DE747417C - Manufacture of chromium oxide green - Google Patents
Manufacture of chromium oxide greenInfo
- Publication number
- DE747417C DE747417C DES147064D DES0147064D DE747417C DE 747417 C DE747417 C DE 747417C DE S147064 D DES147064 D DE S147064D DE S0147064 D DES0147064 D DE S0147064D DE 747417 C DE747417 C DE 747417C
- Authority
- DE
- Germany
- Prior art keywords
- chromium
- manufacture
- chromium oxide
- oxide green
- chromium sulfate
- Prior art date
- Legal status (The legal status is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the status listed.)
- Expired
Description
Herstellung von Chromoxydgrün Chromoxyde für Farbkörper werden bekanntlich meist durch Reduktion -von C'hromaten oder durch Fällung dreiivertiger Chromsalze mit alkalischen Stoffen hergestellt. Ferner ist es auch bekannt, Chromoxydbrün ,durch thermische Zersetzung von Chrominitrat oder Chromisulfat oder von basischen ChromIisalzen mit oder ohne Zusatz von alkalischen Stoffen zu erzeugen. Chrominitrat ist jedoch ein nur schwierig und unter erheblichen 'Kosten herstellbarer Ausgangsstoff. Bel der thermischen Zersetzung von Chromisulfat aber erhält man Glühprodukte, die sich bekanntlich nicht-als Farbpigmente eignen.Production of chromium oxide green Chromium oxides for color bodies are known mostly by reducing chromates or by precipitating tri-finished chromium salts made with alkaline substances. It is also known to use Chromoxydbrün thermal decomposition of chromium nitrate or chromium sulfate or of basic chromium salts with or without the addition of alkaline substances. Chromium nitrate is however a starting material that can only be produced with difficulty and at considerable cost. Bel the thermal decomposition of chromium sulfate, however, one obtains glow products that are as is known, not suitable as color pigments.
Es wurde nun befunden; daß man zu Chromoxyden, die sich hervorragend für Pigmentzwecke eignen, in einfacher Weise dadurch gelangen kann, daß man die thermische Zersetzung des Chromisulfats. in Anwesenheit von Alkalisalzen starleer Mineralsäuren vornimmt oder von Doppelsalzen des Chromisulfats mit solchen Alkal.isalzen ausgeht. Als Alkalisalze starker Säuren kommen beispielsweise :die Chloride, Sulfate oder Nitrate in Betracht. Das Verfahren ist sowohl .mit geringen als auch mit großen Zusätzen von solchen Alkalisalzen zum Chromisulfat durchführbar. Als geeignetes Doppelsalz des Chromisulfats kann z. B. Chromalaun genommen werden. Die thermische Zersetzung wird zweckmäßig :bei ` Temperaturen von etwa 65obis iooo° vorgenommen.It has now been found; that you get to chromium oxides, which are excellent suitable for pigment purposes, can be achieved in a simple manner by the fact that thermal decomposition of chromium sulfate. more rigid in the presence of alkali salts Mineral acids or double salts of chromium sulfate with such Alkal.isalzen goes out. The alkali salts of strong acids are, for example: the chlorides, sulfates or nitrates. The process is both minor and major Additions of such alkali salts to the chromium sulfate can be carried out. As a suitable The double salt of chromium sulfate can, for. B. Chrome alum can be taken. The thermal Decomposition is expedient: carried out at temperatures of about 65 to 100 °.
Das Glühgut, das in besonders weicher Form anfällt, wird in üblicher Weise mit Wasser ausgewaschen und getrocknet. Es bildet einen Farbkörper, der sich durch besondere Feinheit des Kornes und durch sehr hohe Mischkraft auszeichnet.The annealing material, which is obtained in a particularly soft form, is more common Way washed out with water and dried. It forms a body of color, which characterized by the particular fineness of the grain and very high mixing power.
Dieses Ergebnis ist im Hinblick auf die bekannte Ungeei.gnetheit des Chromisulfats zur Herstellung von Farbpigrnenten völlig überraschend und bedeutet einen wesentlichen Fortschritt, insbesondere auch weil die Herstellung des Farbkärpers unter einfachen Arbeitsbedingungen und mit Hilfe leicht beschaffbarer Ausgangsstoffe erfolgt.This result is in view of the well-known inappropriateness of the Chromium sulfate for the production of color pigments completely surprising and means a significant advance, especially because of the production of Farbkärpers under simple working conditions and with the help of easily obtainable Starting materials takes place.
Beispiel i io kg Chromisulfat «-erden unter Zusatz von 5 kg Iialiumchlorid eine Stunde bei 750' gegliiht. Nach Auswaschen und Trocknen erhält man ein grünes Pigment hoher Mischkraft mit ausgezeichneten Echtheitseigenschaften.EXAMPLE 10 kg of chromium sulphate earths with the addition of 5 kg of iialium chloride, heated at 750 ° for one hour. After washing out and drying, a green pigment of high mixing power with excellent fastness properties is obtained.
Beispiel io kg Chromalaun werden in einem Tiegel eine Stunde bei 8oo@ geglüht. -Nach Auswaschen und Trocknen erhält man ein reines Chrornoxcdgrün von ausgezeichneter Mischkraft.Example 10 kg of chrome alum are placed in a crucible for one hour at 8oo @ annealed. -After washing and drying, a pure chromium oxide green of excellent mixing power.
Claims (1)