DE3339535A1 - Structural adhesive - Google Patents
Structural adhesiveInfo
- Publication number
- DE3339535A1 DE3339535A1 DE19833339535 DE3339535A DE3339535A1 DE 3339535 A1 DE3339535 A1 DE 3339535A1 DE 19833339535 DE19833339535 DE 19833339535 DE 3339535 A DE3339535 A DE 3339535A DE 3339535 A1 DE3339535 A1 DE 3339535A1
- Authority
- DE
- Germany
- Prior art keywords
- parts
- cement
- construction adhesive
- adhesive according
- weight
- Prior art date
- Legal status (The legal status is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the status listed.)
- Withdrawn
Abstract
Description
PatentanmeldungPatent application
D 6891D 6891
"Baukleber""Construction Adhesive"
Die Erfindung betrifft einen 2-kompenentigen Baukleber, der sich insbesondere für die Verklebung von wasserundurchlässigen Substraten eignet.The invention relates to a 2-component construction adhesive, which is particularly suitable for bonding waterproof substrates.
Im Bauhandwerk besteht zunehmend ein.Bedarf nach Klebstoffen, cie es erlauben, wasserundurchlässige Wand- und Bodenbeläge mit ebensolchen zu überkleben. Eine derartige Vorgehensweise bietet z.B. bei der Altbaurenovierung eine erhebliche Arbeitsersparnis. Zur technischen Realisierung dieser Arbeitsweise werden Klebstoffe benötigt, die ohne Stoffaustausch mit der Umgebung härten. Geeignete Klebstoffe sollen hinsichtlich ihrer anwendungstechnischen Eigenschaften, wie auch hinsichtlich ihres Preises den am Bau üblichen Anforderungen entsprechen und keine besonderen Verarbeitungsprobleme mit sich bringen.In the building trade there is an increasing need for adhesives, cie allow waterproof wall and floor coverings to be pasted over with the same. Such a one The procedure offers considerable labor savings, e.g. when renovating old buildings. To the technical Realization of this working method requires adhesives that do not exchange substances with the environment harden. Suitable adhesives should with regard to their application properties, as well as with regard to their price correspond to the requirements customary in construction and do not have any special processing problems bring yourself.
So sind die bisher verwendeten Lösungsmittelklebstoffe für diese Anwendung nicht geeignet, da eine beschichtete Fläche erst nach völligem Verdunsten des Lösungsmittels belegt werden kann. Sogenannte Full-Solid-Klebstoffe, wie z.B. Schmelzkleber und Reaktionsklebstoffe setzen besondere Arbeitstechniken voraus und sind meist für derartige Anwendungen zu teuer.Such are the solvent adhesives used to date Not suitable for this application, as a coated surface only occurs after the solvent has completely evaporated can be proven. So-called full-solid adhesives, such as E.g. hot melt adhesives and reactive adhesives set special features Techniques ahead and are usually too expensive for such applications.
8d 230/438539 4.04 838d 230/438539 4.04 83
BAD 0RJG5NALBAD 0RJG5NAL
Patentanmeldung D 6891 HENKELKGaAPatent application D 6891 HENKELKGaA
ZR-FE/PatenteZR-FE / patents
Es ist somit Aufgabe der Erfindung, auf Basis eines kunststoffvergüteten hydraulischen Bindemittels einen Baukleber zu schaffen, der den genannten Anforderungen entspricht. Der Baukleber soll insbesondere zum Verkleben extrem dichter Boden- und Wandbeläge, wie z.B. PVC oder Gummi mit sich selbst und ähnlichen Substraten geeignet sein.It is therefore the object of the invention to provide a hydraulic binder based on a plastic-modified hydraulic binder To create construction adhesive that meets the stated requirements. The construction adhesive is intended in particular for gluing extremely dense floor and wall coverings, such as PVC or rubber, are suitable for themselves and similar substrates be.
