DE3130868A1 - ADHESIVE COMPOSITION AND SANITARY BANDAGE CONTAINING THIS - Google Patents
ADHESIVE COMPOSITION AND SANITARY BANDAGE CONTAINING THISInfo
- Publication number
- DE3130868A1 DE3130868A1 DE19813130868 DE3130868A DE3130868A1 DE 3130868 A1 DE3130868 A1 DE 3130868A1 DE 19813130868 DE19813130868 DE 19813130868 DE 3130868 A DE3130868 A DE 3130868A DE 3130868 A1 DE3130868 A1 DE 3130868A1
- Authority
- DE
- Germany
- Prior art keywords
- adhesive
- water
- adhesive composition
- sanitary napkin
- copolymers
- Prior art date
- Legal status (The legal status is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the status listed.)
- Withdrawn
Description
Sanitäre BindeSanitary napkin
Beschreibungdescription
Die Erfindung betrifft eine sanitäre Binde, enthaltend eine Klebstoffzusammensetzung, die geeignet ist zur . !,aminierung bzw. Schichtstoff bildung und Verstärkung von porösen Absorbens-Substraten.The invention relates to a sanitary napkin containing an adhesive composition which is suitable for. !, amination or laminate formation and reinforcement of porous absorbent substrates.
In der letzten Zeit erzielte ein neuer Typ von Damenbinden einen großen Handelserfolg. Dieser spezielle Typ von Damenbinden, der als Schlüpfer-Ausfütterung bekannt ist, weist ein begrenztes Aufnahmevermögen auf und wurde bestimmt zur Anwendung für vaginale Ausflüsse zwischen der Menstruation oder zu anderen Zeiten, wenn geringe Menstruationsausflüsse auftreten. Recently, a new type of sanitary napkin has achieved great commercial success. This special one The type of sanitary napkin known as panty liners has a limited capacity and was intended to be used for vaginal discharge between menstruation or to another Times when low menstrual discharge occurs.
Damenbinden des iSchlüpfer-Ausfütterungstyps sind, da sie dazu bestimmt sind, nur minimale Flüssigkeitsmengen aufzunehmen, kleiner und kompakter als die größeren, stärker absorbierenden üblichen sanitären BindenSanitary napkins of the i-panty lining type are there they are designed to absorb only minimal amounts of liquid, smaller and more compact than the larger ones, more absorbent common sanitary napkins
(bzw. Damenbinden oder sanitären Windeln).(or sanitary napkins or sanitary diapers).
Binden dieser Art werden flexibel und weich entworfen. Die Flexibilität ist notwendig, damit die Schlüpfer-Ausfütterung der Bauweise des Perineums angepaßt ist, insbesondere wenn sich der Träger bewegt. Die Flexibilität ist wichtig, insbesondere an den Rändern desSanitary towels of this type are designed to be flexible and soft. Flexibility is necessary so that the panty-lining is adapted to the construction of the perineum, especially when the wearer is moving. The flexibility is important, especially around the edges of the
Umfangs, wegen der Scheuermöglichkeit r die sich bei aufgerauhten Rändern im Kontakt mit der zarten Haut der Fläche der Perineums ergibt*Circumference, r due to the scouring ability of the perineum which results in roughened edges in contact with the delicate skin of the area *
Eine gegenwärtig verfügbare Schlüpfer-Ausfütterung bewirkt die Weichheit an den Längsseiten durch Überfalten der äußeren Umhüllung und des Absorbens unter Bildung eines weichen Rands entlang der Seiten der Binde. Dies kann ohne besondere Schwierigkeit längs den Seiten erzielt werden, jedoch nicht an den Längsenden. Diese Enden sind als angrenzende Schichten der Umhüllung und des Absorptionskissens ausgebildet und können aufschürfen. Die Schichten können sich auch trennen, wodurch nicht nur das Aufschürfen durch Freisetzen mehrerer Enden gegenüber zartem Gewebe verstärkt wird, sondern wordurch auch die Gesamtheit der Binde zerstört werden kann und selbst bei den für die Anwendung der Binde in Betracht kommen den geringen Ausflußmengen könnten Undichtigkeitsstellen entstehen.A currently available panty lining causes the softness on the long sides by overfolding the outer cover and absorbent forming a soft edge along the sides of the Bandage. This can be achieved without particular difficulty along the sides, but not at the longitudinal ends. These ends are designed as adjacent layers of the envelope and the absorbent pad and can dig up. The layers can also separate, which not only causes abrasion is strengthened by exposing several ends to delicate tissue, but also the entirety the bandage can be destroyed and can even be considered for the use of the bandage the small amounts of discharge could cause leaks develop.
