DE3136678A1 - Reduction of the electrostatic charge of sheet-like textile structures - Google Patents
Reduction of the electrostatic charge of sheet-like textile structuresInfo
- Publication number
- DE3136678A1 DE3136678A1 DE19813136678 DE3136678A DE3136678A1 DE 3136678 A1 DE3136678 A1 DE 3136678A1 DE 19813136678 DE19813136678 DE 19813136678 DE 3136678 A DE3136678 A DE 3136678A DE 3136678 A1 DE3136678 A1 DE 3136678A1
- Authority
- DE
- Germany
- Prior art keywords
- fabric
- textile
- sheet
- polyacrylonitrile
- charge
- Prior art date
- Legal status (The legal status is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the status listed.)
- Withdrawn
Abstract
Description
Verminderung der elektrostatischen Aufladung von textilenReduction of the electrostatic charge on textiles
Flächengebilden Bei der Benutzung von textilen Flächengebilden aus synthetischen Faserstoffen, beispielsweise Teppichböden oder Automobilsitzen, ergeben sich elektrostatische Personenaufladungen, die sich beim Berühren von Metall durch die betreffende Person in unangenehmer Weise entladen.Flat structures When using textile flat structures synthetic fibers, for example carpets or automobile seats electrostatic charges, which result from touching metal uncomfortably discharge the person concerned.
Es wurde gefunden, daß sich diese Aufladung so weit vermindern läßt, daß die Entladung nicht mehr spürbar ist, wenn man dem textilen Flächengebilde ein geerdetes, metallisiertes Polgewebe unterlegt.It has been found that this charge can be reduced to such an extent that that the discharge is no longer noticeable when you enter the textile fabric grounded, metallized pile fabric underneath.
Als Polwaren kommen z.B. Samt, Velours oder Plüsche in Betracht, die z.B. aus Polyamid oder Polyacrylnitril bestehen und beispielsweise nach DE-PS 2 743 768 metallisiert, insbesondere vernickelt sind. Die metallisierte Polware hat vorzugsweise die gleichen Maße in Länge und Breite wie das zu unterlegende textile Flächengebilde.Velvet, velor or plush, for example, come into consideration as pile goods e.g. consist of polyamide or polyacrylonitrile and for example according to DE-PS 2 743 768 are metallized, in particular nickel-plated. The metallized pile ware has preferably the same dimensions in length and width as the textile to be underlaid Fabrics.
De Verminderung der elektrostatischen Aufladung wurde mit der in Fig. 1 gezeigten Versuchsanordnung in folgender Weise bestimmt.The electrostatic charge was reduced with the method shown in Fig. 1 is determined in the following manner.
Ein im Automobilbereich gebräuchlicher Schaumstoffsitz (1) wurde auf einem Metailsockel (2) aufgebracht. Je nach Messung wurde einmal nur der Bezugstoff auf dem Schaumstoffsitz mit dem entsprechenden Reibungspartner Polyamid- oder Polyacrylnitrilgewebe (3) gerieben, das andere Mal wurde unter den Bezugstoff (4) ein geerdetes vernickeltes Polgewebe (5) gelegt. Dann wurde ein Ladungsmeßgerät (6) an der Reibelektrode (7) angeschlossen Die aus Aluminium (Durchmesser 170 mm, Gewicht 5 kg) hergestellte Elektrode wurde mit dem Reibungspartner Polyamid- bzw. Polyacrylnitrilgewebe überzogen.A foam seat (1) commonly used in the automotive sector was placed on applied to a metal base (2). Depending on the measurement, only the cover fabric was used once on the foam seat with the corresponding friction partner polyamide or polyacrylonitrile fabric (3) rubbed, the other time a grounded nickel-plated one was under the cover fabric (4) Pile fabric (5) laid. Then a charge meter (6) was attached to the friction electrode (7) connected The one made of aluminum (diameter 170 mm, weight 5 kg) The electrode was coated with the friction partner polyamide or polyacrylonitrile fabric.
Die beiden Gewebequalitäten stehen am positiven (Polyamid) bzw. am negativen (Polyacrylnitril) Ende der triboelektrischen Spannungsreihe.The two fabric qualities are on the positive (polyamide) and on the negative (polyacrylonitrile) end of the triboelectric series.
