DE4014910C2 - - Google Patents
Info
- Publication number
- DE4014910C2 DE4014910C2 DE19904014910 DE4014910A DE4014910C2 DE 4014910 C2 DE4014910 C2 DE 4014910C2 DE 19904014910 DE19904014910 DE 19904014910 DE 4014910 A DE4014910 A DE 4014910A DE 4014910 C2 DE4014910 C2 DE 4014910C2
- Authority
- DE
- Germany
- Prior art keywords
- wood wool
- insulation
- latex
- packaging
- objects according
- Prior art date
- Legal status (The legal status is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the status listed.)
- Expired - Fee Related
Description
Die Erfindung betrifft einen Dämm- und Verpackungsgegenstand, der im wesentlichen aus Holzwolle besteht, die durch ein Bindemittel miteinander verbunden ist.The invention relates to an insulation and Packaging object, essentially made of wood wool exists, which are connected by a binder is.
Ein derartiger Verpackungsgegenstand ist aus der DE-PS 5 28 004 bekannt. Bei diesem Verpackungsgegenstand handelt es sich um eine Holzwollehülse, die aus zirkular umlaufend angeordneten Holzwollefäden besteht, die in axialen Streifen mit einem Leimauftrag verbunden und versteift sind. Diese Art der Herstellung der Holzwollehülse setzt somit speziell gefertigte lange Holzwollefäden voraus, die außerdem umlaufend angeordnet werden müssen. Durch diese gerichtete Ordnung ist die Dichte und Steifigkeit einer solchen Hülle wesentlich höher als bei der üblich hergestellten ungerichteten Anordnung von Holzwolle. Außerdem erbringen die Leimstreifen eine erhebliche Versteifung der Hülle.Such an article of packaging is from DE-PS 5 28th 004 known. This packaging item is about is a wood wool sleeve that is made of circular all-round arranged wood wool threads that exist in axial strips are connected and stiffened with a glue application. These The type of manufacture of the wood wool sleeve thus sets special manufactured long wood wool threads ahead, which also must be arranged all around. Directed by this Order is the density and rigidity of such a shell much higher than that of the commonly manufactured undirected arrangement of wood wool. Also provide the strips of glue significantly stiffen the shell.
Es ist weiterhin bekannt, Holzwolle wegen ihres geringen Gewichtes, ihrer Elastizität und ihres niedrigen Preises zu Verpackungszwecken zu benutzen, indem die Zwischenräume zwischen zu verpackenden Gegenständen und einer umgebenden Verpackungskiste oder einem Karton mit Holzwolle befüllt und ausgestopft wird. Nachteilig dabei ist die relativ aufwendige Handarbeit des Stopfens und daß Holzstaub und die Holzwolleschnitzel beim ein- und Auspacken der Ware herumfliegen und auch die Ware davon entstaubt werden muß.It is also known to use wood wool because of its low Weight, its elasticity and its low price Use packaging by the spaces between objects to be packaged and a surrounding one Packing box or a box filled with wood wool and is stuffed. The disadvantage here is the relatively complex Handicraft of the plug and that wood dust and the Wood wool chips when packing and unpacking the goods fly around and the goods must be dedusted from it.
Aus diesem Grunde werden zunehmend wesentlich teurere geschäumte Kunststoffe als Verpackungsmaterialien genutzt, die jedoch den Verpackungsmüllberg vergrößern, und deren Schäummittel die Umwelt belasten. Außerdem weisen diese bei gleicher Dämmung wie Holzwolle ein wesentlich höheres Verpackungsgewicht auf, das auch erhöhte Transportkosten verursacht.Because of this, are becoming increasingly more expensive foamed plastics used as packaging materials, which, however, enlarge the mountain of packaging waste, and their Foaming agents pollute the environment. They also demonstrate same insulation as wood wool a much higher Packing weight on, which also increased transportation costs caused.
Weiterhin sind im Bauwesen Dämmplatten aus Holzwolle bekannt, die mit einer Zementschlämmung verfestigt sind. Diese weisen eine geringe Elastizität auf, und ihr Gewicht ist durch den mineralischen Binder sehr hoch, so daß sie für Verpackungszwecke nicht brauchbar sind.Furthermore, insulation boards made of wood wool are used in construction known that are solidified with a cement slurry. These have low elasticity and weight is very high due to the mineral binder, so that it is suitable for Packaging purposes are not usable.
