DE7007347U - LIGHTWEIGHT PANEL WITH LAYERS. - Google Patents

LIGHTWEIGHT PANEL WITH LAYERS.

Info

Publication number
DE7007347U
DE7007347U DE7007347U DE7007347U DE7007347U DE 7007347 U DE7007347 U DE 7007347U DE 7007347 U DE7007347 U DE 7007347U DE 7007347 U DE7007347 U DE 7007347U DE 7007347 U DE7007347 U DE 7007347U
Authority
DE
Germany
Prior art keywords
layer
binder
glass fiber
board
lightweight
Prior art date
Legal status (The legal status is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the status listed.)
Expired
Application number
DE7007347U
Other languages
German (de)
Current Assignee (The listed assignees may be inaccurate. Google has not performed a legal analysis and makes no representation or warranty as to the accuracy of the list.)
Osterreichisch Amerikanische Magnesit AG
Original Assignee
Osterreichisch Amerikanische Magnesit AG
Priority date (The priority date is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the date listed.)
Filing date
Publication date
Application filed by Osterreichisch Amerikanische Magnesit AG filed Critical Osterreichisch Amerikanische Magnesit AG
Publication of DE7007347U publication Critical patent/DE7007347U/en
Expired legal-status Critical Current

Description

3885238852

österreichisch Amerikanische Magnesit Aktiengesellschaft in Radenthein (Kärnten, Österreich)Austrian American Magnesit Aktiengesellschaft in Radenthein (Carinthia, Austria)

Leichtbauplatte mit AuflageschichtenLightweight panel with support layers

In der österreichischen Patentschrift 220.533 ist ein Verfahren zur kontinuierlichen Herstellung von Holzwolle-Leichtbauplatten mit Auflageschichten auf mindestens einer Plattenseite beschrieben, welches im wesentlichen darin besteht, daß das die Auflageschicht bildende, insbesondere faserige und mörtelartige Material in losem Zustand gemeinsam mit einer losen Schicht des plattenbildenden Materials der Formmaschine zugeführt wird und in dieser zu einer unmittelbar gebrauchsfertigen Schichtplatte verformt wird. Als A iflagematerial sind gemäß der genannten Patentschrift mörtelartige Massen u.a. aus anorganischen und/ oder organischen Pasern und einem Bindemittel, wie Kalk, Portlandzement , Magnesiazement, Gips, Kunstharzbindern oder bituminösen Bindern, vorgesehen.The Austrian patent specification 220.533 describes a process for the continuous production of wood wool lightweight panels with overlay layers described on at least one side of the plate, which essentially consists in the fact that the Support layer forming, in particular fibrous and mortar-like Material in the loose state is fed to the molding machine together with a loose layer of the plate-forming material and is deformed in this to a ready-to-use layer plate. As a flagematerial are according to the mentioned Patent specification of mortar-like masses made from inorganic and / or organic pastes and a binding agent such as lime, Portland cement , Magnesia cement, plaster of paris, synthetic resin binders or bituminous Binders, provided.

700734?700734?

Es wurde nun gefunden, daß im Falle einer ^anz besonderen Auswahl des Materials für die Auflageschicht beschichtete Bauplatten von einer bisher nicht erreichbaren Sonderquälität erhalten werden können. Die vorliegende Neuerung betrifft daher eine weitere Ausgestaltung der nach der österreichischen Patentschrift 220-533 erhältlichen Leichtbauplatte, die eine Holzwolleplatte, insbesondere mit Magnesiazementbindung, und wenigstens eine, anorganische Fasern und ein Bindemittel enthaltende Auflageschicht aufweist. Gemäß der Neuerung ist eine solche Leichtbauplatte dadurch gekennzeichnet, daß die mit der Holzwolleplatte zu einer unmittelbar gebrauchsfertigen Schichtplatte vereinigte Auflageschicht aus einem feinen Glasfasermaterial, insbesondere Vlies oder Gewebe, als Einbettungsmaterial und einem erhärteten Bindemittel aus einem Magnesiazement-Kunstharz-Gemisch besteht.It has now been found that in the case of a ^ Selection of the material for the support layer coated building boards obtained from a previously unattainable special quality can be. The present innovation therefore relates to a further embodiment according to the Austrian patent specification 220-533 available lightweight board, which is a wood wool board, in particular with a magnesia cement bond, and at least has an overlay layer containing inorganic fibers and a binder. According to the innovation is such a lightweight panel characterized in that it was combined with the wood wool board to form an immediately ready-to-use layer board Support layer made of a fine glass fiber material, in particular Fleece or fabric, as an embedding material and a hardened binder made of a magnesia cement-synthetic resin mixture.

