DE818408C - Process for the production of glass coverings - Google Patents

Process for the production of glass coverings

Info

Publication number
DE818408C
DE818408C DEP285A DEP0000285A DE818408C DE 818408 C DE818408 C DE 818408C DE P285 A DEP285 A DE P285A DE P0000285 A DEP0000285 A DE P0000285A DE 818408 C DE818408 C DE 818408C
Authority
DE
Germany
Prior art keywords
water glass
lime
layer
glass
application
Prior art date
Legal status (The legal status is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the status listed.)
Expired
Application number
DEP285A
Other languages
German (de)
Inventor
Joseph Ploerer
Current Assignee (The listed assignees may be inaccurate. Google has not performed a legal analysis and makes no representation or warranty as to the accuracy of the list.)
Individual
Original Assignee
Individual
Priority date (The priority date is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the date listed.)
Filing date
Publication date
Application filed by Individual filed Critical Individual
Priority to DEP285A priority Critical patent/DE818408C/en
Application granted granted Critical
Publication of DE818408C publication Critical patent/DE818408C/en
Expired legal-status Critical Current

Description

Verfahren zur Herstellung von Glasbelägen Vorliegende Erfindung sieht das Belegen mit Glas durch Verkieselung von Wasserglasgemischen vor.Process for making glass coverings The present invention provides covering with glass by silicification of water glass mixtures.

Um mit diesem in Wasser gelösten Gemenge auch eine Färbung des Glases auf seiner Rückseite auszubauen, wurde erkannt und durch Versuche bestätigt, daß auf kleinen, mosaikgroßen Glasoberflächen bei Verwendung des in der Silicatfarbentechnik üblichen Wasserglases, jedoch mit größerer Kalkpulverbeimischung, die auch pigmentiert sein kann, die gut deckende, breiige Mischung durch die Verkieselung so schrumpft, daß durch ein zusätzliches Auftragen von Wasserglas allein die Farbschicht feuchtigkeitsdicht wird.To color the glass with this mixture dissolved in water to expand on its rear side, it was recognized and confirmed by tests that on small, mosaic-sized glass surfaces when using the silicate color technique usual water glass, but with a larger amount of lime powder, which is also pigmented can be, the well-covering, pulpy mixture shrinks as a result of the silicification, that by an additional application of water glass alone the paint layer is moisture-proof will.

Um bei größeren Glasoberflächen die zweckgebundene Schließung der wasseransaugenden Poren zu erreichen, wird zweckmäßig Natronwasserglas, mit möglichst wenig Wasser, grobkörnigem Kalkpulver und Pigment verwendet. Der so erhaltene Brei gewährleistet insbesondere bei Beimischung von Emulsionen, Dispersionen nach Erwärmung eine porendichte Verkieselung und eine außerordent liehe Haftfestigkeit bzw. Verkieselung mit dem Glase.In order to allow the dedicated closure of the To achieve water-sucking pores, soda waterglass is expedient, with if possible little water, coarse-grain lime powder and pigment are used. The porridge thus obtained guaranteed especially when adding emulsions or dispersions after heating a pore-dense silicification and an extraordinary liehe adhesive strength or silicification with the glass.

Da Aluminiumpulver_porenschlieBendwirkt, kann bei einer weiteren Schicht von Natronwasserglas und Aluminiumpulver die Emulsion durch Aluminiumpulver ersetzt werden.Since aluminum powder has a pore-closing effect, it can be used for a further layer of soda waterglass and aluminum powder replaced the emulsion with aluminum powder will.

Um bei Verwendung von Natronwasserglas eine Entmischung der Farbpigmente vom Kalk zu verhindern, sieht die Erfindung vor, daß auf das Glas eine dünne Schicht von Wasserglas allein, angerührt mit Farbpigmenten und einer Emulsion, Dispersion, angebracht wird. Die Dispersion kann auch durch das Aufbringen der Natronwasserglas-Aluminiumpulver-Schicht ersetzt werden. Gegebenenfalls kann auch etwas Kalk zugegeben werden. Diese Schicht wird vorteilhaft erwärmt.In order to separate the color pigments when using soda waterglass To prevent limescale, the invention provides that a thin layer on the glass of water glass alone, mixed with color pigments and an emulsion, dispersion, is attached. The dispersion can also be achieved by applying a layer of soda waterglass and aluminum powder be replaced. If necessary, can some lime can also be added. This layer is advantageously heated.