Gegenstand der Erfindung ist somit ein 2-Komponenten-Baukleber auf Basis eines Kunststoff modifizierten hydraulischen Bindemitt&s zum Verkleben von wasserundurchlässigen Substraten, dadurch gekennzeichnet, daß er in getrennter Verpackung enthält:The invention thus provides a 2-component construction adhesive based on a plastic modified hydraulic Binder & s for bonding water-impermeable substrates, characterized in that it is in separate packaging contains:
1) 25-60 Gew.-% einer wäßrigen Kunststoffdispersion1) 25-60% by weight of an aqueous plastic dispersion
eines bei Temperaturen über O0C flexiblen Polymerena polymer flexible at temperatures above 0 ° C
2) 40-75 Gew.-% einer Zementmischung, bestehend aus2) 40-75% by weight of a cement mixture consisting of
(Gew.-Teile):(Parts by weight):
40 - 70 Teile Tonerdeschmelzzement 3-20 Teile Portlandzement 3 - 30 Teile Stuckgips (Halbhydrat)40 - 70 parts high-alumina cement 3 - 20 parts Portland cement 3 - 30 parts stucco plaster (hemihydrate)
und/oder Mischung aus Calciurn-Hydro-and / or mixture of Calciurn-Hydro-
xid und Aluminiumsulfat im Gewichts-oxide and aluminum sulfate by weight
verhältnis 2 : 3 sowie gewünschtenfalls bis zu 40 Teile Zuschlagsstoffe undratio 2: 3 and if desired up to 40 parts of aggregates and
bis zu 10 Teile weitere Hilfsstoffe.up to 10 parts of other auxiliaries.
BAD ORIGINALBATH ORIGINAL
Patentanmeldung ü fiogi HENKELKGaAPatent application ü fi o gi HENKELKGaA
ZR-FE/PatenteZR-FE / patents
Die Erfindung geht von der literaturbekannten Tatsache aus, daß bei Einhaltung eines Molverhältnisses TricalciumaluKiinat zu Calciumsulfat", wie 3 : 1 Zementmischungen herstellbar sind, die beim Erhärten das Anmachwasser chemisch binden. Derartige Sementmischungen sind jedoch als solche noch nicht für Verklebungszwecke geeignet. Die Erfindung schlägt demzufolge vor, eine wasserbindende Zementmasse mit einer wäßrigen Kunststoffdispersion zu einem Klebstoff zu vermischen, wobei die wäßrige Phase der Dispersion als Anmachwasser für die Zementmasse dient und die organische Phase entscheidend die Klebkraft bestimmt. Der erfindungsgemäße Baukleber ist ein 2-Komponenten-Produkt, d.h. Kunststoffdispersion und Zementmischung werden erst kurz vor der Anwendung zu den gebrauchsfertigen Bauklebern vermischt.The invention is based on the fact, known from the literature, that if a molar ratio of tricalcium aluminum to calcium sulfate is maintained , such as 3 : 1, cement mixtures can be produced which chemically bind the mixing water when it hardens. However, such cement mixtures as such are not yet suitable for bonding purposes. The invention proposes Accordingly, before mixing a water-binding cement mass with an aqueous plastic dispersion to form an adhesive, the aqueous phase of the dispersion serving as mixing water for the cement mass and the organic phase decisively determining the bond strength. The construction adhesive according to the invention is a 2-component product, ie plastic dispersion and cement mix are mixed into the ready-to-use construction adhesives shortly before use.
Die erfindungsgemäßen Baukleber enthalten als Kunststoffdispersion wäßrige Dispersionen von Kunststoffen (Polymeren) . Dabei ist das Polymere so zu wählen, daß seine Glastemperatur unterhalb von O0C liegt oder daß es durch Zusatz von Weichmacher bei Temperaturen bis zu O0C nicht spröde ist. Bezüglich der Glastemperatur von Polymeren sei verwiesen auf J. Brandrup, E.H. Immergut, Polymer-Handbook, 2. Auflage, Johri Wiley, New York, 1975, III 139 ff. Erfindungsgemäß geeignet sind insbesondere Polymerdispersionen auf Basis vonThe construction adhesives according to the invention contain aqueous dispersions of plastics (polymers) as plastics dispersions. The polymer should be chosen so that its glass transition temperature is below 0 ° C. or that it is not brittle at temperatures up to 0 ° C. due to the addition of plasticizers. With regard to the glass transition temperature of polymers, reference is made to J. Brandrup, EH Immergut, Polymer-Handbook, 2nd edition, Johri Wiley, New York, 1975, III 139 ff. Particularly suitable according to the invention are polymer dispersions based on
