DE922188C - Corrosion protection and sealing agent in tape form as external protection for metallic surfaces - Google Patents

Corrosion protection and sealing agent in tape form as external protection for metallic surfaces

Info

Publication number
DE922188C
DE922188C DET4175A DET0004175A DE922188C DE 922188 C DE922188 C DE 922188C DE T4175 A DET4175 A DE T4175A DE T0004175 A DET0004175 A DE T0004175A DE 922188 C DE922188 C DE 922188C
Authority
DE
Germany
Prior art keywords
paraffin
molecular weight
paraffins
synthetic
low molecular
Prior art date
Legal status (The legal status is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the status listed.)
Expired
Application number
DET4175A
Other languages
German (de)
Inventor
Jaques Trachet
Current Assignee (The listed assignees may be inaccurate. Google has not performed a legal analysis and makes no representation or warranty as to the accuracy of the list.)
Individual
Original Assignee
Individual
Priority date (The priority date is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the date listed.)
Filing date
Publication date
Application filed by Individual filed Critical Individual
Application granted granted Critical
Publication of DE922188C publication Critical patent/DE922188C/en
Expired legal-status Critical Current

Description

Korrosionsschutz- und Abdichtungsmittel in Bandform als Außenschutz für metallische Oberflächen Die Erfindung bezieht sich sowohl auf korrosionsfeste, paraffinartige Schutzbekleidungen, insbesondere auf Metallen ergebende Überzugsmittel, die Bandform besitzen können, als auch auf das Verfahren zur Herstellung solcher Bänder.Corrosion protection and sealing agent in tape form as external protection for metallic surfaces The invention relates to both corrosion-resistant, paraffin-like protective clothing, in particular coating agents that result in metals, may have the tape shape, as well as the process for making such Tapes.

Die Verwendung paraffinartiger Kohlenwasserstoffverbindungen für sich oder auch in Mischungen, denen Füllmittel zugesetzt sein können, als korrosionsfester Bekleidungsschutz ist bislang mangels eines widerstandsfähigen, zum Übertragen der genannten Bekleidung auf das Metall geeigneten Mittels gescheitert.The use of paraffin-like hydrocarbon compounds for themselves or in mixtures to which fillers can be added, as more corrosion-resistant Clothing protection is so far due to the lack of a resistant, to transmit the Said clothing on the metal suitable means failed.

Gerade aber das Übertragungsmittel, z. B. ein Träger aus Cellulose (oder Derivaten), hat eine besondere Bedeutung in der so erhaltenen Bekleidung. Tatsächlich bleiben die vorerwähnten Kohlenwasserstoffverbindungen, ob sie mit Füllstoffen versetzt sind oder nicht, in Mischung mit Wachsen oder Harzen amorph, und folglich ist der Träger unvermeidlich das verbindende Element der Schutzbekleidung.But just the transmission medium, z. B. a carrier made of cellulose (or derivatives), has a special meaning in the clothing obtained in this way. Indeed, the aforementioned hydrocarbon compounds remain whether they contain fillers are mixed or not, amorphous in admixture with waxes or resins, and consequently the wearer is inevitably the unifying element of protective clothing.

Die Cellulose als Träger aber ist nicht ohne Nachteile, von denen die wesentlichsten a) Aufsaugung der Feuchtigkeit, b) Empfindlichkeit gegenüber Gärungserscheinungen allgemein, Bakterien u. dgl. sind. Hiergegen hat man Hilfsmittel vorgeschlagen, die sich aber nicht als besonders wirksam erwiesen haben. Denn der Hauptzweck, nämlich ein korrosionsfester Schutz der Metalle, wird verfehlt, wenn der Träger der Verbindung selber das Element- der Zerstörung in der Verkleidung sein würde. Denn ein. solcher Träger würde, nachdem er eine gewisse Zeit den korrosiven Einflüssen ausgesetzt ist, die guten Schutzeigenschaften der genannten Kohlenwasserstoffverbindungen aufheben, sei es durch Absorbieren von Wasser, sei es durch Fäulnis.Cellulose as a carrier, however, is not without its disadvantages the most essential a) absorption of moisture, b) sensitivity to it General fermentation phenomena, bacteria and the like. You have tools against this suggested but not found to be particularly effective. Because the The main purpose, namely a corrosion-resistant protection of the metals, is missed if the Bearer of the connection itself the element of destruction in the disguise would be. Because a. such carrier would after having a certain Time is exposed to corrosive influences, the good protective properties of the cancel said hydrocarbon compounds, be it by absorbing water, be it by putrefaction.