Es ist Aufgabe der Erfindung, den eingangs bezeichneten Verpackungsgegenstand derart zu verbessern, daß er einfacher herzustellen ist, höhere Elastizität und Stoßdämmung aufweist und er keinen Holzstaub oder Holzwolleschnitzel absondert.It is an object of the invention, the one mentioned Improve packaging item so that it is easier is to produce higher elasticity and shock insulation and it has no wood dust or wood wool chips secretes.
Die Lösung besteht darin, daß die Holzwolle aus Holzwollestreifen und Holzwolleabschnitten besteht, die in loser Schüttung angeordnet und vollständig mit dem Bindemittel beschichtet sind, das ein zähelastisch verfestigtes Latex ist.The solution is that the wood wool from Wood wool strips and wood wool sections that exist in arranged in bulk and completely with the Binders are coated, which is tough and elastic solidified latex.
Vorteilhafte Ausgestaltungen der Gegenstände und eines Herstellungsverfahrens derselben sind in den Unteransprüchen angegeben.Advantageous configurations of the objects and one Manufacturing processes of the same are in the subclaims specified.
Die Holzwolle ist ein äußerst preiswerter Naturstoff, der vorwiegend aus billigen, schnellwachsenden Hölzern hergestellt wird. Als elastisches Bindemittel ist Naturlatex bevorzugt, da das damit hergestellte Material, so weit es nicht mehrfach benutzt wird, umweltfreundlich zu entsorgen ist, da es verbrannt, kompostiert oder problemlos zu deponieren ist. Auch entstehen bei der Verfestigung des Latex keine schädlichen Abgase. Die Prozeßtemperatur von 100°C ist durch Niedertemperaturabwärme anderer Industrieprozesse preiswert verfügbar zu machen.Wood wool is an extremely inexpensive natural product that predominantly from cheap, fast-growing woods will be produced. Natural latex is an elastic binder preferred since the material made with it as far as it is is not used more than once and is disposed of in an environmentally friendly manner is because it's burned, composted, or hassle-free deposit. Also arise during the solidification of the Latex no harmful fumes. The process temperature of 100 ° C is due to low temperature waste heat from others To make industrial processes inexpensively available.
Die Beschichtung der Holzwolle erfolgt vorzugsweise in einem dünnflüssigen Zustand des Latex durch Besprühen oder durch eine Durchmischung mit Latexschaum, so daß eine vollständige Einhüllung der Holzwollefasern erfolgt und diese später keine Stäube mehr absondern. Die dicht mit Latex bedeckte Holzwolle wird entweder in einzelne Formen eingefüllt, so daß darin zu bestimmten zu verpackenden Gegenstände, z. B. Flaschen, passende Verpackungsteile entstehen, oder sie wird auf Förderbändern durch zu den gewünschten Außenabmessungen passende Schächte gefördert. Die Formen, Förderbänder und -Schachtwände sind vorzugsweise gitterartig oder mit in Transportrichtung verlaufenden Stegen ausgebildet, so daß die warme Prozeßluft die Form und die Formlinge gut durchströmen kann und eine kurze Prozeßdurchlaufzeit benötigt wird. Da das Holzwollematerial sehr locker ist, kann die Prozeßluft diese gut durchlüften und die Wärme durch und durch darin wirksam werden, wodurch eine schnelle Verfestigung erfolgt.The wood wool is preferably coated in one thin state of the latex by spraying or by a mix with latex foam so that a complete The wood wool fibers are wrapped and later no longer separate dust. The one covered with latex Wood wool is either filled into individual forms, so that it contains certain items to be packed, e.g. B. Bottles, suitable packaging parts are created, or they will on conveyor belts through to the desired external dimensions suitable shafts funded. The forms, conveyor belts and -Shaft walls are preferably grid-like or with in Transport direction extending webs formed so that the warm process air flows through the mold and the moldings well can and a short process cycle time is required. There the wood wool material is very loose, the process air ventilate them well and heat through and through become effective, resulting in a rapid solidification.
