCA des anodes confirme aussi la présence des polymères sur leur surface. Les spectres C1s mettent en évidence les groupes chimiques distincts par . les valeurs des énergies de liaison caractéristiques. On obtient les mêmes résultats pour les dérivés ortho, méta ou para.

Figure imgb0017
ESCA analysis of the anodes also confirms the presence of polymers on their surface. The C 1s spectra show the distinct chemical groups par. the values of the characteristic bond energies. The same results are obtained for the ortho, meta or para derivatives.
Figure imgb0017

Compte tenu de la présence d'un groupe chimique réactif sur toute.la surface les films polymères de l'invention peuvent être utilisés pour le greffage de diverses matières réagissant sur ces fonctions.Given the presence of a reactive chemical group on the entire surface, the polymer films of the invention can be used for the grafting of various materials reacting on these functions.

Ainsi il est possible de fixer des enzymes ou bien de faire réagir d'autres composés comportant des groupes réactifs, par exemple des chlorures ou anhydrides d'acides sur les films polymères portant un.groupe hydroxy ou amine (ce qui permet d'obtenir une surface de poly-ester et respectivement poly-amide). Cette propriété permet l'utilisation des films polymères de l'invention comme couches intermédiaires pour la fixation des résines, laques et peintures, notamment sur les métaux auxquels celles-ci adhèrent très mal.Thus it is possible to fix enzymes or else to react other compounds comprising reactive groups, for example chlorides or acid anhydrides on polymer films carrying a hydroxy or amine group (which makes it possible to obtain a surface of poly-ester and respectively poly-amide). This property allows the use of the polymer films of the invention as intermediate layers for fixing resins, lacquers and paints, especially on metals to which they adhere very poorly.

Claims (15)

1.- Films d'oxydes de polyphénylène obtenus à partir de monomères répondant à la formule :
Figure imgb0018
dans laquelle : R représente un groupe acyle de 1 à 7 atomes de carbone, un groupe hydroxy, carboxy, alcoxycarbonyle, amino, alkylamino.ou phénylamino, et n est un nombre entier qui peut être nul dans le cas où R est un groupe acyle. 1.- Films of polyphenylene oxides obtained from monomers corresponding to the formula:
Figure imgb0018
 in which : R represents an acyl group of 1 to 7 carbon atoms, a hydroxy, carboxy, alkoxycarbonyl, amino, alkylamino or phenylamino group, and n is an integer which can be zero in the case where R is an acyl group. 2.- Films d'oxydes de polyphénylène selon la revendication 1, obtenus à partir de monomères répondant à la formule (I) dans laquelle -(CH2)n-R représente un groupe formule, acétyle, propionyle, benzoyle, oxo-3 butyle, hydroxyméthyle, carboxyméthyle, aminoéthyle ou anilinométhyle.2. Polyphenylene oxide films according to claim 1, obtained from monomers corresponding to formula (I) in which - (CH 2 ) n -R represents a group of formula, acetyl, propionyl, benzoyl, oxo-3 butyl, hydroxymethyl, carboxymethyl, aminoethyl or anilinomethyl. 3.- Films polymères obtenus à partir d'ortho-, méta- ou para-hydroxybenzaldéhyde.3.- Polymeric films obtained from ortho-, meta- or para-hydroxybenzaldehyde. 4.- Films polymères obtenus à partir d'ortho-, . méta- ou para-hydroxyacétophénone.4.- Polymeric films obtained from ortho-,. meta- or para-hydroxyacetophenone. 5.- Films polymères obtenus à partir d'ortho-ou para-hydroxypropiophénone.5.- Polymeric films obtained from ortho- or para-hydroxypropiophenone. 6.- Films polymères obtenus à partir d'ortho-ou para-hydroxybenzophénone.6.- Polymeric films obtained from ortho- or para-hydroxybenzophenone. 7.- Films polymères obtenus à partir de parahydroxyphényl-4 butanone-2.7.- Polymeric films obtained from 4-parahydroxyphenyl-2-butanone. 8.- Films polymères obtenus à partir d'alcool ortho-, méta- ou para-hydroxy-benzylique.8.- Polymeric films obtained from ortho-, meta- or para-hydroxy-benzyl alcohol. 9.- Films polymères obtenus à partir de p-hydroxy-phényl-2 éthylamine.9.- Polymeric films obtained from p-hydroxy-phenyl-2 ethylamine. 10.- Films polymères obtenus à partir de N-ortho- hydroxybenzyl-aniline.10.- Polymeric films obtained from N-ortho-hydroxybenzyl-aniline. 11.- Films polymères obtenus à partir d'acide or tho-, méta- ou para-hydroxyphénylacétique.11.- Polymeric films obtained from tho-, meta- or para-hydroxyphenylacetic acid. 12.- Procédé de préparation par voie électrolytique des films d'oxydes de polyphénylène définis dans la revendication 1 ou la revendication 2, procédé caractérisé en ce qu'on effectue une oxydation anodique de phénols de formule (I) dans un bain électrolytique alcoolique et fortement basique.12.- A process for the electrolytic preparation of polyphenylene oxide films defined in claim 1 or claim 2, process characterized in that an anodic oxidation of phenols of formula (I) is carried out in an alcoholic electrolytic bath and strongly basic. 13.- Application des films polymères.selon l'une quelconque des revendications 1 à 11 pour la fixation d'enzymes.13.- Application of polymer films. According to any one of claims 1 to 11 for the fixation of enzymes. 14.- Application'des films polymères selon l'une quelconque des revendications 1 à 11 pour le greffage de résines.14.- Application'des polymer films according to any one of claims 1 to 11 for grafting resins. 15.- Application des films polymères selon l'une quelconque des revendications 1 à 11 pour la fixation de laques ou de peintures notamment sur des surfacesmétalli- ques ou métallisées.15.- Application of the polymer films according to any one of claims 1 to 11 for the attachment of lacquers or paints, in particular to metallic or metallized surfaces.
EP78400001A 1977-06-10 1978-06-01 Metallic or metallised article coated with a polyphenylene oxide film carrying reactive groups, its electrochemical preparation and its use Expired EP0000107B1 (en)