Die Herstellung einer solchen Platte kann wieder auf kontinuierlichem Wege, zweckmäßig in der Weise erfolgen, daß als Material für die Auflageschicht ein Glasfaservlies od^r eine Glasfaserbahn eingesetzt wird, welches Fasermaterial mit dem härtbaren Bindemittel, bestehend aus einer Suspension von kaustischem Magnesit in Magnesiumsalζlauge und einem mit der MagnesitsuspeE-sion verträglichen, elektrolytbeständigen Kunstharzbinder, insbesondere auf Polyvinylacetatbasis bzw. vom Phenolharztypus, in Form einer wässerigen Mischung getränkt bzw. imprägniert wird, worauf das so vorbehandelte Glasfaservlies zugleich mit dem Strang des plattenbildenden Materials der Formgebung in der Formmaschine zugeführt wird.The production of such a plate can be continued on a continuous basis Ways, expediently take place in such a way that a glass fiber fleece or a glass fiber web as the material for the support layer is used, which fiber material with the curable binder, consisting of a suspension of caustic Magnesite in magnesium saline and one with the magnesite suspension Compatible, electrolyte-resistant synthetic resin binders, in particular based on polyvinyl acetate or of the phenolic resin type, in Is soaked or impregnated in the form of an aqueous mixture, whereupon the thus pretreated glass fiber fleece at the same time with the Strand of the plate forming material of the molding in the molding machine is fed.

Durch die neuerungsgemäße Auswahl eines Glasfaservlieses b^w. -gewebes von geringer Dicke, das mit einer Kombination von zwei Bindemitteln, nämlich Magnesiazement und einer damit verträglichen Kunstharzdispersion, vorbehandelt wurde, wird es nun ermöglicht, eine Leichtbauplatte zu schaffen, die sich durch eine sehr dünne und dadurch sehr leichte Porenverschlußschicht auszeichnet. Die Beimischung eines mit der Magnesiumsalzlauge verträglichen Kunstharzbinders macht es möglich, daß trotz der dünnen Ausführung der Beschichtung die Bindung innerhalb derDue to the selection of a glass fiber fleece b ^ w according to the innovation. -woven fabric of thin thickness, made with a combination of two binders, namely magnesia cement and a compatible synthetic resin dispersion, has been pretreated, it is now makes it possible to create a lightweight board that is characterized by a very thin and therefore very light pore closure layer excels. The admixture of a synthetic resin binder compatible with the magnesium salt liquor makes it possible that in spite of the thin execution of the coating the bond within the

Porenverschlußmasse und zum Plattengrund verstärkt wird und der Porenverschlußbelag witterungsjtempfindlicher wird. Dadurch wird auch der Zusatz des Funstharzbinders wirtschaftlich vertretbar.Pore sealing compound and to the plate base is reinforced and the The pore closure layer is more sensitive to weathering. This will the addition of the synthetic resin binder is also economically justifiable.