Versuche, die Aufspaltung bzw. Delamination an den Enden des Produkts vom Schlüpfer-Ausfütterungstyp zu verhindern, gingen in zwei generelle Richtungen. Die erste besteht in dem Zusammendrücken oder im Prägen der Schichten an den Enden. Der zweite Versuch besteht in dem Auftrag von Klebstoff auf die Enden,um die Umhüllung an das Absorptionskissen in der Fläche zu kleben. Beide Lösungen haben zu Problemen geführt.Attempts to reduce the splitting or delamination of the Preventing ends of the panty-lining type product went in two general directions. the the first is to compress or emboss the layers at the ends. The second attempt is successful in the application of glue on the ends to make the wrapper to the absorbent pad in the area to glue. Both solutions have created problems.
Zwar verhindert der Klebstoff wirksam die Delaminierung, jedoch werden die Endteile auch versteift, wodurch die gewünschte Flexibilität verhindert wird, und die Fähigkeit, die Lage während der Bewegung des Trägers beizubehalten, wird verringert. Wird im Gegensatz hierzu nur eine Prägung verwendet, so wird zwarAlthough the adhesive effectively prevents delamination, however, the end parts are also stiffened, which prevents the desired flexibility, and the ability to control the location while moving the Maintaining the vehicle is reduced. Will in opposition only one embossing is used for this, it is true
die Weichheit erhalten, jedoch tritt häufig, wenn die Enden naß sind, eine Delaminierung auf. Die Delaminierung tritt tatsächlich selbst im trockenen Zustand nach einer gewissen Lagerungszeit auf, wenn das Kissen seinen Feuchtigkeitsausgleich erreicht. Die Delaminierung kann auch während der Anwendung aufgrund der Bewegung des Trägers, die auf die Enden ausgeübt wird, auftreten. Die Nachteile dieser beiden Versuche wurden durch den Gegenstand der vorliegenden Erfindung überwunden.maintain softness, but delamination often occurs when the ends are wet. The delamination actually occurs even in the dry state after a certain storage time, if the pillow reaches its moisture balance. Delamination can also occur during application due to the movement of the wearer exerted on the ends. The disadvantages of both of these Attempts have been overcome by the subject matter of the present invention.
Ein Versuch zur Lösung dieses Problems wurde in der US-Patentanmeldung Serial Nr. 153 210 beschrieben, wo ein Emulsionsklebstoff auf Wasserbasis, zusammen mit einer Prägestufe angewendet wurde, um delaminierungsbeständige Enden bereitzustellen, wobei gleichzeitig die in diesen Gebieten erwünschte Flexibilität erhalten bleibt. Dies wurde erzielt durch Anwendung üblicher Emulsionsklebstoffe auf Wasserbasis, zusammen mit einer Feuchtig- keitsbehandlung, die den Klebstoff reaktivierte. Durch die Erfindung wird eine Verbesserung des vorstehend beschriebenen Konzepts bereitgestellt.One attempt to solve this problem was described in U.S. Patent Application Serial No. 153,210, where a water based emulsion adhesive, along with an embossing step, was applied to make delamination resistant To provide ends, while at the same time maintaining the flexibility desired in these areas. This was achieved by using common water-based emulsion adhesives, together with a moisturizing agent. treatment that reactivated the adhesive. The invention is an improvement on the above described concept provided.