Durch vorliegende Erfindung werden die obenerwähnten, den Trägern aus Cellulose (oder Derivaten) anhaftenden Nachteile gänzlich vermieden durch Anwendung bestimmter hochpolymerisierter, synthetischer Paraffine als Träger für die Bekleidung aus Paraffinen oder paraffinartigen, z. B. protoparaffinartigen Kohlenwasserstoffverbindungen von mittlerem oder niedrigem Molekulargewicht, vorzugsweise in Bandform, weil sich Bänder leicht auf alle möglichen Metallformen (Leitungen, Profile usw.) aufbringen lassen.The present invention provides the above-mentioned carriers Adhering disadvantages from cellulose (or derivatives) are completely avoided by use certain highly polymerized, synthetic paraffins as a carrier for clothing from paraffins or paraffin-like, e.g. B. protoparaffinic hydrocarbon compounds of medium or low molecular weight, preferably in ribbon form, because Easily apply tapes to all kinds of metal shapes (pipes, profiles, etc.) permit.

Gemäß der Erfindung werden bestimmte hochpolymerisierte, synthetische Paraffine verwendet, die die Fähigkeit besitzen, sich formen zu lassen neben der Eigenschaft, unter gewissen Bedingungen. in protoparaffinartigen oder paraffinartigen Kohlenwasserstoffverbindungen von geringem Molekulargewicht löslich zu sein.In accordance with the invention, certain highly polymerized, synthetic Paraffins are used, which have the ability to be shaped in addition to the Property, under certain conditions. in protoparaffinic or paraffinic To be soluble in hydrocarbon compounds of low molecular weight.

Auf diese Weise gelingt die Erzeugung a) einer in sich verfestigten Bekleidung, die aus paraffinartigen oder protoparaffinartigen Kohlenwasserstoffverbindungen von mittlerem oder niederem Molekulargewicht zusammengesetzt ist (vorzugsweise mit Füllstoffen versetzt) und die bei Bandform des Trägers die beiden Außenflächen der Bekleidung bildet, während die angegebenen synthetischen Kohlenwasserstoffverbindungen mit hohem Molekulargewicht darin den Träger bilden, b) einer plastischen Masse mit neuen Eigenschaften, die sich auf irgendeinen Metallkörper aufbringen läßt und deren Schutzeigenschaften nicht mehr durch das Übertragungsmittel beeinträchtigt werden.In this way, the production of a) a solidified one succeeds Clothing made from paraffinic or protoparaffinic hydrocarbon compounds is composed of medium or low molecular weight (preferably with Fillers added) and the two outer surfaces of the band shape of the carrier Clothing forms while the specified synthetic hydrocarbon compounds with high molecular weight therein form the carrier, b) a plastic mass with new properties that can be applied to any metal body and their Protective properties are no longer impaired by the transmission medium.

Die Erfindung bietet auf Grund der Eigenschaften, welche die verwendeten paraffinartigen, synthetischen Kohlenwasserstoffverbindungen mit hohen Molekulargewichten besitzen, die Möglichkeit, diese ohne Zuhilfenahme eines zersetzlichen Übertragungsmittels auf eine zu schützende Fläche aufzutragen und eine Bekleidung zu erzielen, die die ihr gegebene Form beibehält selbst unter gewissen mechanischen Ein= wirkungen, was nicht der Fall ist bei paraffinartigen Kohlenwasserstoffverbindungen mit weniger hohem Molekulargewicht.The invention offers, by virtue of the properties, which it employs paraffin-like, synthetic hydrocarbon compounds with high molecular weights have the possibility of doing this without the aid of a decomposable transmission medium to apply to a surface to be protected and to achieve clothing that its given form retains what even under certain mechanical influences is not the case with paraffin-like hydrocarbon compounds with less high molecular weight.

Die Verwendung solcher synthetischen hohen Polymere würde eine vollkommene sein, wenn die so gebildete Bekleidung eine gute Haftfähigkeit auf der Grundfläche besitzen würde. Das ist leider nicht der Fall, denn infolge von Stockflecken, Splittern, Mangel an Elastizität, schwacher Haftfähigkeit bleibt eine solche Bekleidung unwirksam.The use of such synthetic high polymers would be perfect if the clothing formed in this way has good adhesion to the base surface would own. Unfortunately, this is not the case, because due to mold stains, splinters, Such clothing remains ineffective due to a lack of elasticity and poor adhesion.

