DE89179C - - Google Patents
Info
- Publication number
- DE89179C DE89179C DENDAT89179D DE89179DA DE89179C DE 89179 C DE89179 C DE 89179C DE NDAT89179 D DENDAT89179 D DE NDAT89179D DE 89179D A DE89179D A DE 89179DA DE 89179 C DE89179 C DE 89179C
- Authority
- DE
- Germany
- Prior art keywords
- iron
- carbon
- free carbon
- reduction
- hand
- Prior art date
- Legal status (The legal status is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the status listed.)
- Active
Description
KAISERLICHESIMPERIAL
PATENTAMT.PATENT OFFICE.
PATENTSCHRIFTPATENT LETTERING
KLASSE 18: Eisenerzeugung.CLASS 18: Ironmaking.
Fatentirt im Deutschen Reiche vom 25. Oktober 1895 ab.Fatentirt in the German Empire from October 25, 1895.
Während bei der Herstellung von metallischem Eisen aus den Eisenerzen bisher lediglich Reductionsmittel zur Verwendung kamen, welche freien, nicht gebundenen Kohlenstoff enthalten, ist es zur Herstellung von Eisen und Stahl aus den Eisenerzen in directer Erzeugung nothwendig, andere Reductionsmittel zu verwenden. Es hat sich dies namentlich deshalb als erforderlich erwiesen, weil die Reductionswirkung des freien, als Kohle und dergleichen benuzten Kohlenstoffes bei einer Temperatur erfolgt, bei welcher nicht nur die Eisenerze, sondern auch die denselben beigemischten Phosphate reducirt werden. Ein weiterer Grund, welcher bei der directen Erzeugung von Eisen und Stahl die Verwendung nicht freie Kohle enthaltender Reductionsmittel empfehlenswerth erscheinen lä'fst, besteht darin, dafs bei der Benutzung von Kohlenstoff in gebundener Form enthaltenden Mitteln ausschliefslich eine Reduction ohne gleichzeitige Kohlung erfolgt.While so far only reducing agents have been used in the production of metallic iron from iron ores which contain free, unbound carbon were used, it is used for the production of iron and steel from the iron ores in direct production it is necessary to use other reducing agents. This has been shown to be necessary because of the reducing effect of the free carbon used as coal and the like takes place at a temperature which not only reduces the iron ores, but also the phosphates admixed with them will. Another reason which, in the direct production of iron and steel, the The use of reducing agents that do not contain free carbon appear to be advisable lä'fst consists in the fact that when using carbon in bonded form, they contain Means exclusively a reduction without simultaneous carbonization.
Als vorteilhafte Reductionsmittel, welche keinen freien Kohlenstoff enthalten und trotzdem in ihrer Wirksamkeit nicht nur dem freien Kohlenstoff gleichwerthig, sondern sogar überlegen sind, haben sich organische Verbindungen, welche bei verhältnifsmäfsig niederer Temperatur ■—unterhalb 1 300—flüssig werden, erwiesen. Derartige Verbindungen, welche ihre Wirkung bei bedeutend niedrigerer Temperatur als der freie Kohlenstoff auszuüben vermögen, sind mineralische oder vegetabilische OeIe, Fette und Harze. Namentlich hat sich die Verwendung von Petroleum oder Petroleumrück-Die Menge, in welcherAs an advantageous reducing agent containing no free carbon, yet of equal value in their effectiveness not only the free carbon, but even superior, have organic compounds that are -liquid at proportionably low temperature ■ -unterhalb 1 30 0 proved. Such compounds, which are able to exert their effect at a significantly lower temperature than the free carbon, are mineral or vegetable oils, fats and resins. In particular, the use of kerosene or kerosene-The amount in which
ständen gut bewährt.stands well proven.
die Reductionsmittel zur Verwendung gelangen, ist von der Quantität des Eisens, welche man zu erzielen beabsichtigt, abhängig. Man benutzt 20 bis 25 pCt. von dem zu producirenden Eisen.the reducing agents used depends on the quantity of iron which is used intends to achieve dependent. 20 to 25 pCt are used. of what is to be produced Iron.
