DE3130018A1 - Objects having reflection and screening properties for electromagnetic radiation, and a method for manufacturing them - Google Patents

Objects having reflection and screening properties for electromagnetic radiation, and a method for manufacturing them

Info

Publication number
DE3130018A1
DE3130018A1 DE19813130018 DE3130018A DE3130018A1 DE 3130018 A1 DE3130018 A1 DE 3130018A1 DE 19813130018 DE19813130018 DE 19813130018 DE 3130018 A DE3130018 A DE 3130018A DE 3130018 A1 DE3130018 A1 DE 3130018A1
Authority
DE
Germany
Prior art keywords
metal
object according
carrier
article
electromagnetic radiation
Prior art date
Legal status (The legal status is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the status listed.)
Withdrawn
Application number
DE19813130018
Other languages
German (de)
Inventor
Fritz 4154 Tönisvorst Stahl
Current Assignee (The listed assignees may be inaccurate. Google has not performed a legal analysis and makes no representation or warranty as to the accuracy of the list.)
RUWEL WERKE GmbH
Original Assignee
RUWEL WERKE GmbH
Priority date (The priority date is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the date listed.)
Filing date
Publication date
Application filed by RUWEL WERKE GmbH filed Critical RUWEL WERKE GmbH
Priority to DE19813130018 priority Critical patent/DE3130018A1/en
Publication of DE3130018A1 publication Critical patent/DE3130018A1/en
Withdrawn legal-status Critical Current

Abstract

The present invention relates to objects for screening and for reflecting electromagnetic radiation, such as radar signals for example, which consist of a carrier or contain such a carrier, whose externally accessible surface is provided with a metal coating.

Description

Die vorliegende Erfindung betrifft Gegenstände zum Abschir-The present invention relates to objects for shielding

men bzw. zum Reflektieren von elektromagnetischer Strahlung, beispielsweise von Radarsignalen, und Verfahren zu deren Herstellung.men or for reflecting electromagnetic radiation, for example of radar signals, and methods of producing them.

Als Abschirmung bzw. als Reflektor werden bislang entsprechend geformte Gebilde aus: Metall benutzt. Solche -Gebilde bestehen aus geschlossenen Metallflächen, .Metallgeweben oder Konstruktionen aus Metallelementen.So far, appropriately shaped ones have been used as a shield or as a reflector Structure made of: metal used. Such structures consist of closed metal surfaces, .Metal fabrics or constructions made from metal elements.

So wurde bereits vorgeschlagen, Landebahnbegrenzungen in Form von Radar-Reflektoren aus tafelförmigem Material bzw. in Form von Metallzäunen zu verwenden. Zur besseren Kenntlichmachung von Schiffen mit Bootskörpern aus nichtmetallischem Material c wie Holz oder faserverstärktem Polyestermaterial wurden bereits Radar-Reflektoren vorgeschlagen, die beispielsweise auf dem Mast von Segelbooten bzw. dem Kabinendach von Motorbooten oder dergleichen angebracht werden. Diese Reflektoren bestehen beispielsweise aus vier senkrecht aufeinander stehenden, halbkreisförmigen Metallscheiben oder aus zwei unter einem Winkel von 900 zueinander angeordneten Metallringen mit gemeinsamem Ringmittelpunkt oder dergleichen.It has already been proposed to use runway boundaries in the form of To use radar reflectors made of sheet material or in the form of metal fences. For better identification of ships with hulls made of non-metallic Material c such as wood or fiber-reinforced polyester material were already radar reflectors proposed, for example, on the mast of sailboats or the cabin roof be attached by motor boats or the like. These reflectors exist for example from four perpendicular, semicircular metal disks or of two metal rings arranged at an angle of 900 to each other with a joint Ring center point or the like.

Ahnliche Reflektor-Anordnungen zum Markieren von Flughindernissen oder von geographischen Orten auf See oder Land bzw.Similar reflector arrangements for marking flight obstacles or from geographical locations at sea or on land or

zum Richten von auszusendenden oder zu empfangenden elektromagnetischen Signalen wurden gleichfalls bereits vorg$schlagen.for directing electromagnetic signals to be transmitted or received Signals have also been suggested.