Anders ausgedrückt: die Bildung einer intergralen paraffinartigen Bekleidung, die gleichzeitig eine gute Haftung an der zu schützenden Fläche, Plastizität und eine gewisse Widerstandsfähigkeit gegen Deformation durch mechanische Einflüsse besitzt, war das sich stellende Problem. Die den Gegenstand der Erfindung bildenden Überzugsmassen besitzen die zur Lösung dieses Problems erforderlichen Eigenschaften.In other words: the formation of an integral paraffin-like Clothing that at the same time has good adhesion to the surface to be protected, plasticity and a certain resistance to deformation due to mechanical influences possessed was the problem at hand. The forming the subject of the invention Coating compounds have the properties required to solve this problem.

Unter paraffinartiger Kohlenwasserstoffverbindung versteht man jede Kohlenwasserstoffverbindung der Reihe C"H2n,+s allein oder in Mischung mit seinem Homologen, um ein Öl oder halbfestes Wachs mit beliebigem Schmelzpunkt oder ein Wachs mit genauer bezeichnetem Schmelzpunkt zu bilden, wie es insbesondere bekannt ist unter dem Namen der Paraffine.A paraffin-like hydrocarbon compound is understood to mean any Hydrocarbon compound of the series C "H2n, + s alone or in a mixture with his Homologs to an oil or semi-solid wax with any melting point or a To form wax with a specified melting point, as it is known in particular is under the name of paraffins.

Dabei soll die Bezeichnung gleichwohl die unbearbeiteten Produkte (mit irgendwelchen Spuren von Insaturationen) wie auch die verfeinerten Produkte decken, und der Ausdruck »paraffinartig« vor allen Dingen das Vorherrschen des Kennzeichens der Sättigung der Kohlenwasserstoffe andeuten.The designation should nevertheless include the unprocessed products (with any traces of insaturation) as well as the refined products cover, and the expression "paraffin-like" above all the predominance of the indicator indicate the saturation of the hydrocarbons.

An sich sind verformbare Überzugsmittel für die verschiedensten Gegenstände, wie Holz, Stein und andere festen Stoffe, bestehend aus hochpolymeren (Molekulargewicht zooo bis 30 000) synthetischen Kohlenwasserstoffe, ferner Paraffinen und gegebenenfalls Füllstoffen bekannt.Deformable coating agents are per se for a wide variety of objects, such as wood, stone and other solid materials, consisting of high polymer (molecular weight zooo to 30,000) synthetic hydrocarbons, also paraffins and possibly Known fillers.

Demgegenüber handelt es sich bei den für die Zwecke der vorliegenden Erfindung verwendeten paraffinartigen synthetischen Kohlenwasserstoffen mit hohem Molekulargewicht (hochpolymere synthetische Paraffine) um Polymere gemäß der allgemeinen Strukturformel C H3 - (C H2) n - C H = C HZ.In contrast, it concerns with the purposes of the present Invention used paraffin-like synthetic hydrocarbons with high Molecular weight (high polymer synthetic paraffins) around polymers according to the general Structural formula C H3 - (C H2) n - C H = C HZ.

Die anwendbaren Molekulargewichte schwanken zwischen 500 und 3o ooo; für den Erfindungszweck kommen vorzugsweise Werte zwischen 8ooo und 2o ooo in Frage.The applicable molecular weights vary between 500 and 30,000; Values between 8,000 and 2o,000 are preferred for the purpose of the invention.

Diese Produkte werden zur Zeit durch Polymerisation von Äthylen unter hohem Drucke erzeugt und sind allgemein unter dem Namen Polyäthylen beschrieben. Diese Polyäthylene sind unter verschiedenen Namen und in verschiedenen Formen im Handel, z. B. als Körner, Pulver (das die Formgebung gestattet) oder unmittelbar in bearbeiteter Form, z. B. als Filme.These products are currently being made by the polymerization of ethylene high pressure and are generally described under the name polyethylene. These polyethylenes are available under various names and in various forms Trade, e.g. B. as grains, powder (which allows shaping) or directly in processed form, e.g. B. as films.