Die Erfindung betrifft eine sanitäre Binde, enthaltend eine Klebstoffzusammensetzung, die besonders geeignet ist zum Eindringen und zum Verfestigen von einem porösen Substrat und zum Kleben einer Oberfläche des Substrats an eine andere Oberfläche, enthaltend:The invention relates to a sanitary napkin containing an adhesive composition which is particularly suitable is for penetrating and solidifying a porous substrate and for bonding a surface of the substrate to another surface containing:
a) mindestens ein-.Wasser-Emulsions-Polymeres, ausgewählt aus der Klasse von Polyvinylacetat-Homopolymeren, Vinylacetat-fithylen-Copolymeren, Polyvinylacetat-Maleat-Copolymeren, Polyvinylacetat-Acryl-a) at least one water emulsion polymer selected from the class of polyvinyl acetate homopolymers, vinyl acetate-ethylene copolymers, polyvinyl acetate-maleate copolymers, Polyvinyl acetate acrylic
Copolymeren und Acrylcopolymeren und 35Copolymers and acrylic copolymers and 35
b) mindestens ein wasserlösliches Polymeres, ausgewählt aus der Klasse von Polyvinylpyrrolidon, einem teil-b) at least one water-soluble polymer selected from the class of polyvinylpyrrolidone, a partially
weise hydrolysierten Polyvinylalkohol und einem vollständig hydrolysierten Polyvinylalkohol.wise hydrolyzed polyvinyl alcohol and a fully hydrolyzed polyvinyl alcohol.
Die erfindungsgemäße Binde enthält eine neuartige Klebstoffzusammensetzung mit besonders günstigen Eigenschaften, geeignent zur Wirkung auf poröse Materialien, mit einem geringen Ausmaß an Kohäsionsfestigkeit, bereitgestellt. The sanitary napkin of the present invention contains a novel adhesive composition with particularly favorable properties, suitable for acting on porous materials, with a low level of cohesive strength.
TO Die Klebstoffzusammensetzung ist besonders geeignet, in ein poröses Substrat einzudringen und es zu festigen ' und eine Oberfläche dieses Substrats an eine andere Oberfläche zu binden, wobei ein Zweikomponenten-Klebstoff system verwendet wird. Die erste Komponente ist- ein Wasser-Emulsions-Polymeres, ausgewählt ausTO The adhesive composition is particularly suitable to penetrate into a porous substrate and to consolidate it 'and one surface of this substrate to another Surface using a two-component adhesive system. The first component is- a water emulsion polymer selected from
der Klasse von Polyvinylacetat-(PVAc)-Homopolymeren, Vinylacetat - Äthylen - (VA-E)-Copolymeren, Polyvinylacetat-Maleat-(PVAcM)-Copolymeren, acrylischen Copolymeren und PVAc-acrylischen-Copolymeren. Die Wasser-Emulsions-Polymeren werden mit einem wasserlöslichen Polymeren vermischt, das ausgewählt wird aus einer Klasse von Polyvinylpyrrolidon (PVP) und einem teilweise oder völlig hydrolysieren Polyvinylalkohol (PVA)the class of polyvinyl acetate (PVAc) homopolymers, vinyl acetate - ethylene (VA-E) copolymers, polyvinyl acetate maleate (PVAcM) copolymers, acrylic copolymers and PVAc-acrylic copolymers. The water emulsion polymers are mixed with a water-soluble polymer selected from one Class of polyvinylpyrrolidone (PVP) and a partially or fully hydrolyzed polyvinyl alcohol (PVA)
Polyvinylacetat-Homopolymeres, wie "Vinac XX-230", der Air Products and Chemicals, Inc., Allentown, Pa., wird gegenwärtig bevorzugt. Aufgrund der Brüchigkeit dieses speziellen Polymeren ist jedoch ein Weichmacher bzw. Plastifiziermittel erforderlich, um den flexiblen Klebstoffilm zu ergeben, der für die meisten Arten von Klebstoffanwendungszwecken erwünscht ist. Ein geeigneter Weichmacher ist Dipropylcnglykol-dibenzoat. Diese Verbindung dient als ein wirksamer Weichmacher und als Adhäsionsbeschleuniger. "Benzoflex 9-88" ist ein handelsüblicher Dipropylenglykol-dibenzoat-Weichmacher, der Velsicol Chemical Corporation, Chicago 111., und ist gegenwärtig bevorzugt.Polyvinyl acetate homopolymer, such as "Vinac XX-230", from Air Products and Chemicals, Inc., Allentown, Pa., Is presently preferred. However, because of the brittleness of this particular polymer, a plasticizer is required to provide the flexible adhesive film desired for most types of adhesive applications. A suitable plasticizer is dipropylene glycol dibenzoate. This compound serves as an effective plasticizer and as an adhesion accelerator. "Benzoflex 9-88" is a commercial dipropylene glycol dibenzoate plasticizer available from Velsicol Chemical Corporation, Chicago 111., and is currently preferred.