1. Polyvinylacetat1. Polyvinyl acetate
2. Polyacrylat2. polyacrylate
3. Polyacrylat-co-styrol.3. polyacrylate-co-styrene.
Unter Polyvinylacetat-Dispersionen werden hier Dispersionen auf Basis von Homo- und Copolymeren des Vinylacetats verstanden. Derartige Dispersionen enthalten dasPolyvinyl acetate dispersions are used here as dispersions based on homo- and copolymers of vinyl acetate Understood. Such dispersions contain the
BAD ORIGINALBATH ORIGINAL
Sd230/438539 4 04.83 "««>\./-U_Sd230 / 438539 4 04.83 "« «> \ ./- U_
Patentanmeldung - n (-nQ1 HENKELKGaAPatent application - n (-n Q1 HENKELKGaA
0689106891
ZR-FE/PatenteZR-FE / patents
Polymere in Gewichtsmengen zwischen 25 und 60 %, vorzugsweise zwischen 40 und 60 bzw. 50 und 60 Gew.-%. Sie v/erden durch Emulsionspolymerisation hergestellt und enthalten die üblichen Hilfsstoffe wie Emulgatoren und/oder Schutzkolloide. Im einzelnen gilt hier das allgemeine Fachwissen über Emulsionspolymerisation. Geeignete Copolymere des Vinylacetats sind die Copolymeren mit Ethylen, mit Vinylether - insbesondere mit Alkylvinylethern, die einen Alkylrest mit einen bis zu 20 C-Atomen aufweisen - weiterhin mit Vinylestern von Co bis C-Q-Carbonsäuren, insbesondere Vinylester verzweigter Säuren, wie z.B. Versatic-Säure (C. ..-Carbonsäur e-Vinylester) sowie mit ungesättigten Carbonsäuren, wie z.B. Crotonsäure. Dabei werden unter Copolymeren des Vinylacetats auch solche verstanden, die außer Vinylacetat noch mehr als ein zusätzliches Monomeres enthalten. Weitere geeignete Copolymere des Vinylacetats sind die durch Teilverseifung von Polyvinylacetat entstandenen Copolymeren mit Vinylalkohol. Derartige Produkte sind jedoch nur insoweit von Bedeutung, wie sie nicht wasserlöslich sind und daher in Dispersion vorliegen können.Polymers in amounts by weight between 25 and 60%, preferably between 40 and 60 or 50 and 60% by weight. They are produced by emulsion polymerization and contain the usual auxiliaries such as emulsifiers and / or protective colloids. In particular, the general specialist knowledge of emulsion polymerization applies here. Suitable copolymers of vinyl acetate are the copolymers with ethylene, with vinyl ether - in particular with Alkyl vinyl ethers, which contain an alkyl radical with up to Have 20 carbon atoms - still branched with vinyl esters of C0 to C-Q carboxylic acids, especially vinyl esters Acids, such as Versatic acid (C. .. carboxylic acid e-vinyl ester) as well as with unsaturated carboxylic acids such as crotonic acid. In doing so, copolymers of vinyl acetate also includes those which, in addition to vinyl acetate, are more than an additional monomer contain. Further suitable copolymers of vinyl acetate are those formed by partial saponification of polyvinyl acetate Copolymers with vinyl alcohol. However, such products are only important insofar as they are not water-soluble and can therefore be present in dispersion.
Nach einer weiteren Ausfuhrungsform der Erfindung sind Baukleber geeignet, die Polyacrylat-Dispersionen enthalten. Geeignet sind Dispersionen auf Basis von Polymeren, esternde Acrylsäure und/oder der Methacrylsäure. Geeignet sind Acrylester linearer oder verzweigter Alkohole mit einem bis zu 10 C-Atomen, so z.B. Methylacrylat, Ethylacrylat, Propylacrylat, Isopropylacrylat, ßutylacrylat und 2-Ethyl-Hexyl-Acrylat. Weiterhin geeignet sind Ester der Methacrylsäure mit Alkoholen, die mehr als 4 C-Atome aufweisen, z.B. Butylmethacrylat und 2-Ethyl-hexylacrylat. Ester der Methacrylsäure mit einemAccording to a further embodiment of the invention are Suitable for construction adhesives that contain polyacrylate dispersions. Dispersions based on polymers, esterifying acrylic acid and / or methacrylic acid are suitable. Acrylic esters of linear or branched alcohols with up to 10 carbon atoms are suitable, e.g. methyl acrylate, Ethyl acrylate, propyl acrylate, isopropyl acrylate, butyl acrylate and 2-ethyl hexyl acrylate. Still suitable are esters of methacrylic acid with alcohols that have more than 4 carbon atoms, e.g. butyl methacrylate and 2-ethyl hexyl acrylate. Ester of methacrylic acid with a
BAD ORIGINALBATH ORIGINAL
Patentanmeldung D 5391 HENKELKGaAPatent application D 5391 HENKELKGaA
ZR-FE/PatenteZR-FE / patents
-f.-f.
bis zu 3 C-Atomen, wie Methylmethacrylat oder Ethylmethacrylat sind nur als Coiaonomere mit einem Anteil bis zu 50 Gew.-% geeignet, da ansonsten Polymere mit zu geringer Flexibilität entstehen. Im einzelnen gilt hier das Fachwissen der Polymer-Chemie. Die den Acrylatdispersionen zugrunde liegenden Polymeren können auch noch weitere Comonomere enthalten, so z.B. Methacrylsäure oder Acrylsäure wie auch 2-Hydroxyethylacrylat.up to 3 carbon atoms, such as methyl methacrylate or ethyl methacrylate, are only available as coiaonomers with a proportion of up to 50% by weight suitable, as otherwise polymers with insufficient flexibility are formed. In detail applies here the expertise of polymer chemistry. The polymers on which the acrylate dispersions are based can also contain other comonomers, such as methacrylic acid or acrylic acid as well as 2-hydroxyethyl acrylate.
