Verwendung von Goldlegierungen für Potentiometer Zusatz zum Patent
,888 18'0 Im Patent 888 i8o ist die Verwendung von Legierungen der Zusammensetzung
i bis 12%, vorzugsweise q. bis 110%1 Nickel, o,2 bis io%, vorzugsweise i bis 5%
Mangan und Rest Gold für Potentiometer beschrieben. Außerdem ist dort auch bereits
erwähnt, daß durch einen Zusatz von Eisen in Mengen von o,i bis 2%,die Widerstandswerte
erhöht werden.Use of gold alloys for potentiometers. Patent addition
, 888 18'0 In the 888 18o patent is the use of alloys of the composition
i to 12%, preferably q. up to 110% 1 nickel, 0.2 to 10%, preferably 1 to 5%
Manganese and remainder gold for potentiometers described. Besides, there is already
mentions that by adding iron in amounts of 0.1 to 2%, the resistance values
increase.
Bei weiterer Untersuchung der manganhaltigen Goldlegierungen wurde
nunmehr .gefunden, daß dem Eisen in den manganhaltigen Golidlegierungen zur Anwendung
für Potentiometerteile eine besondere Bedeutung zukommt und der Ersatz des Nickels
durch Eisen in .den obenerwähnten Legierungen erhebliche Fortschritte bringt. Erfindungsgemäß
werden deshalb für Teile von Potentiometern Legierungen der Zusammensetzung o,i
bis 5'/0, vorzugsweise 2f bis 3"/o Eisen, o, i bis 514, vorzugsweise i bis 3 % Mangan
und Rest Gold benutzt. Vorteilhaft wird neben einem Eisengehalt von 2 bis 5"/0,
insbesondere 2 bis 3"/0" noch ein gewisser Nickelgehalt, und zwar in Grenzen von
etwa o, i bis 5010, vorzugsweise i bis 3%, beibehalten; die Summe der Unedelmetalle
Eisen, Mangan und Nickel soll hierbei io0/a nicht überschreiten.
Während
mit den Legierungen - .des -Patents 8888o nur spezifische Widerstände -bis zu etwa
o,5 Ohm - mm2/m erzielt werden können, ist es mit den eisenreicheren Legierungen
der eben genannten Zusammensetzung möglich, zu noch wesentlich höheren Wertendes
spezifischen Widerstandes zu gelangen, ohne daß die sonstigen guten Eigenschaften
verlorengehen. Dabei ist es für die Anwendung in Potentiometern, bei denen es@ auf
höchste Genauigkeit ankommt, von besonderer Bedeutung, daß sich die Gold-Eisen-Mangan-Legierungen
.durch gute Konstanz des Widerstandes auszeichnen; sie unterscheiden sich hierin
vorteilhaft von .den manganfreien Gold-Eisen_-Nickel-Legierungen.Upon further investigation the manganese-containing gold alloys was
now. found that iron is used in manganese-containing gold alloys
for potentiometer parts is of particular importance and the replacement of nickel
by iron in. the alloys mentioned above brings considerable progress. According to the invention
Therefore, alloys with the composition o, i are used for parts of potentiometers
to 5 '/ 0, preferably 2f to 3 "/ o iron, 0.1 to 514, preferably 1 to 3% manganese
and the rest of the gold used. In addition to an iron content of 2 to 5 "/ 0, it is advantageous
in particular 2 to 3 "/ 0" still have a certain nickel content, within limits of
about 0.1 to 5010, preferably i to 3% retained; the sum of the base metals
Iron, manganese and nickel should not exceed 10% per year.
While
with the alloys - .des -patents 8888o only specific resistances -up to about
0.5 ohms - mm2 / m can be achieved, it is with the iron-rich alloys
of the composition just mentioned possible, at an even higher end of value
resistivity to arrive without affecting the other good properties
get lost. It is for use in potentiometers with @ on
The highest level of accuracy matters, of particular importance, that the gold-iron-manganese alloys
. characterized by good constancy of resistance; they differ in this
advantageous from the manganese-free gold-iron-nickel alloys.
Wenn man auf die Zugfestigkeit besonderen Wert legt, gibt man den
Legierungen den erwähnten kleinen Nickelgehalt.If you attach particular importance to tensile strength, you give it
Alloys have the mentioned low nickel content.
Die Legierungen sind leicht verarbeitbar,_ so daß :auch die Herstellung
feinster Drähte keine Schwierigkeiten bereitet.The alloys are easy to process, so that: also the production
finest wires are no problem.
Im folgenden werden einige. Beispiele für die neuen Potentiometerlegierungen
gegeben: 1. 940/a Au, 2% Fe, 2 °/o Mn, 2.°/o Ni, 2. 95 % Au, 3 °/o Fe, 2 °/o Mn,
3. 93 °/o Au, 3 % Fe, 2 °/a Mn, 2 °/o Ni, 4. 92 °/o@ Au, 3 % Fe, 2 °/o Mn, 3 °/o@
Ni.. __ Der spezifische Widerstand beträgt-,bei dem Beispiel 2 o,69 und steigt bei
den Beispielen 3 und 4 sogär auf 0,71 Ohm - mm2/m. Die nickelhaltigen Legierungen
zeichnen- sich hierbei, wie gesagt, durch besonders hohe Zugfestigkeit aus; sie
beträgt im Beispiel 3 68,8 und im Beispiel 4 76,4 kg/mm2.The following are some. Examples of the new potentiometer alloys are given: 1. 940 / a Au, 2% Fe, 2% Mn, 2.% Ni, 2. 95% Au, 3% Fe, 2% Mn, 3 .93% Au, 3% Fe, 2% Mn, 2% Ni, 4. 92% Au, 3% Fe, 2% Mn, 3% Ni .. __ The specific resistance is - in Example 2 o.69 and in Examples 3 and 4 even increases to 0.71 Ohm - mm2 / m. The nickel-containing alloys are, as I said, distinguished by their particularly high tensile strength; in example 3 it is 68.8 and in example 4 76.4 kg / mm 2.