Reflektoren nach dem Stand der Technik haben den Nachteil eines relativ hohen Gewichtes sowie einer aufwendigen Konstruktion.Prior art reflectors have the disadvantage of being relatively high weight and a complex construction.

Weiterhin wirkt sich deren relativ hoher Widerstand auf verschiedenen Anwendungsgebieten nachteilig aus.Furthermore, their relatively high resistance affects various Areas of application are disadvantageous.

Abschirmungen gegen elektromagnetische Strahlung bestehen in der Regel aus Metallgehäusen für den abzuschirmenden Raum bzw.There are usually shields against electromagnetic radiation made of metal housings for the room to be screened or

zum Umschließen einer abzuschirmenden Anordnung. Diese Gehäuse bestehen entweder aus massivem Metall oder aus Metallgittern, -netzen oder dergleichen. Auch das Auftragen von Leitlacken auf Flächen von Behältnissen oder dergleichen wurde bereits vorgeschlagen.for enclosing an arrangement to be shielded. These housings exist either from solid metal or from metal grids, nets or the like. Even the application of conductive lacquers to surfaces of containers or the like already proposed.

Für die zunächst benannten Abschirmanordnungen gelten die im Bezug auf Reflektoren aufgeführten Nachteile in gleicher Weise; Leitlacküberzüge sind nicht nur relativ instabil, sondern auch von nur begrenzter Wirksamkeit.For the shielding arrangements mentioned first, those in relation apply disadvantages listed on reflectors in the same way; Conductive lacquer coatings are not only relatively unstable, but also of limited effectiveness.

Die vorliegende Erfindung betrifft einen Gegenstand bzw. Gegenstände, die die aufgeführten Nachteile vermeiden und weitere, wirtschaftliche und technische Vorzüge gegenüber dem bekannten Stand der Technik aufweisen, sowie Verfahren zu deren Herstellung.The present invention relates to an object or objects, which avoid the disadvantages listed and others, economic and technical Have advantages over the known prior art, as well as methods their manufacture.

Nach der vorliegenden Erfindung wird die Aufgabe derart gelöst, daß der Gegenstand zum Abschirmen bzw. zum Reflektieren von elektromagnetischer Strahlung, beispielsweise von Radarsignalen, aus einem Träger aus der Reihe der Wirrgespinste, insbesondere Kunststoff-Wirrgespinste, Fasergewebe und Schaumkörper besteht, dessen von außen zugängliche Flächen mindestens eine durch stromlose Metallabscheidung aufgebrachte Metallschicht aufweisen, bzw. einen solchen mit mindestens einer Metallschicht versehen# Träger enthält.According to the present invention, the object is achieved in such a way that the object for shielding or for reflecting electromagnetic radiation, for example from radar signals from a carrier from the series of random webs, in particular there is random plastic spun, fiber fabric and foam body, its Areas accessible from the outside at least one by electroless metal deposition have applied metal layer, or such with at least one metal layer provided # carrier contains.

Vorteilhafterweise wird die Metallschicht bzw. werden die Metallschichten aus einem oder mehreren der Metalle aus der Reihe von Kupfer, Nickel, Kobalt, Chrom, Zink, einem Edelmetall, Legierungen dieser Metalle bzw. einer Nickel-Zinn-Legierung aufgebaut.The metal layer or the metal layers are advantageously from one or more of the metals from the Series of copper, nickel, Cobalt, chromium, zinc, a noble metal, alloys of these metals or a nickel-tin alloy built up.