Weiterhin geeignet sind Polyacrylat-co-styrol-dispersionen. Es sind dies Dispersionen von Copolymeren der vorgenannten Acrylatmonomeren mit Styrol, wobei der Styrolanteil 10-60 Gew.-% des Copolymeren ausmacht. Die Styrolacrylat-Dispersionen können ebenfalls saure Comonomere wie Acrylsäure oder Methacrylsäure enthalten. Polyacrylate-co-styrene dispersions are also suitable. These are dispersions of copolymers of the aforementioned acrylate monomers with styrene, the Styrene content makes up 10-60% by weight of the copolymer. The styrene acrylate dispersions can also be acidic Contain comonomers such as acrylic acid or methacrylic acid.
Polyacrylat-Dispersionen und Polyacrylat-co-styrol-'Dispersionen enthalten weiterhin die bei den Polyvinylacetat-Dispersionen genannten Hilfsstoffe, nämlich Emulgatoren und Schutzkolloide. Bevorzugte Emulgatoren sind anionische Emulgatoren.Polyacrylate dispersions and polyacrylate-co-styrene dispersions also contain the auxiliaries mentioned for the polyvinyl acetate dispersions, namely Emulsifiers and protective colloids. Preferred emulsifiers are anionic emulsifiers.
Die in den erfindungsgemäßen Bauklebern verwendeten Dispersionen haben einen Feststoffgehalt zwischen 40 und 60 Gew.-%. Weiterhin können sie bis zu 15 Gew.-% übliche Hilfsstoffe wie z.B. Weichmacher und EntschäuThose used in the construction adhesives of the invention Dispersions have a solids content between 40 and 60% by weight. Furthermore, they can contain up to 15% by weight Usual auxiliaries such as plasticizers and defoaming agents mer sowie Netzmittel und/oder Konservierungsmittel ent halten. Als Weichmacher sind Ester schwerflüchtiger Flüssigkeiten geeignet, z.B. die Ester von aromatischen Dicarbonsäuren wie Phthalsäure, mit Alkoholen mit 6 und mehr C-Atomen, andererseits Ester aliphatischer Dimer as well as wetting agents and / or preservatives ent keep. Esters of low-volatility liquids are suitable as plasticizers, e.g. the esters of aromatic ones Dicarboxylic acids such as phthalic acid, with alcohols with 6 or more carbon atoms, on the other hand esters of aliphatic di carbonsäuren wie Sebacinsäure-, Adipinsäure- oder Azelain-carboxylic acids such as sebacic acid, adipic acid or azelaic acid
BAD ORIGINALBATH ORIGINAL
Sd 230/438539 4.04 83Sd 230/438539 4.04 83
Patentanmeldung D 6891 HENKELKGaAPatent application D 6891 HENKELKGaA
ZR-FE/PatenteZR-FE / patents
-y-t-y-t
säureester. Als Entschäumer können beispielsweise die Umsetzungsprodukte von langkettigen Alkoholen, insbesondere C1 vC O-Alkoholen mit bis zu 3 mol Ethylenoxid oder Propylenoxid verwendet werden.acid ester. The reaction products of long-chain alcohols, in particular C 1 vC O alcohols with up to 3 mol of ethylene oxide or propylene oxide, for example, can be used as defoamers.
Die dem erfindungsgemäßen Baukleber zugrunde liegende Zementmischung besteht aus:The cement mixture on which the construction adhesive according to the invention is based consists of:
40 - 80 Teilen Tonerdeschmelzzement 3-20 Teilen Portlandzement40-80 parts high-alumina cement 3-20 parts Portland cement
3-30 Teilen Stuckgips und/oder einer Mischung aus Calciumhydroxid und Aluminiumsulfat im3-30 parts of plaster of paris and / or a mixture of calcium hydroxide and aluminum sulfate im
Gewichtsverhältnis 2 : 3 und gewünschtenfalls weiteren Zuschlags- und Hilfsstoffen.Weight ratio 2: 3 and, if desired, other additives and auxiliaries.