Die gemäß der Neuerung ausgebildete Schichtplatte "besitzt ein sehr niederes Flächengewicht der Beschichtung, das im allgemeinen, bezogen auf den trockenen Zustand, unter 2 kg/m liegt. Es wurde festgestellt, daß die neuerungsgemäß mit dem vorbehandelten Glasfaservlies beschichteten Leichtbauplatten für alle Plattenstärken mit einer gleichbleibenden Beschichtung von etwa 1,3 kg/m bei etwa 0,75 mm Schichtdicke versehen werden können, ohne daß dies einen Nachteil für die Qualität der Erzeugnisse zur Folge hätte. Bei den gemäß der eingangs genannten österreichischen Patentschrift erzeugten Schichtplatten schwankt dagegen die Schichtdicke des aus einem Holzstoffmörtel bestehenden Auflagematerials je nach Plattenstärke und liegt bei der 2,5 cm Platte bei etwa 6,5 mm und bei der 7»5 cm bzw. 10,0 cm Platte bei etwa 9 bis 10 mm. Dementsprechend liegt das Flächengewicht der Porenverschlußschicht bei der 2,5 cm Porenverschlußplatte bei etwa 5»5 kg/m und das der 7i5 cm Porenverschlußschicht bei 8 bis 9 kg/m2.The layered board formed according to the innovation "has a very low surface weight of the coating, which is generally, based on the dry state, below 2 kg / m constant coating of about 1.3 kg / m 2 with a layer thickness of about 0.75 mm without this resulting in a disadvantage for the quality of the products of a wood pulp mortar depending on the panel thickness and is around 6.5 mm for the 2.5 cm panel and around 9 to 10 mm for the 7 »5 cm or 10.0 cm panel in the case of the 2.5 cm pore closure plate at about 5 »5 kg / m and that of the 7.5 cm pore closure layer at 8 up to 9 kg / m 2 .

Infolge der dünnen und leichten Ausbildung der neuerungsgemäß beschichteten Platte (Schichtdicke im allgemeinen zwischen 0,5 und 1,2 mm) ist ein Verziehen bzw. Verwerfen weitestgehend ausgeschaltet und die Wärmeisolierung gegenüber der herkömmlichen Porenverschlußplatte besser. Die Porenverschlußschicht neigt auch nicht zu Rissebildungen. Die beträchtliche Leichtigkeit der neuen Schichtplatte gegenüber den bisher bekannten Porenverschlußplatten ist für die praktische Anwendung "besonders günstig, wodurch sich Einsparungen bei der Fracht and Vorteile durch geringere Belastungen von Tragkonstruktionen ergeben,As a result of the thin and light training according to the innovation coated plate (layer thickness generally between 0.5 and 1.2 mm) is warping or warping to the greatest possible extent turned off and the thermal insulation compared to the conventional pore closure plate better. The pore closure layer Nor does it tend to crack. The considerable lightness the new layer plate compared to the previously known pore closure plates is "special for practical use inexpensive, which results in savings in freight and benefits from lower loads on supporting structures,

Als mit der Magnesitsuspsenion verträgliche Kunstharzbinder eignen sich vor allem solche vom "Mowilith"-Typus, d.s. Polymerisate und Copolymerisate auf Basis von Vinylacetat, insbesondere in Dispersionsform, doch kommen auch unter den herrschenden Bedingungen beständige Phenolharztypen sowie ge^ibenenfalls Polyesterharze in Betracht. ^Λ Λ um Cl ft Suitable synthetic resin binders compatible with the magnesite psyche are above all those of the "Mowilith" type, i.e. polymers and copolymers based on vinyl acetate, especially in dispersion form, but phenolic resin types that are stable under the prevailing conditions and possibly polyester resins are also suitable. ^ Λ Λ around Cl ft

7007370073

Als Ausführungsbeispiel wird nachfolgend die Herstellung und der Aufbau einer gemäß der Neuerung ausgebildeten Leichtbauplatte mit einseitig aufgebrachter Beschichtung näher beschrieben. Dabei dient als Bindemittel eine Suspension von folgender Zusammensetzung:As an exemplary embodiment, the production and construction of a lightweight construction panel designed according to the innovation is described below described in more detail with a coating applied to one side. A suspension of the following composition:

12 Gew.-Teile kaustischer Magnesit 10,5 Gew.-Teile Magnesiumsulfatlösung, 17° Be 9 Gew.-Teile Wasser12 parts by weight of caustic magnesite, 10.5 parts by weight of magnesium sulfate solution, 17 ° Be 9 parts by weight of water

1,5 Gew.-Teile elektrolytbeständiger Kunstharzbinder auf Polyvinylacetatbasis, z.B. das unter der Bezeichnung Mowilith DMC 2 erhältliche Mischpolymerisat (Vinylacetat mit polymerisierbarer Komponente, gemischtdispers mit einem wasserlöslichen Zellulosederivat als Schutzkolloid).1.5 parts by weight of electrolyte-resistant synthetic resin binder based on polyvinyl acetate, e.g. the copolymer available under the name Mowilith DMC 2 (Vinyl acetate with a polymerizable component, mixed disperse with a water-soluble one Cellulose derivative as protective colloid).

Dieser Ansatz wird mittels einer Mischturbine in einem Gefäß angerührt und nach erfolgter gründlicher Durchmischung in ein Tauchgefäß abgelassen. In diesem wird eine von einer Solle abgezogene Glasfaserbahn mit dem in der vorstehend beschriebenen Weise hergestellten Bindemittel getränkt.This batch is mixed in a vessel by means of a mixing turbine and after thorough mixing has taken place drained into a dip vessel. In this, a fiberglass web peeled off from a target is combined with that described above Way-made binder soaked.

Der BeschichtungsVorgang selbst wird im Prinzip in der in der österreichischen Patentschrift 220-533 beschriebenen Weise in einer Bandformmaschine durchgeführt. Die mit dem Bindemittel getränkte Glasfaserbahn gelangt dabei auf das rücklaufende Trum des oberen Stahlbandes dei Bandfonnmaschine und w_. d nach. Umlenkung dieses Bandes in die Maschinenlaufrichtung mit dem auf dem unteren Stahlband der Bandformmaschine vorgeordneten Strang von mit Magnesiazement bemörtelten Holzwollefäden zusammengeführt, wonach im Formkanal der Bandformmaschine der Strang aus plattenbildendem Material mit der Auflageschicht aus Glasfaservlies mit kombiniertem Magnesia- und Kunstharzbinder zum fertigen Schichtkörper geformt und gepreßt wird. The coating process itself is in principle in the Austrian patent specification 220-533 described in carried out on a tape forming machine. The one soaked with the binder The fiberglass web arrives at the returning strand of the upper steel belt of the belt forming machine and w_. d after. Redirection this tape in the machine direction with the on the lower steel belt of the belt forming machine is brought together by a strand of wood wool threads grouted with magnesia cement, after which in the molding channel of the belt molding machine, the strand of plate-forming material with the overlay made of glass fiber fleece is shaped and pressed with a combined magnesia and synthetic resin binder to form the finished laminate.

Das Glasfaservlies wird bei der Erzeugung von 50 cm breiten Platten zweckmäßig in 55 cm breiten Bahnen verwendet, damit vor dem Aufbringen auftretende kleine Verschiebungen des VliesesThe fiberglass fleece becomes 50 cm wide when it is produced Panels are expediently used in 55 cm wide strips so that there are small shifts in the fleece before application

gegenüber dem Holzwollestrang das Grundmaterial an den Bändern nicht sichtbar werden lassen . Als Glasfaservlies wird beispielsweise ein solches mit einer liiere von 0,35 inm verwendet.do not let the base material become visible on the ribbons compared to the wood wool strand. As a glass fiber fleece, for example one with a length of 0.35 inm is used.