Es hat sich weiterhin als vorteilhaft erwiesen, die Metallschicht, bei mehreren Schichten zumindest die oberste Schicht, aus einem Metall bzw. einer Legierung aufzubauen, die korrosionsbeständig gegen See- und/oder Süßwasser und/oder atmosphärischen Einflüssen ist.In einer anderen Ausführungsform wird die Metallbeschichtung mit einem korrosionsfesten Kunststoffüberzug ausgerüstet. Das Trägermaterial wird aus Kunststoff-Wirrgespinsten bzw. geschäumten Kunststoffen, hier als Kunststoff-Schaumkörper bezeichnet, sowie aus Kunststoffschwämmen ausgewählt. Nach der vorliegenden Erfindung kann von Formkörpern wie Platten, vorgeformten Gestaltungen sowie Rotationskörpern einsc'hließlich aufgeschäumter Granulate oder Chips ausgegangen werden, deren von außen zugängliche Flächen metallbeschichtet werden. Ebenso kann beispielsweise von metallbeschichtetem Rollenmaterial ausgegangen werden, das nach träglich in die gewünschte Endform gebracht wird.It has also proven to be advantageous to use the metal layer, in the case of several layers, at least the top layer, made of one metal or one Build alloy that is corrosion-resistant to sea and / or fresh water and / or atmospheric influences. In another embodiment, the metal coating Equipped with a corrosion-resistant plastic coating. The carrier material will made of random-spun plastic or foamed plastics, here as a plastic foam body as well as selected from plastic sponges. According to the present invention can consist of shaped bodies such as plates, preformed shapes and solid bodies of revolution including foamed granules or chips are assumed, whose of externally accessible surfaces are coated with metal. Likewise, for example, from metal-coated roll material are assumed, which is subsequently added to the desired final shape is brought.

Weiterhin werden nach einer Ausgestaltungsform erfindungsgemäße Gegenstände hergestellt, indem metallbeschichtetes Trägermaterial als Füllstoff bzw. Verstärkungsmaterial in Kunststoff eingebettet wird, beispielsweise als Lagenmaterial für Bootskörper aus Kunststoff, wie z.B. Polyesterharzen, oder als Einlage in anderen Wickelkörpern wowie in im Gieß- bzw.Furthermore, according to one embodiment, objects according to the invention are provided produced by using metal-coated carrier material as filler or reinforcement material is embedded in plastic, for example as a sheet material for boat hulls made of plastic, such as polyester resins, or as an insert in other wound cores how in the pouring resp.

Schichtpreßstoff-Verfahren hergestellten Formkörpern.Moldings produced by laminate method.

Nach einer weiteren Ausführungsform besteht der Träger aus schwimmfahigem Material, beispielsweise aus Schaumkunststoff--Chips mit geschlossenen Poren.According to a further embodiment, the carrier is made of buoyant Material, for example made of foam plastic - chips with closed pores.

Geeignete Wirrgespinste und Fasergewebe sind solche aus Glas sowie, bevorzugt, Kunststoffen. -Beispielsweise geeignete Schaumstoffe sind solche aus Kautschuk sowie Kautschuk/Kunststoff-Mischungen wie Moos-, Schaum- und Schwammgummi sowie frei- oder formgeschäumte Körper beispielsweise aus Polystyrol und dessen Copolymeren, Hart- sowie Weich-PVC, Polykarbonate, Polyolefine, Polyurethane, Polyisocyanurate, Polycarbodiimide, Polymethakrylatamide, Polyamide, ABS, Phenol- und Harnstoffharze. Je nach Anwendungszweck des Schaumstoffes wird dieser in an sich bekannter Weise mit offener bzw. geschlossener oder gemischter Zellstruktur hergestellt. In bestimmten Fällen eignen sich auch besonders offenzellige Schaumstoffe mit geschlossener Außenhaut.Suitable random webs and fiber fabrics are those made of glass as well as, preferred plastics. - For example, suitable foams are those made of Rubber and rubber / plastic mixtures such as foam, foam and sponge rubber as well as free or molded foam bodies, for example made of polystyrene and its Copolymers, rigid and soft PVC, polycarbonates, polyolefins, polyurethanes, polyisocyanurates, Polycarbodiimides, polymethacrylate amides, polyamides, ABS, phenolic and urea resins. Depending on the intended use of the foam, it is made in a manner known per se manufactured with open or closed or mixed cell structure. In particular In some cases, open-cell foams with a closed outer skin are also particularly suitable.