Die Erfindung sieht als zweckmäßig das weitere Anbringen einer dicken Kalk-Wasserglas-Schicht vor, die unter anderem die Aufgabe hat, die I_ruckfeckeit des Glases wesentlich zu erhöhen.The invention sees the further attachment of a thick one as expedient Lime-water glass layer in front, which has the task, among other things, of the I_ruckfeckeit of the glass to increase significantly.

Das Kalk-Wäsgefgläs-Gemisch kann bei Druck, der vorteilhaft gleichzeitig mit der Erwärmung erfolgt, zu einer homogenen Masse von großer Bruchfestigkeit gepreßt werden, wobei auch Spannungsschrumpfungen begegnet wird.The lime-Wäsgefgläs mixture can be used at the same time at pressure, which is advantageous takes place with the heating, pressed into a homogeneous mass of great breaking strength stress shrinkage is also countered.

Adhäsionsvermindernden Schrumpfungsspannungen kann auch durch Auftragen von zwei oder mehreren Schichten, die vorteilhaft auch verschiedener Mischungszusammensetzung sein können; begegnet werden..Adhesion-reducing shrinkage stresses can also be achieved by applying of two or more layers, which advantageously also have different mixture compositions could be; to be met ..

Es wurde weiter erkannt, daß die Beimischung von Quarzsand in dem Kalk-Wasserglas-Gemisch außer der Förderung der Verkieselung den Vorteil hat, daß sich der Sand mit dem Verlegungsmörtel gut verzahnt bzw. sich die plastischen Schichten, wie Bitumen, gut einlagern können, so daß auch durchgefärbtes Glas zweckmäßig mit dieser Schicht versehen wird.It was further recognized that the admixture of quartz sand in the Lime-water glass mixture besides promoting silicification has the advantage that the sand interlocks well with the laying mortar or the plastic layers, like bitumen, can be stored well, so that through-colored glass can also be used appropriately this layer is provided.

Um diese Verbindung mit der anlagernden Schicht zu erhöhen und gleichzeitig einen Ausgleich zwischen den verschiedenen Ausdehnungen zu schaffen, können auch Sand, Split oder andere zweckdienliche Stoffe in die nasse Schicht eingestreut werden.To increase this connection with the accumulating layer and at the same time to create a balance between the different expansions, too Sand, grit or other suitable material can be sprinkled into the wet layer.

Der gemäß der Erfindung verwendete Kalk-Wasserglas-Brei kann auch als Verlegungsmasse zum Ersatz des Zementmörtels, Bitumens usw. dienen und gleichzeit_ig-das_Glas a.der Rücksei e ff ä@ `-Außer zur Überbrückung der verschiedenartigen Dehnungen von Glas und der zu belegenden Oberfläche sieht die Erfindung zur weiteren Isolierung das Anbringen von plastischen Schichten entweder auf das Glas allein oder zum Teil auf die zu belegende Oberfläche vor.The lime-water glass slurry used according to the invention can also serve as laying compound to replace cement mortar, bitumen, etc. and at the same time_ig-das_glass the back side ff ä @ `` -Except for bridging the various types of stretching of glass and the surface to be covered, the invention provides for further insulation the application of plastic layers either on the glass alone or in part on the surface to be covered.

Es ist unter anderem Bitumen, das emulgiert, heißflüssig oder gelöst, vorteilhaft mit Füllstoffen, wie Asbestmehl, Kokereischlacke, Traß usw., versetzt wird, vorgesehen. Diese Schicht kann zweckmäßig mit Sand, Split oder ähnlichen Stoffen, die vorteilhaft mit Bitumenlöser angefeuchtet sind, bestreut werden.Among other things, it is bitumen that emulsifies, hot liquid or dissolved, advantageously mixed with fillers such as asbestos flour, coke oven slag, trass, etc. is provided. This layer can expediently with sand, grit or similar substances, which are advantageously moistened with bitumen remover, are sprinkled.