Andere Weichmacher, die verwendet werden können, sind Dibutylphthalat, "Santicizer 160", ein Butylbenzylphthalat, "Santicizer 141", ein Cresylphenylphosphat, "Santicizer 8", N-Ä'thyl-o- und p-toluolsulfonämide, alle erhältlich von der Monsanto Chemical Company,Other plasticizers that can be used are dibutyl phthalate, "Santicizer 160", a butyl benzyl phthalate, "Santicizer 141", a cresylphenyl phosphate, "Santicizer 8", N-ethyl-o- and p-toluenesulfonamides, all available from Monsanto Chemical Company,
St. Louis, Mo.
30St. Louis, Mo.
30th
Die (VA-E)-Copolymeren sind "geeignete Alternativen" und weisen ähnliche Adhäsionscharakteristika wie die (PVAc)-Polymeren auf, jedoch ist aufgrund der Anwesenheit des Äthylen -Comonomeren wenig oder kein WeichmacherThe (VA-E) copolymers are "suitable alternatives" and have similar adhesion characteristics to them (PVAc) polymers, but there is little or no plasticizer due to the presence of the ethylene comonomer
erforderlich, um die Flexibilität und bestimmterequired to have the flexibility and certain
Adhäsionsarten, insbesondere an nichtporösem Substrat, • zu erzielen. Ein geeignetes (VA-E)-Copolymeres istTypes of adhesion, especially on non-porous substrates, • to achieve. A suitable (VA-E) copolymer is
Airflex 400 der Air Products and Chemicals, Inc., Allentown, Pa.
5Airflex 400 from Air Products and Chemicals, Inc., Allentown, Pa.
5
Geeignete wasserlösliche Polymere für diese Klebstoff-Kombination sind Polyvinylpyrrolidon (PVP), das eine ausgezeichnete Wasserlöslichkeit in. Verbindung mit guten Substrat-Benetzungseigenschaften aufweist.Suitable water-soluble polymers for this adhesive combination are polyvinylpyrrolidone (PVP), which has excellent water solubility in. Compound with good substrate wetting properties.
