Abstract

Process for producing a customer, credit or identity card which can be printed on by a cold-laser printer from a piece of PVC sheet in card form. The PVC sheet has a surface roughness of 5-15 mu m and is coated at least on one side, at least partially, with a UV varnish, which is left to cure in the UV light.

Description

Die Erfindung betrifft ein Verfahren zum Herstellen einer Kunden-, Kredit- oder Kennkarte aus einem kartenförmigen Stück einer PVC-Folie.The invention relates to a method for producing a Customer, credit or identification card from a card-shaped Piece of a PVC film.

Kunststoffkarten aus einer PVC-Folie, die als Kunden-, Kredit- oder Kennkarten, beispielsweise als Service- und Mitgliedskarten verwandt werden, müssen mit Angaben, bei spielsweise zum Karteninhaber, bedruckt werden. Diese An gaben schließen den Namen, die Mitgliedsnummer, die An schrift und ähnliches ein, so daß diese Karten individuell dem zugehörigen Karteninhaber zugeordnet werden können.Plastic cards made of a PVC film that can be used as customer, Credit or identification cards, for example as service and Membership cards must be used with details at for example to the cardholder. This to gave the name, the membership number, the details writing and the like, so that these cards individually can be assigned to the associated cardholder.

Aus optischen Gründen sowie aus Gründen der Unempfindlich keit, beispielsweise gegenüber Fingerabdrücken und ähnlichem, ist es dabei wünschenswert, daß derartige Karten eine glän zende Oberflächenbeschaffenheit haben.For visual reasons and for reasons of insensitivity speed, for example against fingerprints and the like, it is desirable that such cards a glossy have a surface texture.

Bisher wurden diese Karten daher dadurch hergestellt, daß eine Glanz-PVC-Folie durch Siebdruck mit einem Feld zum Beschriften versehen wurde, um die Karten mit den notwendigen Angaben, beispielsweise zum Karteninhaber, zu versehen. Das durch Siebdruck aufgebrachte Feld besteht dabei aus einem kreideartigen Aufdruck, der in verschiedener Weise beschreib- und bedruckbar ist.So far, these cards have therefore been produced in that a gloss PVC film by screen printing with a box for Labeling was provided to provide the cards with the necessary Provide information, for example about the cardholder. The the field applied by screen printing consists of a chalk-like print that describes in different ways and is printable.

Als Hochleistungsdrucker werden gegenwärtig, insbesondere in Verbindung mit Rechnersystemen, Laserdrucker ver wandt. Derartige Laserdrucker, die als Kaltlaserdrucker erhält lich sind, arbeiten auf einem elektrofotografischen Druckprin zip mit Lasertechnik. Eine rotierende mit einem Fotohalb leiter beschichtete Trommel wird dabei elektrostatisch aufgeladen. Der Laserstrahl und die Druckeinrichtung bringen die Information durch Belich tung in Form von Ladungsbildern auf die Trommel. In der Entwicklerstation setzt sich entsprechend den Ladungs bildern der Toner an den belichteten Stellen fest. Das ent standene Druckbild wird an der Umdruckstation auf das zu bedruckende Material übertragen und in der nachfolgenden Fixierstation fixiert.High performance printers are currently used, particularly in Connection with computer systems, laser printer ver turns. Such laser printer, which receives as a cold laser printer are working on an electrophotographic print zip with laser technology. A rotating one with a photo half conductor coated drum is charged electrostatically. The laser beam and the printing device bring the information through Belich tion in the form of charge images on the drum. In the Developer station sits down according to the cargo image the toner in the exposed areas. That ent standing print image is at the transfer station to the printing material transferred and in the subsequent Fuser station fixed.

Aufgrund der hohen Leistung derartiger Laserdrucker wäre es wünschenswert, diese Drucker auch beim Bedrucken der durch Siebdruck aufgebrachten Beschriftungsfelder der aus Glanz- PVC-Folie bestehenden Kunden-, Kenn- oder Kreditkarten ein zusetzen. Das war jedoch bisher nicht möglich, da beim Be drucken mit einem Laserdrucker keine ausreichende Haftung des Toners auf dem Siebdruckfeld und damit ein akzeptables Er gebnis erzielbar war.Because of the high performance of such laser printers would be it is desirable to use these printers even when printing through Screen printing applied labeling fields made of glossy PVC film existing customer, identification or credit cards clog. However, this has not been possible until now, since the Be printing with a laser printer is not sufficient of the toner on the screen printing field and thus an acceptable Er result was achievable.