Ausführungsbeispiele Herstellung eines paraffinartigen Bekleidungsmittels in Bandform Die paraffinartigen Kohlenwasserstoffverbindungen von niedrigem Molekulargewicht werden geschmolzen, dann gegebenenfalls mit einem oder mehreren Füllstoffen gemischt und in Behälter eingeführt, die so eingerichtet sind, daß sie den Durchlauf der vorher in Filmform gebrachten hochpolymerisierten synthetischen Paraffine gestatten.EXEMPLARY EMBODIMENTS Production of a paraffin-like clothing material in ribbon form The paraffin-like hydrocarbon compounds of low molecular weight are melted, then optionally mixed with one or more fillers and introduced into containers which are adapted to allow the passage of the allow highly polymerized synthetic paraffins previously made into film form.

In der Zeichnung ist ein Behälter z dargestellt, in dem die paraffinartigen Kohlenwasserstoffverbindungen von niedrigem Molekulargewicht eingefüllt sind. Mit 2 ist der Weg des synthetischen hohen Polymeres angedeutet, das um Rollen 3 geführt ist.In the drawing, a container z is shown, in which the paraffin-like Low molecular weight hydrocarbon compounds are filled. With 2 the path of the synthetic high polymer is indicated, which led to rollers 3 is.

Die Temperatur der geschmolzenen Masse wird in den Grenzen zwischen 6o und g5° gehalten.The temperature of the molten mass is in the range between 6o and g5 ° held.

Bei 6o° sind die hochpolymerisierten synthetischen Paraffine in den Paraffinen mit niedrigem Molekulargewicht lösbar. Da die Geschwindigkeit des Films derart geregelt wird, daß der Film gerade anfängt, auf seiner Oberfläche in Lösung zu gehen, wenn er die geschmolzenen Paraffine durchläuft, so erhält man ein Band, das in seiner ganzen Dicke paraffinartig ist, ohne daß dazu die besonderen Eigenarten der beiden Sorten der verwendeten Kohlenwasserstoffverbindungen verändert werden. Auf diese Weise erhält man ein paraffinartiges Bekleidungsmittel, das sich auf alle Arten von Flächen bringen iäßt, und bei dem nicht zu befürchten ist, daß mit der Zeit seine Schutzeigenschaften durch physikalische Einwirkungen (Stöße, Wasseransaugung, Auflösung der Haftung) oder biologische Einwirkungen (Fäulnis), wie das bei den Trägern aus Cellulose zu befürchten ist, leiden. Beispiel der Herstellung einer paraffinastigen Komposition zum Schutze von Metallen gegen Koriosion Gemäß diesem Beispiele werden synthetische hohe Polymere in Körner- oder Pulverform verwendet. Bei höheren Temperaturen bis zu iio° wird das Gemisch aus synthetischen hohen Polymerisationsprodukten und paraffinartigen Kohlenwasserstoffverbindungen niederen Molekulargewichtes durch einfaches Rühren behandelt. Nötigenfalls setzt man Füllstoffe zu. Die so erhaltene Komposition kann alsdann zur Bildung einer paraffinartigen Bekleidung, wie vorher beschrieben, dienen oder als irgendein Hilfsmittel zum Übertragen auf irgendwelche zu schützende Flächen verwendet werden. Auf alle Fälle vermindert die Anwesenheit der synthetischen hohen Polymere merklich den nachteiligen Einfluß des Übertragungsmittels selbst dann, wenn dieses cellulosehaltiger Natur ist. Andererseits erzielt man eine merkliche Erhöhung des Tropfpunktes nach Ubbelohde.At 60 ° the highly polymerized synthetic paraffins are in the Low molecular weight paraffins soluble. As the speed of the film is regulated in such a way that the film just begins, on its surface going into solution as it passes through the molten paraffins is obtained a band that is paraffin-like in its entire thickness, without adding any special ones Changed the characteristics of the two types of hydrocarbon compounds used will. In this way a paraffin-like clothing material is obtained which can be brought to all kinds of surfaces, and there is no reason to fear that its protective properties over time due to physical impacts (impacts, Water suction, dissolution of adhesion) or biological effects (putrefaction), as is to be feared with cellulose carriers, suffer. Example of manufacture According to a paraffin-like composition to protect metals against corrosion These examples use synthetic high polymers in granular or powder form. At higher temperatures up to 100 °, the mixture of synthetic high polymerization products and low molecular weight paraffinic hydrocarbon compounds treated with simple stirring. If necessary, fillers are added. The thus obtained Composition can then lead to the formation of paraffin-like clothing, as before described, serve or as any means of transferring to any areas to be protected are used. In any case, the presence diminishes of synthetic high polymers markedly the adverse influence of the transfer agent even if this is cellulosic in nature. On the other hand, you get one noticeable increase in the dropping point after Ubbelohde.

