DE616858C - - Google Patents
Info
- Publication number
- DE616858C DE616858C DENDAT616858D DE616858DA DE616858C DE 616858 C DE616858 C DE 616858C DE NDAT616858 D DENDAT616858 D DE NDAT616858D DE 616858D A DE616858D A DE 616858DA DE 616858 C DE616858 C DE 616858C
- Authority
- DE
- Germany
- Prior art keywords
- nickel
- alloys
- tantalum
- chromium
- carbon
- Prior art date
- Legal status (The legal status is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the status listed.)
- Active
Description
DEUTSCHES REICHGERMAN EMPIRE
AUSGEGEBEN AM 6. AUGUST 1935ISSUED AUGUST 6, 1935
REiCHSPATENTAMTREICH PATENT OFFICE
PATENTSCHRIFTPATENT LETTERING
JVl 616858
KLASSE 40 b GRUPPE 14JVl 616858
CLASS 40 b GROUP 14
St 48494 VIJ40 b Tag der Bekanntmachung über die Erteilung des Patents: τι. Juli 1935St 48494 VIJ40 b Date of publication of the patent grant: τι. July 1935
Stahlwerke Röchling-Buderus A.-G. und Alfred Kropf in WetzlarSteelworks Röchling-Buderus A.-G. and Alfred Kropf in Wetzlar
Verformbare, vergütbare MetallegierungDeformable, heat treatable metal alloy
Patentiert im Deutschen Reiche vom 4. November 1931 abPatented in the German Empire on November 4, 1931
Für chirurgische Instrumente sind eine größere Reihe von binären, ternären und komplexen Metallegierungen in Verwendung, die rostsicher, sterilisierbar, warmbeständig und vor allem hart und schneidend sein sollen. Um diese Eigenschaften zu erreichen, ist vorgeschlagen worden, der bekannten korrosionsbeständigen Metallgruppe Nickel-Chrom Zusätze von Eisen, Mangan, Kupfer, Aluminium, Silicium u. a. zu machen. Zur Steigerung der Härte schlug man vor, Wolfram, Molybdän und neuerlich auch Beryllium zuzusetzen. For surgical instruments there are a wider range of binary, ternary, and complex metal alloys in use that are rustproof, sterilizable and heat-resistant and above all should be hard and cutting. To achieve these properties is has been proposed, the well-known corrosion-resistant metal group nickel-chromium Additions of iron, manganese, copper, aluminum, silicon and others. close. To increase In view of the hardness, it was suggested that tungsten, molybdenum and, more recently, also beryllium be added.
Dabei sollte der Kohlenstoffgehalt mögliehst vermieden oder doch so niedrig wie möglich gehalten werden.The carbon content should be avoided as much as possible or as low as possible be kept possible.
Reine Nickel-Tantal-Legierungen und deren Eigenschaften sind auch bekannt, wie Säurebeständigkeit, Festigkeit, Verformbarkeit, Elastizität und eine für die Herstellung medizinischer Instrumente und Schreibfedern noch hinlängliche Härte. Doch ist diese in erster Linie nur durch einen Kaltreckprozeß zu erreichen und läßt nach einiger Zeit erheblich nach. Mit Rücksicht auf die angegebenen Eigenschaften von Nickel-Chrom-Legierungen war 'daher zu erwarten, daß auch Nickei-Chrom-Tantal-Legierungen solche Eigenschaften besitzen würden. Ebenso ist bekannt, daß man ohne wesentliche Änderung der Eigenschaften bei Nickel-Chrom-Legierungen einen Teil des Nickels durch Eisen ersetzen kann und so Ersparnisse in der Herstellung erzielt.Pure nickel-tantalum alloys and their properties are also known, such as acid resistance, Strength, ductility, elasticity and one for making medical Instruments and nibs still hard enough. However, this can primarily only be achieved through a cold stretching process and decreases considerably after a while. With regard to the specified properties of nickel-chromium alloys it was therefore to be expected that nickel-chromium-tantalum alloys would also have such properties would own. It is also known that there is no significant change in the properties of nickel-chromium alloys can replace some of the nickel with iron, thus saving production achieved.
Die Erfindung besteht nun im wesentlichen darin, daß der Legierung Kohlenstoff in Mengen von 0,1 bis i,o°/0 zugesetzt wird, und daß dieser sich mit einem TeM des Tantals zu Tantalkarbid verbindet. Dadurch werden die genannten technischen Eigenschaften, im besonderen die Schneidhärte, noch verbessert, was sich damit erklärt, daß das Tantalkarbid sich aus der Lösung der übrigen Bestandteile bei geeigneter Wärmebehandlung ausscheidet.The invention now consists essentially in the fact that the alloy carbon in amounts of 0.1 to i, o 0 ° is added /, and in that this is combined with a TEM of the tantalum to tantalum. As a result, the technical properties mentioned, in particular the cutting hardness, are further improved, which is explained by the fact that the tantalum carbide separates out of the solution of the other constituents with suitable heat treatment.