Weiter sieht die Erfindung die Verwendung von anderen, und zwar in Öl und Benzin nicht löslichen plastischen Massen, insbesondere Latex, dort vor, wo Bitumenlöser vorkommen, z. B. bei Öl- und Benzintankanlagen.The invention also envisions the use of others, namely in Oil and gasoline insoluble plastic masses, especially latex, there before, where bitumen removers occur, e.g. B. in oil and petrol tank systems.

Die Erfindung sieht endlich auch vor, daß das Material der Verlegungsmasse auf das nach den verschiedenen vorgeschilderten Arten vorbereitete Glas aufgebracht wird; hierbei ist insbesondere das Aufgießen des zu Porenbeton zu verarbeitenden Zementgemisches vorgesehen. Ausführungsbeispiel Eine Fensterglasscheibe wird mit einem mit Natronwasserglas angefeuchteten Lappen auf der Rückseite gereinigt. Dann wird auf diese eine dünne Schicht, die z. B. aus Natronwasserglas, Pigmenten und Kreide besteht, mit einer Spritzpistole aufgebracht.The invention finally also provides that the material of the laying compound applied to the glass prepared according to the various types described above will; in particular, the pouring of the aerated concrete to be processed is important here Cement mix provided. Embodiment A window pane is with cleaned with a cloth moistened with soda water glass on the back. then is on this a thin layer, which z. B. from soda water glass, pigments and Chalk is made, applied with a spray gun.

Nach dem Antrocknen wird die Schicht ansteigend erwärmt.After drying, the layer is heated upwards.

Claims (7)