PVP wird gegenwärtig als wasserlösliche polymerePVP is currently used as a water-soluble polymer
Komponente bevorzugt. Alternativ sind wasserlösliche Polymere, die für die Lehre der Erfindung geeignet sind, teilweise hydrolysierte und vollständig hydrolysierte Polyvinylalkohole. Teilweise hydrolysierte PVA sind erhältlich in einer Vielzahl von Molekulargewichtsbereichen von der Monsanto Chemical Company und werden als Gelvatol-Harze verkauft. PVA-Polymere sind besonders geeignet aufgrund ihrer hohen Kohäsionsfestigkeit und ihrer guten filmbildenden Eigenschäften. Die Wahl des Polymergrads bzw. der Polymersorte in der Kategorie der teilweise hydrolysieren Polyvinylalkohole hängt von der gewünschten Viskosität ab, die für die Klebstoffanwendungszwecke erforderlich ist. Dies wird nachstehend genauer diskutiert , kann aber abhängen von der Anwendungsmethode des Klebstoffs. Wird beispielsweise der Klebstoff durch Sprühen aufgetragen, so ist die höchst lösliche Sorte und die Sorte mit dem geringsten Molekulargewicht an PVA-Polymeren bevorzugt. Völlig hydrolysierteComponent preferred. Alternatively, water-soluble polymers are suitable for the teaching of the invention are, partially hydrolyzed and fully hydrolyzed polyvinyl alcohols. Partly hydrolyzed PVAs are available in a variety of molecular weight ranges from Monsanto Chemical Company and are sold as Gelvatol resins. PVA polymers are particularly suitable due to their high cohesive strength and their good film-forming properties. The choice of the polymer grade or type in the category of partially hydrolyze polyvinyl alcohols depends on the desired viscosity required for the adhesive application purposes. This is discussed in more detail below, but may depend on the method of application of the adhesive. For example, the glue gets through Spray applied so is the most soluble variety and the variety with the lowest molecular weight preferred on PVA polymers. Completely hydrolyzed
^0 PVA-Polymere sind von der E. I. DuPont de Nemour &^ 0 PVA polymers are from EI DuPont de Nemour &
Company, Wilmington, Delaware, unter dem Warenzeichen Elvanol erhältlich- Es sei festgestellt, daß PoIyvinylalkoholpolymere hergestellt werden dadurch, daß man zuerst das Polyvinylacetatpolymere bildet und anschließend das Polyvinylacetatpolymere unter BildungCompany, Wilmington, Delaware, under the trademark Elvanol. It should be noted that polyvinyl alcohol polymers are made by first forming the polyvinyl acetate polymer and then forming forming the polyvinyl acetate polymer
eines PVA-Polymeren hydrolysiert. Teilweise hydrolysierte Sorten von Polyvinylalkohol enthalten daher 10 bis 25 % Vinylacetatgruppen, während die völlig hydrolysierten Sorten weniger als 1 % der Vinylacetatgruppen enthalten. Die völlig hydrolysierten PVA-Polymeren sind geeignet für Klebstoffanwendungen, die eine besondere Feuchtigkeitsbeständigkeit in der Klebe- : bindung erfordern.of a PVA polymer hydrolyzed. Partly hydrolyzed Varieties of polyvinyl alcohol therefore contain 10 to 25% vinyl acetate groups, while the completely hydrolyzed varieties contain less than 1% of the vinyl acetate groups. The fully hydrolyzed PVA polymers are suitable for adhesive applications that require a require special moisture resistance in the adhesive bond.
Zusätzlich zu Weichmachern kann das erfindungsgemäße Klebstoffgemisch geringe Mengen, d.h. 0,1 bis 0,2 % an Benetzungsmitteln und/oder Entschäumungsmitteln enthalten, um die Lagerungsstabilität des flüssigen Klebstoffs zu fördern und die Schaumbildung während des Auftrags des Klebstoffs auf ein Minimum herabzusetzen. Geeignete Benetzungsmibtel sind "Aerosol OT" der American Cyanamid Company, Wayne, N.J. und "Triton X-100" der Rohm & Haas Company, Philadelphia, Pa. Ein alternativer Entschäumer ist Nopco JMY, erhältlieh von der Nopco Chemical Company, Newark, N.J.In addition to plasticizers, the adhesive mixture according to the invention can contain small amounts, i.e. 0.1 to 0.2% contained in wetting agents and / or defoaming agents to ensure the storage stability of the liquid To promote the adhesive and reduce the formation of foam to a minimum during the application of the adhesive. Suitable wetting agents are "Aerosol OT" of the American Cyanamid Company, Wayne, N.J. and "Triton X-100" from Rohm & Haas Company, Philadelphia, Pa. An alternative defoamer is Nopco JMY, available from Nopco Chemical Company, Newark, N.J.