Im folgenden wird die Erfindung anhand von Beispielen näher erläutert, ohne daß damit eine Beschränkung auf diese erfolgt.In the following the invention is explained in more detail by means of examples, without this being restricted to these.

Beispiel 1 Als Ausgangsmaterial dient eine forngeschäumte Kugel mit offenzelliger Struktur aus Hart-PVC mit einem Durchmesser von 400 mm. Example 1 A pre-foamed ball is used as the starting material open-cell structure made of rigid PVC with a diameter of 400 mm.

Nach der Reinigung mit einem Entfettungsmittel wird die Oberfläche in bekannter Weise mikroporös und benetzbar gemacht und für die stromlose Metallabscheidung durch Tauchen in eine SnCl2-Lösung, gefolgt von einer PdCl2-Lösung, katalysiert.After cleaning with a degreaser, the surface becomes Made microporous and wettable in a known manner and for electroless metal deposition catalyzed by immersion in a SnCl2 solution followed by a PdCl2 solution.

Dann wird zunächst eine Kupferschicht aus einer ohne äußere Stromzufuhr arbeitenden Badlösung bis zu einer Dicke von bei= spielsweise 10 zum aufgebracht. Anschließend wird eine weitere Metallschicht aus Nickel auf der Kupferschicht abgeschieden, deren Dicke beispielsweise 5 ßm beträgt.Then a copper layer is first made from one without an external power supply working bath solution up to a thickness of at = for example 10 to applied. Then another metal layer of nickel is applied to the Copper layer deposited, the thickness of which is, for example, 5 .mu.m.

Der so gebildete Reflektor für Radar-Signale, beispielsweise mittels einer zentralen Öffnung auf dem Mast einer Segelyacht angebracht, eignet sich ausgezeichnet zum Radar-Markieren der Yacht.The reflector formed in this way for radar signals, for example by means of attached to a central opening on the mast of a sailing yacht is excellent for radar marking the yacht.

Beispiel 2 Die wie in Beispiel 1 hergestellte Kupferschicht wird zusätzlich oder anstelle der Nickelschicht mit einer korrosionsfesten Lackschicht ausgerüstet. Example 2 The copper layer produced as in Example 1 is in addition to or instead of the nickel layer with a corrosion-resistant lacquer layer equipped.

Beispiel 3 Ausgehend von plattenförmigem, seewasserbeständigem Kunststoff-Wirrgespinst wird dieses als Platten- oder Rollenmaterial gereinigt und für die stromlose Metallabscheidung katalysiert. Example 3 Starting from a plate-shaped, seawater-resistant plastic random web this is cleaned as plate or roll material and for electroless metal deposition catalyzed.

Hierzu dient beispielsweise eine Lösung eines Sn(II)Chlorid-Pd(II)Chlorid-Komplexes bzw. eine Lösung von PdCl2 in Isopropanol.A solution of a Sn (II) chloride-Pd (II) chloride complex, for example, is used for this purpose or a solution of PdCl2 in isopropanol.

Nach dem Aufbringen einer oder mehrerer Metallschichten aus ohne äußere Stromzufuhr arbeitenden Bädern werden drei kreisförmige Platten mit einem Durchmesser von je 400 mm angefertigt. Jede dieser Scheiben wird mit einem von der Peripherie bis zum Kreismittelpunkt reichenden Schlitz geeigneter Breite versehen. Sodann werden die drei Scheiben derart zusammengesetzt, daß 8 Trippelspiegel gebildet werden. Der so hergestellte Radarreflektor eignet sich zum Markieren von an sich zur Reflexion von Radarsignalen wenig oder gar nicht geeigneten Hindernissen und dergleichen.After applying one or more metal layers without outer Electric power working baths are three circular plates with a diameter made of 400 mm each. Each of these disks comes with one from the periphery Provide a slot of suitable width reaching to the center of the circle. Then be the three disks are assembled in such a way that 8 triple mirrors are formed. The one made in this way Radar reflector is suitable for marking obstacles that are hardly or not at all suitable for reflecting radar signals and the same.