Die Reibelektrode wurde mit einem isolierten Griff von Hand über die Sitzfläche gezogen und abgehoben. Das Meßgerät zeigt dabei die entstandene Ladung an. Diese Ladungswerte wurden nach der Beziehung Q = C U U und unter Benutzung des Wertes für die mittlere Kapazität eines Menschen (C = 10 1ob) auf Spannungswerte umgerechnet auf die eine Person von einem solchen Sitz aufgeladen wird.The friction electrode was hand over the with an insulated handle Seat pulled and lifted. The measuring device shows the resulting charge at. These charge values were calculated according to the relationship Q = C U U and using the Value for the average capacity of a person (C = 10 1ob) on voltage values converted to which a person is charged from such a seat.
Bei Verwendung metallisierter textiler Polgewebe kann die elektrostatische Personenauf ladung etwa halbiert, d.h. auf Werte unter etwa 3000 Volt, vorzugsweise 2000 Volt und kleiner gesenkt werden. Eine Entladung durch Berühren von Metall ist bei diesen Werten nicht mehr spürbar.When using metallized textile pile fabric, the electrostatic Personal charge about halved, i.e. to values below about 3000 volts, preferably 2000 volts and less can be lowered. A discharge from touching metal is no longer noticeable at these values.
Das metallisierte textile Polgewebe kann gleichzeitig ohne Verlust des vorstehend genannten Effektes durch Anlegen einer Spannung (Gleich- oder Wechselstrom) zu Heizzwecken verwendet werden.The metallized textile pile fabric can be used at the same time without loss the above-mentioned effect by applying a voltage (direct or alternating current) used for heating purposes.
Anstelle der Kombination textiles Flächengebilde / unterlegte geerdete metallisierte Polware kann mit ähnlichem Erfolg auch ein nur rückseitig metallisiertes geerdetes Flächengebilde als Bezugstoff für einen Autositz verwendet werden. Die nur rückseitige Metallisierung erfolgt nach DE-OS 29 10 460.Instead of the combination of textile fabric / underlaid grounded Metallized pile goods can also be metallized only on the back with similar success Grounded fabric can be used as a cover fabric for a car seat. the only the rear side is metallized according to DE-OS 29 10 460.
Beispiel 1 Ein Polyester-Baumwoll-Spinnfasergewebe mit einem Ober-12 flächenwiderstand ROA von ca. 10 OHM gemäß DIN 54345 wurde auf einen Polyurethanschaumstoff gemäß Fig. 1 gelegt und mit einem auf der Reibelektrode aufgespannten Polyacrylnitrilgewebe gerieben. Eine Personenaufladung von 6000 Volt wurde erhalten Unter das Polyester-Baumwoll-Spinnfasergewebe wurde anschließend ein vernickelter, geerdeter Velours gelegt und die Reibung wiederholt. Der Velours (Kettwirkware) bestand aus einem Grundfaden von Polyamid-6, 78 dtex f 17 x 2. Der Polfaden bestand aus einer Polyacrylnitrilspinnfaser, glänzend, Nm 36/1. Die Polhöhe des Velours war 2 mm. Die Nickelaufnahme des Velours betrug 50,3 g/m².Example 1 A polyester-cotton staple fabric with a top 12 Surface resistance ROA of approx. 10 OHM according to DIN 54345 was applied to a polyurethane foam placed according to FIG. 1 and with a polyacrylonitrile fabric stretched on the friction electrode rubbed. A 6000 volt personal charge was obtained under the polyester-cotton staple web a nickel-plated, earthed velor was then placed and the rubbing repeated. The velor (warp knitted fabric) consisted of a base thread of polyamide-6, 78 dtex f 17 x 2. The pile thread consisted of a polyacrylonitrile staple fiber, glossy, Nm 36/1. The pile height of the velor was 2 mm. The nickel uptake of the velor was 50.3 g / m².
Der Widerstand pro Quadrat, gemessen auf der glatten Rückseite, lag bei 10 Ohm. Die Personenaufladung sank auf 1800 Volt.The resistance per square, measured on the smooth back, was at 10 ohms. The personal charge dropped to 1,800 volts.
Beispiel 2 Ein Polyester-Baumwoll-Spinnfasergewebe mit einem Oberflächenwiderstand ROA von ca. 10 Ohm gemäß DIN 54345 wurde auf einen Polyurethanschaumstoff gemäß Abb o 1 gelegt und mit einem auf der Reibelektrode aufgespannten Polyamidgewebe gerieben. Eine Personenaufladung von 4000 Volt wurde erhalten.Example 2 A polyester-cotton staple fabric with a surface resistance ROA of approx. 10 ohms according to DIN 54345 was applied to a polyurethane foam according to Fig o 1 and with a polyamide fabric stretched on the friction electrode rubbed. A 4000 volt personal charge was obtained.