Im allgemeinen weist die erfindungsgemäße Klebstoffzusammensetzung 20 bis 90 % der Wasser-Emulsions-Polymerkomponente und 5 bis 50 % der wasserlöslichen PoIymerkomponente auf. Diese Prozentsätze sind Gew.-% der festen Komponenten des Klebstoffgemischs im Gegensatz zu dem % des handelsüblichen Bestandteils, der Wasser enthält. Die günstigen Mengen der Bestandteile variieren mit der Menge und dem Ausmaß des gewünschten Eindrin-In general, the adhesive composition of the invention has 20 to 90% of the water emulsion polymer component and 5 to 50% of the water soluble polymer component on. In contrast, these percentages are percentages by weight of the solid components of the adhesive mixture to the% of the commercial component that contains water. The beneficial amounts of the ingredients will vary with the amount and extent of penetration desired
ow gens (Penetration) in poröses Substrat , sowie mit dem Ausmaß der verbleibenden Adhäsion, die an der Oberfläche des Absorbenssubstrats benötigt wird, sowie mit anderen Faktoren, die auf dem Gebiet der Klebstoffe bekannt sind. Ein. Weichmacher ist im allgemeinen von 5 bis 40 Gew.-% der Klebstoffzusammensetzung vorhanden, wobei die Menge des Weichmachers ow gens (penetration) into the porous substrate, as well as the amount of remaining adhesion needed to the surface of the absorbent substrate, as well as other factors known in the adhesive art. A. Plasticizer is generally present from 5 to 40 percent by weight of the adhesive composition, the amount of plasticizer being
von der speziellen Wahl des Wasseremulsionspolymeren und der gewünschten vorhandenen Flexibilitätsmenge sowie von der Oberfläche abhängt, an die das poröse Substrat geklebt werden soll.on the special choice of water emulsion polymer and the desired amount of flexibility present as well as the surface to which the porous Substrate to be glued.
Im folgenden wird die beigefügte Figur beschrieben. Die Verwendung dieses Klebstoffs in der erfindungsgemäßen Schlüpfer-Ausfütterung ist anhand der Fig. gut verständlich, die eine perspektivische Ansicht, teilweise im Querschnitt, einer mit diesem Klebstoff hergestellten Schlüpfer-Ausfütterung zeigt.The attached figure is described below. The use of this adhesive in the inventive The lining of the panties is easy to understand with reference to the figure, which is a perspective view, shows partially in cross section, a panty lining made with this adhesive.
Bei dieser speziellen Ausfuhrungsform ist das Kissen aufgebaut durch Luftauflage von Holzzellstoffflaum (air laying) auf eine Trägerschicht aus grobem Gewebe (bzw. grobem Leinen- oder Baumwollgewebe) 5. Eine dünne Schicht des erfindungsgemäßen Klebstoffs wird anschließend auf den oberen Teil des Flaums aufgeschichtet, und ein Deckmaterial, wie ein gebundenes kardiertes Gewebe oder ein gebundener Krempelflor 2 mit einem Prägemuster 1 wird über den mit Klebstoff beschichteten Flaum 4 golegt. Der Klebstoff wird anschließend auf den grob gewebten Träger aufgeschichtet und dringt in ihn ein, um ihn an den Flaum 4 zu binden. Der Klebstoff verleiht der Flaumschicht 4 auch Integrität und bindet sie an das Deckmaterial 2. Zwar ergibt das in der vorstehend genannten US-Patentanmeldung 153 210In this special embodiment, the pillow built up by an air layer of wood pulp fluff (air laying) on a carrier layer made of coarse fabric (or coarse linen or cotton fabric) 5. One thin layer of the adhesive according to the invention is then coated on the upper part of the fluff, and a cover material such as a bonded carded fabric or a bonded card pile 2 with a Embossing pattern 1 is placed over the fluff 4 coated with adhesive. The adhesive is then applied to the coarsely woven carrier is piled up and penetrates into it to bind it to the fluff 4. The adhesive also gives the fluff layer 4 integrity and binds it to the cover material 2. Although this results in the above U.S. Patent Application No. 153,210 referred to above
beschriebene Verfahren eine geeignete Bindung an das Deckmaterial, jedoch ist esmethod described a suitable bond to the cover material, however, it is
°^ nicht so wirksam bei der Erhöhung der Integrität der Flaumschicht, und selbst mit der dort beschriebenen Behandlung kann sich die Flaumschicht trennen.° ^ not so effective in increasing the integrity of the Fluff layer, and even with the treatment described there, the fluff layer can separate.
