DE898313C - Process to increase the durability of converter floors in the wind freshening process

Info

Publication number: DE898313C
Application number: DEW7353A
Authority: DE
Inventors: Erwin Dr-Ing Eickworth
Original assignee: WESTFALENHUETTE AG
Current assignee: WESTFALENHUETTE AG
Priority date: 1951-12-05
Filing date: 1951-12-05
Publication date: 1953-11-30

Description

Verfahren zur Erhöhung der Haltbarkeit von Konverterböden beim Windfrischverfahren Die Erfindung betrifft ein Verfahren zur Erhöhung der Haltbarkeit der Konverterbödenbeim Windfrischverfahren, d. h. beim Bessemer- oder Thomasverfähren zur Stahlerzeugung.Process to increase the durability of converter floors in the wind freshening process The invention relates to a method for increasing the durability of the converter bottoms Wind freshening process, d. H. in the Bessemer or Thomas process for steel production.

Die Böden der z. B. beim Thomasverfahren verwendeten Konverter, in .denen eine Vielzahl von Blaslöchern angeordnet ist, bestehen aus gebrannten Teer-Dolomit-M@ischungen. Die Haltbarkeit solcher Konverberböden wird in hohem Maße dadurch beeinträchtigt, daß gebrannter Dolomit belcann.tlich sehr stark reaktionsfähig gegenüber dem im Blaswind enthaltenen Wasserdampf und Kohlensäure ist.The floors of the z. B. in the Thomas method converter used in .whose a large number of blowholes are arranged, consist of burnt tar-dolomite mixtures. The durability of such Converber floors is greatly impaired by that burnt dolomite can sometimes be very reactive to the im The wind contains water vapor and carbonic acid.

Die Reaktion zwischen: Wasserdampf bzw. Kohlensäure und dem gebrannten Dolomit führt daher zu einer Volumenvergrößerung des !Dolomits und als deren Folge zu Aufplatzungen im Gefüge, durch die Dampf und Kohlensäure weiter in den Körper des Bodens eindringen und damit zu einer verhältnismäßig schnellen Zerstörung desselben führen.The reaction between: water vapor or carbon dioxide and the burnt Dolomite therefore leads to an increase in volume of the dolomite and as a result to cracks in the structure, through which steam and carbonic acid continue into the body penetrate the soil and thus to a relatively quick destruction of the same to lead.

Es ist bereits vorgeschlagen worden, diese nachteiligen Einflüsse des im Blasmittel enthaltenen Wasserdampfes bzw. der Kohlensäure dadurch zu verringern oder zu vermeiden, daß ,die Blaslöcher durch eingesetzte Hülsen, beispielsweise aus Eisen, ausgefüttert werden. Hierbei ,aber ergibt sich wieder, abgesehen von. den hohen Kosten dieser Maßnahme, die Gefahr von Reaktionen zwischen dem Eisen der Düse und dem Sauerstoff des Blaswindes und damit der Bildung einer niedrig schmelzenden Verbindung zwischen dem entstehenden Eisenoxyd und dem Dolomit, die zu einem vorzeitigen Abschmelzen des Bodens führt. Die Verwendung von Düseneinsätzen -aus edlerem Metall verbietet sich in der Regel wegen der außerordentlichen, hierdurch eintretenden Verteuerung. Die gleichen Gründe stehen auch der Verwendung keramischer .Düseneinsätze entgegen. Gemäß ,der Erfindung wird die gleiche Aufgabe in wesentlich einfacherer und: billigerer Weise durch gelöst, daß die Innenflächen der Blaslöcher des bereits gebrannten. oder auch des roch ungebrannten Bodens des Konverters, mit einem in feiner Verteilung, vorzugsweise in flüssigem oder staubförmigem Zustand, aufgebrachten Überzug versehen werden, der wassendampf- und kohlensäureabweisende Eigenschaften besitzt.It has already been proposed to reduce or avoid these adverse effects of the water vapor or carbonic acid contained in the blowing agent in that the blow holes are lined with inserted sleeves, for example made of iron. Here, however, results again, apart from. the high costs of this measure, the risk of reactions between the iron in the nozzle and the oxygen in the wind and thus the formation of a low-melting compound between the iron oxide and the dolomite, which leads to premature melting of the soil. The use of nozzle inserts made of noble metal is generally prohibited because of the extraordinary increase in price that occurs as a result. The same reasons prevent the use of ceramic nozzle inserts. According to the invention, the same object is achieved in a much simpler and cheaper way by that the inner surfaces of the blow holes of the already fired. or the smell of the unburnt floor of the converter can be provided with a finely dispersed coating, preferably in a liquid or dusty state, which has water vapor and carbonic acid repellent properties.

Als Überzugsstoffe, die nach dem Brennen des Bodens .aufgebracht werden, sind z. B. Kunstharzlacke, Lacke .auf Teerölb,asis und Metallbronzen geeignet, soweit sie hinreichend widerstandsfähig gegen die auftretenden Temperaturen sind.As covering materials that are applied after the floor has burned, are z. B. synthetic resin lacquers, lacquers .auf tar oil, asis and metal bronzes suitable, as far as they are sufficiently resistant to the temperatures that occur.

Im Falle der Anwendung des Verfahrens auf noch nicht gebrannte Konverterböden werden geeignete, glasurbildende Stoffe an sich bekannter Zusammensetzung verwendet und beim Brand aufgeschmolzen. Das Auftragen der Stoffe kann. in beliebiger Weise, vorzugsweise mittels einer Spritzvorrichtung erfolgen.If the method is used on converter floors that have not yet been fired suitable, glaze-forming substances of known composition are used and melted in the fire. Applying the fabrics can. in any way, preferably take place by means of a spray device.

E's hat sich gezeigt, daß die Haltbarkeit von Konverterböden, deren Blaslöcher einen, Wasserdampf- und kohlensäureabweisenden Innenüberzug gemäß der Erfindung aufweisen, auf ein Vielfaches der bisher erreichten L°bensJauer gesteigert wird, wobei die durch -die Anwendung des neuen Verfahrens bedingten :Mehrkosten sich in sehr niedrigen Grenzen halten und -in keiner Weise mit denen vergleichbar sind, die durch die bekannte Ausfütterung der Blaslöcher bedingt sind.It has been shown that the durability of converter bases, their Blowholes have a water vapor and carbonic acid repellent inner coating according to FIG Invention have increased to a multiple of the L ° bensJauer achieved so far will, whereby the application of the new procedure-related: additional costs keep within very low limits and in no way comparable to those which are caused by the well-known lining of the blowholes.

Claims

PATENT CLAIMS: e.g. Process to increase the durability of converter floors in the wind freshening process by covering the inner surfaces of the blowholes against immediate ones Contact with the blowing agent, characterized in that the inner surfaces with a water vapor and carbonic acid repellent applied in a finely divided state Be provided with a coating. a. Procedure. according to claim i, characterized in that that a solidifying coating is applied in the liquid state. 3. Procedure according to claims i and z, characterized by the use of synthetic resin paints, Lacquers based on tar, oil, metal ground lacquers or metal bronzes as coating materials. .4. Method according to claims i to 3, characterized in that & ß .the applicator Covering materials are made after the converter base is fired. 5th embodiment of the method according to claims i to 3, characterized in that d @ aß before Burning the converter bottom through (the following fire in a glaze-like State substances to be transferred are applied to the inner surfaces of the blowholes.