Beispiel 4 Rollenmaterial aus Kunstschaumstoff, beispielsweise aus Phenolharz, wird nach entsprechender Vorbehandlung einer ohne äußere Stromzufuhr metalli-sierenden Badlösung ausgesetzt, um so alle von außen zugänglichen Flächen mit einer Metallschicht zu versehen. Die Dicke dieser Schicht richtet sich nach dem Anwendungszweck und ihre Wahl bildet für den Durchschnittsfaj mann kein Problem. Das derart hergestellte plattenförmige Material dient sodann zum Auskleiden von von elektromåggetischer Strahlung abzuschirmenden Räumen. Example 4 Roll material made of synthetic foam, for example from Phenolic resin, after appropriate pretreatment, becomes one without an external power supply exposed to a metallizing bath solution, so all externally accessible surfaces to be provided with a metal layer. The thickness of this layer depends on the application and its choice is not a problem for the average man. The plate-shaped material produced in this way is then used to line Rooms to be shielded from electromagnetic radiation.

Claims (23)

Gegenstände mit Reflexions- bzw. Abschirm-Eigenschaften für elektromagnetische Strahlung sowie Verfahren zu deren Herstellung Patentansprüche: f#71 Gegenstand zum Abschirmen bzw. zur Reflexion von elektromagnetischer Strahlung, beispielsweise Radarsignalen, d ad u r c h g e k e n n z e i c h n e t , daß er aus einem Träger aus der Reihe der Wirrgespinste, insbesondere Kunststoff-Wirrgespinste, Fasergewebe und Schaumkörper besteht, dessen von außen zugängliche Flächen mindestens eine durch stromlose Metallabscheidung aufgebrachte Metallschicht aufweisen, bzw. einen solchen mit mindestens einer Metallschicht versehenen Träger enthält. Objects with reflective or shielding properties for electromagnetic Radiation and a method for producing it. Claims: f # 71 Subject matter for shielding or for reflecting electromagnetic radiation, for example Radar signals that show that it comes from a carrier from the series of random webs, in particular plastic random webs, fiber fabrics and foam body consists, whose externally accessible surfaces at least one through have electroless metal deposition applied metal layer, or such a Contains carrier provided with at least one metal layer. 2 0 Gegenstand nach Anspruch 1, dadurch gekennzeichnet, daß mindestens eine der Schichten aus einem stromlos und/oder galvanisch abgeschiedenen Metall aus der Reihe von Kupfer, Nickel, Kobalt, Chrom, Zink, einem Edelmetall, Legierungen der Metalle sowie einer Nickel-Zinn-Legierung besteht.2 0 object according to claim 1, characterized in that at least one of the layers made of an electroless and / or electrodeposited metal from the series of copper, nickel, cobalt, chromium, zinc, a precious metal, alloys the metals and a nickel-tin alloy. 3. Gegenstand nach einem der Ansprüche 1 oder 2, dadurch gekennzeichnet, daß die Metallschicht, bei mehreren Schichten zumindest die oberste Schicht, korrosionsbeständig gegenüber See- und/oder Süßwasser und/oder atmosphärischen Einflüssen ist.3. Object according to one of claims 1 or 2, characterized in that that the metal layer, in the case of several layers at least the top layer, is corrosion-resistant against sea and / or fresh water and / or atmospheric influences. 4. Gegenstand nach einem der Ansprüche 1 bis 3, dadurch gekennzeichnet, daß die Oberfläche der Metallbeschichtung mit einem korrosionsfesten Kunststoffüberzug versehen ist.4. Object according to one of claims 1 to 3, characterized in that that the surface of the metal coating with a corrosion-resistant plastic coating is provided. 5. Gegenstand nach Anspruch 1, dadurch gekennzeichnet, daß der Träger luftdurchlässig ist.5. The article of claim 1, characterized in that the carrier is air permeable. 6. Gegenstand nach Anspruch 1, dadurch gekennzeichnet, daß der Träger im wesentlichen bzw. zur Gänze flüssigkeitsundurchlässig ist.6. The article of claim 1, characterized in that the carrier is substantially or entirely impermeable to liquids. 