PATENTANSPRÜCHE: i. Verfahren zur Herstellung von Glasbelägen, gekennzeichnet durch die Verwendung von Kalkwasserglas zwischen Glas und der zu belegenden Oberfläche oder der Verlegungsmasse, in der Art, daß das bei der Silicatfarbentechnik übliche dünnflüssige Wasserglas verwendet wird, jedoch mit einer größeren Menge von Kalkpulver, und daß nach Trocknung dieses Breies Wasserglas allein aufgebracht wird. PATENT CLAIMS: i. Process for the production of glass coverings, characterized by using lime water glass between the glass and the surface to be covered or the laying compound, in the manner that is common with the silicate paint technique thin water glass is used, but with a larger amount of lime powder, and that after this paste has dried, water glass alone is applied. 2. Verfahren nach Anspruch i, gekennzeichnet durch die Beimischung von Farbpigmenten. 2. Procedure according to claim i, characterized by the addition of color pigments. 3. Verfahren nach Anspruch i und 2, gekennzeichnet durch die Verwendung von konzentriertem Wasserglas und stärkerer Korngröße des Kalkpulvers und der Pigmente oder des Kalkpulvers allein. 3. Procedure according to claims 1 and 2, characterized by the use of concentrated water glass and larger grain size of the lime powder and the pigments or the lime powder alone. 4. Verfahren nach Anspruch i bis 3, gekennzeichnet durch die Verkieselung durch Wärme. 4. The method according to claim i to 3, characterized by the silicification by Warmth. 5. Verfahren nach Anspruch i bis 4, gekennzeichnet durch die Verwendung von Natron wasserglas. 5. The method according to claim i to 4, characterized by the use of Soda water glass. 6. Verfahren nach Anspruch i bis 5, gekennzeichnet durch die Beimischung von Emulsionen, Dispersionen. 6. The method according to claim i to 5, characterized by the Adding emulsions, dispersions. 7. Verfahren nach Anspruch i bis 6, gekennzeichnet durch das Auftragen einer dünnen Schicht aus Wasserglas, Pigmenten und Dispersionen. B. Verfahren nach Anspruch i bis 7, gekennzeichnet durch das Anbringen einer dünnen Schicht von Wasserglas, Pigmenten und Emulsionen, Dispersionen mit kleinem Kalkanteil. g. Verfahren nach Anspruch i bis 8, gekennzeichnet durch das Anbringen einer Schicht aus Wasserglas und Aluminiumpulver als Isolierschicht oder Farbschicht. io. Verfahren nach Anspruch i bis 9, gekennzeichnet durch Beimischung von Quarzsand. i i. Verfahren nach Anspruch i bis io, gekennzeichnet durch Auftragen von zwei oder mehreren Schichten des Kalk-Wasserglas-Gemisches, auch verschiedener Zusammensetzung. 12. Verfahren nach Anspruch i bis i i, gekennzeichnet durch Einstreuen von Sand; Split oder anderen zweckdienlichen Mitteln auf die noch nasse Kalk-Wasserglas-Rückschicht. 13. Verfahren nach Anspruch i bis 12, gekennzeichnet durch Anbringen einer dicken Schicht des vorgesehenen Kalk-Wasserglas-Gemisches. 14. Verfahren nach Anspruch i bis 13, gekennzeichnet durch das Aufbringen der Schicht unter Verwendung von Druck. 15. Verfahren nach Anspruch i bis 14, gekennzeichnet durch Verwendung von Druck bei gleichzeitiger Erwärmung. 16. Verfahren nach Anspruch i bis 15, gekennzeichnet durch die Verwendung von Kalk-Wasserglas-Gemisch als Verlegungskitt. 17. Verfahren nach Anspruch i bis 16, gekennzeichnet durch das Aufbringen von heißflüssigem, gelöstem oder emulgiertem Bitumen, das zweckmäßig mit Füllstoffen, wie Traß, Asbest, Kokereischlacke, versetzt ist und mit Sand, Split und ähnlichen Stoffen, die auch mit Bitumenlöser angefeuchtet sein können, abgestreut wird. i8. Verfahren nach Anspruch i bis 17, gekennzeichnet durch .das Aufbringen der plastischen Masse zum Teil an die zu verkleidende Oberfläche. i9. Verfahren nach Anspruch i bis 18, gekennzeichnet durch die Verwendung ariderer plastischer Massen anstatt des Bitumens, z. B. Latex. 2o. Verfahren nach Anspruch i bis i9, gekennzeichnet durch Aufschütten porenbildenden Zementbreies auf die mit Kalk-Wasserglas-Gemenge versehenen Glasplatten..7. The method according to claim i to 6, characterized by the application of a thin layer of water glass, pigments and dispersions. B. The method according to claim i to 7, characterized by the application of a thin layer of water glass, pigments and emulsions, dispersions with a small proportion of lime. G. Method according to Claims 1 to 8, characterized by the application of a layer of water glass and aluminum powder as an insulating layer or a layer of paint. ok Method according to Claims 1 to 9, characterized by adding quartz sand. i i. Method according to claims i to io, characterized by applying two or more layers of the lime-waterglass mixture, also of different compositions. 12. The method according to claim i to ii, characterized by sprinkling sand; Split or other appropriate means on the still wet lime-water glass backing layer. 13. The method according to claim i to 12, characterized by applying a thick layer of the intended lime-water glass mixture. 14. The method according to claim i to 13, characterized by applying the layer using pressure. 1 5. The method according to claim i to 14, characterized by the use of pressure with simultaneous heating. 16. The method according to claim i to 15, characterized by the use of lime-water glass mixture as laying putty. 17. The method according to claim i to 16, characterized by the application of hot liquid, dissolved or emulsified bitumen, which is expediently mixed with fillers such as trass, asbestos, coke oven slag and with sand, grit and similar substances that are also moistened with bitumen remover can, is scattered. i8. Method according to Claims 1 to 17, characterized by the application of the plastic compound in part to the surface to be clad. i9. Method according to claim i to 18, characterized by the use of other plastic masses instead of bitumen, e.g. B. latex. 2o. Method according to claims i to i9, characterized by pouring pore-forming cement paste onto the glass plates provided with the lime-water glass mixture.
DEP285A 1949-11-16 1949-11-16 Process for the production of glass coverings Expired DE818408C (en)