Je nach der gewünschten Tragfähigkeit des fertigen Dämmaterials wird die benetzte Holzwolle in loser Schüttung oder auf einen Bruchteil seines Ausgangsvolumens verdichtet der Wärmebehandlung zugeführt. In jedem Fall weist die lockig strukturierte Holzwolle eine Vielzahl von Berührungsstellen auf, die mit dem Latex elastisch verbunden werden, so daß ein dreidimensional vernetztes elastisches Material geringer Dichte und hoher Elastizität entsteht. Durch diese dreidimensionale Vernetzung weist das Material eine Scherfestigkeit auf, die wesentlich höher als bei der Holzwolle allein ist, bei der nur ein gegenseitiges Abstützen und Verhaken der Fasern vorhanden ist, aber noch eine Verschieblichkeit gegeneinander besteht.Depending on the desired load capacity of the finished The wetted wood wool is used in bulk as insulation material or compressed to a fraction of its original volume fed to the heat treatment. In any case, the curly point structured wood wool a variety of points of contact on, which are elastically connected to the latex, so that a three-dimensionally cross-linked elastic material less Dense and high elasticity arises. Through this The material exhibits three-dimensional networking Shear strength which is much higher than that of the Wood wool alone is only mutual Bracing and snagging of the fibers is present, but still there is movement towards one another.
Die Handhabbarkeit der fertigen Gegenstände, die als Matten, Schläuche oder Hohlräume aufweisende Formstücke ausgebildet sind, ist genau so einfach wie die von solchen Teilen aus Schaumstoffen.The manageability of the finished objects, which are used as mats, Hoses or cavities formed fittings is just as simple as that from such parts Foams.
Anhand der Fig. 1 bis 4 sind beispielhaft die Gegenstände beschrieben.The objects are described by way of example with reference to FIGS. 1 to 4.
Fig. 1 zeigt einen Abschnitt einer Dämm-Matte; Fig. 1 shows a section of an insulation mat;
Fig. 2 zeigt einen Abschnitt eines Dämmschlauches; Fig. 2 shows a section of an insulation hose;
Fig. 3 zeigt ein Verpackungsformstück; Fig. 3 shows a packaging molding;
Fig. 4 zeigt eine Ausschnittsvergrößerung. Fig. 4 shows an enlarged detail.
Fig. 1 zeigt verkleinert einen Dämmattenabschnitt (1). Dieser besteht beispielsweise aus lose geschütteter Holzwolle (H), die mit Latex kontaminiert und an den Berührungsstellen der Fasern dadurch miteinander elastisch verbunden ist. Diese Matten lassen sich in beliebigen Abmessungen praktisch endlos herstellen und passend zum Verwendungszweck zuschneiden. Die Matte ist beispielsweise 5 cm stark. Fig. 1 shows a reduced size of an insulation section ( 1 ). This consists, for example, of loosely poured wood wool (H) which is contaminated with latex and is thus elastically connected to one another at the points of contact of the fibers. These mats can be made practically endless in any dimensions and cut to fit the intended purpose. For example, the mat is 5 cm thick.
Fig. 2 zeigt einen Dämmschlauchabschnitt (2). Er dient beispielsweise als eine Flaschenumhüllung zur Stoßdämpfung beim Transport und ersetzt so die bekannten Strohhüllen, die lästigen Staub und Späne abgeben. Die Holzwolle (H) ist vorzugsweise während der Abbindung des Latex so weit verdichtet, daß die Wandstärke des Schlauches nur wenige Millimeter beträgt und der Schlauch bei guter Dämmung nur wenig Raum in einem Verpackungsbehältnis einnimmt. Fig. 2 shows an insulation hose section ( 2 ). It serves, for example, as a bottle wrapper for shock absorption during transport and thus replaces the well-known straw covers that give off annoying dust and chips. The wood wool (H) is preferably compressed to such an extent during the setting of the latex that the wall thickness of the hose is only a few millimeters and, with good insulation, the hose takes up little space in a packaging container.
Fig. 3 zeigt ein Verpackungsformstück (3) für eine Glaskörperverpackung in Aufsicht. Seine Außenmaße sind an ein Standardpaket angepaßt, und den Umrissen der einzupackenden Gegenstände angepaßt sind verschieden große Ausnehmungen (10, 11) darin eingeformt. Ein gleiches Formstück (3) wird zum vollständigen Verpacken der Gegenstände umgekehrt daraufgesetzt, so daß die empfindlichen Gegenstände allseitig sicher eingehüllt sind. Die Elastizität des Materials gleicht Größentoleranzen aus, und ein vorgegebenes Untermaß der Ausnehmungen erbringt eine elastische Halterung der Gegenstände unter einer Vorspannung, so daß keine Beschädigung der Oberfläche bei einem gegebenenfalls rüttelnden Transport durch Scheuern oder Schaben entstehen können. Fig. 3 shows a packaging molding ( 3 ) for a glass body packaging in supervision. Its external dimensions are adapted to a standard package, and recesses ( 10, 11 ) of different sizes are formed in it to match the outlines of the objects to be packed. An identical shaped piece ( 3 ) is placed upside down to completely pack the objects, so that the sensitive objects are safely encased on all sides. The elasticity of the material compensates for size tolerances, and a predetermined undersize of the recesses provides elastic holding of the objects under a pretension, so that no damage to the surface can occur during a possibly shaking transport by rubbing or scraping.