Beispiel Eine Masse, die -aus ioo Gewichtsteilen Paraffinen und 75 Gewichtsteilen Füllstoffen (Silikaten) besteht, kann nur bei Temperaturen verwendet werden, die 45° nicht überschreiten (Tropfpunkt 54 bis 55°), während eine Masse, die aus ioo paraffinartigen Teilen und 75 Teilen Füllstoffen und 7 Teilen hochpolymerisierter synthetischer Paraffine besteht, unbedenklich eine Temperatur von 7o bis 75° (Tropfpunkt nach Ubbelohde: 84°) aushält.Example A mass composed of 100 parts by weight of paraffins and 75 Parts by weight of fillers (silicates) can only be used at high temperatures which do not exceed 45 ° (dropping point 54 to 55 °), while a mass, those of 100 paraffin-like parts and 75 parts of fillers and 7 parts of highly polymerized synthetic paraffins, a temperature of 70 to 75 ° (dropping point according to Ubbelohde: 84 °).

Auf dieses Beispiel soll die Erfindung nicht beschränkt bleiben.The invention is not intended to be restricted to this example.

Vergleich der Eigenschaften verschiedener paraffinartiger Bekleidungen A bedeutet eine paraffinartige Bekleidung auf einem Träger aus Cellulose, B eine paraffinartige (Paraffine mit niederem Molekulargewicht und hochpolymerisieite synthetische Paraffine) Bekleidung wie weiter oben beschrieben auf einem Träger aus Cellulose, C nur aus Paraffinen bestehende Bekleidung wie beschrieben. A B C Dielektrische Festigkeit ............ 2200 Volt q97aVolt iroooVolt dieselbe nach 8 Tagen in Wasser . . . . . . . . . . . . . . 800 Volt i 700 Volt i x ooo Volt Widerstandsfähigkeit in der Tiefe in Megohm/Cm2 ... 37000 18500 > 50000 dieselbe nach 8 Tagen in H20 . . . . . . . . . . . . . . . . . . . 3,7 8,5 > 50000 dieselbe nach 15 Tagen in H20 . . . . . . . . . . . . . . . . . . 0,85 519 > 50000 dieselbe nach 8 Tagen in H2 S 04 (5 °/o) . . . . . . . . . . . 17,8 5,1 3200 dieselbe nach 15 Tagen in H2 SO, (5 °/o) . . . . . . . . . . 0,4 0,95 450 dieselbe nach 8 Tagen in H2 S 04 (20 °/o) . . . . . . . . . . - - 16 88o dieselbe nach 15 Tagen in H2 S 04 (20 °/o) . . . . . . . . . - - 36 Zoo dieselbe nach 8 Tagen in N a O H (5 °/o) . . . . . . . . . . . o,6 43200 dieselbe nach 15 Tagen in Na OH (5 °/o) . . . . . . . . . . o,o18 o,6 > 50000 dieselbe nach 8 Tagen in Na O H (2o °/o) . . . . . . . . . . - - 6o7 dieselbe nach 15 Tagen in Na O H (2o °/o) . . . . . . . . . - - 4000 Widerstandsfähigkeit in der Fläche in Megohm/cm2.. 941 790 >i 000 000 dieselbe nach 8 Tagen in H20 . . . . . . . . . . . . . . . . . . . 2,9 3,5 >i 000 000 dieselbe nach 15 Tagen in H20 . . . . . . . . . . . . . . . . . . 2,6 12,5 >i 000 000 dieselbe nach 8 Tagen in H2 S 04 (5 °/o) . . . . . . . . . . . 