Bevorzugt ist die Verwendung von Zementmischungen aus:The use of cement mixtures consisting of:
50 - 70 Teilen Tonerdeschmelzzement 5-15 Teilen Portlandzement und 20-25 Teilen Stuckgips sowie gewünschtenfalls bis zu 20 Teilen Zuschlagsstoffen und bis zu 10 Teilen weiteren Hilfsstoffen.50-70 parts high-alumina cement 5-15 parts Portland cement and 20-25 parts of plaster of paris and, if desired, up to 20 parts of aggregates and up to 10 parts of other auxiliary materials.
Nach einer weiteren Ausfuhrungsform der Erfindung ist es bevorzugt, die Baukleber auf Basis von Zementmischungen herzustellen, die die folgende Zusammensetzung aufweisen:According to a further embodiment of the invention is it is preferable to produce the construction adhesives on the basis of cement mixes that have the following composition exhibit:
50 - 70 Teilen Tonerdeschmelzzement 5-15 Teilen Portlandzement sowie 2-15 Teilen, insbesondere50-70 parts high-alumina cement 5-15 parts Portland cement as well 2-15 parts, in particular
33335353333535
Patentanmeldung q 6891 HENKELKGaAPatent application q 6891 HENKELKGaA
ZR-FE/PatenteZR-FE / patents
3-10 Teilen einer Mischung aus Calciumhydroxid und Aluminiumsulfat im Gewichtsverhältnis 2 : 3 und gewünschtenfalls weitere Hilfsstoffe und/oder Zuschlagsstoffen.3-10 parts of a mixture of calcium hydroxide and aluminum sulfate in a weight ratio 2: 3 and, if desired, other auxiliaries and / or aggregates.
Dabei ist es bevorzugt, in den Zementmischungen ein Verhältnis Tonerdeschmelzzement : Portlandzement zwischen 5 : 1 und 15:1 einzustellen. Weiterhin ist es bevorzugt, das Verhältnis Zement : Gips zwischen 2,5 : 1 und 3,5 : 1 zu halten. Wenn nicht gleichzeitig die Mischung aus Calciumhydroxid und Aluminiumsulfat verwendet wird. Im Falle der alleinigen Verwendung der Mischung aus Calciumhydroxid und Aluminiumsulfat (2:3 Gewichtsteile) ist bevorzugt, diese in Mengen von 1:6 bis 1 : 20, vorzugsweise 1:8 bis 1 : 10, bezogen auf Gesamtzement, einzusetzen.It is preferred in the cement mixes to have a ratio of high-alumina cement: Portland cement between 5: 1 and 15: 1 to be set. Furthermore, it is preferred that the ratio of cement: plaster of paris is between 2.5: 1 and 3.5: 1 to hold. If the mixture of calcium hydroxide and aluminum sulphate is not used at the same time. In the case of the sole use of the mixture of calcium hydroxide and aluminum sulfate (2: 3 parts by weight) it is preferred to use this in amounts of 1: 6 to 1:20, preferably 1: 8 to 1:10, based on total cement.
Die erfindungsgemäßen Baukleber können weiterhin als Bestandteil der Zementmischung übliche Zuschlagsstoffe enthalten. Geeignete Zuschlagsstoffe sind beispielsweise Quarzmehl, Quarzsand, Kalksteinmehl, Leichtspat oder Tonmehl oder dergleichen.The construction adhesives according to the invention can also be used as a component of the cement mixture contain. Suitable additives are, for example, quartz powder, quartz sand, limestone powder, light spar or powdered clay or the like.
Weiterhin können die Baukleber als Bestandteil der Zementmischung auch weitere in vergüteten Zementklebern übliche Hilfsstoffe enthalten. So können z.B. Verzögerer zugegen sein. Geeignete Verzögerer sind komplexierende Carbonsäuren wie z.B. Zitronensäure oder Weinsäure. Weiterhin können Klebkraftverbesserer mitverwendet werden. Ein geeigneter Klebkraftverbesserer ist Polyvinylacetat-Dispersionspulver. Weiterhin sindFurthermore, the construction adhesives can also be used as part of the cement mix in modified cement adhesives Contain the usual auxiliaries. For example, retarders can be present. Suitable retarders are complexing carboxylic acids such as citric acid or tartaric acid. Bond strength improvers can also be used can also be used. A suitable bond strength improver is polyvinyl acetate dispersion powder. Furthermore are
Sd 23O/438S39 4. 04 83Sd 23O / 438S39 04/04 83
ORIGINALORIGINAL
Patentanmeldung D 6891 HENKELKGaAPatent application D 6891 HENKELKGaA
ZR-FE/PatenteZR-FE / patents
- 44. - 44.