Gemäß der Neuerung bietet sich *.±e Möglichkeit, doppelseitig beschichtete Platten nicht mehr auf beiden Seiten mit dem bisher üblichen, verhältnismäßig schweren Belag erzeugen zu müssen. So brauchen beispielsweise die Holzwolle-Leichtbauplatten nur auf der einen Seite mit der Auflageschicht aus getränktem Glasfaservlies versehen zu sein, wogegen auf der anderen Plattenseite in bekannter Weise eine stärkere bzw. schwerere Porenverschlußschicht, insbesondere auf Grundlage von Sägespänen , kaustischem Magnesit und Mangesiumsalzlauge, aufgebracht sein kann.According to the innovation, there is *. ± e possibility to no longer have to produce double-sided coated panels on both sides with the previously usual, relatively heavy covering. For example, the wood wool lightweight panels only need to be provided with the layer of impregnated glass fiber fleece on one side, while a thicker or heavier pore closure layer, in particular based on sawdust, caustic magnesite and magnesium brine, is applied to the other side of the panel in a known manner can.

Eine weitere vorteilhafte Ausführungsform der Neuerung besteht darin, das in der Magnesiasuspension samt Kunstharzbinder getränkte Glasfaservlies als Armierung in eine stärkere bzw. schwerere PorenverscMuiischicht aus dem bekannten Holzstoffmörtel einzubetten. Dadurch tritt eine erhöhte Oberflächenarmierung der Porenverschlußschicht, eine erhöhte Zug- und Eindruckfestigkeit und eine bessere Witterungsbeständigkeit ein.Another advantageous embodiment of the innovation exists in it, the one in the magnesia suspension including synthetic resin binder Impregnated glass fiber fleece as reinforcement in a thicker or heavier layer of pores made from the well-known wood pulp mortar to embed. This results in increased surface reinforcement of the pore closure layer, increased tensile and indentation strength and a better weather resistance.

Der Gegenstand der Neuerung ist in den Fig. 1-4- der angeschlossenen Zeichnung anhand mehrerer Ausführungsbeispiele schematisch dargestellt.The subject of the innovation is in Figs. 1-4 - the attached Drawing shown schematically on the basis of several exemplary embodiments.

Pig. 1 zeigt die Leichtbauplatte 1 mit einseitig aufgebrachter Auflageschicht 2 aus Glasfasermaterial und erhärtetem Bindemittel aus Magnesiazement-Kunstharz-Gemisch, im Schaubild.Pig. 1 shows the lightweight construction panel 1 with a Support layer 2 made of fiberglass material and hardened binder made of magnesia cement-synthetic resin mixture, im Graph.

Fig. 2 zeigt die Leichtbauplatte 1 mit zweiseitig aufgebrachter Auflageschicht 2, 3 aus Glasfasermaterial und erhärtetem Bindemittel aus Magnesiazement-Kunstharz-Gemisch, im Schaubild.Fig. 2 shows the lightweight panel 1 with two-sided applied Support layer 2, 3 made of fiberglass material and hardened Binder made from a mixture of magnesia cement and synthetic resin, in the diagram.

Fig. 3 ist ein Querschnitt durch eine Leichtbauplatte 1 mit einseitig aufgebrachter Auflageschicht 2 gemäß der Neuerung und einer auf der zweiten Seite aufgebrachtenFig. 3 is a cross section through a lightweight panel 1 with overlay layer 2 applied on one side according to FIG Innovation and one applied to the second page

70078477007847

stärkeren Porenverschlußsciiicht 4·, die aus Sägespänen, kaustischem Magnesit und Magnesiumsalzlauge hergestellt ist.stronger pore-closing layer 4, which is made of sawdust, caustic magnesite and magnesium brine.

Fig. 4 ist ein Querschnitt durch eine Leichtbauplatte 1 mit einer einseitig aufgebrachten stärkeren Porenverschiußschicht 4- wie in Fig. 3» in welche aber eine gemäß der Neuerung ausgebildete, als Armierung wirkende Schicht eingebettet ist.Fig. 4 is a cross section through a lightweight panel 1 with a stronger pore closure layer 4 applied on one side as in FIG Innovation trained, acting as a reinforcement layer is embedded.