0,36 0,72 >i 000 000 dieselbe nach 15 Tagen in H2 S04 (5 °/°) . . . . . . . . . . 0,17 o,63 >i 000 000 dieselbe nach 8 Tagen in H2 S 04 (20 °/o) . . . . . . . . . . - - > i 000 000 dieselbe nach 15 Tagen in H2 S 04 (20 °/o) . . . . . . . . . - - > i 000 000 dieselbe nach 8 Tagen in Na OH (5 °/o) . . . . . . . . . . . 0,2 1,3 >i 000 000 dieselbe nach 15 Tagen in Na OH (5 °/o) . . . . . . . . . . 0,13 2 >i aoo 000 dieselbe nach 8 Tagen in Na OH (2o °/o) . . . . . . . . . . - - >i 000 000 dieselbe nach 15 Tagen in Na O H (2o °/o) . . . . . . . . . - - > i 000 000 Comparison of the properties of different paraffin-like clothing A means a paraffin-like clothing on a cellulose carrier, B a paraffin-like (paraffins with low molecular weight and highly polymerized synthetic paraffins) clothing as described above on a cellulose carrier, C clothing consisting only of paraffins as described. ABC Dielectric strength ............ 2200 volts q97aVolt iroooVolt the same after 8 days in water. . . . . . . . . . . . . . 800 volts i 700 volts ix ooo volts Resistance in depth in Megohm / Cm2 ... 37000 18500 > 50000 same after 8 days in H20. . . . . . . . . . . . . . . . . . . 3.7 8.5> 50,000 same after 15 days in H20. . . . . . . . . . . . . . . . . . 0.85 519> 50,000 the same after 8 days in H2 S 04 (5%). . . . . . . . . . . 17.8 5.1 3200 the same after 15 days in H2 SO, (5%). . . . . . . . . . 0.4 0.95 450 the same after 8 days in H2 S 04 (20%). . . . . . . . . . - - 16 88o the same after 15 days in H2 S 04 (20%). . . . . . . . . - - 36 zoo the same after 8 days in N a OH (5%). . . . . . . . . . . o.6 43200 the same after 15 days in NaOH (5%). . . . . . . . . . o, o18 o, 6> 50000 the same after 8 days in NaOH (20%). . . . . . . . . . - - 6o7 the same after 15 days in NaOH (20%). . . . . . . . . - - 4000 Resistance in the area in megohms / cm2 .. 941 790 > i 000 000 same after 8 days in H20. . . . . . . . . . . . . . . . . . . 2.9 3.5> i 000 000 same after 15 days in H20. . . . . . . . . . . . . . . . . . 2.6 12.5> i 000 000 the same after 8 days in H2 S 04 (5%). . . . . . . . . . . 0.36 0.72 > i 000 000 the same after 15 days in H2 SO4 (5 ° / °). . . . . . . . . . 0.17 o. 63> i 000 000 the same after 8 days in H2 S 04 (20%). . . . . . . . . . - -> i 000 000 the same after 15 days in H2 S 04 (20%). . . . . . . . . - -> i 000 000 the same after 8 days in Na OH (5%). . . . . . . . . . . 0.2 1.3> i 000 000 the same after 15 days in NaOH (5%). . . . . . . . . . 0.13 2> i aoo 000 the same after 8 days in NaOH (20%). . . . . . . . . . - -> i 000 000 the same after 15 days in NaOH (20%). . . . . . . . . - -> i 000 000

Claims (7)