auch verschiedene Harzsorten geeignete Klebkraftverbesserer. In den Zementmischungen können weiterhin Mittel zur Verbesserung des-Wasserrückhaltevermögens mitverwendet werden. Derartige Mittel sind z.B. Celluloseether mit Säuregruppen wie z.B. Carboxymethylcellulose oder auch nichtionische Celluloseether wie Hydroxyethyl-oder Methylcellulose. Auch Glättungsmittel wie Casein oder dergleichen können in Zementmischungen miteingesetzt werden. Weitere Hilfsstoffe, die mitverwendet werden können, sind Verdickungsmittel. Geeignete Verdickungsmittel sind Polysaccharide wie beispielsweise Xanthan oder Guar, sowie verschiedene Celluloseether. Eingesetzt werden können aber auch wasserlösliche synthetische Polymere wie Polyacrylamid oder Copolymere aus Acrylsäure bzw. Methacrylsäure und Acrylestern wie Acrylacrylat. Besonders geeignete Fertigungsmittel sind teilweise vernetzte Polyacrylsäuren. Als weitere Hilfsstoffe können den Zementmischungen Pigmentdispergatoren zugegeben werden. Hier sind beispielsweise verseifte Copolymere aus Styrol und Maleinsäureanhydrid, kurzkettige Copolymere aus Acrylestern, Styrol und Acrylsäure oder Methacrylsäure, Copolymere auf Basis Vinylalkohol, Vinylether sowie die üblicherweise bei der Pigmentierung von Wasserlacken verwendeten Dispergiermittel geeignet. Schließlich können die Zementmassen Konservierungsmittel enthalten. Die Konservierungsmittel dienen zur Verhinderung des oxidativen photochemischen oder bakteriellen Abbaus der organischen Komponenten. Geeignet sind hier Radikalfänger, z.B. mehrkernige Phenole sowie übliche Mikrobicide.also different types of resin suitable bond strength improvers. In the cement mixes can continue Agents for improving the water retention capacity can also be used. Such agents are, for example, cellulose ethers with acid groups such as carboxymethyl cellulose or also nonionic cellulose ethers such as hydroxyethyl or methyl cellulose. Also smoothing agents such as casein or the like can also be used in cement mixes. Other auxiliary materials that are also used are thickeners. Suitable thickeners are polysaccharides such as Xanthan or guar, as well as various cellulose ethers. However, water-soluble ones can also be used synthetic polymers such as polyacrylamide or copolymers of acrylic acid or methacrylic acid and Acrylic esters such as acrylic acrylate. Particularly suitable means of production are partially crosslinked polyacrylic acids. Pigment dispersants can be added to the cement mixes as further auxiliaries. Here are for example saponified copolymers of styrene and maleic anhydride, short-chain copolymers of acrylic esters, Styrene and acrylic acid or methacrylic acid, copolymers based on vinyl alcohol, vinyl ethers and the usual Suitable dispersants used in the pigmentation of water-based paints. After all, they can Cement compounds contain preservatives. The preservatives serve to prevent the oxidative photochemical or bacterial degradation of the organic components. Radical scavengers are suitable here, e.g. polynuclear phenols and common microbicides.
Patentanmeldung Q ggq-j HENKELKGaAPatent application Q ggq-j HENKELKGaA
ZR-FE/PatenteZR-FE / patents
- Al'- Al '
Das Verhältnis der Kunststoffdispersion zu der Zementmischung in den erfindungsgemäßen Bauklebern liegt zwischen 25 und 60 Gew.-% Dispersion, zu 40 - 75 Gew.-% Zementmasse. Es richtet sich in erster Linie nach dem Wassergehalt der Dispersion und läßt sich über Veränderungen des Wassergehalts einerseits sowie über die Menge der Zuschlagsstoffe innerhalb der Zementmischung andererseits steuern. Aus Gründen der Arbeitsvereinfachung wird der Fachmann den erfindungsgemäßen Baukleber so einstellen, daß bei Vermischen gleicher Volumenteile Dispersion und Pulver die günstigsten Ergebnisse zu erzielen sind. Dazu ist im allgemeinen bei Dispersionen mit etwa 50 Gew.-% Wasseranteil die Verwendung von Zementmassen mit 5-30 Gew.-% Zuschlagsstoffen nötig.The ratio of the plastic dispersion to the cement mixture in the construction adhesives according to the invention there is between 25 and 60% by weight dispersion, 40-75% by weight Cement paste. It depends primarily on the water content of the dispersion and can be changed via changes the water content on the one hand and the amount of aggregates within the cement mixture on the other hand control. In order to simplify the work, the person skilled in the art will use the construction adhesive according to the invention Adjust so that the best results are obtained when mixing equal parts by volume of dispersion and powder are to be achieved. For this purpose, it is generally used for dispersions with a water content of about 50% by weight of cement masses with 5-30% by weight of aggregates necessary.
