DE575257C - Gold alloy - Google Patents

Gold alloy

Info

Publication number
DE575257C
DE575257C DE1930575257D DE575257DD DE575257C DE 575257 C DE575257 C DE 575257C DE 1930575257 D DE1930575257 D DE 1930575257D DE 575257D D DE575257D D DE 575257DD DE 575257 C DE575257 C DE 575257C
Authority
DE
Germany
Prior art keywords
nickel
gold
gold alloy
copper
less
Prior art date
Legal status (The legal status is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the status listed.)
Expired
Application number
DE1930575257D
Other languages
German (de)
Current Assignee (The listed assignees may be inaccurate. Google has not performed a legal analysis and makes no representation or warranty as to the accuracy of the list.)
RAU FA G
Original Assignee
RAU FA G
Priority date (The priority date is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the date listed.)
Filing date
Publication date
Application filed by RAU FA G filed Critical RAU FA G
Application granted granted Critical
Publication of DE575257C publication Critical patent/DE575257C/en
Expired legal-status Critical Current

Description

Die bisher zur Herstellung von Gebrauchsund Schmuckgegenständen, verwendeten Goldlegierungen haben eine solche Farbe, daß sie von derjenigen der Haut in hohem Maße ab-S stechen. Dies gilt in ungefähr gleicher Weise von allen bisher bekannten Rot-, Gelb- und Weißgoldlegierungen.The gold alloys previously used for the production of everyday objects and jewelry are of such a color as to be highly distinctive from that of the skin. This is roughly the same of all previously known red, yellow and white gold alloys.

Man hat zwar versucht, durch Färben der Gegenstände den Farbengegensatz zu mildern, der sehr oft stark ins Auge fällt und bei Gebrauchsgegenständen, die nicht unsehön auffallen sollen, wie z. B. bei Brillenfassungen, unerwünscht ist.Attempts have been made to soften the contrast of colors by coloring the objects, which is very often very eye-catching and with everyday objects that do not attract attention should, such as B. in eyeglass frames, is undesirable.

Diese Goldfärbungen sind jedoch, da nur oberflächlich, zu wenig dauerhaft.However, since these gold colors are only superficial, they are not permanent enough.

Man hat nun schon Goldlegierungen hergestellt, in welchen Metalle der Platingruppe enthalten sind. Auch ist es bekannt, die Metalle der Platingruppe in mehr oder minderGold alloys have now been produced, in which metals of the platinum group are included. It is also known that the metals of the platinum group in more or less

ao weitem Maße durch Metalle der Eisen-Nickel-: Gruppe, im besonderen durch Nickel zu ersetzen. Schließlich ist man bei der Herstellung solcher Legierungen anstatt von reinem Gold auch schon von Kupfergoldlegierungen ausgegangen. Die Zusammensetzung ist aber stets so gewählt worden, daß die Goldlegierungen bzw. Kupfergoldlegierungen von weißer Farbe waren.ao by far by iron-nickel metals: Group, in particular to be replaced by nickel. After all, you are in the process of manufacturing of such alloys, instead of pure gold, copper-gold alloys have already been used. The composition has always been chosen so that the gold alloys or copper gold alloys of were white in color.

Gold-Kupfer-Nickel-Legierungen mit 5 °/0 Nickel und 36,5 °/o Kupfer sowie 10 °/0 Nickel und 31,5 % Kupfer sind als blaßgelbe bzw. weiße Legierungen bekannt.Gold-copper-nickel alloys with 5 ° / 0 nickel and 36.5 ° / o copper, and 10 ° / 0 nickel and 31.5% copper are known as pale yellow or white alloys.

Gegenstand der vorliegenden Erfindung ist nun eine fleischfarbige Goldlegierung, die einem vorhandenen Bedürfnis, insbesondere auf optischem Gebiet, in weitgehendem Maße entspricht.The present invention is now a flesh-colored gold alloy that an existing need, especially in the optical field, to a large extent is equivalent to.

Die neue Legierung besteht aus 50 bis 60 °/0 Feingold, 34 bis 45 °/0 Kupfer und mehr als 5 und weniger als io°/0 Nickel.The new alloy consists of 50 to 60 ° / 0 fine gold, 34 to 45 ° / 0 copper and more than 5 and less than 10 ° / 0 nickel.

Es hat sich gezeigt, daß die mehr als 5 und weniger als 10 °/o Nickel ganz oder teilweise durch andere, dem Nickel ähnliche Metalle, nämlich Kobalt, Eisen oder Chrom, oder auch durch Metalle der Platingruppe, insbesondere durch Platin und Palladium, ersetzt werden können.It has been shown that the more than 5 and less than 10% nickel in whole or in part by other metals similar to nickel, namely cobalt, iron or chromium, or else be replaced by metals of the platinum group, in particular by platinum and palladium can.

Durch einen Zusatz von höchstens 4 °/o Zink wird die Legierung leichter bearbeitbar, ohne daß die Farbe eine wesentliche Änderung erfährt.The addition of not more than 4% zinc makes the alloy easier to work with, without the color undergoing any significant change.

Die neue Goldlegierung kann sowohl voll als auch doubliert mit einer Unterlage aus unedlem Metall verwendet werden.The new gold alloy can be made either fully or doubled with a backing base metal can be used.

Claims (4)

Patentansprüche:Patent claims: 1. Aus Gold, Kupfer und Nickel bestehende Goldlegierung, dadurch gekennzeichnet, daß sie 50 bis 6o°/0 Feingold, 34 bis 45°/o Kupfer und mehr als 5 und weniger als 10 °/o Nickel enthält.In that it contains 1 from gold, copper and nickel existing gold alloy, characterized in that 50 to 6o ° / 0 Feingold, 34 to 45 ° / o copper, and more than 5 and less than 10 ° / o nickel. 2. Goldlegierung nach Anspruch 1, gekennzeichnet durch einen Gehalt von höchstens 4°/0 Zink.2. Gold alloy according to claim 1, characterized by a content of not more than 4 ° / 0 zinc. 3· Goldlegierung nach. Anspruch ι und 2, dadurch gekennzeichnet, daß die mehr als 5 und weniger als io°/0 Nickel ganz oder teilweise durch dem Nickel ähnliche Metalle, nämlich Kobalt, Eisen oder Chrom, ersetzt sind.3 · gold alloy after. Claims ι and 2, characterized in that the more than 5 and less than 10 ° / 0 nickel are completely or partially replaced by metals similar to nickel, namely cobalt, iron or chromium. 4. Goldlegierung nach Anspruch 1 und 2, dadurch gekennzeichnet, daß die mehr als 5 und weniger als io°/0 Nickel ganz oder teilweise durch. Metalle der Platingruppe, insbesondere durch Platin oder Palladium, ersetzt sind.4. Gold alloy according to claim 1 and 2, characterized in that the more than 5 and less than io ° / 0 nickel in whole or in part. Metals of the platinum group, in particular by platinum or palladium, are replaced.
DE1930575257D 1930-05-03 1930-05-03 Gold alloy Expired DE575257C (en)