7. Gegenstand nach einem der Ansprüche 1 bis 6, dadurch gekennzeichnet, daß dieser kugelförmig ist.7. Object according to one of claims 1 to 6, characterized in that that this is spherical. 8. Gegenstand nach einem der Ansprüche 1 bis 6, dadurch gekennzeichnet, daß dieser aus einem aus plattenförmigem Trägermaterial gebildeten Dachkantenprisma besteht oder ein solchea enthält.8. Object according to one of claims 1 to 6, characterized in that that this is made of a roof prism formed from plate-shaped support material exists or contains such a. 9. Gegenstand nach einem der Ansprüche 1 bis 6, dadurch gekennzeichnet, daß das metallisierte Trägermaterial eine Oberfläche mit Spiegelform bildet.9. Object according to one of claims 1 to 6, characterized in that that the metallized carrier material forms a surface with a mirror shape. 10. Gegenstand nach einem der Ansprüche 1 bis 6, dadurch gekennzeichnet, daß das metallisierte Trägermaterial als Füllstoff für einen Formkörper aus Kunststoff dient.10. Object according to one of claims 1 to 6, characterized in that that the metallized carrier material as a filler for a molded body made of plastic serves. 11. Gegenstand nach Anspruch 10, dadurch gekennzeichnet, daß der Formkörper die Außenflächen eines Fahrzeugs oder eines Teiles desselben, beispielsweise eines Bootsrumpfes oder Bootsmastes, bildet.11. The article according to claim 10, characterized in that the shaped body the outer surfaces of a vehicle or a part thereof, for example one Boat hull or boat mast, forms. 12. Gegenstand nach einem der Ansprüche 1 bis 10, dadurch gekennzeichnet, daß dieser zur Radar markierung von Landebahnen, Flughindernissen und dergleichen dient.12. Object according to one of claims 1 to 10, characterized in that that this for radar marking of runways, flight obstacles and the like serves. 13. Gegenstand nach einem der Ansprüche 1 bis 7, dadurch gekennzeichnet, daß als Träger ein Kunstschaumstoff-Rotationskörper, beispielsweise ein Granulat bzw. Chip, dient.13. Object according to one of claims 1 to 7, characterized in that that as a carrier a synthetic foam body of revolution, for example a granulate or chip. 14. Gegenstand nach Anspruch 13, dadurch gekennzeichnet, daß das metall-beschichtete Granulat im wesentlichen bzw. vollständig wasserundurchlässig und schwimmfähig ist; und daß es sich in einem Behältnis aus wasserlöslichem Material befindet; und daß das freigelegte Granulat eine große, auf der Wasseroberfläche schwimmende Reflexionsfläche für Radarsignale bildet.14. The article of claim 13, characterized in that the metal-coated Granules are essentially or completely impermeable to water and buoyant; and that it is in a container made of water-soluble material; and that the exposed granules create a large reflective surface floating on the surface of the water for radar signals. 15. Gegenstand nach Anspruch 14, dadurch gekennzeichnet, daß sich das Granulat innerhalb eines ersten, wasserlöslichen Behältnisses in einem zweiten, beispidsweise netzförmigen Behältnis aus wasserunlöslichem Material befindet, das so bemessen ist, daß es sich nach dem Auflösen des ersten Behältnisses entfaltet und damit die Ausbildung des großflächigen, aus dem metallisierten Granulat bestehenden Radar-Reflektors bewirkt.15. The article of claim 14, characterized in that the granules within a first, water-soluble container in a second, for example a net-shaped container made of water-insoluble material is located, which is dimensioned so that it is after dissolving the first container unfolds and thus the formation of the large-area, from the metallized granulate existing radar reflector causes. 16. Gegenstand nach einem der Ansprüche 1 bis 6 in Form einer Schwimmweste, Rettungsinsel bzw. eines Rettungsringes, dadurch gekennzeichnet, daß die Füllung bzw. Ausfütterung zumindest teilweise aus metallisiertem Trägermaterial besteht.16. Object according to one of claims 1 to 6 in the form of a life jacket, Life raft or a life ring, characterized in that the filling or lining consists at least partially of metallized carrier material. 