Verfahren zur Herstellung von Nischzenient. Die Erfindung bezieht
sich auf ein `"erfahren zur Verbilligung von Zement, welches dadurch gekennzeichnet
ist, daß gewöhnlichem Portlandzeinent eine verhältnismäßig kleine Menge (etwa 25
Prozent oder weniger) von Schieferkalk, (1. h. einer innigen, fein verteilten Mischung.
von gebranntem Alaunschiefer und Kalk, beigefügt wird.Process for the production of niche scenes. The invention relates
to learn about the cheaper cement, which is characterized by it
is that ordinary portland tins are a comparatively small amount (about 25
Percent or less) of shale lime, (1. i.e. an intimate, finely divided mixture.
of burnt alum slate and lime.
Bei der Zementherstellung hat inan von alters her versucht, zti fertigem
Zement gelirannten Alatinschiefer in fein verteiltem Zustand zuzusetzen. Hierbei
wirkt aber der platinschiefer hauptsächlich als Füllmittel, und eine Verhesserung
des Abbindungsverin iigens und der Festigkeit des Zements wird dadurch nicht erreicht.
Dadurch, daß man gemäß der Erfindung dein Portlandzeinent sowohl Alaunschiefer als
auch Kalk in Gestalt einer vorher hergestellten innigen, fein verteilten Mischung,
welche an und für sich ein Bindemittel darstellt, zusetzt und diese Gesamtmischung
als fertigen Zement verwendet, erhält man aber ein Erzeugnis, das eine hiihere Festigkeit
erhält als Zement allein. Da der Schieferkalk viel billiger ist als Portlandzeinent,
erreicht man auch durch den genannten Zusatz, (laß der erhaltene Zement bedeutend
billiger wird als Portlandzeinent allein. Die Erfindung besitzt somit eine große
wirtschaftliche Bedeutung. Bei der Herstellung verfährt inan beispielsweise derart,
(laß gebrannter Alaunschiefer etwa zu gleichen Teilen mit Kalk (vorzugsweise ungelöschtem
Kalk) gemischt wird, worauf diese Stoffe zusammen in einer Kugelmühle o. dgl. gemahlen
werden, und zwar zu derselben Feinheit wie Zement. Die erhaltcnc Mischung (sogenannter
Schieferkalk) wird dann mit gewöhnlichem Portlandzenient gemischt in zweckmäßigen
Mengenverhälti@issen, nämlich bis zu 25 Gewichtsteilen Schieferkalk auf wenigstens
7; Gewichtsteile Portlandzement. Dann wird auch diese Misaiting von Portlandzement
und Schieferkalk in einer Kugelmühle o. dgl. gemahlen, uni eine möglichst innige
:Mischung zu erhalten, die das grölitmögliclie Al:bindungsvermögen und Festigkeit
Lesitzt, Man kann auch die Mischung in einer anderen Weise ausführen als durch Zusaininetnnahlen.When it came to cement production, inan tried from time immemorial to produce zti
Add cement to finely divided Alatin slate. Here
but the platinum slate acts mainly as a filler, and an improvement
the setting and the strength of the cement are not achieved.
In that, according to the invention, your Portlandzeinent both alum slate and
also lime in the form of a previously prepared intimate, finely divided mixture,
which in and of itself is a binder, adds and this overall mixture
Used as a finished cement, however, one obtains a product which has a higher strength
receives as cement alone. Since the shale lime is much cheaper than portlandzeinent,
can also be achieved by the addition mentioned, (let the cement obtained be significant
becomes cheaper than Portland tents alone. The invention thus has a great
economical meaning. In the production process, for example,
(Leave burnt alum slate in roughly equal parts with lime (preferably unslaked
Lime) is mixed, whereupon these substances are ground together in a ball mill or the like
to the same fineness as cement. The mixture obtained (so-called
Shale lime) is then mixed with ordinary Portland scent in appropriate
Quantitative proportions, namely up to 25 parts by weight of shale lime at least
7; Parts by weight of portland cement. Then this too will be misaiting from portland cement
and shale lime ground in a ball mill or the like, uni as intimately as possible
: Mixture to obtain the greatest possible Al: binding capacity and strength
Lesitzt, the mixture can also be carried out in a different way than by adding together.
Bei Anwendung der Erfindung kann man einen Zement erhalten, der bei
zwezkmäßigen Mischungsverhältnissen, -r_.13. 75 Gewichtsteile Portlandzeinent und
25 Gewichtsteile Schieferkalk, eine höhere Festigkeit und ein größeres Abbindungsverinögen
erhält als Portlandzenient allein, wobei der neue Zeinent wesentlich billiger wird
als Portlandzeinent allein.Using the invention, a cement can be obtained which is at
two-way mixing ratios, -r_.13. 75 parts by weight of Portland zeinent and
25 parts by weight of shale lime, greater strength and greater setting properties
receives as a portland scene alone, whereby the new Zeinent is much cheaper
as a portland tenant alone.
Als ein Beispiel sei angeführt, daß eine
Probe von
Portlandzement allein eine: Druckfertigkeit von 278 kgjqcrn 'nach 28 Tagea gemäß
dir üblichen Zementp@pNe aufwies, während eine Mischung von 75 Gewichtsteilen derselben
Zementart mit 25 Gewichtsteilen Schieferkalk eine entsprechende Festigkeit von 3
i 2 kgqcm zeigte.As an example, consider that a
Sample of
Portland cement alone one: ready to print 278 kgjqcrn 'after 28 days a according to
the usual cement p @ pNe, while a mixture of 75 parts by weight of the same
Cement type with 25 parts by weight of shale lime a corresponding strength of 3
i showed 2 kgqcm.