Zu diesem Zeitpunkt des Verfahrens stoßen sämtliche Schichten an ihrem gesamtem Umfang aneinander undAt this point in the process, all of the layers abut each other and at their entire perimeter
werden in langen Rollen hergestellt, die etwa zweimal der Breite des fertiggestellten Kissens entsprechen. Zusätzlich wird der erfindungsgemäße Klebstoff dann auf die Fläche 3 aufgetragen. Die Struktur wird an den Seiten umgefaltet, so daß die peripheren Seitenränder aneinanderstoßen. Wie aus der Fig. 1 ersichtlich, führt dies zu einer Bauweise, bei der die äußeren Schichten sowohl oben als auch unten das Deckmaterial 2 sind. Das grobgewebte Trägermaterial 5 wird als innerste Schicht über sich selbst gefaltet,und der Flaum 4 liegt zwischen der Deckschicht 2 und der grobgewebten Stütze 5 an jeder Seite des groben Gewebes. Die Faltung bleibt durch gelinden Druck erhalten, und es wird der weiche gefaltete Rand 10 erzeugt. Die wasserundurchlässige Trennwand 6 wird anschließend an die aneinanderstoßende Fläche durch Kleben befestigt.are made in long rolls about twice the width of the finished pillow. In addition, the adhesive according to the invention is then applied to the surface 3. The structure is on folded over the sides so that the peripheral side edges abut one another. As can be seen from Fig. 1, this leads to a construction in which the outer layers both above and below the cover material 2 are. The coarsely woven carrier material 5 is folded over itself as the innermost layer, and the fluff 4 lies between the cover layer 2 and the coarse woven support 5 on each side of the coarse fabric. The folding is retained by applying gentle pressure, and the soft folded edge 10 is produced. The waterproof one Partition 6 is then attached to the abutting surface by gluing.
Anschließend wird die Rolle an jedem Ende geprägt, um das randversteifte Ende 3 zu bilden. Ein Wäsche-Klebstoff und ein Abzugspapier werden anschließend in üblicher Weise aufgebracht, und die Enden werden gebildet. Anschließend wird die Binde geschnitten.Then the roll is embossed to at each end to form the stiffened edge 3. A laundry glue and a release paper are then applied in a conventional manner and the ends are formed. Then the bandage is cut.
Eine besonders bevorzugte Klebstoffzusammensetzung der Erfindung zur Anwendung als eine Endabdichtung für Schlüpferausfütterungen ist ein Gemisch aus 70 % Polyvinylacetat-Homopolymerem mit 10 % PVP und 10 % teilweise hydrolysiertem PVA und 10 % Dipropylenglykol-dibenzoat als einem Weichmacher. Das PVP lie-A particularly preferred adhesive composition of the invention for use as an end seal for panty linings is a mixture of 70% Polyvinyl acetate homopolymer with 10% PVP and 10% partially hydrolyzed PVA and 10% dipropylene glycol dibenzoate as a plasticizer. The PVP provides
fert die Substratbenetzung- und Penetrationseigenschaften, die benötigt werden, um die Integrität zu erhalten und verhindert die Delaminierung der verschiedenen Absorptionsschichten an den Enden des Kissens, während das teilweise hydrolysierte PVA zur Klebstoffilm-Festigkeit beiträgt, die benötigtproduces the substrate wetting and penetration properties needed to maintain integrity and prevents delamination of the various absorbent layers at the ends of the Cushion, while the partially hydrolyzed PVA adds to the adhesive film strength that is needed
1 wird, um eine günstige Bindung zwischen der Umhüllung und den Absorptionsmaterialien zu ergeben.1 is used to create a favorable bond between the wrapping and to give the absorbent materials.
Claims (5)