Die der Erfindung zugrundeliegende Aufgabe besteht daher darin, ein Verfahren zum Herstellen einer Kunden-, Kredit- oder Kenn karte der eingangs genannten Art zu schaffen, das Kunden-, Kredit- oder Kennkarten liefert, die mit einem Kaltlaser drucker bedruckbar sind.The object on which the invention is based is therefore a method of making a customer, credit or identification to create a card of the type mentioned at the beginning, Supplies credit or identification cards using a cold laser printers are printable.

Diese Aufgabe wird gemäß der Erfindung dadurch gelöst, daß als PVC-Folie eine solche mit einer Oberflächenrauhigkeit von 5-15 µm verwendet wird und das PVC-Folienstück auf wenigstens einer Seite wenigstens teilweise mit einer UV-Farbe lackiert wird, die in UV-Licht aushärten gelassen wird.This object is achieved according to the invention in that as PVC film is used with a surface roughness of 5-15 microns and the PVC film piece on at least one side at least partially painted with a UV paint that is in UV light is allowed to harden.

Die PVC-Folie hat vorzugsweise eine Oberflächenrauhigkeit von 10 µm.The PVC film preferably has a surface roughness of 10 µm.

Im folgenden wird ein besonders bevorzugtes Ausführungsbei spiel des erfindungsgemäßen Verfahrens näher beschrieben. The following is a particularly preferred embodiment game of the inventive method described in more detail.

Eine schlagzähe Homopolymer-PVC-Hartfolie ohne Weichmacher mit einer Oberflächenrauhigkeit von 10 µm wird mit einer UV-Farbe, beispielsweise einem UV-Lack, d. h. einer UV-Farbe ohne Pigmente, lackiert. Der Lack besteht aus einem vorpoly merisierten Kunststoffmaterial mit Fotoinitiatoren, die durch UV-Licht aktiviert werden, so daß das Kunststoff material fotopolymerisiert.An impact-resistant homopolymer PVC hard film without plasticizer with a surface roughness of 10 µm is with a UV ink, for example a UV varnish, d. H. a UV color without pigments, lacquered. The paint consists of a prepoly merized plastic material with photo initiators, the be activated by UV light so that the plastic material photopolymerized.

Vorzugsweise werden UV-Farben und UV-Lacke mit mittlerer Viskosität und hoher Elastizität verwandt, die bis zu 200°C pro 5 Sekunden heißsiegelbeständig und insbesondere wasser fest, alterungsbeständig und beispielsweise gegenüber Benzin unempfindlich sind.Preferably UV inks and UV varnishes with medium Viscosity and high elasticity related, up to 200 ° C per 5 seconds heat seal resistant and especially water firm, resistant to aging and, for example, against petrol are insensitive.

Die UV-Farbe wird im Naß- oder Trockenoffsetverfahren aufge bracht, wobei das Naßoffsetverfahren zum Aufbringen der UV- Farben mit Pigmenten bevorzugt ist, während das Trockenoff setverfahren zum Aufbringen der UV-Lacke ohne Pigmente be vorzugt ist.The UV ink is applied using the wet or dry offset process brings, the wet offset process for applying the UV Colors with pigments are preferred, while the dry off set process for applying UV varnishes without pigments is preferred.

Nach dem Lackieren mit der UV-Farbe oder dem UV-Lack wird die in dieser Weise bedruckte Folie unter einer UV-Lampe hindurch geführt, wobei die Farbe oder der Lack in wenigen Sekunden bruchteilen aushärtet.After painting with the UV ink or UV varnish, the in this way printed film under a UV lamp led, the paint or varnish in a few seconds parts hardened.

Die in dieser Weise hergestellten Karten werden nach ihrem Zuschnitt auf eine Form aufgebracht und im Laserdrucker mit den erforderlichen Angaben bedruckt.The cards produced in this way are made according to their Cutting applied to a form and in the laser printer printed the required information.

Claims

1. A method for producing a customer, credit or identification card from a card-shaped piece of PVC film, characterized in that the PVC film is used with a surface roughness of 5-15 microns and the PVC film piece on at least one side is at least partially coated with a UV ink that is allowed to harden in UV light.

2. The method according to claim 1, characterized in that that a PVC with a surface roughness of 10 microns is used.