Unter das Polyester-Baumwoll-Spinnfasergewebe wurde anschließend ein vernickelter, geerdeter Velours gelegt und die Reibung wiederholt. Der Velours (Kettwirkware) bestand aus einem Grundfaden von Polyamid-6, 78 dtex f 17 x 2. Der Polfaden bestand aus einer Polyacrylnitrilspinnfaser, glänzend, Nm 36/1. Die Polhöhe des Verlours war 2 mm. Die Nickelaufnahme des Velours betrug 50,3 g/m2.A was then placed under the polyester-cotton staple fiber fabric nickel-plated, earthed velor laid and the friction repeated. The velor (warp knitted fabric) consisted of a base thread of polyamide-6, 78 dtex f 17 x 2. The pile thread consisted made of a polyacrylonitrile staple fiber, glossy, Nm 36/1. The pole height of the Verlours was 2 mm. The nickel uptake of the velor was 50.3 g / m2.
Der Widerstand pro Quadrat, gemessen auf der glatten Rückseite, lag bei 10 Ohm. Die Personenaufladung sank auf 1700 Volt.The resistance per square, measured on the smooth back, was at 10 ohms. The personal charge dropped to 1700 volts.
Beispiel 3 Ein Polyester-Baumwoll-Spinnfasergewebe mit einem Ober-12 flächenwiderstand ROA von 10 Ohm gemäß DIN 54345 wurde, wie im Beispiel 1 beschrieben, mit einem Polyacrylnitrilgewebe gerieben. Eine Personenauf ladung von 6000 Volt wurde erhalten.Example 3 A polyester-cotton staple fabric with a top 12 Surface resistance ROA of 10 ohms according to DIN 54345 was, as described in Example 1, rubbed with a polyacrylonitrile cloth. A person charge of 6000 volts has been received.
Unter dieses Gewebe wurde ein vernickelter, geerdeter Polyacrylnitrilplüsch gelegt und die Reibung wiederholt.A nickel-plated, grounded polyacrylonitrile plush was placed under this fabric laid and the friction repeated.
Der Plüsch (Webpelz) bestand aus einem Polyacrylnitril-Grundgewebe, der Pol aus Polyacrylnitril-Spinnfasern.The plush (woven fur) consisted of a polyacrylonitrile base fabric, the pile made of polyacrylonitrile staple fibers.
Die Polhöhe war 10 mm. Die Nickelaufnahme des Plüsch betrug 79,8 g/m2. Der Widerstand pro Quadrat, gemessen auf der glatten Rückseite, lag bei 80 Ohm. Die Personenaufladung sank auf 1600 Volt.The pole height was 10 mm. The nickel uptake of the plush was 79.8 g / m2. The resistance per square, measured on the smooth back, was 80 ohms. The personal charge dropped to 1600 volts.
Beispiel 4 Ein Polyester-Baumwoll-Spinnfasergewebe mit einem Oberflächenwiderstand ROA von 1012 Ohm gemäß DIN 54345 wurde, wie im Beispiel 1 beschrieben, mit einem Polyamidgewebe gerieben. Eine Personenaufladung von 4000 Volt wurde erhalten.Example 4 A polyester-cotton staple fabric with a surface resistance ROA of 1012 ohms according to DIN 54345 was, as described in Example 1, with a Rubbed polyamide fabric. A 4000 volt personal charge was obtained.
Unter dieses Gewebe wurde ein vernickelter, geerdeter Polyacrylnitrilplüsch gelegt und die Reibung wiederholt.A nickel-plated, grounded polyacrylonitrile plush was placed under this fabric laid and the friction repeated.
Der Plüsch (Webpelz) bestand aus einem Polyacrylnitril-Grundgewebe, der Pol aus Polyacrylnitril-Spinnfasern.The plush (woven fur) consisted of a polyacrylonitrile base fabric, the pile made of polyacrylonitrile staple fibers.
Die Polhöhe war 10 mm. Die Nickelaufnahme des Plüsch betrug 79,8 g/m2. Der Widerstand pro Quadrat, gemessen auf der glatten Rückseite, lag bei 80 Ohm. Die Personenaufladung sank auf 2000 Volt.The pole height was 10 mm. The nickel uptake of the plush was 79.8 g / m2. The resistance per square, measured on the smooth back, was 80 ohms. The personal charge dropped to 2000 volts.
LeerseiteBlank page
Claims (2)