Zur Herstellung des erfindungsgemäßen Bauklebers aus der 2-komponentigen Lagerform werden Zementmischung und Dispersion miteinander verrührt. Dazu ist es bevorzugt, die Zementmischung in die Dispersion einzurühren. Das Mischungsverhältnis, in Volumenteilen, beträgt dabei etwa 1:1, Bei dem Verrühren entsteht eine viskose Klebstoffmasse üblicher Konsistenz, die mit Mitteln, wie sie im Bauhandwerk üblich und dem Bodenverleger vertraut sind, verarbeitet werden kann.Cement mixes are used to produce the construction adhesive according to the invention from the 2-component storage form and dispersion stirred together. For this purpose, it is preferred to stir the cement mixture into the dispersion. The mixing ratio, in parts by volume, is about 1: 1, when the mixture is stirred a viscous adhesive mass of usual consistency, which with means, as they are common in the building trade and the Floor installers are familiar, can be processed.
So können die Klebstoffe beispielsweise mit gezahnten Spachteln aufgetragen werden.For example, the adhesives can be applied with serrated spatulas.
Die erfindungsgemäßen Baukleber härten ohne Stoffaustausch mit der Umgebung, d.h. es ist weder das Verdunsten von Wasser noch das Eindiffundieren von bei-The construction adhesives according to the invention cure without material exchange with the environment, i.e. there is neither evaporation of water nor the diffusion of two
SAO ORIGINALSAO ORIGINAL
AH93O/43H539 4.04.83AH93O / 43H539 4.04.83
Patentanmeldung D 6891 HENKELKGaAPatent application D 6891 HENKELKGaA
ZR-FE/PatenteZR-FE / patents
<- AS.<- AS.
spielsweise CO2 aus der luft nötig. Sie eignen sich daher hervorragend zur Verklebung undurchlässiger Substrate auf undurchlässige Untergründe. So können z.B. alte PVC- oder Linoleum-Böden mit PVC oder Linoleum oder anderen dichten Belägen überklebt werden. Auch das überkleben keramischer Fliesen mit PVC oder neuen Fliesen ist möglich. Besonders geeignet sind die Klebstoffe zur Verarbeitung von sogenannten CV-Belägen (Cushioned Vinyls)von Flexplatten oder auch von Poly-Ίο styrolschaumstoffen.For example, CO 2 from the air is necessary. They are therefore ideal for bonding impermeable substrates to impermeable substrates. For example, old PVC or linoleum floors can be pasted over with PVC or linoleum or other dense coverings. Gluing over ceramic tiles with PVC or new tiles is also possible. The adhesives are particularly suitable for processing so-called CV coverings (cushioned vinyls) from flex plates or from poly-styrene foams.
Patentanmeldung D 6891 HENKELKGaAPatent application D 6891 HENKELKGaA
ZR-FE/PatenteZR-FE / patents
a) Zementmischung:a) cement mix:
67,2 Gew.-Teile Tonerdeschmelzzement (Fondu-Lafarge)67.2 parts by weight of high-alumina cement (Fondu-Lafarge)
7,5 Gew.-Teile Portlandzement (PZ 35)7.5 parts by weight Portland cement (PZ 35)
25 Gew.-Teile Stuckgips (Halbhydrat)25 parts by weight stucco (hemihydrate)
0,3 Gew.-Teile Methylcellulosepulver (Culminal ,0.3 part by weight of methyl cellulose powder (Culminal,
15000 PFR)15000 PFR)
b) Dispersion:b) dispersion:
93,9 Gew.-Teile Polystyrol-co-acrylat-dispersion93.9 parts by weight of polystyrene-co-acrylate dispersion
(AcronaliR), S 400, BASF AG.)(Acronal iR) , S 400, BASF AG.)
0,5 Gew.-Teile Natriummetaphosphat 33 %ige wäßrige Lösung
0,3 Gew.-Teile eines üblichen Entschäumers (z.B.0.5 part by weight of sodium metaphosphate, 33% strength aqueous solution
0.3 part by weight of a conventional defoamer (e.g.