PATENTANSPRU CHE: i. Korrosionsschutz- und Abdichtungsmittel in Bandform als Außenschutz für metallische Oberflächen, von z. B unterirdisch zu verlegenden Rohrleitungen, Behältern, Kabeln od. dgl., gekennzeichnet durch einen als Träger dienenden Kern aus Polyäthylen oder ähnlichen hochpolymeren paraffinartigen Kohlenwasserstoffen und einen zweiseitigen Belag aus paraffinartigen Körpern niedrigen Molekulargewichtes. PATENT CLAIMS: i. Corrosion protection and sealing agent in tape form as external protection for metallic surfaces, e.g. B to be laid underground Pipelines, containers, cables or the like, characterized by a carrier Serving core made of polyethylene or similar high-polymer paraffin-like hydrocarbons and a two-sided covering of paraffin-like bodies of low molecular weight. 2. Überzugsmittel nach Anspruch i, dadurch gekennzeichnet, daß es außen beiderseitig aus Paraffinen und/oder Protoparaffinen, vorzugsweise mit Füllstoffen versetzten Kohlenwasserstoffverbindungen von mittlerem oder niedrigem Molekulargewicht besteht, während die synthetischen Kohlenwasserstoffverbindungen hohen Molekulargewichtes darin Träger bilden. 2. Coating agent according to claim i, characterized in that it is on the outside on both sides from paraffins and / or protoparaffins, preferably mixed with fillers Consists of hydrocarbon compounds of medium or low molecular weight, while the high molecular weight synthetic hydrocarbon compounds form carriers therein. 3. Überzugsmittel nach Anspruch i, dadurch gekennzeichnet, daß es aus einer Mischung von synthetischen hochpolymerisierten Paraffinen und Paraffinkohlenwasserstoffen von niedrigem Molekulargewicht besteht, die auf einen Träger oder irgendein Übertragungsmittel gebracht ist. q. 3. Coating agent according to claim i, characterized in that that it is made from a mixture of synthetic highly polymerized paraffins and paraffin hydrocarbons of low molecular weight, carried on a carrier or some transfer agent is brought. q. Überzugsmittel nach Anspruch i, dadurch gekennzeichnet, daß in ihm als hochpolymerisierte synthetische Paraffine solche mit einem Molekulargewicht zwischen 8ooo und -o ooo verwendet sind. Coating agent according to claim i, characterized in that in him as highly polymerized synthetic paraffins with a molecular weight between 8ooo and -o ooo are used. 5. Verfahren zur Erzeugung eines paraffinartigen Überzugsmittels in Bandform nach Anspruch i, dadurch gekennzeichnet, daß die paraffinartigen Kohlenwassezstoffverbindungen von geringem Molekulargewicht geschmolzen und in Behälter eingefüllt werden, durch welche die hochpolymerisierten synthetischen Paraffine, die zu Filmen geformt sind, hindurchlaufen. 5. Method of producing a paraffin-like Coating agent in tape form according to claim i, characterized in that the paraffin-like Low molecular weight hydrocarbon compounds melted and placed in containers are filled, through which the highly polymerized synthetic paraffins, which are shaped into films pass through. 6. Verfahren nach Anspruch 5, dadurch gekennzeichnet, daß die Transportgeschwindigkeit des Films so geregelt .ist, daß der Film gerade oberflächlich anfängt, in Lösung zu gehen, während er die geschmolzenen Paraffine durchläuft. 6. The method according to claim 5, characterized characterized in that the transport speed of the film is regulated so that the film just superficially begins to go into solution while it is melted Paraffins going through. 7. Verfahren nach Anspruch 5, dadurch gekennzeichnet, daß die Temperatur der geschmolzenen Masse innerhalb der Grenzen zwischen etwa 6o und g5° gehalten wird. B. Verfahren zur Erzeugung eines paraffinartigen, zum Schutze von Metallen gegen Korrosion geeigneten Überzugsmittels nach Anspruch i, dadurch gekennzeichnet, daß die synthetischen hohen Polymere in Körner- oder Pulverform verwendet werden und daß die Mischung dieser synthetischen hohen Polymere mit den paraffinartigen Kohlenwasserstoffverbindungen von, niederem Molekulargewicht bei Temperaturen über iio° durch einfaches Rühren vollzogen wird. Angezogene Druckschriften: USA.-Patentschrift Nr. 2 q.o6 03g; britische Patentschrift Nr. 567 oi2; Pabst, »Kunststofftaschenbuch«, B. Ausg. S. 232; »I. G. Kunststoffe, Taschenbuch für die verarbeitende Industrie«, igq,2, S. 57/58.7. The method according to claim 5, characterized in that the temperature of the molten mass within the limits between about 6o and g5 ° is held. B. Process for producing a paraffin-like, for protection of metals suitable against corrosion coating agent according to claim i, characterized characterized in that the synthetic high polymers are in granular or powder form be used and that the blend of these synthetic high polymers with the paraffin-like hydrocarbon compounds of low molecular weight Temperatures above iio ° is accomplished by simple stirring. Referred publications: U.S. Patent No. 2q.o6 03g; British Patent No. 567 oi2; Pabst, »plastic pocket book«, B. Ed. P. 232; »I. G. Kunststoffe, pocket book for the processing industry «, igq, 2, pp. 57/58.
DET4175A 1950-04-28 1951-04-21 Corrosion protection and sealing agent in tape form as external protection for metallic surfaces Expired DE922188C (en)