Die bekannten Legierungen aus Nickel-Chrom-Eisen und Molybdän oder Wolfram enthalten sehr wenig (0,02 °/0) oder gar keinen Kohlenstoff, um einen schädlichen Einfluß auf die Säurebeständigkeit und um die Abschei dung des Kohlenstoffs durch das Nickel in Form von Graphit zu vermeiden. Nach der vorliegenden Erfindung sind einmal erheblich höhere Kohlenstoffmengen vorhanden, wobei diese mit dem Tantal zusammen eine größere Schneidhärte verursachen und das Tantal dabei die schädliche Wirkung des Nickels auf die Ausscheidung des Kohlenstoffes als Graphit verhindert.The known alloys of nickel-chromium-iron and molybdenum or tungsten contain very little (0.02 ° / 0 ) or no carbon at all, to have a detrimental effect on the acid resistance and to the separation of carbon by the nickel in the form of graphite to avoid. According to the present invention, considerably higher amounts of carbon are present, which together with the tantalum cause a greater cutting hardness and the tantalum prevents the harmful effect of nickel on the precipitation of carbon as graphite.
Dadurch ist solchen Legierungen auch eine besonders günstige Warm- und Kaltverformbarkeit gegeben. Was aber besonders ausschlaggebend ist, ist die Eigenschaft derAs a result, such alloys are also particularly suitable for hot and cold deformability given. But what is particularly crucial is the property of the
Hartibarkeit, wodurch diese Legierungen harte, insbesondere schneidende Eigenschaften erhalten, die den Nickel-Chrom-Legierungen mit Eisen, Wolfram, Molybdän nicht in diesem Maße zukommen, ganz abgesehen davon, daß diesen genannten Legierungen die thermische Eigenschaft der Härtbarkeit fehlt.Hardability, which makes these alloys hard, especially cutting properties are given to those of the nickel-chromium alloys with iron, tungsten, molybdenum do not come to this extent, quite apart from that, that these alloys mentioned lack the thermal property of hardenability.
Eine besonders gut geeignete Legierung besteht aus 0,50/0 Kohlenstoff, 10,00/0 Tantal, 30,0°/0 Chrom, Rest Nickel. Die Legierung besitzt im geglühten Zustand eine Festigkeit von etwa 75 kg, die durch geeignete Wärmebehandlung noch erhöht wird.A particularly suitable alloy is composed of 0.50 / 0 carbon, 10.00 / 0 tantalum, 30.0 ° / 0 chromium, balance nickel. In the annealed state, the alloy has a strength of around 75 kg, which is further increased by suitable heat treatment.
Sie kann im offenen Ofen ohne Anwendung von Vakuum oder in indifferenter Gasatmosphäre erschmolzen werden. Ein> Teil des in der Schmelze vorhandenen Tantalkarbids kann schon eine besondere desoxydierende Wirkung ausüben, welche schädliche Bestandteile zum größten Teil in Gasform entweichei läßt und einen schädlichen Einfluß des Luftsauerstoffes verhindert.It can be carried out in an open furnace without the use of a vacuum or in an inert gas atmosphere be melted. A> part of the tantalum carbide present in the melt can be a special deoxidizing Have an effect which harmful components escape for the most part in gaseous form and prevents the harmful influence of atmospheric oxygen.
Zur Erleichterung des metallurgischen Schmelzprozesses setzt man dieser Legierung uähi-end des SchmclFpro/esses noch Silicium, Vanadin oder auch Zirkon in Mengen bis zuThis alloy is used to facilitate the metallurgical melting process uähi-end of the SchmclFpro / esses still silicon, Vanadium or zircon in amounts up to
zu.to.
Ein Teil des Nickels kann, wie bei vielen bekannten Legierungen, durch Kobalt ersetzt werden.As with many known alloys, some of the nickel can be replaced by cobalt will.
Völlig unterschiedlich und physikalisch anders geartet sind die legierungen der Erfindung von den bekannten korrosionsbeständigen Chrom-Nickel-Stahllegierungen mit größeren Eisengehalten, die weit weniger korrosionsbeständig sind und ebenfalls in höherem Maße den Mangel der geringen Hartibarkeit und Schneidhaltigkeit besitzen.The alloys of the invention are completely different and physically different from the well-known corrosion-resistant chrome-nickel steel alloys with larger iron contents, which are far less corrosion-resistant and also in to a greater extent have the lack of low hardness and edge retention.
Claims (2)