CO 0734CO 0734

Claims (2)

Schutzansprüche :Protection claims: 1. Leichtbauplatte, die eine Holzwolleplatte, insbesondere mit Magnesia*ementbindung, und wenigstens eine, anorganische Fasern und ein Bindemittel enthaltende Auflageschicht aufweist, dadurch gekennzeichnet , daß die mit der Holzwolleplatte zu einer unmittelbar gebrauchsfertigen Schichtplatte vereinigte Auflageschicht aus einem feinen Glasfasermaterial, insbesondere Vlies oder Gewebe, als Einbettungsmaterial und einem erhärteten Bindemittel aus einen Magnesiaaement-Kunstharz-Gemisch besteht.1. Lightweight construction board, which is a wood wool board, in particular with magnesia * ementbinding, and at least one, inorganic Has an overlay layer containing fibers and a binding agent, characterized in that the one with the wood wool board to a ready-to-use layer plate unified support layer made of a fine glass fiber material, in particular fleece or fabric, as an embedding material and a hardened binder made of a magnesia cement-synthetic resin mixture consists. 2. Leichtbauplatte nach Anspruch 1, dadurch gekennzeichnet , daß die Auflageschicht ein durch Erhärten eines Gemisches von kaustischem Magnesit^ Magnesiumsulfat und Eunstharzbinder auf Polyvinylacetatbasis bzw. Phenolharztypus erhaltenes Bindemittel aufweist.2. Lightweight panel according to claim 1, characterized in that the supporting layer is a hardening a mixture of caustic magnesite ^ magnesium sulfate and synthetic resin binder based on polyvinyl acetate or phenolic resin type Has obtained binder. 3· Leichtbauplatte nach Anspruch 1 oder 2, dadurch gekennzeichnet , daß die erhärtete Auflageschicht, bestehend aus dem mit dem Bindemittel behandelten Glasfaservlies, in einer solchen Menge bzw. Stärke vorliegt, daß die3 · Lightweight building board according to claim 1 or 2, characterized in that the hardened support layer, consisting of the glass fiber fleece treated with the binder, is present in such an amount or strength that the Beschichtung ein Flächengewicht von nicht mehr als etwa 2 kg/m t Coating has a weight per unit area of no more than about 2 kg / m t vorzugsweise von etwa 1,3 kg/m bzw. eine Schichtdicke von 0,5 bis 1,2 mm, vorzugsweise etwa 0,75 nim, aufweist.preferably of about 1.3 kg / m or a layer thickness of 0.5 to 1.2 mm, preferably about 0.75 nm. 4-. Leichtbauplatte nach einem der Ansprüche 1 bis 3* dadurch gekennze ichnet , daß die Holzwolleplatte nur auf der einen Seite mit der erhärteten Auflageschicht aus dem mit dem Bindemittel behandelten Glasfaservlies versehen ist, wogegen auf der anderen Plattenseite eine stärkere bzw. schwerere Porenverschlußschicht, insbesondere auf Grundlage von Lägespänen, kaustischem Magnesit und Magnesiumsalzlauge, aufgebracht ist.4-. Lightweight construction panel according to one of Claims 1 to 3 * gekennze ichnet that the wood wool board with the hardened support layer from the with only on one side the binder-treated glass fiber fleece is provided, whereas on the other side of the board a stronger or heavier pore-sealing layer, in particular on the basis of wood chips, caustic magnesite and magnesium brine. 5· Leichtbauplatte nach Anspruch 1 oder 2, dadurch gekennzeichnet , daß das mit dem Bindemittel behandelte Glasfaservlies als Armierung in eine stärkere bzw. schwerere PorenTarschlußschicht, insbesondere auf der Grundlage von Sägespänen, kaustischem Magnesit und Magnesiumsalzlauge, eingebettet I ist. 5 · Lightweight construction panel according to claim 1 or 2, characterized in that the glass fiber fleece treated with the binder is embedded as reinforcement in a thicker or heavier pore closure layer, in particular based on sawdust, caustic magnesite and magnesium salt lye . Dr.Pf/Bb 18.2.1970Dr.Pf/Bb February 18, 1970
DE7007347U 1969-03-05 1970-02-27 LIGHTWEIGHT PANEL WITH LAYERS. Expired DE7007347U (en)