17. Gegenstand nach einem der Ansprüche 1 bis 6 in Form einer Abwurfbombe zum Markieren von geografischen Orten, dadurch gekennzeichnet, daß die Füllung der Abwurfbombe aus metallisiertem Füllstoff, vorzugsweise aus schwimmfähigen Chips, besteht.17. Object according to one of claims 1 to 6 in the form of a dropping bomb for marking geographical locations, characterized in that the filling of the Drop bomb made of metallized filler, preferably made of floatable chips, consists. 18. Verfahren zum Herstellen einer Abschirmung bzw. eines Reflektors für elektromagnetische Strahlung, beispielsweise für Radarsignale, nach einem oder mehreren der Ansprüche 1 bis 6, dadurch gekennzeichnet, daß ein Formkörper aus dem Trägermaterial zunächst in diege#wünschte Form gebracht und anschließend mit einer oder mehreren Metallschichten versehen wird.18. Method for producing a shield or a reflector for electromagnetic radiation, for example for radar signals, according to an or several of claims 1 to 6, characterized in that a molded body from the Carrier material first brought into the desired shape and then with a or several metal layers is provided. 19. Verfahren zum Herstellen einer Abschirmung bzw. eines Reflektors für elektromagnetische Strahlung, beispielsweise Radarsignale, nach einem der Ansprüche 1 bis 6, dadurch gekennzeichnet, daß das Trägermaterial nach dem Aufbringen einer oder mehrerer Metallschichten in die für den Reflektor bzw.19. Method for producing a shield or a reflector for electromagnetic radiation, for example radar signals, according to one of the claims 1 to 6, characterized in that the carrier material after the application of a or several metal layers in the for the reflector or die Abschirmung gewünschte Form gebracht wird.the shielding is brought into the desired shape. 20. Verfahren nach einem der Ansprüche 18 oder 19, dadurch gekennzeichnet, daß der Formkörper als Rotationskörper, vorzugsweise in Kugelform ausgebildet ist.20. The method according to any one of claims 18 or 19, characterized in that that the shaped body is designed as a body of revolution, preferably in spherical shape. 21. Verfahren zum Herstellen eines Gegenstandes mit Reflexionseigenschaften für Radar-Strahlung, dadurch gekennzeichnet, daß der metallisierte Träger nach einem der Ansprüche 1 bis 6 als Füllstoff für einen Formkörper aus Kunststoff dient.21. A method of making an article with reflective properties for radar radiation, characterized in that the metallized carrier according to a of claims 1 to 6 is used as a filler for a molded body made of plastic. 22. Verfahren nach einem der Ansprüche 18 bis 21, dadurch gekennzeichnet, daß das Trägermaterial gereinigt, gegebenenfalls nach einer Vorbehandlung zur Benetzbarmachung seiner Oberfläche für die stromlose Metallabscheidung katalysiert und anschließend mit einer oder mehreren, ohne äußere Stromzufuhr abgeschiedenen Metallschicht(en) allein oder zusammen mit einer oder mehreren, galvanischaufgebauten Metallschicht(en) überzogen wird.22. The method according to any one of claims 18 to 21, characterized in that that the carrier material is cleaned, if necessary after a pretreatment to make it wettable its surface catalyzed for electroless metal deposition and then with one or more metal layer (s) deposited without an external power supply alone or together with one or more, electroplated metal layer (s) is covered. 23. Verfahren nach Anspruch 22, dadurch gekennzeichnet, daß zum Katalysieren eine alkoholische Lösung von PdCl2, vorzugsweise eine solche in Isopropanol, benutzt wird.23. The method according to claim 22, characterized in that for catalyzing an alcoholic solution of PdCl2, preferably one in isopropanol, is used will.
DE19813130018 1981-07-30 1981-07-30 Objects having reflection and screening properties for electromagnetic radiation, and a method for manufacturing them Withdrawn DE3130018A1 (en)