Das vorstehend geschilderte Reductionsverfahren unterscheidet sich von den bisherigen Verwendungsarten von Oelen, Fetten und Harzen dadurch, dafs die genannten Stoffe lediglich als Reductionsmittel, und zwar als einzig benutzte zur Verwendung gelangen. Eine Beimischung von "unschmelzbaren, freie Kohle, enthaltenden Reductionsmitteln. wie sie in der Patentschrift Nr. 81906 vorgeschlagen ist, findet nicht statt und würde dem durch das vorliegende Verfahren angestrebten Zweck geradezu entgegenwirken. Eine Folge davon, dafs die OeIe, Harze und Fette nur als Reductionsmittel , und zwar als einzig benutzte zur Verwendung gelangen, ist, dafs die genannten Körper erstens in bedeutend gröfserer Menge angewendet werden müssen, als dies bei dem früheren Verfahren der Fall ist, während gleichzeitig zweitens jede Substanz, welche eine oxydirende Wirkung auszuüben vermag, ausgeschlossen werden mufs. Infolge dessen müssen die OeIe für sich allein Verwendung finden und können besonders im Gegensatz zu den in den Patentschriften Nr. 57883 und Nr. 60078 beschriebenen Verfahren nicht durch Wasser ersetzt werden oder in Vermischung mit demselben Verwendung finden.The reduction process described above differs from the previous ones Types of use of oils, fats and resins by using the substances mentioned can only be used as a reducing agent, namely as the only one used. An admixture of "infusible, free coal, containing reducing agents. Like them proposed in patent specification No. 81906 does not take place and would do so the present proceedings virtually counteract the intended purpose. A consequence of this that oils, resins, and fats were used only as reducing agents, and indeed as the only ones are used is that the bodies mentioned are, first of all, considerably larger Amount must be applied while as is the case with the earlier method at the same time, secondly, every substance which is capable of exerting an oxidizing effect, must be excluded. As a result, the oils must be used for themselves find and can be found particularly in contrast to those in Patent Nos. 57883 and No. 60078 process described can not be replaced by water or mixed with the same use.
Die Form, in welcher das Erz mit dem Reductionsmittel verarbeitet wird, ist gleichgültig, so dafs das Erz nicht als Brei oder inThe form in which the ore is processed with the reducing agent is irrelevant, so that the ore is not as pulp or in
(2, Auflage, ausgegeben am IQ. Juni i8gj.)(2nd edition, issued on June 1st, 18th)
Form von Briquettes benutzt zu werden braucht. Im Gegensatz zu der Patentschrift Nr. 81906 findet nicht ein Schmelzen des Harzes und ein darauf folgendes Erkalten der Mischung statt, vielmehr findet die Verarbeitung des Erzes in continuirlicher Operation sofort nach der Vermengung mit dem Reductionsmittel statt. Weiter ist es zur Ausführung des vorliegenden Verfahrens nothwendig, dafs die bei der Reduction innegehaltene Temperatur niedrig ist, so dafs eine Reduction der Phosphate .und eine Abscheidung freien Kohlenstoffes nicht stattfindet. Im Gegensatz zu dem Verfahren des Patentes Nr. 57883 soll daher der Zweck des Verwendens von schmelzbaren Kohlenstoffverbindungen nicht in der Vermeidung einer Abkühlung des Erzes bestehen, vielmehr bezweckt die Benutzung der erwähnten Stoffe gerade die Vermeidung einer zu hohen Temperatur.Form of briquettes to be used. In contrast to patent specification No. 81906 there is no melting of the resin and a subsequent cooling of the mixture, on the contrary, the ore is processed in a continuous operation immediately after the mixing with the reducing agent instead. Next it is to carry out the present method it is necessary that the temperature maintained during the reduction be low, so that a reduction of the phosphates. and a deposition free carbon does not take place. In contrast to the method of the patent No. 57883 is therefore said to be the purpose of using fusible carbon compounds do not consist in avoiding a cooling of the ore, rather the use of the substances mentioned aims at precisely this Avoid too high a temperature.
Claims (1)