Verfahren zur Herstellung von Zündsätzen. In dem Patent 369104 ist
ein Verfahren zur Herstellung von Zündsätzen aus Lösungen hochnitrierter Phenole.
mit Alkalien und Bleisalzlösungen bei erhöhter oder gewöhnlicher Temperatur beschrieben.Process for the production of ignition charges. In the patent 369104 is
a process for the production of ignition charges from solutions of highly nitrated phenols.
described with alkalis and lead salt solutions at elevated or ordinary temperature.
Es wurden nun folgende Beobachtungen gemacht Auch Nitrokörper anderer
Natur als die Nitrophenole, die zur Salzbildung befähigt sind, bilden zu Zündsätzen
geeignete basische Bleisalze. Hierher gehören u. a. Hexanitrodiphenylamin, Di- und
Trinitrobenzoesäure, die basischen nitrosauren Salze, z. B. basisches dinitrobenzolnitrosaures
Blei von der Formel:
In einer Arbeit von A. H an t zs c h und Hermann K i s s e1 , Chemisches Centralblatt
1900 1A15, Berichte d. dtsch. chem. Gesellschaft, Band 32, 1899, S. 3137
bis 3148 ist die Bildung nitrosaurer Salze, die sich vom Trinitrobenzol und vom
Trinitrotoluol ableiten, beschrieben. Ferner sind noch verschiedene andere Derivate
in der angegebenen Arbeit erwähnt und ihre Darstellung beschrieben.The following observations have now been made. Nitro bodies of a different nature than the nitrophenols, which are capable of forming salts, also form basic lead salts suitable for ignition charges. This subheading includes hexanitrodiphenylamine, di- and trinitrobenzoic acid, the basic nitro-acid salts, e.g. B. basic dinitrobenzene nitro acid lead of the formula: In a work by A. H an t zs ch and Hermann K iss e1, Chemisches Centralblatt 1900 1A15, reports d. German chem. Gesellschaft, Volume 32, 1899, pp. 3137 to 3148 describes the formation of nitrosate salts derived from trinitrobenzene and trinitrotoluene. In addition, various other derivatives are mentioned in the cited work and their representation is described.
Ferner zum Teil basische Salze und Salze, die mit Pb O oder Pb (O
H2) Doppelsalze bilden oder mit ihnen isomorph sind, z.B. basisches Bleipikrat
mit wechselnden Mengen Bleihydroxyd oder Bleioxyd. Verwendet man eine Mischung von
Lösungen mehrerer Nitrokörper oder ihrer Salze, so entstehen beim Einlaufen dieser
Lösungen in die Bleisalzlösungen häufig isomorphe Salze oder Mischkristalle und
auch Doppelsalze. Es kann auch ein Zusammenkristallisieren mit Salzen anderer Metallen
erfolgen bzw. Doppelsalzbüdung eintreten. Es kommt auch vor, daB eine Mischung verschiedener
Kristallarten entsteht, die sich durch mechanische Mittel nicht trennen läBt, da
die Kriställchen der
einzelnen Bestandteile aneinander- und durcheinandergewachsen
-sind. Ferner ist es möglich, falls vollkommene Isomorphie vorliegt, durch nachelrfanderfolgendes
Zugeben der Lösungen unter Rührung oder Bewegung Kriställchen herzustellen, die
mit einem kristallinischen Mantel eines anderen Salzes umgeben sind. Zur Erhöhung
der Empfindlichkeit oder Unempfindlichkeit und auch für andere Zwecke kann dies
von Vorteil sein. Für das isomorphe Zusammenkristallisieren ist es nicht erforderlich,
daß alle Bestandteile basische Salze sind; ein oder mehrere Bestandteile können
auch neutral oder nur zum Teil basisch sein.Furthermore, some basic salts and salts which form double salts with Pb O or Pb (O H2) or are isomorphic with them, eg basic lead picrate with varying amounts of lead hydroxide or lead oxide. If a mixture of solutions of several nitro bodies or their salts is used, isomorphic salts or mixed crystals and also double salts are often formed when these solutions run into the lead salt solutions. It can also crystallize together with salts of other metals or double salt formation can occur. It also happens that a mixture of different types of crystals is formed which cannot be separated by mechanical means, since the small crystals of the individual components have grown together and mixed up. Furthermore, if there is complete isomorphism, it is possible, by successive addition of the solutions with stirring or agitation, to produce crystals which are surrounded by a crystalline coat of another salt. This can be advantageous to increase the sensitivity or insensitivity and also for other purposes. For isomorphic crystallization together, it is not necessary that all of the constituents are basic salts; one or more constituents can also be neutral or only partially basic.
Die Herstellung dieser neuen Zündsätze, die aus den Lösungen als gut
verarbeitbare schwere kristallinische Pulver ausfallen, bietet den großen Vorteil,
daß man die Brisanz bis zu einem gewissen Grade regeln kann. Man ist also in der
Lage, die Zündsätze zum Teil dem Verwendungszweck anzupassen. Hierdurch ist es möglich,
Einheitszündsätze zu erhalten und das seither für viele Zündsätze erforderliche
mechanische Mischen zu vermeiden. Die Körper können natürlich auch in Mischung mit
den üblichen Zündsatzbestandteilen verwendet werden. Die meisten sind außerordentlich
stabil und besitzen auf Metallen wie Eisen, Zink und Aluminium sehr große Lagerbeständigkeit.
Infolgedessen kann man ihnen zur Erhöhung der Flammentemperatur auch Aluminium-,
Magnesium-, Zer- und andere Metallpulver zusetzen, was bei Verwendung in Zündhütchen
äußerst vorteilhaft ist, da durch die starke Erhöhung der Temperatur der Explosionsgase
eine ausgezeichnete Zündung des Pulvers in den Patronen usw. erfolgt. Außerdem ist
man infolge dieser Eigenschaften von der Verwendung von Kupfer und Messing als Hülsenmaterial
unabhängig und kann Aluminium, Aluminiumlegierungen und andere Metalle verwenden.Making these new primers out of the solutions as well
Processable heavy crystalline powder precipitate, offers the great advantage
that you can regulate the explosiveness to a certain extent. So you are in the
Able to adapt the ignition charges to the intended use. This makes it possible
To get unit primers and that has since been required for many primers
avoid mechanical mixing. The body can of course also blend in with it
the usual primer components can be used. Most are extraordinary
stable and have a very long shelf life on metals such as iron, zinc and aluminum.
As a result, you can also use aluminum,
Add magnesium, cerium and other metal powders, which is when used in primers
is extremely advantageous because of the sharp increase in the temperature of the explosion gases
excellent ignition of the powder in the cartridges, etc., takes place. Also is
As a result of these properties, copper and brass are not used as sleeve material
independent and can use aluminum, aluminum alloys and other metals.