DehydraniR)F, Henkel) 0,3 Gew.-Teile Konservierungsmittel(z.B. ProxelDehydran iR) F, Henkel) 0.3 parts by weight preservative (e.g. Proxel
AB, ICI)AB, ICI)
5,0 Gew.-Teile Wasser5.0 parts by weight of water
Zementmischung a) und Dispersion b) wurden im Gewichtsverhältnis 1:1 vermischt. Es entstand ein Klebstoff mit den folgenden Eigenschaften:Cement mixture a) and dispersion b) were in weight ratio Mixed 1: 1. The result was an adhesive with the following properties:
Tropfzeit: 40'Drop Time: 40 '
Viskosität: Haake Viskosimeter Drehkörper E 500/IV 55 SktViscosity: Haake viscometer rotating body E 500 / IV 55 Skt
Schälfestigkeit: nach DIN 53278
Lagerung: 14 Tage 20°C 10,2 N/cmPeel strength: according to DIN 53278
Storage: 14 days at 20 ° C 10.2 N / cm
7 Tage 20°C+7 days 20 ° C +
5 Tage 500C+ 16,0 N/cm 2 Tage 20°C5 days 50 0 C + 16.0 N / cm 2 days 20 ° C
Sd 230/438539 4.04 83Sd 230/438539 4.04 83
Patentanmeldung D ßQ91 HENKELKGaAPatent application D ßQ91 HENKELKGaA
ZR-FE/Patente - 12/- *'' ZR-FE / Patents - 12 / - * ''
Schälfestigkeit: mit Federwaage an verklebten PVC-Be-Peel strength: with spring balance on glued PVC
lägen auf alten PVOBelägen: über 10 N/crawould be on old PVO coverings: over 10 N / cra
a) Zementmischung:a) cement mix:
87,4 Gew.~Teile Tonerdeschmelzzement (Fondu-Lafarge) 7,5 Gew.-Teile Portlandzement (PZ 35)87.4 parts by weight of high-alumina cement (Fondu-Lafarge) 7.5 parts by weight Portland cement (PZ 35)
2 Gew.-Teile Calciumhydroxid2 parts by weight calcium hydroxide
3 Gew.-Teile Aluminiumsulfat (18 H0O)3 parts by weight of aluminum sulfate (18 H 0 O)
(R) -0,1 Gew.-Teile Methylcellulosepulver (Culminal(R) -0.1 parts by weight methyl cellulose powder (Culminal
15000 PFR)15000 PFR)
b) Dispersion:b) dispersion:
93,9 Gew.-Teile Polystyrol-co-acrylat-dispersion93.9 parts by weight of polystyrene-co-acrylate dispersion
(Acronal1 , S 400, BASF AG.)
o,5 Gew.-Teile Natriummetaphosphat 33 %ige wäßrige Lösung
0,3 Gew.-Teile eines üblichen Entschäumers (z.B.(Acronal 1 , S 400, BASF AG.) 0.5 parts by weight of sodium metaphosphate, 33% strength aqueous solution
0.3 part by weight of a conventional defoamer (e.g.
Dehydran(R*F, Henkel)Dehydran (R * F, handle)
(R) 0,3 Gew.-Teile Konservierungsmittel (z.B. Proxel AB, XCI)(R) 0.3 parts by weight preservative (e.g. Proxel AB, XCI)
5,0 Gew.-Teile Wasser5.0 parts by weight of water
Zementmischung a) und Dispersion b) wurden wie bei Beispiel 1 vermischt. Es entstand ein Klebstoff mit den folgenden Eigenschaften:Cement mixture a) and dispersion b) were mixed as in Example 1. An adhesive was created with the following properties:
Tropfzeit: 40'Drop Time: 40 '
Viskosität: Haake Viskosimeter Drehkörper E 500/IV 95 Skt
Schälfestigkeit: nach DIN 53278
Lagerung: 14 Tage 20°C > 5 N/cm 7 Tage 20°C+Viscosity: Haake viscometer rotating body E 500 / IV 95 Skt Peel strength: according to DIN 53278
Storage: 14 days 20 ° C> 5 N / cm 7 days 20 ° C +
Patentanmeldung D gQ91 HENKELKGaAPatent application D gQ91 HENKELKGaA
ZR-FE/PatenteZR-FE / patents
Lagerung: 5 Tage 500C+ > 5 N/cmStorage: 5 days at 50 ° C. +> 5 N / cm
2 Tage 20°C * .2 days 20 ° C *.
Vergleich: Verklebung mit handelsüblichen PVC· KlebstoffComparison: Bonding with commercially available PVC adhesive
Lagerung: 14 Tage 20°C 10-20 N/cmStorage: 14 days at 20 ° C 10-20 N / cm
7 Tage 20°C+7 days 20 ° C +
5 Tage 50°C+ 10-20 N/cm5 days 50 ° C + 10-20 N / cm
2 Tage 20°C2 days 20 ° C
BAD ORfGSMALBAD ORfGSMAL
Sd 230/438539 4.04 63Sd 230/438539 4.04 63
Claims (10)