Fig. 4 zeigt einen kleinen Ausschnitt vergrößert. Die spiral- oder wendelförmigen Holzwollestreifen (H1, H2) sind von einer dünnen Latexschicht (L) völlig umhüllt, wie der Querschnitt zeigt. An den Berührungsstellen (B) der Streifen umgibt die Latexschicht (L) beide Fasern oder Streifen (H1, H2), und sie bildet eine Bindebrücke (12) aus. Die Elastizität des Latexmaterials ermöglicht eine elastische Beweglichkeit der Streifen unter Last; diese Verbindung ist haltbar, da die dort auftretenden Scher- und Biegekräfte wegen der begrenzten Steifigkeit der gebogenen Holzwollestreifen (H1, H2) gewöhnlich unterhalb der Festigkeit der Latexbindung im Kreuzungsbereich liegen. Auch nach wechselnder Druck- und/oder Biegebeanspruchung der Verpackungsgegenstände lösen sich keine Einzelteile aus dem Verbund, und die Elastizität und das Stoß-Dämpfungsverhalten bleibt dabei unverändert. Fig. 4 shows a small section enlarged. The spiral or helical wood wool strips (H 1 , H 2 ) are completely covered by a thin layer of latex (L), as the cross-section shows. At the points of contact (B) of the strips, the latex layer (L) surrounds both fibers or strips (H 1 , H 2 ) and forms a connecting bridge ( 12 ). The elasticity of the latex material allows the strips to move flexibly under load; this connection is durable since the shear and bending forces that occur there are usually below the strength of the latex bond in the area of intersection due to the limited rigidity of the bent wood wool strips (H 1 , H 2 ). Even after changing pressure and / or bending stress on the packaging objects, no individual parts are released from the composite, and the elasticity and the shock-absorbing behavior remain unchanged.
Bei der handelsüblichen Holzwolle, die aus 1-2 mm breiten Holzspan-Streifen besteht, hat sich eine Latexmenge von etwa 40 g auf 100 g Holzwolle als zweckmäßig erwiesen, um eine völlige Umschließung der Späne und eine gute Bindung der Berührungsstellen zu gewährleisten. Abhängig von der Holzart und der Spanbreite und Spandicke sowie der gewünschten Elastizität des Materials können Latexmengen von 20-70 g pro 100 g Holzwolle eingesetzt werden.With the commercially available wood wool, which is made of 1-2 mm wide Wood chip strips exist, has a latex amount of about 40 g to 100 g of wood wool proved to be useful to a complete encapsulation of the chips and good binding of the To ensure contact points. Depending on the type of wood and the chip width and chip thickness as well as the desired Elasticity of the material can amount to 20-70 g latex can be used per 100 g of wood wool.
Bei loser Schüttung der Holzwolle und 40 g Latexeinsatz pro 100 g Holzwolle ergibt sich eine Dichte von unter 20 g/l. Bei einer Vorverdichtung und bei anderen Spanabmessungen oder Holzarten ergeben sich Dichten zwischen 10-80 g/l. Die Eigenschaften des Materials lassen sich demgemäß leicht den jeweiligen Anforderungen optimal anpassen. Somit ist ein sauberes vielseitig verwendbares Verpackungsmaterial aus reinem Naturstoff durch dieses neuartige elastische Bindeverfahren der Holzwolle geschaffen.With loose fill of wood wool and 40 g latex insert per 100 g wood wool results in a density of less than 20 g / l. With pre-compaction and with other chip dimensions or types of wood there are densities between 10-80 g / l. The properties of the material can therefore be easily optimally adapt to the respective requirements. So is a clean, versatile packaging material pure natural material through this new elastic Wood wool binding process created.
Die Auswahl eines jeweils geeigneten Latexrohstoffes bietet eine weitere Möglichkeit, die Eigenschaften des Endproduktes den jeweils geforderten Festigkeits- und Elastizitätsanforderungen anzupassen und vielfältige Anwendungen zu erschließen.The selection of a suitable latex raw material offers another way of determining the properties of the end product the required strength and Adapt elasticity requirements and diverse Open up applications.
Claims (8)