Description

Elastischer Kaltkitt Die Erfindung betrifft die Verwendung einer aus geschmolzenen bituminösen Kittbindemitteln und aus in Wasser begrenzt quellbaren Emulgatoren, wie Ton oder Huininsubstanzen, hergestellten Mischung, die eine geringe, mit dem gequollenen Emulgator eingebrachte Menge Wasser und gegebenenfalls Füllstoffe, wie Asbestpulver, Kreide oder Kieselgur., enthält, als elastischer Kaltkitt.Elastic cold cement The invention relates to the use of a molten bituminous cement binders and from limited swellable in water Emulsifiers, such as clay or Huinin substances, produced mixture that have a low, the amount of water and fillers added with the swollen emulsifier, such as asbestos powder, chalk or kieselguhr., contains, as elastic cold cement.

Es ist der Technik bekannt, Kittbindemittel unter Wasserzusatz mit Emulgatoren zu behandeln und in wasserlösliche Emulsionen oder Pasten überzuführen. Diese können dann unter Verwendung von Wasser als Dispersionsmittel und mit Zuschlagstoffen weiterverarbeitet werden.It is known in the art to use putty binders with the addition of water To treat emulsifiers and to convert them into water-soluble emulsions or pastes. These can then be made using water as a dispersant and with aggregates are further processed.

Im Gegensatz dazu weisen die erfindungsgemäß als elastischer Kaltkitt zu verwendenden Mischungen eine äußerst geringe Menge an Wasser auf; solche Kitte sind dadurch glatt verstreichbar, genügend weich, temperatur- und wetterbeständig. Sie laufen, auf Flächen aufgestrichen, nicht ab und sind viele Monate hindurch verwendungsbereit. Diese Vorteile werden dadurch erreicht, daß der Kitt eine Art Gerüstsubstanz enthält, wodurch die Spanne Erstarrungspunkt-Erweichungspunkt ganz wesentlich erweitert ist. Hierdurch wird ermöglicht, daß der Bindemittelgehalt stark erhöht werden kann und neben einer ausgezeichneten Wetterbeständigkeit auch die erforderlichen mechanischen Eigenschaften, wie leichte Verarbeitbarkeit, gute Weichheit, Klebkraft und Schmiegsamkeit sowie ganz glatter Abstrich beim Ziehen mit dem Kittmesser, erzielt werden.In contrast to this, according to the invention, have as elastic cold cement mixtures to be used contain an extremely small amount of water; such putties are therefore smoothly spreadable, sufficiently soft, temperature and weather resistant. When painted on surfaces, they do not run off and are ready for use for many months. These advantages are achieved by the fact that the putty contains a kind of structural substance, whereby the range of the solidification point-softening point is expanded considerably. This enables the binder content to be increased significantly and in addition to excellent weather resistance, also the necessary mechanical Properties such as easy processability, good softness, adhesive strength and pliability as well as a very smooth smear when pulling with the putty knife.

Die Herstellung der erfindungsgemäß als elastischer Kaltkitt verwendeten Mischung aus bitumenhaltigen Kittbindemitteln mit den Emulgatoren sowie einem geringen Wassergehalt und gegebenenfalls einem Gehalt an Füllstoffen kann derart erfolgen, daß man das Bindemittel mit Emulgatoren unter Zugabe von geringen Mengen von Wasser bei höherer Temperatur vorbehandelt. Es ergibt sich, daß man auf diese Weise niedrigschmelzende, hochelastische Bindemittel mit Füllstoffen zu Kitten verarbeiten kann, die bei gewöhnlicher Temperatur gut verarbeitbar sind und nach ihrem Einbringen auch bei Temperaturen bis zu 10o° keinerlei Fließerscheinungen zeigen, die aber ebensowenig bei starker Kälteeinwirkung ihre Elastizität und Klebkraft verlieren. Auffallend ist dabei auch, daß die Klebwirkung der Kitte durch die Behandlung erhöht wird, was auf eine geringe Emulgierung des Bindemittels und einen erhöhten kolloidalen Zustand hinweist.The production of those used according to the invention as elastic cold cement Mixture of bituminous cement binders with emulsifiers and a small one The water content and optionally a content of fillers can be made in such a way that that the binder with emulsifiers with the addition of small amounts of water pretreated at a higher temperature. It turns out that in this way low-melting, Highly elastic binders with fillers can process into putty that with ordinary Temperature are easily processable and after their introduction also at temperatures up to 10o ° show no flow phenomena, but neither do they show at strong Exposure to cold will lose their elasticity and adhesive strength. It is also noticeable that that the adhesive effect of the putty is increased by the treatment, which is low Indicates emulsification of the binder and an increased colloidal state.

Als Emulgatoren haben sich gut bewährt jene, die, wieTon, Huminsubstanzen, begrenzt in Wasser quellbare Extrakte von Humuskohle, Braunkohle oder Torf, ferner Methylcellulose und ähnliche Kolloide, die in Wasser nicht unbegrenzt quellbar sind und die offenbar für das weiche, elastische Bindemittel eine Art Gerüstsubstanz bilden.As emulsifiers, those that, like clay, humic substances, Extracts of humus coal, lignite or peat that are limited in water swell, also Methyl cellulose and similar colloids, which are not indefinitely swellable in water and that apparently for the soft, elastic binding agent a kind Form structural substance.

Man kann z. B. den erfindungsgemäß verwendeten Kaltkitt wie folgt herstellen: d.o Teile eines Bitumens vom Erweichungspunkt von z5° (Krämer-Sarnow) oder ein entsprechendes Gemisch von Bitumen mit Mineralölen werden bei 6o° mit einer Aufquellung von 1,5 Teilen Ton mit a,5 Teilen Wasser gemischt und mit einer Mischung von 56 Teilen von Füllstoffen, wie Kieselgür, Talkum, Asbest, Mineralmehl usw., homogenisiert. Dieser Kitt, der große Elastizität und Klebkraft besitzt, ist bis zu Temperaturen von 8o° konsistent und zeigt keinerlei Fließerscheinungen von schrägen Flächen, außerdem ist die Kältebeständigkeit sehr gut. Der Kitt zeigt eine beachtenswerte Klebkraft und die Fähigkeit, sich beträchtlichen Deformationsänderungen der Kittstellen anzupassen, ohne seine Schutzwirkung zu verlieren.You can z. B. the cold cement used according to the invention as follows manufacture: d.o parts of a bitumen with a softening point of z5 ° (Krämer-Sarnow) or a corresponding mixture of bitumen with mineral oils are at 60 ° with a Swelling of 1.5 parts of clay mixed with a, 5 parts of water and mixed with a mixture of 56 parts of fillers, such as kieselguhr, talc, asbestos, mineral powder, etc., homogenized. This putty, which has great elasticity and adhesive strength, is up to consistent to temperatures of 80 ° and shows no flow phenomena from inclines Surfaces, and the resistance to cold is very good. The putty shows a remarkable Adhesive strength and the ability to undergo considerable deformation changes in the putty adapt without losing its protective effect.

Die neuen Kaltkitte finden hauptsächlich Verwendung für Verglasungen (Dachkitte), für Schwindrisse und Ausfugungen von Mauerwerk.The new cold putties are mainly used for glazing (Roof putty), for shrinkage cracks and grouting in masonry.

Claims

PATENT CLAIM: The use of a mixture produced from molten bituminous cement binders and from emulsifiers which have limited swelling in water, such as clay or humic substances; the small amount of water and optionally fillers such as asbestos powder, chalk or diatomaceous earth brought in with the swollen emulsifier; contains, as an elastic cold putty.